“Structures in textured Cu-Al-Ni shape memory thin films grown by sputtering”. Espinoza Torres C, Condó, AM, Haberkorn N, Zelaya E, Schryvers D, Guimpel J, Lovey FC, Materials characterization 96, 256 (2014). http://doi.org/10.1016/j.matchar.2014.08.005
Abstract: The structure and texture formation in CuAlNi thin films of different thicknesses (1 μm to 5 μm) grown by DC magnetron sputtering without any intentional heating of the substrate are reported. The as-grown films present grains with an average size of 20 nm. The films with thickness of 1 μm have a single metastable phase with a hexagonal structure and are textured with planes (0002) parallel to the plane of the films. It was observed that thicker films present phase coexistence between metastable hexagonal and body centered cubic structures with a gradual increment of the body centered cubic phase fraction. The films with thickness of 5 μm are textured with planes (0002) and View the MathML source101¯0 in the hexagonal structure, whereas in the body centered cubic structure the films are textured with {110} planes parallel to the plane of the films. This fact can be associated with self-heating of the substrate during the growth of the films and with the relative stability of the metastable phases. Free standing films annealed in a second step (1123 K for 1 h) present austenitic phase with L21 structure and sub-micrometric grains textured with {220}L21 planes parallel to the plane of the films. The martensitic transformation temperature was determined from the analysis of resistance against temperature measurements.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.714
Times cited: 9
DOI: 10.1016/j.matchar.2014.08.005
|
|
|
“Structures of three polymorphs of the complex oxide K5Yb(MoO4)4”. Morozov VA, Lazoryak BI, Lebedev OI, Amelinckx S, Van Tendeloo G, Journal of solid state chemistry 176, 76 (2003). http://doi.org/10.1016/S0022-4596(03)00350-5
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 8
DOI: 10.1016/S0022-4596(03)00350-5
|
|
|
“Study and modeling of the Solid Electrolyte Interphase behavior on nano-silicon anodes by Electrochemical Impedance Spectroscopy”. Radvanyi E, Van Havenbergh K, Porcher W, Jouanneau S, Bridel J-S, Put S, Franger S, Electrochimica acta 137, 751 (2014). http://doi.org/10.1016/j.electacta.2014.06.069
Abstract: The instability of the Solid Electrolyte Interphase (SEI) at the surface of nano-silicon electrodes has been recognized as one of the key issues to explain the rapid capacity fading of theses electrodes. In this paper, two distinct Si-based systems are studied by using Electrochemical Impedance Spectroscopy (EIS). First, several EIS spectra are recorded along the second electrochemical cycle. Although the active material, the electrode formulation, and the experimental conditions are different for the two systems, the same phenomena are observed in both cases: (i) the SEI deposit around 50 kHz, (ii) the charge transfer (CT) with a characteristic frequency varying from 300 to 1 500 Hz, and (iii) an inductive loop at ∼1 Hz which appears only when the potential of the electrode is below 0.35 V vs Li. As the latter has never been reported for Si-based electrodes, the second step of the work consists in understanding this phenomenon. Thanks to the results obtained in a set of several complementary experiments, we finally attribute the inductive loop to the constant formation/deposition of SEI products, in competition with the CT process. In addition, we propose a mechanism for this specific phenomenon and the equivalent circuit to fit the recorded EIS spectra.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.798
Times cited: 36
DOI: 10.1016/j.electacta.2014.06.069
|
|
|
“The study of carbon nanotubes produced by catalytic method”. Ivanov V, Nagy JB, Lambin P, Lucas A, Zhang XB, Zhang XF, Bernaerts D, Van Tendeloo G, Amelinckx S, van Landuyt J, Chemical physics letters 223, 329 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.897
Times cited: 405
|
|
|
“Study of changes in composition and EELS ionization edges upon Ni4Ti3 precipitation in a NiTi alloy”. Yang Z, Schryvers D, Micron 37, 503 (2006). http://doi.org/10.1016/j.micron.2005.08.002
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.98
Times cited: 10
DOI: 10.1016/j.micron.2005.08.002
|
|
|
“Study of changes in L32 EELS ionisation edges upon formation of Ni-based intermetallic compounds”. Potapov PL, Kulkova SE, Schryvers D, Journal of microscopy 210, 102 (2003). http://doi.org/10.1046/j.1365-2818.2003.01176.x
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.692
Times cited: 11
DOI: 10.1046/j.1365-2818.2003.01176.x
|
|
|
“The study of partially ordered 11/20 alloys by HREM”. De Meulenaere P, Van Tendeloo G, van Landuyt J, Microscopy research and technique 25, 169 (1993). http://doi.org/10.1002/jemt.1070250208
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.154
DOI: 10.1002/jemt.1070250208
|
|
|
“Study of ramp-type Josephson junctions by HREM”. Verbist K, Lebedev OI, Van Tendeloo G, Verhoeven MAJ, Rijnders AJHM, Blank DHA, Electronic Applications, Vol 2: Large Scale And Power Applications , 49 (1997)
Abstract: Structural aspects of ramp-type Josephson junctions based on REBa2Cu3O7-delta high-T-c superconductors, are investigated by cross-section transmission electron microscopy and results related to fabrication process or physical properties. The barrier layer material is PrBa2Cu3-xGaxO7-delta. The ramp-geometry depends on the etching conditions. High levels of Ga doping (x>0.7) influence the microstructure of the barrier layer thereby changing the junctions properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“A study of the domain structure of epitaxial (La-Ca)MnO3 films by high-resolution transmission electron microscopy”. Lebedev OI, Van Tendeloo G, Abakumov AM, Amelinckx S, Leibold B, Habermeier H-U, Philosophical magazine: A: physics of condensed matter: defects and mechanical properties 79, 1461 (1999). http://doi.org/10.1080/01418619908210372
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 27
DOI: 10.1080/01418619908210372
|
|
|
“Study of the interaction between copper and carbon nanotubes”. Bittencourt C, Ke X, Van Tendeloo G, Thiess S, Drube W, Ghijsen J, Ewels CP, Chemical physics letters 535, 80 (2012). http://doi.org/10.1016/j.cplett.2012.03.045
Abstract: Copper deposited by thermal evaporation onto pristine and oxygen plasma treated carbon nanotubes (CNTs) diffuse over the CNT surface, coalescing and forming crystalline islands. The nucleation sites of the islands are preferentially defects, and more homogeneous island dispersion was observed at the CNT oxygen functionalized surface. The presence of weakly bound oxygen atoms at the CNT surface induces the formation of CuO bonds at the Cu/CNT interface, as described through density functional calculations. Exposure to air allows further oxidation to facetted crystalline Cu2O. Oxygen plasma pre-treatment represents a promising route for homogenous disperse Cu2O nanoparticle decoration of CNTs.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.815
Times cited: 27
DOI: 10.1016/j.cplett.2012.03.045
|
|
|
“Study of the interface between rhodium and carbon nanotubes”. Suarez-Martinez I, Ewels CP, Ke X, Van Tendeloo G, Thiess S, Drube W, Felten A, Pireaux J-J, Ghijsen J, Bittencourt C, ACS nano 4, 1680 (2010). http://doi.org/10.1021/nn9015955
Abstract: X-ray photoelectron spectroscopy at 3.5 keV photon energy, in combination with high-resolution transmission electron microscopy, is used to follow the formation of the interface between rhodium and carbon nanotubes. Rh nucleates at defect sites, whether initially present or induced by oxygen-plasma treatment. More uniform Rh cluster dispersion is observed on plasma-treated CNTs. Experimental results are compared to DFT calculations of small Rh clusters on pristine and defective graphene. While Rh interacts as strongly with the carbon as Ti, it is less sensitive to the presence of oxygen, suggesting it as a good candidate for nanotube contacts.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 26
DOI: 10.1021/nn9015955
|
|
|
“Study of the packing of double-walled carbon nanotubes into bundles by transmission electron microscopy and electron diffraction”. Colomer J-F, Henrard L, Van Tendeloo G, Lucas A, Lambin P, Journal of materials chemistry 14, 603 (2004). http://doi.org/10.1039/b311551h
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 27
DOI: 10.1039/b311551h
|
|
|
“Sub-nanometer free electrons with topological charge”. Schattschneider P, Stöger-Pollach M, Löffler S, Steiger-Thirsfeld A, Hell J, Verbeeck J, Ultramicroscopy 115, 21 (2012). http://doi.org/10.1016/j.ultramic.2012.01.010
Abstract: The holographic mask technique is used to create freely moving electrons with quantized angular momentum. With electron optical elements they can be focused to vortices with diameters below the nanometer range. The understanding of these vortex beams is important for many applications. Here, we produce electron vortex beams and compare them to a theory of electrons with topological charge. The experimental results show excellent agreement with simulations. As an immediate application, fundamental experimental parameters like spherical aberration and partial coherence are determined. (C) 2012 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 24
DOI: 10.1016/j.ultramic.2012.01.010
|
|
|
“Substitution of mercury for thallium in the 2223 cuprate: the 130K superconductor Tl1.6Hg0.4Ba2Cu3O10-x”. Goutenoire F, Maignan A, Van Tendeloo G, Martin C, Michel C, Hervieu M, Raveau B, Solid state communications 90, 47 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.897
Times cited: 16
|
|
|
“Substitutional phosphorus incorporation in nanocrystalline CVD diamond thin films”. Janssen W, Turner S, Sakr G, Jomard F, Barjon J, Degutis G, Lu YG, D'Haen J, Hardy A, Bael MV, Verbeeck J, Van Tendeloo G, Haenen K, Physica status solidi: rapid research letters 8, 705 (2014). http://doi.org/10.1002/pssr.201409235
Abstract: Nanocrystalline diamond (NCD) thin films were produced by chemical vapor deposition (CVD) and doped by the addition of phosphine to the gas mixture. The characterization of the films focused on probing the incorporation and distribution of the phosphorus (P) dopants. Electron microscopy evaluated the overall film morphology and revealed the interior structure of the nanosized grains. The homogeneous films with distinct diamond grains featured a notably low sp(2):sp(3)-ratio as confirmed by Raman spectroscopy. High resolution spectroscopy methods demonstrated a homogeneous P-incorporation, both in-depth and in-plane. The P concentration in the films was determined to be in the order of 10(19) cm(-3) with a significant fraction integrated at substitutional donor sites. (C) 2014 WILEY-VCH Verlag GmbH Co. KGaA, Weinheim
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.032
Times cited: 20
DOI: 10.1002/pssr.201409235
|
|
|
“Superconducting single-phase Sr1-xLaxCuO2 thin films with improved crystallinity grown by pulsed laser deposition”. Leca V, Blank DHA, Rijnders G, Bals S, Van Tendeloo G, Applied physics letters 89 (2006). http://doi.org/10.1063/1.2339840
Abstract: Sr1-xLaxCuO2-delta (x=0.10-0.20) thin films exhibiting an oxygen-deficient 2 root 2a(p)x2 root a(p) x c structure (a(p) and c represent the cell parameters of the perovskite subcell) were epitaxially grown by means of pulsed laser deposition in low-pressure oxygen ambient. (001) KTaO3 and (001) SrTiO3 single crystals were used as substrates, with BaTiO3 as buffer layer. The Sr1-xLaxCuO2-delta films were oxidized during cooling down in order to yield the infinite-layer-type structure. By applying this method, high quality single-phase Sr1-xLaxCuO2 thin films could be obtained for 0.10 <= x <= 0.175 doping range. The films grown on BaTiO3/KTaO3 show superconductivity for 0.15 <= x <= 0.175 with optimum doping at x=0.15, in contrast with previously reported data. (c) 2006 American Institute of Physics.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 32
DOI: 10.1063/1.2339840
|
|
|
“Superconductivity and microstructure of YSr2Cu3O6.875”. Lebedev OI, Van Tendeloo G, Licci F, Gilioli E, Gauzzi A, Prodi A, Marezio M, Physical review : B : condensed matter and materials physics 66, 132510 (2002). http://doi.org/10.1103/PhysRevB.66.132510
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 9
DOI: 10.1103/PhysRevB.66.132510
|
|
|
“Superconductivity up to 110K in the 1212-Hg based cuprate Nd1-xCaxBa2Hg1-xCu2+xO6+y”. Maignan A, Michel C, Van Tendeloo G, Hervieu M, Raveau B, Physica: C : superconductivity 216, 1 (1993)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.942
Times cited: 32
|
|
|
“Supercooled molecular liquids and the glassy phases of chemically bonded N, P, As, Si and Ge”. Matthai CC, March NH, Lamoen D, Physics and chemistry of liquids 47, 607 (2009). http://doi.org/10.1080/00319100903148553
Abstract: Glassy phases which have insulating character exist for a variety of monatomic species. By contrast, until recently, it has been possible to make bulk metallic glasses (BMG) by vitrification only for multicomponent systems. After a relatively brief summary on supercooling of a few molecular liquids, we review some of the recently reported results on molecular assemblies of the series N, P, As and amorphous Si and Ge. Based on these results, we suggest that the transition metals with their directional bonding might be suitable candidates for the production of BMG by vitrification.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.145
Times cited: 1
DOI: 10.1080/00319100903148553
|
|
|
“Superlattice variants in Sr2CuO2(CO3): an electron microscopy study”. Milat O, Van Tendeloo G, van Landuyt J, Amelinckx S, Acta crystallographica: section A: foundations of crystallography 49, 357 (1993)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.307
|
|
|
“The superlattices in high Tc superconducting cuprates”. Milat O, Krekels T, Van Tendeloo G, Amelinckx S, Physica: C : superconductivity 235/240, 729 (1994). http://doi.org/10.1016/0921-4534(94)91589-X
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.942
DOI: 10.1016/0921-4534(94)91589-X
|
|
|
“Superspace crystallography : a key to the chemistry and properties”. Pinheiro CB, Abakumov AM, IUCrJ 2, 137 (2015). http://doi.org/10.1107/S2052252514023550
Abstract: An overview is given of the recent advances in the field of modulated molecular and inorganic crystals with an emphasis on the links between incommensurability, intermolecular and interatomic interactions and, wherever possible, the properties of the materials. The importance of detailed knowledge on the modulated structure for understanding the crystal chemistry and the functional properties of modulated phases is shown using selected examples of incommensurate modulations in organic molecular compounds and inorganic complex oxides.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.793
Times cited: 15
DOI: 10.1107/S2052252514023550
|
|
|
“Superspace description, crystal structures, and electric conductiof the Ba4In6-xMgxO13-x/2 solid solutions”. Abakumov AM, Rossell MD, Gutnikova OY, Drozhzhin OA, Leonova LS, Dobrovolsky YA, Istomin SY, Van Tendeloo G, Antipov EV, Chemistry of materials 20, 4457 (2008). http://doi.org/10.1021/cm8004216
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 15
DOI: 10.1021/cm8004216
|
|
|
“Superstructure and structural variants in Sr2CuO2(CO3)”. Milat O, Van Tendeloo G, Amelinckx S, Babu TGN, Greaves C, Journal of solid state chemistry 109, 5 (1994). http://doi.org/10.1006/jssc.1994.1063
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 11
DOI: 10.1006/jssc.1994.1063
|
|
|
“The superstructure and superconductivity of Ru1222 based RuSr2Gd2-x-yYyCexCu2O10-\delta compounds”. Tan H, Lebedev OI, McLaughlin AC, Van Tendeloo G, Superconductor science and technology 23, 115013 (2010). http://doi.org/10.1088/0953-2048/23/11/115013
Abstract: For the first time, the local structure and physical properties of Ru1222 based compounds (RuSr(2)Gd(1.4)Ce(0.6)Cu(2)O(10-delta) and RuSr(2)Gd(1.8-x)Y(0.2)CexCu(2)O(10) (x = 0.90-0.55)) have been investigated and analyzed together on the very same compounds. The Ru1222 superstructure was confirmed by TEM at a local scale and was suggested to have an orthorhombic symmetry with space group Aba2 and lattice parameters a(s) similar or equal to root 2a, b(s) similar or equal to root 2a and c(s) = c. This new Ru1222 superstructure distortion from tetragonal symmetry is proposed to have a positive correlation with the superconductivity variation of these compounds. The more the distortion towards orthorhombic symmetry, the higher the critical superconducting temperature these compounds can achieve. The T(c)(0) of RuSr(2)Gd(1.8-x)Y(0.2)Ce(x)Cu(2)O(10-delta) (x = 0.85-0.55) increases monotonically from 4 to 16 K when x decreases from 0.85 to 0.70, then RuSr(2)Gd(2)Cu(2)O(8) defects emerge and the T(c) decreases with decreasing x. Ru1212 defects are observed to intergrow epitaxially with the Ru1222 structure as lamellas along the c-axis in RuSr(2)Gd(1.4)Ce(0.6)Cu(2)O(10-delta). Although Ru1212 is a superconductor, the intergrowth severely restrains its superconductivity.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 1
DOI: 10.1088/0953-2048/23/11/115013
|
|
|
“Suppression of modulations in fluorinated Bi-2201 phases”. Hadermann J, Khasanova NR, Van Tendeloo G, Abakumov AM, Rozova MG, Alekseeva AM, Antipov EV, Journal of solid state chemistry 156, 445 (2001). http://doi.org/10.1006/jssc.2000.9020
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 8
DOI: 10.1006/jssc.2000.9020
|
|
|
“Suppression of superconductivity in Hg-1223 and Hg-1234 by partial replacement of Hg by carbon”. Kopnin EM, Antipov EV, Capponi JJ, Bordet P, Chaillout C, de Brion S, Marezio M, Bobylev AP, Van Tendeloo G, Physica: C : superconductivity 243, 222 (1995). http://doi.org/10.1016/0921-4534(95)00010-0
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.942
Times cited: 22
DOI: 10.1016/0921-4534(95)00010-0
|
|
|
“Surface chemistry and properties of ozone-purified detonation nanodiamonds”. Shenderova O, Koscheev A, Zaripov N, Petrov I, Skryabin Y, Detkov P, Turner S, Van Tendeloo G, The journal of physical chemistry: C : nanomaterials and interfaces 115, 9827 (2011). http://doi.org/10.1021/jp1102466
Abstract: Nanodiamond from ozone purification (NDO) demonstrates very distinctive properties within the class of detonation nanodiamonds, namely very high acidity and high colloidal stability in a broad pH range. To understand the origin of these unusual properties of NDO, the nature of the surface functional groups formed during detonation soot oxidation by ozone needs to be revealed. In this work, thermal desorption mass spectrometry (TDMS) and IR spectroscopy were used for the identification of surface groups and it was concluded that carboxylic anhydride groups prevail on the NDO surface. On the basis of the temperature profiles of the desorbed volatile products and their mass balance, it is hypothesized that decomposition of carboxylic anhydride groups from NDO during heating proceeds by two different mechanisms. Other distinctive features of NDO in comparison with air-treated nanodiamond are also reported.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 105
DOI: 10.1021/jp1102466
|
|
|
“Surface enhanced Raman scattering of silver sensitized cobalt nanoparticles in metaldielectric nanocomposites”. Margueritat J, Gonzalo J, Afonso CN, Hörmann U, Van Tendeloo G, Mlayah A, Murray DB, Saviot L, Zhou Y, Hong MH, Luk'yanchuk BS, Nanotechnology 19, 375701 (2008). http://doi.org/10.1088/0957-4484/19/37/375701
Abstract: We report the preparation of a new type of nanocomposite containing cobalt and silver nanoparticles organized in parallel layers with a well controlled separation. This arrangement allows the observation of an enhanced low-frequency Raman signal at the vibration frequency of cobalt nanoparticles excited through the surface plasmons of silver nanoparticles. Numerical simulations of the electric field confirm the emergence of hot spots when the separation between silver and cobalt nanoparticles is small enough.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.44
Times cited: 11
DOI: 10.1088/0957-4484/19/37/375701
|
|
|
“Swift heavy ion irradiation of Cu-Zn-Al and Cu-Al-Ni alloys”. Zelaya E, Tolley A, Condo AM, Schumacher G, Journal of physics : condensed matter 21, 185009 (2009). http://doi.org/10.1088/0953-8984/21/18/185009
Abstract: The effects produced by swift heavy ions in the martensitic (18R) and austenitic phase (beta) of Cu based shape memory alloys were characterized. Single crystal samples with a surface normal close to [210](18R) and [001](beta) were irradiated with 200 MeV of Kr(15+), 230 MeV of Xe(15+), 350 and 600 MeV of Au(26+) and Au(29+). Changes in the microstructure were studied with transmission electron microscopy (TEM) and high resolution transmission electron microscopy (HRTEM). It was found that swift heavy ion irradiation induced nanometer sized defects in the 18R martensitic phase. In contrast, a hexagonal close-packed phase formed on the irradiated surface of beta phase samples. HRTEM images of the nanometer sized defects observed in the 18R martensitic phase were compared with computer simulated images in order to interpret the origin of the observed contrast. The best agreement was obtained when the defects were assumed to consist of local composition modulations.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.649
Times cited: 8
DOI: 10.1088/0953-8984/21/18/185009
|
|