“Deciphering the role of water in promoting the optoelectronic performance of surface-engineered lead halide perovskite nanocrystals”. Bhatia H, Martin C, Keshavarz M, Dovgaliuk I, Schrenker NJ, Ottesen M, Qiu W, Fron E, Bremholm M, Van de Vondel J, Bals S, Roeffaers MBJ, Hofkens J, Debroye E, ACS applied materials and interfaces 15, 7294 (2023). http://doi.org/10.1021/ACSAMI.2C20605
Abstract: Lead halide perovskites are promising candidates for applicability is limited by their structural instability toward moisture. Although a deliberate addition of water to the precursor solution has recently been shown to improve the crystallinity and optical properties of perovskites, the corresponding thin films still do not exhibit a near-unity quantum yield. Herein, we report that the direct addition of a minute amount of water to post-treated substantially enhances the stability while achieving a 95% photoluminescence quantum yield in a NC thin film. We unveil the mechanism of how moisture assists in the formation of an additional NH4Br component. Alongside, we demonstrate the crucial role of moisture in assisting localized etching of the perovskite crystal, facilitating the partial incorporation of NH4+, which is key for improved performance under ambient conditions. Finally, as a proof-of-concept, the application of post-treated and watertreated perovskites is tested in LEDs, with the latter exhibiting a superior performance, offering opportunities toward commercial application in moisture-stable optoelectronics.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 9.5
Times cited: 3
DOI: 10.1021/ACSAMI.2C20605
|
|
“Plasmonic gold-embedded TiO2 thin films as photocatalytic self-cleaning coatings”. Peeters H, Keulemans M, Nuyts G, Vanmeert F, Li C, Minjauw M, Detavernier C, Bals S, Lenaerts S, Verbruggen SW, Applied Catalysis B-Environmental 267, 118654 (2020). http://doi.org/10.1016/j.apcatb.2020.118654
Abstract: Transparent photocatalytic TiO2 thin films hold great potential in the development of self-cleaning glass sur-
faces, but suffer from a poor visible light response that hinders the application under actual sunlight. To alleviate this problem, the photocatalytic film can be modified with plasmonic nanoparticles that interact very effectively with visible light. Since the plasmonic effect is strongly concentrated in the near surroundings of the nano- particle surface, an approach is presented to embed the plasmonic nanostructures in the TiO2 matrix itself, rather than deposit them loosely on the surface. This way the interaction interface is maximised and the plasmonic effect can be fully exploited. In this study, pre-fabricated gold nanoparticles are made compatible with the organic medium of a TiO2 sol-gel coating suspension, resulting in a one-pot coating suspension. After spin coating, homogeneous, smooth, highly transparent and photoactive gold-embedded anatase thin films are ob- tained.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation); Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 22.1
Times cited: 57
DOI: 10.1016/j.apcatb.2020.118654
|
|
“3D characterization of heat-induced morphological changes of Au nanostars by fast in situ electron tomography”. Vanrompay H, Bladt E, Albrecht W, Béché, A, Zakhozheva M, Sánchez-Iglesias A, Liz-Marzán LM, Bals S, Nanoscale 10, 22792 (2018). http://doi.org/10.1039/C8NR08376B
Abstract: A thorough understanding of the thermal stability and potential reshaping of anisotropic gold nanostars is required for various potential applications. Combination of a tomographic heating holder with fast tilt series acquisition has been used to monitor temperature-induced morphological changes of Au nanostars. The outcome of our 3D investigations can be used as an input for boundary element method simulations, enabling us to investigate the influence of reshaping on the nanostars’ plasmonic properties. Our work leads to a better understanding of the mechanism behind thermal reshaping. In addition, the approach presented here is generic and can hence be applied to a wide variety of nanoparticles made of different materials and with arbitrary morphology.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 55
DOI: 10.1039/C8NR08376B
|
|
“Experimental Evaluation of Undersampling Schemes for Electron Tomography of Nanoparticles”. Vanrompay H, Béché, A, Verbeeck J, Bals S, Particle and particle systems characterization 36, 1900096 (2019). http://doi.org/10.1002/ppsc.201900096
Abstract: One of the emerging challenges in the field of 3D characterization of nanoparticles by electron tomography is to avoid degradation and deformation of the samples during the acquisition of a tilt series. In order to reduce the required electron dose, various undersampling approaches have been proposed. These methods include lowering the number of 2D projection images, reducing the probe current during the acquisition, and scanning a smaller number of pixels in the 2D images. A comparison is made between these approaches based on tilt series acquired for a gold nanoparticle.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.474
Times cited: 12
DOI: 10.1002/ppsc.201900096
|
|
“Real-time tilt undersampling optimization during electron tomography of beam sensitive samples using golden ratio scanning and RECAST3D”. Craig TM, Kadu AA, Batenburg KJ, Bals S, Nanoscale 15, 5391 (2023). http://doi.org/10.1039/D2NR07198C
Abstract: Electron tomography is a widely used technique for 3D structural analysis of nanomaterials, but it can cause damage to samples due to high electron doses and long exposure times. To minimize such damage, researchers often reduce beam exposure by acquiring fewer projections through tilt undersampling. However, this approach can also introduce reconstruction artifacts due to insufficient sampling. Therefore, it is important to determine the optimal number of projections that minimizes both beam exposure and undersampling artifacts for accurate reconstructions of beam-sensitive samples. Current methods for determining this optimal number of projections involve acquiring and post-processing multiple reconstructions with different numbers of projections, which can be time-consuming and requires multiple samples due to sample damage. To improve this process, we propose a protocol that combines golden ratio scanning and quasi-3D reconstruction to estimate the optimal number of projections in real-time during a single acquisition. This protocol was validated using simulated and realistic nanoparticles, and was successfully applied to reconstruct two beam-sensitive metal–organic framework complexes.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 6.7
Times cited: 1
DOI: 10.1039/D2NR07198C
|
|
“Study of the Mechanism and Increasing Crystallinity in the Self-Templated Growth of Ultrathin PbS Nanosheets”. van der Sluijs MM, Salzmann BBV, Arenas Esteban D, Li C, Jannis D, Brafine LC, Laning TD, Reinders JWC, Hijmans NSA, Moes JR, Verbeeck J, Bals S, Vanmaekelbergh D, Chemistry of materials (2023). http://doi.org/10.1021/acs.chemmater.3c00300
Abstract: Colloidal 2D semiconductor nanocrystals, the analogue of solid-state quantum wells, have attracted strong interest in material science and physics. Molar quantities of suspended quantum objects with spectrally pure absorption and emission can be synthesized. For the visible region, CdSe nanoplatelets with atomically precise thickness and tailorable emission have been (almost) perfected. For the near-infrared region, PbS nanosheets (NSs) hold strong promise, but the photoluminescence quantum yield is low and many questions on the crystallinity, atomic structure, intriguing rectangular shape, and formation mechanism remain to be answered. Here, we report on a detailed investigation of the PbS NSs prepared with a lead thiocyanate single source precursor. Atomically resolved HAADF-STEM imaging reveals the presence of defects and small cubic domains in the deformed orthorhombic PbS crystal lattice. Moreover, variations in thickness are observed in the NSs, but only in steps of 2 PbS monolayers. To study the reaction mechanism, a synthesis at a lower temperature allowed for the study of reaction intermediates. Specifically, we studied the evolution of pseudo-crystalline templates towards mature, crystalline PbS NSs. We propose a self-induced templating mechanism based on an oleylamine-lead-thiocyanate (OLAM-Pb-SCN) complex with two Pb-SCN units as a building block; the interactions between the long-chain ligands regulate the crystal structure and possibly the lateral dimensions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.6
Times cited: 2
DOI: 10.1021/acs.chemmater.3c00300
|
|
“Fast Electron Tomography for Nanomaterials”. Albrecht W, Bals S, Journal Of Physical Chemistry C , acs.jpcc.0c08939 (2020). http://doi.org/10.1021/acs.jpcc.0c08939
Abstract: Electron tomography (ET) has become a well-established technique to visualize nanomaterials in three dimensions. A vast richness in information can be gained by ET, but the conventional acquisition of a tomography series is an inherently slow process on the order of 1 h. The slow acquisition limits the applicability of ET for monitoring dynamic processes or visualizing nanoparticles, which are sensitive to the electron beam. In this Perspective, we summarize recent work on the development of emerging experimental and computational schemes to enhance the data acquisition process. We particularly focus on the application of these fast ET techniques for beam-sensitive materials and highlight insight into dynamic transformations of nanoparticles under external stimuli, which could be gained by fast in situ ET. Moreover, we discuss challenges and possible solutions for simultaneously increasing the speed and quality of fast ET.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.7
Times cited: 26
DOI: 10.1021/acs.jpcc.0c08939
|
|
“Effectiveness of reducing the influence of CTAB at the surface of metal nanoparticles during in situ heating studies by TEM”. De Meyer R, Albrecht W, Bals S, Micron 144, 103036 (2021). http://doi.org/10.1016/j.micron.2021.103036
Abstract: In situ TEM is a valuable technique to offer novel insights in the behavior of nanomaterials under various conditions. However, interpretation of in situ experiments is not straightforward since the electron beam can impact the outcome of such measurements. For example, ligands surrounding metal nanoparticles transform into a protective carbon layer upon electron beam irradiation and may impact the apparent thermal stability during in situ heating experiments. In this work, we explore the effect of different treatments typically proposed to remove such ligands. We found that plasma treatment prior to heating experiments for Au nanorods and nanostars increased the apparent thermal stability of the nanoparticles, while an activated carbon treatment resulted in a decrease of the observed thermal stability. Treatment with HCl barely changed the experimental outcome. These results demonstrate the importance of carefully selecting pre-treatments procedures during in situ heating experiments.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.98
DOI: 10.1016/j.micron.2021.103036
|
|
“From CdSe nanoplatelets to quantum rings by thermochemical edge reconfiguration”. Salzmann BBV, Vliem JF, Maaskant DN, Post LC, Li C, Bals S, Vanmaekelbergh D, Chemistry Of Materials 33, 6853 (2021). http://doi.org/10.1021/ACS.CHEMMATER.1C01618
Abstract: The variation in the shape of colloidal semiconductor nanocrystals (NCs) remains intriguing. This interest goes beyond crystallography as the shape of the NC determines its energy levels and optoelectronic properties. While thermodynamic arguments point to a few or just a single shape(s), terminated by the most stable crystal facets, a remarkable variation in NC shape has been reported for many different compounds. For instance, for the well-studied case of CdSe, close-to-spherical quantum dots, rods, two-dimensional nanoplatelets, and quantum rings have been reported. Here, we report how two-dimensional CdSe nanoplatelets reshape into quantum rings. We monitor the reshaping in real time by combining atomically resolved structural characterization with optical absorption and photoluminescence spectroscopy. We observe that CdSe units leave the vertical sides of the edges and recrystallize on the top and bottom edges of the nanoplatelets, resulting in a thickening of the rims. The formation of a central hole, rendering the shape into a ring, only occurs at a more elevated temperature.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 7
DOI: 10.1021/ACS.CHEMMATER.1C01618
|
|
“Achieving High Moisture Tolerance in Pseudohalide Perovskite Nanocrystals for Light-Emitting Diode Application”. Bhatia H, Keshavarz M, Martin C, Van Gaal L, Zhang Y, de Coen B, Schrenker NJ, Valli D, Ottesen M, Bremholm M, Van de Vondel J, Bals S, Hofkens J, Debroye E, ACS Applied Optical Materials 1, 1184 (2023). http://doi.org/10.1021/acsaom.3c00096
Abstract: The addition of potassium thiocyanate (KSCN) to the FAPbBr3 structure and subsequent post-treatment of nanocrystals (NCs) lead to high quantum confinement, resulting in a photoluminescent quantum yield (PLQY) approaching unity and microsecond decay times. This synergistic approach demonstrated exceptional stability under humid conditions, retaining 70% of the PLQY for over a month, while the untreated NCs degrade within 24 h. Additionally, the devices incorporating the post-treated NCs displayed 1.5% external quantum efficiency (EQE), a 5-fold improvement over untreated devices. These results provide promising opportunities for the use of perovskites in moisture-stable optoelectronics.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
DOI: 10.1021/acsaom.3c00096
|
|
“Linearized radially polarized light for improved precision in strain measurements using micro-Raman spectroscopy”. Prabhakara V, Nuytten T, Bender H, Vandervorst W, Bals S, Verbeeck J, Optics Express 29, 34531 (2021). http://doi.org/10.1364/OE.434726
Abstract: Strain engineering in semiconductor transistor devices has become vital in the semiconductor industry due to the ever-increasing need for performance enhancement at the nanoscale. Raman spectroscopy is a non-invasive measurement technique with high sensitivity to mechanical stress that does not require any special sample preparation procedures in comparison to characterization involving transmission electron microscopy (TEM), making it suitable for inline strain measurement in the semiconductor industry. Indeed, at present, strain measurements using Raman spectroscopy are already routinely carried out in semiconductor devices as it is cost effective, fast and non-destructive. In this paper we explore the usage of linearized radially polarized light as an excitation source, which does provide significantly enhanced accuracy and precision as compared to linearly polarized light for this application. Numerical simulations are done to quantitatively evaluate the electric field intensities that contribute to this enhanced sensitivity. We benchmark the experimental results against TEM diffraction-based techniques like nano-beam diffraction and Bessel diffraction. Differences between both approaches are assigned to strain relaxation due to sample thinning required in TEM setups, demonstrating the benefit of Raman for nondestructive inline testing.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.307
Times cited: 2
DOI: 10.1364/OE.434726
|
|
“3D arrangement of epitaxial graphene conformally grown on porousified crystalline SiC”. Veronesi S, Pfusterschmied G, Fabbri F, Leitgeb M, Arif O, Esteban DA, Bals S, Schmid U, Heun S, Carbon 189, 210 (2022). http://doi.org/10.1016/j.carbon.2021.12.042
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 10.9
Times cited: 3
DOI: 10.1016/j.carbon.2021.12.042
|
|
“Multimodal imaging of micron-sized iron oxide particles following in vitro and in vivo uptake by stem cells: down to the nanometer scale”. Roose D, Leroux F, De Vocht N, Guglielmetti C, Pintelon I, Adriaensen D, Ponsaerts P, Van der Linden A, Bals S, Contrast Media &, Molecular Imaging 9, 400 (2014). http://doi.org/10.1002/cmmi.1594
Abstract: In this study, the interaction between cells and micron-sized paramagnetic iron oxide (MPIO) particles was investigated by characterizing MPIO in their original state, and after cellular uptake in vitro as well as in vivo. Moreover, MPIO in the olfactory bulb were studied 9 months after injection. Using various imaging techniques, cell-MPIO interactions were investigated with increasing spatial resolution. Live cell confocal microscopy demonstrated that MPIO co-localize with lysosomes after in vitro cellular uptake. In more detail, a membrane surrounding the MPIO was observed by high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM). Following MPIO uptake in vivo, the same cell-MPIO interaction was observed by HAADF-STEM in the subventricular zone at 1 week and in the olfactory bulb at 9 months after MPIO injection. These findings provide proof for the current hypothesis that MPIO are internalized by the cell through endocytosis. The results also show MPIO are not biodegradable, even after 9 months in the brain. Moreover, they show the possibility of HAADF-STEM generating information on the labeled cell as well as on the MPIO. In summary, the methodology presented here provides a systematic route to investigate the interaction between cells and nanoparticles from the micrometer level down to the nanometer level and beyond.
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
Impact Factor: 3.307
Times cited: 8
DOI: 10.1002/cmmi.1594
|
|
“Wet-STEM tomography : principles, potentialities and limitations”. Masenelli-Varlot K, Malchere A, Ferreira J, Heidari Mezerji H, Bals S, Messaoudi C, Garrido SM, Microscopy and microanalysis 20, 366 (2014). http://doi.org/10.1017/S1431927614000105
Abstract: The characterization of biological and inorganic materials by determining their three-dimensional structure in conditions closer to their native state is a major challenge of technological research. Environmental scanning electron microscopy (ESEM) provides access to the observation of hydrated samples in water environments. Here, we present a specific device for ESEM in the scanning transmission electron microscopy mode, allowing the acquisition of tilt-series suitable for tomographic reconstructions. The resolution which can be obtained with this device is first determined. Then, we demonstrate the feasibility of tomography on wet materials. The example studied here is hydrophilic mesoporous silica (MCM-41). Finally, the minimum thickness of water which can be detected is calculated from Monte Carlo simulations and compared with the resolution expected in the tomograms.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 9
DOI: 10.1017/S1431927614000105
|
|
“Enhanced self-assembly of metal oxides and metal-organic frameworks from precursors with magnetohydrodynamically induced long-lived collective spin states”. Breynaert E, Emmerich J, Mustafa D, Bajpe SR, Altantzis T, Van Havenbergh K, Taulelle F, Bals S, Van Tendeloo G, Kirschhock CEA, Martens JA;, Advanced materials 26, 5173 (2014). http://doi.org/10.1002/adma.201400835
Abstract: Magneto-hydrodynamic generation of long-lived collective spin states and their impact on crystal morphology is demonstrated for three different, technologically relevant materials: COK-16 metal organic framework, manganese oxide nanotubes, and vanadium oxide nano-scrolls.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 19.791
Times cited: 7
DOI: 10.1002/adma.201400835
|
|
“Structural characterization of Er-doped Li2O-Al2O3-SiO2 glass ceramics”. Krsmanovic R, Bals S, Bertoni G, Van Tendeloo G, Optical materials 30, 1183 (2008). http://doi.org/10.1016/j.optmat.2007.05.045
Abstract: Particularly favourable properties of glass ceramics are developed on the basis of two key advantages of these materials: the variation of chemical composition and of microstructure. Therefore, detailed structural and chemical information are necessary to get insight in novel glass ceramic materials. We present here two examples of Er-doped Li2O-Al2O3-SiO2, with different quantities of ZrO2, both obtained with sol-gel synthesis. Different transmission electron microscopy techniques: conventional TEM, HRTEM, and EELS are used and the results are compared with those previously obtained with XRD and Rietveld analysis. We also demonstrate the 3D reconstruction, obtained from HAADF-STEM imaging, to determine the morphology of nanosize precipitates in these composites. (c) 2007 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.238
Times cited: 12
DOI: 10.1016/j.optmat.2007.05.045
|
|
“The remarkable and intriguing resistance to oxidation of 2D ordered hcp Co nanocrystals: a new intrinsic property”. Lisiecki I, Turner S, Bals S, Pileni MP, Van Tendeloo G, Chemistry of materials 21, 2335 (2009). http://doi.org/10.1021/cm900284u
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 28
DOI: 10.1021/cm900284u
|
|
“Atomic scale investigation of a PbTiO3/SrRuO3/DyScO3 heterostructure”. Egoavil R, Tan H, Verbeeck J, Bals S, Smith B, Kuiper B, Rijnders G, Koster G, Van Tendeloo G, Applied physics letters 102, 223106 (2013). http://doi.org/10.1063/1.4809597
Abstract: An epitaxial PbTiO3 thin film grown on self-organized crystalline SrRuO3 nanowires deposited on a DyScO3 substrate with ordered DyO and ScO2 chemical terminations is investigated by transmission electron microscopy. In this PbTiO3/SrRuO3/DyScO3 heterostructure, the SrRuO3 nanowires are assumed to grow on only one type of substrate termination. Here, we report on the structure, morphology, and chemical composition analysis of this heterostructure. Electron energy loss spectroscopy reveals the exact termination sequence in this complex structure. The energy loss near-edge structure of the Ti-L-2,L-3, Sc-L-2,L-3, and O K edges shows intrinsic interfacial electronic reconstruction. Furthermore, PbTiO3 domain walls are observed to start at the end of the nanowires resulting in atomic steps on the film surface. (C) 2013 AIP Publishing LLC.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 12
DOI: 10.1063/1.4809597
|
|
“Transmission electron microscopy on interface engineered superconducting thin films”. Bals S, Van Tendeloo G, Rijnders G, Huijben M, Leca V, Blank DHA, IEEE transactions on applied superconductivity 13, 2834 (2003). http://doi.org/10.1109/TASC.2003.812023
Abstract: Transmission electron microscopy is used to evaluate different deposition techniques, which optimize the microstructure and physical properties of superconducting thin films. High-resolution electron microscopy proves that the use of an YBa2Cu2Ox buffer layer can avoid a variable interface configuration in YBa2Cu3O7-delta thin films grown on SrTiO3. The growth can also be controlled at an atomic level by, using sub-unit cell layer epitaxy, which results in films with high quality and few structural defects. Epitaxial strain in Sr0.85La0.15CuO2 infinite layer thin films influences the critical temperature of these films, as well as the microstructure. Compressive stress is released by a modulated or a twinned microstructure, which eliminates superconductivity. On the other hand, also tensile strain seems to lower the critical temperature of the infinite layer.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 13
DOI: 10.1109/TASC.2003.812023
|
|
“Self-Assembly of Pluronic F127—Silica Spherical Core–Shell Nanoparticles in Cubic Close-Packed Structures”. Kerkhofs S, Willhammar T, Van Den Noortgate H, Kirschhock CEA, Breynaert E, Van Tendeloo G, Bals S, Martens JA, Chemistry of materials 27, 5161 (2015). http://doi.org/10.1021/acs.chemmater.5b01772
Abstract: A new ordered mesoporous silica material (COK-19) with cubic symmetry is synthesized by silicate polycondensation in a citric acid/citrate buffered micellar solution of Pluronic F127 triblock copolymer near neutral pH. SAXS, nitrogen adsorption, TEM, and electron tomography reveal the final material has a cubic close packed symmetry (Fm3̅m) with isolated spherical mesopores interconnected through micropores. Heating of the synthesis medium from room temperature to 70 °C results in a mesopore size increase from 7.0 to 11.2 nm. Stepwise addition of the silicate source allows isolation of a sequence of intermediates that upon characterization with small-angle X-ray scattering uncovers the formation process via formation and aggregation of individual silica-covered Pluronic micelles.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 39
DOI: 10.1021/acs.chemmater.5b01772
|
|
“Tuning the Growth of Chiral Gold Nanoparticles Through Rational Design of a Chiral Molecular Inducer”. Van Gordon K, Baúlde S, Mychinko M, Heyvaert W, Obelleiro-Liz M, Criado A, Bals S, Liz-Marzán LM, Mosquera J, Nano Letters (2023). http://doi.org/10.1021/acs.nanolett.3c02800
Abstract: The bottom-up production of chiral gold nanomaterials holds great potential for the advancement of biosensing and nano-optics, among other applications. Reproducible preparations of colloidal nanomaterials with chiral morphology have been reported, using cosurfactants or chiral inducers such as thiolated amino acids. However, the underlying growth mechanisms for these nanomaterials remain insufficiently understood. We introduce herein a purposely devised chiral inducer, a cysteine modified with a hydrophobic chain, as a versatile chiral inducer. The amphiphilic and chiral features of this molecule provide control over the chiral morphology and the chiroptical signature of the obtained nanoparticles by simply varying the concentration of chiral inducer. These results are supported by circular dichroism and electromagnetic modeling as well as electron tomography to analyze structural evolution at the facet scale. Our observations suggest complex roles for the factors involved in chiral synthesis: the chemical nature of the chiral inducers and the influence of cosurfactants.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 10.8
DOI: 10.1021/acs.nanolett.3c02800
|
|
“Electrodeposition of Highly Porous Pt Nanoparticles Studied by Quantitative 3D Electron Tomography: Influence of Growth Mechanisms and Potential Cycling on the Active Surface Area”. Ustarroz J, Geboes B, Vanrompay H, Sentosun K, Bals S, Breugelmans T, Hubin A, ACS applied materials and interfaces 9, 16168 (2017). http://doi.org/10.1021/acsami.7b01619
Abstract: Nanoporous Pt nanoparticles (NPs) are promising fuel cell catalysts due to their large surface area and increased electrocatalytic activity towards the oxygen reduction reaction (ORR). Herein, we report on the infuence of the growth mechanisms on the surface properties of electrodeposited Pt dendritic NPs with large surface areas. The electrochemically active surface was studied by hydrogen underpotential deposition (HUPD) and compared for the rst time to high angle annular dark eld scanning transmission electron microscopy (HAADF-STEM) quantitative 3D electron tomography of individual nanoparticles. Large nucleation overpotential leads to a large surface coverage of Pt roughened spheroids, which provide large roughness factor (Rf ) but low mass-specic electrochemically active surface area (EASA). Lowering the nucleation overpotential leads to highly porous Pt NPs with pores protruding to the center of the structure. At the expense of smaller Rf , the obtained EASA values of these structures are in the range of these of large surface area supported fuel cell catalysts. The active surface area of the Pt dendritic NPs was measured by electron tomography and it was found that the potential cycling in the H adsorption/desorption and Pt oxidation/reduction region, which is generally performed to determine the EASA, leads to a signicant reduction of that surface area due to a partial collapse of their dendritic and porous morphology. Interestingly, the extrapolation of the microscopic tomography results to macroscopic electrochemical parameters indicated that the surface properties measured by H UPD are comparable to the values measured on individual NPs by electron tomography after the degradation caused by the H UPD measurement. These results highlight that the combination of electrochemical and quantitative 3D surface analysis techniques is essential to provide insights into the surface properties, the electrochemical stability and, hence, the applicability of these materials. Moreover, it indicates that care must be taken with widely used electrochemical methods of surface area determination, especially in the case of large surface area and possibly unstable nanostructures, since the measured surface can be strongly aected by the measurement itself.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 7.504
Times cited: 24
DOI: 10.1021/acsami.7b01619
|
|
“Artifact Reduction Based on Sinogram Interpolation for the 3D Reconstruction of Nanoparticles Using Electron Tomography”. Sentosun K, Lobato I, Bladt E, Zhang Y, Palenstijn WJ, Batenburg KJ, Van Dyck D, Bals S, Particle and particle systems characterization 34, 1700287 (2017). http://doi.org/10.1002/ppsc.201700287
Abstract: Electron tomography is a well-known technique providing a 3D characterization of the morphology and chemical composition of nanoparticles. However, several reasons hamper the acquisition of tilt series with a large number of projection images, which deteriorate the quality of the 3D reconstruction. Here, an inpainting method that is based on sinogram interpolation is proposed, which enables one to reduce artifacts in the reconstruction related to a limited tilt series of projection images. The advantages of the approach will be demonstrated for the 3D characterization of nanoparticles using phantoms and several case studies.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Vision lab
Times cited: 2
DOI: 10.1002/ppsc.201700287
|
|
“In Situ Plasma Studies Using a Direct Current Microplasma in a Scanning Electron Microscope”. Grünewald L, Chezganov D, De Meyer R, Orekhov A, Van Aert S, Bogaerts A, Bals S, Verbeeck J, Advanced Materials Technologies (2024). http://doi.org/10.1002/admt.202301632
Abstract: Microplasmas can be used for a wide range of technological applications and to improve the understanding of fundamental physics. Scanning electron microscopy, on the other hand, provides insights into the sample morphology and chemistry of materials from the mm‐ down to the nm‐scale. Combining both would provide direct insight into plasma‐sample interactions in real‐time and at high spatial resolution. Up till now, very few attempts in this direction have been made, and significant challenges remain. This work presents a stable direct current glow discharge microplasma setup built inside a scanning electron microscope. The experimental setup is capable of real‐time in situ imaging of the sample evolution during plasma operation and it demonstrates localized sputtering and sample oxidation. Further, the experimental parameters such as varying gas mixtures, electrode polarity, and field strength are explored and experimental<italic>V</italic>–<italic>I</italic>curves under various conditions are provided. These results demonstrate the capabilities of this setup in potential investigations of plasma physics, plasma‐surface interactions, and materials science and its practical applications. The presented setup shows the potential to have several technological applications, for example, to locally modify the sample surface (e.g., local oxidation and ion implantation for nanotechnology applications) on the µm‐scale.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 6.8
DOI: 10.1002/admt.202301632
|
|
“An Expanded Surface-Enhanced Raman Scattering Tags Library by Combinatorial Encapsulation of Reporter Molecules in Metal Nanoshells”. Rodal-Cedeira S, Vázquez-Arias A, Bodelon G, Skorikov A, Núñez-Sanchez S, La Porta A, Polavarapu L, Bals S, Liz-Marzán LM, Perez-Juste J, Pastoriza-Santos I, Acs Nano (2020). http://doi.org/10.1021/acsnano.0c04368
Abstract: Raman-encoded gold nanoparticles have been widely employed as photostable multifunctional probes for sensing, bioimaging, multiplex diagnostics, and surface-enhanced Raman scattering (SERS)-guided tumor therapy. We report a strategy toward obtaining a particularly large library of Au nanocapsules encoded with Raman codes defined by the combination of different thiol-free Raman reporters, encapsulated at defined molar ratios. The fabrication of SERS tags with tailored size and pre-defined codes is based on the in situ incorporation of Raman reporter molecules inside Au nanocapsules during their formation via Galvanic replacement coupled to seeded growth on Ag NPs. The hole-free closed shell structure of the nanocapsules is confirmed by electron tomography. The unusually wide encoding possibilities of the obtained SERS tags are investigated by means of either wavenumber-based encoding or Raman frequency combined with signal intensity, leading to an outstanding performance as exemplified by 26 and 54 different codes, respectively. We additionally demonstrate that encoded nanocapsules can be readily bioconjugated with antibodies for applications such as SERS-based targeted cell imaging and phenotyping.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 17.1
Times cited: 14
DOI: 10.1021/acsnano.0c04368
|
|
“Micelle-directed chiral seeded growth on anisotropic gold nanocrystals”. González-Rubio G, Mosquera J, Kumar V, Pedrazo-Tardajos A, Llombart P, Solís DM, Lobato I, Noya EG, Guerrero-Martínez A, Taboada JM, Obelleiro F, MacDowell LG, Bals S, Liz-Marzán LM, Science 368, 1472 (2020). http://doi.org/10.1126/science.aba0980
Abstract: Surfactant-assisted seeded growth of metal nanoparticles (NPs) can be engineered to produce anisotropic gold nanocrystals with high chiroptical activity through the templating effect of chiral micelles formed in the presence of dissymmetric cosurfactants. Mixed micelles adsorb on gold nanorods, forming quasihelical patterns that direct seeded growth into NPs with pronounced morphological and optical handedness. Sharp chiral wrinkles lead to chiral plasmon modes with high dissymmetry factors (~0.20). Through variation of the dimensions of chiral wrinkles, the chiroptical properties can be tuned within the visible and near-infrared electromagnetic spectrum. The micelle-directed mechanism allows extension to other systems, such as the seeded growth of chiral platinum shells on gold nanorods. This approach provides a reproducible, simple, and scalable method toward the fabrication of NPs with high chiral optical activity.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 56.9
Times cited: 187
DOI: 10.1126/science.aba0980
|
|
“Controlled Living Nanowire Growth: Precise Control over the Morphology and Optical Properties of AgAuAg Bimetallic Nanowires”. Mayer M, Scarabelli L, March K, Altantzis T, Tebbe M, Kociak M, Bals S, Garcia de Abajo FJ, Fery A, Liz-Marzan LM, Nano letters 15, 5427 (2015). http://doi.org/10.1021/acs.nanolett.5b01833
Abstract: Inspired by the concept of living polymerization reaction, we are able to produce silver-gold-silver nanowires with a precise control over their total length and plasmonic properties by establishing a constant silver deposition rate on the tips of penta-twinned gold nanorods used as seed cores. Consequently, the length of the wires increases linearly in time. Starting with approximately 210 nm x 32 nm gold cores, we produce nanowire lengths up to several microns in a highly controlled manner, with a small self-limited increase in thickness of approximately 4 nm, corresponding to aspect ratios above 100, whereas the low polydispersity of the product allows us to detect up to nine distinguishable plasmonic resonances in a single colloidal solution. We analyze the spatial distribution and the nature of the plasmons by electron energy loss spectroscopy and obtain excellent agreement between measurements and electromagnetic simulations, clearly demonstrating that the presence of the gold core plays a marginal role, except for relatively short wires or high-energy modes.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 117
DOI: 10.1021/acs.nanolett.5b01833
|
|
“Reversible Clustering of Gold Nanoparticles under Confinement”. Sánchez-Iglesias A, Claes N, Solís DM, Taboada JM, Bals S, Liz-Marzán LM, Grzelczak M, Angewandte Chemie: international edition in English 57, 3183 (2018). http://doi.org/10.1002/anie.201800736
Abstract: A limiting factor of solvent-induced nanoparticle self-assembly is the need for constant sample dilution in assembly/disassembly cycles. Changes in the nanoparticle concentration alter the kinetics of the subsequent assembly process, limiting optical signal recovery. Herein, we show that upon confining hydrophobic nanoparticles in permeable silica nanocapsules, the number of nanoparticles participating in cyclic aggregation remains constant despite bulk changes in solution, leading to highly reproducible plasmon band shifts at different solvent compositions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 11.994
Times cited: 53
DOI: 10.1002/anie.201800736
|
|
“Fast A-site cation cross-exchange at room temperature : single-to double- and triple-cation halide perovskite nanocrystals”. Otero-Martinez C, Imran M, Schrenker NJ, Ye J, Ji K, Rao A, Stranks SD, Hoye RLZ, Bals S, Manna L, Perez-Juste J, Polavarapu L, Angewandte Chemie: international edition in English 61, e202205617 (2022). http://doi.org/10.1002/ANIE.202205617
Abstract: We report here fast A-site cation cross-exchange between APbX(3) perovskite nanocrystals (NCs) made of different A-cations (Cs (cesium), FA (formamidinium), and MA (methylammonium)) at room temperature. Surprisingly, the A-cation cross-exchange proceeds as fast as the halide (X=Cl, Br, or I) exchange with the help of free A-oleate complexes present in the freshly prepared colloidal perovskite NC solutions. This enabled the preparation of double (MACs, MAFA, CsFA)- and triple (MACsFA)-cation perovskite NCs with an optical band gap that is finely tunable by their A-site composition. The optical spectroscopy together with structural analysis using XRD and atomically resolved high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) and integrated differential phase contrast (iDPC) STEM indicates the homogeneous distribution of different cations in the mixed perovskite NC lattice. Unlike halide ions, the A-cations do not phase-segregate under light illumination.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 16.6
Times cited: 28
DOI: 10.1002/ANIE.202205617
|
|
“Use of nanoscale carbon layers on Ag-based gas diffusion electrodes to promote CO production”. Pacquets L, Van den Hoek J, Arenas Esteban D, Ciocarlan R-G, Cool P, Baert K, Hauffman T, Daems N, Bals S, Breugelmans T, ACS applied nano materials 5, 7723 (2022). http://doi.org/10.1021/ACSANM.2C00473
Abstract: A promising strategy for the inhibition of the hydrogen evolution reaction along with the stabilization of the electrocatalyst in electrochemical CO2 reduction cells involves the application of a nanoscale amorphous carbon layer on top of the active catalyst layer in a gas diffusion electrode. Without modifying the chemical nature of the electrocatalyst itself, these amorphous carbon layers lead to the stabilization of the electrocatalyst, and a significant improvement with respect to the inhibition of the hydrogen evolution reaction was also obtained. The faradaic efficiencies of hydrogen could be reduced from 31.4 to 2.1% after 1 h of electrolysis with a 5 nm thick carbon layer. Furthermore, the impact of the carbon layer thickness (5–30 nm) on this inhibiting effect was investigated. We determined an optimal thickness of 15 nm where the hydrogen evolution reaction was inhibited and a decent stability was obtained. Next, a thickness of 15 nm was selected for durability measurements. Interestingly, these durability measurements revealed the beneficial impact of the carbon layer already after 6 h by suppressing the hydrogen evolution such that an increase of only 37.9% exists compared to 56.9% without the use of an additional carbon layer, which is an improvement of 150%. Since carbon is only applied afterward, it reveals its great potential in terms of electrocatalysis in general.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 5.9
Times cited: 3
DOI: 10.1021/ACSANM.2C00473
|