Records |
Author |
Sankaran, K.J.; Hoang, D.Q.; Srinivasu, K.; Korneychuk, S.; Turner, S.; Drijkoningen, S.; Pobedinskas, P.; Verbeeck, J.; Leou, K.C.; Lin, I.N.; Haenen, K. |
Title |
|
Type |
A1 Journal article |
Year |
2016 |
Publication |
Physica status solidi : A : applications and materials science |
Abbreviated Journal |
Phys Status Solidi A |
Volume |
213 |
Issue |
10 |
Pages |
2654-2661 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
Utilization of Au and nanocrystalline diamond ( NCD) as interlayers noticeably modifies the microstructure and field electron emission ( FEE) properties of hexagonal boron nitride nanowalls ( hBNNWs) grown on Si substrates. The FEE properties of hBNNWs on Au could be turned on at a low turn-on field of 14.3V mu m(-1), attaining FEE current density of 2.58mAcm(-2) and life-time stability of 105 min. Transmission electron microscopy reveals that the Au-interlayer nucleates the hBN directly, preventing the formation of amorphous boron nitride ( aBN) in the interface, resulting in enhanced FEE properties. But Au forms as droplets on the Si substrate forming again aBN at the interface. Conversely, hBNNWs on NCD shows superior in life-time stability of 287 min although it possesses inferior FEE properties in terms of larger turn-on field and lower FEE current density as compared to that of hBNNWs-Au. The uniform and continuous NCD film on Si also circumvents the formation of aBN phases and allows hBN to grow directly on NCD. Incorporation of carbon in hBNNWs from the NCD-interlayer improves the conductivity of hBNNWs, which assists in transporting the electrons efficiently from NCD to hBNNWs that results in better field emission of electrons with high life-time stability. (C) 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000388321500017 |
Publication Date |
2016-09-27 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
1862-6300 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
1.775 |
Times cited |
5 |
Open Access |
|
Notes |
The authors like to thank the financial support of the Research Foundation Flanders (FWO) via Research Projects G.0456.12 and G.0044.13N, the Methusalem “NANO” network. K. J. Sankaran, P. Pobedinskas, and S. Turner are FWO Postdoctoral Fellows of the Research Foundations Flanders (FWO). |
Approved |
Most recent IF: 1.775 |
Call Number |
UA @ lucian @ c:irua:144644UA @ admin @ c:irua:144644 |
Serial |
4655 |
Permanent link to this record |
|
|
|
Author |
Deshmukh, S.; Sankaran, K.J.; Srinivasu, K.; Korneychuk, S.; Banerjee, D.; Barman, A.; Bhattacharya, G.; Phase, D.M.; Gupta, M.; Verbeeck, J.; Leou, K.C.; Lin, I.N.; Haenen, K.; Roy, S.S. |
Title |
Local probing of the enhanced field electron emission of vertically aligned nitrogen-doped diamond nanorods and their plasma illumination properties |
Type |
A1 Journal article |
Year |
2018 |
Publication |
Diamond and related materials |
Abbreviated Journal |
Diam Relat Mater |
Volume |
83 |
Issue |
83 |
Pages |
118-125 |
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
Abstract |
A detailed conductive atomic force microscopic investigation is carried out to directly image the electron emission behavior for nitrogen-doped diamond nanorods (N-DNRs). Localized emission measurements illustrate uniform distribution of high-density electron emission sites from N-DNRs. Emission sites coupled to nano graphitic phases at the grain boundaries facilitate electron transport and thereby enhance field electron emission from N-DNRs, resulting in a device operation at low turn-on fields of 6.23 V/mu m, a high current density of 1.94 mA/cm(2) (at an applied field of 11.8 V/mu m) and a large field enhancement factor of 3320 with a long lifetime stability of 980 min. Moreover, using N-DNRs as cathodes, a microplasma device that can ignite a plasma at a low threshold field of 390 V/mm achieving a high plasma illumination current density of 3.95 mA/cm2 at an applied voltage of 550 V and a plasma life-time stability for a duration of 433 min was demonstrated. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
Amsterdam |
Editor |
|
Language |
|
Wos |
000430767200017 |
Publication Date |
2018-02-07 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
0925-9635 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
2.561 |
Times cited |
9 |
Open Access |
Not_Open_Access |
Notes |
; S. Deshmulch, D. Banerjee and G. Bhattacharya are indebted to Shiv Nadar University for providing Ph.D. scholarships. K.J. Sankaran and K. Haenen like to thank the financial support of the Research Foundation Flanders (FWO) via Research Grant 12I8416N and Research Project 1519817N, and the Methusalem “NANO” network. K.J. Sankaran is a Postdoctoral Fellow of the Research Foundation-Flanders (FWO). The Qu-Ant-EM microscope used for the TEM experiments was partly funded by the Hercules fund from the Flemish Government. S. Korneychuk and J. Verbeeck acknowledge funding from GOA project “Solarpaint” of the University of Antwerp. ; |
Approved |
Most recent IF: 2.561 |
Call Number |
UA @ lucian @ c:irua:151609UA @ admin @ c:irua:151609 |
Serial |
5030 |
Permanent link to this record |
|
|
|
Author |
Ramaneti, R.; Sankaran, K.J.; Korneychuk, S.; Yeh, C.J.; Degutis, G.; Leou, K.C.; Verbeeck, J.; Van Bael, M.K.; Lin, I.N.; Haenen, K. |
Title |
Vertically aligned diamond-graphite hybrid nanorod arrays with superior field electron emission properties |
Type |
A1 Journal article |
Year |
2017 |
Publication |
APL materials |
Abbreviated Journal |
Apl Mater |
Volume |
5 |
Issue |
6 |
Pages |
066102 |
Keywords |
A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT) |
Abstract |
A “patterned-seeding technique” in combination with a “nanodiamond masked reactive ion etching process” is demonstrated for fabricating vertically aligned diamond-graphite hybrid (DGH) nanorod arrays. The DGH nanorod arrays possess superior field electron emission (FEE) behavior with a low turn-on field, long lifetime stability, and large field enhancement factor. Such an enhanced FEE is attributed to the nanocomposite nature of theDGHnanorods, which contain sp(2)-graphitic phases in the boundaries of nano-sized diamond grains. The simplicity in the nanorod fabrication process renders the DGH nanorods of greater potential for the applications as cathodes in field emission displays and microplasma display devices. (C) 2017 Author(s). All article content, except where otherwise noted, is licensed under a Creative Commons Attribution (CC BY) license. |
Address |
|
Corporate Author |
|
Thesis |
|
Publisher |
|
Place of Publication |
|
Editor |
|
Language |
|
Wos |
000404623000002 |
Publication Date |
2017-06-08 |
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
Series Volume |
|
Series Issue |
|
Edition |
|
ISSN |
2166-532x |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
Impact Factor |
4.335 |
Times cited |
16 |
Open Access |
|
Notes |
The authors would like to thank the Methusalem “NANO” network for financial support and Mr. B. Ruttens and Professor Jan D'Haen for technical and experimental assistance. K.J. Sankaran is a Postdoctoral Fellow of the Research Foundation-Flanders (FWO). |
Approved |
Most recent IF: 4.335 |
Call Number |
UA @ admin @ c:irua:152633 |
Serial |
5369 |
Permanent link to this record |