“Effect of deposition rate on the microstructure of electron beam evaporated nanocrystalline palladium thin films”. Amin-Ahmadi B, Idrissi H, Galceran M, Colla MS, Raskin JP, Pardoen T, Godet S, Schryvers D, Thin solid films : an international journal on the science and technology of thin and thick films 539, 145 (2013). http://doi.org/10.1016/j.tsf.2013.05.083
Abstract: The influence of the deposition rate on the formation of growth twins in nanocrystalline Pd films deposited by electron beam evaporation is investigated using transmission electron microscopy. Statistical measurements prove that twin boundary (TB) density and volume fraction of grains containing twins increase with increasing deposition rate. A clear increase of the dislocation density was observed for the highest deposition rate of 5 Å/s, caused by the increase of the internal stress building up during deposition. Based on crystallographic orientation indexation using transmission electron microscopy, it can be concluded that a {111} crystallographic texture increases with increasing deposition rate even though the {101} crystallographic texture remains dominant. Most of the TBs are fully coherent without any residual dislocations. However, for the highest deposition rate (5 Å/s), the coherency of the TBs decreases significantly as a result of the interaction of lattice dislocations emitted during deposition with the growth TBs. The analysis of the grain boundary character of different Pd films shows that an increasing fraction of high angle grain boundaries with misorientation angles around 5565° leads to a higher potential for twin formation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.879
Times cited: 13
DOI: 10.1016/j.tsf.2013.05.083
|
“Effect of interface evolution on thermal conductivity of vacuum hot pressed SiC/Al composites”. Chen Z, Tan Z, Ji G, Schryvers D, Ouyang Q, Li Z, Advanced engineering materials 17, 1076 (2015). http://doi.org/10.1002/adem.201400412
Abstract: The SiC/Al composites have been fabricated by a vacuum hot pressing (VHP) process in order to study the effect of interface evolution on the global thermal conductivity (TC). By optimizing the VHP parameters of sintering temperature and time, the three different kinds of SiC/Al interface configurations, that is, non-bonded, diffusion-bonded, and reaction-bonded interfaces, are formed and identified by measurement of relative density, X-ray diffraction, scanning and (high-resolution) transmission electron microscopy. The VHPed composite sintered at 655 °C for 60 min is fully dense and presents a tightly-adhered and clean SiC/Al interface at the nanoscale, the ideal diffusion-bonded interface being the most favorable for minimizing interfacial thermal resistance, which in turn results in the highest TC of around 270 W/mK.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.319
Times cited: 9
DOI: 10.1002/adem.201400412
|
“Electron diffraction refinement of the TiNi(Fe) R-phase structure”. Schryvers D, Potapov P, Journal de physique 112, 751 (2003). http://doi.org/10.1051/jp4:2003991
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 7
DOI: 10.1051/jp4:2003991
|
“Electron-diffraction structure refinement of Ni4Ti3 precipitates in Ni52Ti48”. Tirry W, Schryvers D, Jorissen K, Lamoen D, Acta crystallographica: section B: structural science 62, 966 (2006). http://doi.org/10.1107/S0108768106036457
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 30
DOI: 10.1107/S0108768106036457
|
“Electron-energy-loss spectra of NiO”. Dobysheva LV, Potapov PL, Schryvers D, Physical review : B : condensed matter and materials physics 69, 184404 (2004). http://doi.org/10.1103/PhysRevB.69.184404
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 17
DOI: 10.1103/PhysRevB.69.184404
|
“Electron energy-loss spectroscopy and first-principles calculation studies on a Ni-Ti shape memory alloy”. Yang Z, Tirry W, Lamoen D, Kulkova S, Schryvers D, Acta materialia 56, 395 (2008). http://doi.org/10.1016/j.actamat.2007.10.001
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 20
DOI: 10.1016/j.actamat.2007.10.001
|
“Electron energy-loss spectroscopy study of NiTi shape memory alloys”. Yang ZQ, Schryvers D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 481, 214 (2008). http://doi.org/10.1016/j.msea.2006.12.227
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 7
DOI: 10.1016/j.msea.2006.12.227
|
“Electron microscopical investigation of AgBr needle crystals”. Goessens C, Schryvers D, van Landuyt J, Millan A, de Keyzer R, Journal of crystal growth 151, 335 (1995). http://doi.org/10.1016/0022-0248(95)00080-1
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.698
Times cited: 14
DOI: 10.1016/0022-0248(95)00080-1
|
“Electron microscopical investigation of tetrahedral-shaped AgBr microcrystals”. Goessens C, Schryvers D, van Landuyt J, de Keyzer R, Journal of crystal growth 172, 426 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.751
Times cited: 15
|
“Electron microscopy and diffraction study of the composition dependency of the 3R microtwinned martensite in Ni-Al”. Schryvers D, de Saegher B, van Landuyt J, Materials research bulletin 26, 57 (1991)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.288
Times cited: 11
|
“Electron microscopy studies of martensite microstructures”. Schryvers D, Journal de physique: 4 C5, 109 (1997). http://doi.org/10.1051/jp4:1997517
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.1051/jp4:1997517
|
“Electron microscopy study of the formation of Ni5Al3 in a Ni62.5Al37.5 B2 alloy: 1: precipitation and growth”. Schryvers D, Ma Y, Toth L, Tanner LE, Acta metallurgica et materialia 43, 4045 (1995). http://doi.org/10.1016/0956-7151(95)00101-Z
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 27
DOI: 10.1016/0956-7151(95)00101-Z
|
“Electron microscopy study of the formation of Ni5Al3 in a Ni62.5Al37.5 B2 alloy: 2: plate crystallography”. Schryvers D, Ma Y, Toth L, Tanner LE, Acta metallurgica et materialia 43, 4057 (1995). http://doi.org/10.1016/0956-7151(95)00102-2
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 11
DOI: 10.1016/0956-7151(95)00102-2
|
“ELNES study of carbon K-edge spectra of plasma deposited carbon films”. Hamon A-L, Verbeeck J, Schryvers D, Benedikt J, van den Sanden RMCM, Journal of materials chemistry 14, 2030 (2004). http://doi.org/10.1039/b406468m
Abstract: Electron energy loss spectroscopy was used to investigate the bonding of plasma deposited carbon films. The experimental conditions include the use of a specific collection angle for which the shape of the spectra is free of the orientation dependency usually encountered in graphite due to its anisotropic structure. The first quantification process of the energy loss near-edge structure was performed by a standard fit of the collected spectrum, corrected for background and multiple scattering, with three Gaussian functions followed by a comparison with the graphite spectrum obtained under equivalent experimental conditions. In a second approach a fitting model directly incorporating the background subtraction and multiple scattering removal was applied. The final numerical results are interpreted in view of the deposition conditions of the films and the actual fitting procedure with the related choice of parameters.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.626
Times cited: 61
DOI: 10.1039/b406468m
|
“EM investigation of precursors and precipitation in a Ni39.6Mn47.5Ti12.9 alloy”. Seo JW, Schryvers D, Vermeulen W, Richard O, Potapov P, Philosophical magazine: A: physics of condensed matter: defects and mechanical properties 79, 1279 (1999)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 3
|
“EM study of sensitisation of silver halide grains”. Buschmann V, Schryvers D, van Landuyt J, van Roost C, Icem 13 (1994)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
“Epitaxial Ni-Al thin films on NaCl using a Ag buffer layer”. Yandouzi M, Toth L, Vasudevan V, Cannaerts M, van Haesendonck C, Schryvers D, Philosophical magazine letters 80, 719 (2000). http://doi.org/10.1080/09500830050192936
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.941
Times cited: 2
DOI: 10.1080/09500830050192936
|
“Evaluation of top, angle, and side cleaned FIB samples for TEM analysis”. Montoya E, Bals S, Rossell MD, Schryvers D, Van Tendeloo G, Microscopy research and technique 70, 1060 (2007). http://doi.org/10.1002/jemt.20514
Abstract: ITEM specimens of a LaAlO3/SrTiO3 multilayer are prepared by FIB with internal lift out. Using a Ga+1 beam of 5 kV, a final cleaning step yielding top, top-angle, side, and bottom-angle cleaning is performed. Different cleaning procedures, which can be easily implemented in a dual beam FIB system, are described and compared; all cleaning types produce thin lamellae, useful for HRTEM and HAADF-STEM work up to atomic resolution. However, the top cleaned lamellae are strongly affected by the curtain effect. Top-angle cleaned specimens show an amorphous layer of around 5 nm at the specimen surfaces, due to damage and redeposition. Furthermore, it is observed that the LaAlO3 layers are preferentially destroyed and transformed into amorphous material, during the thinning process.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.147
Times cited: 36
DOI: 10.1002/jemt.20514
|
“Evolution of the phase stability of NiAl under low energy ball milling”. Zelaya E, Esquivel MR, Schryvers D, Advanced powder technology 24, 1063 (2013). http://doi.org/10.1016/j.apt.2013.03.008
Abstract: Low energy mechanical alloying of Ni35 at.%Al and Ni40 at.%Al material was performed and the resulting structures were investigated by XRD and TEM. The final intermetallics observed consist of two phases, NiAl(B2) and Ni3Al while 7R and 3R martensite was observed in post-annealed samples. Different integrated milling times were associated to the intermetallic consolidation and initial blend dissociation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.659
Times cited: 10
DOI: 10.1016/j.apt.2013.03.008
|
“Fabrication and characterization of functionally graded Ni-Ti multilayer thin films”. Tian H, Schryvers D, Mohanchandra KP, Carman GP, van Humbeeck J, Functional materials letters 2, 61 (2009). http://doi.org/10.1142/S1793604709000570
Abstract: A functionally graded multilayer NiTi thin film was deposited on a SiO2/Si substrate by d.c. sputtering using a ramped heated NiTi alloy target. The stand-alone films were crystallized at 500°C in vacuum better than 10-7 Torr. Transmission electron microscopy micrographs taken along the film cross section show two distinct regions, thin and thick, with weak R and B2 phases, respectively. The film compositions along the thickness were measured and quantified using the standard-less EELSMODEL method. The film deposited during the initial thermal ramp (thin regions) displays an average of 54 at.% Ni while the film deposited at a more elevated target temperature (thick regions) shows about 51 at.% Ni.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.234
Times cited: 9
DOI: 10.1142/S1793604709000570
|
“Fabrication, interface characterization and modeling of oriented graphite flakes/Si/Al composites for thermal management applications”. Zhou C, Ji G, Chen Z, Wang M, Addad A, Schryvers D, Wang H, Materials and design 63, 719 (2014). http://doi.org/10.1016/j.matdes.2014.07.009
Abstract: Highly thermally conductive graphite flakes (Gf)/Si/Al composites have been fabricated using Gf, Si powder and an AlSi7Mg0.3 alloy by an optimized pressure infiltration process for thermal management applications. In the composites, the layers of Gf were spaced apart by Si particles and oriented perpendicular to the pressing direction, which offered the opportunity to tailor the thermal conductivity (TC) and coefficient of thermal expansion (CTE) of the composites. Microstructural characterization revealed that the formation of a clean and tightly-adhered interface at the nanoscale between the side surface of the Gf and Al matrix, devoid of a detrimental Al4C3 phase and a reacted amorphous AlSiOC layer, contributed to excellent thermal performance along the alignment direction. With increasing volume fraction of Gf from 13.7 to 71.1 vol.%, the longitudinal (i.e. parallel to the graphite layers) TC of the composites increased from 179 to 526 W/m K, while the longitudinal CTE decreased from 12.1 to 7.3 ppm/K (matching the values of electronic components). Furthermore, the modified layers-in-parallel model better fitted the longitudinal TC data than the layers-in-parallel model and confirmed that the clean and tightly-adhered interface is favorable for the enhanced longitudinal TC.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 61
DOI: 10.1016/j.matdes.2014.07.009
|
“FCC surface precipitation in Cu-Zn-Al after low angle GA+ ion irradiation”. Zelaya E, Schryvers D, Materials transactions 51, 2177 (2010). http://doi.org/10.2320/matertrans.M2010171
Abstract: The precipitation of a disordered FCC surface structure after low angle Ga+ ion irradiation during focused ion beam thinning of a B2 Cu-Zn-Al alloy with e/a=1.48 is reported. Conventional as well as high-resolution transmission electron microscopy techniques reveal FCC layers on both sides of the thinned sample. The occurrence of this structure is attributed to disordering and dezincification of the alloy resulting from the sputtering process during the irradiation. Changes in crystallographic sample orientation with respect to the incoming ion beam do not have a significant effect on the appearance of the FCC surface structure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.713
Times cited: 2
DOI: 10.2320/matertrans.M2010171
|
“FIB/SEM applied to quantitative 3D analysis of precipitates in Ni-Ti”. Cao S, Nishida M, Schryvers D, Diffusion and defect data : solid state data : part B : solid state phenomena 172/174, 1284 (2011). http://doi.org/10.4028/www.scientific.net/SSP.172-174.1284
Abstract: Ni4Ti3 precipitates with a heterogeneous distribution growing in a polycrystalline Ni50.8Ti49.2 alloy have been investigated in a Dual-Beam FIB/SEM system. The volume ratio, mean volume, central plane diameter, thickness, aspect ratio and sphericity of the precipitates in the grain interior as well as near to the grain boundary were measured or calculated. The morphology of the precipitates was classified according to the Zingg scheme. The multistage martensitic transformation occurring in these kinds of samples is interpreted in view of the data of this heterogeneous microstructure of matrix and precipitates.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.4028/www.scientific.net/SSP.172-174.1284
|
“From olivine to ringwoodite : a TEM study of a complex process”. Pittarello L, Ji G, Yamaguchi A, Schryvers D, Debaille V, Claeys P, Meteoritics and Planetary Science 50, 944 (2015). http://doi.org/10.1111/maps.12441
Abstract: The study of shock metamorphism of olivine might help to constrain impact events in the history of meteorites. Although shock features in olivine are well known, so far, there are processes that are not yet completely understood. In shock veins, olivine clasts with a complex structure, with a ringwoodite rim and a dense network of lamellae of unidentified nature in the core, have been reported in the literature. A highly shocked (S5-6), L6 meteorite, Asuka 09584, which was recently collected in Antarctica by a Belgian-Japanese joint expedition, contains this type of shocked olivine clasts and has been, therefore, selected for detailed investigations of these features by transmission electron microscopy (TEM). Petrographic, geochemical, and crystallographic studies showed that the rim of these shocked clasts consists of an aggregate of nanocrystals of ringwoodite, with lower Mg/Fe ratio than the unshocked olivine. The clast's core consists of an aggregate of iso-oriented grains of olivine and wadsleyite, with higher Mg/Fe ratio than the unshocked olivine. This aggregate is crosscut by veinlets of nanocrystals of olivine, with extremely low Mg/Fe ratio. The formation of the ringwoodite rim is likely due to solid-state, diffusion-controlled, transformation from olivine under high-temperature conditions. The aggregate of iso-oriented olivine and wadsleyite crystals is interpreted to have formed also by a solid-state process, likely by coherent intracrystalline nucleation. Following the compression, shock release is believed to have caused opening of cracks and fractures in olivine and formation of olivine melt, which has lately crystallized under postshock equilibrium pressure conditions as olivine.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.391
Times cited: 8
DOI: 10.1111/maps.12441
|
“From the lattice measurements of the austenite and the martensite cells to the macroscopic mechanical behavior of shape memory alloys”. Lexcellent C, Vivet A, Bouvet C, Blanc P, Satto C, Schryvers D, Journal de physique: 4 11, 317 (2001)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
“Functional twin boundaries”. Van Aert S, Turner S, Delville R, Schryvers D, Van Tendeloo G, Ding X, Salje EKH, Phase transitions 86, 1052 (2013). http://doi.org/10.1080/01411594.2012.748909
Abstract: Functional interfaces are at the core of research in the emerging field of domain boundary engineering where polar, conducting, chiral, and other interfaces and twin boundaries have been discovered. Ferroelectricity was found in twin walls of paraelectric CaTiO3. We show that the effect of functional interfaces can be optimized if the number of twin boundaries is increased in densely twinned materials. Such materials can be produced by shear in the ferroelastic phase rather than by rapid quench from the paraelastic phase.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.06
Times cited: 5
DOI: 10.1080/01411594.2012.748909
|
“GP-zones in Al-Zn-Mg alloys and their role in artificial aging”. Berg LK, Gjønnes J, Hansen V, Li XZ, Knutson-Wedel M, Waterloo G, Schryvers D, Wallenberg LR, Acta materialia 49, 3443 (2001). http://doi.org/10.1016/S1359-6454(01)00251-8
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 261
DOI: 10.1016/S1359-6454(01)00251-8
|
“Grain growth and precipitation in an annealed cold-rolled Ni50.2Ti49.8 alloy”. Srivastava AK, Schryvers D, van Humbeeck J, Intermetallics 15, 1538 (2007). http://doi.org/10.1016/j.intermet.2007.06.003
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.14
Times cited: 37
DOI: 10.1016/j.intermet.2007.06.003
|
“The growth of Ni5Al3 in L10 martensite studied by in situ transmission electron microscopy and high resolution electron microscopy”. Schryvers D, Ma Y, Journal of alloys and compounds 221, 227 (1995). http://doi.org/10.1016/0925-8388(94)01467-1
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.999
Times cited: 19
DOI: 10.1016/0925-8388(94)01467-1
|
“High-quality sample preparation by low kV FIB thinning for analytical TEM measurements”. Bals S, Tirry W, Geurts R, Yang Z, Schryvers D, Microscopy and microanalysis 13, 80 (2007). http://doi.org/10.1017/S1431927607070018
Abstract: Focused ion beam specimen preparation has been used for NiTi samples and SrTiO(3)/SrRuO(3) multilayers with prevention of surface amorphization and Ga implantation by a 2-kV cleaning procedure. Transmission electron microscopy techniques show that the samples are of high quality with a controlled thickness over large scales. Furthermore, preferential thinning effects in multicompounds are avoided, which is important when analytical transmission electron microscopy measurements need to be interpreted in a quantitative manner. The results are compared to similar measurements acquired for samples obtained using conventional preparation techniques such as electropolishing for alloys and ion milling for oxides.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 82
DOI: 10.1017/S1431927607070018
|