Abstract: Nanocrystalline diamond films have generated much interested due to their diamond-like properties and low surface roughness. Several techniques have been used to obtain a high re-nucleation rate, such as hydrogen poor or high methane concentration plasmas. In this work, the properties of nano-diamond films grown on silicon substrates using a continuous DC bias voltage during the complete duration of growth are studied. Subsequently, the layers were characterised by several morphological, structural and optical techniques. Besides a thorough investigation of the surface structure, using SEM and AFM, special attention was paid to the bulk structure of the films. The application of FTIR, XRD, multi wavelength Raman spectroscopy, TEM and EELS yielded a detailed insight in important properties such as the amount of crystallinity, the hydrogen content and grain size. Although these films are smooth, they are under a considerable compressive stress. FTIR spectroscopy points to a high hydrogen content in the films, while Raman and EELS indicate a high concentration of sp2 carbon. TEM and EELS show that these films consist of diamond nano-grains mixed with an amorphous sp2 bonded carbon, these results are consistent with the XRD and UV Raman spectroscopy data.

Abstract: Supplementary information for the article “In-situ Plasma Studies using a Direct Current Microplasma in a Scanning Electron Microscope” containing the videos of in-situ SEM imaging (mp4 files), raw data/images, and Jupyter notebooks (ipynb files) for data treatment and plots. Link to the preprint: https://doi.org/10.48550/arXiv.2308.15123 Explanation of the data files can be found in the Information.pdf file. The Videos folder contains the in-situ SEM image series mentioned in the paper. If there are any questions/bugs, feel free to contact me at lukas.grunewaldatuantwerpen.be

Abstract: The plasma-based dry reforming in a dielectric barrier discharge (DBD) reactor is important to achieve sustainable goals, but many challenges remain. For example, the conversion and energy yield of DBD reactors are relatively low, and the catalysts or packing materials used in existing studies cannot improve them, possibly due to the unsuitable properties and structures of catalysts or packing materials for plasma processes. In order to study the effect of catalyst structure on plasma-based dry reforming, a controllable synthesis of the catalyst supports or templates was explored. In Chapter 2, an initially immiscible synthesis method was proposed to synthesize uniform silica spheres, which can replace the organic solvent-based Stöber method to successfully synthesize silica particles with the same size ranges as the original Stöber process without addition of organic solvents. Using the silica spheres as templates, 3D porous Cu and CuO catalysts with different pore sizes were synthesized in Chapter 3 to study the effect of catalyst pore size on the plasma-catalytic dry reforming. In most cases, the smaller the pore size, the higher the conversion of CH4 and CO2 due to the reaction of radicals and ions formed in the plasma. An exception are the samples synthesized from 1 μm silica, which show better performance due to the electric field enhancement for pore sizes close to the Debye length. Besides the pore size, the particle diameter of the catalyst or packing is also one of the important factors affecting the interaction between plasma and catalyst. In Chapter 4, SiO2 spheres (with or without supported metal) were used to study the effect of different support particle sizes on plasma-based dry reforming. We found that a uniform SiO2 packing improves the conversion of plasma-based dry reforming. The conversion of plasma-based dry reforming first increases and then decreases with increasing particle size, due to the balance between the promoting and hindering effect of the particle filling on the plasma discharge. Chapter 5 is to improve the design of the DBD reactor itself, in order to try to increase its low energy yield. Some stainless steel rings were put over the inner electrode rod of the DBD reactor. The presence of rings increases the local electric field, the displaced charges and the discharge fraction, and also makes the discharge more stable and with more uniform intensity. The placement of the rings improves the performance of the reactor at 30 W supplied power.