“Anion ordering and defect structure in Ruddlesden-Popper strontium niobium oxynitrides”. Tobías G, Beltrán-Porter D, Lebedev OI, Van Tendeloo G, Rodríguez-Carvajal J, Fuertes A, Inorganic chemistry 43, 8010 (2004). http://doi.org/10.1021/ic049236k
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 31
DOI: 10.1021/ic049236k
|
|
|
“Copper(II)-binding ability of stereoisomeric cis- and trans-2-aminocyclohexanecarboxylic acidl-phenylalanine dipeptides : a combined CW/pulsed EPR and DFT study”. Nagy NV, Van Doorslaer S, Szabó-Plánka T, Van Rompaey S, Hamza A, Fülöp F, Tóth GK, Rockenbauer A, Inorganic chemistry 51, 1386 (2012). http://doi.org/10.1021/ic2016116
Abstract: With the aim of an improved understanding of the metal-complexation properties of alicyclic β-amino acid stereoisomers, and their peptides, the complex equilibria and modes of coordination with copper(II) of l-phenylalanine (F) derivatives of cis/trans-2-aminocyclohexanecarboxylic acid (c/tACHC), i.e. the dipeptides F-c/tACHC and c/tACHC-F, were investigated by a combination of CW and pulsed EPR methods. For the interpretation of the experimental data, DFT quantum-chemical calculations were carried out. Simulation of a pH-dependent series of room-temperature CW-EPR spectra revealed the presence of EPR-active complexes ([Cu(aqua)]2+, [CuL]+, [CuLH1], [CuLH2]−, and [CuL2H1]−), and an EPR-inactive species ([Cu2L2H3]−) in aqueous solutions for all studied cases. [CuLH]2+ was included in the equilibrium model for the c/tACHC-Fcopper(II) systems, and [CuL2], together with two coordination isomers of [CuL2H1]−, were also identified in the F-tACHCcopper(II) system. Comparison of the complexation properties of the diastereomeric ligand pair F-(1S,2R)-ACHC and F-(1R,2S)-ACHC did not reveal significant differences. Considerably lower formation constants were obtained for the trans than for the cis isomers for both the F-c/tACHC and the c/tACHC-F pairs in the case of [CuLH1] involving tridentate coordination by the amino, the deprotonated peptide, and the carboxylate groups. A detailed structural analysis by pulsed EPR methods and DFT calculations indicated that there was no significant destabilization for the complexes of the trans isomers. The lower stability of their complexes was explained by the limitation that only the conformer with donor groups in equatorialequatorial ring positions can bind to copper(II), whereas both equatorial-axial conformers of the cis isomers are capable of binding. From a consideration of the proton couplings obtained with X-band 1H HYSCORE, 2H exchange experiments, and DFT, the thermodynamically most stable cyclohexane ring conformer was assigned for all four [CuLH1] complexes. For the F-cACHC case, the conformer did not match the most stable conformer of the free ligand.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 18
DOI: 10.1021/ic2016116
|
|
|
“Crystal structure and phase transitions in Sr3WO6”. King G, Abakumov AM, Hadermann J, Alekseeva AM, Rozova MG, Perkisas T, Woodward PM, Van Tendeloo G, Antipov EV, Inorganic chemistry 49, 6058 (2010). http://doi.org/10.1021/ic100598v
Abstract: The crystal structures of the beta and gamma polymorphs of Sr3WO6 and the gamma <->beta phase transition have been investigated using electron diffraction, synchrotron X-ray powder diffraction, and neutron powder diffraction. The gamma-Sr3WO6 polymorph is stable above T-c approximate to 470 K and adopts a monoclinically distorted double perovskite A(2)BB'O-6= Sr2SrWO6 structure (space group Cc, a = 10.2363(1)angstrom, b= 17.9007(1)angstrom, c= 11.9717(1)angstrom, beta=125.585(1)degrees at T= 1373 K, Z=12, corresponding to a = a(p)+1/2b(p) – 1/2c(p), b =3/2b(p) + 3/2c(p), c =-b(p) + c(p), a(p),b(p), c(p), lattice vectors of the parent Fm (3) over barm double perovskite structure). Upon cooling it undergoes a continuous phase transition into the triclinically distorted beta-Sr3WO6 phase (space group Cl, a = 10.09497(3)angstrom, b = 17.64748(5)angstrom, c = 11.81400(3)angstrom, alpha = 89.5470(2)degrees, beta= 125.4529(2)degrees, gamma =90.2889(2)degrees at T= 300 K). Both crystal structures of Sr3WO6 belong to a family of double perovskites with broken corner sharing connectivity of the octahedral framework. A remarkable feature of the gamma-Sr3WO6 structure is a non-cooperative rotation of the WO6 octahedra. One third of the WO6 octahedra are rotated by 45 about either the bp or the cp axis of the parent double perovskite structure. As a result, the WO6 octahedra do not share corners but instead share edges with the coordination polyhedra of the Sr cations at the B positions increasing their coordination number from 6 to 7 or 8. The crystal structure of the beta-phase is very close to the structure of the gamma-phase; decreasing symmetry upon the gamma ->beta transformation occurs because of unequal octahedral rotation angles about the bp and cp axes and increasing distortions of the WO6 octahedra.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 18
DOI: 10.1021/ic100598v
|
|
|
“The crystal structure of \alpha-K3AIF6: elpasolites and double perovskites with broken corner-sharing connectivity of the octahedral framework”. Abakumov AM, King G, Laurinavichute VK, Rozova MG, Woodward PM, Antipov EV, Inorganic chemistry 48, 9336 (2009). http://doi.org/10.1021/ic9013043
Abstract: The crystal structure of α-K3AlF6 was solved and refined from a combination of powder X-ray and neutron diffraction data (a = 18.8385(3)Å, c = 33.9644(6)Å, S.G. I41/a, Z = 80, RP(X-ray) = 0.037, RP(neutron) = 0.053). The crystal structure is of the A2BB′X6 elpasolite type with the a = b ≈ ae√5, c = 4ae superstructure (ae, parameter of the elpasolite subcell) and rock-salt-type ordering of the K and Al cations over the B and B′ positions, respectively. The remarkable feature of α-K3AlF6 is a rotation of 2/5 of the AlF6 octahedra by π/4 around one of the crystal axes of the elpasolite subcell, coinciding with the 4-fold symmetry axes of the AlF6 octahedra. The rotation of the AlF6 octahedra replaces the corner-sharing between the K and Al polyhedra by edge-sharing, resulting in an increase of coordination numbers of the K cations at the B positions up to 7 and 8. Due to significant deformations of the K polyhedra, the corner-sharing connectivity of the octahedral elpasolite framework is broken and the rotations of the AlF6 octahedra do not have a cooperative character. Elpasolites and double perovskites with similar structural organization are discussed. The difference in ionic radii of the B and B′ cations as well as the tolerance factor are proposed to be the parameters governing the formation of elpasolites and double perovskites with broken corner-sharing connectivity of the octahedral framework.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 20
DOI: 10.1021/ic9013043
|
|
|
“Electron-microscopy investigation of superconducting la2cu(o, f)4+y oxyfluoride”. Weill, Chevalier, Chambon, Tressaud, Darriet, Etourneau, Van Tendeloo G, European journal of solid state and inorganic chemistry 30, 1095 (1993)
Abstract: The fluorination of La2CuO4 can lead to different oxyfluoride compounds depending on the TF2 temperature of the fluorine gas treatment. When 150-degrees-C T(F2) less-than-or-equal-to 200-degrees-c less-than-or-equal-to 200-degrees-C a superconducting material is obtained. Previous neutron diffraction experiments as well as the EXAFS measurements at the La L(III) edge indicate that extra anions lie in an interstitial site between the two (LaO) layers. Electron diffraction patterns clearly show the existence of an incommensurate modulation due to the presence of shear planes. A second phase is also pointed out which can be obtained as a major component when the fluorination temperature is raised to 230-degrees-C. This phase which is not a superconductor crystallizes with the monoclinic symmetry.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 2
|
|
|
“Electron microscopy investigation of superconducting La2Cu(O,F)4+y oxyfluoride”. Weill F, Chevalier B, Chambon M, Tressaud A, Darriet B, Etourneau J, Van Tendeloo G, European journal of solid state and inorganic chemistry 30, 1095 (1993)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 2
|
|
|
“Expanding the Ruddlesden-Popper manganite family : the n=3 La3.2Ba0.8Mn3O10 Member”. Hadermann J, Abakumov AM, Tsirlin AA, Rozova MG, Sarakinou E, Antipov EV, Inorganic chemistry 51, 11487 (2012). http://doi.org/10.1021/ic301332e
Abstract: La3.2Ba0.8Mn3O10, a representative of the rare n = 3 members of the Ruddlesden-Popper manganites A(n+1)Mn(n)O(3n+1), was synthesized in an evacuated sealed silica tube. Its crystal structure was refined from a combination of powder X-ray diffraction (PXD) and precession electron diffraction (PED) data, with the rotations of the MnO6 octahedra described within the symmetry-adapted mode approach (space group Cccm, a = 29.068(1) angstrom, b = 5.5504(5) angstrom, c = 5.5412(5) angstrom; PXD RF = 0.053, RP = 0.026; PED RF = 0.248). The perovskite block in La3.2Ba0.8Mn3O10 features an octahedral tilting distortion with out-of-phase rotations of the Mn06 octahedra according to the (Phi,Phi,0)(Phi,Phi,0) mode, observed for the first time in the n = 3 Ruddlesden-Popper structures. The Mn06 octahedra demonstrate a noticeable deformation with the elongation of two apical Mn-O bonds due to the Jahn-Teller effect in the Mn3+ cations. The relationships between the octahedral tilting distortion, the ionic radii of the cations at the A- and B-positions, and the mismatch between the perovslcite and rock-salt blocks of the Ruddlesden-Popper structure are discussed. At low temperatures, La3.2Ba0.8Mn3O10 reveals a sizable remnant magnetization of about 1.3 mu(B)/Mn at 2K, and shows signatures of spin freezing below 150 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 2
DOI: 10.1021/ic301332e
|
|
|
“The high-temperature polymorphs of K3AlF6”. King G, Abakumov AM, Woodward PM, Llobet A, Tsirlin AA, Batuk D, Antipov EV, Inorganic chemistry 50, 7792 (2011). http://doi.org/10.1021/ic200956a
Abstract: The crystal structures of the three high-temperature polymorphs of K3AlF6 have been solved from neutron powder diffraction, synchrotron X-ray powder diffraction, and electron diffraction data. The β-phase (stable between 132 and 153 °C) and γ-phase (stable between 153 to 306 °C) can be described as unusually complex superstructures of the double-perovskite structure (K2KAlF6) which result from noncooperative tilting of the AlF6 octahedra. The β-phase is tetragonal, space group I4/m, with lattice parameters of a = 13.3862(5) Å and c = 8.5617(3) Å (at 143 °C) and Z = 10. In this phase, one-fifth of the AlF6 octahedra are rotated about the c-axis by 45° while the other four-fifths remain untilted. The large 45° rotations result in edge sharing between these AlF6 octahedra and the neighboring K-centered polyhedra, resulting in pentagonal bipyramidal coordination for four-fifths of the K+ ions that reside on the B-sites of the perovskite structure. The remaining one-fifth of the K+ ions on the B-sites retain octahedral coordination. The γ-phase is orthorhombic, space group Fddd, with lattice parameters of a = 36.1276(4) Å, b = 17.1133(2) Å, and c = 12.0562(1) Å (at 225 °C) and Z = 48. In the γ-phase, one-sixth of the AlF6 octahedra are randomly rotated about one of two directions by 45° while the other five-sixths remain essentially untilted. These rotations result in two-thirds of the K+ ions on the B-site obtaining 7-fold coordination while the other one-third remain in octahedral coordination. The δ-phase adopts the ideal cubic double-perovskite structure, space group Fmm, with a = 8.5943(1) Å at 400 °C. However, pair distribution function analysis shows that locally the δ-phase is quite different from its long-range average crystal structure. The AlF6 octahedra undergo large-amplitude rotations which are accompanied by off-center displacements of the K+ ions that occupy the 12-coordinate A-sites.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 19
DOI: 10.1021/ic200956a
|
|
|
“Hole doping and structural transformation in CsTl1-xHgxCl3”. Retuerto M, Yin Z, Emge TJ, Stephens PW, Li MR, Sarkar T, Croft MC, Ignatov A, Yuan Z, Zhang SJ, Jin C, Paria Sena R, Hadermann J, Kotliar G, Greenblatt M;, Inorganic chemistry 54, 1066 (2015). http://doi.org/10.1021/ic502400d
Abstract: CsTlCl3 and CsTlF3 perovskites have been theoretically predicted to be superconductors when properly hole-doped. Both compounds have been previously prepared as pure compounds: CsTlCl3 in a tetragonal (I4/m) and a cubic (Fm3̅m) perovskite polymorph and CsTlF3 as a cubic perovskite (Fm3̅m). In this work, substitution of Tl in CsTlCl3 with Hg is reported, in an attempt to hole-dope the system and induce superconductivity. The whole series CsTl1xHgxCl3 (x = 0.0, 0.1, 0.2, 0.4, 0.6, and 0.8) was prepared. CsTl0.9Hg0.1Cl3 is tetragonal as the more stable phase of CsTlCl3. However, CsTl0.8Hg0.2Cl3 is already cubic with the space group Fm3̅m and with two different positions for Tl+ and Tl3+. For x = 0.4 and 0.5, solid solutions could not be formed. For x ≥ 0.6, the samples are primitive cubic perovskites with one crystallographic position for Tl+, Tl3+, and Hg2+. All of the samples formed are insulating, and there is no signature of superconductivity. X-ray absorption spectroscopy indicates that all of the samples have a mixed-valence state of Tl+ and Tl3+. Raman spectroscopy shows the presence of the active TlClTl stretching mode over the whole series and the intensity of the TlClHg mode increases with increasing Hg content. First-principle calculations confirmed that the phases are insulators in their ground state and that Hg is not a good dopant in the search for superconductivity in this system.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 5
DOI: 10.1021/ic502400d
|
|
|
“Layered perovskite-like Pb2Fe2O5 structure as a parent matrix for the nucleation and growth of crystallographic shear planes”. Batuk D, Hadermann J, Abakumov A, Vranken T, Hardy A, van Bael M, Van Tendeloo G, Inorganic chemistry 50, 4978 (2011). http://doi.org/10.1021/ic200211x
Abstract: The Pb2Fe2O5 compound with a layered intergrowth structure has been prepared by a solid-state reaction at 700 °C. The incommensurate compound crystallizes in a tetragonal system with a = 3.9037(2) Å, c = 3.9996(4) Å, and q = 0.1186(4)c*, or when treated as a commensurate approximant, a = 3.9047(2) Å, c = 36.000(3) Å, space group I4/mmm. The crystal structure of Pb2Fe2O5 was resolved from transmission electron microscopy data. Atomic coordinates and occupancies of the cation positions were estimated from high-angle annular dark-field scanning transmission electron microscopy data. Direct visualization of the positions of the oxygen atoms was possible using annular bright-field scanning transmission electron microscopy. The structure can be represented as an intergrowth of perovskite blocks and partially disordered blocks with a structure similar to that of the Bi2O2 blocks in Aurivillius-type phases. The A-cation positions at the border of the perovskite block and the cation positions in the Aurivillius-type blocks are jointly occupied by Pb2+ and Fe3+ cations, resulting in a layer sequence along the c axis: PbOFeO2PbOFeO2Pb7/8Fe1/8O1xFe5/8Pb3/8O2Fe5/8Pb3/8. Upon heating, the layered Pb2Fe2O5 structure transforms into an anion-deficient perovskite modulated by periodically spaced crystallographic shear (CS) planes. Considering the layered Pb2Fe2O5 structure as a parent matrix for the nucleation and growth of CS planes allows an explanation of the specific microstructure observed for the CS structures in the PbFeO system.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 16
DOI: 10.1021/ic200211x
|
|
|
“Magnetic and structural studies of the multifunctional material SrFe0.75Mo0.25O3-\text{\textgreek{d}}”. Retuerto M, Li MR, Go YB, Ignatov A, Croft M, Ramanujachary KV, Hadermann J, Hodges JP, Herber RH, Nowik I, Greenblatt M;, Inorganic chemistry 51, 12273 (2012). http://doi.org/10.1021/ic301550m
Abstract: SrFe0.75Mo0.25O3-delta has been recently discovered as an extremely efficient electrode for intermediate temperature solid oxide fuel cells (IT-SOFCs). We have performed structural and magnetic studies to fully characterize this multifunctional material. We have observed by powder neutron diffraction (PND) and transmission electron microscopy (TEM) that its crystal symmetry is better explained with a tetragonal symmetry (I4/mcm space group) than with the previously reported orthorhombic symmetry (Pnma space group). The temperature dependent magnetic properties indicate an exceptionally high magnetic ordering temperature (T-N similar to 750 K), well above room temperature. The ordered magnetic structure at low temperature was determined by PND to be an antiferromagnetic coupling of the Fe cations. Mossbauer spectroscopy corroborated the PND results. A detailed study, with X-ray absorption spectroscopy (XAS), in agreement with the Mossbauer results, confirmed the formal oxidation states of the cations to be mixed valence Fe3+/4+ and Mo6+.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 12
DOI: 10.1021/ic301550m
|
|
|
“Mixed tellurides Ni3-xGaTe2 (0\leq x\leq0.65): crystal and electronic structures, properties, and nickel deficiency effects on vacancy ordering”. Isaeva AA, Makarevich ON, Kutznetsov AN, Doert T, Abakumov AM, Van Tendeloo G, European journal of inorganic chemistry , 1395 (2010). http://doi.org/10.1002/ejic.200901027
Abstract: The Ni3-xGaTe2 series of compounds (0 x 0.65) was synthesized by a high-temperature ceramic technique at 750 °C. Crystal structures of three compounds in the series were determined by X-ray powder diffraction: Ni2.98(1)GaTe2 (RI = 0.042, Rp = 0.023, Rwp = 0.035), Ni2.79(1)GaTe2 (RI = 0.053, Rp = 0.028, Rwp = 0.039), Ni2.58(1)GaTe2 (RI = 0.081, Rp = 0.037, Rwp = 0.056); the structures were verified by electron diffraction and, for the former compound, high-resolution electron microscopy. The compounds crystallize in a hexagonal lattice with P63/mmc, and the structures can be regarded as a hexagonal close-packed array with a -Ga-Te-Te- stacking sequence. The octahedral and trigonal bipyramidal voids in the hcp structure are selectively filled with Ni atoms to form one entirely occupied and two partially occupied sites, thus allowing variations in the nickel content in the series of compounds Ni3-xGaTe2 (0 x 0.65). A superstructure with asup = 2asub (P63/mmc) has been identified for Ni3-xGaTe2 (0.5 x 0.65) by electron diffraction. Real-space, high-resolution images confirm an ordering of Ni atoms and vacancies inthe ab plane. Quantum-chemical calculations performed forNi3-xGaTe2 (x = 0, 0.25, 0.75, 1) suggest anisotropic metallic conductivity and Pauli paramagnetic behavior that are experimentally confirmed for Ni3GaTe2.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.444
Times cited: 8
DOI: 10.1002/ejic.200901027
|
|
|
“Mixed valent iron oxides with the 0201-1201 intergrowth structure: (Pb1-xTlx)Sr4Fe2O9 (0≤x≤1)”. Daniel P, Barbey L, Groult D, Nguyen N, Van Tendeloo G, Raveau B, European journal of solid state and inorganic chemistry 31, 235 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 12
|
|
|
“New cation deficient perovskite-like oxides in the system La4Ti3O12-LaTiO3”. Bontchev R, Darriet B, Darriet J, Weill F, Van Tendeloo G, Amelinckx S, European journal of solid state and inorganic chemistry 30, 521 (1993)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 19
|
|
|
“New class of single-source precursors for the synthesis of main group-transition metal oxides: heterobimetallic Pb-Mn \beta-diketonates”. Zhang H, Yang J-H, Shpanchenko RV, Abakumov AM, Hadermann J, Clérac R, Dikarev EV, Inorganic chemistry 48, 8480 (2009). http://doi.org/10.1021/ic901107s
Abstract: Heterometallic lead−manganese â-diketonates have been isolated in pure form by several synthetic methods that include solid-state and solution techniques. Two compounds with different Pb/Mn ratios, PbMn2(hfac)6 (1) and PbMn(hfac)4 (2) (hfac = hexafluoroacetylacetonate), can be obtained in quantitative yield by using different starting materials. Single crystal X-ray investigation revealed that the solid-state structure of 1 contains trinuclear molecules in which lead metal center is sandwiched between two [Mn(hfac)3] units, while 2 consists of infinite chains of alternating [Pb(hfac)2] and [Mn(hfac)2] fragments. The heterometallic structures are held together by strong Lewis acid−base interactions between metal atoms and diketonate ligands acting in chelating-bridging fashion. Spectroscopic investigation confirmed the retention of heterometallic structures in solutions of non-coordinating solvents as well as upon sublimation-deposition procedure. Thermal decomposition of heterometallic diketonates has been systematically investigated in a wide range of temperatures and annealing times. For the first time, it has been shown that thermal decomposition of heterometallic diketonates results in mixed-metal oxides, while both the structure of precursors and the thermolysis conditions have a significant influence on the nature of the resulting oxides. Five different Pb−Mn oxides have been detected by X-ray powder diffraction when studying the decomposition of 1 and 2 in the temperature range 500−800 °C. The phase that has been previously reported as Pb0.43MnO2.18 was synthesized in the pure form by decomposition of 1, and crystallographically characterized. The orthorhombic unit cell parameters of this oxide, obtained by electron diffraction technique, have been subsequently refined using X-ray powder diffraction data. Besides that, a previously unknown lead−manganese oxide has been obtained at low temperature decomposition and short annealing times. The parameters of its monoclinically distorted unit cell have been determined. The EDX analysis revealed that this compound has a Pb/Mn ratio close to 1:4 and contains no appreciable amount of fluorine.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 28
DOI: 10.1021/ic901107s
|
|
|
“Polar and magnetic layered A-site and rock salt B-site-ordered NaLnFeWO6 (Ln = La, Nd) perovskites”. Retuerto M, Li MR, Ignatov A, Croft M, Ramanujachary KV, Chi S, Hodges JP, Dachraoui W, Hadermann J, Tran TT, Halasyamani PS, Grams CP, Hemberger J, Greenblatt M;, Inorganic chemistry 52, 12482 (2013). http://doi.org/10.1021/ic401491y
Abstract: We have expanded the double perovskite family of materials with the unusual combination of layered order in the A sublattice and rock salt order over the B sublattice to compounds NaLaFeWO6 and NaNdFeWO6. The materials have been synthesized and studied by powder X-ray diffraction, neutron diffraction, electron diffraction, magnetic measurements, X-ray absorption spectroscopy, dielectric measurements, and second harmonic generation. At room temperature, the crystal structures of both compounds can be defined in the noncentrosymmetric monoclinic P2(1) space group resulting from the combination of ordering both in the A and B sublattices, the distortion of the cell due to tilting of the octahedra, and the displacement of certain cations. The magnetic studies show that both compounds are ordered antiferromagnetically below T-N approximate to 25 K for NaLaFeWO6 and at similar to 21 K for NaNdFeWO6. The magnetic structure of NaNdFeWO6 has been solved with a propagation vector k = (1/2 0 1/2) as an antiferromagnetic arrangement of Fe and Nd moments. Although the samples are potential multiferroics, the dielectric measurements do not show a ferroelectric response.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 17
DOI: 10.1021/ic401491y
|
|
|
“Sr21Bi8Cu2(CO3)(2)O-41, a Bi5+ Oxycarbonate with an Original 10L Structure”. Malo S, Abakumov AM, Daturi M, Pelloquin D, Van Tendeloo G, Guesdon A, Hervieu M, Inorganic chemistry 53, 10266 (2014). http://doi.org/10.1021/ic501322w
Abstract: The layered structure of Sr21Bi8Cu2(CO3)(2)O-41 (Z = 2) was determined by transmission electron microscopy, infrared spectroscopy, and powder X-ray diffraction refinement in space group P6(3)/mcm (No. 194), with a = 10.0966(3)angstrom and c = 26.3762(5)angstrom. This original 10L-type structure is built from two structural blocks, namely, [Sr15Bi6Cu2(CO3)O-29] and [Sr6Bi2(CO3)O-12]. The Bi5+ cations form [Bi2O10] dimers, whereas the Cu2+ and C atoms occupy infinite tunnels running along (c) over right arrow. The nature of the different blocks and layers is discussed with regard to the existing hexagonal layered compounds. Sr21Bi8Cu2(CO3)(2)O-41 is insulating and paramagnetic.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
DOI: 10.1021/ic501322w
|
|
|
“Synthesis and structure of fluorinated RBa2Cu2O6+. (R=Dy, Ho and Tm) phases”. Oleynikov PN, Shpanchenko RV, Rozova MG, Abakumov AM, Antipov EV, Hadermann J, Lebedev OI, Van Tendeloo G, Russian journal of inorganic chemistry 46, 153 (2001)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.787
|
|
|
“Synthesis, crystal structure, transport, and magnetic properties of novel ternary copper phosphides, A2Cu6P5(A = Sr, Eu) and EuCu4P3”. Charkin DO, Urmanov AV, Kazakov SM, Batuk D, Abakumov AM, Knöner S, Gati E, Wolf B, Lang M, Shevelkov AV, Van Tendeloo G, Antipov EV;, Inorganic chemistry 51, 8948 (2012). http://doi.org/10.1021/ic301033h
Abstract: Three new ternary copper phosphides, Sr2Cu6P5, Eu2Cu6P5, and EuCu4P3, have been synthesized from the elements in evacuated silica capsules. Eu2Cu6P5 and Sr2Cu6P5 adopt the Ca2Cu6P5-type structure, while EuCu4P3 is isostructural to BaMg4Si3 and still remains the only representative of this structure type among the ternary Cu pnictides. All three materials show metallic conductivity in the temperature range 2 K <= T <= 290 K, with no indication for superconductivity. For Eu2Cu6P5 and EuCu4P3, long-range magnetic order was observed, governed by 4f local moments on the Eu atoms with predominant ferromagnetic interactions. While Eu2Cu6P5 shows a single ferromagnetic transition at T-C = 34 K, the magnetic behavior of EuCu4P3 is more complex, giving rise to three consecutive magnetic phase transitions at 70, 43, and 18 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 13
DOI: 10.1021/ic301033h
|
|
|
“Synthesis, structure, and transport properties of type-I derived clathrate Ge46-xPxSe8-y (x=15.4(1), y=0-2.65) with diverse host-guest bonding”. Kirsanova MA, Mori T, Maruyama S, Matveeva, Batuk D, Abakumov AM, Gerasimenko AV, Olenev AV, Grin Y, Shevelkov AV, Inorganic chemistry 52, 577 (2013). http://doi.org/10.1021/ic3011025
Abstract: A first clathrate compound with selenium guest atoms, [Ge46-xPx]Se8-y square(y) (x = 15.4(1); y = 0-2.65; square denotes a vacancy), was synthesized as a single-phase and structurally characterized. It crystallizes in the space group Fm (3) over bar with the unit cell parameter a varying from 20.310(2) to 20.406(2) angstrom and corresponding to a 2 x 2 x 2 supercell of a usual clathrate-I structure. The superstructure is formed due to the symmetrical arrangement of the three-bonded framework atoms appearing as a result of the framework transformation of the parent clathrate-I structure. Selenium guest atoms occupy two types of polyhedral cages inside the positively charged framework; all selenium atoms in the larger cages form a single covalent bond with the framework atoms, relating the title compounds to a scanty family of semiclathrates. According to the measurements of electrical resistivity and Seebeck coefficient, [Ge46-xPx]Se8-y square(y) is an n-type semiconductor with E-g = 0.41 eV for x = 15.4(1) and y = 0; it demonstrates the maximal thermoelectric power factor of 2.3 x 10(-5) W K-2 m(-1) at 660 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 14
DOI: 10.1021/ic3011025
|
|
|
“Ternary magnesium rhodium boride Mg2Rh1-xB6+2x with a modified Y2ReB6-type crystal structure”. Alekseeva AM, Abakumov AM, Chizhov PS, Leithe-Jasper A, Schnelle W, Prots Y, Hadermann J, Antipov EV, Grin Y, Inorganic chemistry 46, 7378 (2007). http://doi.org/10.1021/ic7004453
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 12
DOI: 10.1021/ic7004453
|
|
|
“Cs7Nd11(SeO3)12Cl16 : first noncentrosymmetric structure among alkaline-metal lanthanide selenite halides”. Berdonosov PS, Akselrud L, Prots Y, Abakumov AM, Smet PF, Poelman D, Van Tendeloo G, Dolgikh VA, Inorganic chemistry 52, 3611 (2013). http://doi.org/10.1021/ic301442f
Abstract: Cs7Nd11(SeO3)(12)Cl-16, the complex selenite chloride of cesium and neodymium, was synthesized in the NdOCl-SeO2-CsCl system. The compound has been characterized using single-crystal X-ray diffraction, electron diffraction, transmission electron microscopy, luminescence spectroscopy, and second-harmonic-generation techniques. Cs7Nd11(SeO3)(12)Cl-16 crystallizes in an orthorhombic unit cell with a = 15.911(1) angstrom, b = 15.951(1) angstrom, and c = 25.860(1) angstrom and a noncentrosymmetric space group Pna2(1) (No. 33). The crystal structure of Cs7Nd11(SeO3)(12)Cl-16 can be represented as a stacking of Cs7Nd11(SeO3)(12) lamellas and CsCl-like layers. Because of the layered nature of the Cs7Nd11(SeO3)(12)Cl-16 structure, it features numerous planar defects originating from occasionally missing the CsCl-like layer and violating the perfect stacking of the Cs7Nd11(SeO3)(12)Cl-16 lamellas. Cs7Nd11(SeO3)(12)Cl-16 represents the first example of a noncentrosymmetric structure among alkaline-metal lanthanide selenite halides. Cs7Nd11(SeO3)(12)Cl-16 demonstrates luminescence emission in the near-IR region with reduced efficiency due to a high concentration of Nd3+ ions causing nonradiative cross-relaxation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 10
DOI: 10.1021/ic301442f
|
|
|
“Na2/7Gd4/7MoO4 : a modulated scheelite-type structure and conductivity properties”. Morozov V, Arakcheeva A, Redkin B, Sinitsyn V, Khasanov S, Kudrenko E, Raskina M, Lebedev O, Van Tendeloo G, Inorganic chemistry 51, 5313 (2012). http://doi.org/10.1021/ic300221m
Abstract: Scheelite-type compounds with the general formula (A1,A2)n[(B1,B2)O4]m (2/3 ≤ n/m ≤ 3/2) are the subject of large interest owing to their stability, relatively simple preparation, and optical properties. The creation of cation vacancies (□) in the scheelite-type framework and the ordering of A cations and vacancies can be a new factor in controlling the scheelite-type structure and properties. For a long time, cation-deficient Nd3+:M2/7Gd4/7□1/7MoO4 (M = Li, Na) compounds were considered as potential lasers with diode pumping. They have a defect scheelite-type 3D structure (space group I41/a) with a random distribution of Li+(Na+), Gd3+, and vacancies in the crystal. A Na2/7Gd4/7MoO4 single crystal with scheelite-type structure has been grown by the Czochralski method. Transmission electron microscopy revealed that Na2/7Gd4/7MoO4 has a (3 + 2)D incommensurately modulated structure. The (3 + 2)D incommensurately modulated scheelite-type cation-deficient structure of Na2/7Gd4/7MoO4 [super space group I4̅ (αβ0,βα0)00] has been solved from single-crystal diffraction data. The solution of the (3 + 2)D incommensurately modulated structure revealed the partially disordered distribution of vacancies and Na and Gd cations. High-temperature conductivity measurements performed along the [100] and [001] orientation of the single crystal revealed that the conductivity of Na2/7Gd4/7MoO4 at T = 973 K equals σ = 1.13 × 105 Ω1 cm1.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 37
DOI: 10.1021/ic300221m
|
|
|
“Sn19.3Cu4.7As22I8: a new clathrate-I compound with transition-metal atoms in the cationic framework”. Kovnir KA, Sobolev AV, Presniakov IA, Lebedev OI, Van Tendeloo G, Schnelle W, Grin Y, Shevelkov AV, Inorganic chemistry 44, 8786 (2005). http://doi.org/10.1021/ic051160k
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 38
DOI: 10.1021/ic051160k
|
|
|
“_Sr{2}GaScO5, Sr10Ga6Sc4O25, and SrGa0.75Sc0.25O2.5 : a play in the octahedra to tetrahedra ratio in oxygen-deficient perovskites”. Chernov SV, Dobrovolsky YA, Istomin SY, Antipov EV, Grins J, Svensson G, Tarakina NV, Abakumov AM, Van Tendeloo G, Eriksson SG, Rahman SMH;, Inorganic chemistry 51, 1094 (2012). http://doi.org/10.1021/ic202236h
Abstract: Three different perovskite-related phases were isolated in the SrGa(1-x)Sc(x)O(2.5) system: Sr(2)GaScO(5), Sr(10)Ga(6)Sc(4)O(25), and SrGa(0.75)Sc(0.25)O(2.5), Sr(2)GaScO(5) (x = 0.5) crystallizes in a brownrnillerite-type structure [space group (S.G.) Icmm, a = 5.91048(5) angstrom, b = 15.1594(1) angstrom, and c = 5.70926(4) angstrom] with complete ordering of Sc(3+) and Ga(3+) over octahedral and tetrahedral positions, respectively. The crystal structure of Sr(10)Ga(6)Sc(4)O(25) (x = 0.4) was determined by the Monte Carlo method and refined using a combination of X-ray, neutron, and electron diffraction data [S.G. I4(1)/a, a = 17.517(1) angstrom, c = 32.830(3) angstrom]. It represents a novel type of ordering of the B cations and oxygen vacancies in perovskites. The crystal structure of Sr(10)Ga(6)Sc(4)O(25) can be described as a stacking of eight perovskite layers along the c axis ...[-(Sc/Ga)O(1.6)-SrO(0.8)-(Sc/Ga)O(1.8)-SrO(0.8)-](2 center dot center dot center dot) Similar to Sr(2)GaScO(5), this structure features a complete ordering of the Sc(3+) and Ga(3+) cations over octahedral and tetrahedral positions, respectively, within each layer. A specific feature of the crystal structure of Sr(10)Ga(6)Sc(4)O(25) is that one-third of the tetrahedra have one vertex not connected with other Sc/Ga cations. Further partial replacement of Sc(3+) by Ga(3+) leads to the formation of the cubic perovskite phase SrGa(0.75)Sc(0.25)O(2.5) (x = 0.25) with a = 3.9817(4) angstrom. This compound incorporates water molecules in the structure forming SrGa(0.75)Sc(0.25)O(2.5)center dot xH(2)O hydrate, which exhibits a proton conductivity of similar to 2.0 x 10(-6) S/cm at 673 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 14
DOI: 10.1021/ic202236h
|
|
|
“Two New Arsenides, Eu7Cu44As23 and Sr7Cu44As23, With a New Filled Variety of the BaHg11 Structure”. Charkin DO, Demchyna R, Prots Y, Borrmann H, Burkhardt U, Schwarz U, Schnelle W, Plokhikh IV, Kazakov SM, Abakumov AM, Batuk D, Verchenko VY, Tsirlin AA, Curfs C, Grin Y, Shevelkov AV;, Inorganic chemistry 53, 11173 (2014). http://doi.org/10.1021/ic5017615
Abstract: Two new ternary arsenides, namely, Eu7Cu44As23 and Sr7Cu44As23, were synthesized from elements at 800 degrees C. Their crystal structure represents a new filled version of the BaHg11 motif with cubic voids alternately occupied by Eu(Sr) and As atoms, resulting in a 2 x 2 x 2 superstructure of the aristotype: space group Fm (3) over barm, a = 16.6707(2) angstrom and 16.7467(2) angstrom, respectively. The Eu derivative exhibits ferromagnetic ordering below 17.5 K. In agreement with band structure calculations both compounds are metals, exhibiting relatively low thermopower, but high electrical and low thermal conductivity.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 9
DOI: 10.1021/ic5017615
|
|
|
“Pb2MnTeO6 double perovskite : an antipolar anti-ferromagnet”. Retuerto M, Skiadopoulou S, Li MR, Abakumov AM, Croft M, Ignatov A, Sarkar T, Abbett BM, Pokorný, J, Savinov M, Nuzhnyy D, Prokleška J, Abeykoon M, Stephens PW, Hodges JP, Vaněk P, Fennie CJ, Rabe KM, Kamba S, Greenblatt M;, Inorganic chemistry 55, 4320 (2016). http://doi.org/10.1021/acs.inorgchem.6b00054
Abstract: Pb2MnTeO6, a new double perovskite, was synthesized. Its crystal structure was determined by synchrotron X-ray and powder neutron diffraction. Pb2MnTeO6 is monoclinic (I2/m) at room temperature with a regular arrangement of all the cations in their polyhedra. However, when the temperature is lowered to similar to 120 K it undergoes a phase transition from I2/m to C2/c structure. This transition is accompanied by a displacement of the Pb atoms from the center of their polyhedra due to the 6s2 lone-pair electrons, together with a surprising off-centering of Mn2+ (d5) magnetic cations. This strong first-order phase transition is also evidenced by specific heat, dielectric, Raman, and infrared spectroscopy measurements. The magnetic characterizations indicate an anti-ferromagnetic (AFM) order below TN approximate to 20 K; analysis of powder neutron diffraction data confirms the magnetic structure with propagation vector k = (0 1 0) and collinear AFM spins. The observed jump in dielectric permittivity near similar to 150 K implies possible anti-ferroelectric behavior; however, the absence of switching suggests that Pb2MnTeO6 can only be antipolar. First-principle calculations confirmed that the crystal and magnetic structures determined are locally stable and that anti-ferroelectric switching is unlikely to be observed in Pb2MnTeO6.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 9
DOI: 10.1021/acs.inorgchem.6b00054
|
|
|
“Ba-3(Cr0.97(1)Te0.03(1))(2)TeO9: in Search of Jahn-Teller Distorted Cr(II) Oxide”. Li M-R, Deng Z, Lapidus SH, Stephens PW, Segre CU, Croft M, Sena RP, Hadermann J, Walker D, Greenblatt M, Inorganic chemistry 55, 10135 (2016). http://doi.org/10.1021/ACS.INORGCHEM.6B01047
Abstract: A novel 6H-type hexagonal perovskite Ba-3(Cr0.97(1)Te0.03(1))(2)TeO9 was prepared at high pressure (6 GPa) and temperature (1773 K). Both transmission electron microscopy and synchrotron powder X-ray diffraction data demonstrate that Ba-3(Cr0.97(1)Te0.03(1))(2)TeO9 crystallizes in P6(3)/mmc with face-shared (Cr0.97(1)Te0.03(1))O-6 octahedral pairs interconnected with TeO6 octahedra via corner-sharing. Structure analysis shows a mixed Cr2+/Cr3+ valence state with similar to 10% Cr2+. The existence of Cr2+ in Ba-3(Cr0.10(1)2+Cr0.87(1)3+Te0.036+)(2)TeO9 is further evidenced by X-ray absorption near-edge spectroscopy. Magnetic properties measurements show a paramagnetic response down to 4 K and a small glassy-state curvature at low temperature. In this work, the octahedral Cr2+O6 component is stabilized in an oxide material for the first time; the expected Jahn-Teller distortion of high-spin (d(4)) Cr2+ is not found, which is attributed to the small proportion of Cr2+ (similar to 10%) and the face-sharing arrangement of CrO6 octahedral pairs, which structurally disfavor axial distortion.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 2
DOI: 10.1021/ACS.INORGCHEM.6B01047
|
|
|
“Fe3O4@MIL-101-A selective and regenerable adsorbent for the removal of as species from water”. Folens K, Leus K, Nicomel NR, Meledina M, Turner S, Van Tendeloo G, Du Laing G, Van Der Voort P, European journal of inorganic chemistry 2016, 4395 (2016). http://doi.org/10.1002/EJIC.201600160
Abstract: The chromium-based metal organic framework MIL-101(Cr) served as a host for the in situ synthesis of Fe3O4 nano particles. This hybrid nanomaterial was tested as an adsorbent for arsenite and arsenate species in groundwater and surface water and showed excellent affinity towards As-III and As-V species. The adsorption capacities of 121.5 and 80.0 mg g(-1) for arsenite and arsenate species, respectively, are unprecedented. The presence of Ca2+, Mg2+, and phosphate ions and natural organic matter does not affect the removal efficiency or the selectivity. The structural integrity of the hybrid nanomaterial was maintained during the adsorption process and even after desorption through phosphate elution. Additionally, no significant leaching of Cr or Fe species was observed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.444
Times cited: 27
DOI: 10.1002/EJIC.201600160
|
|
|
“Ambient and high pressure CuNiSb₂, : metal-ordered and metal-disordered NiAs-type derivative pnictides”. Skaggs CM, Kang C-J, Perez CJ, Hadermann J, Emge TJ, Frank CE, Pak C, Lapidus SH, Walker D, Kotliar G, Kauzlarich SM, Tan X, Greenblatt M, Inorganic Chemistry 59, 14058 (2020). http://doi.org/10.1021/ACS.INORGCHEM.0C01848
Abstract: The mineral Zlatogorite, CuNiSb2, was synthesized in the laboratory for the first time by annealing elements at ambient pressure (CuNiSb2-AP). Rietveld refinement of synchrotron powder X-ray diffraction data indicates that CuNiSb2-AP crystallizes in the NiAs-derived structure (P (3) over bar m1, #164) with Cu and Ni ordering. The structure consists of alternate NiSb6 and CuSb6 octahedral layers via face-sharing. The formation of such structure instead of metal disordered NiAs-type structure (P6(3)/mmc, #194) is validated by the lower energy of the ordered phase by first-principle calculations. Interatomic crystal orbital Hamilton population, electron localization function, and charge density analysis reveal strong Ni-Sb, Cu-Sb, and Cu-Ni bonding and long weak Sb-Sb interactions in CuNiSb2-AP. The magnetic measurement indicates that CuNiSb2-AP is Pauli paramagnetic. First-principle calculations and experimental electrical resistivity measurements reveal that CuNiSb2-AP is a metal. The low Seebeck coefficient and large thermal conductivity suggest that CuNiSb2 is not a potential thermoelectric material. Single crystals were grown by chemical vapor transport. The high pressure sample (CuNiSb2-8 GPa) was prepared by pressing CuNiSb2-AP at 700 degrees C and 8 GPa. However, the structures of single crystal and CuNiSb2-8 GPa are best fit with a disordered metal structure in the P (3) over bar m1 space group, corroborated by transmission electron microscopy.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.6
DOI: 10.1021/ACS.INORGCHEM.0C01848
|
|