Abstract: Historical glass, especially medieval glass, can undergo weathering under the influence of time and environmental conditions. The aim of this investigation was to better understand the processes involved in this natural degradation process by studying artificially altered glass samples prepared for the use of evaluation of conservation methods. Non-durable glass sensors produced by the Fraunhofer Institute (type M1.0) were used as a starting material for artificial alteration. These were immersed in acidic (pH = 0, 2, 4) and neutral solutions (1 h – 8 h). In a second stage the glass samples were immersed in a 0.5 M MnCl2 solution (24 h, 48 h and 72 h), allowing intrusion of Mn from the solution into the gel layer. The samples were characterized at different stages with reflectance FTIR spectroscopy, mu XRF mapping and mu XANES. All measurements were carried out at ESRF, beamline ID21. Reflectance FTIR spectroscopy measurements were performed in the 800 4000 cm(-1) range. Cluster analysis of the resulting maps evidenced the rapid growth of the gel layer in strong acidic conditions. The average spectra for each cluster feature show for the original glass a strong Si-O- stretching band between 900 and 1000 cm(-1), whereas the gel layer could be identified by the increasing Si-O-Si bands around 1100 and 1250 cm(-1). mu XRF maps were recorded at different stages of the experiment at energies around the Mn-K edge (6.539 keV) and with a step size of 2 by 2 m. These confirm the leaching of K+ and Ca+2 from the glass and the intrusion of Mn from the solution. Mn was found throughout the entire gel layer, but with a concentration gradient peaking at the surface. XANES point measurements were recorded at various points where Mn was present. No spatial variation was found, but linear combination fitting of the spectra with various Mn reference compounds indicated that Mn2+Mn23+O4 is the main Mn compound in the gel layer, as was hypothesised by Watkinson et al. The standard corroded glass samples studied here can be used for the evaluation of conservation treatments in follow-up experiments. (C) 2013 The Authors. Published by Elsevier B.V. Selection and peer-review under responsibility of the IA-CS (Italian Association of Conservation Scientists) and University of Antwerp

Abstract: The radiation damage created in silicon materials by Mn-57 -> Fe-57 ion implantation has been studied and characterized by Mossbauer spectroscopy showing four main lines, assigned to: substitutional, interstitial and damaged configuration sites of the implanted ions. Nevertheless, the Mossbauer spectrum of Fe-57 in this materials remains with some ambiguous identification regarding the implantation configurations before and after annealing, specially the damaged configurations and its evolution. In the present work some possible implantation configurations are suggested and evaluated using a multiscale approach by Monte Carlo ion transport and electronic structure calculations within DFT. The proposed implantation environments were evaluated in terms of stability and the Fe-57 hyperfine parameters were calculated to establish the connections with the experimental observations. Good agreement was found between the experimental and the calculated hyperfine parameters for some configurations; suggesting which ones could be the implantation environments before and after sample annealing.

Abstract: The aim of the present work is to study the radiation damage induced in LYSO and LuYAP crystals by the gamma radiation and the secondary electrons/positrons generated. The displacements per atom (dpa) distributions inside each material were calculated following the Monte Carlo assisted Classical Method (MCCM) introduced by the authors. As gamma sources were used Sc-44, Na-22 and V-48. Also the energy of gammas from the annihilation processes (511 keV) was included in the study. This procedure allowed studying the in-depth dpa distributions inside each crystal for all four sources. It was also possible to obtain the separate contribution from each atom to the total dpa. The LYSO crystals were found to receive more damage, mainly provoked by the displacements of silicon and oxygen atoms.

Abstract: The amount of animal manure that can be brought back to agricultural land is limited by legislation. Because pig manure is available in too large quantities in some areas, we investigate the techno-economic feasibility of converting it into valuable products. First, slurry is separated in water, a thick fraction and a fertilizer concentrate poor in phosphate. Then, the thick fraction is dried and pyrolyzed. Our goal is to identify the optimal pyrolysis and activation conditions for the production of biochar or activated carbon. The latter has interesting adsorption characteristics due to the presence of nitrogen. It can also be used as a soil amendment as it improves biomass quantity and quality. On top, it immobilizes toxic elements and stores carbon in the soil. Char thus has many interesting characteristics and can be valued in different ways. The economic feasibility has been explored by a first techno-economic modelling iteration. The critical factors influencing the feasibility are identified by Monte Carlo simulations for further improvement of the process design.

Abstract: Pure and Nb-doped TiO2 thick-films were prepared by screen-printing, starting from nanosized powders. Grain growth and crystalline phase modification occurred as consequence of firing at high temperature. It has been shown that niobium addition inhibits grain coarsening and hinders anatase-to-rutile phase transition. These semiconducting films exhibited n-type behavior, while Nb acted as donor-dopant. Gas measurements demonstrated that the films are suitable for CO or NO2 sensing. Microstructural characterization by electron microscopy and differential thermal analysis (DTA) highlights the dependence of gas-sensing behavior on film's properties. (C) 2000 Elsevier Science S.A. All rights reserved.

Abstract: Positrons can be trapped in localized states at the surface of a material, and thus quite selectively interact with core or valence surface electrons. Hence, advanced surface positron spectroscopy techniques can present the ideal tools to study a topological insulator, where surface states play a fundamental role. We analyze the problem of a positron at a TI surface, assuming that it is a weakly physisorbed positronium (Ps) atom. To determine if the surface of interest in a material can sustain such a physisorption, an accurate description of the underlying van der Waals (vdW) interaction is essential. We have developed a first-principles parameterfree method, based on the density functional theory, to extract key parameters determining the vdW interaction potential between a Ps atom and the surface of a given material. The method has been successfully applied to quartz and preliminary results on Bi2Te2Se indicate the existence of a positron surface state. We discuss the robustness of our predictions versus the most relevant approximations involved in our approach.

Abstract: Strain fields introduced by coherent Ni4Ti3 precipitates in austenitic Ni-Ti are believed to be a possible origin of why the R-phase transformation is introduced as an extra step before transforming to the B19'. The presence of this strain field was already confirmed in the past by conventional transmission electron microscopy (TEM) techniques and measured quantitatively by high resolution TEM (HRTEM). This time the geometrical phase method is applied on HRTEM micrographs to measure the full 3D strain tensor of the strain fields. Since each atomic resolution micrograph only results in a 2D measurement of the strain, observations in two different zone orientations are combined to retrieve the 3 x 3 strain tensor. In this work observations in a [1-1 1](B2) and [1 0-1](B2) zone orientation are used and this in case of precipitates with a diameter of around 50nm. In a next step the measured strain tensor is compared to the calculated eigenstrain of the R-phase in reference to the B2 matrix. This comparison shows that the introduced strain is very similar to the eigenstrain of one R-phase variant. Since for both structures, Ni4Ti3 and R-phase, four orientation variants are possible, each variant of the R-phase is thus able to accommodate the strain field of one of the Ni4Ti3 variants.

Abstract: Infrared absorption spectra of oxygen precipitates in boron doped silicon with a boron concentration between 10(17) and 10(19) cm(-3) are analyzed, applying the spectral function theory of the composite precipitates. The aspect ratio of the platelet precipitates has been determined by transmission electron microscopy measurements. Our analysis shows that in samples with moderate doping levels (<10(18) B cm(-3)) SiOgamma precipitates are formed with stoichiometry as in the lightly doped case. In the heavily (>10(18) cm(-3)) boron doped samples, however, the measured spectra of the precipitates are consistent with a mixture of SiO2 and B2O3. with a volume fraction of B2O3 as high as 0.41 in the most heavily doped case.

Abstract: The atomic structure of single-wall carbon nanotube bundles produced by three different techniques has been characterized by electron diffraction and microscopy. Small bundles produced by Catalytical Chemical Vapor Deposition (CCVD) exhibit only one or two tube chiralities within a single bundle while bundles produced by arc-discharge or laser-ablation exhibit more chiralities. A detailed analysis of the central line of diffraction is also presented. The CCVD nanotubes present more intense spots around 1.7 Angstrom(-1) < k < 2Angstrom(-1) (k is the momentum transfer) compared to what is observed for nanotubes produced by other methods. Amongst the possible explanation for such an anomaly, we put forward that in this range of momentum transfer, the relative tube orientations and translations are important for what concerns the interpretation of the diffraction peaks intensities.