“Synthesis and structural investigations on the new Sr1.32Mn0.83Cu0.17O3 compound”. Abakumov AM, Mironov AV, Govorov VA, Lobanov MV, Rozova MG, Antipov EV, Lebedev OI, Van Tendeloo G, Solid state sciences 5, 1117 (2003). http://doi.org/10.1016/S1293-2558(03)00141-9
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.811
Times cited: 8
DOI: 10.1016/S1293-2558(03)00141-9
|
“Synthesis and structural study of hexagonal pervoskites in the Ba5>Ta4O15-MZrO3 (M=Ba, Sr) system”. Abakumov AM, Shpanchenko RV, Antipov EV, Lebedev OI, Van Tendeloo G, Amelinckx S, Journal of solid state chemistry 141, 492 (1998). http://doi.org/10.1006/jssc.1998.8001
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 17
DOI: 10.1006/jssc.1998.8001
|
“Synthesis and structural study of Pb2Re2O7-x pyrochlores”. Abakumov AM, Shpanchenko RV, Antipov EV, Kopnin EM, Capponi JJ, Marezio M, Lebedev OI, Van Tendeloo G, Amelinckx S, Journal of solid state chemistry 138, 220 (1998). http://doi.org/10.1006/jssc.1998.7778
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 5
DOI: 10.1006/jssc.1998.7778
|
“Synthesis and structure of fluorinated RBa2Cu2O6+. (R=Dy, Ho and Tm) phases”. Oleynikov PN, Shpanchenko RV, Rozova MG, Abakumov AM, Antipov EV, Hadermann J, Lebedev OI, Van Tendeloo G, Russian journal of inorganic chemistry 46, 153 (2001)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.787
|
“Synthesis and structure of Ln4Re6-xO19 (Ln=Ce, Pr, Nd) complex oxides”. Bramnik KG, Abakumov AM, Shpanchenko RV, Antipov EV, Van Tendeloo G, Journal of alloys and compounds 278, 98 (1998). http://doi.org/10.1016/S0925-8388(98)00252-7
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 8
DOI: 10.1016/S0925-8388(98)00252-7
|
“Synthesis and structure of Sr2MnGaO5+\delta brownmillerites with variable oxygen content”. Abakumov AM, Rozova MG, Alekseeva AM, Kovba ML, Antipov EV, Lebedev OI, Van Tendeloo G, Solid state sciences 5, 871 (2003). http://doi.org/10.1016/S1293-2558(03)00112-2
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.811
Times cited: 12
DOI: 10.1016/S1293-2558(03)00112-2
|
“Synthesis, crystal structure, and magnetic properties of a novel layered manganese oxide Sr2MnGaO5+\delta”. Abakumov AM, Rozova MG, Pavlyuk BP, Lobanov MV, Antipov EV, Lebedev OI, Van Tendeloo G, Ignatchik OL, Ovtchenkov EA, Koksharov YA, Vasil'ev AN, Journal of solid state chemistry 160, 353 (2001). http://doi.org/10.1006/jssc.2001.9240
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 46
DOI: 10.1006/jssc.2001.9240
|
“Synthesis, crystal structure, transport, and magnetic properties of novel ternary copper phosphides, A2Cu6P5(A = Sr, Eu) and EuCu4P3”. Charkin DO, Urmanov AV, Kazakov SM, Batuk D, Abakumov AM, Knöner S, Gati E, Wolf B, Lang M, Shevelkov AV, Van Tendeloo G, Antipov EV;, Inorganic chemistry 51, 8948 (2012). http://doi.org/10.1021/ic301033h
Abstract: Three new ternary copper phosphides, Sr2Cu6P5, Eu2Cu6P5, and EuCu4P3, have been synthesized from the elements in evacuated silica capsules. Eu2Cu6P5 and Sr2Cu6P5 adopt the Ca2Cu6P5-type structure, while EuCu4P3 is isostructural to BaMg4Si3 and still remains the only representative of this structure type among the ternary Cu pnictides. All three materials show metallic conductivity in the temperature range 2 K <= T <= 290 K, with no indication for superconductivity. For Eu2Cu6P5 and EuCu4P3, long-range magnetic order was observed, governed by 4f local moments on the Eu atoms with predominant ferromagnetic interactions. While Eu2Cu6P5 shows a single ferromagnetic transition at T-C = 34 K, the magnetic behavior of EuCu4P3 is more complex, giving rise to three consecutive magnetic phase transitions at 70, 43, and 18 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 13
DOI: 10.1021/ic301033h
|
“Synthesis, structure and magnetic properties of the new mixed-valence vanadate Na2SrV3O9”. Shpanchenko RV, Chernaya VV, Antipov EV, Hadermann J, Kaul EE, Geibel C, Journal of solid state chemistry 173, 244 (2003). http://doi.org/10.1016/S0022-4596(03)00039-2
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 5
DOI: 10.1016/S0022-4596(03)00039-2
|
“Synthesis, structure and properties of layered bismuthates: (Ba,K)3Bi2O7 and (Ba,K)2BiO4”. Khasanova NR, Kovba ML, Putilin SN, Antipov EV, Lebedev OI, Van Tendeloo G, Solid state communications 122, 189 (2002). http://doi.org/10.1016/S0038-1098(02)00096-0
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.554
Times cited: 3
DOI: 10.1016/S0038-1098(02)00096-0
|
“Ternary magnesium rhodium boride Mg2Rh1-xB6+2x with a modified Y2ReB6-type crystal structure”. Alekseeva AM, Abakumov AM, Chizhov PS, Leithe-Jasper A, Schnelle W, Prots Y, Hadermann J, Antipov EV, Grin Y, Inorganic chemistry 46, 7378 (2007). http://doi.org/10.1021/ic7004453
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 12
DOI: 10.1021/ic7004453
|
“Mg8Rh4B: a new type of boron stabilized Ti2Ni structure”. Alekseeva AM, Abakumov AM, Leithe-Jasper A, Schnelle W, Prots Y, Van Tendeloo G, Antipov EV, Grin Y, Journal of solid state chemistry 179, 2751 (2006). http://doi.org/10.1016/j.jssc.2005.11.029
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 11
DOI: 10.1016/j.jssc.2005.11.029
|
“Pb2.85Ba2.15Fe4SnO13 : a new member of the AnBnO3n-2 anion-deficient perovskite-based homologous series”. Korneychik OE, Batuk M, Abakumov AM, Hadermann J, Rozova MG, Sheptyakov DV, Pokholok KV, Filimonov DS, Antipov EV, Journal of solid state chemistry 184, 3150 (2011). http://doi.org/10.1016/j.jssc.2011.09.029
Abstract: Pb2.85Ba2.15Fe4SnO13, a new n=5 member of the anion-deficient perovskite based AnBnO3n−2 (A=Pb, Ba, B=Fe, Sn) homologous series, was synthesized by the solid state method. The crystal structure of Pb2.85Ba2.15Fe4SnO13 was investigated using a combination of neutron powder diffraction, electron diffraction, high angle annular dark field scanning transmission electron microscopy and Mössbauer spectroscopy. It crystallizes in the Ammm space group with unit cell parameters a=5.7990(1) Å, b=4.04293(7) Å and c=26.9561(5) Å. The Pb2.85Ba2.15Fe4SnO13 structure consists of quasi two-dimensional perovskite blocks separated by 1/2[110](1̄01)p crystallographic shear (CS) planes. The corner-sharing FeO6 octahedra at the CS planes are transformed into edge-sharing FeO5 distorted tetragonal pyramids. The octahedral positions in the perovskite blocks between the CS planes are jointly taken up by Fe and Sn, with a preference of Sn towards the position at the center of the perovskite block. The chains of FeO5 pyramids and (Fe,Sn)O6 octahedra of the perovskite blocks delimit six-sided tunnels at the CS planes occupied by double chains of Pb atoms. The compound is antiferromagnetically ordered below TN=368±15 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 7
DOI: 10.1016/j.jssc.2011.09.029
|
“Sn2-2xSbxFexO4 solid solutions as possible inert anode materials in aluminum electrolysis”. Govorov VA, Abakumov AM, Rozova MG, Borzenko AG, Vassiliev SY, Mazin VM, Afanasov MI, Fabritchnyi PB, Tsirlina GA, Antipov EV, Morozova EN, Gippius AA, Ivanov VV, Van Tendeloo G, Chemistry of materials 17, 3004 (2005). http://doi.org/10.1021/cm048145i
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 11
DOI: 10.1021/cm048145i
|
“_Sr{2}GaScO5, Sr10Ga6Sc4O25, and SrGa0.75Sc0.25O2.5 : a play in the octahedra to tetrahedra ratio in oxygen-deficient perovskites”. Chernov SV, Dobrovolsky YA, Istomin SY, Antipov EV, Grins J, Svensson G, Tarakina NV, Abakumov AM, Van Tendeloo G, Eriksson SG, Rahman SMH;, Inorganic chemistry 51, 1094 (2012). http://doi.org/10.1021/ic202236h
Abstract: Three different perovskite-related phases were isolated in the SrGa(1-x)Sc(x)O(2.5) system: Sr(2)GaScO(5), Sr(10)Ga(6)Sc(4)O(25), and SrGa(0.75)Sc(0.25)O(2.5), Sr(2)GaScO(5) (x = 0.5) crystallizes in a brownrnillerite-type structure [space group (S.G.) Icmm, a = 5.91048(5) angstrom, b = 15.1594(1) angstrom, and c = 5.70926(4) angstrom] with complete ordering of Sc(3+) and Ga(3+) over octahedral and tetrahedral positions, respectively. The crystal structure of Sr(10)Ga(6)Sc(4)O(25) (x = 0.4) was determined by the Monte Carlo method and refined using a combination of X-ray, neutron, and electron diffraction data [S.G. I4(1)/a, a = 17.517(1) angstrom, c = 32.830(3) angstrom]. It represents a novel type of ordering of the B cations and oxygen vacancies in perovskites. The crystal structure of Sr(10)Ga(6)Sc(4)O(25) can be described as a stacking of eight perovskite layers along the c axis ...[-(Sc/Ga)O(1.6)-SrO(0.8)-(Sc/Ga)O(1.8)-SrO(0.8)-](2 center dot center dot center dot) Similar to Sr(2)GaScO(5), this structure features a complete ordering of the Sc(3+) and Ga(3+) cations over octahedral and tetrahedral positions, respectively, within each layer. A specific feature of the crystal structure of Sr(10)Ga(6)Sc(4)O(25) is that one-third of the tetrahedra have one vertex not connected with other Sc/Ga cations. Further partial replacement of Sc(3+) by Ga(3+) leads to the formation of the cubic perovskite phase SrGa(0.75)Sc(0.25)O(2.5) (x = 0.25) with a = 3.9817(4) angstrom. This compound incorporates water molecules in the structure forming SrGa(0.75)Sc(0.25)O(2.5)center dot xH(2)O hydrate, which exhibits a proton conductivity of similar to 2.0 x 10(-6) S/cm at 673 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 14
DOI: 10.1021/ic202236h
|
“The superconducting bismuth-based mixed oxides”. Antipov EV, Khasanova NR, Pshirkov JS, Putilin SN, Bougerof C, Lebedev OI, Van Tendeloo G, Baranov A, Park YW, Journal of low temperature physics
T2 –, International Conference on Physics and Chemistry of Molecular and Oxide, Superconductors (MOS2002), AUG 13-18, 2002, HSINCHU, TAIWAN 131, 575 (2003). http://doi.org/10.1023/A:1022923924607
Abstract: The present paper describes the synthesis, characterization of mixed-valence bismuthates with 3- or 2-dimensional perovskite-like structures and structural criteria that influence superconductivity in these compounds. Single-phase samples of Sr1-xKxBiO3 were prepared for the broad range of K-content: 0.25 less than or equal to x less than or equal to 0.65. For these bismuthates the symmetry of the structure changes from monoclinic to orthorhombic and finally to tetragonal upon increasing the K-content thus resulting in the decrease of the Bi-O distances and reduction of the network distortions. Superconductivity with maximum T-c = 12K exists in the narrow range (x approximate to 0.5 – 0.6) within the stability field of the tetragonal phase (0.33 less than or equal to x less than or equal to 0.65), when the 3-dimensional octahedral framework has close to the ideal perovskite structure arrangement. At the same time compositions with close to optimal Bi-valence (x = 0.33 and 0.43) do not show any sign of superconductivity, probably, due to structural distortions. The layered type (BaK)(3)Bi2O7 and (Ba,K)(2)BiO4 bismuthates belonging to the A(n+1)B(n)O(3n+1) homologous series were investigated Buckling of the (BiO2) layers in the structure of the n = 2 member was revealed The formation of the n=1 bismuthate was found by Electron Microscopy and X-ray powder diffraction studies. Both types of compounds are considered to be possible candidates for new superconducting materials among bismuthates.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.3
Times cited: 3
DOI: 10.1023/A:1022923924607
|
“The superconducting bismuth-based mixed oxides”. Antipov EV, Khasanova NR, Pshirkov JS, Putilin SN, Bougerol C, Lebedev OI, Van Tendeloo G, Baranov AN, Park YW, Current applied physics
T2 –, QTSM and QFS 02 Symposium, MAY 08-10, 2002, SEOUL, SOUTH KOREA 2, 425 (2002). http://doi.org/10.1016/S1567-1739(02)00105-0
Abstract: The present paper describes the synthesis, characterization of mixed-valence bismuthates with three- or two-dimensional perovskite-like structures and structural criteria that influence superconductivity in these compounds. Single-phase samples of Sr1-xKxBiO3 were prepared for the broad range of K-content: 0.25 less than or equal to x less than or equal to 0.65. For these bismuthates the symmetry of the structure changes from monoclinic to orthorhombic and finally to tetragonal upon increasing the K-content thus resulting in the decrease of the Bi-O distances and reduction of the network distortions. Superconductivity with maximum T-c = 12 K exists in the narrow range (x approximate to 0.5-0.6) within the stability field of the tetragonal phase (0.33 less than or equal to x less than or equal to 0.65), when the three-dimensional octahedral framework has close to the ideal perovskite structure arrangement. The layered type (Ba,K)(3)Bi2O7 and (Ba,K)(2)BiO4 bismuthates belonging to the A(n+1)B(n)O(3n+1) homologous series were investigated. Buckling of the (BiO2) layers in the structure of the n = 2 member occurs due to the ordering of alkaline- and alkaline-earth cations between two independent positions. The formation of the one-layer bismuthate was revealed by Electron Microscopy and XRPD studies. Both types of compounds are considered to be possible candidates for new superconducting materials among bismuthates. (C) 2002 Published by Elsevier Science B.V.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.971
Times cited: 2
DOI: 10.1016/S1567-1739(02)00105-0
|
“Transmission electron microscopic study of the defect structure in Sr4Fe6O12+\delta compounds with variable oxygen content”. Rossell MD, Abakumov AM, Van Tendeloo G, Lomakov MV, Istomin SY, Antipov EV, Chemistry and materials 17, 4717 (2005). http://doi.org/10.1021/cm050777x
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 17
DOI: 10.1021/cm050777x
|
“Transmission electron microscopy study of polymorphism in barium gallate BaGa2O4”. Lemmens H, Amelinckx S, Van Tendeloo G, Abakumov AM, Rozova MG, Antipov EV, Phase transitions 76, 653 (2003). http://doi.org/10.1080/0141159021000051055
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.06
Times cited: 6
DOI: 10.1080/0141159021000051055
|
“Uniform patterns of Fe-vacancy ordering in the Kx(Fe,Co)2-ySe2 superconductors”. Kazakov SM, Abakumov AM, Perz-Mato JM, Ovchinnikov AV, Roslova MV, Boltalin AI, Morozov IV, Antipov EV, Van Tendeloo G, Chemistry of materials 23, 4311 (2011). http://doi.org/10.1021/cm201203h
Abstract: The Fe-vacancy ordering patterns in the superconducting KxFe2ySe2 and nonsuperconducting Kx(Fe,Co)2ySe2 samples have been investigated by electron diffraction and high angle annular dark field scanning transmission electron microscopy. The Fe-vacancy ordering occurs in the ab plane of the parent ThCr2Si2-type structure, demonstrating two types of patterns. Superstructure I retains the tetragonal symmetry and can be described with the aI = bI = as√5 (as is the unit cell parameter of the parent ThCr2Si2-type structure) supercell and I4/m space group. Superstructure II reduces the symmetry to orthorhombic with the aII = as√2, bII = 2as√2 supercell and the Ibam space group. This type of superstructure is observed for the first time in KxFe2ySe2. The Fe-vacancy ordering is inhomogeneous: the disordered areas interleave with the superstructures I and II in the same crystallite. The observed superstructures represent the compositionally dependent uniform ordering patterns of two species (the Fe atoms and vacancies) on a square lattice. More complex uniform ordered configurations, including compositional stripes, can be predicted for different chemical compositions of the KxFe2ySe2 (0 < y < 0.5) solid solutions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 20
DOI: 10.1021/cm201203h
|
“Rationalizing the influence of the Mn(IV)/Mn(III) red-Ox transition on the electrocatalytic activity of manganese oxides in the oxygen reduction reaction”. Ryabova AS, Napolskiy FS, Poux T, Istomin SY, Bonnefont A, Antipin DM, Baranchikov AY, Levin EE, Abakumov AM, Kéranguéven G, Antipov EV, Tsirlina GA, Savinova ER;, Electrochimica acta 187, 161 (2016). http://doi.org/10.1016/j.electacta.2015.11.012
Abstract: Knowledge on the mechanisms of oxygen reduction reaction (ORR) and descriptors linking the catalytic activity to the structural and electronic properties of transition metal oxides enable rational design of more efficient catalysts. In this work ORR electrocatalysis was studied on a set of single and complex Mn (III) oxides with a rotating disc electrode method and cyclic voltammetry. We discovered an exponential increase of the specific electrocatalytic activity with the potential of the surface Mn(IV)/Mn(III) red-ox couple, suggesting the latter as a new descriptor for the ORR electrocatalysis. The observed dependence is rationalized using a simple mean-field kinetic model considering availability of the Mn( III) centers and adsorbate-adsorbate interactions. We demonstrate an unprecedented activity of Mn2O3, ca. 40 times exceeding that of MnOOH and correlate the catalytic activity of Mn oxides to their crystal structure. (C) 2015 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.798
Times cited: 51
DOI: 10.1016/j.electacta.2015.11.012
|
“Synthesis, structure and magnetic ordering of the mullite-type Bi2Fe4-xCrxO9 solid solutions with a frustrated pentagonal Cairo lattice”. Rozova MG, Grigoriev VV, Bobrikov IA, Filimonov DS, Zakharov KV, Volkova OS, Vasiliev AN, Antipov EV, Tsirlin AA, Abakumov AM, Journal of the Chemical Society : Dalton transactions 45, 1192 (2016). http://doi.org/10.1039/c5dt04296h
Abstract: Highly homogeneous mullite-type solid solutions Bi2Fe4-xCrxO9 (x = 0.5, 1, 1.2) were synthesized using a soft chemistry technique followed by a solid-state reaction in Ar. The crystal structure of Bi2Fe3CrO9 was investigated using X-ray and neutron powder diffraction, transmission electron microscopy and Fe-57 Mossbauer spectroscopy (S.G. Pbam, a = 7.95579(9) angstrom , b = 8.39145(9) angstrom, c = 5.98242(7) angstrom, R-F(X-ray) = 0.022, R-F(neutron) = 0.057). The ab planes in the structure are tessellated with distorted pentagonal loops built up by three tetrahedrally coordinated Fe sites and two octahedrally coordinated Fe/Cr sites, linked together in the ab plane by corner-sharing forming a pentagonal Cairo lattice. Magnetic susceptibility measurements and powder neutron diffraction show that the compounds order antiferromagnetically (AFM) with the Neel temperatures decreasing upon increasing the Cr content from T-N similar to 250 K for x = 0 to T-N similar to 155 K for x = 1.2. The magnetic structure of Bi2Fe3CrO9 at T = 30 K is characterized by a propagation vector k = (1/2,1/2,1/2). The tetrahedrally coordinated Fe cations form singlet pairs within dimers of corner-sharing tetrahedra, but spins on the neighboring dimers are nearly orthogonal. The octahedrally coordinated (Fe, Cr) cations form antiferromagnetic up-up-down-down chains along c, while the spin arrangement in the ab plane is nearly orthogonal between nearest neighbors and collinear between second neighbors. The resulting magnetic structure is remarkably different from the one in pure Bi2Fe4O9 and features several types of spin correlations even on crystallographically equivalent exchange that may be caused by the simultaneous presence of Fe and Cr on the octahedral site.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.029
DOI: 10.1039/c5dt04296h
|
“Study of hydrogen peroxide reactions on manganese oxides as a tool to decode the oxygen reduction reaction mechanism”. Ryabova AS, Bonnefont A, Zagrebin P, Poux T, Sena RP, Hadermann J, Abakumov AM, Kerangueven G, Istomin SY, Antipov EV, Tsirlina GA, Savinova ER, ChemElectroChem 3, 1667 (2016). http://doi.org/10.1002/CELC.201600236
Abstract: Hydrogen peroxide has been detected as a reaction intermediate in the electrochemical oxygen reduction reaction (ORR) on transition-metal oxides and other electrode materials. In this work, we studied the electrocatalytic and catalytic reactions of hydrogen peroxide on a set of Mn oxides, Mn2O3, MnOOH, LaMnO3, MnO2, and Mn3O4, that adopt different crystal structures to shed light on the mechanism of the ORR on these materials. We then combined experiment with kinetic modeling with the objective to correlate the differences in the ORR activity to the kinetics of the elementary reaction steps, and we uncovered the importance of structural and compositional factors in the catalytic activity of the Mn oxides. We concluded that the exceptional activity of Mn2O3 in the ORR is due to its high catalytic activity both in the reduction of oxygen to hydrogen peroxide and in the decomposition of the latter, and furthermore, we proposed a tentative link between crystal structure and reactivity.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.136
Times cited: 20
DOI: 10.1002/CELC.201600236
|
“Crystallographic shear structures as a route to anion-deficient perovskites”. Abakumov AM, Hadermann J, Bals S, Nikolaev IV, Antipov EV, Van Tendeloo G, Angewandte Chemie: international edition in English 45, 6697 (2006). http://doi.org/10.1002/anie.200602480
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 11.994
Times cited: 62
DOI: 10.1002/anie.200602480
|
“Doping of Bi4Fe5O13F with pentagonal Cairo lattice with Cr and Mn: Synthesis, structure and magnetic properties”. Rozova MG, Grigoriev VV, Tyablikov OA, Filimonov DS, Zakharov KV, Volkova OS, Vasiliev AN, Antipov EV, Abakumov AM, Materials research bulletin 87, 54 (2017). http://doi.org/10.1016/J.MATERRESBULL.2016.11.018
Abstract: The substitution of Cr3+ and Mn3+ for Fe3+ in the Bi4Fe6O13F oxyfluoride featuring the magnetically frustrated pentagonal Cairo lattice is reported. Bi4Fe4.1Cr0.9O13F and BiFe4.2Mn0.8O13F have been prepared using a solid state reaction in inert atmosphere. Their crystal structures were studied with transmission electron microscopy, powder X-ray diffraction and Fe-57 Mossbauer spectroscopy (S.G. P4(2)/mbc, a = 8.27836(2)angstrom, c = 18.00330(9) angstrom, R-F = 0.031 (Bi4Fe4.1Cr0.9O13F)), a= 8.29535(3)angstrom, c= 18.0060(1)angstrom, R-F = 0.027 (Bi4Fe4.1Cr0.9O13F)). The structures are formed by infinite rutile-like chains of the edge sharing BO6 octahedra (B transition metal cations) linked by the Fe2O7 groups of two corner-sharing tetrahedra. The"voids in thus formed framework are occupied by the Bi4F tetrahedra. The Fe-57 Mossbauer spectroscopy reveals that Cr3+ and Mn3+ replace Fe3+. exclusively at the octahedral positions. The Mn- and Cr-doped compounds demonstrate antiferromagnetic ordering below T-N =165 K and 120 K, respectively. (C) 2016 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 1
DOI: 10.1016/J.MATERRESBULL.2016.11.018
|
“High-temperature properties of (La,Ca)(Fe,Mg,Mo)O3-\delta perovskites as prospective electrode materials for symmetrical SOFC”. Istomin SY, Morozov AV, Abdullayev MM, Batuk M, Hadermann J, Kazakov SM, Sobolev AV, Presniakov IA, Antipov EV, Journal of solid state chemistry 258, 1 (2018). http://doi.org/10.1016/J.JSSC.2017.10.005
Abstract: La1-yCayFe0.5+x(Mg,Mo)(0.5-x)O3-delta oxides with the orthorhombic GdFeO3-type perovskite structure have been synthesized at 1573 K. Transmission electron microscopy study for selected samples shows the coexistence of domains of perovskite phases with ordered and disordered B-cations. Mossbauer spectroscopy studies performed at 300 K and 573 K show that while compositions with low Ca-content (La0.55Ca0.45Fe0.5Mg0.2625Mo0.2375O3-delta and La0.5Ca0.5Fe0.6Mg0.175Mo0.225O3-delta) are nearly oxygen stoichiometric, La0.2Ca0.8Fe0.5Mg0.2625Mo0.2375O3-delta is oxygen deficient with delta approximate to 0.15. Oxides are stable in reducing atmosphere (Ar/H-2, 8%) at 1173 K for 12 h. No additional phases have been observed at XRPD patterns of all studied perovskites and Ce1-xGdxO2-x/2 electrolyte mixtures treated at 1173-1373K, while Fe-rich compositions (x >= 0.1) react with Zr1-xYxO2-x/2 electrolyte above 1273 K. Dilatometry studies reveal that all samples show rather low thermal expansion coefficients (TECs) in air of 11.4-12.7 ppm K-1. In reducing atmosphere their TECs were found to increase up to 12.1-15.4 ppm K-1 due to chemical expansion effect. High-temperature electrical conductivity measurements in air and Ar/H-2 atmosphere show that the highest conductivity is observed for Fe- and Ca-rich compositions. Moderate values of electrical conductivity and TEC together with stability towards chemical interaction with typical SOFC electrolytes make novel Fe-containing perovskites promising electrode materials for symmetrical solid oxide fuel cell.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 5
DOI: 10.1016/J.JSSC.2017.10.005
|
“Homologous series of layered perovskites An+1BnO3n-1Cl : crystal and magnetic structure of a new oxychloride Pb4BiFe4O11Cl”. Batuk M, Batuk D, Tsirlin AA, Rozova MG, Antipov EV, Hadermann J, Van Tendeloo G, Inorganic chemistry 52, 2208 (2013). http://doi.org/10.1021/ic302667a
Abstract: The nuclear and magnetic structure of a novel oxychloride Pb4BiFe4O11Cl has been studied over the temperature range 1.5700 K using a combination of transmission electron microscopy and synchrotron and neutron powder diffraction [space group P4/mbm, a = 5.5311(1) Å, c = 19.586(1) Å, T = 300 K]. Pb4BiFe4O11Cl is built of truncated (Pb,Bi)3Fe4O11 quadruple perovskite blocks separated by CsCl-type (Pb,Bi)2Cl slabs. The perovskite blocks consist of two layers of FeO6 octahedra located between two layers of FeO5 tetragonal pyramids. The FeO6 octahedra rotate about the c axis, resulting in a √2ap × √2ap × c superstructure. Below TN = 595(17) K, Pb4BiFe4O11Cl adopts a G-type antiferromagnetic structure with the iron magnetic moments confined to the ab plane. The ordered magnetic moments at 1.5 K are 3.93(3) and 3.62(4) μB on the octahedral and square-pyramidal iron sites, respectively. Pb4BiFe4O11Cl can be considered a member of the perovskite-based An+1BnO3n1Cl homologous series (A = Pb/Bi; B = Fe) with n = 4. The formation of a subsequent member of the series with n = 5 is also demonstrated.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 6
DOI: 10.1021/ic302667a
|
“Structural and magnetic phase transitions in the AnBnO3n-2 anion-deficient perovskites Pb2Ba2BiFe5O13 and Pb1.5Ba2.5Bi2Fe6O16”. Abakumov AM, Batuk M, Tsirlin AA, Tyablikov OA, Sheptyakov DV, Filimonov DS, Pokholok KV, Zhidal VS, Rozova MG, Antipov EV, Hadermann J, Van Tendeloo G;, Inorganic chemistry 52, 7834 (2013). http://doi.org/10.1021/ic3026667
Abstract: Novel anion-deficient perovskite-based ferrites Pb2Ba2BiFe5O13 and Pb1.5Ba2.5Bi2Fe6O16 were synthesized by solid-state reaction in air. Pb2Ba2BiFe5O13 and Pb1.5Ba2.5Bi2Fe6O16 belong to the perovskite-based AnBnO3n2 homologous series with n = 5 and 6, respectively, with a unit cell related to the perovskite subcell ap as ap√2 × ap × nap√2. Their structures are derived from the perovskite one by slicing it with 1/2[110]p(1̅01)p crystallographic shear (CS) planes. The CS operation results in (1̅01)p-shaped perovskite blocks with a thickness of (n 2) FeO6 octahedra connected to each other through double chains of edge-sharing FeO5 distorted tetragonal pyramids which can adopt two distinct mirror-related configurations. Ordering of chains with a different configuration provides an extra level of structure complexity. Above T ≈ 750 K for Pb2Ba2BiFe5O13 and T ≈ 400 K for Pb1.5Ba2.5Bi2Fe6O16 the chains have a disordered arrangement. On cooling, a second-order structural phase transition to the ordered state occurs in both compounds. Symmetry changes upon phase transition are analyzed using a combination of superspace crystallography and group theory approach. Correlations between the chain ordering pattern and octahedral tilting in the perovskite blocks are discussed. Pb2Ba2BiFe5O13 and Pb1.5Ba2.5Bi2Fe6O16 undergo a transition into an antiferromagnetically (AFM) ordered state, which is characterized by a G-type AFM ordering of the Fe magnetic moments within the perovskite blocks. The AFM perovskite blocks are stacked along the CS planes producing alternating FM and AFM-aligned FeFe pairs. In spite of the apparent frustration of the magnetic coupling between the perovskite blocks, all n = 4, 5, 6 AnFenO3n2 (A = Pb, Bi, Ba) feature robust antiferromagnetism with similar Néel temperatures of 623632 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 10
DOI: 10.1021/ic3026667
|
“Slicing the Perovskite structure with crystallographic shear planes : the AnBnO3n-2 homologous series”. Abakumov AM, Hadermann J, Batuk M, d' Hondt H, Tyablikov OA, Rozova MG, Pokholok KV, Filimonov DS, Sheptyakov DV, Tsirlin AA, Niermann D, Hemberger J, Van Tendeloo G, Antipov EV, Inorganic chemistry 49, 9508 (2010). http://doi.org/10.1021/ic101233s
Abstract: A new AnBnO3n−2 homologous series of anion-deficient perovskites has been evidenced by preparation of the members with n = 5 (Pb2.9Ba2.1Fe4TiO13) and n = 6 (Pb3.8Bi0.2Ba2Fe4.2Ti1.8O16) in a single phase form. The crystal structures of these compounds were determined using a combination of transmission electron microscopy and X-ray and neutron powder diffraction (S.G. Ammm, a = 5.74313(7), b = 3.98402(4), c = 26.8378(4) Å, RI = 0.035, RP = 0.042 for Pb2.9Ba2.1Fe4TiO13 and S.G. Imma, a = 5.7199(1), b = 3.97066(7), c = 32.5245(8) Å, RI = 0.032, RP = 0.037 for Pb3.8Bi0.2Ba2Fe4.2Ti1.8O16). The crystal structures of the AnBnO3n−2 homologues are formed by slicing the perovskite structure with (01)p crystallographic shear (CS) planes. The shear planes remove a layer of oxygen atoms and displace the perovskite blocks with respect to each other by the 1/2[110]p vector. The CS planes introduce edge-sharing connections of the transition metal−oxygen polyhedra at the interface between the perovskite blocks. This results in intrinsically frustrated magnetic couplings between the perovskite blocks due to a competition of the exchange interactions between the edge- and the corner-sharing metal−oxygen polyhedra. Despite the magnetic frustration, neutron powder diffraction and Mssbauer spectroscopy reveal that Pb2.9Ba2.1Fe4TiO13 and Pb3.8Bi0.2Ba2Fe4.2Ti1.8O16 are antiferromagnetically ordered below TN = 407 and 343 K, respectively. The Pb2.9Ba2.1Fe4TiO13 and Pb3.8Bi0.2Ba2Fe4.2Ti1.8O16 compounds are in a paraelectric state in the 5−300 K temperature range.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 23
DOI: 10.1021/ic101233s
|
“Solving the structure of Li ion battery materials with precession electron diffraction : application to Li2CoPo4F”. Hadermann J, Abakumov AM, Turner S, Hafideddine Z, Khasanova NR, Antipov EV, Van Tendeloo G, Chemistry of materials 23, 3540 (2011). http://doi.org/10.1021/cm201257b
Abstract: The crystal structure of the Li2CoPO4F high-voltage cathode for Li ion rechargeable batteries has been completely solved from precession electron diffraction (PED) data, including the location of the Li atoms. The crystal structure consists of infinite chains of CoO4F2 octahedra sharing common edges and linked into a 3D framework by PO4 tetrahedra. The chains and phosphate anions together delimit tunnels filled with the Li atoms. This investigation demonstrates that PED can be successfully applied for obtaining structural information on a variety of Li-containing electrode materials even from single micrometer-sized crystallites.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 46
DOI: 10.1021/cm201257b
|