“Nonlinear optical properties of Ag nanoclusters and nanoparticles dispersed in a glass host”. Mai HH, Kaydashev VE, Tikhomirov VK, Janssens E, Shestakov MV, Meledina M, Turner S, Van Tendeloo G, Moshchalkov VV, Lievens P, The journal of physical chemistry: C : nanomaterials and interfaces 118, 15995 (2014). http://doi.org/10.1021/jp502294u
Abstract: The nonlinear absorption of Ag atomic clusters and nanoparticles dispersed in a transparent oxyfluoride glass host has been studied. The as-prepared glass, containing 0.15 atom % Ag, shows an absorption band in the UV/violet attributed to the presence of amorphous Ag atomic nanoclusters with an average size of 1.2 nm. Upon heat treatment the Ag nanoclusters coalesce into larger nanoparticles that show a surface plasmon absorption band in the visible. Open aperture z-scan experiments using 480 nm nanosecond laser pulses demonstrated nonsaturated and saturated nonlinear absorption with large nonlinear absorption indices for the Ag nanoclusters and nanoparticles, respectively. These properties are promising, e.g., for applications in optical limiting and objects contrast enhancement.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 43
DOI: 10.1021/jp502294u
|
|
|
“On the stress state dependence of the twinning rate and work hardening in twinning-induced plasticity steels”. Renard K, Idrissi H, Schryvers D, Jacques PJ, Scripta materialia 66, 966 (2012). http://doi.org/10.1016/j.scriptamat.2012.01.063
Abstract: The influence of the stress state on the twinning rate and work hardening is studied in the case of an FeMnC TWIP steel strained in uniaxial tension, simple shear and rolling. The resulting stressstrain responses exhibit marked differences. The twinning rate, number of activated twinning systems in each grain, twin thickness and transmission of twins across grain boundaries are dependent on the imposed stress state during straining. Relationships between twin features and macroscopic work hardening rate are established.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 41
DOI: 10.1016/j.scriptamat.2012.01.063
|
|
|
“One particle@one cell : highly monodispersed PtPd bimetallic nanoparticles for enhanced oxygen reduction reaction”. Ying J, Yang X-Y, Hu Z-Y, Mu S-C, Janiak C, Geng W, Pan M, Ke X, Van Tendeloo G, Su B-L, Nano energy 8, 214 (2014). http://doi.org/10.1016/j.nanoen.2014.06.010
Abstract: Highly monodispersed platinum-based nanoalloys are the best-known catalysts for the oxygen reduction reaction. Although certainly promising, the durability and stability are among the main requirements for commercializing fuel cell electrocatalysts in practical applications. Herein, we synthesize highly stable, durable and catalytic active monodispersed PtPd nano-particles encapsulated in a unique one particle@one cell structure by adjusting the viscosity of solvents using mesocellular foam. PtPd nanoparticles in mesocellular carbon foam exhibit an excellent electrocatalytic activity (over 4 times mass and specific activities than the commercial Pt/C catalyst). Most importantly, this nanocatalyst shows no obvious change of structure and only a 29.5% loss in electrochemically active surface area after 5000 potential sweeps between 0.6 and 1.1 V versus reversible hydrogen electrode cycles. (C) 2014 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.343
Times cited: 40
DOI: 10.1016/j.nanoen.2014.06.010
|
|
|
“Optimizing Er/Yb ratio and content in Er-Yb co-doped glass-ceramics for enhancement of the up- and down-conversion luminescence”. Tikhomirov VK, Rodríguez VD, Méndez-Ramos J, del- Castillo J, Kirilenko D, Van Tendeloo G, Moshchalkov VV, Solar energy materials and solar cells 100, 209 (2012). http://doi.org/10.1016/j.solmat.2012.01.019
Abstract: Er3+Yb3+ co-doped transparent glass-ceramics with varying Er/Yb content and ratio have been prepared. High quantum yields for up- and down-conversion luminescence by energy transfer from Yb3+ to Er3+ and from Er3+ to Yb3+, respectively, have been detected and optimized with respect to the Er/Yb content and ratio, and proposed in particular for up- and down-conversion of solar spectrum for enhancement of the efficiency of solar cells. The rise and decay kinetics for the population of the excited levels of Er3+ and Yb3+ have been studied and fit. Based on these experimental data, the mechanisms for the energy transfers have been suggested with emphasis on the optimized Er/Yb content and ratio for enhancement of the efficiency of the Er3+↔Yb3+ energy transfers.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.784
Times cited: 66
DOI: 10.1016/j.solmat.2012.01.019
|
|
|
“Pd nanoparticles on SnO2(Sb) whiskers : aggregation and reactivity in CO detection”. Zhukova AA, Rumyantseva MN, Zaytsev VB, Zaytseva AV, Abakumov AM, Gaskov AM, Journal of alloys and compounds 565, 6 (2013). http://doi.org/10.1016/j.jallcom.2013.02.184
Abstract: Single crystal antimony-doped SnO2 whiskers have been synthesized by in situ doping process in horizontal flow reactor. The produced whiskers were modified with 0.1, 0.2, 0.5, 1 or 2 wt.% Pd. The processes of Pd particles growth and aggregation are described on the base of AFM and STEM data. Depending on the content of introduced Pd precursor, the various mechanisms (Volmer-Weber or Stranski-Krastanov) of Pd nanoparticles growth realize. The dependence of sensor signal to CO on Pd concentration has non-monotonous character determined by the size of Pd nanoparticles and their aggregation degree. The best sensor signal toward CO was observed for whiskers decorated with 0.1 wt.% Pd. This concentration corresponds to the presence of individual 3-5 nm Pd nanoparticles on the surface of the whiskers. (C) 2013 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
DOI: 10.1016/j.jallcom.2013.02.184
|
|
|
“Phase formation in intermixed NiGe thin films : influence of Ge content and low-temperature nucleation of hexagonal nickel germanides”. De Schutter B, Devulder W, Schrauwen A, van Stiphout K, Perkisas T, Bals S, Vantomme A, Detavernier C, Microelectronic engineering 120, 168 (2014). http://doi.org/10.1016/j.mee.2013.09.004
Abstract: In this study, we focus on phase formation in intermixed NiGe thin films as they represent a simplified model of the small intermixed interface layer that is believed to form upon deposition of Ni on Ge and where initial phase formation happens. A combinatorial sputter deposition technique was used to co-deposit a range of intermixed NiGe thin films with Ge concentrations varying between 0 and 50 at.%Ge in a single deposition on both Ge (100) and inert SiO2 substrates. In situ X-ray diffraction and transmission electron microscopy where used to study phase formation. In almost the entire composition range under investigation, crystalline phases where found to be present in the as-deposited films. Between 36 and 48 at.%Ge, high-temperature hexagonal nickel germanides were found to occur metastabily below 300 °C, both on SiO2 and Ge (100) substrates. For Ge concentrations in the range between 36 and 42 at.%, this hexagonal germanide phase was even found to be present at room temperature in the as-deposited films. The results obtained in this work could provide more insight in the phase sequence of a pure Ni film on Ge.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.806
Times cited: 9
DOI: 10.1016/j.mee.2013.09.004
|
|
|
“Phase problem in the B-site ordering of La2CoMnO6 : impact on structure and magnetism”. Egoavil R, Huehn S, Jungbauer M, Gauquelin N, Béché, A, Van Tendeloo G, Verbeeck, Moshnyaga V, Nanoscale 7, 9835 (2015). http://doi.org/10.1039/c5nr01642h
Abstract: Epitaxial double perovskite La2CoMnO6 (LCMO) films were grown by metalorganic aerosol deposition on SrTiO3(111) substrates. A high Curie temperature, T-C = 226 K, and large magnetization close to saturation, M-S(5 K) = 5.8 mu(B)/f.u., indicate a 97% degree of B-site (Co,Mn) ordering within the film. The Co/Mn ordering was directly imaged at the atomic scale by scanning transmission electron microscopy with energy-dispersive X-ray spectroscopy (STEM-EDX). Local electron-energy-loss spectroscopy (EELS) measurements reveal that the B-sites are predominantly occupied by Co2+ and Mn4+ ions in quantitative agreement with magnetic data. Relatively small values of the (1/2 1/2 1/2) superstructure peak intensity, obtained by X-ray diffraction (XRD), point out the existence of ordered domains with an arbitrary phase relationship across the domain boundary. The size of these domains is estimated to be in the range 35-170 nm according to TEM observations and modelling the magnetization data. These observations provide important information towards the complexity of the cation ordering phenomenon and its implications on magnetism in double perovskites, and similar materials.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.367
Times cited: 37
DOI: 10.1039/c5nr01642h
|
|
|
“Hematite iron oxide nanorod patterning inside COK-12 mesochannels as an efficient visible light photocatalyst”. Wee LH, Meledina M, Turner S, Custers K, Kerkhofs S, Van Tendeloo G, Martens JA, Journal of materials chemistry A : materials for energy and sustainability 3, 19884 (2015). http://doi.org/10.1039/C5TA05075H
Abstract: The uniform dispersion of functional oxide nanoparticles on the walls of ordered mesoporous silica to tailor optical, electronic, and magnetic properties for biomedical and environmental applications is a scientific challenge. Here, we demonstrate homogeneous confined growth of 5 nanometer-sized hematite iron oxide (α-Fe2O3) inside mesochannels of ordered mesoporous COK-12 nanoplates. The three-dimensional inclusion of the α-Fe2O3 nanorods in COK-12 particles is studied using high-angle annular dark field scanning transmission electron microscopy (HAADF-STEM), energy-dispersive X-ray (EDX) spectroscopy and electron tomography. High resolution imaging and EDX spectroscopy provide information about the particle size, shape and crystal phase of the loaded α-Fe2O3 material, while electron tomography provides detailed information on the spreading of the nanorods throughout the COK-12 host. This nanocomposite material, having a semiconductor band gap energy of 2.40 eV according to diffuse reflectance spectroscopy, demonstrates an improved visible light photocatalytic degradation activity with rhodamine 6G and 1-adamantanol model compounds.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 8.867
Times cited: 9
DOI: 10.1039/C5TA05075H
|
|
|
“Photovoltaic effect and evidence of carrier multiplication in graphene vertical homojunctions with asymmetrical metal contacts”. Chen JJ, Wang Q, Meng J, Ke X, Van Tendeloo G, Bie YQ, Liu J, Liu K, Liao ZM, Sun D, Yu D;, ACS nano 9, 8851 (2015). http://doi.org/10.1021/acsnano.5b02356
Abstract: Graphene exhibits exciting potentials for high-speed wideband photodetection and high quantum efficiency solar energy harvest because of its broad spectral absorption, fast photoelectric response, and potential carrier multiplication. Although photocurrent can be generated near a metalgraphene interface in lateral devices, the photoactive area is usually limited to a tiny one-dimensional line-like interface region. Here, we report photoelectric devices based on vertical graphene two-dimensional homojunction, which is fabricated via vertically stacking four graphene monolayers with asymmetric metal contacts. The devices show excellent photovoltaic output with excitation wavelength ranging from visible light to mid-infrared. The wavelength dependence of the internal quantum efficiency gives direct evidence of the carrier multiplication effect in graphene. The simple fabrication process, easy scale-up, large photoresponsive active area, and broadband response of the vertical graphene device are very promising for practical applications in optoelectronics and photovoltaics.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 11
DOI: 10.1021/acsnano.5b02356
|
|
|
“Plasmon mapping in Au@Ag nanocube assemblies”. Goris B, Guzzinati G, Fernández-López C, Pérez-Juste J, Liz-Marzán LM, Trügler A, Hohenester U, Verbeeck J, Bals S, Van Tendeloo G, The journal of physical chemistry: C : nanomaterials and interfaces 118, 15356 (2014). http://doi.org/10.1021/jp502584t
Abstract: Surface plasmon modes in metallic nanostructures largely determine their optoelectronic properties. Such plasmon modes can be manipulated by changing the morphology of the nanoparticles or by bringing plasmonic nanoparticle building blocks close to each other within organized assemblies. We report the EELS mapping of such plasmon modes in pure Ag nanocubes, Au@Ag coreshell nanocubes, and arrays of Au@Ag nanocubes. We show that these arrays enable the creation of interesting plasmonic structures starting from elementary building blocks. Special attention will be dedicated to the plasmon modes in a triangular array formed by three nanocubes. Because of hybridization, a combination of such nanotriangles is shown to provide an antenna effect, resulting in strong electrical field enhancement at the narrow gap between the nanotriangles.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 41
DOI: 10.1021/jp502584t
|
|
|
“Point defect reactions in silicon studied in situ by high flux electron irradiation in high voltage transmission electron microscope”. Vanhellemont J, Romano Rodriguez A, Fedina L, van Landuyt J, Aseev A, Materials science and technology 11, 1194 (1995). http://doi.org/10.1179/mst.1995.11.11.1194
Abstract: Results are presented of in situ studies of 1 MeV electron irradiation induced (113) defect generation in silicon containing different types and concentrations of extrinsic point defects. A semiquantitative model is developed describing the influence of interfaces and stress fields and of extrinsic point defects on the (113) defect generation in silicon during irradiation. The theoretical results obtained are correlated with experimental data obtained on silicon uniformly doped with boron and phosphorus and with observations obtained by irradiating cross-sectional samples of wafers with highly doped surface layers. It is shown that in situ irradiation in a high voltage election microscope is a powerful tool for studying local point defect reactions in silicon. (C) 1995 The Institute of Materials.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 0.995
Times cited: 7
DOI: 10.1179/mst.1995.11.11.1194
|
|
|
“Polyethylene glycol conjugated polymeric nanocapsules for targeted delivery of quercetin to folate-expressing cancer cells in vitro and in vivo”. El-Gogary RI, Rubio N, Wang JTW, Al-Jamal WT, Bourgognon M, Kafa H, Naeem M, Klippstein R, Abbate V, Leroux F, Bals S, Van Tendeloo G, Kamel AO, Awad GAS, Mortada ND, Al-Jamal KT;, ACS nano 8, 1384 (2014). http://doi.org/10.1021/nn405155b
Abstract: In this work we describe the formulation and characterization of chemically modified polymeric nanocapsules incorporating the anticancer drug, quercetin, for the passive and active targeting to tumors. Folic acid was conjugated to poly(lactide-co-glycolide) (PLGA) polymer to facilitate active targeting to cancer cells. Two different methods for the conjugation of PLGA to folic acid were employed utilizing polyethylene glycol (PEG) as a spacer. Characterization of the conjugates was performed using FTIR and H-1 NMR studies. The PEG and folk acid content was independent of the conjugation methodology employed. PEGylation has shown to reduce the size of the nanocapsule; moreover, zeta-potential was shown to be polymer-type dependent. Comparative studies on the cytotoxicity and cellular uptake of the different formulations by He La cells, in the presence and absence of excess folic acid, were carried out using MTT assay and Confocal Laser Scanning Microscopy, respectively. Both results confirmed the selective uptake and cytotoxicity of the folic acid targeted nanocapsules to the folate enriched cancer cells in a folate-dependent manner. Finally, the passive tumor accumulation and the active targeting of the nanocapsules to folate-expressing cells were confirmed upon intravenous administration in He La or IGROV-1 tumor-bearing mice. The developed nanocapsules provide a system for targeted delivery of a range of hydrophobic anticancer drugs in vivo.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 144
DOI: 10.1021/nn405155b
|
|
|
“Porous nanostructured metal oxides synthesized through atomic layer deposition on a carbonaceous template followed by calcination”. Deng S, Kurttepeli M, Cott DJ, Bals S, Detavernier C, Journal of materials chemistry A : materials for energy and sustainability 3, 2642 (2015). http://doi.org/10.1039/C4TA05165C
Abstract: Porous metal oxides with nano-sized features attracted intensive interest in recent decades due to their high surface area which is essential for many applications, e.g. Li ion batteries, photocatalysts, fuel cells and dye-sensitized solar cells. Various approaches have so far been investigated to synthesize porous nanostructured metal oxides, including self-assembly and template-assisted synthesis. For the latter approach, forests of carbon nanotubes are considered as particularly promising templates, with respect to their one-dimensional nature and the resulting high surface area. In this work, we systematically investigate the formation of porous metal oxides (Al2O3, TiO2, V2O5 and ZnO) with different morphologies using atomic layer deposition on multi-walled carbon nanotubes followed by post-deposition calcination. X-ray diffraction, scanning electron microscopy accompanied by X-ray energy dispersive spectroscopy and transmission electron microscopy were used for the investigation of morphological and structural transitions at the micro- and nano-scale during the calcination process. The crystallization temperature and the surface coverage of the metal oxides and the oxidation temperature of the carbon nanotubes were found to produce significant influence on the final morphology.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 8.867
Times cited: 23
DOI: 10.1039/C4TA05165C
|
|
|
“Possibilities and limitations of advanced transmission electron microscopy for carbon-based nanomaterials”. Ke X, Bittencourt C, Van Tendeloo G, Beilstein journal of nanotechnology 6, 1541 (2015). http://doi.org/10.3762/bjnano.6.158
Abstract: A major revolution for electron microscopy in the past decade is the introduction of aberration correction, which enables one to increase both the spatial resolution and the energy resolution to the optical limit. Aberration correction has contributed significantly to the imaging at low operating voltages. This is crucial for carbon-based nanomaterials which are sensitive to electron irradiation. The research of carbon nanomaterials and nanohybrids, in particular the fundamental understanding of defects and interfaces, can now be carried out in unprecedented detail by aberration-corrected transmission electron microscopy (AC-TEM). This review discusses new possibilities and limits of AC-TEM at low voltage, including the structural imaging at atomic resolution, in three dimensions and spectroscopic investigation of chemistry and bonding. In situ TEM of carbon-based nanomaterials is discussed and illustrated through recent reports with particular emphasis on the underlying physics of interactions between electrons and carbon atoms.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.127
Times cited: 10
DOI: 10.3762/bjnano.6.158
|
|
|
“One-Step Microheterogeneous Formation of Rutile@Anatase Core–Shell Nanostructured Microspheres Discovered by Precise Phase Mapping”. Tarasov A, Hu Z-Y, Meledina M, Trusov G, Goodilin E, Van Tendeloo G, Dobrovolsky Y, The journal of physical chemistry: C : nanomaterials and interfaces 121, 4443 (2017). http://doi.org/10.1021/acs.jpcc.6b12991
Abstract: Nanostructured core−shell microspheres with a rough rutile core and a thin anatase shell are synthesized via a one-step heterogeneous templated hydrolysis process of TiCl4 vapor on the aerosol water−air interface. The rutile-in-anatase core−shell structure has been evidenced by different electron microscopy techniques, including electron energy-loss spectroscopy and 3D electron tomography. A new mechanism for the formation of a crystalline rutile core inside the anatase shell is proposed based on a statistical evaluation of a large number of electron microscopy data. We found that the control over the TiCl4 vapor pressure, the ratio between TiCl4 and H2O aerosol, and the reaction conditions plays a crucial role in the formation of the core−shell morphology and increases the yield of nanostructured microspheres.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 4
DOI: 10.1021/acs.jpcc.6b12991
|
|
|
“Pressure-Collapsed Amorphous Mg(BH4)(2): An Ultradense Complex Hydride Showing a Reversible Transition to the Porous Framework”. Ban V, Soloninin AV, Skripov AV, Hadermann J, Abakumov A, Filinchuk Y, The journal of physical chemistry: C : nanomaterials and interfaces 118, 23402 (2014). http://doi.org/10.1021/jp507286m
Abstract: Hydrogen-storage properties of complex hydrides depend of their form, such as a polymorphic form or an eutectic mixture. This Paper reports on an easy and reproducible way to synthesize a new stable form of magnesium borohydride by pressure-induced collapse of the porous gamma-Mg(BH4)(2). This amorphous complex hydride was investigated by temperature-programmed synchrotron X-ray diffraction (SXRD), transmission electron microscopy (TEM), thermogravimetric analysis, differential scanning calorimetry analysis, and Raman spectroscopy, and the dynamics of the BH4 reorientation was studied by spinlattice relaxation NMR spectroscopy. No long-range order is observed in the lattice region by Raman spectroscopy, while the internal vibration modes of the BH4 groups are the same as in the crystalline state. A hump at 4.9 angstrom in the SXRD pattern suggests the presence of nearly linear MgBH4 Mg fragments constituting all the known crystalline polymorphs of Mg(BH4)(2), which are essentially frameworks built of tetrahedral Mg nodes and linear BH4 linkers. TEM shows that the pressure-collapsed phase is amorphous down to the nanoscale, but surprisingly, SXRD reveals a transition at similar to 90 degrees C from the dense amorphous state (density of 0.98 g/cm(3)) back to the porous ? phase having only 0.55 g/cm(3) crystal density. The crystallization is slightly exothermic, with the enthalpy of -4.3 kJ/mol. The volumetric hydrogen density of the amorphous form is 145 g/L, one of the highest among hydrides. Remarkably, this form of Mg(BH4)2 has different reactivity compared to the crystalline forms. The parameters of the reorientational motion of BH4 groups in the amorphous Mg(BH4)(2) found from NMR measurements differ significantly from those in the known crystalline forms. The behavior of the nuclear spinlattice relaxation rates can be described in terms of a Gaussian distribution of the activation energies centered on 234 +/- 9 meV with the dispersion of 100 +/- 10 meV.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 23
DOI: 10.1021/jp507286m
|
|
|
“Preventing the reconstruction of the polar discontinuity at oxide heterointerfaces”. Boschker H, Verbeeck J, Egoavil R, Bals S, Van Tendeloo G, Huijben M, Houwman EP, Koster G, Blank DHA, Rijnders G, Advanced functional materials 22, 2235 (2012). http://doi.org/10.1002/adfm.201102763
Abstract: Perovskite oxide heteroepitaxy receives much attention because of the possibility to combine the diverse functionalities of perovskite oxide building blocks. A general boundary condition for the epitaxy is the presence of polar discontinuities at heterointerfaces. These polar discontinuities result in reconstructions, often creating new functionalities at the interface. However, for a significant number of materials these reconstructions are unwanted as they alter the intrinsic materials properties at the interface. Therefore, a strategy to eliminate this reconstruction of the polar discontinuity at the interfaces is required. We show that the use of compositional interface engineering can prevent the reconstruction at the La0.67Sr0.33MnO3/SrTiO3 (LSMO/STO) interface. The polar discontinuity at this interface can be removed by the insertion of a single La0.33Sr0.67O layer, resulting in improved interface magnetization and electrical conductivity.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 72
DOI: 10.1002/adfm.201102763
|
|
|
“Producing photoluminescent species from Sp2 carbons”. Hens SC, Shenderova O, Turner S, Fullerenes, nanotubes, and carbon nanostructures 20, 502 (2012). http://doi.org/10.1080/1536383X.2012.655667
Abstract: The treatment of sp2 carbon materials, including micrographite, nanographite, HOPG, onion-like-carbon, and single-walled carbon nanotubes, in a 3:1 sulfuric to nitric acid mixture produced photoluminescent reaction solutions. These colloidal, aqueous solutions appeared photoluminescently stable under a UV lamp and ranged in color from red to blue. The photoluminescent wavelength shifted to shorter wavelength with increasing reaction time or increasing reaction temperature. Raman spectroscopy showed evidence of defect structures in graphitic residue, and transmission electron microscopy showed unusual structures present in the supernatant including graphitic balls.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.35
Times cited: 4
DOI: 10.1080/1536383X.2012.655667
|
|
|
“Damage evaluation in graphene underlying atomic layer deposition dielectrics”. Tang X, Reckinger N, Poncelet O, Louette P, Urena F, Idrissi H, Turner S, Cabosart D, Colomer J-F, Raskin J-P, Hackens B, Francis LA, Scientific reports 5, 13523 (2015). http://doi.org/10.1038/srep13523
Abstract: Based on micro-Raman spectroscopy (muRS) and X-ray photoelectron spectroscopy (XPS), we study the structural damage incurred in monolayer (1L) and few-layer (FL) graphene subjected to atomic-layer deposition of HfO2 and Al2O3 upon different oxygen plasma power levels. We evaluate the damage level and the influence of the HfO2 thickness on graphene. The results indicate that in the case of Al2O3/graphene, whether 1L or FL graphene is strongly damaged under our process conditions. For the case of HfO2/graphene, muRS analysis clearly shows that FL graphene is less disordered than 1L graphene. In addition, the damage levels in FL graphene decrease with the number of layers. Moreover, the FL graphene damage is inversely proportional to the thickness of HfO2 film. Particularly, the bottom layer of twisted bilayer (t-2L) has the salient features of 1L graphene. Therefore, FL graphene allows for controlling/limiting the degree of defect during the PE-ALD HfO2 of dielectrics and could be a good starting material for building field effect transistors, sensors, touch screens and solar cells. Besides, the formation of Hf-C bonds may favor growing high-quality and uniform-coverage dielectric. HfO2 could be a suitable high-K gate dielectric with a scaling capability down to sub-5-nm for graphene-based transistors.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.259
Times cited: 18
DOI: 10.1038/srep13523
|
|
|
“Prussian blue analogues of reduced dimensionality”. Gengler RYN, Toma LM, Pardo E, Lloret F, Ke X, Van Tendeloo G, Gournis D, Rudolf P, Small 8, 2532 (2012). http://doi.org/10.1002/smll.201200517
Abstract: Mixed-valence polycyanides (Prussian Blue analogues) possess a rich palette of properties spanning from room-temperature ferromagnetism to zero thermal expansion, which can be tuned by chemical modifications or the application of external stimuli (temperature, pressure, light irradiation). While molecule-based materials can combine physical and chemical properties associated with molecular-scale building blocks, their successful integration into real devices depends primarily on higher-order properties such as crystal size, shape, morphology, and organization. Herein a study of a new reduced-dimensionality system based on Prussian Blue analogues (PBAs) is presented. The system is built up by means of a modified Langmuir-Blodgett technique, where the PBA is synthesized from precursors in a self-limited reaction on a clay mineral surface. The focus of this work is understanding the magnetic properties of the PBAs in different periodic, low-dimensional arrangements, and the influence of the “on surface” synthesis on the final properties and dimensionality of the system.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 8.643
Times cited: 17
DOI: 10.1002/smll.201200517
|
|
|
“Quantifying inflow uncertainties for CFD simulations of the flow in downtown Oklahoma City”. García-Sánchez C, Philips DA, Gorlé, C, Building and environment 78, 118 (2014). http://doi.org/10.1016/j.buildenv.2014.04.013
Abstract: Computational Fluid Dynamics (CFD) methods are widely used to investigate wind flow and dispersion in urban environments. Validation with field experiments that represent the full complexity of the problem should be performed to assess the predictive capabilities of the computations. In this context it will be necessary to quantify the effect of uncertainties in simulations of the full-scale problem. The present study aims at quantifying the uncertainty related to the variability in the inflow boundary conditions for Reynolds-averaged Navier-Stokes (RANS) simulations of the flow in downtown Oklahoma City to address validation with the Joint Urban 2003 field measurements. Three uncertain inflow parameters were defined: the wind speed and wind direction at a reference height, and the aerodynamic roughness in the logarithmic velocity inlet profile. An ensemble of 729 RANS simulations were performed to determine the polynomial chaos expansion coefficients that define the response surfaces for the velocity magnitude and direction at 13 field measurement stations, and the results are compared to the experimental data. For the velocity magnitude the mean experimental velocity magnitude is encompassed within the 95% confidence interval for the magnitudes predicted by the Uncertainty Quantification study in all stations. For the velocity direction this holds in 11 out of 13 locations. The study demonstrates the significant potential of applying advanced uncertainty quantification methods to address validation with field measurements and to develop a more realistic approach to the definition of inflow boundary conditions in atmospheric CFD simulations. (C) 2014 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.053
Times cited: 29
DOI: 10.1016/j.buildenv.2014.04.013
|
|
|
“Quantitative 3-D morphologic and distributional study of Ni4Ti3 precipitates in a Ni51Ti49 single crystal alloy”. Cao S, Pourbabak S, Schryvers D, Scripta materialia 66, 650 (2012). http://doi.org/10.1016/j.scriptamat.2012.01.045
Abstract: The size, shape and distribution of Ni4Ti3 precipitates in Ni51Ti49 single crystals annealed under stress-free and 〈1 1 1〉B2 compressive conditions are studied via focused ion beam/scanning electron microscopy slice-and-view. The precipitates in the stress-free material grow in autocatalytic pockets with larger size, lower number density, flatter shape and larger inter-particle distance than in the compressed material. Nevertheless, a new quantification method called water penetration reveals that, due to the precipitate alignment, martensite can grow more easily in the compressed material perpendicular to the compression direction.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 8
DOI: 10.1016/j.scriptamat.2012.01.045
|
|
|
“Quantitative study of particle size distribution in an in-situ grown Al-TiB2 composite by synchrotron X-ray diffraction and electron microscopy”. Tang Y, Chen Z, Borbely A, Ji G, Zhong SY, Schryvers D, Ji V, Wang HW, Materials characterization 102, 131 (2015). http://doi.org/10.1016/j.matchar.2015.03.003
Abstract: Synchrotron X-ray diffraction and transmission electron microscopy (TEM) were applied to quantitatively characterize the average particle size and size distribution of free-standing TiB2 particles and TiB2 particles in an insitu grown Al–TiB2 composite. The detailed evaluations were carried out by X-ray line profile analysis using the restrictedmoment method and multiplewhole profile fitting procedure (MWP). Both numericalmethods indicate that the formed TiB2 particles are well crystallized and free of crystal defects. The average particle size determined from different Bragg reflections by the restricted moment method ranges between 25 and 55 nm, where the smallest particle size is determined using the 110 reflection suggesting the highest lateral-growth velocity of (110) facets. TheMWP method has shown that the in-situ grown TiB2 particles have a very low dislocation density (~1011 m−2) and their size distribution can be described by a log-normal distribution. Good agreement was found between the results obtained from the restricted moment and MWP methods, which was further confirmed by TEM.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.714
Times cited: 41
DOI: 10.1016/j.matchar.2015.03.003
|
|
|
“R-phase transition and related mechanical properties controlled by low-temperature aging treatment in a Ti50.8 at.% Ni thin wire”. Wang X, Li K, Schryvers D, Verlinden B, Van Humbeeck J, Scripta materialia 72-73, 21 (2014). http://doi.org/10.1016/j.scriptamat.2013.10.006
Abstract: A cold-drawn Ti50.8 at.% Ni wire was annealed at 600 °C for 30 min, followed by aging at 250 °C for different times. A microstructure with small grains and nanoscaled precipitates was obtained. The thermally induced martensite transformation is suppressed in the samples aged for 4 h or longer, leaving a one-stage R-phase transition between −150 and +150 °C. The transformation behavior, work output and recovery stress associated with the R-phase transition are presented.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 27
DOI: 10.1016/j.scriptamat.2013.10.006
|
|
|
“Recent EM investigations on nano-and micro-defect structures in SMAs”. Schryvers D, Cao S, Pourbabak, Shi H, Lu, Journal of alloys and compounds 577, S705 (2013). http://doi.org/10.1016/j.jallcom.2011.10.112
Abstract: The present contribution reviews some recent electron microscopy investigations on different shape memory systems in which a variety of nano- and micro-defect structures play an essential role in the functional behaviour of the material. (NiTi3)-Ti-4 precipitates in Ni-Ti are a well-known example for which the focus is now on the 3D configurations, in Ni-Ti-Nb Nb-rich nanoprecipitates are thought to have a large impact on the hysteresis, in Co-Ni-Al an Al-enriched zone nearby the y'-precipitates yields a small sandwiched austenite while some first signs of quasidynamical lattice deformation in non-frozen Ni-Ti strain glass are measured by Cs-aberration-corrected transmission electron microscopy. (C) 2011 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 7
DOI: 10.1016/j.jallcom.2011.10.112
|
|
|
“Relaxor ferroelectricity and magnetoelectric coupling in ZnOCo nanocomposite thin films : beyond multiferroic composites”. Li DY, Zeng YJ, Batuk D, Pereira LMC, Ye ZZ, Fleischmann C, Menghini M, Nikitenko S, Hadermann J, Temst K, Vantomme A, Van Bael MJ, Locquet JP, Van Haesendonck C;, ACS applied materials and interfaces 6, 4737 (2014). http://doi.org/10.1021/am4053877
Abstract: ZnOCo nanocomposite thin films are synthesized by combination of pulsed laser deposition of ZnO and Co ion implantation. Both superparamagnetism and relaxor ferroelectricity as well as magnetoelectric coupling in the nanocomposites have been demonstrated. The unexpected relaxor ferroelectricity is believed to be the result of the local lattice distortion induced by the incorporation of the Co nanoparticles. Magnetoelectric coupling can be attributed to the interaction between the electric dipole moments and the magnetic moments, which are both induced by the incorporation of Co. The introduced ZnOCo nanocomposite thin films are different from conventional strain-mediated multiferroic composites.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.504
Times cited: 21
DOI: 10.1021/am4053877
|
|
|
“Revealing the innermost nanostructure of sputtered NiCrOx solar absorber cermets”. Gaouyat L, He Z, Colomer J-F, Lambin P, Mirabella F, Schryvers D, Deparis O, Solar energy materials and solar cells 122, 303 (2014). http://doi.org/10.1016/j.solmat.2013.10.009
Abstract: Conversion of solar energy into thermal energy helps reducing consumption of non-renewable energies. Cermets (ceramicmetal composites) are versatile materials suitable, amongst other applications, for solar selective absorbers. Although the presence of metallic Ni particles in the dielectric matrix is a prerequisite for efficient solar selective absorption in NiCrOx cermets, no clear evidence of such particles is reported so far. By combining comprehensive chemical and structural analyses, we reveal the presumed nanostructure which is at the origin of the remarkable optical properties of this cermet material. Using sputtered NiCrOx layers in a solar absorber multilayer stack on aluminium substrate allows us to achieve solar absorptance as high as α=96.1% while keeping thermal emissivity as low as ε=2.2%, both values being comparable to best values recorded so far. With the nanostructure of sputtered NiCrOx cermets eventually revealed, further optimization of solar absorbers can be anticipated and technological exploitation of cermet materials in other applications can be foreseen.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.784
Times cited: 12
DOI: 10.1016/j.solmat.2013.10.009
|
|
|
“Role of PdOx and RuOy clusters in oxygen exchange between nanocrystalline tin dioxide and the gas phase”. Marikutsa AV, Rumyantseva MN, Frolov DD, Morozov IV, Boltalin AI, Fedorova AA, Petukhov IA, Yashina LV, Konstantinova EA, Sadovskaya EM, Abakumov AM, Zubavichus YV, Gaskov AM;, The journal of physical chemistry: C : nanomaterials and interfaces 117, 23858 (2013). http://doi.org/10.1021/jp408646k
Abstract: The effect of palladium- and ruthenium-based clusters on nanocrystalline tin dioxide interaction with oxygen was studied by temperature-programmed oxygen isotopic exchange with mass-spectrometry detection. The modification of aqueous sol-gel prepared SnO2 by palladium and, to a larger extent, by ruthenium, increases surface oxygen concentration on the materials. The revealed effects on oxygen exchange-lowering the threshold temperature, separation of surface oxygen contribution to the process, increase of heteroexchange rate and oxygen diffusion coefficient, decrease of activation energies of exchange and diffusion-were more intensive for Ru-modified SnO2 than in the case of SnO2/Pd. The superior promoting activity of ruthenium on tin dioxide interaction with oxygen was interpreted by favoring the dissociative O-2 adsorption and increasing the oxygen mobility, taking into account the structure and chemical composition of the modifier clusters.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.536
Times cited: 20
DOI: 10.1021/jp408646k
|
|
|
“Selectivity in sorption and hydrogenation of methyl oleate and elaidate on MFI zeolites”. Philippaerts A, Paulussen S, Turner S, Lebedev OI, Van Tendeloo G, Poelman H, Bulut M, de Clippel F, Smeets P, Sels B, Jacobs P, Journal of catalysis 270, 172 (2010). http://doi.org/10.1016/j.jcat.2009.12.022
Abstract: Different zeolites were tested for selective removal of methyl elaidate (trans isomer) from an equimolar mixture with methyl oleate (cis isomer). Sorption experiments of the geometric isomers show that only ZSM-5 samples with reduced Al content in the framework are able to discriminate among the bent cis and the linear trans fatty acid methyl esters. Hydrogenation experiments of equimolar methyl oleate and elaidate mixtures at low temperature (65 °C) and high hydrogen pressure (6.0 MPa), using Pt catalysts, confirm this result. Only with a Pt/NaZSM-5 catalyst outspoken selectivity for the hydrogenation of the trans isomer is obtained. In order to prepare a selective Pt/ZSM-5 catalyst, the influence of Pt addition (impregnation, ion-exchange and competitive ion-exchange) and Pt activation (different calcination and reduction temperatures) on the Pt-distribution and Pt particle size was investigated using SEM, bright-field and HR TEM, EDX, electron tomography, CO-chemisorption, XPS, XRD, and UVvis measurements. The best result in terms of hydrogenation activity and selectivity is obtained with a Pt/ZSM-5 catalyst, which is prepared via competitive ion-exchange, followed by slow calcination up to 350 °C under high O2 flow and a reduction up to 500 °C under H2. This preparation method leads to a Pt/ZSM-5 catalyst with the best Pt distribution and the smallest Pt clusters occluded in the zeolite structure. Finally, the influence of zeolite crystal size, morphology, and elemental composition of ZSM-5 on hydrogenation activity and selectivity was investigated in detail.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 6.844
Times cited: 24
DOI: 10.1016/j.jcat.2009.12.022
|
|
|
“Self-directed localization of ZIF-8 thin film formation by conversion of ZnO nanolayers”. Khaletskaya K, Turner S, Tu M, Wannapaiboon S, Schneemann A, Meyer R, Ludwig A, Van Tendeloo G, Fischer RA, Advanced functional materials 24, 4804 (2014). http://doi.org/10.1002/adfm.201400559
Abstract: Control of localized metal-organic framework (MOF) thin film formation is a challenge. Zeolitic imidazolate frameworks (ZIFs) are an important sub-class of MOFs based on transition metals and imidazolate linkers. Continuous coatings of intergrown ZIF crystals require high rates of heterogeneous nucleation. In this work, substrates coated with zinc oxide layers are used, obtained by atomic layer deposition (ALD) or by magnetron sputtering, to provide the Zn2+ ions required for nucleation and localized growth of ZIF-8 films ([Zn(mim)(2)]; Hmim = 2-methylimidazolate). The obtained ZIF-8 films reveal the expected microporosity, as deduced from methanol adsorption studies using an environmentally controlled quartz crystal microbalance (QCM) and comparison with bulk ZIF-8 reference data. The concept is transferable to other MOFs, and is applied to the formation of [Al(OH)(1,4-ndc)](n) (ndc = naphtalenedicarboxylate) thin films derived from Al2O3 nanolayers.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 77
DOI: 10.1002/adfm.201400559
|
|