“Defects in high-dose oxygen implanted silicon : a TEM study”. Deveirman A, van Landuyt J, Vanhellemont J, Maes HE, Yallup K, Vacuum: the international journal and abstracting service for vacuum science and technology
T2 –, 1ST SIOMX WORKSHOP ( SEPARATION BY IMPLANTATION OF OXYGEN ) ( SWI-88 ), NOV 07-08, 1988, UNIV SURREY, GUILDFORD, ENGLAND 42, 367 (1991). http://doi.org/10.1016/0042-207X(91)90055-N
Abstract: Results are discussed of a transmission electron microscopy study of high-dose oxygen implanted silicon. In addition to the general high temperature (> 1200-degrees-C) annealing treatments also annealings at 'low' temperatures (1000-1100-degrees-C) were performed in order to slow down the precipitate and defect reactions. The observed dissolution of the oxide precipitates during prolonged high temperature annealing is explained by critical radius considerations. Threading dislocations are the remaining lattice defects in the silicon overlayer and cannot be removed by further annealing. Low temperature annealing results in the formation and subsequent unfaulting of extrinsic stacking fault loops below the buried oxide layer.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.858
Times cited: 4
DOI: 10.1016/0042-207X(91)90055-N
|
|
|
“Density functional theory calculations of energy-loss carbon near-edge spectra of small diameter armchair and zigzag nanotubes: core-hole, curvature, and momentum-transfer orientation effects”. Titantah JT, Jorissen K, Lamoen D, Physical review : B : condensed matter and materials physics 69, 125406 (2004). http://doi.org/10.1103/PhysRevB.69.125406
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 28
DOI: 10.1103/PhysRevB.69.125406
|
|
|
“Density-functional theory calculations of the electron energy-loss near-edge structure of Li-intercalated graphite”. Titantah JT, Lamoen D, Schowalter M, Rosenauer A, Carbon 47, 2501 (2009). http://doi.org/10.1016/j.carbon.2009.05.002
Abstract: We have studied the structural and electronic properties of lithium-intercalated graphite (LIG) for various Li content. Atomic relaxation shows that Li above the center of the carbon hexagon in a AAAA stacked graphite is the only stable Li configuration in stage 1 intercalated graphite. Lithium and Carbon 1s energy-loss near-edge structure (ELNES) calculations are performed on the Li-intercalated graphite using the core-excited density-functional theory formulation. Several features of the Li 1s ELNES are correlated with reported experimental features. The ELNES spectra of Li is found to be electron beam orientation sensitive and this property is used to assign the origin of the various Li 1s ELNES features. Information about core-hole screening by the valence electrons and charge transfer in the LIG systems is obtained from the C 1s ELNES and valence charge density difference calculations, respectively.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.337
Times cited: 12
DOI: 10.1016/j.carbon.2009.05.002
|
|
|
“Design and synthesis of hierarchical materials from ordered zeolitic building units”. Kirschhock CEA, Kremer SPB, Vermant J, Van Tendeloo G, Jacobs PA, Martens JA, Chemistry: a European journal 11, 4306 (2005). http://doi.org/10.1002/chem.200401329
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.317
Times cited: 93
DOI: 10.1002/chem.200401329
|
|
|
“Design of Ru-zeolites for hydrogen-free production of conjugated linoleic acid”. Philippaerts A, Goossens S, Vermandel W, Tromp M, Turner S, Geboers J, Van Tendeloo G, Jacobs PA, Sels BF, Chemsuschem 4, 757 (2011). http://doi.org/10.1002/cssc.201100015
Abstract: While conjugated vegetable oils are currently used as additives in the drying agents of oils and paints, they are also attractive molecules for making bio-plastics. Moreover, conjugated oils will soon be accepted as nutritional additives for functional food products. While current manufacture of conjugated vegetable oils or conjugated linoleic acids (CLAs) uses a homogeneous base as isomerisation catalyst, a heterogeneous alternative is not available today. This contribution presents the direct production of CLAs over Ru supported on different zeolites, varying in topology (ZSM-5, BETA, Y), Si/Al ratio and countercation (H+, Na+, Cs+). Ru/Cs-USY, with a Si/Al ratio of 40, was identified as the most active and selective catalyst for isomerisation of methyl linoleate (cis-9,cis-12 (C18:2)) to CLA at 165 °C. Interestingly, no hydrogen pre-treatment of the catalyst or addition of hydrogen donors is required to achieve industrially relevant isomerisation productivities, namely, 0.7 g of CLA per litre of solvent per minute. Moreover, the biologically most active CLA isomers, namely, cis-9,trans-11, trans-10,cis-12 and trans-9,trans-11, were the main products, especially at low catalyst concentrations. Ex situ physicochemical characterisation with CO chemisorption, extended X-ray absorption fine structure measurements, transmission electron microscopy analysis, and temperature-programmed oxidation reveals the presence of highly dispersed RuO2 species in Ru/Cs-USY(40).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 7.226
Times cited: 24
DOI: 10.1002/cssc.201100015
|
|
|
“Design of zeolite by inverse sigma transformation”. Verheyen E, Joos L, Van Havenbergh K, Breynaert E, Kasian N, Gobechiya E, Houthoofd K, Martineau C, Hinterstein M, Taulelle F, Van Speybroeck V, Waroquier M, Bals S, Van Tendeloo G, Kirschhock CEA, Martens JA;, Nature materials 11, 1059 (2012). http://doi.org/10.1038/NMAT3455
Abstract: Although the search for new zeolites has traditionally been based on trial and error, more rational methods are now available. The theoretical concept of inverse transformation of a zeolite framework to generate a new structure by removal of a layer of framework atoms and contraction has for the first time been achieved experimentally. The reactivity of framework germanium atoms in strong mineral acid was exploited to selectively remove germanium-containing four-ring units from an UTL type germanosilicate zeolite. Annealing of the leached framework through calcination led to the new all-silica COK-14 zeolite with intersecting 12- and 10-membered ring channel systems. An intermediate stage of this inverse transformation with dislodged germanate four-rings still residing in the pores could be demonstrated. Inverse transformation involving elimination of germanium-containing structural units opens perspectives for the synthesis of many more zeolites.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 39.737
Times cited: 140
DOI: 10.1038/NMAT3455
|
|
|
“Designed multifunctional nanocomposites for biomedical applications”. Yiu HHP, Niu H-jun, Biermans E, Van Tendeloo G, Rosseinsky MJ, Advanced functional materials 20, 1599 (2010). http://doi.org/10.1002/adfm.200902117
Abstract: The assembly of multifunctional nanocomposite materials is demonstrated by exploiting the molecular sieving property of SBA-16 nanoporous silica and using it as a template material. The cages of the pore networks are used to host iron oxide magnetic nanoparticles, leaving a pore volume of 0.29 cm3 g-1 accessible for drug storage. This iron oxide-silica nanocomposite is then functionalized with amine groups. Finally the outside of the particle is decorated with antibodies. Since the size of many protein molecules, including that of antibodies, is too large to enter the pore system of SBA-16, the amine groups inside the pores are preserved for drug binding. This is proven using a fluorescent protein, fluorescein-isothiocyanate-labeled bovine serum albumin (FITC-BSA), with the unreacted amine groups inside the pores dyed with rhodamine B isothiocyanate (RITC). The resulting nanocomposite material offers a dual-targeting drug delivery mechanism, i.e., magnetic and antibody-targeting, while the functionalization approach is extendable to other applications, e.g., fluorescence-magnetic dual-imaging diagnosis.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 56
DOI: 10.1002/adfm.200902117
|
|
|
“Determination of size, morphology, and nitrogen impurity location in treated detonation nanodiamond by transmission electron microscopy”. Turner S, Lebedev OI, Shenderova O, Vlasov II, Verbeeck J, Van Tendeloo G, Advanced functional materials 19, 2116 (2009). http://doi.org/10.1002/adfm.200801872
Abstract: Size, morphology, and nitrogen impurity location, all of which are all thought to be related to the luminescent properties of detonation nanodiamonds, are determined in several detonation nanodiamond samples using a combination of transmission electron microscopy techniques. Results obtained from annealed and cleaned detonation nanodiamond samples are compared to results from conventionally purified detonation nanodiamond. Detailed electron energy loss spectroscopy combined with model-based quantification provides direct evidence for the sp3 like embedding of nitrogen impurities into the diamond cores of all the studied nanodiamond samples. Simultaneously, the structure and morphology of the cleaned detonation nanodiamond particles are studied using high resolution transmission electron microscopy. The results show that the size and morphology of detonation nanodiamonds can be modified by temperature treatment and that by applying a special cleaning procedure after temperature treatment, nanodiamond particles with clean facets almost free from sp2 carbon can be prepared. These clean facets are clear evidence that nanodiamond cores are not necessarily in coexistence with a graphitic shell of non-diamond carbon.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 100
DOI: 10.1002/adfm.200801872
|
|
|
“Determination of the electron effective band mass in amorphous carbon from density-functional theory calculations”. Titantah JT, Lamoen D, Physical review : B : condensed matter and materials physics 70, 033101 (2004). http://doi.org/10.1103/PhysRevB.70.033101
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 24
DOI: 10.1103/PhysRevB.70.033101
|
|
|
“The determination of the interface structure between ionocovalent compounds: the general case study of the Al2O3/ZrO2 large mis-fit system”. Trolliard G, Benmechta R, Mercurio D, Lebedev OI, Journal of materials chemistry 16, 3640 (2006). http://doi.org/10.1039/b604232e
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 6
DOI: 10.1039/b604232e
|
|
|
“The deviation from parallel shear flow as an indicator of linear eddy-viscosity model inaccuracy”. Gorlé, C, Larsson J, Emory M, Iaccarino G, Physics of fluids 26, 051702 (2014). http://doi.org/10.1063/1.4876577
Abstract: A marker function designed to indicate in which regions of a generic flow field the results from linear eddy-viscosity turbulence models are plausibly inaccurate is introduced. The marker is defined to identify regions that deviate from parallel shear flow. For two different flow fields it is shown that these regions largely coincide with regions where the prediction of the Reynolds stress divergence is inaccurate. The marker therefore offers a guideline for interpreting results obtained from Reynolds-averaged Navier-Stokes simulations and provides a basis for the further development of turbulence model-form uncertainty quantification methods. (C) 2014 AIP Publishing LLC.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.232
Times cited: 19
DOI: 10.1063/1.4876577
|
|
|
“Diamond nucleation by carbon transport from buried nanodiamond TiO2 sol-gel composites”. Doenen M, Zhang L, Erni R, Williams OA, Hardy A, van Bael MK, Wagner P, Haenen K, Nesladek M, Van Tendeloo G, Advanced materials 21, 670 (2009). http://doi.org/10.1002/adma.200802305
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 19.791
Times cited: 20
DOI: 10.1002/adma.200802305
|
|
|
“Direct evidence for the existence of multi-walled carbon nanotubes with hexagonal cross-sections”. He Z, Ke X, Bals S, Van Tendeloo G, Carbon 50, 2524 (2012). http://doi.org/10.1016/j.carbon.2012.01.075
Abstract: Carbon nanotubes (CNTs) with a polygonal cross-section have been paid increasing attention since their three-dimensional structure is related to specific physical properties, which are found to be different in comparison to CNTs with a circular cross-section. Here, we report the existence of novel multi-walled CNTs yielding walls with a rounded-hexagonal configuration. This structure was directly confirmed for the first time by both cross-sectional transmission electron microscopy and electron tomography. The morphology of the Fe catalytic particle also exhibits hexagonal characteristics, and is proposed as the origin of the formation of the rounded-hexagonal walls of the CNT. This observation is of great importance with respect to the design of polygonal (such as pentagonal or hexagonal) cross-sectional CNTs. By controlling the morphology of the catalytic nanoparticles it will be possible to grow CNTs with desired electronic and mechanical properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.337
Times cited: 8
DOI: 10.1016/j.carbon.2012.01.075
|
|
|
“Direct evidence of spontaneous quantum dot formation in a thick InGaN epilayer”. Nistor L, Bender H, Vantomme A, Wu MF, van Landuyt J, O'Donnell KP, Martin R, Jacobs K, Moerman I, Applied physics letters 77, 507 (2000). http://doi.org/10.1063/1.127026
Abstract: We report a direct observation of quantum dots formed spontaneously in a thick InGaN epilayer by high resolution transmission electron microscopy. Investigation of a (280 nm thick) In0.22Ga0.78N single layer, emitting in the blue/green spectral region, reveals quantum dots with estimated sizes in the range of 1.5-3 nm. Such sizes are in very good agreement with calculations based on the luminescence spectra of this specimen. (C) 2000 American Institute of Physics. [S0003-6951(00)00930-X].
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 44
DOI: 10.1063/1.127026
|
|
|
“Direct imaging of loaded metal-organic framework materials (metal@MOF-5)”. Turner S, Lebedev OI, Schroeder F, Fischer RA, Van Tendeloo G, Chemistry of materials 20, 5622 (2008). http://doi.org/10.1021/cm801165s
Abstract: We illustrate the potential of advanced transmission electron microscopy for the characterization of a new class of soft porous materials: metal@Zn4O(bdc)3 (metal@MOF-5; bdc = 1,4-benzenedicarboxylate). By combining several electron microscopy techniques (transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM), electron diffraction (ED), high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM), and electron tomography) and by carefully reducing the electron dose to avoid beam damage, it is possible to simultaneously characterize the MOF-5 framework material and the loaded metal nanoparticles. We also demonstrate that electron tomography can be used to accurately determine the position and distribution of the particles within the MOF-5 framework. To demonstrate the implementation of these microscopy techniques and what kind of results can be expected, measurements on gas-phase-loaded metal−organic framework materials Ru@MOF-5 and Pd@MOF-5 are presented.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 112
DOI: 10.1021/cm801165s
|
|
|
“Direct observation of clusters in some FCC alloys by HREM”. De Meulenaere P, Van Tendeloo G, van Landuyt J, Icem 13, 447 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
|
|
“Direct observation of ferrielectricity at ferroelastic domain boundaries in CaTiO3 by electron microscopy”. Van Aert S, Turner S, Delville R, Schryvers D, Van Tendeloo G, Salje EKH, Advanced materials 24, 523 (2012). http://doi.org/10.1002/adma.201103717
Abstract: High-resolution aberration-corrected transmission electron microscopy aided by statistical parameter estimation theory is used to quantify localized displacements at a (110) twin boundary in orthorhombic CaTiO3. The displacements are 36 pm for the Ti atoms and confined to a thin layer. This is the first direct observation of the generation of ferroelectricity by interfaces inside this material which opens the door for domain boundary engineering.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 19.791
Times cited: 150
DOI: 10.1002/adma.201103717
|
|
|
“Direct observation of laser-induced crystallization of a-C : H films”. Nistor LC, van Landuyt J, Ralchenko VG, Kononenko TV, Obraztsova ED, Strelnitsky VE, Applied physics A : materials science &, processing 58, 137 (1994). http://doi.org/10.1007/BF00332170
Abstract: The post-growth modification of diamond-like amorphous hydrogenated carbon a-C:H films by laser treatment has been studied by transmission electron microscopy and Raman spectroscopy. a-C:H films grown on Si substrates by benzene decomposition in a rf glow discharge were irradiated with 15 ns pulses of a KrF-excimer laser with fluences in the ran e of E = 50-700 mJ/cm(2). At fluences below 100 mJ/cm(2) an increase in the number of graphitic clusters and in their ordering was evidenced from Raman spectra, while the film structure remained amorphous according to electron microscopy and electron diffraction observations. At higher fluences the appearance of diamond particles of 2-7 nm size, embedded into the lower crystallized graphitic matrix, was observed and simultaneously a progressive growth of graphite nanocrystals with dimensions from 2 nm to 4 nm was deduced from Raman measurements. The maximum thickness of the crystallized surface layer (approximate to 400 nm) and the degree of laser annealing are limited by the film ablation which starts at E > 250 mJ/cm(2). The laser-treated areas lose their chemical inertness. In particular, chemical etching in chromium acid becomes possible, which may be used for patterning the highly inert carbon films.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 73
DOI: 10.1007/BF00332170
|
|
|
“Direct observation of nanometer-scale pinning sites in (Nd0.33Eu0.20Gd0.47)Ba2Cu3O7-\delta single crystals”. Das P, Koblischka MR, Turner S, Van Tendeloo G, Wolf T, Jirsa M, Hartmann U, Europhysics letters 83, 37005 (2008). http://doi.org/10.1209/0295-5075/83/37005
Abstract: We report on the observation of self-organized stripe-like structures on the as-grown surface and in the bulk of (Nd,Eu,Gd)Ba2Cu3Oy single crystals. The periodicity of the stripes on the surface lies between 500800 nm. These are possibly the growth steps of the crystal. Transmission electron microscopy investigations revealed stripes of periodicity in the range of 2040 nm in the bulk. From electron back scattered diffraction investigations, no crystallographic misorientation due to the nanostripes has been found. Scanning tunneling spectroscopic experiments revealed nonsuperconducting regions, running along twin directions, which presumably constitute strong pinning sites.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.957
Times cited: 5
DOI: 10.1209/0295-5075/83/37005
|
|
|
“Direct room-temperature synthesis of methyl-functionalized Ti-MCM-41 nanoparticles and their catalytic performance in epoxidation”. Lin K, Pescarmona PP, Houthoofd K, Liang D, Van Tendeloo G, Jacobs PA, Journal of catalysis 263, 75 (2009). http://doi.org/10.1016/j.jcat.2009.01.013
Abstract: Methyl-functionalized Ti-MCM-41 nanoparticles with a size of 80 to 160 nm (Me-Ti-MCM-41 NP) were directly prepared via a dilute solution route by the co-condensation of tetraethoxysilane and methylalkoxysilanes in sodium hydroxide medium at room temperature. The characterization results showed the existence of ordered hexagonal mesoporous structure and tetrahedral Ti species in the nanoparticles. In the epoxidation of cyclohexene with tert-butyl hydroperoxide and aqueous H2O2, Me-Ti-MCM-41 NP samples displayed higher turnover frequencies (TOFs) for cyclohexene and initial reaction rates compared to Ti-MCM-41 and methyl-functionalized Ti-MCM-41 with normal particle size and to non-functionalized Ti-MCM-41 nanoparticles. Simultaneously, a higher selectivity for cyclohexene epoxide was observed in the case of aqueous H2O2, suggesting that the hydrolysis of cyclohexene epoxide with water is reduced on Me-Ti-MCM-41 NP samples. The improved catalytic behavior of Me-Ti-MCM-41 NP is discussed both in terms of the nanosize and methylation of the surface of the catalyst particles. The regeneration of Me-Ti-MCM-41 NP with tert-butyl hydroperoxide solution was evaluated via washing and calcination approaches.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.844
Times cited: 89
DOI: 10.1016/j.jcat.2009.01.013
|
|
|
“Direct space structure solution from precession electron diffraction data: resolving heavy and light scatterers in Pb13Mn9O25”. Hadermann J, Abakumov AM, Tsirlin AA, Filonenko VP, Gonnissen J, Tan H, Verbeeck J, Gemmi M, Antipov EV, Rosner H, Ultramicroscopy 110, 881 (2010). http://doi.org/10.1016/j.ultramic.2010.03.012
Abstract: The crystal structure of a novel compound Pb13Mn9O25 has been determined through a direct space structure solution with a Monte-Carlo-based global optimization using precession electron diffraction data (a=14.177(3) Å, c=3.9320(7) Å, SG P4/m, RF=0.239) and compositional information obtained from energy dispersive X-ray analysis and electron energy loss spectroscopy. This allowed to obtain a reliable structural model even despite the simultaneous presence of both heavy (Pb) and light (O) scattering elements and to validate the accuracy of the electron diffraction-based structure refinement. This provides an important benchmark for further studies of complex structural problems with electron diffraction techniques. Pb13Mn9O25 has an anion- and cation-deficient perovskite-based structure with the A-positions filled by the Pb atoms and 9/13 of the B positions filled by the Mn atoms in an ordered manner. MnO6 octahedra and MnO5 tetragonal pyramids form a network by sharing common corners. Tunnels are formed in the network due to an ordered arrangement of vacancies at the B-sublattice. These tunnels provide sufficient space for localization of the lone 6s2 electron pairs of the Pb2+ cations, suggested as the driving force for the structural difference between Pb13Mn9O25 and the manganites of alkali-earth elements with similar compositions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 24
DOI: 10.1016/j.ultramic.2010.03.012
|
|
|
“Direct structural and spectroscopic investigation of ultrathin films of tetragonal CuO: Six-fold coordinated copper”. Samal D, Tan H, Takamura Y, Siemons W, Verbeeck J, Van Tendeloo G, Arenholz E, Jenkins CA, Rijnders G, Koster G, Europhysics letters 105, 17003 (2014). http://doi.org/10.1209/0295-5075/105/17003
Abstract: Unlike other 3d transition metal monoxides (MnO, FeO, CoO, and NiO), CuO is found in a low-symmetry distorted monoclinic structure rather than the rocksalt structure. We report here of the growth of ultrathin CuO films on SrTiO3 substrates; scanning transmission electron microscopy was used to show the stabilization of a tetragonal rocksalt structure with an elongated c-axis such that c/a similar to 1.34 and the Cu-O-Cu bond angle similar to 180 degrees, pointing to metastable six-fold coordinated Cu. X-ray absorption spectroscopy demonstrates that the hole at the Cu site for the CuO is localized in 3d(x2-y2) orbital unlike the well-studied monoclinic CuO phase. The experimental confirmation of the tetragonal structure of CuO opens up new avenues to explore electronic and magnetic properties of six-fold coordinated Cu. Copyright (C) EPLA, 2014
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.957
Times cited: 15
DOI: 10.1209/0295-5075/105/17003
|
|
|
“Direct visualization of boron dopant distribution and coordination in individual chemical vapor deposition nanocrystalline B-doped diamond grains”. Lu Y-G, Turner S, Verbeeck J, Janssens SD, Wagner P, Haenen K, Van Tendeloo G, Applied physics letters 101, 041907 (2012). http://doi.org/10.1063/1.4738885
Abstract: The boron dopant distribution in individual heavily boron-doped nanocrystalline diamond film grains, with sizes ranging from 100 to 350nm in diameter, has been studied using a combination of high resolution annular dark field scanning transmission electron microscopy and spatially resolved electron energy-loss spectroscopy. Using these tools, the boron distribution and local boron coordination have been determined. Quantification results reveal embedding of B dopants in the diamond lattice, and a preferential enrichment of boron at defective areas and twin boundaries. Coordination mapping reveals a distinct difference in coordination of the B dopants in “pristine” diamond areas and in defective regions. (C) 2012 American Institute of Physics. [http://dx.doi.org/10.1063/1.4738885]
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 59
DOI: 10.1063/1.4738885
|
|
|
“Discovery of a superhard iron tetraboride superconductor”. Gou H, Dubrovinskaia N, Bykova E, Tsirlin AA, Kasinathan D, Schnelle W, Richter A, Merlini M, Hanfland M, Abakumov AM, Batuk D, Van Tendeloo G, Nakajima Y, Kolmogorov AN, Dubrovinsky L;, Physical review letters 111, 157002 (2013). http://doi.org/10.1103/PhysRevLett.111.157002
Abstract: Single crystals of novel orthorhombic (space group Pnnm) iron tetraboride FeB4 were synthesized at pressures above 8 GPa and high temperatures. Magnetic susceptibility and heat capacity measurements demonstrate bulk superconductivity below 2.9 K. The putative isotope effect on the superconducting critical temperature and the analysis of specific heat data indicate that the superconductivity in FeB4 is likely phonon mediated, which is rare for Fe-based superconductors. The discovered iron tetraboride is highly incompressible and has the nanoindentation hardness of 62(5) GPa; thus, it opens a new class of highly desirable materials combining advanced mechanical properties and superconductivity.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.462
Times cited: 127
DOI: 10.1103/PhysRevLett.111.157002
|
|
|
“Dislocation distributions in brown diamond”. Willems B, Martineau PM, Fisher D, van Royen J, Van Tendeloo G, Physica status solidi: A: applied research 203, 3076 (2006). http://doi.org/10.1002/pssa.200671129
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.775
Times cited: 21
DOI: 10.1002/pssa.200671129
|
|
|
“Dislocations and plasticity of experimentally deformed coesite”. Idrissi H, Cordier P, Jacob D, Walte N, European journal of mineralogy 20, 665 (2008). http://doi.org/10.1127/0935-1221/2008/0020-1849
Abstract: Dislocation microstructures have been characterized by transmission electron microscopy in polycrystalline coesite deformed experimentally at 4 GPa, 1200 degrees C. Burgers vectors have been determined by large-angle convergent-beam electron diffraction. Sample orientation was assisted by precession electron diffraction to overcome difficulties arising from pseudo-hexagonal symmetry. The results are explained by using a pseudo-hexagonal setting. We found that most dislocations observed are of the 1/3 < 2 (1) over bar(1) over bar0 > type. No clear glide plane was identified, suggesting that climb is activated under these conditions. This conclusion is supported by the observation of numerous subgrain boundaries. We have also observed some [00011 dislocations. Finally, the C12/cl space group to which coesite belongs being centred, an additional slip system is observed: 1/6[(1) over bar2 (1) over bar3](01 (1) over bar1) (1/2[(1) over bar 10](110) in the monoclinic setting).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.362
Times cited: 5
DOI: 10.1127/0935-1221/2008/0020-1849
|
|
|
“Dislocations in diamond : dissociation into partials and their glide motion”. Blumenau AT, Jones R, Frauenheim T, Willems B, Lebedev OI, Van Tendeloo G, Fisher D, Martineau PM, Physical review : B : condensed matter and materials physics 68, 014115 (2003). http://doi.org/10.1103/PhysRevB.68.014115
Abstract: The dissociation of 60degrees and screw dislocations in diamond is modeled in an approach combining isotropic elasticity theory with ab initio-based tight-binding total-energy calculations. Both dislocations are found to dissociate with a substantial lowering of their line energies. For the 60degrees dislocation, however, an energy barrier to dissociation is found. We investigate the core structure of a screw dislocation distinguishing “shuffle,” “mixed,” and “glide” cores. The latter is found to be the most stable undissociated screw dislocation. Further, the glide motion of 90degrees and 30degrees partials is discussed in terms of a process involving the thermal formation and subsequent migration of kinks along the dislocation line. The calculated activation barriers to dislocation motion show that the 30degrees partial is less mobile than the 90degrees partial. Finally, high-resolution electron microscopy is performed on high-temperature, high-pressure annealed natural brown diamond, allowing the core regions of 60degrees dislocations to be imaged. The majority of dislocations are found to be dissociated. However, in some cases, undissociated 60degrees dislocations were also observed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 39
DOI: 10.1103/PhysRevB.68.014115
|
|
|
“'Disordered' Ba(Mg1/3Ta2/3)O3 and its ordering transition”. Lei CH, Amelinckx S, Van Tendeloo G, Philosophical magazine: A: physics of condensed matter: defects and mechanical properties 82, 2321 (2002). http://doi.org/10.1080/01418610210138969
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 5
DOI: 10.1080/01418610210138969
|
|
|
“Dispersion in the wake of a rectangular building : validation of two Reynolds-averaged Navier-Stokes modelling approaches”. Gorlé, C, van Beeck J, Rambaud P, Boundary-layer meteorology 137, 115 (2010). http://doi.org/10.1007/s10546-010-9521-0
Abstract: When modelling the turbulent dispersion of a passive tracer using Reynolds-averaged Navier-Stokes (RANS) simulations, two different approaches can be used. The first consists of solving a transport equation for a scalar, where the governing parameters are the mean velocity field and the turbulent diffusion coefficient, given by the ratio of the turbulent viscosity and the turbulent Schmidt number Sc (t) . The second approach uses a Lagrangian particle tracking algorithm, where the governing parameters are the mean velocity and the fluctuating velocity field, which is determined from the turbulence kinetic energy and the Lagrangian time T (L) . A comparison between the two approaches and wind-tunnel data for the dispersion in the wake of a rectangular building immersed in a neutral atmospheric boundary layer (ABL) is presented. Particular attention was paid to the influence of turbulence model parameters on the flow and concentration field. In addition, an approach to estimate Sc (t) and T (L) based on the calculated flow field is proposed. The results show that applying modified turbulence model constants to enable correct modelling of the ABL improves the prediction for the velocity and concentration fields when the modification is restricted to the region for which it was derived. The difference between simulated and measured concentrations is smaller than 25% or the uncertainty of the data on 76% of the points when solving the transport equation for a scalar with the proposed formulation for Sc (t) , and on 69% of the points when using the Lagrangian particle tracking with the proposed formulation for T (L) .
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.573
Times cited: 16
DOI: 10.1007/s10546-010-9521-0
|
|
|
“Displacive-replacive phase transformation in a Ni62.5Al37.5 phase studies by HREM and microdiffraction”. Muto S, Merk N, Schryvers D, Tanner LE, Philosophical magazine: B: physics of condensed matter: electronic, optical and magnetic properties 67, 673 (1993). http://doi.org/10.1080/13642819308219316
Abstract: The structure of the metastable Ni2Al phase, which has long been a matter of controversy, has been carefully re-examined by means of high-resolution transmission electron microscopy (HREM) and electron microdiffraction. First, it is concluded that theas-quenched NixAl100-x(60 less-than-or-equal-to x less-than-or-equal-to 65) material already exhibits a partial omega-type collapse in a one-dimensional fashion which and is consistent with the anomalous dip in the phonon dispersion curve. Ni2Al precipitates are formed on annealing by thermal decomposition of the high-temperature NixAl100-xB2 phase and still retain the small omega-type shuffle. The amount of displacement in the well developed Ni2Al phase was estimated to be between 20 and 50% of the ideal omega collapse; this was determined by means of a combined technique of HREM and microdiffraction together with dynamical calculations of HREM images and diffraction intensities.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 16
DOI: 10.1080/13642819308219316
|
|