“Multiple twinning as a structure directing mechanism in layered rock-salt-type oxides : NaMnO2 polymorphism, redox potentials, and magnetism”. Abakumov AM, Tsirlin AA, Bakaimi I, Van Tendeloo G, Lappas A, Chemistry of materials 26, 3306 (2014). http://doi.org/10.1021/cm5011696
Abstract: New polymorphs of NaMnO2 have been observed using transmission electron microscopy and synchrotron X-ray powder diffraction. Coherent twin planes confined to the (NaMnO2) layers, parallel to the (10 (1) over bar) crystallographic planes of the monoclinic layered rock-salt-type alpha-NaMnO2 (O3) structure, form quasi-periodic modulated sequences, with the known alpha-and beta-NaMnO2 polymorphs as the two limiting cases. The energy difference between the polymorphic forms, estimated using a DFT-based structure relaxation, is on the scale of the typical thermal energies that results in a high degree of stacking disorder in these compounds. The results unveil the remarkable effect of the twin planes on both the magnetic and electrochemical properties. The polymorphism drives the magnetic ground state from a quasi-1D spin system for the geometrically frustrated alpha-polymorph through a two-leg spin ladder for the intermediate stacking sequence toward a quasi-2D magnet for the beta-polymorph. A substantial increase of the equilibrium potential for Na deintercalation upon increasing the concentration of the twin planes is calculated, providing a possibility to tune the electrochemical potential of the layered rock-salt ABO(2) cathodes by engineering the materials with a controlled concentration of twins.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 35
DOI: 10.1021/cm5011696
|
“Photoemission study of CF4 rf-plasma treated multi-wall carbon nanotubes”. Felten A, Ghijsen J, Pireaux J-J, Whelan CM, Liang D, Van Tendeloo G, Bittencourt C, Carbon 46, 1271 (2008). http://doi.org/10.1016/j.carbon.2008.04.027
Abstract: Multi-wall carbon nanotubes (MWCNTs) were exposed to a CF4 rf-plasma. X-ray photoelectron spectroscopy analysis shows that the treatment effectively grafts fluorine atoms onto the MWCNTs. The fluorine atomic concentration and the nature of the CF bond (semi-ionic or covalent) can be tuned by varying the exposure time. Ultraviolet photoelectron spectroscopy analysis confirms that the valence electronic states are altered by the grafting of fluorine atoms. Characterization with high-resolution transmission electron microscopy reveals that while the plasma treatment does not induce significant etching impact on the CNT-surface, it does increase the number of active sites for gold cluster formation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.337
Times cited: 21
DOI: 10.1016/j.carbon.2008.04.027
|
“Preparation of nanocrystalline titania powder via aerosol pyrolysis of titanium tetrabutoxide”. Ahonen PP, Kauppinen EI, Joubert JC, Deschanvres JL, Van Tendeloo G, Journal of materials research 14, 3938 (1999). http://doi.org/10.1557/JMR.1999.0533
Abstract: Nanocrystalline titanium dioxide was prepared via aerosol pyrolysis of titanium alkoxide precursor at 200-580 degrees C in air and in nitrogen atmospheres. Powders were characterized by x-ray diffraction, thermogravimetric analysis, Brunauer-Emmett-Teller analysis, scanning electron microscopy, transmission electron microscopy, energy dispersive spectroscopy, x-ray fluorescence, Raman and infrared spectroscopy, and Berner-type low-pressure impactor. The anatase phase transition was initiated at 500 degrees C in nitrogen and at 580 degrees C in air. Under other conditions amorphous powders were observed and transformed to nanocrystalline TiO2 via thermal postannealing. In air, smooth and spherical particles with 2-4-mu m diameter were formed with an as-expected tendency to convert to rutile in the thermal postannealings. In nitrogen, a fraction of the titanium tetrabutoxide precursor evaporated and formed ultrafine particles via the gas-to-particle conversion. At 500 degrees C thermally stable anatase phase was formed in nitrogen. A specific surface area as high as 280 m(2) g(-1) was observed for an as-prepared powder.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.673
Times cited: 38
DOI: 10.1557/JMR.1999.0533
|
“Quantitative atomic resolution mapping using high-angle annular dark field scanning transmission electron microscopy”. Van Aert S, Verbeeck J, Erni R, Bals S, Luysberg M, van Dyck D, Van Tendeloo G, Ultramicroscopy 109, 1236 (2009). http://doi.org/10.1016/j.ultramic.2009.05.010
Abstract: A model-based method is proposed to relatively quantify the chemical composition of atomic columns using high angle annular dark field (HAADF) scanning transmission electron microscopy (STEM) images. The method is based on a quantification of the total intensity of the scattered electrons for the individual atomic columns using statistical parameter estimation theory. In order to apply this theory, a model is required describing the image contrast of the HAADF STEM images. Therefore, a simple, effective incoherent model has been assumed which takes the probe intensity profile into account. The scattered intensities can then be estimated by fitting this model to an experimental HAADF STEM image. These estimates are used as a performance measure to distinguish between different atomic column types and to identify the nature of unknown columns with good accuracy and precision using statistical hypothesis testing. The reliability of the method is supported by means of simulated HAADF STEM images as well as a combination of experimental images and electron energy-loss spectra. It is experimentally shown that statistically meaningful information on the composition of individual columns can be obtained even if the difference in averaged atomic number Z is only 3. Using this method, quantitative mapping at atomic resolution using HAADF STEM images only has become possible without the need of simultaneously recorded electron energy loss spectra.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
Times cited: 166
DOI: 10.1016/j.ultramic.2009.05.010
|
“A-site ordering versus electronic inhomogeneity in colossally magnetoresistive manganite films”. Moshnyaga V, Sudheendra L, Lebedev OI, Koster SA, Gehrke K, Shapoval O, Belenchuk A, Damaschke B, Van Tendeloo G, Samwer K, Physical review letters 97, 107205 (2006). http://doi.org/10.1103/PhysRevLett.97.107205
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.462
Times cited: 43
DOI: 10.1103/PhysRevLett.97.107205
|
“Spin ladder compound Pb0.55Cd0.45V2O5: synthesis and investigation”. Tsirlin AA, Shpanchenko RV, Antipov EV, Bougerol C, Hadermann J, Van Tendeloo G, Schnelle W, Rosner H, Physical review : B : condensed matter and materials physics 76, 104429 (2007). http://doi.org/10.1103/PhysRevB.76.104429
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 1
DOI: 10.1103/PhysRevB.76.104429
|
“Structural phase transitions and stress accommodation in (La0.67Ca0.33MnO3)1.x:(MgO)x composite films”. Lebedev OI, Verbeeck J, Van Tendeloo G, Shapoval O, Belenchuk A, Moshnyaga V, Damaschke B, Samwer K, Physical review : B : condensed matter and materials physics 66, 104421 (2002). http://doi.org/10.1103/PhysRevB.66.104421
Abstract: Composite (La0.67Ca0.33MnO3)(1-x):(MgO)(x) films were prepared by metalorganic aerosol deposition on a (100)MgO substrate for different concentrations of the (MgO) phase (0less than or equal toxless than or equal to0.8). At xapproximate to0.3 a percolation threshold in conductivity is reached, at which an infinite insulating MgO cluster forms around the La0.67Ca0.33MnO3 grains. This yields a drastic increase of the electrical resistance for films with x>0.3. The film structure is characterized by x-ray diffraction and transmission electron microscopy. The local structure of the La0.67Ca0.33MnO3 within the film depends on the MgO concentration which grows epitaxially along the domain boundaries. A different structural phase transition from the orthorhombic Pnma structure to an unusual rhombohedral R (3) over barc structure at the percolation threshold xapproximate to0.3 is found for La0.67Ca0.33MnO3. A three-dimensional stress accommodation in thick films through a phase transition is suggested.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 48
DOI: 10.1103/PhysRevB.66.104421
|
“Structure and properties of the YBa2Cu3O7-x/LaAlO3 superlattices”. Lebedev OI, Hamet JF, Van Tendeloo G, Beaumont V, Raveau B, Journal of applied physics 90, 5261 (2001). http://doi.org/10.1063/1.1406963
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.068
Times cited: 13
DOI: 10.1063/1.1406963
|
“Tailored vapor-phase growth of CuxO-TiO2(x=1,2) nanomaterials decorated with Au particles”. Barreca D, Carraro G, Gasparotto A, Maccato C, Lebedev OI, Parfenova A, Turner S, Tondello E, Van Tendeloo G, Langmuir: the ACS journal of surfaces and colloids 27, 6409 (2011). http://doi.org/10.1021/la200698t
Abstract: We report on the fabrication of CuxOTiO2 (x = 1, 2) nanomaterials by an unprecedented vapor-phase approach. The adopted strategy involves the growth of porous CuxO matrices by means of chemical vapor deposition (CVD), followed by the controlled dispersion of TiO2 nanoparticles. The syntheses are performed on Si(100) substrates at temperatures of 400550 °C under wet oxygen atmospheres, adopting Cu(hfa)2·TMEDA (hfa =1,1,1,5,5,5-hexafluoro-2,4-pentanedionate; TMEDA = N,N,N′,N′-tetramethylethylenediamine) and Ti(O-iPr)2(dpm)2 (O-iPr = isopropoxy; dpm = 2,2,6,6-tetramethyl-3,5-heptanedionate) as copper and titanium precursors, respectively. Subsequently, finely dispersed gold nanoparticles are introduced in the as-prepared systems via radio frequency (RF)-sputtering under mild conditions. The synthesis process results in the formation of systems with chemical composition and nano-organization strongly dependent on the nature of the initial CuxO matrix and on the deposited TiO2 amount. The decoration with low-size gold clusters paves the way to the engineering of hierarchically organized nanomaterials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.833
Times cited: 36
DOI: 10.1021/la200698t
|
“Ca6.3Mn3Ga4.4Al1.3O18: a novel complex oxide with 3D tetrahedral framework”. Abakumov AM, Hadermann J, Kalyuzhnaya AS, Rozova MG, Mikheev MG, Van Tendeloo G, Antipov EV, Journal of solid state chemistry 178, 3137 (2005). http://doi.org/10.1016/j.jssc.2005.07.028
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 5
DOI: 10.1016/j.jssc.2005.07.028
|
“Three-dimensional valency mapping in ceria nanocrystals”. Goris B, Turner S, Bals S, Van Tendeloo G, ACS nano 8, 10878 (2014). http://doi.org/10.1021/nn5047053
Abstract: Using electron tomography combined with electron energy loss spectroscopy (EELS), we are able to map the valency of the Ce ions in CeO2-x nanocrystals in three dimensions. Our results show a clear facet-dependent reduction shell at the surface of ceria nanoparticles; {111} surface facets show a low surface reduction, whereas at {001} surface facets, the cerium ions are more likely to be reduced over a larger surface shell. Our generic tomographic technique allows a full 3D data cube to be reconstructed, containing an EELS spectrum in each voxel. This possibility enables a three-dimensional investigation of a plethora of material-specific physical properties such as valency, chemical composition, oxygen coordination, or bond lengths, triggering the synthesis of nanomaterials with improved properties.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 85
DOI: 10.1021/nn5047053
|
“Fabrication and Characterization of Fe2O3-Based Nanostructures Functionalized with Metal Particles and Oxide Overlayers”. Barreca D, Carraro G, Gasparotto A, Maccato C, Warwick MEA, Turner S, Van Tendeloo G, Journal of advanced microscopy research 10, 239 (2015). http://doi.org/10.1166/jamr.2015.1270
Abstract: We report on the design of nanosystems based on functionalized -Fe 2 O 3 nanostructures supported on fluorine-doped tin oxide (FTO) substrates. The target materials were developed by means of hybrid vapor phase approaches, combining plasma assisted-chemical vapor deposition (PA-CVD) for the production of iron(III) oxide systems and the subsequent radio frequency (RF)-sputtering or atomic layer deposition (ALD) for the functionalization with Au nanoparticles or TiO 2 overlayers, respectively. The interplay between material characteristics and the adopted processing parameters was investigated by complementary analytical techniques, encompassing X-ray photoelectron spectroscopy (XPS), field emission-scanning electron microscopy (FE-SEM), high angle annular dark field-scanning transmission electron microscopy (HAADF-STEM), and energy dispersive X-ray spectroscopy (EDXS). The obtained results highlight the possibility of fabricating Au/ -Fe 2 O 3 nanocomposites, with a controlled dispersion and distribution of metal particles, and TiO 2 / -Fe 2 O 3 heterostructures, characterized by an intimate coupling between the constituent oxides.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1166/jamr.2015.1270
|
“Direct Observation of Luminescent Silver Clusters Confined in Faujasite Zeolites”. Altantzis T, Coutino-Gonzalez E, Baekelant W, Martinez GT, Abakumov AM, Van Tendeloo G, Roeffaers MBJ, Bals S, Hofkens J, ACS nano 10, 7604 (2016). http://doi.org/10.1021/acsnano.6b02834
Abstract: One of the ultimate goals in the study of metal clusters is the correlation between the atomic-scale organization and their physicochemical properties. However, direct observation of the atomic organization of such minuscule metal clusters is heavily hindered by radiation damage imposed by the different characterization techniques. We present direct evidence of the structural arrangement, at an atomic level, of luminescent silver species stabilized in faujasite (FAU) zeolites using aberration-corrected scanning transmission electron microscopy. Two different silver clusters were identified in Ag-FAU zeolites, a trinuclear silver species associated with green emission and a tetranuclear silver species related to yellow emission. By combining direct imaging with complementary information obtained from X-ray powder diffraction and Rietveld analysis, we were able to elucidate the main differences at an atomic scale between luminescent (heat-treated) and nonluminescent (cation-exchanged) Ag-FAU zeolites. It is expected that such insights will trigger the directed synthesis of functional metal nanocluster-zeolite composites with tailored luminescent properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.942
Times cited: 57
DOI: 10.1021/acsnano.6b02834
|
“β-Na1.7IrO3: A Tridimensional Na-Ion Insertion Material with a Redox Active Oxygen Network”. Pearce PE, Rousse G, Karakulina OM, Hadermann J, Van Tendeloo G, Foix D, Fauth F, Abakumov AM, Tarascon J-M, Chemistry of materials 30, 3285 (2018). http://doi.org/10.1021/acs.chemmater.8b00320
Abstract: The revival of the Na-ion battery concept has prompted an intense search for new high capacity Na-based positive electrodes. Recently, emphasis has been placed on manipulating Na-based layered compounds to trigger the participation of the anionic network. We further explored this direction and show the feasibility of achieving anionic-redox activity in three-dimensional Na-based compounds. A new 3D β-Na1.7IrO3 phase was synthesized in a two-step process, which involves first the electrochemical removal of Li from β-Li2IrO3 to produce β-IrO3, which is subsequently reduced by electrochemical Na insertion. We show that β-Na1.7IrO3 can reversibly uptake nearly 1.3 Na+ per formula unit through an uneven voltage profile characterized by the presence of four plateaus related to structural transitions. Surprisingly, the β-Na1.7IrO3 phase was found to be stable up to 600 °C, while it could not be directly synthesized via conventional synthetic methods. Although these Na-based iridate phases are of limited practical interest, they help to understand how introducing highly polarizable guest ions (Na+) into host rocksalt-derived oxide structures affects the anionic redox mechanism.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 6
DOI: 10.1021/acs.chemmater.8b00320
|
“Manipulating topological transformations of polar structures through real-time observation of the dynamic polarization evolution”. Du K, Zhang M, Dai C, Zhou ZN, Xie YW, Ren ZH, Tian H, Chen LQ, Van Tendeloo G, Zhang Z, Nature communications 10, 4864 (2019). http://doi.org/10.1038/S41467-019-12864-5
Abstract: Topological structures based on controllable ferroelectric or ferromagnetic domain configurations offer the opportunity to develop microelectronic devices such as high-density memories. Despite the increasing experimental and theoretical insights into various domain structures (such as polar spirals, polar wave, polar vortex) over the past decade, manipulating the topological transformations of polar structures and comprehensively understanding its underlying mechanism remains lacking. By conducting an in-situ non-contact bias technique, here we systematically investigate the real-time topological transformations of polar structures in PbTiO3/SrTiO3 multilayers at an atomic level. The procedure of vortex pair splitting and the transformation from polar vortex to polar wave and out-of-plane polarization are observed step by step. Furthermore, the redistribution of charge in various topological structures has been demonstrated under an external bias. This provides new insights for the symbiosis of polar and charge and offers an opportunity for a new generation of microelectronic devices.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
DOI: 10.1038/S41467-019-12864-5
|
“Development of photocatalytic efficient Ti-based nanotubes and nanoribbons by conventional and microwave assisted synthesis strategies”. Ribbens S, Meynen V, Van Tendeloo G, Ke X, Mertens M, Maes BUW, Cool P, Vansant EF, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 114, 401 (2008). http://doi.org/10.1016/j.micromeso.2008.01.028
Abstract: Titanate nanotubes were prepared via a hydrothermal treatment of TiO2 powders (Riedel De Haen) in a basic solution. Morphology and structure of the prepared samples were characterized by high resolution transmission electron microscopy (HRTEM), selected area electron diffraction (SAED), XRD, FT-Raman spectroscopy, nitrogen sorption and DSC. The photocatalytic activity was evaluated by photocatalytic oxidation of rhodamine 6G. Trititanate nanotubes (TTNT) with inner pore diameters between 4 and 4.2 nm and surface areas up till 360 m(2)/g could be synthesized. The synthesis route was modified by introduction of a calcination step, by applying a lower hydrothermal temperature and microwave irradiation in order to increase the photocatalytic activity of the porous photoactive nanotubular materials. Calcination and a softer hydrothermal treatment led to the formation of anatase without affecting the surface area and nanotubular shape of the samples. In this way, the photocatalytic activity of the original trititanate nanotubes could be significantly increased. By making use of microwave assisted synthesis, the photocatalytic activity call also be increased due to the presence of anatase. However, by applying microwave synthesis, a different structure was obtained, nanoribbons (NR) instead of nanotubcs, resulting in a decrease in surface area and porosity.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA); Organic synthesis (ORSY)
Impact Factor: 3.615
Times cited: 47
DOI: 10.1016/j.micromeso.2008.01.028
|
“Graphitic nanocrystals inside the pores of mesoporous silica : synthesis, characterization and an adsorption study”. de Clippel F, Harkiolakis A, Vosch T, Ke X, Giebeler L, Oswald S, Houthoofd K, Jammaer J, Van Tendeloo G, Martens JA, Jacobs PA, Baron GV, Sels BF, Denayer JFM, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 144, 120 (2011). http://doi.org/10.1016/j.micromeso.2011.04.003
Abstract: This work presents a new carbonsilica hybrid material, denoted as CSM, with remarkable sorption properties. It consists of intraporous graphitic nanocrystals grown in the pores of mesoporous silica. CSM is obtained by a subtle incipient wetness impregnation of Al-containing mesoporous silica with furfuryl alcohol (FA)/hemelitol solutions. Both the volume match of the impregnation solution with that of the silica template pore volume, and the presence of Al3+ in the silica, are crucial to polymerize FA selectively inside the mesopores. Carbonization of the intraporous polymer was then performed by pyrolysis under He up to 1273 K. The resulting CSMs were examined by SEM, HRTEM, 27Al MAS NMR, N2 adsorption, XRD, TGA, TPD, XPS, pycnometry and Raman spectroscopy. Mildly oxidized graphitic-like carbon nanoblocks, consisting of a few graphene-like sheets, were thus identified inside the template mesopores. Random stacking of these carbon crystallites generates microporosity resulting in biporous materials at low carbon content and microporous materials at high carbon loadings. Very narrow pore distributions were obtained when pyrolysis was carried out under slow heating rate, viz. 1 K min−1. Adsorption and shape selective properties of the carbon filled mesoporous silica were studied by performing pulse chromatography and breakthrough experiments, and by measuring adsorption isotherms of linear and branched alkanes. Whereas the parent mesoporous silica shows unselective adsorption, their CSM analogues preferentially adsorb linear alkanes. The sorption capacity and selectivity can be adjusted by changing the pore size of the template or by varying the synthesis conditions. A relation between the carbon crystallites size and the shape selective behaviour of the corresponding CSM for instance is demonstrated. Most interestingly, CSM shows separation factors for linear and branched alkanes up to values comparable to those of zeolitic molecular sieves.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.615
Times cited: 15
DOI: 10.1016/j.micromeso.2011.04.003
|
“Synthesis and characterization of the new cyclosilicate hydrate (hexamethyleneimine)4.[Si8O16(OH)4].12H2O”. Verlooy PLH, Robeyns K, van Meervelt L, Lebedev OI, Van Tendeloo G, Martens JA, Kirschhock CEA, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 130, 14 (2010). http://doi.org/10.1016/j.micromeso.2009.10.006
Abstract: A new cyclosilicate hydrate with composition (C6H14N)4·[Si8O16(OH)4]·12H2O was crystallized and the structure determined by single-crystal X-ray diffraction. The structure, described by the tetragonal space group I41/a, with unit cell dimensions of a = 39.2150(2) Å and c = 14.1553(2) Å, contains columns of hydrogen-bonded cubic octamer silicate anions. The space between silicate columns holds hydrogen-bonded water and protonated hexamethyleneimine molecules compensating the negative charge of the silicate. The crystal water can be removed resulting in a rearrangement of the columns into orthorhombic symmetry. Removal of the organic moiety causes amorphisation. Flash evacuation results in a new microporous material with pore volumes typical of a zeolite.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.615
Times cited: 5
DOI: 10.1016/j.micromeso.2009.10.006
|
“Cu(OH)2 nanowires, CuO nanowires and CuO nanobelts”. Du GH, Van Tendeloo G, Chemical physics letters 393, 64 (2004). http://doi.org/10.1016/j.cplett.2004.06.017
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.815
Times cited: 145
DOI: 10.1016/j.cplett.2004.06.017
|
“Zn-Al layered double hydroxides: synthesis, characterization and photocatalytic application”. Seftel EM, Popovici E, Mertens M, de Witte K, Van Tendeloo G, Cool P, Vansant EF, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 113, 296 (2008). http://doi.org/10.1016/j.micromeso.2007.11.029
Keywords: A1 Journal article; Laboratory of adsorption and catalysis (LADCA); Electron microscopy for materials research (EMAT)
Impact Factor: 3.615
Times cited: 154
DOI: 10.1016/j.micromeso.2007.11.029
|
“Deposition of vanadium silicalite-1 nanoparticles on SBA-15 materials: structural and transport characteristics of SBA-VS-15”. Meynen V, Cool P, Vansant EF, Kortunov P, Grinberg F, Kärger J, Mertens M, Lebedev OI, Van Tendeloo G, Microporous and mesoporous materials 99, 14 (2007). http://doi.org/10.1016/j.micromeso.2006.08.029
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.615
Times cited: 23
DOI: 10.1016/j.micromeso.2006.08.029
|
“Flux pinning by Al-based nanoparticles embedded in YBCO: a transmission electron microscopic study”. ben Azzouz F, Zouaoui M, Mellekh A, Annabi M, Van Tendeloo G, ben Salem M, Physica: C : superconductivity 455, 19 (2007). http://doi.org/10.1016/j.physc.2007.01.033
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.404
Times cited: 39
DOI: 10.1016/j.physc.2007.01.033
|
“Formation of a combined micro- and mesoporous material using zeolite Beta nanoparticles”. van Oers CJ, Stevens WJJ, Bruijn E, Mertens M, Lebedev OI, Van Tendeloo G, Meynen V, Cool P, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 120, 29 (2009). http://doi.org/10.1016/j.micromeso.2008.08.056
Abstract: Composite micro- and mesoporous materials are synthesized using zeolite Beta nanoparticles without the need for a structure directing agent to form the mesopores. This leads to important ecological and economical advantages. The influence of the way of cooling the aged nanoparticles solution on the formation of the composite materials has been studied. The materials have been characterized towards porosity by N2-sorption, towards zeolitic properties by TGA, DRIFT, XRD and TEM, towards aluminium content by EPMA. All prepared structures possess zeolitic properties. However, the method of cooling down of the aged seeds leads to differences in the porosity and intensity of the zeolitic characteristics.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.615
Times cited: 42
DOI: 10.1016/j.micromeso.2008.08.056
|
“Modulation-free phase in heavily Pb-doped (Bi,Pb)2212 crystals”. Musolino N, Bals S, Van Tendeloo G, Clayton N, Walker E, Flükiger R, Physica: C : superconductivity 399, 1 (2003). http://doi.org/10.1016/S0921-4534(03)01324-8
Abstract: We report the complete disappearance of the structural modulation in heavily lead-doped Bi2-xPbxSr2CaCu2O8+delta crystals observed by transmission electron microscopy. Crystals with a nominal lead content of x = 0.8, corresponding to an effective lead content of x = 0.39, yield the non-modulated phase. The superconducting properties of this modulation-free phase (beta phase) have been studied and compared to those of undoped crystals displaying the modulated phase (alpha phase). Magnetisation measurements reveal that the irreversibility field H-irr(T) and relaxation rates are strongly improved within the beta phase. Measurements of the lower critical field, H-c1, show that the anisotropy factor, epsilon, is considerably reduced in the modulation-free crystals. This is the signature of stronger coupling between CuO2 layers which in turn deeply influences the effectiveness of the pinning. These measurements explain the enhanced pinning properties in moderately Pb-doped crystals in which the alpha phase and beta phase coexist. The enhanced pinning is not only due to the alpha/beta interfaces, which act as effective pinning centers: the emergence of modulation-free domains, characterized by a strongly reduced anisotropy, also significantly contribute to this effect. (C) 2003 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.404
Times cited: 31
DOI: 10.1016/S0921-4534(03)01324-8
|
“Multi-step loading of titania on mesoporous silica: influence of the morphology and the porosity on the catalytic degradation of aqueous pollutants and VOC's”. de Witte K, Meynen V, Mertens M, Lebedev OI, Van Tendeloo G, Sepúlveda-Escribano A, Rodríguez-Reinoso F, Vansant EF, Cool P, Applied catalysis : B : environmental 84, 125 (2008). http://doi.org/10.1016/j.apcatb.2008.03.015
Abstract: Titania nanoparticles have been deposited on inert porous silica supports with high specific surface area. These materials have potential applications in paint and textile industry as the titania particles selectively deposited on the inner surface of the silica supports act as a photocatalyst. The inert external surface is necessary to avoid photodegradation of the textile material or the paint components. The photocatalytic activity of the catalysts has been evaluated with two catalytic setups. One setup in aqueous phase, for the degradation of dyes such as rhodamine-6G, is commonly used. The second setup is a continuous flow gaseous phase setup which was used for the mineralization of ethanol as a representative volatile organic compound (VOC). The influence of the porosity and the morphology of the silica supports on the photocatalytic activity are discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 9.446
Times cited: 24
DOI: 10.1016/j.apcatb.2008.03.015
|
“Origin of different deactivation of Pd/SnO2 and Pd/GeO2 catalysts in methanol dehydrogenation and reforming: a comparative study”. Lorenz H, Zhao Q, Turner S, Lebedev OI, Van Tendeloo G, Kloetzer B, Rameshan C, Pfaller K, Applied catalysis : A : general 381, 242 (2010). http://doi.org/10.1016/j.apcata.2010.04.015
Abstract: Pd particles supported on SnO2 and GeO2 have been structurally investigated by X-ray diffraction, (High-Resolution) transmission and scanning electron microscopy after different reductive treatments to monitor the eventual formation of bimetallic phases and catalytically tested in methanol dehydrogenation/ reforming. For both oxides this included a thin film sample with well-defined Pd particles and a powder catalyst prepared by incipient wetness impregnation. The hexagonal and the tetragonal polymorph were studied for powder GeO2. Pd2Ge formation was observed on all GeO2-supported catalysts, strongly depending on the specific sample used. Reduction of the thin film at 573K resulted in full transformation into the bimetallic state. The partial solubility of hexagonal GeO2 in water and its thermal structural instability yielded Pd2Ge formation at 473 K, at the cost of a structurally inhomogeneous support and Ge metal formation at higher reduction temperatures. Pd on tetragonal GeO2 entered a state of strong metalsupport interaction after reduction at 573673 K, resulting in coalescing Pd2Ge particles on a sintered and re-crystallized support, apparently partially covering the bimetallic particles and decreasing the catalytic activity. Pd2Ge on amorphous thin film and hexagonal GeO2 converted methanol primarily via dehydrogenation to CO and H2. At 573 K, formation of Pd2Sn and also PdSn occurred on the Pd/SnO2 thin film. Pd3Sn2 (and to some extent Pd2Sn) were predominantly obtained on the respective powder catalyst. Strong deactivation with increasing reduction temperature was observed, likely not based on the classical strong metalsupport interaction effect, but rather on a combination of missing active structural ensembles on Sn-enriched bimetallic phases and the formation of metallic -Sn. Correlations to Pd and its bimetallics supported on ZnO, Ga2O3 and In2O3 were also discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.339
Times cited: 14
DOI: 10.1016/j.apcata.2010.04.015
|
“Preparation of sulfonated ordered mesoporous carbon and its use for the esterification of fatty acids”. Peng L, Philippaerts A, Ke X, van Noyen J, de Cleppel F, Van Tendeloo G, Jacobs PA, Sels BF, Catalysis today 150, 140 (2010). http://doi.org/10.1016/j.cattod.2009.07.066
Abstract: Mesoporous carbon, which can be replicated from mesoporous silica and whose surface is hydrophobic, can be an ideal catalyst for the esterification of fatty acids. Here we report an easy and low cost way to prepare sulfonic acid group-functionalized mesoporous carbon. A sample of calcined mesoporous silica SBA-15 was added to an aqueous sucrose solution followed by drying and calcination at different temperatures. In contrast to existing procedures, the obtained hybrid Si/C material was then first sulfonated in H2SO4, before the final removal of the silica template in order to stabilize the porous structure towards the liquid phase sulfonation treatment. Thus the silicacarbon composites, instead of the mesoporous carbon, were successfully sulfonated to introduce SO3H groups, while keeping the ordered mesoporous structure intact. The influence of carbonization temperature was investigated, suggesting an optimum temperature of 873 K. The SO3H group-functionalized mesoporous carbon, denoted as CMK-3-873-SO3H, was characterized by means of XRD, N2 physisorption, SEM, FT-IR, elemental analysis and TEM. It followed that a uniform mesoporous carbon was obtained with an average pore size of 3.89 nm, a specific surface of 807 m2/g and a SO3H group loading of 0.39 meq/g of dry material. Compared with other solid acid catalysts, the resulting material shows enhanced activity in the acid-catalyzed esterification of oleic acid with methanol, and can be used repeatedly. The increased catalytic performance is attributed to the hydrophobic surface and larger pore size of the new catalyst. It can effectively accommodate long chain fatty acids and reject formed water, making the active sites easily accessible.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.636
Times cited: 132
DOI: 10.1016/j.cattod.2009.07.066
|
“Pd-In2O3 interaction due to reduction in hydrogen: consequences for methanol steam reforming”. Lorenz H, Turner S, Lebedev OI, Van Tendeloo G, Klötzer B, Rameshan C, Pfaller K, Penner S, Applied catalysis : A : general 374, 180 (2010). http://doi.org/10.1016/j.apcata.2009.12.007
Abstract: Two different Pd/In2O3 samples including a thin film model catalyst with well-defined Pd particles grown on NaCl(0 0 1) supports and a powder catalyst prepared by an impregnation technique are examined by electron microscopy, X-ray diffraction and catalytic measurements in methanol steam reforming in order to correlate the formation of different oxide-supported bimetallic PdIn phases with catalytic activity and selectivity. A PdIn shell around the Pd particles is observed on the thin film catalyst after embedding the Pd particles in In2O3 at 300 K, likely because alloying to PdIn and oxidation to In2O3 are competing processes. Increased PdIn bimetallic formation is observed up to 573 K reduction temperature until at 623 K the film stability limit in hydrogen is reached. Oxidative treatments at 573 K lead to decomposition of PdIn and to the formation of an In2O3 shell covering the Pd particles, which irreversibly changes the activity and selectivity pattern to clean In2O3. PdIn and Pd2In3 phases are obtained on the powder catalyst after reduction at 573 K and 673 K, respectively. Only CO2-selective methanol steam reforming is observed in the reduction temperature range between 473 K and 573 K. After reduction at 673 K encapsulation of the bimetallic particles by crystalline In2O3 suppresses CO2 formation and only activity and selectivity of clean In2O3 are measured.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.339
Times cited: 55
DOI: 10.1016/j.apcata.2009.12.007
|
“Two phase intergrowth in Bi2Sr2Ca0.6Y0.4Cu2Oy single crystals”. Zhang XF, Van Tendeloo G, Ge SL, Emmen JHPM, Brabers VAM, Physica: C : superconductivity 215, 39 (1993). http://doi.org/10.1016/0921-4534(93)90362-T
Abstract: In Bi2Sr2Ca0.6Y0.4Cu2Oy single crystals we have identified the intergrowth of two phases; a normal Bi2Sr2CaCu2Oy type phase with a 4.6b modulation period and a secondary,phase with a 9.4b modulation period. Both the two phases have orthorhombic basic structures with similar lattice parameters but different symmetries, i.e. Bbmb for the normal phase and Ccca for the secondary phase. The c-parameters of these two phases are found to vary independently upon changing the nominal Y content. The modulation characteristics of the secondary phase implies a close structural relation between the two phases. Both phases are discussed from a structural and a compositional point of view.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.942
Times cited: 17
DOI: 10.1016/0921-4534(93)90362-T
|
“P-type ZnO thin films grown by RF plasma beam assisted Pulsed Laser Deposition”. Epurescu G, Dinescu G, Moldovan A, Birjega R, Dipietrantonio F, Verona E, Verardi P, Nistor LC, Ghica C, Van Tendeloo G, Dinescu A, Superlattices and microstructures 42, 79 (2007). http://doi.org/10.1016/j.spmi.2007.04.072
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.123
Times cited: 19
DOI: 10.1016/j.spmi.2007.04.072
|