Abstract: By changing the testing temperature, an austenitic FeMnAlSi alloy presents either å-martensite transformation or mechanical twinning during straining. In order to understand the nucleation and growth mechanisms involved in both phenomena, defects and particularly stacking faults, were characterized by transmission electron microscopy. It is observed that the character of the stacking faults also changes (from extrinsic to intrinsic) together with the temperature and the activated mode of plasticity.

Abstract: A large number of materials have a highly degenerate ground state and therefore a complex microstructure. Because of this degenerate state, phase transitions between the different phases play an important role. High resolution techniques in electron microscopy and nano-scale chemical analysis allow to study not only the microstructure but also the interfaces down to an atomic scale. We focus particularly on the ambiguity of alloys oil approaching the phase transition. The short range order (SRO) in ''1 1/20'' type alloys and the microstructure of ''tweed'' and needle formation in martensite like alloys with composition Ni5Al3 are considered in more detail.

Abstract: The large-scale production of single-wall carbon nanotubes (SWNTs) is reported. Large quantities of SWNTs can be synthesised by catalytic decomposition of methane over well-dispersed metal particles supported on MgO at 1000 degrees C. The thus produced SWNTs can be separated easily from the support by a simple acidic treatment to obtain a product with high yields (70-80%) of SWNTs. Because the typical synthesis time is 10 min, 1 g of SWNTs can be synthesised per day by this method. The SWNTs are characterized by high-resolution transmission electron microscopy and by Raman spectroscopy, showing the quality and the quantity of products. (C) 2000 Elsevier Science B.V. All rights reserved.

Abstract: Advanced transmission electron microscopy and statistical parameter estimated quantification procedures were applied to study the room temperature quasi-dynamical strain glass state in NiTi alloys. Nanosized strain pockets are visualised and the displacements of the atom columns are quantified. A comparison is made with conventional high-resolution transmission electron microscopy images of point defect induced strains in NiAl alloys.

Abstract: New layered structures corresponding to the general formula [PbBiO2]A(n+1)B(n)O(3n-1)Cl(2) Were prepared. Pb5BiFe3O10Cl2 (n = 3) and Pb5Bi2Fe4O13Cl2 (n = 4) are built as a stacking of truncated A(n+1)B(n)O(3n-1) perovskite blocks and alpha-PbO-type [A(2)O(2)](2+) (A = Pb, Bi) blocks combined with chlorine sheets. The alternation of these structural blocks can be represented as an intergrowth between the hematophanite and Sullen-type structural blocks. The crystal and-Magnetic structures of Pb5BiFe3O10Cl2 and Pb5Bi2Fe4O13Cl2 were investigated in the temperature range of 1.5-700 K using X-ray and neutron powder diffraction, transmission electron microscopy and Fe-57 Mossbauer spectroscopy. Both compounds crystallize in the I4/mmm space group with the unit cell parameters a approximate to a(p) approximate to 3.92 angstrom (a unit-cell parameter of the perovskite-structure), c approximate to 43.0 angstrom for the n = 3 member and c approximate to 53.5 angstrom for the n = 4 member. Despite the large separation between the slabs containing the Fe3+ ions (nearly 14 angstrom), long-range antiferromagnetic order sets in below similar to 600 K with the G-type arrangement of the Fe magnetic moments aligned along the c-axis. The possibility of mixing d(0) and d(n) cations at the B sublattice of these structures was also demonstrated by preparing the Ti-substituted n = 4 member Pb6BiFe3TiO13Cl2.

Abstract: The Pb2Fe2O5 compound with a layered intergrowth structure has been prepared by a solid-state reaction at 700 °C. The incommensurate compound crystallizes in a tetragonal system with a = 3.9037(2) Å, c = 3.9996(4) Å, and q = 0.1186(4)c*, or when treated as a commensurate approximant, a = 3.9047(2) Å, c = 36.000(3) Å, space group I4/mmm. The crystal structure of Pb2Fe2O5 was resolved from transmission electron microscopy data. Atomic coordinates and occupancies of the cation positions were estimated from high-angle annular dark-field scanning transmission electron microscopy data. Direct visualization of the positions of the oxygen atoms was possible using annular bright-field scanning transmission electron microscopy. The structure can be represented as an intergrowth of perovskite blocks and partially disordered blocks with a structure similar to that of the Bi2O2 blocks in Aurivillius-type phases. The A-cation positions at the border of the perovskite block and the cation positions in the Aurivillius-type blocks are jointly occupied by Pb2+ and Fe3+ cations, resulting in a layer sequence along the c axis: PbOFeO2PbOFeO2Pb7/8Fe1/8O1xFe5/8Pb3/8O2Fe5/8Pb3/8. Upon heating, the layered Pb2Fe2O5 structure transforms into an anion-deficient perovskite modulated by periodically spaced crystallographic shear (CS) planes. Considering the layered Pb2Fe2O5 structure as a parent matrix for the nucleation and growth of CS planes allows an explanation of the specific microstructure observed for the CS structures in the PbFeO system.

Abstract: We demonstrate that electron irradiation of colloidal CdS nanorods carrying Au domains causes their evolution into AuS/Cd core/shell nanoparticles as a result of a concurrent chemical and morphological transformation. The shrinkage of the CdS nanorods and the growth of the Cd shell around the Au tips are imaged in real time, while the displacement of S atoms from the CdS nanorod to the Au domains is evidenced by high-sensitivity energy-dispersive X-ray (EDX) spectroscopy. The various nanodomains display different susceptibility to the irradiation, which results in nanoconfigurations that are very different from those obtained after thermal annealing. Such physical manipulations of colloidal nanocrystals can be exploited as a tool to access novel nanocrystal heterostructures.

Abstract: Wadsley-Roth phase LixNb6PO25 has been studied as a potential candidate for anode material of Li-ion batteries. Its crystal structure, which consists of ReO3-type blocks of NbO6 octahedra connected with PO4 tetrahedra, provides a good stability and performance during Li+ insertion/removal. Li-ion chemical diffusion coefficient (D-chem) in LixNb6PO25 was determined by means of potentiostatic intermittent titration technique and electrochemical impedance spectroscopy. Different data treatments (classical Warburg equation or the model of an electrode system with ohmic potential drop and/or slow kinetics of the interfacial Li+ ion transfer across the electrode/electrolyte interface) were used for calculation of D-chem of the Li ion inside this material; their applicability is discussed in the article. D-chem changes with the Li-ion doping degree, x, in LixNb3PO25 and has a sharp minimum near the two-phase region at appr. 1.7V vs. Li+/Li. These values of D-chem in LixNb9PO25 (similar to 10(-9)-10(-11) cm(2) s(-1)) were found to be in average noticeably higher than in the widely studied anode material, Li4Ti5O12. (C) 2012 Elsevier Ltd. All rights reserved.

Abstract: NiTi is one of the most popular shape-memory alloys, a phenomenon resulting from a martensitic transformation. Commercial NiTi-based alloys are often thermally treated to contain Ni4Ti3 precipitates. The presence of these precipitates can introduce an extra transformation step related to the so-called R-phase. It is believed that the strain field surrounding the precipitates, caused by the matrixprecipitate lattice mismatch, lies at the origin of this intermediate transformation step. Atomic-resolution transmission electron microscopy in combination with geometrical phase analysis is used to measure the elastic strain field surrounding these precipitates. By combining measurements from two different crystallographic directions, the three-dimensional strain matrix is determined from two-dimensional measurements. Comparison of the measured strain matrix to the eigenstrain of the R-phase shows that both are very similar and that the introduction of the R-phase might indeed compensate the elastic strain introduced by the precipitate.

Abstract: The structure of Bi0.81Pb0.19FeO2.905 was investigated on different length scales using a combination of electron diffraction, high-resolution scanning transmission electron microscopy, synchrotron X-ray powder diffraction, and Mössbauer spectroscopy. In the 80300 K temperature range, the average crystal structure of Bi0.81Pb0.19FeO2.905 is a cubic Pm3̅m perovskite with a = 3.95368(3) Å at T = 300 K. The (Pb2+, Bi3+) cations and O2 anions are randomly displaced along the 110 cubic directions, indicating the steric activity of the lone pair on the Pb2+ and Bi3+ cations and a tilting distortion of the perovskite framework. The charge imbalance induced by the heterovalent Bi3+ → Pb2+ substitution is compensated by the formation of oxygen vacancies preserving the trivalent state of the Fe cations. On a short scale, oxygen vacancies are located in anion-deficient (FeO1.25) layers that are approximately 6 perovskite unit cells apart and transform every sixth layer of the FeO6 octahedra into a layer with a 1:1 mixture of corner-sharing FeO4 tetrahedra and FeO5 tetragonal pyramids. The anion-deficient layers act as twin planes for the octahedral tilting pattern of adjacent perovskite blocks. They effectively randomize the octahedral tilting and prevent the cooperative distortion of the perovskite framework. The disorder in the anion sublattice impedes cooperative interactions of the local dipoles induced by the off-center displacements of the Pb and Bi cations. Magnetic susceptibility measurements evidence the antiferromagnetic ordering in Bi0.81Pb0.19FeO2.905 at low temperatures.