Abstract: For many years, photocatalysis has been proposed as one of the promising techniques to abate environmental pollutants. To improve these reactions it is vital to know the reaction mechanisms of the photocatalytic degradation. This new reactor will make it possible to study the catalytic surface at the moment the reactions occur. By the means of UV LED illumination there is no need of an external UV lamp and thus lowers the cost. The validation of this newly developed reactor is done by investigating the photocatalytic reaction mechanism of nitric oxide (NO) and comparing these findings with those already discussed in literature. From these results, it became clear that the newly developed FTIR in situ reactor allows real time study of photocatalytic degradations.

Abstract: The precipitation of a disordered FCC surface structure after low angle Ga+ ion irradiation during focused ion beam thinning of a B2 Cu-Zn-Al alloy with e/a=1.48 is reported. Conventional as well as high-resolution transmission electron microscopy techniques reveal FCC layers on both sides of the thinned sample. The occurrence of this structure is attributed to disordering and dezincification of the alloy resulting from the sputtering process during the irradiation. Changes in crystallographic sample orientation with respect to the incoming ion beam do not have a significant effect on the appearance of the FCC surface structure.

Abstract: Dielectric properties of materials are crucial in describing the electromagnetic response of materials. As devices are becoming considerably smaller than the optical wavelength, the conventional measuring methods based on optical response are limited by their spatial resolution. Electron energy loss spectroscopy performed in a scanning transmission electron microscope is a good alternative to obtain the dielectric properties with excellent spatial resolution. Due to the overlap of diffraction discs in scanning transmission electron microscopy, it is difficult to apply conventional experimental settings to suppress retardation losses. In this contribution, a relativistic dielectric model for the loss function is presented which is used in a model based optimization scheme to estimate the complex dielectric function of a material. The method is applied to experiments on bulk diamond and SrTiO3 and shows a good agreement with optical reference data when retardation effects are included. Application of this technique to nanoparticles is possible but several theoretical assumptions made in the model of the loss function are violated and interpretation becomes problematic.

Abstract: The selective formation and stabilization of very small, naked metal particles inside the cavities of metal organic frameworks (MOFs) and the simultaneous realization of an even distribution of the particles throughout the crystalline MOF host matrix over a wide range of metal loading are challenging goals. MOFs reveal high specific surface areas, tunable pore sizes, and organic linkers, which are able to interact with guests. The chemically very robust zeolite imidazolate frameworks (ZIFs) are a subclass of MOFs. We chose the microporous sodalite-like ZIF-8 (Zn(MelM)(2); IM = imidazolate) and ZIF-90 (Zn(ICA)(2); ICA = imidazolate-2-carboxyaldehyde) as host matrices to influence the dispersion of imbedded gold nanoparticles (Au NPs). The metal loading was achieved via gas phase infiltration of [Au(CO)Cl] followed by a thermal hydrogenation step to form the Au NPs. Low-dose high-resolution transmission electron microscopy ((HR)TEM) and electron tomography reveal a homogeneous distribution of Au NPs throughout the ZIF matrix. The functional groups of ZIF-90 direct the anchoring of intermediate Au species and stabilize drastically smaller and quite monodisperse Au NPs in contrast to the parent not functionalized ZIF-8. The particles can be very small, match the cavity size and approach defined molecular clusters of magic numbers, i.e., Au(55), independently from the level of loading. Post-synthetic oxidation of the aldehyde groups to yield alkyl esters by the adjacent, catalytically active metal NPs is presented as a new concept of encapsulating nanoparticles inside MOFs and allows multiple steps of metal loadings without decomposition of the MOF.

Abstract: Structural changes of a variety of different SnO, SnO2 and GeO2 catalysts upon reduction in hydrogen were correlated with associated catalytic changes in methanol steam reforming. Studied systems include SnO, SnO2 and GeO2 thin film model catalysts prepared by vapour phase deposition and growth on polycrystalline NaCl surfaces and, for comparison, the corresponding pure oxide powder catalysts. Reduction of both the SnO2 thin film and powder at around 673 K in 1 bar hydrogen leads to a substantial reduction of the bulk structure and yields a mixture of SnO2 and metallic β-Sn. On the powder catalyst this transformation is fully reversible upon oxidation in 1 bar O2 at 673 K. Strongly reduced thin films, however, can only be re-transformed to SnO2 if the reduction temperature did not exceed 573 K. For GeO2, the situation is more complex due to its polymorphism. Whereas the tetragonal phase is structurally stable during reduction, oxidation or catalytic reaction, a small part of the hexagonal phase is always transformed into the tetragonal at 673 K independent of the gas phase used. SnO2 is highly active and CO2 selective in methanol steam reforming, but the initial high activity drops considerably upon reduction between 373 and 573 K and almost complete catalyst deactivation is observed after reduction at 673 K, which is associated with the parallel formation of β-Sn. In close correlation to the structural results, the catalytic activity and selectivity can be restored upon an oxidative catalyst regeneration at 673 K. Tetragonal GeO2 exhibits only a small activity and no pronounced selectivity to either CO or CO2, at least after reduction. In its fully oxidized state release of surface/lattice oxygen results in a non-catalytic formation of CO2 by oxidation of CO originating from catalytic dehydrogenation.

Abstract: The origin of the incommensurability in the crystallographic shear (CS) structure of the ferri-Manganite (Sr0.61Pb0.18)(Fe0.75Mn0.25)O2.29, related to the cation deficient perovskite, has been determined by careful analysis of the boundaries between the two variants constituting the phasoid. High Resolution Electron Microscopy/HAADF-STEM images allow the structural mechanisms to be understood through the presence of structural units common to both phases, responsible of the incommensurate character observed in the electron diffraction patterns. The structural analysis allows for identifying different types of CS phases in the Pb−Sr−Fe(Mn)−O diagram and shows that the stabilization of the six-sided tunnels requires a higher A/B cationic ratio. A description of these phases is proposed through simple structural building units (SBU), based on chains of octahedra bordered by two pyramids. The (Sr0.61Pb0.18)(Fe0.75Mn0.25)O2.29 CS compound exhibits a strong antiferromagnetic and insulating behavior, similar to the Fe-2201 and terrace ferrites but differs by the presence of a hysteresis, with a small coercive field.

Abstract: Metalorganic frameworks (MOFs) as well as porous coordination polymers (PCPs) are porous, organicinorganic hybrid solids with zeolite-like structures and properties. Due to their extraordinarily high surface area and well defined pore structure MOFs can be used for the stabilization of metal nanoparticles with adjustable size. The embedded metal nanoparticles are still accessible for other reagents due to the high porosity of the MOF systems. This fact makes metal@MOF systems especially interesting for heterogeneous catalysis, gas storage and chemical sensing. This review compiles the cases of metal nanoparticles supported by or embedded into MOFs reported so far and the main aspects and problems associated with these novel nanocomposite systems. The determination of the dispersion and the location of the particles at the MOF support, the control of the loading degree and its effect on the catalytic activity of the system are discussed as well as the partial degradation of the MOF structure upon particle formation. Examples of the introduction of stabilizing groups into the MOF network that direct the loading and can influence the size and shape of the embedded particles are still rare and point into the possible direction of future investigations. Finally, the formation of bimetallic nanoparticles, which are stabilized and supported by a MOF network, will also be reviewed.

Abstract: Pd particles supported on SnO2 and GeO2 have been structurally investigated by X-ray diffraction, (High-Resolution) transmission and scanning electron microscopy after different reductive treatments to monitor the eventual formation of bimetallic phases and catalytically tested in methanol dehydrogenation/ reforming. For both oxides this included a thin film sample with well-defined Pd particles and a powder catalyst prepared by incipient wetness impregnation. The hexagonal and the tetragonal polymorph were studied for powder GeO2. Pd2Ge formation was observed on all GeO2-supported catalysts, strongly depending on the specific sample used. Reduction of the thin film at 573K resulted in full transformation into the bimetallic state. The partial solubility of hexagonal GeO2 in water and its thermal structural instability yielded Pd2Ge formation at 473 K, at the cost of a structurally inhomogeneous support and Ge metal formation at higher reduction temperatures. Pd on tetragonal GeO2 entered a state of strong metalsupport interaction after reduction at 573673 K, resulting in coalescing Pd2Ge particles on a sintered and re-crystallized support, apparently partially covering the bimetallic particles and decreasing the catalytic activity. Pd2Ge on amorphous thin film and hexagonal GeO2 converted methanol primarily via dehydrogenation to CO and H2. At 573 K, formation of Pd2Sn and also PdSn occurred on the Pd/SnO2 thin film. Pd3Sn2 (and to some extent Pd2Sn) were predominantly obtained on the respective powder catalyst. Strong deactivation with increasing reduction temperature was observed, likely not based on the classical strong metalsupport interaction effect, but rather on a combination of missing active structural ensembles on Sn-enriched bimetallic phases and the formation of metallic -Sn. Correlations to Pd and its bimetallics supported on ZnO, Ga2O3 and In2O3 were also discussed.

Abstract: Epitaxial rare earth manganite thin films (ReMnO3; Re = Tb, Ho, Er, and Y) and multilayers were grown by liquid injection metal organic chemical vapor deposition (MOCVD) on YSZ(111) and the same systems were grown c-oriented on Pt(111) buffered Si substrates. They have been structurally investigated by electron diffraction (ED) and high resolution transmission electron microscopy (HRTEM). Nanodomains of secondary orientation are observed in the hexagonal YMnO3 films. They are related to a YSZ(111) and Pt(111) misorientation. The epitaxial film thickness has an influence on the defect formation. TbO2 and Er2O3 inclusions are observed in the TbMnO3 and ErMnO3 films respectively. The structure and orientation of these inclusions are correlated to the resembling symmetry and structure of film and substrate. The type of defect formed in the YMnO3/HoMnO3 and YMnO3/ErMnO3 multilayers is also influenced by the type of substrate they are grown on. In our work, atomic growth models for the interface between the film/substrate are proposed and verified by comparison with observed and computer simulated images.

Abstract: The cubic perovskite Ba(0.5)Sr(0.5)Co(0.8)Fe(0.2)O(3-delta) (denoted BSCF) is the state-of-the-art ceramic membrane material used for oxygen separation technologies above 1150 K. BSCF is a mixed oxygen-ion and electron conductor (MIEC) and exhibits one of the highest oxygen permeabilities reported so far for dense oxides. Additionally, it has excellent phase stability above 1150 K. In the intermediate temperature range (750-1100 K), however, BSCF suffers from a slow decomposition of the cubic perovskite into variants with hexagonal stacking that are barriers to oxygen transport. To elucidate details of the decomposition process, both sintered BSCF ceramic and powder were annealed for 180-240 h in ambient air at temperatures below 1123 K and analyzed by different transmission electron microscopy techniques. Aside from hexagonal perovskite Ba(0.5)Sr(0.5)CoO(3-delta) , the formation of lamellar noncubic phases was observed in the quenched samples. The structure of the lamellae with the previously unknown composition Ba(1-x)Sr(x)Co(2-y)Fe(y)O(5-delta) was found to be related to the 15R hexagonal perovskite polytype. The valence and spin-state transition of cobalt leading to a considerable diminution of its ionic radius can be considered a reason for BSCF's inherent phase instability at intermediate temperatures.

Abstract: Electron-energy-loss spectroscopy (EELS) is used to investigate single layers of LaAlO3 grown on SrTiO3 having an n-type interface as well as multilayers of LaAlO3 and SrTiO3 in which both n- and p-type interfaces occur. Only minor changes in Ti valence at the n-type interface are observed. This finding seems to contradict earlier experiments for other SrTiO3/LaAlO3 systems where large deviations in Ti valency were assumed to be responsible for the conductivity of these interfaces. Ab initio calculations have been carried out in order to interpret our EELS results. Using the concept of Bader charges, it is demonstrated that the so-called polar discontinuity is mainly resolved by lattice distortions and to a far lesser extent by changes in valency for both single layer and multilayer geometries.

Abstract: A new AnBnO3n−2 homologous series of anion-deficient perovskites has been evidenced by preparation of the members with n = 5 (Pb2.9Ba2.1Fe4TiO13) and n = 6 (Pb3.8Bi0.2Ba2Fe4.2Ti1.8O16) in a single phase form. The crystal structures of these compounds were determined using a combination of transmission electron microscopy and X-ray and neutron powder diffraction (S.G. Ammm, a = 5.74313(7), b = 3.98402(4), c = 26.8378(4) Å, RI = 0.035, RP = 0.042 for Pb2.9Ba2.1Fe4TiO13 and S.G. Imma, a = 5.7199(1), b = 3.97066(7), c = 32.5245(8) Å, RI = 0.032, RP = 0.037 for Pb3.8Bi0.2Ba2Fe4.2Ti1.8O16). The crystal structures of the AnBnO3n−2 homologues are formed by slicing the perovskite structure with (01)p crystallographic shear (CS) planes. The shear planes remove a layer of oxygen atoms and displace the perovskite blocks with respect to each other by the 1/2[110]p vector. The CS planes introduce edge-sharing connections of the transition metal−oxygen polyhedra at the interface between the perovskite blocks. This results in intrinsically frustrated magnetic couplings between the perovskite blocks due to a competition of the exchange interactions between the edge- and the corner-sharing metal−oxygen polyhedra. Despite the magnetic frustration, neutron powder diffraction and Mssbauer spectroscopy reveal that Pb2.9Ba2.1Fe4TiO13 and Pb3.8Bi0.2Ba2Fe4.2Ti1.8O16 are antiferromagnetically ordered below TN = 407 and 343 K, respectively. The Pb2.9Ba2.1Fe4TiO13 and Pb3.8Bi0.2Ba2Fe4.2Ti1.8O16 compounds are in a paraelectric state in the 5−300 K temperature range.

Abstract: The three-dimensional (3D) distribution of carbon nanotubes (CNTs) grown inside semiconductor contact holes is studied by electron tomography. The use of a specialized tomography holder results in an angular tilt range of ±90°, which means that the so-called missing wedge is absent. The transmission electron microscopy (TEM) sample for this purpose consists of a micropillar that is prepared by a dedicated procedure using the focused ion beam (FIB) but keeping the CNTs intact. The 3D results are combined with energy dispersive X-ray spectroscopy (EDS) to study the relation between the CNTs and the catalyst particles used during their growth. The reconstruction, based on the full range of tilt angles, is compared with a reconstruction where a missing wedge is present. This clearly illustates that the missing wedge will lead to an unreliable interpretation and will limit quantitative studies

Abstract: An innovative experimental approach to study the electrodeposition of small nanoparticles and the early stages of electrochemical nucleation and growth is presented. Carbon coated gold TEM grids are used as substrates for the electrodeposition of silver nanoparticles so that electrochemical data, FESEM, HAADFSTEM and HRTEM data can be acquired from the same sample without the need to remove the particles from the substrate. It is shown that the real distribution of nanoparticles cannot be resolved by FESEM whereas HAADFSTEM analysis confirms that a distribution of small nanoparticles (d ≈ 12 nm) coexist with large nanoparticles corresponding to a bimodal size distribution. Besides, particles grown under the same conditions have been found to present different structures such as monocrystals, polycrystals or aggregates of smaller particles.

Abstract: Multifrequency electron paramagnetic resonance (EPR) and high resolution transmission electron microscopy (HRTEM) investigations were performed on small (2 nm) cubic ZnS nanocrystals (quantum dotsQDs) doped with 0.2% mol Mn2+, self-assembled into a mesoporous structure. The EPR data analysis shows that the substitutional Mn2+ ions are localized at Zn2+ sites subjected to a local axial lattice distortion, resulting in the observed zero-field-splitting parameter |D|=41×10−4 cm−1. The local distortion is attributed to the presence in the second shell of ligands of a stacking fault or twin, which alters the normal stacking sequence of the cubic structure. The HRTEM results confirm the presence of such extended planar defects in a large percentage of the investigated QDs, which makes possible the proposed substitutional Mn2+ impurity ions localization model. Based on these results it is suggested that the high doping levels of Mn2+ ions observed in cubic ZnS and possible in other II-VI semiconductor QDs prepared at low temperatures can be explained by the assistance of the extended lattice defects in the impurities incorporation.