“Comparison of As- and P-based metamorphic buffers for high performance InP heterojunction bipolar transistor and high electron mobility transistor applications”. Lubyshev D, Fastenau JM, Fang X-M, Wu Y, Doss C, Snyder A, Liu WK, Lamb MSM, Bals S, Song C, Journal of vacuum science &, technology. B. Microelectronics and nanometer structures. Processing, measurement and phenomena 22, 1565 (2004). http://doi.org/10.1116/1.1691412
Abstract: Metamorphic buffers (M-buffers) consisting of graded InAlAs or bulk InP were employed for the production of InP-based epiwafers on GaAs substrates by molecular-beam epitaxy. The graded InAlAs is the standard for production metamorphic high electron mobility transistors (M-HEMTs), while the bulk InP offers superior thermal properties for higher current density circuits. The surface morphology and crystal structure of the two M-buffers showed different relaxation mechanisms. The graded InAlAs gave a cross-hatched pattern with nearly full relaxation and very effective dislocation filtering, while the bulk InP had a uniform isotropic surface with dislocations propagating further up towards the active layers. Both types of M-buffers had atomic force microscopy root-mean-square roughness values around 2030 Å. The Hall transport properties of high electron mobility transistors (HEMTs) grown on the InAlAs M-buffer, and a baseline HEMT grown lattice matched on InP, both had room-temperature mobilities >10 000 cm2/V s, while the M-HEMT on the InP M-buffer showed a decrease to 9000 cm2/V s. Similarly, the dc parameters of a double heterojunction bipolar transistor (DHBT) grown on the InAlAs M-buffer were much closer to the baseline heterojunction bipolar transistor than a DHBT grown on the InP M-buffer. A high breakdown voltage of 11.3 V was achieved on an M-DHBT with the InAlAs M-buffer. We speculate that the degradation in device characteristics on the InP M-buffer was related to the incomplete dislocation filtering.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 25
DOI: 10.1116/1.1691412
|
|
“Composition and crystal structure of resorbable calcium phosphate thin films”. Tuck L, Sayer M, Mackenzie M, Hadermann J, Dunfield D, Pietak A, Reid JW, Stratilatov AD, Journal of materials science 41, 4273 (2006). http://doi.org/10.1007/s10853-005-5532-5
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.599
Times cited: 2
DOI: 10.1007/s10853-005-5532-5
|
|
“Compositional changes of Pd-Au bimetallic nanoclusters upon hydrogenation”. di Vece M, Bals S, Lievens P, Van Tendeloo G, Physical review : B : solid state 80, 125420 (2009). http://doi.org/10.1103/PhysRevB.80.125420
Abstract: Changes in the size distribution and composition of bimetallic Pd-Au nanoclusters have been observed after hydrogen exposure. This effect is caused by hydrogen-induced Ostwald ripening whereby the hydrogen reduces the binding energy of the cluster atoms leading to their detachment from the cluster. The composition changes due to a difference in mobility of the detached palladium and gold atoms on the surface. Fast palladium atoms contribute to the formation of larger nanoclusters, while the slower gold atoms are confined to the smaller nanoclusters. These transformations in the Pd-Au nanocluster size and composition set a limit for chemical reactions in which such nanoclusters are involved together with hydrogen.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 28
DOI: 10.1103/PhysRevB.80.125420
|
|
“Compositionally induced phase transition in the Ca2MnGa1-xAlxO5 solid solutions: ordering of tetrahedral chains in brownmillerite structure”. Abakumov AM, Kalyuzhnaya AS, Rozova MG, Antipov EV, Hadermann J, Van Tendeloo G, Solid state sciences 7, 801 (2005). http://doi.org/10.1016/j.solidstatesciences.2005.01.020
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.811
Times cited: 38
DOI: 10.1016/j.solidstatesciences.2005.01.020
|
|
“Computation and parametrization of the temperature dependence of Debye-Waller factors for group IV, III-V and II-VI semiconductors”. Schowalter M, Rosenauer A, Titantah JT, Lamoen D, Acta crystallographica: section A: foundations of crystallography 65, 5 (2009). http://doi.org/10.1107/S0108767308031437
Abstract: We calculated the temperature dependence of the Debye-Waller factors for a variety of group IV, III-V and II-VI semiconductors from 0.1 to 1000 K. The approach used to fit the temperature dependence is described and resulting fit parameters are tabulated for each material. The Debye-Waller factors are deduced from generalized phonon densities of states which were derived from first principles using the WIEN2k and the ABINIT codes.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.725
Times cited: 51
DOI: 10.1107/S0108767308031437
|
|
“Conceptual frame rationalizing the self-stabilization of H-USY zeolites in hot liquid water”. Ennaert T, Geboers J, Gobechiya E, Courtin CM, Kurttepeli M, Houthoofd K, Kirschhock CEA, Magusin PCMM, Bals S, Jacobs PA, Sels BF, ACS catalysis 5, 754 (2015). http://doi.org/10.1021/cs501559s
Abstract: The wide range of liquid-phase reactions required for the catalytic conversion of biomass compounds into new bioplatform molecules defines a new set of challenges for the development of active, selective, and stable catalysts. The potential of bifunctional Ru/H-USY catalysts for conversions in hot liquid water (HLW) is assessed in terms of physicochemical stability and long-term catalytic performance of acid sites and noble metal functionality, as probed by hydrolytic hydrogenation of cellulose. It is shown that zeolite desilication is the main zeolite degradation mechanism in HLW. USY zeolite stability depends on two main parameters, viz., framework and extra-framework aluminum content. The former protects the zeolite lattice by counteracting hydrolysis of framework bonds, and the latter, when located at the external crystal surface, prevents solubilization of the zeolite framework which is the result of its low water-solubility. Hence, the hot liquid water stability of commercial H-USY zeolites, in contrast to their steam stability, increased with decreasing Si/AI ratio. As a result, mildly steamed USY zeolites containing a high amount of both Al species exhibit the highest resistance to HLW. During an initial period of transformations, Al-rich zeolites form additional protective extra-framework Al species at the outer surface, self-stabilizing the framework. A critical bulk Si/AI ratio of 3 was determined whereby USY zeolites with a lower Si/AI ratio will self-stabilize over time. Besides, due to the initial transformation period, the accessibility of the catalytic active sites is extensively enhanced resulting in a material that is more stable and drastically more accessible to large substrates than the original zeolite. When these findings are applied in the hydrolytic hydrogenation of cellulose, unprecedented nearly quantitative hexitol yields were obtained with a stable catalytic system.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 10.614
Times cited: 65
DOI: 10.1021/cs501559s
|
|
“Control of surface plasmon localization via self-assembly of silver nanoparticles along silver nanowires”. Tran ML, Centeno SP, Hutchison JA, Engelkamp H, Liang D, Van Tendeloo G, Sels BF, Hofkens J, Uji-i H, Journal of the American Chemical Society 130, 17240 (2008). http://doi.org/10.1021/ja807218e
Abstract: A simple and low-cost method to create metal−metal hybrid nanostructures possessing fairly regularly spaced hot-spots of surface plasmon resonances is proposed. The nanohybrid structure was prepared via self-assembly during a simple drop-casting procedure, using chemically synthesized silver nanowires and silver nanoparticles prepared in a single batch of a polyol process. Wide field illumination of these nanohybrids produced hot-spots with spacings of around 500 nm to 1 ìm. The intensity of the emission/scattering from the hot-spots fluctuates over time. The proposed structure can be useful for the development of molecular-sensors or as a substrate for surface enhanced Raman/fluorescence spectroscopy.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 51
DOI: 10.1021/ja807218e
|
|
“Convergent beam electron-diffraction investigation of lattice mismatch and static disorder in GaAs/GaAs1-xNx intercalated GaAs/GaAs1-xNx:H heterostructures”. Frabboni S, Grillo V, Gazzadi GC, Balboni R, Trotta R, Polimeni A, Capizzi M, Martelli F, Rubini S, Guzzinati G, Glas F;, Applied physics letters 101, 111912 (2012). http://doi.org/10.1063/1.4752464
Abstract: Hydrogen incorporation in diluted nitride semiconductors dramatically modifies the electronic and structural properties of the crystal through the creation of nitrogen-hydrogen complexes. We report a convergent beam electron-diffraction characterization of diluted nitride semiconductor-heterostructures patterned at a sub-micron scale and selectively exposed to hydrogen. We present a method to determine separately perpendicular mismatch and static disorder in pristine and hydrogenated heterostructures. The roles of chemical composition and strain on static disorder have been separately assessed. (C) 2012 American Institute of Physics. [http://dx.doi.org/10.1063/1.4752464]
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 1
DOI: 10.1063/1.4752464
|
|
“Copper oxycarbonates and mercury-based cuprates: promising high Tc superconductors”. Raveau B, Michel C, Hervieu M, Van Tendeloo G, Martin C, Maignan A, Journal of superconductivity 7, 9 (1994). http://doi.org/10.1007/BF00730359
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 6
DOI: 10.1007/BF00730359
|
|
“Copper oxycarbonates and mercury based cuprates: structural mechanisms of new superconductors”. Hervieu M, Michel C, Van Tendeloo G, Martin C, Maignan A, Raveau B, Physica: C : superconductivity 235/240, 25 (1994). http://doi.org/10.1016/0921-4534(94)91305-6
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.942
Times cited: 8
DOI: 10.1016/0921-4534(94)91305-6
|
|
“Correlation of microstructure and magnetotransport properties of epitaxially grown La-Ca-Mn-O3 thin films”. Habermeier HU, Razavi F, Lebedev O, Gross GM, Praus R, Zhang PX, Physica status solidi: B: basic research
T2 –, International Conference on Solid State Spectroscopy –, (ICSSS), SEP 05-07, 1999, SCHWABISCH-GMUND, GERMANY 215, 679 (1999). http://doi.org/10.1002/(SICI)1521-3951(199909)215:1<679::AID-PSSB679>3.0.CO;2-H
Abstract: We have investigated epitaxially grown single-crystalline Ca-doped LaMnO3 thin films using the pulsed laser deposition technique in a case study aimed to explore the possibilities buried in epitaxial stress tailoring in order to control the transport properties of CMR materials beyond the limits set by equilibrium thermodynamics. Depending on the film thickness there is an abrupt transition from pseudomorphic to epitaxial granular growth observable which is related to the epitaxial strain of the films. This is associated with microscopic stress relaxation and leads to well controllable modifications of the atomic arrangements of the Mn-O sublattice in the films. Due to the interrelation of double exchange, spin-, charge- and orbital ordering and the Jahn-Teller effect mediated coupling of the electronic system to the crystal lattice, the magnetotransport properties of the firms can be modified in a controllable way.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.674
Times cited: 3
DOI: 10.1002/(SICI)1521-3951(199909)215:1<679::AID-PSSB679>3.0.CO;2-H
|
|
“Corrigendum: Structural phase transition at the percolation threshold in epitaxial (La0.7Ca0.3MnO3)1-x:(MgO)x nanocomposite films”. Moshnyaga V, Damaschke B, Shapoval O, Belenchuk A, Faupel J, Lebedev OI, Verbeeck J, Van Tendeloo G, Mücksch M, Tsurkan V, Tidecks R, Samwer K, Nature materials 4, 104 (2005)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 39.737
|
|
“Coupled anion and cation ordering in Sr3RFe4O10.5 (R=Y, Ho, Dy) anion-deficientperovskites”. Abakumov AM, d' Hondt H, Rossell MD, Tsirlin AA, Gutnikova O, Filimonov DS, Schnelle W, Rosner H, Hadermann J, Van Tendeloo G, Antipov EV, Journal of solid state chemistry 183, 2845 (2010). http://doi.org/10.1016/j.jssc.2010.09.039
Abstract: The Sr3RFe4O10.5 (R=Y, Ho, Dy) anion-deficient perovskites were prepared using a solid-state reaction in evacuated sealed silica tubes. Transmission electron microscopy and 57Fe Mössbauer spectroscopy evidenced a complete A-cations and oxygen vacancies ordering. The structure model was further refined by ab initio structure relaxation, based on density functional theory calculations. The compounds crystallize in a tetragonal a≈2√2ap≈11.3 Å, с≈4сp≈16 Å unit cell (ap: parameter of the perovskite subcell) with the P42/mnm space group. Oxygen vacancies reside in the (FeO5/4□3/4) layers, comprising corner-sharing FeO4 tetrahedra and FeO5 tetragonal pyramids, which are sandwiched between the layers of the FeO6 octahedra. Smaller R atoms occupy the 9-fold coordinated position, whereas the 10-fold coordinated positions are occupied by larger Sr atoms. The Fe sublattice is ordered aniferromagnetically up to at least 500 K, while the rare-earth sublattice remains disordered down to 2 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 8
DOI: 10.1016/j.jssc.2010.09.039
|
|
“Coupled cation and charge ordering in the CaMn306 tunnel structure”. Hadermann J, Abakumov AM, Gillie LJ, Martin C, Hervieu M, Chemistry of materials 18, 5530 (2006). http://doi.org/10.1021/cm0618998
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 33
DOI: 10.1021/cm0618998
|
|
“Creating arrays of electron vortices”. Niermann T, Verbeeck J, Lehmann M, Ultramicroscopy 136, 165 (2014). http://doi.org/10.1016/j.ultramic.2013.10.002
Abstract: We demonstrate the production of an ordered array of electron vortices making use of an electron optical setup consisting of two electrostatic biprisms. The biprism filaments are oriented nearly orthogonal with respect to each other in a transmission electron microscope. Matching the position of the filaments, we can choose to form different topological features in the electron wave. We outline the working principle of the setup and demonstrate fist experimental results. This setup partially bridges the gap between angular momentum carried by electron spin, which is intrinsic and therefore present in any position of the wave, and angular momentum carried by the vortex character of the wave, which can be extrinsic depending on the axis around which it is measured. (C) 2013 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 9
DOI: 10.1016/j.ultramic.2013.10.002
|
|
“Critical influence of alumina content on the low temperature degradation of 2-3 mol% yttria-stabilized TZP for dental restorations”. Zhang F, Vanmeensel K, Inokoshi M, Batuk M, Hadermann J, Van Meerbeek B, Naert I, Vleugels J, Journal of the European Ceramic Society 35, 741 (2015). http://doi.org/10.1016/j.jeurceramsoc.2014.09.018
Abstract: The influence of 0.25, 2 and 5 wt.% alumina addition on the mechanical properties and low temperature degradation (LTD) of 3, 2.5 and 2 mol% yttria-stabilized TZP ceramics was investigated. The amount of alumina addition was observed to have a crucial impact on the degradation of Y-TZP ceramics. Independent on the yttria stabilizer content, 0.25 wt.% alumina had a higher degradation retarding effect to Y-TZP ceramics than 2 and 5 wt.% of alumina addition, which had a comparable effect. The apparent activation energy for the degradation process was increased by adding alumina, but it was the same for 0.255 wt.% alumina doped 3Y-TZP ceramics. For Y-TZPs containing a small amount of alumina addition, only the segregated Al3+ at the grain boundaries of the zirconia grains was effective to retard the degradation of Y-TZPs. The secondary phase Al2O3 grains increased the degradation kinetics, which might be attributed to the residual stresses.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 37
DOI: 10.1016/j.jeurceramsoc.2014.09.018
|
|
“Cross-section transmission electron microscopy characterization of the near-surface structure of medical Nitinol superelastic tubing”. Potapov PL, Tirry W, Schryvers D, Sivel VGM, Wu M-Y, Aslanidis D, Zandbergen H, Journal of materials science: materials in medicine 18, 483 (2007). http://doi.org/10.1007/s10856-007-2008-y
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.325
Times cited: 14
DOI: 10.1007/s10856-007-2008-y
|
|
“Crystal fields, disorder, and antiferromagnetic short-range order in Yb0.24Sn0.76Ru”. Klimczuk T, Wang CH, Lawrence JM, Xu Q, Durakiewicz T, Ronning F, Llobet A, Trouw F, Kurita N, Tokiwa Y, Lee Ho, Booth CH, Gardner JS, Bauer ED, Joyce JJ, Zandbergen HW, Movshovich R, Cava RJ, Thompson JD;, Physical review : B : condensed matter and materials physics 84, 075152 (2011). http://doi.org/10.1103/PhysRevB.84.075152
Abstract: We report extensive measurements on a new compound (Yb0.24Sn0.76)Ru that crystallizes in the cubic CsCl structure. Valence-band photoemission (PES) and L3 x-ray absorption show no divalent component in the 4f configuration of Yb. Inelastic neutron scattering (INS) indicates that the eight-fold degenerate J-multiplet of Yb3+ is split by the crystalline electric field (CEF) into a Γ7-doublet ground state and a Γ8 quartet at an excitation energy 20 meV. The magnetic susceptibility can be fit very well by this CEF scheme under the assumption that a Γ6-excited state resides at 32 meV; however, the Γ8/Γ6 transition expected at 12 meV was not observed in the INS. The resistivity follows a Bloch-Grüneisen law shunted by a parallel resistor, as is typical of systems subject to phonon scattering with no apparent magnetic scattering. All of these properties can be understood as representing simple local moment behavior of the trivalent Yb ion. At 1 K there is a peak in specific heat that is too broad to represent a magnetic-phase transition, consistent with absence of magnetic reflections in neutron diffraction. On the other hand this peak also is too narrow to represent the Kondo effect in the Γ7-doublet ground state. On the basis of the field dependence of the specific heat, we argue that antiferromagnetic (AF) short-range order (SRO) (possibly coexisting with Kondo physics) occurs at low temperatures. The long-range magnetic order is suppressed because the Yb site occupancy is below the percolation threshold for this disordered compound.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 8
DOI: 10.1103/PhysRevB.84.075152
|
|
“Crystal Structure and Luminescent Properties of R2-xEux(MoO4)(3) (R = Gd, Sm) Red Phosphors”. Morozov VA, Raskina MV, Lazoryak BI, Meert KW, Korthout K, Smet PF, Poelman D, Gauquelin N, Verbeeck J, Abakumov AM, Hadermann J;, Chemistry of materials 26, 7124 (2014). http://doi.org/10.1021/cm503720s
Abstract: The R-2(MoO4)(3) (R = rare earth elements) molybdates doped with Eu3+ cations are interesting red-emitting materials for display and solid-state lighting applications. The structure and luminescent properties of the R2-xEux(MoO4)(3) (R = Gd, Sm) solid solutions have been investigated as a function of chemical composition and preparation conditions. Monoclinic (alpha) and orthorhombic (beta') R2-xEux(MoO4)(3) (R = Gd, Sm; 0 <= x <= 2) modifications were prepared by solid-state reaction, and their structures were investigated using synchrotron powder X-ray diffraction and transmission electron microscopy. The pure orthorhombic beta'-phases could be synthesized only by quenching from high temperature to room temperature for Gd2-xEux(MoO4)(3) in the Eu3+-rich part (x > 1) and for all Sm2-xEux(MoO4)(3) solid solutions. The transformation from the alpha-phase to the beta'-phase results in a notable increase (similar to 24%) of the unit cell volume for all R2-xEux(MoO4)(3) (R = Sm, Gd) solid solutions. The luminescent properties of all R2-xEux(MoO4)(3) (R = Gd, Sm; 0 <= x <= 2) solid solutions were measured, and their optical properties were related to their structural properties. All R2-xEux(MoO4)(3) (R = Gd, Sm; 0 <= x <= 2) phosphors emit intense red light dominated by the D-5(0)-> F-7(2) transition at similar to 616 nm. However, a change in the multiplet splitting is observed when switching from the monoclinic to the orthorhombic structure, as a consequence of the change in coordination polyhedron of the luminescent ion from RO8 to RO7 for the alpha- and beta'-modification, respectively. The Gd2-xEux(MoO4)(3) solid solutions are the most efficient emitters in the range of 0 < x < 1.5, but their emission intensity is comparable to or even significantly lower than that of Sm2-xEux(MoO4)(3) for higher Eu3+ concentrations (1.5 <= x <= 1.75). Electron energy loss spectroscopy (EELS) measurements revealed the influence of the structure and element content on the number and positions of bands in the ultraviolet-visible-infrared regions of the EELS spectrum.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 24
DOI: 10.1021/cm503720s
|
|
“Crystal structure and magnetic properties of novel reduced V(IV)-based oxide Pb2V5O12”. Shpanchenko RV, Chyornaya VV, Abakumov AM, Antipov EV, Hadermann J, Van Tendeloo G, Kaul E, Geibel C, Sheptyakov D, Balagurov AM, Zeitschrift für anorganische und allgemeine Chemie 627, 2143 (2001). http://doi.org/10.1002/1521-3749(200109)627:9<2143::AID-ZAAC2143>3.0.CO;2-R
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.144
Times cited: 4
DOI: 10.1002/1521-3749(200109)627:9<2143::AID-ZAAC2143>3.0.CO;2-R
|
|
“Crystal structure and magnetic properties of the Cr-doped spiral antiferromagnet BiMnFe2O6”. Batuk D, de Dobbelaere C, Tsirlin AA, Abakumov AM, Hardy A, van Bael MK, Greenblatt M, Hadermann J, Materials research bulletin 48, 2993 (2013). http://doi.org/10.1016/j.materresbull.2013.04.038
Abstract: We report the Cr3+ for Mn3+ substitution in the BiMnFe2O6 structure. The BiCrxMn1-xFe2O6 solid solution is obtained by the solution-gel synthesis technique for the x values up to 0.3. The crystal structure investigation using a combination of X-ray powder diffraction and transmission electron microscopy demonstrates that the compounds retain the parent BiMnFe2O6 structure (for x = 0.3, a = 5.02010(6)angstrom, b = 7.06594(7)angstrom, c = 12.6174(1)angstrom, S.G. Pbcm, R-1 = 0.036, R-p = 0.011) with only a slight decrease in the cell parameters associated with the Cr3+ for Mn3+ substitution. Magnetic susceptibility measurements suggest strong similarities in the magnetic behavior of BiCrxMn1-xFe2O6 (x = 0.2; 0.3) and parent BiMnFe2O6. Only T-N slightly decreases upon Cr doping that indicates a very subtle influence of Cr3+ cations on the magnetic properties at the available substitution rates. (C) 2013 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 3
DOI: 10.1016/j.materresbull.2013.04.038
|
|
“Crystal structure and phase transitions in Sr3WO6”. King G, Abakumov AM, Hadermann J, Alekseeva AM, Rozova MG, Perkisas T, Woodward PM, Van Tendeloo G, Antipov EV, Inorganic chemistry 49, 6058 (2010). http://doi.org/10.1021/ic100598v
Abstract: The crystal structures of the beta and gamma polymorphs of Sr3WO6 and the gamma <->beta phase transition have been investigated using electron diffraction, synchrotron X-ray powder diffraction, and neutron powder diffraction. The gamma-Sr3WO6 polymorph is stable above T-c approximate to 470 K and adopts a monoclinically distorted double perovskite A(2)BB'O-6= Sr2SrWO6 structure (space group Cc, a = 10.2363(1)angstrom, b= 17.9007(1)angstrom, c= 11.9717(1)angstrom, beta=125.585(1)degrees at T= 1373 K, Z=12, corresponding to a = a(p)+1/2b(p) – 1/2c(p), b =3/2b(p) + 3/2c(p), c =-b(p) + c(p), a(p),b(p), c(p), lattice vectors of the parent Fm (3) over barm double perovskite structure). Upon cooling it undergoes a continuous phase transition into the triclinically distorted beta-Sr3WO6 phase (space group Cl, a = 10.09497(3)angstrom, b = 17.64748(5)angstrom, c = 11.81400(3)angstrom, alpha = 89.5470(2)degrees, beta= 125.4529(2)degrees, gamma =90.2889(2)degrees at T= 300 K). Both crystal structures of Sr3WO6 belong to a family of double perovskites with broken corner sharing connectivity of the octahedral framework. A remarkable feature of the gamma-Sr3WO6 structure is a non-cooperative rotation of the WO6 octahedra. One third of the WO6 octahedra are rotated by 45 about either the bp or the cp axis of the parent double perovskite structure. As a result, the WO6 octahedra do not share corners but instead share edges with the coordination polyhedra of the Sr cations at the B positions increasing their coordination number from 6 to 7 or 8. The crystal structure of the beta-phase is very close to the structure of the gamma-phase; decreasing symmetry upon the gamma ->beta transformation occurs because of unequal octahedral rotation angles about the bp and cp axes and increasing distortions of the WO6 octahedra.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 18
DOI: 10.1021/ic100598v
|
|
“Crystal structure and properties of Ru-stoichiometric LaSrMnRuO6”. Bune RO, Lobanov MV, Popov G, Greenblatt M, Botez CE, Stephens PW, Croft M, Hadermann J, Van Tendeloo G, Chemistry of materials 18, 2611 (2006). http://doi.org/10.1021/cm052371q
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 17
DOI: 10.1021/cm052371q
|
|
“Crystal structure and properties of the Na1-xRu2O4 phase”. Panin RV, Khasanova NR, Abakumov AM, Schnelle W, Hadermann J, Antipov EV, Russian chemical bulletin 55, 1717 (2006). http://doi.org/10.1007/s11172-006-0478-6
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.529
Times cited: 5
DOI: 10.1007/s11172-006-0478-6
|
|
“The crystal structure of \alpha-K3AIF6: elpasolites and double perovskites with broken corner-sharing connectivity of the octahedral framework”. Abakumov AM, King G, Laurinavichute VK, Rozova MG, Woodward PM, Antipov EV, Inorganic chemistry 48, 9336 (2009). http://doi.org/10.1021/ic9013043
Abstract: The crystal structure of α-K3AlF6 was solved and refined from a combination of powder X-ray and neutron diffraction data (a = 18.8385(3)Å, c = 33.9644(6)Å, S.G. I41/a, Z = 80, RP(X-ray) = 0.037, RP(neutron) = 0.053). The crystal structure is of the A2BB′X6 elpasolite type with the a = b ≈ ae√5, c = 4ae superstructure (ae, parameter of the elpasolite subcell) and rock-salt-type ordering of the K and Al cations over the B and B′ positions, respectively. The remarkable feature of α-K3AlF6 is a rotation of 2/5 of the AlF6 octahedra by π/4 around one of the crystal axes of the elpasolite subcell, coinciding with the 4-fold symmetry axes of the AlF6 octahedra. The rotation of the AlF6 octahedra replaces the corner-sharing between the K and Al polyhedra by edge-sharing, resulting in an increase of coordination numbers of the K cations at the B positions up to 7 and 8. Due to significant deformations of the K polyhedra, the corner-sharing connectivity of the octahedral elpasolite framework is broken and the rotations of the AlF6 octahedra do not have a cooperative character. Elpasolites and double perovskites with similar structural organization are discussed. The difference in ionic radii of the B and B′ cations as well as the tolerance factor are proposed to be the parameters governing the formation of elpasolites and double perovskites with broken corner-sharing connectivity of the octahedral framework.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 20
DOI: 10.1021/ic9013043
|
|
“The crystal structure of Ba8Ta6NiO24: cation ordering in hexagonal perovskites”. Abakumov AM, Van Tendeloo G, Scheglov AA, Shpanchenko RV, Antipov EV, Journal of solid state chemistry 125, 102 (1996). http://doi.org/10.1006/jssc.1996.0270
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 38
DOI: 10.1006/jssc.1996.0270
|
|
“The crystal structure of Ca3ReO6”. Abakumov AM, Shpanchenko RV, Antipov EV, Lebedev OI, Van Tendeloo G, Journal of solid state chemistry 131, 305 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 10
|
|
“Crystal structure of the double Hg-layer copper oxide superconductor (Hg, Pr)2Ba2(Y, Ca)Cu2O8-\delta as a function of doping”. Radaelli PG, Marezio M, Tholence JL, de Brion S, Santoro A, Huang Q, Capponi JJ, Chaillout C, Krekels T, Van Tendeloo G, The journal of physics and chemistry of solids 56, 1471 (1995)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.853
Times cited: 16
|
|
“Crystal-structure of the double-hg-layer copper-oxide superconductor (Hg,Pr)2Ba2(Y,Ca)Cu2O8-\deltaas a function of doping”. Radaelli PG, Marezio M, Tholence JL, Debrion S, Santoro A, Huang Q, Capponi JJ, Chaillout C, Krekels T, Van Tendeloo G, The journal of physics and chemistry of solids 56, 1471 (1995). http://doi.org/10.1016/0022-3697(95)00084-4
Abstract: The crystal structure of the newly discovered double-Hg-layer copper oxide superconductor (Hg, Pr)(2)Ba-2(Y, Ca)Cu2O8-delta was studied as a function of chemical doping using neutron and electron diffraction and high-resolution transmission electron microscopy (HREM). Rietveld refinements of the structural parameters from neutron powder diffraction data indicate that the oxygen site O3 on the mercury plane is highly defective, being both partially occupied and displaced from the high-symmetry position. The variable concentration of oxygen vacancies partially compensates for the cation doping and, together with the O3 displacement field, makes some of the Hg atoms acquire an unusual pyramidal coordination. HREM images confirm that the structure is of the '2212' type, with very few defects. In some grains, faint superstructure reflections were evidenced by electron diffraction, suggesting that both the oxygen vacancies and the O3 displacement field may order at least on a local scale.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.853
Times cited: 16
DOI: 10.1016/0022-3697(95)00084-4
|
|
“Crystal structure, phase transition, and magnetic ordering in perovskitelike Pb2-xBaxFe2O5 solid solutions”. Nikolaev IV, d' Hondt H, Abakumov AM, Hadermann J, Balagurov AM, Bobrikov IA, Sheptyakov DV, Pomjakushin VY, Pokholok KV, Filimonov DS, Van Tendeloo G, Antipov EV, Physical review : B : condensed matter and materials physics 78, 024426 (2008). http://doi.org/10.1103/PhysRevB.78.024426
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 29
DOI: 10.1103/PhysRevB.78.024426
|