“Improving the performance of gliding arc plasma-catalytic dry reforming via a new post-plasma tubular catalyst bed”. Xu W, Buelens LC, Galvita VV, Bogaerts A, Meynen V, Journal of CO2 Utilization 83, 102820 (2024). http://doi.org/10.1016/j.jcou.2024.102820
Abstract: A combination of a gliding arc plasmatron (GAP) reactor and a newly designed tubular catalyst bed (N-bed) was applied to investigate the post-plasma catalytic (PPC) effect for dry reforming of methane (DRM). As comparison, a traditional plasma catalyst bed (T-bed) was also utilized. The post-plasma catalytic effect of a Ni-based mixed oxide (Ni/MO) catalyst with a thermal catalytic performance of 77% CO2 and 86% CH4 conversion at 700 ℃ was studied. Although applying the T-bed had little effect on plasma based CO2 and CH4 conversion, an increase in selectivity to H2 was obtained with a maximum value of 89% at a distance of 2 cm. However, even when only α-Al2O3 packing material was used in the N-bed configuration, compared to the plasma alone and the T-bed, an increase of the CO2 and CH4 conversion from 53% and 53% to 69% and 69% to 83% was achieved. Addition of the Ni/MO catalyst further enhanced the DRM reaction, resulting in conversions of 79% for CO2 and 91% for
CH4. Hence, although no insulation nor external heating was applied to the N-bed post plasma, it provides a slightly better conversion than the thermal catalytic performance with the same catalyst, while being fully electrically driven. In addition, an enhanced CO selectivity to 96% was obtained and the energy cost was reduced from ~ 6 kJ/L (plasma alone) to 4.3 kJ/L. To our knowledge, it is the first time that a post-plasma catalytic system achieves this excellent catalytic performance for DRM without extra external heating or insulation.
Keywords: A1 Journal Article; Dry reforming Gliding arc plasma Plasma catalytic DRM Ni-based mixed oxide Post-plasma catalysis; Plasma, laser ablation and surface modeling Antwerp (PLASMANT) ;
Impact Factor: 7.7
DOI: 10.1016/j.jcou.2024.102820
|
“Assessing policy impacts on nutrient circularity : a comprehensive review”. Teleshkan E, Van Schoubroeck S, Spiller M, Van Passel S, Nutrient cycling in agroecosystems , 1 (2024). http://doi.org/10.1007/S10705-024-10340-1
Abstract: Nutrient circularity is an emerging concept that seeks to address the environmental problems and nutrient losses caused by agriculture and food consumption. The implementation of circular nutrient technologies and practices (CNTPs), that recover, reuse, and recycle nutrients from agricultural and urban waste is an important policy objective. Yet, which policies govern the adoption of CNTPs is not well defined. This study presents the first systematic review of impact evaluations of policy measures that aim to improve nutrient circularity regulating components of the biological cycle of the circular economy, particularly focusing on bioaccessible nutrients. The key CNTPs that were subject to existing impact evaluations were identified. CNTPs were categorized into nutrient circularity themes, with manure management emerging as a prominent focus. The reviewed studies implemented several methods to assess the impacts of policies on various dependent variables, associated with nutrient circularity. Economic simulation models and linear programming were the most prevalent methods for impact evaluation. Policy measures were labeled as either enabling or not-enabling nutrient circularity based on whether they sufficiently promoted nutrient circularity through facilitating the adoption of CNTPs, and controlling for soil, water and air health, preventing its contamination. It is concluded that incentive policies, harmonizing market support, tax incentives, and technological advancements, as well as coherence of local, national and cross-country legislation prove indispensable in steering the economic feasibility and sustainability of CNTPs, offering a promising avenue for progress and a transformative shift towards nutrient circularity.
Keywords: A1 Journal article; Economics; Engineering sciences. Technology; Engineering Management (ENM)
Impact Factor: 3.1
DOI: 10.1007/S10705-024-10340-1
|
“Sailing through end-of-life challenges : a comprehensive review for offshore wind”. Vetters J, Thomassen G, Van Passel S, Renewable and sustainable energy reviews 199, 114486 (2024). http://doi.org/10.1016/J.RSER.2024.114486
Abstract: Over the past thirty years, European offshore wind farm development surged, yet end-of-life and decommissioning considerations were overshadowed by initial climate and energy security objectives during design and construction. As the first major projects near their final decade, numerous unanswered questions persist. Through a comprehensive literature review, this study identifies, maps, and evaluates challenges across technical, economic, environmental, social, and policy dimensions spanning five end-of-life phases: planning, dismantling, transport and logistics, waste management, and site recovery. Examining 42 publications reveals 46 distinct challenges affecting stakeholders such as the end-of-life supply chain, policy makers, and society. While 33% of the challenges manifested in the technical dimension, 48% of the challenges covered the planning phase. Notably, the economic challenge of vessel cost and availability was raised most often. Less-explored challenges underscore the importance of consideration before the end-of-life phase intensifies. The study illustrates the complex interconnection of numerous end-of-life challenges across phases, dimensions, and disciplines, emphasizing the imperative of addressing bottlenecks in a comprehensive and integrated manner. The results of this study help steering future research, while also improving awareness of challenges for stakeholders, emphasizing the need for collaborative efforts between governmental bodies and industry stakeholders to address imminent challenges through transparent guidelines, data exchange, and circular design principles. The novelty of this study lies in its holistic, multidisciplinary approach, systematic framework for identifying challenges, and critical perspective unveiling interconnectedness.
Keywords: A1 Journal article; Economics; Engineering sciences. Technology; Engineering Management (ENM)
Impact Factor: 15.9
DOI: 10.1016/J.RSER.2024.114486
|
“Using natural language processing to monitor circular activities and employment”. Borms L, Multani M, Bachus K, Dams Y, Brusselaers J, Van Passel S, Sustainable Production and Consumption 46, 42 (2024). http://doi.org/10.1016/J.SPC.2024.02.007
Abstract: In Europe, NACE codes are used for the official classification of sectors, however, the circular economy is not sufficiently captured in this classification. Therefore, this paper improves previous attempts for defining circular activities and jobs by web scraping techniques applied to each company in Belgium. We analyze their first, second, and third official NACE codes and compare these to the NACE codes they should have been allocated to according to the web scraping data. Subsequently, we calculate circularity scores for every sector to construct an indicator for the number of circular companies and jobs. The results show that the number of circular companies is lower than the baseline from official statistics when we only consider the companies' first and main NACE code. The estimates are higher than the baseline when we also take the second and third NACE codes into account and the estimated number of circular jobs is far higher than the baseline. This research upgrades previous classifications of circular sectors and demonstrates how web scraping and novel data might improve our understanding and capacity to build data. Based on the results in this paper, we recommend a uniform data collection such as reporting standards, and an inclusion of all circular strategies in sectoral classifications.
Keywords: A1 Journal article; Economics; Engineering sciences. Technology; Engineering Management (ENM); Herman Deleeck Centre for Social Policy
Impact Factor: 12.1
DOI: 10.1016/J.SPC.2024.02.007
|
“Economic and environmental implications of policy instruments for the circular economy : a case study for postconsumer polyethylene film recycling in Europe”. Larraín M, Billen P, Cifuentes L, Van Passel S, Resources, conservation and recycling 204, 107519 (2024). http://doi.org/10.1016/J.RESCONREC.2024.107519
Abstract: The objective of this paper is to examine the recycling rates for mechanical and thermochemical recycling of postconsumer polyethylene flexible packaging after the implementation of different policy instruments. The study uses a supply chain equilibrium model that incorporates market data and techno-economic assessments to simulate market equilibrium. It combines this with a life cycle assessment to explore the environmental implications of implementing different policy instruments. The results show that instruments that do not target a specific technology are more likely to increase thermochemical recycling than mechanical recycling. Furthermore, a higher recycling rate is not equivalent to a better environmental outcome. An increased collection target that ensures a supply of plastic waste would increase the overall recycling rates the most. A recycled content standard for mechanical recycling would lead to the highest increase in mechanical recycling, with top results for environmental indicators, but low results for economic indicators.
Keywords: A1 Journal article; Economics; Engineering sciences. Technology; Engineering Management (ENM); Intelligence in PRocesses, Advanced Catalysts and Solvents (iPRACS)
Impact Factor: 13.2
DOI: 10.1016/J.RESCONREC.2024.107519
|
“A Pareto aggregation approach for environmental-economic multi-objective optimization applied on a second-generation bioethanol production model”. Vasilakou K, Billen P, Van Passel S, Nimmegeers P, Energy conversion and management 303, 118184 (2024). http://doi.org/10.1016/J.ENCONMAN.2024.118184
Abstract: Multi-objective optimization is an important decision-making tool for energy processes, as multiple targets need to be achieved. These objectives are usually conflicting since a single solution cannot be optimal for all objectives, resulting in a set of Pareto-optimal solutions. Multiple indicators might be available to describe a sustainability objective, such as the environmental impact which is commonly evaluated by performing a life cycle assessment. In this study, Pareto aggregation is proposed as a method which employs a novel multi-objective optimization-based approach as an alternative to the classically used aggregation in life cycle assessment. This method identifies conflicting environmental indicators and performs an aggregation among those that require a trade-off. An environmental-economic optimization of a second-generation bioethanol plant is used to illustrate and evaluate the proposed method. Process parameters from a biochemical conversion pathway flowsheet simulation model are chosen as optimization variables. To reduce the computational time, surrogate models, based on artificial neural networks, are used. Out of the eighteen ReCiPe Midpoint environmental indicators, five were identified as conflicting, resulting in an aggregated environmental objective, which was then traded off with the economic objective function, chosen as the levelized cost of ethanol. Comparison with the widely used single-score EcoIndicator99 showed that the Pareto aggregation method can reduce most of the environmental indicators by up to 6.5%. This research provides an insight on non-redundant objective functions, aiming at reducing the dimensionality of multi-objective optimization problems, while taking into consideration decision-makers’ preferences.
Keywords: A1 Journal article; Economics; Engineering sciences. Technology; Engineering Management (ENM); Intelligence in PRocesses, Advanced Catalysts and Solvents (iPRACS)
Impact Factor: 10.4
DOI: 10.1016/J.ENCONMAN.2024.118184
|
“Phase offset method of ptychographic contrast reversal correction”. Hofer C, Gao C, Chennit T, Yuan B, Pennycook TJ, Ultramicroscopy , 113922 (2024). http://doi.org/10.1016/j.ultramic.2024.113922
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.2
DOI: 10.1016/j.ultramic.2024.113922
|
“Deep convolutional neural networks to restore single-shot electron microscopy images”. Lobato I, Friedrich T, Van Aert S, N P J Computational Materials 10, 10 (2024). http://doi.org/10.1038/s41524-023-01188-0
Abstract: Advanced electron microscopy techniques, including scanning electron microscopes (SEM), scanning transmission electron microscopes (STEM), and transmission electron microscopes (TEM), have revolutionized imaging capabilities. However, achieving high-quality experimental images remains a challenge due to various distortions stemming from the instrumentation and external factors. These distortions, introduced at different stages of imaging, hinder the extraction of reliable quantitative insights. In this paper, we will discuss the main sources of distortion in TEM and S(T)EM images, develop models to describe them, and propose a method to correct these distortions using a convolutional neural network. We validate the effectiveness of our method on a range of simulated and experimental images, demonstrating its ability to significantly enhance the signal-to-noise ratio. This improvement leads to a more reliable extraction of quantitative structural information from the images. In summary, our findings offer a robust framework to enhance the quality of electron microscopy images, which in turn supports progress in structural analysis and quantification in materials science and biology.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1038/s41524-023-01188-0
|
“Atom counting from a combination of two ADF STEM images”. Şentürk DG, Yu CP, De Backer A, Van Aert S, Ultramicroscopy 255, 113859 (2024). http://doi.org/10.1016/j.ultramic.2023.113859
Abstract: To understand the structure–property relationship of nanostructures, reliably quantifying parameters, such as the number of atoms along the projection direction, is important. Advanced statistical methodologies have made it possible to count the number of atoms for monotype crystalline nanoparticles from a single ADF STEM image. Recent developments enable one to simultaneously acquire multiple ADF STEM images. Here, we present an extended statistics-based method for atom counting from a combination of multiple statistically independent ADF STEM images reconstructed from non-overlapping annular detector collection regions which improves the accuracy and allows one to retrieve precise atom-counts, especially for images acquired with low electron doses and multiple element structures.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.2
DOI: 10.1016/j.ultramic.2023.113859
|
“Disproportionation of Co2+ in the topochemically reduced oxide LaSrCoRuO₅”. Liang Z, Batuk M, Orlandi F, Manuel P, Hadermann J, Hayward MA, Angewandte Chemie: international edition in English 63, e202313067 (2024). http://doi.org/10.1002/ANIE.202313067
Abstract: Complex transition-metal oxides exhibit a wide variety of chemical and physical properties which are a strong function the local electronic states of the transition-metal centres, as determined by a combination of metal oxidation state and local coordination environment. Topochemical reduction of the double perovskite oxide, LaSrCoRuO6, using Zr, yields LaSrCoRuO5. This reduced phase contains an ordered array of apex-linked square-based pyramidal Ru3+O5, square-planar Co1+O4 and octahedral Co3+O6 units, consistent with the coordination-geometry driven disproportionation of Co2+. Coordination-geometry driven disproportionation of d(7) transition-metal cations (e.g. Rh2+, Pd3+, Pt3+) is common in complex oxides containing 4d and 5d metals. However, the weak ligand field experienced by a 3d transition-metal such as cobalt leads to the expectation that d(7+) Co2+ should be stable to disproportionation in oxide environments, so the presence of Co1+O4 and Co3+O6 units in LaSrCoRuO5 is surprising. Low-temperature measurements indicate LaSrCoRuO5 adopts a ferromagnetically ordered state below 120 K due to couplings between S=(1)/(2) Ru3+ and S=1 Co1+.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 16.6
DOI: 10.1002/ANIE.202313067
|
“On central focusing for contrast optimization in direct electron ptychography of thick samples”. Gao C, Hofer C, Pennycook TJ, Ultramicroscopy 256, 113879 (2024). http://doi.org/10.1016/J.ULTRAMIC.2023.113879
Abstract: Ptychography provides high dose efficiency images that can reveal light elements next to heavy atoms. However, despite ptychography having an otherwise single signed contrast transfer function, contrast reversals can occur when the projected potential becomes strong for both direct and iterative inversion ptychography methods. It has recently been shown that these reversals can often be counteracted in direct ptychography methods by adapting the focus. Here we provide an explanation of why the best contrast is often found with the probe focused to the middle of the sample. The phase contribution due to defocus at each sample slice above and below the central plane in this configuration effectively cancels out, which can prevent contrast reversals when dynamical scattering effects are not overly strong. In addition we show that the convergence angle can be an important consideration for removal of contrast reversals in relatively thin samples.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.2
DOI: 10.1016/J.ULTRAMIC.2023.113879
|
“AuNP/MIL-88B-NH₂, nanocomposite for the valorization of nitroarene by green catalytic hydrogenation”. Lelouche SNK, Lemir I, Biglione C, Craig T, Bals S, Horcajada P, Chemistry: a European journal , 1 (2024). http://doi.org/10.1002/CHEM.202400442
Abstract: The efficiency of a catalytic process is assessed based on conversion, yield, and time effectiveness. However, these parameters are insufficient for evaluating environmentally sustainable research. As the world is urged to shift towards green catalysis, additional factors such as reaction media, raw material availability, sustainability, waste minimization and catalyst biosafety, need to be considered to accurately determine the efficacy and sustainability of the process. By combining the high porosity and versatility of metal organic frameworks (MOFs) and the activity of gold nanoparticles (AuNPs), efficient, cyclable and biosafe composite catalysts can be achieved. Thus, a composite based on AuNPs and the nanometric flexible porous iron(III) aminoterephthalate MIL-88B-NH2 was successfully synthesized and fully characterized. This nanocomposite was tested as catalyst in the reduction of nitroarenes, which were identified as anthropogenic water pollutants, reaching cyclable high conversion rates at short times for different nitroarenes. Both synthesis and catalytic reactions were performed using green conditions, and even further tested in a time-optimizing one-pot synthesis and catalysis experiment. The sustainability and environmental impact of the catalytic conditions were assessed by green metrics. Thus, this study provides an easily implementable synthesis, and efficient catalysis, while minimizing the environmental and health impact of the process.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.3
DOI: 10.1002/CHEM.202400442
|
“Enhanced electrical properties of Bi2-xSbxTe3 nanoflake thin films through interface engineering”. Wu X, Ding J, Cui W, Lin W, Xue Z, Yang Z, Liu J, Nie X, Zhu W, Van Tendeloo G, Sang X, Energy &, environment materials , e12755 (2024). http://doi.org/10.1002/EEM2.12755
Abstract: The structure-property relationship at interfaces is difficult to probe for thermoelectric materials with a complex interfacial microstructure. Designing thermoelectric materials with a simple, structurally-uniform interface provides a facile way to understand how these interfaces influence the transport properties. Here, we synthesized Bi2-xSbxTe3 (x = 0, 0.1, 0.2, 0.4) nanoflakes using a hydrothermal method, and prepared Bi2-xSbxTe3 thin films with predominantly (0001) interfaces by stacking the nanoflakes through spin coating. The influence of the annealing temperature and Sb content on the (0001) interface structure was systematically investigated at atomic scale using aberration-corrected scanning transmission electron microscopy. Annealing and Sb doping facilitate atom diffusion and migration between adjacent nanoflakes along the (0001) interface. As such it enhances interfacial connectivity and improves the electrical transport properties. Interfac reactions create new interfaces that increase the scattering and the Seebeck coefficient. Due to the simultaneous optimization of electrical conductivity and Seebeck coefficient, the maximum power factor of the Bi1.8Sb0.2Te3 nanoflake films reaches 1.72 mW m(-1) K-2, which is 43% higher than that of a pure Bi2Te3 thin film.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1002/EEM2.12755
|
“Refining short-range order parameters from the three-dimensional diffuse scattering in single-crystal electron diffraction data”. Poppe R, Roth N, Neder RB, Palatinus L, Iversen BB, Hadermann J, IUCrJ 11, 82 (2024). http://doi.org/10.1107/S2052252523010254
Abstract: Our study compares short-range order parameters refined from the diffuse scattering in single-crystal X-ray and single-crystal electron diffraction data. Nb0.84CoSb was chosen as a reference material. The correlations between neighbouring vacancies and the displacements of Sb and Co atoms were refined from the diffuse scattering using a Monte Carlo refinement in DISCUS. The difference between the Sb and Co displacements refined from the diffuse scattering and the Sb and Co displacements refined from the Bragg reflections in single-crystal X-ray diffraction data is 0.012 (7) angstrom for the refinement on diffuse scattering in single-crystal X-ray diffraction data and 0.03 (2) angstrom for the refinement on the diffuse scattering in single-crystal electron diffraction data. As electron diffraction requires much smaller crystals than X-ray diffraction, this opens up the possibility of refining short-range order parameters in many technologically relevant materials for which no crystals large enough for single-crystal X-ray diffraction are available.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.9
DOI: 10.1107/S2052252523010254
|
“Tailoring mechanical properties and shear band propagation in ZrCu metallic glass nanolaminates through chemical heterogeneities and interface density”. Brognara A, Kashiwar A, Jung C, Zhang X, Ahmadian A, Gauquelin N, Verbeeck J, Djemia P, Faurie D, Dehm G, Idrissi H, Best JP, Ghidelli M, Small Structures , 2400011 (2024). http://doi.org/10.1002/SSTR.202400011
Abstract: The design of high‐performance structural thin films consistently seeks to achieve a delicate equilibrium by balancing outstanding mechanical properties like yield strength, ductility, and substrate adhesion, which are often mutually exclusive. Metallic glasses (MGs) with their amorphous structure have superior strength, but usually poor ductility with catastrophic failure induced by shear bands (SBs) formation. Herein, we introduce an innovative approach by synthesizing MGs characterized by large and tunable mechanical properties, pioneering a nanoengineering design based on the control of nanoscale chemical/structural heterogeneities. This is realized through a simplified model Zr 24 Cu 76 /Zr 61 Cu 39 , fully amorphous nanocomposite with controlled nanoscale periodicity ( Λ , from 400 down to 5 nm), local chemistry, and glass–glass interfaces, while focusing in‐depth on the SB nucleation/propagation processes. The nanolaminates enable a fine control of the mechanical properties, and an onset of crack formation/percolation (>1.9 and 3.3%, respectively) far above the monolithic counterparts. Moreover, we show that SB propagation induces large chemical intermixing, enabling a brittle‐to‐ductile transition when Λ ≤ 50 nm, reaching remarkably large plastic deformation of 16% in compression and yield strength ≈2 GPa. Overall, the nanoengineered control of local heterogeneities leads to ultimate and tunable mechanical properties opening up a new approach for strong and ductile materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1002/SSTR.202400011
|
“Comparative analysis of tight-binding models for transition metal dichalcogenides”. Jorissen B, Covaci L, Partoens B, SciPost physics core 7, 004 (2024). http://doi.org/10.21468/SCIPOSTPHYSCORE.7.1.004
Abstract: We provide a comprehensive analysis of the prominent tight-binding (TB) models for transition metal dichalcogenides (TMDs) available in the literature. We inspect the construction of these TB models, discuss their parameterization used and conduct a thorough comparison of their effectiveness in capturing important electronic properties. Based on these insights, we propose a novel TB model for TMDs designed for enhanced computational efficiency. Utilizing MoS2 as a representative case, we explain why specific models offer a more accurate description. Our primary aim is to assist researchers in choosing the most appropriate TB model for their calculations on TMDs.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
DOI: 10.21468/SCIPOSTPHYSCORE.7.1.004
|
“In Situ Plasma Studies Using a Direct Current Microplasma in a Scanning Electron Microscope”. Grünewald L, Chezganov D, De Meyer R, Orekhov A, Van Aert S, Bogaerts A, Bals S, Verbeeck J, Advanced Materials Technologies (2024). http://doi.org/10.1002/admt.202301632
Abstract: Microplasmas can be used for a wide range of technological applications and to improve the understanding of fundamental physics. Scanning electron microscopy, on the other hand, provides insights into the sample morphology and chemistry of materials from the mm‐ down to the nm‐scale. Combining both would provide direct insight into plasma‐sample interactions in real‐time and at high spatial resolution. Up till now, very few attempts in this direction have been made, and significant challenges remain. This work presents a stable direct current glow discharge microplasma setup built inside a scanning electron microscope. The experimental setup is capable of real‐time in situ imaging of the sample evolution during plasma operation and it demonstrates localized sputtering and sample oxidation. Further, the experimental parameters such as varying gas mixtures, electrode polarity, and field strength are explored and experimental<italic>V</italic>–<italic>I</italic>curves under various conditions are provided. These results demonstrate the capabilities of this setup in potential investigations of plasma physics, plasma‐surface interactions, and materials science and its practical applications. The presented setup shows the potential to have several technological applications, for example, to locally modify the sample surface (e.g., local oxidation and ion implantation for nanotechnology applications) on the µm‐scale.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 6.8
DOI: 10.1002/admt.202301632
|
“Element specific atom counting for heterogeneous nanostructures: Combining multiple ADF STEM images for simultaneous thickness and composition determination”. Şentürk DG, De Backer A, Van Aert S, Ultramicroscopy 259, 113941 (2024). http://doi.org/10.1016/j.ultramic.2024.113941
Abstract: In this paper, a methodology is presented to count the number of atoms in heterogeneous nanoparticles based on the combination of multiple annular dark field scanning transmission electron microscopy (ADF STEM) images. The different non-overlapping annular detector collection regions are selected based on the principles of optimal statistical experiment design for the atom-counting problem. To count the number of atoms, the total intensities of scattered electrons for each atomic column, the so-called scattering cross-sections, are simultaneously compared with simulated library values for the different detector regions by minimising the squared differences. The performance of the method is evaluated for simulated Ni@Pt and Au@Ag core-shell nanoparticles. Our approach turns out to be a dose efficient alternative for the investigation of beam-sensitive heterogeneous materials as compared to the combination of ADF STEM and energy dispersive X-ray spectroscopy.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 2.2
DOI: 10.1016/j.ultramic.2024.113941
|
“Incommensurate Modulations and Perovskite Growth in LaxSr2–xMnO4−δAffecting Solid Oxide Fuel Cell Conductivity”. Vandemeulebroucke D, Batuk M, Hajizadeh A, Wastiaux M, Roussel P, Hadermann J, Chemistry of Materials (2024). http://doi.org/10.1021/acs.chemmater.3c03199
Abstract: Ruddlesden-Popper La????Sr2−????MnO4−???? materials are interesting symmetric solid oxide
fuel cell electrodes due to their good redox stability, mixed ionic and electronic conducting behavior and thermal expansion that matches well with common electrolytes. In reducing environments – as at a solid oxide fuel cell anode – the x = 0.5 member, i.e. La0.5Sr1.5MnO4−????, has a much higher total conductivity than compounds with a different La/Sr ratio, although all those compositions have the same K2NiF4-type I4/mmm structure. The origin for this conductivity difference is not yet known in literature. Now, a combination of in-situ and ex-situ 3D electron diffraction, high-resolution imaging, energy-dispersive X-ray analysis and electron energy-loss spectroscopy uncovered clear differences between x=0.25 and x=0.5 in the pristine structure, as well as in the transformations upon high-temperature reduction. In La0.5Sr1.5MnO4−????, Ruddlesden-Popper n=2 layer defects and an amorphous surface layer are present, but not in La0.25Sr1.75MnO4−????. After annealing at 700°C in 5% H2/Ar, La0.25Sr1.75MnO4−???? transforms to a tetragonal 2D incommensurately modulated structure with modulation vectors ⃗????1 = 0.2848(1) · (⃗????* +⃗????*) and ⃗????2 =0.2848(1) · (⃗????* – ⃗????*), whereas La0.5Sr1.5MnO4−???? only partially transforms to an orthorhombic 1D incommensurately modulated structure,
with ⃗???? = 0.318(2) · ⃗????*. Perovskite domains grow at the crystal edge at 700°C in 5%
H2 or vacuum, due to the higher La concentration on the surface compared to the bulk, which leads to a different thermodynamic equilibrium. Since it is known that a lower degree of oxygen vacancy ordering and a higher amount of perovskite blocks enhance oxygen mobility, those differences in defect structure and structural transformation upon reduction, might all contribute to the higher conductivity of La0.5Sr1.5MnO4−???? in solid oxide fuel cell anode conditions compared to other La/Sr ratios.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 8.6
DOI: 10.1021/acs.chemmater.3c03199
|
“Decoding Excimer Formation in Covalent–Organic Frameworks Induced by Morphology and Ring Torsion”. Chakraborty J, Chatterjee A, Molkens K, Nath I, Arenas Esteban D, Bourda L, Watson G, Liu C, Van Thourhout D, Bals S, Geiregat P, Van der Voort P, Advanced Materials (2024). http://doi.org/10.1002/adma.202314056
Abstract: A thorough and quantitative understanding of the fate of excitons in covalent–organic frameworks (COFs) after photoexcitation is essential for their augmented optoelectronic and photocatalytic applications via precise structure tuning. The synthesis of a library of COFs having identical chemical backbone with impeded conjugation, but varied morphology and surface topography to study the effect of these physical properties on the photophysics of the materials is herein reported. The variation of crystallite size and surface topography substantified different aggregation pattern in the COFs, which leads to disparities in their photoexcitation and relaxation properties. Depending on aggregation, an inverse correlation between bulk luminescence decay time and exciton binding energy of the materials is perceived. Further transient absorption spectroscopic analysis confirms the presence of highly localized, immobile, Frenkel excitons (of diameter 0.3–0.5 nm) via an absence of annihilation at high density, most likely induced by structural torsion of the COF skeletons, which in turn preferentially relaxes via long‐lived (nanosecond to microsecond) excimer formation (in femtosecond scale) over direct emission. These insights underpin the importance of structural and topological design of COFs for their targeted use in photocatalysis.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 29.4
DOI: 10.1002/adma.202314056
|
“Enhancing Electrochemical Properties of Walnut Shell Activated Carbon with Embedded MnO Clusters for Supercapacitor Applications”. Esteban DA, Chamocho EG, Carretero González J, Urones Garrote E, Otero Díaz LC, Brande DÁ, Batteries &, Supercaps (2024). http://doi.org/10.1002/batt.202400101
Abstract: Activated carbon (AC) materials from renewable sources are widely used in electrochemical applications due to their well‐known high surface area. However, their application as electrode material in double‐layer electrochemical devices may be limited due to their relatively low electrical conductivity and lightweight. To overcome these limitations, the incorporation of pseudocapacitance metal oxide nanoparticles is an optimum approach. These nanoparticles can provide a second energy storage mechanism to the composite, mitigating the loss of surface area associated with their incorporation. As a result, the composite material is endowed with increased conductivity and higher density, making it more suitable for practical implementation in real devices. In this study, we have incorporated a fine dispersion of 1 % of MnO clusters into a highly porous activated carbon synthesized from walnut shells (WAC). The high‐resolution electron microscopy studies, combined with their related analytical techniques, allow us to determine the presence of the cluster within the matrix carbon precisely. The resulting MnO@WAC composite demonstrated significantly improved capacitive behavior compared with the WAC material, with increased volumetric capacitance and higher charge retention at higher current densities. The composite‘s electrochemical performance suggests its potential as a promising electrode material for supercapacitors, addressing drawbacks associated with traditional AC materials.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
DOI: 10.1002/batt.202400101
|
“Phase coexistence induced surface roughness in V2O3/Ni magnetic heterostructures”. Ignatova K, Vlasov E, Seddon SD, Gauquelin N, Verbeeck J, Wermeille D, Bals S, Hase TPA, Arnalds UB, APL Materials 12 (2024). http://doi.org/10.1063/5.0195961
Abstract: We present an investigation of the microstructure changes in V2O3 as it goes through its inherent structural phase transition. Using V2O3 films with a well-defined crystal structure deposited by reactive magnetron sputtering on r-plane Al2O3 substrates, we study the phase coexistence region and its impact on the surface roughness of the films and the magnetic properties of overlying Ni magnetic layers in V2O3/Ni hybrid magnetic heterostructures. The simultaneous presence of two phases in V2O3 during its structural phase transition was identified with high resolution x-ray diffraction and led to an increase in surface roughness observed using x-ray reflectivity. The roughness reaches its maximum at the midpoint of the transition. In V2O3/Ni hybrid heterostructures, we find a concomitant increase in the coercivity of the magnetic layer correlated with the increased roughness of the V2O3 surface. The chemical homogeneity of the V2O3 is confirmed through transmission electron microscopy analysis. High-angle annular dark field imaging and electron energy loss spectroscopy reveal an atomically flat interface between Al2O3 and V2O3, as well as a sharp interface between V2O3 and Ni.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 6.1
DOI: 10.1063/5.0195961
|
“High-Throughput Morphological Chirality Quantification of Twisted and Wrinkled Gold Nanorods”. Vlasov E, Heyvaert W, Ni B, Van Gordon K, Girod R, Verbeeck J, Liz-Marzán LM, Bals S, ACS Nano (2024). http://doi.org/10.1021/acsnano.4c02757
Abstract: Chirality in gold nanostructures offers an exciting opportunity to tune their differential optical response to left- and right-handed circularly polarized light, as well as their interactions with biomolecules and living matter. However, tuning and understanding such interactions demands quantification of the structural features that are responsible for the chiral behavior. Electron tomography (ET) enables structural characterization at the single-particle level and has been used to quantify the helicity of complex chiral nanorods. However, the technique is time-consuming and consequently lacks statistical value. To address this issue, we introduce herein a high-throughput methodology that combines images acquired by secondary electron-based electron beam-induced current (SEEBIC) with quantitative image analysis. As a result, the geometric chirality of hundreds of nanoparticles can be quantified in less than 1 h. When combining the drastic gain in data collection efficiency of SEEBIC with a limited number of ET data sets, a better understanding of how the chiral structure of individual chiral nanoparticles translates into the ensemble chiroptical response can be reached.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 17.1
DOI: 10.1021/acsnano.4c02757
|
“Scaling-Up Microwave-Assisted Synthesis of Highly Defective Pd@UiO-66-NH2Catalysts for Selective Olefin Hydrogenation under Ambient Conditions”. Guerrero RM, Lemir ID, Carrasco S, Fernández-Ruiz C, Kavak S, Pizarro P, Serrano DP, Bals S, Horcajada P, Pérez Y, ACS Applied Materials &, Interfaces (2024). http://doi.org/10.1021/acsami.4c03106
Abstract: The need to develop green and cost-effective industrial catalytic processes has led to growing interest in preparing more robust, efficient, and selective heterogeneous catalysts at a large scale. In this regard, microwave-assisted synthesis is a fast method for fabricating heterogeneous catalysts (including metal oxides, zeolites, metal–organic frameworks, and supported metal nanoparticles) with enhanced catalytic properties, enabling synthesis scale-up. Herein, the synthesis of nanosized UiO-66-NH2 was optimized via a microwave-assisted hydrothermal method to obtain defective matrices essential for the stabilization of metal nanoparticles, promoting catalytically active sites for hydrogenation reactions (760 kg·m–3·day–1 space time yield, STY). Then, this protocol was scaled up in a multimodal microwave reactor, reaching 86% yield (ca. 1 g, 1450 kg·m–3·day–1 STY) in only 30 min. Afterward, Pd nanoparticles were formed in situ decorating the nanoMOF by an effective and fast microwave-assisted hydrothermal method, resulting in the formation of Pd@UiO-66-NH2 composites. Both the localization and oxidation states of Pd nanoparticles (NPs) in the MOF were achieved using high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) and X-ray photoelectron spectroscopy (XPS), respectively. The optimal composite, loaded with 1.7 wt % Pd, exhibited an extraordinary catalytic activity (>95% yield, 100% selectivity) under mild conditions (1 bar H2, 25 °C, 1 h reaction time), not only in the selective hydrogenation of a variety of single alkenes (1-hexene, 1-octene, 1-tridecene, cyclohexene, and tetraphenyl ethylene) but also in the conversion of a complex mixture of alkenes (i.e., 1-hexene, 1-tridecene, and anethole). The results showed a powerful interaction and synergy between the active phase (Pd NPs) and the catalytic porous scaffold (UiO-66-NH2), which are essential for the selectivity and recyclability.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 9.5
DOI: 10.1021/acsami.4c03106
|
“Refinement of the uranium dispersion corrections from anomalous diffraction”. Leinders G, Grendal OG, Arts I, Bes R, Prozheev I, Orlat S, Fitch A, Kvashnina K, Verwerft M, Journal of Applied Crystallography 57, 284 (2024). http://doi.org/10.1107/S1600576723010889
Abstract: The evolution of the uranium chemical state in uranium compounds, principally in the oxides, is of concern in the context of nuclear fuel degradation under storage and repository conditions, and in accident scenarios. The U–O system shows complicated phase relations between single-valence uranium dioxide (UO<sub>2</sub>) and different mixed-valence compounds (<italic>e.g.</italic>U<sub>4</sub>O<sub>9</sub>, U<sub>3</sub>O<sub>7</sub>and U<sub>3</sub>O<sub>8</sub>). To try resolving the electronic structure associated with unique atomic positions, a combined application of diffraction and spectroscopic techniques, such as diffraction anomalous fine structure (DAFS), can be considered. Reported here is the application of two newly developed routines for assessing a DAFS data set, with the aim of refining the uranium X-ray dispersion corrections. High-resolution anomalous diffraction data were acquired from polycrystalline powder samples of UO<sub>2</sub>(containing tetravalent uranium) and potassium uranate (KUO<sub>3</sub>, containing pentavalent uranium) using synchrotron radiation in the vicinity of the U<italic>L</italic><sub>3</sub>edge (17.17 keV). Both routines are based on an iterative refinement of the dispersion corrections, but they differ in either using the intensity of a selection of reflections or doing a full-pattern (Rietveld method) refinement. The uranium dispersion corrections obtained using either method are in excellent agreement with each other, and they show in great detail the chemical shifts and differences in fine structure expected for tetravalent and pentavalent uranium. This approach may open new possibilities for the assessment of other, more complicated, materials such as mixed-valence compounds. Additionally, the DAFS methodology can offer a significant resource optimization because each data set contains both structural (diffraction) and chemical (spectroscopy) information, which can avoid the requirement to use multiple experimental stations at synchrotron sources.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 6.1
DOI: 10.1107/S1600576723010889
|
“Single Crystal and Pentatwinned Gold Nanorods Result in Chiral Nanocrystals with Reverse Handedness”. Van Gordon K, Ni B, Girod R, Mychinko M, Bevilacqua F, Bals S, Liz‐Marzán LM, Angewandte Chemie International Edition (2024). http://doi.org/10.1002/anie.202403116
Abstract: Handedness is an essential attribute of chiral nanocrystals, having a major influence on their properties. During chemical growth, the handedness of nanocrystals is usually tuned by selecting the corresponding enantiomer of chiral molecules involved in asymmetric growth, often known as chiral inducers. We report that, even using the same chiral inducer enantiomer, the handedness of chiral gold nanocrystals can be reversed by using Au nanorod seeds with either single crystalline or pentatwinned structure. This effect holds for chiral growth induced both by amino acids and by chiral micelles. Although it was challenging to discern the morphological handedness for<italic>L</italic>‐cystine‐directed particles, even using electron tomography, both cases showed circular dichroism bands of opposite sign, with nearly mirrored chiroptical signatures for chiral micelle‐directed growth, along with quasi‐helical wrinkles of inverted handedness. These results expand the chiral growth toolbox with an effect that might be exploited to yield a host of interesting morphologies with tunable optical properties.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 16.6
DOI: 10.1002/anie.202403116
|
“Decoding Excimer Formation in Covalent–Organic Frameworks Induced by Morphology and Ring Torsion”. Chakraborty J, Chatterjee A, Molkens K, Nath I, Arenas Esteban D, Bourda L, Watson G, Liu C, Van Thourhout D, Bals S, Geiregat P, Van der Voort P, Advanced Materials (2024). http://doi.org/10.1002/adma.202314056
Abstract: A thorough and quantitative understanding of the fate of excitons in covalent–organic frameworks (COFs) after photoexcitation is essential for their augmented optoelectronic and photocatalytic applications via precise structure tuning. The synthesis of a library of COFs having identical chemical backbone with impeded conjugation, but varied morphology and surface topography to study the effect of these physical properties on the photophysics of the materials is herein reported. The variation of crystallite size and surface topography substantified different aggregation pattern in the COFs, which leads to disparities in their photoexcitation and relaxation properties. Depending on aggregation, an inverse correlation between bulk luminescence decay time and exciton binding energy of the materials is perceived. Further transient absorption spectroscopic analysis confirms the presence of highly localized, immobile, Frenkel excitons (of diameter 0.3–0.5 nm) via an absence of annihilation at high density, most likely induced by structural torsion of the COF skeletons, which in turn preferentially relaxes via long‐lived (nanosecond to microsecond) excimer formation (in femtosecond scale) over direct emission. These insights underpin the importance of structural and topological design of COFs for their targeted use in photocatalysis.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 29.4
DOI: 10.1002/adma.202314056
|
“The environmental impacts of the lignin-first biorefineries : a consequential life cycle assessment approach”. Tschulkow M, Pizzol M, Compernolle T, Van den Bosch S, Sels B, Van Passel S, Resources, conservation and recycling 204, 107466 (2024). http://doi.org/10.1016/J.RESCONREC.2024.107466
Abstract: The emerging reductive catalytic fractionation biorefinery which is currently under development aims to convert woody biomass efficiently into high-value products. Despite its potential, the environmental consequences of its implementation are not well known. Therefore, a forward-looking consequential life cycle assessment examines greenhouse gas emissions associated with its products (pulp, phenolic monomers, and oligomers) compared to alternative market options. Findings indicate that current greenhouse gas emissions exceed those of the existing alternatives, with by-products and the gaseous waste stream as major contributors. Process adaption to (i) produce higher-valued products (bleached pulps, phenols, and propylene) and (ii) incinerate gaseous waste stream for energy are proposed, potentially reducing emissions by up to 50 %, outperforming alternative options. Compared to land-based transportation, waterways can increase feedstock availability by up to 1000 km without an increase in emissions. In conclusion, the consequential approach provides valuable insights for enhancing and optimizing the environmental performance of the process.
Keywords: A1 Journal article; Engineering Management (ENM)
Impact Factor: 13.2
DOI: 10.1016/J.RESCONREC.2024.107466
|
“Plasmonic photocatalytic coatings with self-cleaning, antibacterial, air and water purifying properties tested according to ISO standards”. Peeters H, Raes A, Verbruggen SW, Journal of photochemistry and photobiology: A: chemistry 451, 115529 (2024). http://doi.org/10.1016/J.JPHOTOCHEM.2024.115529
Abstract: ISO 10678:2010, ISO 22197–1 and 2, ISO 27447:2019 and ISO 27448:2009 for the photocatalytic degradation of organic dyes (methylene blue), air pollution (NOx and acetaldehyde), bacteria (E. coli and S. aureus) and solid organic fouling (oleic acid) are performed on plasmon-embedded TiO2 thin films on Borofloat® glass, as well as the commercially available titania-based self-cleaning glass PilkingtonActivTM. These standardised protocols measure the performance for the four main applications of photocatalytic materials: water purification, air purification, antibacterial and self-cleaning activity, respectively. The standards are performed exactly as prescribed to measure the activity under UV irradiation, and also in a slightly adapted manner to measure the performance under simulated solar light or visible light. Performing experiments according to ISO standards, enables an objective comparison amongst samples tested here, as well as with results from literature. This is a major asset compared to the myriad of customised setups used in laboratories worldwide that hinder a fair comparison. We point at the importance of meticulously following the ISO instructions, as we have noticed that multiple published studies adopting the ISO standards too often deviate from these protocols, thereby nullifying the added value of standardized testing. Following the ISO tests to the letter, we have demonstrated the superior performance of a previously developed plasmonic titania coating with fully embedded gold-silver nanoparticles towards all four application areas. Furthermore, our empirical data strongly support the need for a nuanced understanding of standardized testing, to ensure accurate assessment of photocatalytic materials. An examination of the ISO standards used in this work reveals notable drawbacks, including concerns about the reliability of the methylene blue degradation protocol, the issues of HNO3 accumulation in the NOx removal test, and limitations in assessing antibacterial activity and water contact angles.
Keywords: A1 Journal article; Engineering sciences. Technology
Impact Factor: 4.3
DOI: 10.1016/J.JPHOTOCHEM.2024.115529
|
“Recent progress in developing non-noble metal-based photocathodes for solar green hydrogen production”. Minja AC, Ag KR, Raes A, Borah R, Verbruggen SW, Current Opinion in Chemical Engineering 43, 101000 (2024). http://doi.org/10.1016/J.COCHE.2024.101000
Abstract: Photocathodes play a vital role in photoelectrocatalytic water splitting by acting as catalysts for reducing protons to hydrogen gas when exposed to light. Recent advancements in photocathodes have focused on addressing the limitations of noble metal-based materials. These noble metal-based photocathodes rely on expensive and scarce metals such as platinum and gold as cocatalysts or ohmic back contacts, respectively, rendering the final system less sustainable and costly when applied at scale. This mini-review summarizes the important recent progress in the development of non-noble metal-based photocathodes and their performance in the hydrogen evolution reaction during photoelectrochemical (PEC) water splitting. These advancements bring non-noble metal-based photocathodes closer to their noble metal-based counterparts in terms of performance, thereby paving the way forward toward industrial-scale photoelectrolyzers or PEC cells for green hydrogen production.
Keywords: A1 Journal article; Engineering sciences. Technology
Impact Factor: 6.6
DOI: 10.1016/J.COCHE.2024.101000
|