Abstract: The post-growth modification of diamond-like amorphous hydrogenated carbon a-C:H films by laser treatment has been studied by transmission electron microscopy and Raman spectroscopy. a-C:H films grown on Si substrates by benzene decomposition in a rf glow discharge were irradiated with 15 ns pulses of a KrF-excimer laser with fluences in the ran e of E = 50-700 mJ/cm(2). At fluences below 100 mJ/cm(2) an increase in the number of graphitic clusters and in their ordering was evidenced from Raman spectra, while the film structure remained amorphous according to electron microscopy and electron diffraction observations. At higher fluences the appearance of diamond particles of 2-7 nm size, embedded into the lower crystallized graphitic matrix, was observed and simultaneously a progressive growth of graphite nanocrystals with dimensions from 2 nm to 4 nm was deduced from Raman measurements. The maximum thickness of the crystallized surface layer (approximate to 400 nm) and the degree of laser annealing are limited by the film ablation which starts at E > 250 mJ/cm(2). The laser-treated areas lose their chemical inertness. In particular, chemical etching in chromium acid becomes possible, which may be used for patterning the highly inert carbon films.

Abstract: The recently discovered superconducting mercury-based cuprates HgBa2Can-1CunO2n+2+delta have proved difficult to synthesize as single phases and are sensitive to environment (CO2, moisture). The present paper gives an overview of new series mercury based superconductors, whose stabilisation is based on the fact that a foreign cation with a higher valency than Hg(II) must be introduced in the mercury layers, in order to fill up partially the oxygen vacancies of these layers. By this method, several new series of superconductors involving strontium instead of barium with critical temperatures ranging from 27 K to 95 K have been isolated : Hg0.5Bi0.5Sr2-xLaxCuO4+delta, Hg(0.5)Bi(0.5)Sr(2)Ca(1-x)R(x)Cu(2)O(6+delta) (R Y, Nd, Pr), Pb0.7Hg0.3Sr2-xLaxCuO4+delta, Pb(0.7)Hg(0.3)Sr(2)Ca(1-x)R(x)Cu(2)O(6+delta) (R = Y, Nd) Hg(1-x)Pr(x)Sr(2)A(1-x')Pr(x') Cu2O6+delta (A = Sr, Ca), Pb0.7Hg0.3Sr2Cu2CO3O7 and Hg1-xCrxSr2CuO4+delta. The behaviour of the praseodymium cuprates that exhibit a rather sharp transition and reach a Tc of 85 K is especially discussed. A method to synthesize new ''Ba-Hg'' superconducting cuprates with the 1212 structure at normal pressure with a Tc up to 110 K is also presented.

Abstract: The structure and defect structure of Bi2-xPbxSr3.5Cu2 (CO3)O8-delta compounds with 0 less-than-or-equal-to x less-than-or-equal-to 0.75 are carefully investigated by electron diffraction and high-resolution electron microscopy. All compounds have an orthorhombic structure with a almost-equal-to b almost-equal-to 5.4 angstrom and c almost-equal-to 39.5 angstrom. The length of the b-axis decreases monotonically with increasing x. The space group for the basic structure is Abm2. The structure can be considered as an intergrowth of Bi2Sr2CuO6 lamellae with Sr2CuO2 (CO3) lamellae along the c-axis. CO3 groups behave as bridges connecting the CuO6 octahedra. In the x = 0 compound the carbon atoms are shifted away from their symmetry positions; the orientational ordering of the CO3 groups (or the carbon shift) in successive CO planes alternates along +b and -b. Typical Bi-type and Pb-type modulations are found along the b-axis up to a Pb content x = 0.5. Electron beam irradiation destroys the ordering of the CO3 groups and alters the modulated structure. (C) 1994 Academic press, inc.