“Direct-synthesis method towards copper-containing periodic mesoporous organosilicas : detailed investigation of the copper distribution in the material”. Lin F, Meng, Kukueva E, Altantzis T, Mertens M, Bals S, Cool P, Van Doorslaer S, Journal of the Chemical Society : Dalton transactions 44, 9970 (2015). http://doi.org/10.1039/c4dt03719g
Abstract: Three-dimensional cubic Fm (3) over barm mesoporous copper-containing ethane-bridged PMO materials have been prepared through a direct-synthesis method at room temperature in the presence of cetyltrimethylammonium bromide as surfactant. The obtained materials have been unambiguously characterized in detail by several sophisticated techniques, including XRD, UV-Vis-Dr, TEM, elemental mapping, continuous- wave and pulsed EPR spectroscopy. The results show that at lower copper loading, the Cu2+ species are well dispersed in the Cu-PMO materials, and mainly exist as mononuclear Cu2+ species. At higher copper loading amount, Cu2+ clusters are observed in the materials, but the distribution of the Cu2+ species is still much better in the Cu-PMO materials prepared through the direct-synthesis method than in a Cu-containing PMO material prepared through an impregnation method. Moreover, the evolution of the copper incorporation during the PMO synthesis has been followed by EPR. The results show that the immobilization of the Cu2+ ion/complex and the formation of the PMO materials are taking place simultaneously. The copper ions are found to be situated on the inner surface of the mesopores of the materials and are accessible, which will be beneficial for the catalytic applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 4.029
Times cited: 11
DOI: 10.1039/c4dt03719g
|
|
|
“{110}-Layered B-cation ordering in the anion-deficient perovskite Pb2.4Ba2.6Fe2Sc2TiO13 with the crystallographic shear structure”. Tyablikov OA, Batuk D, Tsirlin AA, Batuk M, Verchenko VY, Filimonov DS, Pokholok KV, Sheptyakov DV, Rozova MG, Hadermann J, Antipov EV, Abakumov AM;, Journal of the Chemical Society : Dalton transactions 44, 10753 (2015). http://doi.org/10.1039/c4dt03867c
Abstract: A novel anion-deficient perovskite-based compound, Pb2.4Ba2.6Fe2Sc2TiO13, was synthesized via the citrate-based route. This compound is an n = 5 member of the A(n)B(n)O(3n-2) homologous series with unit-cell parameters related to the perovskite subcell a(p) approximate to 4.0 angstrom as a(p)root 2 x a(p) x 5a(p)root 2. The crystal structure of Pb2.4Ba2.6Fe2Sc2TiO13 consists of quasi-2D perovskite blocks with a thickness of three octahedral layers separated by the 1/2[110]((1) over bar 01)(p) crystallographic shear (CS) planes, which are parallel to the {110} plane of the perovskite subcell. The CS planes transform the corner-sharing octahedra into chains of edge-sharing distorted tetragonal pyramids. Using a combination of neutron powder diffraction, Fe-57 Mossbauer spectroscopy and atomic resolution electron energy-loss spectroscopy we demonstrate that the B-cations in Pb2.4Ba2.6Fe2Sc2TiO13 are ordered along the {110} perovskite layers with Fe3+ in distorted tetragonal pyramids along the CS planes, Ti4+ preferentially in the central octahedra of the perovskite blocks and Sc3+ in the outer octahedra of the perovskite blocks. Magnetic susceptibility and Mossbauer spectroscopy indicate a broadened magnetic transition around T-N similar to 45 K and the onset of local magnetic fields at low temperatures. The magnetic order is probably reminiscent of that in other A(n)B(n)O(3n-2) homologues, where G-type AFM order within the perovskite blocks has been observed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.029
Times cited: 1
DOI: 10.1039/c4dt03867c
|
|
|
“Oxygen-driven competition between low-dimensional structures of Sr3CoMO6 and Sr3CoMO7-\delta with M = Ru,Ir”. Mikhailova D, Reichel P, Tsirlin AA, Abakumov AM, Senyshyn A, Mogare KM, Schmidt M, Kuo CY, Pao CW, Pi TW, Lee JF, Hu Z, Tjeng LH;, Journal of the Chemical Society : Dalton transactions 43, 13883 (2014). http://doi.org/10.1039/c4dt01893a
Abstract: We have realized a reversible structure transformation of one-dimensional 1D K4CdCl6-type Sr3CoMO6 with the Co2+/M4+ cation ordering into the two-dimensional 2D double layered Ruddlesden-Popper structure Sr3CoMO7-delta with a random distribution of Co and M (with M = Ru, Ir) upon increasing the partial oxygen pressure. The combined soft and hard X-ray absorption spectroscopy studies show that under transformation, Co and M cations were oxidized to Co3+ and M5+. During oxidation, high-spin Co2+ in Sr3CoMO6 first transforms into high-spin Co3+ in oxygen-deficient Sr3CoMO7-delta, and then further transforms into low-spin Co3+ in fully oxidized Sr3CoMO7 upon further increasing the partial pressure of oxygen. The 1D Sr3CoMO6 compound is magnetically ordered at low temperatures with the magnetic moments lying along the c-axis. Their alignment is parallel for Sr3CoRuO6 and antiparallel for Sr3CoIrO6. The 2D compounds reveal a spin-glass-like behavior related to the random distribution of magnetic cations in the structure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.029
Times cited: 7
DOI: 10.1039/c4dt01893a
|
|
|
“A pseudo-tetragonal tungsten bronze superstructure: a combined solution of the crystal structure of K6.4(Nb,Ta)36.3O94 with advanced transmission electron microscopy and neutron diffraction”. Paria Sena R, Babaryk AA, Khainakov S, Garcia-Granda S, Slobodyanik NS, Van Tendeloo G, Abakumov AM, Hadermann J, Journal of the Chemical Society : Dalton transactions 45, 973 (2016). http://doi.org/10.1039/c5dt03479e
Abstract: The crystal structure of the K6.4Nb28.2Ta8.1O94 pseudo-tetragonal tungsten bronze-type oxide was determined using a combination of X-ray powder diffraction, neutron diffraction and transmission electron microscopy techniques, including electron diffraction, high angle annular dark field scanning transmission electron microscopy (HAADF-STEM), annular bright field STEM (ABF-STEM) and energy-dispersive X-ray compositional mapping (STEM-EDX). The compound crystallizes in the space group Pbam with unit cell parameters a = 37.468(9) A, b = 12.493(3) A, c = 3.95333(15) A. The structure consists of corner sharing (Nb,Ta)O6 octahedra forming trigonal, tetragonal and pentagonal tunnels. All tetragonal tunnels are occupied by K(+) ions, while 1/3 of the pentagonal tunnels are preferentially occupied by Nb(5+)/Ta(5+) and 2/3 are occupied by K(+) in a regular pattern. A fractional substitution of K(+) in the pentagonal tunnels by Nb(5+)/Ta(5+) is suggested by the analysis of the HAADF-STEM images. In contrast to similar structures, such as K2Nb8O21, also parts of the trigonal tunnels are fractionally occupied by K(+) cations.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.029
Times cited: 6
DOI: 10.1039/c5dt03479e
|
|
|
“Synthesis and cation distribution in the new bismuth oxyhalides with the Sillen-Aurivillius intergrowth structures”. Charkin DO, Akinfiev VS, Alekseeva AM, Batuk M, Abakumov AM, Kazakov SM, Journal of the Chemical Society : Dalton transactions 44, 20568 (2015). http://doi.org/10.1039/c5dt02620b
Abstract: About 20 new compounds with the Sillen-Aurivillius intergrowth structure, (MeMeBi3Nb2O11X)-Me-1-Bi-2 (Me-1 = Pb, Sr, Ba; Me-2 = Ca, Sr, Ba; X = Cl, Br, I), have been prepared. They are composed of stacking of [ANb(2)O(7)] perovskite blocks, fluorite-type [M2O2] blocks and halogen sheets. The cation distribution between the fluorite and perovskite layers has been studied for Ba2Bi3Nb2O11I, Ca1.25Sr0.75Bi3Nb2O11Cl, BaCaBi3Nb2O11Br and Sr2Bi3Nb2O11Cl. The smaller Me cations tend to reside in the perovskite block while the larger ones are situated in the fluorite-type block. The distribution of the elements was confirmed for BaCaBi3Nb2O11Br using energy dispersive X-ray analysis combined with scanning transmission electron microscopy (STEM-EDX). An electron diffraction study of this compound reveals a local symmetry lowering caused by weakly correlated rotation of NbO6 octahedra. Based on our findings, we suggest a new stability criterion for mixed-layer structures, which is that net charges of any two consecutive layers do not compensate for each other and only the whole layer sequence is electroneutral.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.029
Times cited: 5
DOI: 10.1039/c5dt02620b
|
|
|
“Synthesis, structure and magnetic ordering of the mullite-type Bi2Fe4-xCrxO9 solid solutions with a frustrated pentagonal Cairo lattice”. Rozova MG, Grigoriev VV, Bobrikov IA, Filimonov DS, Zakharov KV, Volkova OS, Vasiliev AN, Antipov EV, Tsirlin AA, Abakumov AM, Journal of the Chemical Society : Dalton transactions 45, 1192 (2016). http://doi.org/10.1039/c5dt04296h
Abstract: Highly homogeneous mullite-type solid solutions Bi2Fe4-xCrxO9 (x = 0.5, 1, 1.2) were synthesized using a soft chemistry technique followed by a solid-state reaction in Ar. The crystal structure of Bi2Fe3CrO9 was investigated using X-ray and neutron powder diffraction, transmission electron microscopy and Fe-57 Mossbauer spectroscopy (S.G. Pbam, a = 7.95579(9) angstrom , b = 8.39145(9) angstrom, c = 5.98242(7) angstrom, R-F(X-ray) = 0.022, R-F(neutron) = 0.057). The ab planes in the structure are tessellated with distorted pentagonal loops built up by three tetrahedrally coordinated Fe sites and two octahedrally coordinated Fe/Cr sites, linked together in the ab plane by corner-sharing forming a pentagonal Cairo lattice. Magnetic susceptibility measurements and powder neutron diffraction show that the compounds order antiferromagnetically (AFM) with the Neel temperatures decreasing upon increasing the Cr content from T-N similar to 250 K for x = 0 to T-N similar to 155 K for x = 1.2. The magnetic structure of Bi2Fe3CrO9 at T = 30 K is characterized by a propagation vector k = (1/2,1/2,1/2). The tetrahedrally coordinated Fe cations form singlet pairs within dimers of corner-sharing tetrahedra, but spins on the neighboring dimers are nearly orthogonal. The octahedrally coordinated (Fe, Cr) cations form antiferromagnetic up-up-down-down chains along c, while the spin arrangement in the ab plane is nearly orthogonal between nearest neighbors and collinear between second neighbors. The resulting magnetic structure is remarkably different from the one in pure Bi2Fe4O9 and features several types of spin correlations even on crystallographically equivalent exchange that may be caused by the simultaneous presence of Fe and Cr on the octahedral site.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.029
DOI: 10.1039/c5dt04296h
|
|
|
“Composition-dependent charge transfer and phase separation in the V1-xRexO2 solid solution”. Mikhailova D, Kuratieva NN, Utsumi Y, Tsirlin AA, Abakumov AM, Schmidt M, Oswald S, Fuess H, Ehrenberg H, Journal of the Chemical Society : Dalton transactions 46, 1606 (2017). http://doi.org/10.1039/C6DT04389E
Abstract: The substitution of vanadium in vanadium dioxide VO2 influences the critical temperatures of structural and metal-to-insulator transitions in different ways depending on the valence of the dopant. Rhenium adopts valence states between + 4 and + 7 in an octahedral oxygen surrounding and is particularly interesting in this context. Structural investigation of V1-xRexO2 solid solutions (0.01 <= x <= 0.30) between 80 and 1200 K using synchrotron X-ray powder diffraction revealed only two polymorphs that resemble VO2: the low-temperature monoclinic MoO2-type form (space group P2(1)/c), and the tetragonal rutile-like form (space group P4(2)/mnm). However, for compositions with 0.03 < x <= 0.15 a phase separation in the solid solution was observed below 1000 K upon cooling down from 1200 K, giving rise to two isostructural phases with slightly different lattice parameters. This is reflected in the appearance of two metal-toinsulator transition temperatures detected by magnetization and specific heat measurements. Comprehensive X-ray photoelectron spectroscopy studies showed that an increased amount of Re leads to a change in the Re valence state from solely Re6+ at a low doping level (<= 3 at% Re) via mixed-valence states Re4+/Re6+ for at least 0.03 < x <= 0.10, up to nearly pure Re4+ in V0.70Re0.30O2. Thus, compositions V1-xRexO2 with only one valence state of Re in the material (Re6+ or Re4+) can be obtained as a single phase, while intermediate compositions are subjected to a phase separation, presumably due to different valence states of Re.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.029
Times cited: 1
DOI: 10.1039/C6DT04389E
|
|
|
“Small-moment paramagnetism and extensive twinning in the topochemically reduced phase Sr2ReLiO5.5”. Hasanli N, Gauquelin N, Verbeeck J, Hadermann J, Hayward MA, Journal of the Chemical Society : Dalton transactions 47, 15783 (2018). http://doi.org/10.1039/C8DT03463J
Abstract: Reaction of the cation-ordered double perovskite Sr2ReLiO6 with dilute hydrogen at 475 degrees C leads to the topochemical deintercalation of oxide ions from the host lattice and the formation of a phase of composition Sr2ReLiO5.5, as confirmed by thermogravimetric and EELS data. A combination of neutron and electron diffraction data reveals the reduction process converts the -Sr2O2-ReLiO4-Sr2O2-ReLiO4- stacking sequence of the parent phase into a -Sr2O2-ReLiO3-Sr2O2-ReLiO4-, partially anion-vacant ordered sequence. Furthermore a combination of electron diffraction and imaging reveals Sr2ReLiO5.5 exhibits extensive twinning – a feature which can be attributed to the large, anisotropic volume expansion of the material on reduction. Magnetisation data reveal a strongly reduced moment of (eff) = 0.505(B) for the d(1) Re6+ centres in the phase, suggesting there remains a large orbital component to the magnetism of the rhenium centres, despite their location in low symmetry coordination environments.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.029
DOI: 10.1039/C8DT03463J
|
|
|
“Highly porous palladium nanodendrites : wet-chemical synthesis, electron tomography and catalytic activity”. Mourdikoudis S, Montes-Garcia V, Rodal-Cedeira S, Winckelmans N, Perez-Juste I, Wu H, Bals S, Perez-Juste J, Pastoriza-Santos I, Journal of the Chemical Society : Dalton transactions 48, 3758 (2019). http://doi.org/10.1039/C9DT00107G
Abstract: A simple procedure to obtain highly porous hydrophilic palladium nanodendrites in one-step is described. The synthetic strategy is based on the thermal reduction of a Pd precursor in the presence of a positively charged polyelectrolyte such as polyethylenimine (PEI). Advanced electron microscopy techniques combined with X-ray diffraction (XRD), thermogravimetry and BET analysis demonstrate the polycrystalline nature of the nanodendrites as well as their high porosity and active surface area, facilitating a better understanding of their unique morphology. Besides, catalytic studies performed using Raman scattering and UV-Vis spectroscopies revealed that the nanodendrites exhibit a superior performance as recyclable catalysts towards hydrogenation reaction compared to other noble metal nanoparticles.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 23
DOI: 10.1039/C9DT00107G
|
|
|
“An in-depth study of Sn substitution in Li-rich/Mn-rich NMC as a cathode material for Li-ion batteries”. Paulus A, Hendrickx M, Bercx M, Karakulina OM, Kirsanova MA, Lamoen D, Hadermann J, Abakumov AM, Van Bael MK, Hardy A, Journal of the Chemical Society : Dalton transactions 49, 10486 (2020). http://doi.org/10.1039/D0DT01047B
Abstract: Layered Li-rich/Mn-rich NMC (LMR-NMC) is characterized by high initial specific capacities of more than 250 mA h g(-1), lower cost due to a lower Co content and higher thermal stability than LiCoO2. However, its commercialisation is currently still hampered by significant voltage fade, which is caused by irreversible transition metal ion migration to emptied Li positionsviatetrahedral interstices upon electrochemical cycling. This structural change is strongly correlated with anionic redox chemistry of the oxygen sublattice and has a detrimental effect on electrochemical performance. In a fully charged state, up to 4.8 Vvs.Li/Li+, Mn4+ is prone to migrate to the Li layer. The replacement of Mn4+ for an isovalent cation such as Sn4+ which does not tend to adopt tetrahedral coordination and shows a higher metal-oxygen bond strength is considered to be a viable strategy to stabilize the layered structure upon extended electrochemical cycling, hereby decreasing voltage fade. The influence of Sn4+ on the voltage fade in partially charged LMR-NMC is not yet reported in the literature, and therefore, we have investigated the structure and the corresponding electrochemical properties of LMR-NMC with different Sn concentrations. We determined the substitution limit of Sn4+ in Li1.2Ni0.13Co0.13Mn0.54-xSnxO2 by powder X-ray diffraction and transmission electron microscopy to be x approximate to 0.045. The limited solubility of Sn is subsequently confirmed by density functional theory calculations. Voltage fade for x= 0 andx= 0.027 has been comparatively assessed within the 3.00 V-4.55 V (vs.Li/Li+) potential window, from which it is concluded that replacing Mn4+ by Sn4+ cannot be considered as a viable strategy to inhibit voltage fade within this window, at least with the given restricted doping level.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4
DOI: 10.1039/D0DT01047B
|
|
|
“The influence of the 6s², configuration of Bi³+ on the structures of A ' BiNb₂O₇, (A ' = Rb, Na, Li) layered perovskite oxides”. Mallick S, Khalsa G, Kaaret JZ, Zhang W, Batuk M, Gibbs AS, Hadermann J, Halasyamani PS, Benedek NA, Hayward MA, Journal of the Chemical Society : Dalton transactions 50, 15359 (2021). http://doi.org/10.1039/D1DT02974F
Abstract: Solid state compounds which exhibit non-centrosymmetric crystal structures are of great interest due to the physical properties they can exhibit. The 'hybrid improper' mechanism – in which two non-polar distortion modes couple to, and stabilize, a further polar distortion mode, yielding an acentric crystal structure – offers opportunities to prepare a range of novel non-centrosymmetric solids, but examples of compounds exhibiting acentric crystal structures stabilized by this mechanism are still relatively rare. Here we describe a series of bismuth-containing layered perovskite oxide phases, RbBiNb2O7, LiBiNb2O7 and NaBiNb2O7, which have structural frameworks compatible with hybrid-improper ferroelectricity, but also contain Bi3+ cations which are often observed to stabilize acentric crystal structures due to their 6s(2) electronic configurations. Neutron powder diffraction analysis reveals that RbBiNb2O7 and LiBiNb2O7 adopt polar crystal structures (space groups I2cm and B2cm respectively), compatible with stabilization by a trilinear coupling of non-polar and polar modes. The Bi3+ cations present are observed to enhance the magnitude of the polar distortions of these phases, but are not the primary driver for the acentric structure, as evidenced by the observation that replacing the Bi3+ cations with Nd3+ cations does not change the structural symmetry of the compounds. In contrast the non-centrosymmetric, but non-polar structure of NaBiNb2O7 (space group P2(1)2(1)2(1)) differs significantly from the centrosymmetric structure of NaNdNb2O7, which is attributed to a second-order Jahn-Teller distortion associated with the presence of the Bi3+ cations.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1039/D1DT02974F
|
|
|
“The crystal and defect structures of polar KBiNb2O7”. Mallick S, Zhang W, Batuk M, Gibbs AS, Hadermann J, Halasyamani PS, Hayward MA, Journal of the Chemical Society : Dalton transactions 51, 1866 (2022). http://doi.org/10.1039/D1DT04064B
Abstract: KBiNb2O7 was prepared from RbBiNb2O7 by a sequence of cation exchange reactions which first convert RbBiNb2O7 to LiBiNb2O7, before KBiNb2O7 is formed by a further K-for-Li cation exchange. A combination of neutron, synchrotron X-ray and electron diffraction data reveal that KBiNb2O7 adopts a polar, layered, perovskite structure (space group A11m) in which the BiNb2O7 layers are stacked in a (0, ½, z) arrangement, with the K+ cations located in half of the available 10-coordinate interlayer cation sites. The inversion symmetry of the phase is broken by a large displacement of the Bi3+ cations parallel to the y-axis. HAADF-STEM images reveal that KBiNb2O7 exhibits frequent stacking faults which convert the (0. ½, z) layer stacking to (½, 0, z) stacking and vice versa, essentially switching the x- and y-axes of the material. By fitting the complex diffraction peak shape of the SXRD data collected from KBiNb2O7 it is estimated that each layer has approximately an ~11% chance of being defective – a high level which is attributed to the lack of cooperative NbO6 tilting in the material, which limits the lattice strain associated with each fault.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4
DOI: 10.1039/D1DT04064B
|
|
|
“K2CaV2O7 : a pyrovanadate with a new layered type of structure in the A2BV2O7 family”. Tyutyunnik AP, Slobodin BV, Samigullina RF, Verberck B, Tarakina NV, Journal of the Chemical Society : Dalton transactions 42, 1057 (2013). http://doi.org/10.1039/c2dt31246h
Abstract: The crystal structure of K2CaV2O7 prepared by a conventional solid-state reaction has been solved by a direct method and refined using Rietveld full profile fitting based on X-ray powder diffraction data. This compound crystallises in the triclinic space group (P (1) over bar, Z = 2) with unit cell constants a = 7.1577(1) angstrom, b = 10.5104(2) angstrom, c = 5.8187(1) angstrom, alpha = 106.3368(9)degrees, beta = 106.235(1)degrees, gamma = 71.1375(9)degrees. The structure can be described as infinite undulating CaV2O72- layers parallel to the ac plane, which consist of pairs of edge-sharing CaO6 octahedra connected to each other through V2O7 pyrogroups. The potassium atoms are positioned in two sites between the layers, with a distorted IX-fold coordination of oxygen atoms. The chemical composition obtained from the structural solution was confirmed by energy-dispersive X-ray analysis. The stability of compounds in the family of alkali metal calcium pyrovanadates is discussed based on an analysis of the correlation between anion and cation sizes and theoretical first-principles calculations.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 4.029
Times cited: 3
DOI: 10.1039/c2dt31246h
|
|
|
“Optical readout of controlled monomer-dimer self-assembly”. Tarakanov PA, Tarakanova EN, Dorovatovskii PV, Zubavichus YV, Khrustalev VN, Trashin SA, De Wael K, Neganova ME, Mischenko DV, Sessler JL, Stuzhin PA, Pushkarev VE, Tomilova LG, Journal of the Chemical Society : Dalton transactions 47, 14169 (2018). http://doi.org/10.1039/C8DT00384J
Abstract: 5,7-Substituted 1,4-diazepinoporphyrazine magnesium(II) complexes were synthesized via Mg(II)-alkoxide templated macrocyclization. A single crystal growth synchrotron diffraction analysis permitted what is to our knowledge the first structural characterization of a 1,4-diazepinoporphyrazine. It exists as a dimer in the solid state. In silico calculations supported by solution phase spectral studies involving a series of representative derivatives, provided insights into the factors governing dimerization of 1,4-diazepinoporphyrazines. The present 1,4-diazepinoporphyrazines serve as useful probes for understanding the determinants that guide dimermonomer equilibria and the self-assembly of phthalocyanine derivatives.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Times cited: 4
DOI: 10.1039/C8DT00384J
|
|
|
“Synthesis and characterization of heteroleptic rare earth double-decker complexes involving tetradiazepinoporphyrazine and phthalocyanine macrocycles”. Tarakanova EN, Tarakanov PA, Simakov AO, Furuyama T, Kobayashi N, Konev DV, Goncharova OA, Trashin SA, De Wael K, Sulimenkov IV, Filatov VV, Kozlovskiy VI, Tomilova LG, Stuzhin PA, Pushkarev VE, Dalton Transactions 50, 6245 (2021). http://doi.org/10.1039/D1DT00088H
Abstract: Reaction of (2,3,9,10,16,17,23,24-octabutylphthalocyaninato)lanthanide(iii) acetylacetonates ((Bu)PcLn(acac), 1a-c, Ln = Lu (a), Eu (b), La (c)) with a tetrakis(5,7-bis(4-tert-butylphenyl)-6H-1,4-diazepino)[2,3-b,g,l,q]porphyrazine ligand ((tBuPh)DzPzH(2), 2) produced sandwich compounds ((tBuPh)DzPz)Ln(Pc-Bu) (3a-c), which represent the first heteroleptic double-deckers incorporating both Pc and DzPz decks. A combination of high-resolution mass spectrometry, UV-Vis/NIR, MCD, and H-1 NMR spectroscopy, and square-wave voltammetry provided unambiguous characterization of target complexes 3 indicating that their spectral and electrochemical properties are generally intermediate with respect to their homoleptic relatives. Based on the data of solution-state H-1-H-1 NMR (COSY, NOESY) correlation spectroscopy supported by DFT calculations, a dimerization tendency of compounds 3 proportional to the Ln(iii) ion size was found. The spectroelectrochemical study of 3 and the corresponding homoleptic double-deckers revealed a pronounced tendency to aggregation of the one-electron oxidized forms of DzPz-containing double-decker complexes compared to homoleptic Pc(2)Ln compounds.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 4.029
DOI: 10.1039/D1DT00088H
|
|