“Synthesis and catalytic activity of Ti-MCM-41 nanoparticles with highly active titanium sites”. Lin K, Pescarmona PP, Vandepitte H, Liang D, Van Tendeloo G, Jacobs PA, Journal of catalysis 254, 64 (2008). http://doi.org/10.1016/j.jcat.2007.11.017
Abstract: Ti-MCM-41 nanoparticles 80-160 nm in diameter (Ti-MCM-41 NP) were successfully prepared by a dilute solution route in sodium hydroxide medium at ambient temperature. Ti-MCM-41 NP were characterized by X-ray diffraction, nitrogen adsorption/desorption isotherms, SEM, TEM. FT-IR, and UV-vis spectroscopy. The characterization results showed the existence of highly ordered hexagonal mesoporous structure and tetrahedral Ti species in Ti-MCM-41 NP. In the epoxidation of cyclohexene with aqueous H2O2, Ti-MCM-41 NP displayed higher conversion and initial reaction rate than a Ti-MCM-41 sample with normal particle size (Ti-MCM-41 LP). Diffusion of the reactants was accelerated and the accessibility to the catalytic Ti species was enhanced in the shorter channels in Ti-MCM-41 NP samples. Ti-MCM-41 NP showed much higher selectivity for cyclohexene oxide compared with Ti-MCM-41 LP, suggesting reduced hydrolysis of cyclohexene oxide with water in the former case. The increased selectivity for cyclohexene oxide can be attributed to the lower concentration of residual surface silanols in Ti-MCM-41 NP and the shorter residence time of epoxide in the shorter mesoporous channels. Ti-MCM-41 NP also appears to be a suitable catalyst in the epoxidation of a bulky substrate, like cholesterol, with tert-butyl hydroperoxide. (c) 2007 Elsevier Inc. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.844
Times cited: 52
DOI: 10.1016/j.jcat.2007.11.017
|
“Synthesis and crystal structure of novel layered manganese oxide Ca2MnGaO5+\delta”. Abakumov AM, Rozova MG, Pavlyuk BP, Lobanov MV, Antipov EV, Lebedev OI, Van Tendeloo G, Sheptyakov DV, Balagurov AM, Bourée F, Journal of solid state chemistry 158, 100 (2001). http://doi.org/10.1006/jssc.2000.9105
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 48
DOI: 10.1006/jssc.2000.9105
|
“Synthesis and crystal structure of Sr2ScBiO6”. Kazin PE, Abakumov AM, Zaytsev DD, Tretyakov YD, Khasanova NR, Van Tendeloo G, Jansen M, Journal of solid state chemistry 162, 142 (2001). http://doi.org/10.1006/jssc.2001.9375
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 3
DOI: 10.1006/jssc.2001.9375
|
“Synthesis and structure determination of ferromagnetic semiconductors LaAMnSnO6(A = Sr, Ba)”. Yang T, Perkisas T, Hadermann J, Croft M, Ignatov A, Van Tendeloo G, Greenblatt M, Journal of materials chemistry 21, 199 (2011). http://doi.org/10.1039/c0jm02614j
Abstract: LaAMnSnO(6) (A = Sr, Ba) have been synthesized by high temperature solid-state reactions under dynamic 1% H(2)/Ar flow. Rietveld refinements on room temperature powder X-ray diffraction data indicate that LaSrMnSnO(6) crystallizes in the GdFeO(3)-structure, with space group Pnma and, combined with transmission electron microscopy, LaBaMnSnO(6) in Imma. Both space groups are common in disordered double-perovskites. The Mn(3+) and Sn(4+) ions whose valence states were confirmed by X-ray absorption spectroscopy, are completely disordered over the B-sites and the BO(6) octahedra are slightly distorted. LaAMnSnO(6) are ferromagnetic semiconductors with a T(C) = 83 K for the Sr- and 66 K for the Ba-compound. The title compounds, together with the previously reported LaCaMnSnO(6) provide an interesting example of progression from Pnma to Imma as the tolerance factor increases. An analysis of the relationship between space group and tolerance factor for the series LaAMnMO(6) (A = Ca, Sr, Ba; M = Sn, Ru) provides a better understanding of the symmetry determination for double perovskites.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 3
DOI: 10.1039/c0jm02614j
|
“TEM study of YBa2Cu3O7-x thin films with Zn and Fe”. Verbist K, Van Tendeloo G, Ye M, Mehbod M, Deltour R, Physica: C : superconductivity 235, 663 (1994). http://doi.org/10.1016/0921-4534(94)91555-5
Abstract: Analytical and high resolution electron microscopy have been used to study the effect of Zn- and Fe-doping on the micro structure of [001] YBa2Cu3O7-x thin films on [001] MgO substrates grown by magnetron sputtering. Special attention was paid to the presence of second phase inclusions and surface outgrowths such as CuO, Y2Ba1Cu1O5-x, Y2O3 in order to establish a relationship with the critical current density.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.942
DOI: 10.1016/0921-4534(94)91555-5
|
“Temperature and magnetic field dependence of the voltagein GaAs films with superconducting Ga grains”. Willems BL, Taylor DMJ, Fritzsche J, Malfait M, Vanacken J, Moshchalkov VV, Montoya E, Van Tendeloo G, European physical journal : B : condensed matter and complex systems 66, 25 (2008). http://doi.org/10.1140/epjb/e2008-00386-3
Abstract: We have studied granular films consisting of nanoscale Ga droplets formed on GaAs films via a method of vacuum annealing to promote As evaporation. For temperatures and magnetic fields below the bulk Ga critical parameters, the samples are very sensitive towards external microwave radiation when two point voltage measurements are performed. Together with the observation of an oscillating magnetic field dependence of the voltage, a scenario in which the samples consist of Josephson-coupled loops seems to be the most likely one for explaining the obtained results.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.461
DOI: 10.1140/epjb/e2008-00386-3
|
“Fe3O4/ZnO : a high-quality magnetic oxide-semiconductor heterostructure by reactive deposition”. Paul M, Kufer D, Müller A, Brück S, Goering E, Kamp M, Verbeeck J, Tian H, Van Tendeloo G, Ingle NJC, Sing M, Claessen R, Applied physics letters 98, 012512 (2011). http://doi.org/10.1063/1.3540653
Abstract: We demonstrate the epitaxial growth of Fe<sub>3</sub>O<sub>4</sub> films on ZnO by a simple reactive deposition procedure using molecular oxygen as an oxidizing agent. X-ray photoelectron spectroscopy results evidence that the iron-oxide surface is nearly stoichiometric magnetite. X-ray diffraction results indicate monocrystalline epitaxy and almost complete structural relaxation. Scanning transmission electron micrographs reveal that the microstructure consists of domains which are separated by antiphase boundaries or twin boundaries. The magnetite films show rather slow magnetization behavior in comparison with bulk crystals probably due to reduced magnetization at antiphase boundaries in small applied fields.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 27
DOI: 10.1063/1.3540653
|
“Transmission electron microscopy and structural phase transitions in anion-deficient perovskite-based oxides”. Hadermann J, Van Tendeloo G, Abakumov AM, Acta crystallographica: section A: foundations of crystallography 61, 77 (2005). http://doi.org/10.1107/S0108767304023013
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.725
Times cited: 18
DOI: 10.1107/S0108767304023013
|
“Nematic superconducting state in iron pnictide superconductors”. Li J, Pereira PJ, Yuan J, Lv Y-Y, Jiang M-P, Lu D, Lin Z-Q, Liu Y-J, Wang J-F, Li L, Ke X, Van Tendeloo G, Li M-Y, Feng H-L, Hatano T, Wang H-B, Wu P-H, Yamaura K, Takayama-Muromachi E, Vanacken J, Chibotaru LF, Moshchalkov VV, Nature communications 8, 1880 (2017). http://doi.org/10.1038/s41467-017-02016-y
Abstract: Nematic order often breaks the tetragonal symmetry of iron-based superconductors. It arises from regular structural transition or electronic instability in the normal phase. Here, we report the observation of a nematic superconducting state, by measuring the angular dependence of the in-plane and out-of-plane magnetoresistivity of Ba 0.5 K 0.5 Fe 2 As 2 single crystals. We find large twofold oscillations in the vicinity of the superconducting transition, when the direction of applied magnetic field is rotated within the basal plane. To avoid the influences from sample geometry or current flow direction, the sample was designed as Corbino-shape for in-plane and mesa-shape for out-of-plane measurements. Theoretical analysis shows that the nematic superconductivity arises from the weak mixture of the quasi-degenerate s-wave and d-wave components of the superconducting condensate, most probably induced by a weak anisotropy of stresses inherent to single crystals.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 8
DOI: 10.1038/s41467-017-02016-y
|
“Two-in-one solution using insect wings to produce graphene-graphite films for efficient electrocatalysis”. Li H, Zhang L, Li L, Wu C, Huo Y, Chen Y, Liu X, Ke X, Luo J, Van Tendeloo G, Nano Research 12, 33 (2019). http://doi.org/10.1007/S12274-018-2172-Z
Abstract: Natural organisms contain rich elements and naturally optimized smart structures, both of which have inspired various innovative concepts and designs in human society. In particular, several natural organisms have been used as element sources to synthesize low-cost and environmentally friendly electrocatalysts for the oxygen reduction reaction (ORR) in fuel cells and metal-air batteries, which are clean energy devices. However, to date, no naturally optimized smart structures have been employed in the synthesis of ORR catalysts, including graphene-based materials. Here, we demonstrate a novel strategy to synthesize graphene-graphite films (GGFs) by heating butterfly wings coated with FeCl3 in N-2, in which the full power of natural organisms is utilized. The wings work not only as an element source for GGF generation but also as a porous supporting structure for effective nitrogen doping, two-dimensional spreading, and double-face exposure of the GGFs. These GGFs exhibit a half-wave potential of 0.942 V and a H2O2 yield of < 0.07% for ORR electrocatalysis; these values are comparable to those for the best commercial Pt/C and all previously reported ORR catalysts in alkaline media. This two-in-one strategy is also successful with cicada and dragonfly wings, indicating that it is a universal, green, and cost-effective method for developing high-performance graphene-based materials.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 7.354
Times cited: 7
DOI: 10.1007/S12274-018-2172-Z
|
“Direct visualization of irreducible ferrielectricity in crystals”. Du K, Guo L, Peng J, Chen X, Zhou Z-N, Zhang Y, Zheng T, Liang Y-P, Lu J-P, Ni Z-H, Wang S-S, Van Tendeloo G, Zhang Z, Dong S, Tian H, npj Quantum Materials 5, 49 (2020). http://doi.org/10.1038/S41535-020-00252-Y
Abstract: In solids, charge polarity can one-to-one correspond to spin polarity phenomenologically, e.g., ferroelectricity/ferromagnetism, antiferroelectricity/antiferromagnetism, and even dipole-vortex/magnetic-vortex, but ferrielectricity/ferrimagnetism kept telling a disparate story in microscopic level. Since the definition of a charge dipole involves more than one ion, there may be multiple choices for a dipole unit, which makes most ferrielectric orders equivalent to ferroelectric ones, i.e., this ferrielectricity is not necessary to be a real independent branch of polarity. In this work, by using the spherical aberration-corrected scanning transmission electron microscope, we visualize a nontrivial ferrielectric structural evolution in BaFe2Se3, in which the development of two polar sub-lattices is out-of-sync, for which we term it as irreducible ferrielectricity. Such irreducible ferrielectricity leads to a non-monotonic behavior for the temperature-dependent polarization, and even a compensation point in the ordered state. Our finding unambiguously distinguishes ferrielectrics from ferroelectrics in solids.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1038/S41535-020-00252-Y
|
“Atomic defects, functional groups and properties in MXenes”. Cui W, Hu Z-Y, Unocic RR, Van Tendeloo G, Sang X, Chinese Chemical Letters 32, 339 (2021). http://doi.org/10.1016/J.CCLET.2020.04.024
Abstract: MXenes, a new family of functional two-dimensional (2D) materials, have shown great potential for an extensive variety of applications within the last decade. Atomic defects and functional groups in MXenes are known to have a tremendous influence on the functional properties. In this review, we focus on recent progress in the characterization of atomic defects and functional group chemistry in MXenes, and how to control them to directly influence various properties (e.g., electron transport, Li' adsorption, hydrogen evolution reaction (HER) activity, and magnetism) of 2D MXenes materials. Dynamic structural transformations such as oxidation and growth induced by atomic defects in MXenes are also discussed. The review thus provides perspectives on property optimization through atomic defect engineering, and bottom-up synthesis methods based on defect-assisted homoepitaxial growth of MXenes. (C) 2020 Chinese Chemical Society and Institute of Materia Medica, Chinese Academy of Medical Sciences. Published by Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.932
DOI: 10.1016/J.CCLET.2020.04.024
|
“Interfacial gliding-driven lattice oxygen release in layered cathodes”. Sun C, Liao X, Peng H, Zhang C, Van Tendeloo G, Zhao Y, Wu J, Cell reports physical science 3 (2022). http://doi.org/10.1016/J.XCRP.2021.100695
Abstract: The oxygen release of layered cathodes causes many battery failures, but the underlying mechanism in an actual working cathode is still elusive as it involves secondary agglomerates that introduce complicated boundary structures. Here, we report a general structure instability on the mismatch boundaries driven by interfacial gliding-it introduces a shear stress causing a distortion of the metal-oxygen octahedra framework that reduces its kinetic stability. The migration of cations and diffusion of oxygen vacancies continue to degrade the whole particle from the boundary to the interior, followed by the formation of nano-sized cracks on the fast-degrading interfaces. This work reveals a robust chemical and mechanical interplay on the oxygen release inherent to the intergranular boundaries of layered cathodes. It also suggests that radially patterned columnar grains with low-angle planar boundaries would be an efficient approach to mitigate the boundary oxygen release.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
DOI: 10.1016/J.XCRP.2021.100695
|
“Direct observation of cation diffusion driven surface reconstruction at van der Waals gaps”. Cui W, Lin W, Lu W, Liu C, Gao Z, Ma H, Zhao W, Van Tendeloo G, Zhao W, Zhang Q, Sang X, Nature communications 14, 554 (2023). http://doi.org/10.1038/S41467-023-35972-9
Abstract: Weak interlayer van der Waals (vdW) bonding has significant impact on the surface/interface structure, electronic properties, and transport properties of vdW layered materials. Unraveling the complex atomistic dynamics and structural evolution at vdW surfaces is therefore critical for the design and synthesis of the next-generation vdW layered materials. Here, we show that Ge/Bi cation diffusion along the vdW gap in layered GeBi2Te4 (GBT) can be directly observed using in situ heating scanning transmission electron microscopy (STEM). The cation concentration variation during diffusion was correlated with the local Te-6 octahedron distortion based on a quantitative analysis of the atomic column intensity and position in time-elapsed STEM images. The in-plane cation diffusion leads to out-of-plane surface etching through complex structural evolutions involving the formation and propagation of a non-centrosymmetric GeTe2 triple layer surface reconstruction on fresh vdW surfaces, and GBT subsurface reconstruction from a septuple layer to a quintuple layer. Our results provide atomistic insight into the cation diffusion and surface reconstruction in vdW layered materials. Weak interlayer van der Waals (vdW) bonding has significant impact on the structure and properties of vdW layered materials. Here authors use in-situ aberration-corrected ADF-STEM for an atomistic insight into the cation diffusion in the vdW gaps and the etching of vdW surfaces at high temperatures.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 16.6
DOI: 10.1038/S41467-023-35972-9
|
“Analytical TEM study of CVD diamond growth on TiO2 sol-gel layers”. Lu Y-G, Verbeeck J, Turner S, Hardy A, Janssens SD, De Dobbelaere C, Wagner P, Van Bael MK, Van Tendeloo G, Diamond and related materials 23, 93 (2012). http://doi.org/10.1016/j.diamond.2012.01.022
Abstract: The early growth stages of chemical vapor deposition (CVD) diamond on a solgel TiO2 film with buried ultra dispersed diamond seeds (UDD) have been studied. In order to investigate the diamond growth mechanism and understand the role of the TiO2 layer in the growth process, high resolution transmission electron microscopy (HRTEM), energy-filtered TEM and electron energy loss spectroscopy (EELS) techniques were applied to cross sectional diamond film samples. We find evidence for the formation of TiC crystallites inside the TiO2 layer at different diamond growth stages. However, there is no evidence that diamond nucleation starts from these crystallites. Carbon diffusion into the TiO2 layer and the chemical bonding state of carbon (sp2/sp3) were both extensively investigated. We provide evidence that carbon diffuses through the TiO2 layer and that the diamond seeds partially convert to amorphous carbon during growth. This carbon diffusion and diamond to amorphous carbon conversion make the seed areas below the TiO2 layer grow and bend the TiO2 layer upwards to form the nucleation center of the diamond film. In some of the protuberances a core of diamond seed remains, covered by amorphous carbon. It is however unlikely that the remaining seeds are still active during the growth process.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.561
Times cited: 16
DOI: 10.1016/j.diamond.2012.01.022
|
“Atomic resolution mapping of phonon excitations in STEM-EELS experiments”. Egoavil R, Gauquelin N, Martinez GT, Van Aert S, Van Tendeloo G, Verbeeck J, Ultramicroscopy 147, 1 (2014). http://doi.org/10.1016/j.ultramic.2014.04.011
Abstract: Atomically resolved electron energy-loss spectroscopy experiments are commonplace in modern aberration-corrected transmission electron microscopes. Energy resolution has also been increasing steadily with the continuous improvement of electron monochromators. Electronic excitations however are known to be delocalized due to the long range interaction of the charged accelerated electrons with the electrons in a sample. This has made several scientists question the value of combined high spatial and energy resolution for mapping interband transitions and possibly phonon excitation in crystals. In this paper we demonstrate experimentally that atomic resolution information is indeed available at very low energy losses around 100 meV expressed as a modulation of the broadening of the zero loss peak. Careful data analysis allows us to get a glimpse of what are likely phonon excitations with both an energy loss and gain part. These experiments confirm recent theoretical predictions on the strong localization of phonon excitations as opposed to electronic excitations and show that a combination of atomic resolution and recent developments in increased energy resolution will offer great benefit for mapping phonon modes in real space.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 22
DOI: 10.1016/j.ultramic.2014.04.011
|
Blumenau AT, Frauenheim T, Ö,berg S, Willems B, Van Tendeloo G (2004) Dislocation structures in diamond: density-functional based modelling and high resolution electron microscopy. Trans Tech Publications, s.l
Keywords: MA1 Book as author; Electron microscopy for materials research (EMAT)
|
“Electronically coupled complementary interfaces between perovskite band insulators”. Huijben M, Rijnders G, Blank DHA, Bals S, Van Aert S, Verbeeck J, Van Tendeloo G, Brinkman A, Hilgenkamp H, Nature materials 5, 556 (2006). http://doi.org/10.1038/nmat1675
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 39.737
Times cited: 315
DOI: 10.1038/nmat1675
|
“Low-dose patterning of platinum nanoclusters on carbon nanotubes by focused-electron-beam-induced deposition as studied by TEM”. Ke X, Bittencourt C, Bals S, Van Tendeloo G, Beilstein journal of nanotechnology 4, 77 (2013). http://doi.org/10.3762/bjnano.4.9
Abstract: Focused-electron-beam-induced deposition (FEBID) is used as a direct-write approach to decorate ultrasmall Pt nanoclusters on carbon nanotubes at selected sites in a straightforward maskless manner. The as-deposited nanostructures are studied by transmission electron microscopy (TEM) in 2D and 3D, demonstrating that the Pt nanoclusters are well-dispersed, covering the selected areas of the CNT surface completely. The ability of FEBID to graft nanoclusters on multiple sides, through an electron-transparent target within one step, is unique as a physical deposition method. Using high-resolution TEM we have shown that the CNT structure can be well preserved thanks to the low dose used in FEBID. By tuning the electron-beam parameters, the density and distribution of the nanoclusters can be controlled. The purity of as-deposited nanoclusters can be improved by low-energy electron irradiation at room temperature.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.127
Times cited: 12
DOI: 10.3762/bjnano.4.9
|
“Molecular shape-selectivity of MFI zeolite nanosheets in n-decane isomerization and hydrocracking”. Verheyen E, Jo C, Kurttepeli M, Vanbutsele G, Gobechiya E, Korányi TI, Bals S, Van Tendeloo G, Ryoo R, Kirschhock CEA, Martens JA;, Journal of catalysis 300, 70 (2013). http://doi.org/10.1016/j.jcat.2012.12.017
Abstract: MFI zeolite nanosheets with thickness of 2 and 8 nm were synthesized, transformed into bifunctional catalysts by loading with platinum and tested in n-decane isomerization and hydrocracking. Detailed analysis of skeletal isomers and hydrocracked products revealed that the MFI nanosheets display transition-state shape-selectivity similar to bulk MFI zeolite crystals. The suppressed formation of bulky skeletal isomers and C5 cracking products are observed both in the nanosheets and the bulk crystals grown in three dimensions. This is typical for restricted transition-state shape-selectivity, characteristic for the MFI type pores. It is a first clear example of transition-state shape-selectivity inside a zeolitic nanosheet. Owing to the short diffusion path across the sheets, expression of diffusion-based discrimination of reaction products in the MFI nanosheets was limited. The 2-methylnonane formation among monobranched C10 isomers and 2,7-dimethyloctane among dibranched C10 isomers, which in MFI zeolite are favored by product diffusion, was much less favored on the nanosheets compared to the reference bulk ZSM-5 material.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.844
Times cited: 121
DOI: 10.1016/j.jcat.2012.12.017
|
Goorden L, Van Tendeloo G, Lenaerts S, Deblonde M, et al. (2009) Nanotechnologie: gewikt en gewogen. NanoSoc
Keywords: Minutes and reports; Engineering sciences. Technology; Engineering Management (ENM); Sustainable Energy, Air and Water Technology (DuEL); Electron microscopy for materials research (EMAT)
|
Goorden L, Van Tendeloo G, Lenaerts S, Deblonde M, van Oudheusden M, et al. (2009) Nanotechnologie op de agenda. NanoSoc
Keywords: Minutes and reports; Engineering sciences. Technology; Engineering Management (ENM); Society and Environment; Sustainable Energy, Air and Water Technology (DuEL); Electron microscopy for materials research (EMAT)
|
“Oxidation state and chemical shift investigation in transition metal oxides by EELS”. Tan H, Verbeeck J, Abakumov A, Van Tendeloo G, Ultramicroscopy 116, 24 (2012). http://doi.org/10.1016/j.ultramic.2012.03.002
Abstract: Transition metal L2,3 electron energy-loss spectra for a wide range of V-, Mn- and Fe-based oxides were recorded and carefully analyzed for their correlation with the formal oxidation states of the transition metal ions. Special attention is paid to obtain an accurate energy scale which provides absolute energy positions for all core-loss edges. The white-line ratio method, chemical shift method, ELNES fitting method, two-parameter method and other methods are compared and their validity is discussed. Both the ELNES fitting method and the chemical shift method have the advantage of a wide application range and good consistency but require special attention to accurately measure the core-loss edge position. The obtained conclusions are of fundamental importance, e.g., for obtaining atomic resolution oxidation state information in modern experiments.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 413
DOI: 10.1016/j.ultramic.2012.03.002
|
“Systematic evaluation of thermal and mechanical stability of different commercial and synthetic photocatalysts in relation to their photocatalytic activity”. Ribbens S, Beyers E, Schellens K, Mertens M, Ke X, Bals S, Van Tendeloo G, Meynen V, Cool P, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 156, 62 (2012). http://doi.org/10.1016/j.micromeso.2012.01.036
Abstract: The effect of thermal treatment and mechanical stress on the structural and photocatalytic properties of eight different (synthetic and commercial) photocatalysts has been thoroughly investigated. Different mesoporous Ti-based materials were prepared via surfactant based synthesis routes (e.g. Pluronic 123, CTMABr = Cetyltrimethylammonium bromide) or via template-free synthesis routes (e.g. trititanate nanotubes). Also, the stabilizing effect of the NaOH/NH4OH post-treatment on the templated mesoporous materials and their photocatalytic activity was investigated. Furthermore, the thermal and mechanical properties of commercially available titanium dioxides such as P25 Evonik® and Millenium PC500® were studied. The various photocatalysts were analyzed with N2-sorption, X-ray diffraction (XRD), high resolution transmission electron microscopy (HR-TEM), differential scanning calorimetry (DSC) and thermal gravimetric analysis (TGA) to obtain information concerning the specific surface area, pore volume, crystal structure, morphology, phase transitions, etc. In general, results show that the NaOH post-treatment leads to an increased control of the crystallization process during calcination resulting in a higher thermal stability, but at the same time diminishes the photocatalytic activity. Mesoporous materials in which pre-synthesized nanoparticles are used as titania source have the best mechanical stability whereas the mechanical stability of the nanotubes is the most limited. At increased temperatures and pressures, the tested commercial titanium dioxides lose their superior photocatalytic activity caused by a decreased accessibility of the active sites. The observed changes in adsorption capacities and photocatalytic activities cannot be assigned to one single phenomenon. In this respect, it shows the need to define a general/standard method to compare different photocatalysts. Furthermore, it is shown that the photocatalytic properties do not necessarily deteriorate under thermal stress, but can be improved due to crystallization, even though the initial material is (partially) destroyed. It is shown that the usefulness of a specific type of photocatalyst strongly depends on the application and the temperature/pressure to which it needs to resist.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.615
Times cited: 8
DOI: 10.1016/j.micromeso.2012.01.036
|
“The effect of Y2O3 and YFeO3 additions on the critical current density of YBCO coated conductors”. Lao M, Eisterer M, Stadel O, Meledin A, Van Tendeloo G, 1-4 (2014). http://doi.org/10.1088/1742-6596/507/2/022012
Abstract: The pinning mechanism of MOCVD-grown YBCO coated conductors with Y2O3 precipitates was investigated by angle-resolved transport measurement of Je in a wide range of temperature and magnetic fields. Aside from the Y2O3 nanoprecipitates, a-axis grains and threading dislocation along the c-axis were found in the YBCO layer. The Y2O3 precipitates are less effective pinning centers at lower temperature. The tapes with precipitates show a higher anisotropy with larger J(c) at H parallel to ab than H parallel to c. This behavior was attributed to the preferred alignment of the nanoprecipitates along the ab-plane.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
Times cited: 1
DOI: 10.1088/1742-6596/507/2/022012
|
“Using the macroscopic scale to predict the nano-scale behavior of YSZ thin films”. Lamas JS, Leroy WP, Lu Y-G, Verbeeck J, Van Tendeloo G, Depla D, Surface and coatings technology 238, 45 (2014). http://doi.org/10.1016/j.surfcoat.2013.10.034
Abstract: In this work, Yttria-stabilized zirconia (YSZ) thin films were deposited using dual reactive magnetron sputtering. By varying the deposition conditions, the film morphology and texture of the thin films are tuned and biaxial alignment is obtained. Studying the crystallographic and microstructural properties of the YSZ thin films, a tilted columnar growth was identified. This tilt is shown to be dependent on the compositional gradient of the sample. The variation of composition within a single YSZ column measured via STEM-EDX is demonstrated to be equal to the macroscopic variation on a full YSZ sample when deposited under the same deposition parameters. A simple stress model was developed to predict the tilt of the growing columns. The results indicate that this model not only determines the column bending of the growing film but also confirms that a macroscopic approach is sufficient to determine the compositional gradient in a single column of the YSZ thin films. (C) 2013 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.589
Times cited: 8
DOI: 10.1016/j.surfcoat.2013.10.034
|
“Existence of Ti2+States on the Surface of Heavily Reduced SrTiO3Nanocubes”. Shetty S, Sinha SK, Ahmad R, Singh AK, Van Tendeloo G, Ravishankar N, Chemistry of materials , acs.chemmater.7b04113 (2017). http://doi.org/10.1021/acs.chemmater.7b04113
Abstract: Using advanced electron microscopy, we demonstrate the presence of Ti2+ on the 001 surfaces of heavily reduced strontium titanate nanocubes. While high-angle annular dark field images show a clear difference between the surfaces of the unreduced and reduced samples, electron energy loss spectroscopy detects the presence of Ti2+ on the surface of the reduced cubes. Conventional reduction only leads to the formation of Ti3+ and involves the use of high temperatures. In our case, reduction is achieved at relatively lower temperatures in the solid state using sodium borohydride as the reducing agent. Our findings provide insights into the optical properties of the samples and provide a convenient method to produce highly reduced surfaces that could demonstrate a range of exotic physical phenomena
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 8
DOI: 10.1021/acs.chemmater.7b04113
|
“Blue-edge slow photons promoting visible-light hydrogen production on gradient ternary 3DOM TiO 2 -Au-CdS photonic crystals”. Zhao H, Hu Z, Liu J, Li Y, Wu M, Van Tendeloo G, Su B-L, Nano energy 47, 266 (2018). http://doi.org/10.1016/j.nanoen.2018.02.052
Abstract: The slow photon effect, a structural effect of photonic crystal photocatalyst, is very efficient in the enhancement of photocatalytic reactions. However, slow photons in powdered photonic crystal photocatalyst have rarely been discussed because they are usually randomly oriented when the photocatalytic reaction happens in solution under constant stirring. In this work, for the first time we design a gradient ternary TiO2-Au-CdS photonic crystal based on three-dimensionally ordered macroporous (3DOM) TiO2 as skeleton, Au as electron transfer medium and CdS as active material for photocatalytic H2 production under visible-light. As a result, this gradient ternary photocatalyst is favorable to simultaneously enhance light absorption, extend the light responsive region and reduce the recombination rate of the charge carriers. In particular, we found that slow photons at blue-edge exhibit much higher photocatalytic activity than that at red-edge. The photonic crystal photocatalyst with a macropore size of 250 nm exhibits the highest visible-light H2 production rate of 3.50 mmolh⁻¹g⁻¹ due to the slow photon energy at the blue-edge to significantly enhance the incident photons utilization. This work verifies that slow photons at the blue-edge can largely enhance light harvesting and sheds a light on designing the powdered photonic crystal photocatalyst to promote the photocatalytic H2 production via slow photon effect.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.343
Times cited: 33
DOI: 10.1016/j.nanoen.2018.02.052
|
“Hierarchical CdS/m-TiO 2 /G ternary photocatalyst for highly active visible light-induced hydrogen production from water splitting with high stability”. Lu Y, Cheng X, Tian G, Zhao H, He L, Hu J, Wu S-M, Dong Y, Chang G-G, Lenaerts S, Siffert S, Van Tendeloo G, Li Z-F, Xu L-L, Yang X-Y, Su B-L, Nano energy 47, 8 (2018). http://doi.org/10.1016/j.nanoen.2018.02.021
Abstract: Hierarchical semiconductors are the most important photocatalysts, especially for visible light-induced hydrogen production from water splitting. We demonstrate herein a hierarchical electrostatic assembly approach to hierarchical CdS/m-TiO2/G ternary photocatalyst, which exhibits high photoactivity and excellent photostability (more than twice the activity of pure CdS while 82% of initial photoactivity remained after 15 recycles during 80 h irradiation). The ternary nanojunction effect of the photocatalyst has been investigated from orbitals hybrid, bonding energy to atom-stress distortion and nano-interface fusion. And a coherent separation mechanism of charge carriers in the ternary system has been proposed at an atomic/nanoscale. This work offers a promising way to inhibit the photocorrosion of CdS and, more importantly, provide new insights for the design of ternary nanostructured photocatalysts with an ideal heterojunction.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 12.343
Times cited: 58
DOI: 10.1016/j.nanoen.2018.02.021
|
“Influence of 4H-SiC substrate miscut on the epitaxy and microstructure of AlGaN/GaN heterostructures”. Gkanatsiou A, Lioutas CB, Frangis N, Polychroniadis EK, Prystawko P, Leszczynski M, Altantzis T, Van Tendeloo G, Materials science in semiconductor processing 91, 159 (2019). http://doi.org/10.1016/j.mssp.2018.11.008
Abstract: AlGaN/GaN heterostructures were grown on “on-axis” and 2° off (0001) 4H-SiC substrates by metalorganic vapor phase epitaxy (MOVPE). Structural characterization was performed by transmission electron microscopy. The dislocation density, being greater in the on-axis case, is gradually reduced in the GaN layer and is forming
dislocation loops in the lower region. Steps aligned along [11̅00] in the off-axis case give rise to simultaneous defect formation. In the on-axis case, an almost zero density of steps is observed, with the main origin of defects probably being the orientation mismatch at the grain boundaries between the small not fully coalesced AlN grains. V-shaped formations are observed in the AlN nucleation layer, but are more frequent in the off-axis case, probably enhanced by the presence of steps. These V-shaped formations are completely overgrown by the GaN layer, during the subsequent deposition, presenting AlGaN areas in the walls of the defect, indicating an interdiffusion between the layers. Finally, at the AlGaN/GaN heterostructure surface in the on-axis case, V-shapes are observed, with the AlN spacer and AlGaN (21% Al) thickness on relaxed GaN exceeding the critical thickness for relaxation. On the other hand, no relaxation in the form of V-shape creation is observed in the off-axis case, probably due to the smaller AlGaN thickness (less than 21% Al). The AlN spacer layer, grown in between the heterostructure, presents a uniform thickness and clear interfaces.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.359
Times cited: 1
DOI: 10.1016/j.mssp.2018.11.008
|