Abstract: The aim of this paper is to provide a thorough study on the occurrence and importance of deformation twinning in simple shear deformed pure α-Ti. A statistically relevant inspection of the morphology of the deformation twins in relation to the applied strain/deformation is performed. The investigated microstructural aspects are the twin volume fraction, the twin thickness distribution and the resolved shear stress distribution on the twin plane. All these aspects are examined as a function of the twin types and two initial textures. Monotonic simple shear experiments are carried out for three different loading directions with respect to a direction linked to the initial crystallographic texture. EBSD and TEM observations reveal the presence of View the MathML source and View the MathML source twins. The statistical analysis reveals that View the MathML source and View the MathML source twins have a similar average thickness around 1.9 nm, but the View the MathML source twins show a far larger spread on their thickness and can grow to almost the size of the original parent grain. Correlation of the twin fractions with the RSS analysis shows that RSS is an acceptable method explaining the difference in twin fractions for different textures and orientations. A detailed analysis shows that View the MathML source twins occur in average with a smaller volume fraction but with a higher RSS, indicating they are more difficult to nucleate or grow compared to View the MathML source twinning. In general a higher RSS value on the twin plane is not connected to a higher twin thickness; only in the case of View the MathML source twins the highest RSS values show clearly thicker twins.

Abstract: The crystal structure of the Sr2Fe2O5 brownmillerite has been investigated using electron diffraction and high resolution electron microscopy. The Sr2Fe2O5 structure demonstrates two-dimensional order: the tetrahedral chains with two mirror-related configurations (L and R) are arranged within the tetrahedral layers according to the −L−R−L−R− sequence, and the layers themselves are displaced with respect to each other over 1/2[111] or 1/2[11] vectors of the brownmillerite unit cell, resulting in different ordered stacking variants. A unified superspace model is constructed for ordered stacking sequences in brownmillerites based on the average brownmillerite structure with a = 5.5298(4)Å, b = 15.5875(12)Å, c = 5.6687(4)Å, and (3 + 1)-dimensional superspace group I2/m(0βγ)0s, q = βb* + γc*, 0 ≤ β ≤ 1/2, 0 ≤ γ ≤ 1.

Abstract: Particularly favourable properties of glass ceramics are developed on the basis of two key advantages of these materials: the variation of chemical composition and of microstructure. Therefore, detailed structural and chemical information are necessary to get insight in novel glass ceramic materials. We present here two examples of Er-doped Li2O-Al2O3-SiO2, with different quantities of ZrO2, both obtained with sol-gel synthesis. Different transmission electron microscopy techniques: conventional TEM, HRTEM, and EELS are used and the results are compared with those previously obtained with XRD and Rietveld analysis. We also demonstrate the 3D reconstruction, obtained from HAADF-STEM imaging, to determine the morphology of nanosize precipitates in these composites. (c) 2007 Elsevier B.V. All rights reserved.

Abstract: Interfacing oxides with silicon is a long-standing problem related to the integration of multifunctional oxides with semiconductor devices and the replacement of SiO2 with high-k gate oxides. In our study, pulsed laser deposition was used to prepare a SrTiO3 (STO) thin film on a H-terminated Si substrate. The main purpose of our work was to verify the ability of H-termination against the oxidation of Si during the PLD process and to analyze the resulting interfaces. In the first part of the study, the STO was deposited directly on the Si, leading to the formation of a preferentially textured STO film with a (100) orientation. In the second part, SrO was used as a buffer layer, which enabled the partial epitaxial growth of STO with STO(110)parallel to Si(100) and STO[001]parallel to Si[001]. The change in the growth direction induced by the application of a SrO buffer was governed by the formation of a SrO(111) intermediate layer and subsequently by the minimization of the lattice misfit between the STO and the SrO. Under the investigated conditions, approximately 10 nm thick interfacial layers formed between the STO and the Si due to reactions between the deposited material and the underlying H-terminated Si. In the case of direct STO deposition, SiOx formed at the interface with the silicon, while in the case when SrO was used as a buffer, strontium silicate grew directly on the silicon, which improves the growth quality of the uppermost STO.

Abstract: Structural, chemical, and physical properties of whitlockite-type Ca9Bi(VO4)(7) were studied by X-ray powder diffraction (XRD), electron diffraction (ED), second-harmonic generation (SHG), thermogravimetry, differential scanning calorimetry, dielectric, and electrical-conductivity measurements. A new phase-transition of the ferroelectric type was found in Ca9Bi(VO4)(7) with a transition temperature, T-c of 1053 +/- 3 K. The polar phase, beta-Ca9Bi(VO4)(7), is stable below T-c down to at least 160 K. The centrosymmetric beta'-phase is stable above T-c up to 1273 +/- 5 K. Above 1273 K, it decomposes to give BiVO4 and whitlockite-type solid solutions of Ca9+1.5xBi1-x(VO4)(7). The beta<---->beta' phase transition is reversible and of second order. Electrical conductivity of beta'-Ca9Bi(VO4)(7) is rather high (sigma = 0.6 x 10(-3) S/cm at 1200 K) and obeys the Arrhenius law with an activation energy of 1.0 eV. Structure parameters of Ca9Bi(VO4)(7) are refined by the Rietveld method from XRD data measured at room temperature (space group R3c; Z = 6; a = 10.8992(1) Angstrom, c = 38.1192(4) Angstrom, and V = 3921.6(1) Angstrom(3); R-wp = 3.06% and R-p = 2.36%). Bi3+ ions together with Ca2+ ions are statistically distributed among the M1, M2, M3, and M5 sites. Ca9Bi(VO4)(7) has a SHG efficiency of about 140 times that of quartz. Through the powder SHG measurements, we estimated the nonlinear optical susceptibility, Digital, at about 6.1-7.2 pm/V. This value for Ca9Bi(VO4)(7) is comparable with that for known nonlinear optical materials such as LiNbO3 and LiTaO3.

Abstract: We use density functional theory within the local density approximation to investigate the structural, electronic, and optical properties of Al-doped MgO. The concentrations considered range from 6% to 56%. In the latter case, we also compare the optical properties of the amorphous and crystalline phases. We find that, overall, the electronic properties of the crystalline phases change qualitatively little with Al concentration. On the other hand, the changes in the electronic structure in the amorphous phase are more important, most notably because of deep impurity levels in the band gap that are absent in the crystalline phase. This leads to observable effects in, e.g., the optical absorption edge and in the refractive index. Thus, the latter can be used to characterize the crystalline to amorphous transition with Al doping level.