“Use of nanoscale carbon layers on Ag-based gas diffusion electrodes to promote CO production”. Pacquets L, Van den Hoek J, Arenas Esteban D, Ciocarlan R-G, Cool P, Baert K, Hauffman T, Daems N, Bals S, Breugelmans T, ACS applied nano materials 5, 7723 (2022). http://doi.org/10.1021/ACSANM.2C00473
Abstract: A promising strategy for the inhibition of the hydrogen evolution reaction along with the stabilization of the electrocatalyst in electrochemical CO2 reduction cells involves the application of a nanoscale amorphous carbon layer on top of the active catalyst layer in a gas diffusion electrode. Without modifying the chemical nature of the electrocatalyst itself, these amorphous carbon layers lead to the stabilization of the electrocatalyst, and a significant improvement with respect to the inhibition of the hydrogen evolution reaction was also obtained. The faradaic efficiencies of hydrogen could be reduced from 31.4 to 2.1% after 1 h of electrolysis with a 5 nm thick carbon layer. Furthermore, the impact of the carbon layer thickness (5–30 nm) on this inhibiting effect was investigated. We determined an optimal thickness of 15 nm where the hydrogen evolution reaction was inhibited and a decent stability was obtained. Next, a thickness of 15 nm was selected for durability measurements. Interestingly, these durability measurements revealed the beneficial impact of the carbon layer already after 6 h by suppressing the hydrogen evolution such that an increase of only 37.9% exists compared to 56.9% without the use of an additional carbon layer, which is an improvement of 150%. Since carbon is only applied afterward, it reveals its great potential in terms of electrocatalysis in general.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 5.9
Times cited: 3
DOI: 10.1021/ACSANM.2C00473
|
|
|
“Achieving High Moisture Tolerance in Pseudohalide Perovskite Nanocrystals for Light-Emitting Diode Application”. Bhatia H, Keshavarz M, Martin C, Van Gaal L, Zhang Y, de Coen B, Schrenker NJ, Valli D, Ottesen M, Bremholm M, Van de Vondel J, Bals S, Hofkens J, Debroye E, ACS Applied Optical Materials 1, 1184 (2023). http://doi.org/10.1021/acsaom.3c00096
Abstract: The addition of potassium thiocyanate (KSCN) to the FAPbBr3 structure and subsequent post-treatment of nanocrystals (NCs) lead to high quantum confinement, resulting in a photoluminescent quantum yield (PLQY) approaching unity and microsecond decay times. This synergistic approach demonstrated exceptional stability under humid conditions, retaining 70% of the PLQY for over a month, while the untreated NCs degrade within 24 h. Additionally, the devices incorporating the post-treated NCs displayed 1.5% external quantum efficiency (EQE), a 5-fold improvement over untreated devices. These results provide promising opportunities for the use of perovskites in moisture-stable optoelectronics.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
DOI: 10.1021/acsaom.3c00096
|
|
|
“Improving stability of CO₂, electroreduction by incorporating Ag NPs in N-doped ordered mesoporous carbon structures”. Van den Hoek J, Daems N, Arnouts S, Hoekx S, Bals S, Breugelmans T, ACS applied materials and interfaces 16, 6931 (2024). http://doi.org/10.1021/ACSAMI.3C12261
Abstract: The electroreduction of carbon dioxide (eCO2RR) to CO using Ag nanoparticles as an electrocatalyst is promising as an industrial carbon capture and utilization (CCU) technique to mitigate CO2 emissions. Nevertheless, the long-term stability of these Ag nanoparticles has been insufficient despite initial high Faradaic efficiencies and/or partial current densities. To improve the stability, we evaluated an up-scalable and easily tunable synthesis route to deposit low-weight percentages of Ag nanoparticles (NPs) on and into the framework of a nitrogen-doped ordered mesoporous carbon (NOMC) structure. By exploiting this so-called nanoparticle confinement strategy, the nanoparticle mobility under operation is strongly reduced. As a result, particle detachment and agglomeration, two of the most pronounced electrocatalytic degradation mechanisms, are (partially) blocked and catalyst durability is improved. Several synthesis parameters, such as the anchoring agent, the weight percentage of Ag NPs, and the type of carbonaceous support material, were modified in a controlled manner to evaluate their respective impact on the overall electrochemical performance, with a strong emphasis on operational stability. The resulting powders were evaluated through electrochemical and physicochemical characterization methods, including X-ray diffraction (XRD), N2-physisorption, Inductively coupled plasma mass spectrometry (ICP-MS), scanning electron microscopy (SEM), SEM-energy-dispersive X-ray spectroscopy (SEM-EDS), high-angle annular dark field scanning transmission electron microscopy (HAADF-STEM), STEM-EDS, electron tomography, and X-ray photoelectron spectroscopy (XPS). The optimized Ag/soft-NOMC catalysts showed both a promising selectivity (∼80%) and stability compared with commercial Ag NPs while decreasing the loading of the transition metal by more than 50%. The stability of both the 5 and 10 wt % Ag/soft-NOMC catalysts showed considerable improvements by anchoring the Ag NPs on and into a NOMC framework, resulting in a 267% improvement in CO selectivity after 72 h (despite initial losses) compared to commercial Ag NPs. These results demonstrate the promising strategy of anchoring Ag NPs to improve the CO selectivity during prolonged experiments due to the reduced mobility of the Ag NPs and thus enhanced stability.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 9.5
DOI: 10.1021/ACSAMI.3C12261
|
|
|
“Defect-directed growth of symmetrically branched metal nanocrystals”. Smith JD, Bladt E, Burkhart JAC, Winckelmans N, Koczkur KM, Ashberry HM, Bals S, Skrabalak SE, Angewandte Chemie-International Edition 59, 943 (2020). http://doi.org/10.1002/ANIE.201913301
Abstract: Branched plasmonic nanocrystals (NCs) have attracted much attention due to electric field enhancements at their tips. Seeded growth provides routes to NCs with defined branching patterns and, in turn, near-field distributions with defined symmetries. Here, a systematic analysis was undertaken in which seeds containing different distributions of planar defects were used to grow branched NCs in order to understand how their distributions direct the branching. Characterization of the products by multimode electron tomography and analysis of the NC morphologies at different overgrowth stages indicate that the branching patterns are directed by the seed defects, with the emergence of branches from the seed faces consistent with minimizing volumetric strain energy at the expense of surface energy. These results contrast with growth of branched NCs from single-crystalline seeds and provide a new platform for the synthesis of symmetrically branched plasmonic NCs.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 16.6
Times cited: 23
DOI: 10.1002/ANIE.201913301
|
|
|
“A titanium(IV)-based metal-organic framework featuring defect-rich Ti-O sheets as an oxidative desulfurization catalyst”. Smolders S, Willhammar T, Krajnc A, Şentosun K, Wharmby MT, Lomachenko KA, Bals S, Mali G, Roeffaers MBJ, De Vos DE, Bueken B, Angewandte Chemie: international edition in English 58, 9160 (2019). http://doi.org/10.1002/ANIE.201904347
Abstract: While titanium-based metal-organic frameworks (MOFs) have been widely studied for their (photo) catalytic potential, only a few Ti-IV MOFs have been reported owing to the high reactivity of the employed titanium precursors. The synthesis of COK-47 is now presented, the first Ti carboxylate MOF based on sheets of (TiO6)-O-IV octahedra, which can be synthesized with a range of different linkers. COK-47 can be synthesized as an inherently defective nanoparticulate material, rendering it a highly efficient catalyst for the oxidation of thiophenes. Its structure was determined by continuous rotation electron diffraction and studied in depth by X-ray total scattering, EXAFS, and solid-state NMR. Furthermore, its photoactivity was investigated by electron paramagnetic resonance and demonstrated by catalytic photodegradation of rhodamine 6G.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 11.994
Times cited: 97
DOI: 10.1002/ANIE.201904347
|
|
|
“Reversible Clustering of Gold Nanoparticles under Confinement”. Sánchez-Iglesias A, Claes N, Solís DM, Taboada JM, Bals S, Liz-Marzán LM, Grzelczak M, Angewandte Chemie: international edition in English 57, 3183 (2018). http://doi.org/10.1002/anie.201800736
Abstract: A limiting factor of solvent-induced nanoparticle self-assembly is the need for constant sample dilution in assembly/disassembly cycles. Changes in the nanoparticle concentration alter the kinetics of the subsequent assembly process, limiting optical signal recovery. Herein, we show that upon confining hydrophobic nanoparticles in permeable silica nanocapsules, the number of nanoparticles participating in cyclic aggregation remains constant despite bulk changes in solution, leading to highly reproducible plasmon band shifts at different solvent compositions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 11.994
Times cited: 53
DOI: 10.1002/anie.201800736
|
|
|
“Chemical cutting of perovskite nanowires into single-photon emissive low-aspect-ratio CsPbX3(X = Cl, Br, I) nanorods”. Tong Y, Fu M, Bladt E, Huang H, Richter AF, Wang K, Mueller-Buschbaum P, Bals S, Tamarat P, Lounis B, Feldmann J, Polavarapu L, Angewandte Chemie: international edition in English 57, 16094 (2018). http://doi.org/10.1002/ANIE.201810110
Abstract: Post-synthetic shape-transformation processes provide access to colloidal nanocrystal morphologies that are unattainable by direct synthetic routes. Herein, we report our finding about the ligand-induced fragmentation of CsPbBr3 perovskite nanowires (NWs) into low aspect-ratio CsPbX3 (X = Cl, Br and I) nanorods (NRs) during halide ion exchange reaction with PbX2-ligand solution. The shape transformation of NWs-to-NRs resulted in an increase of photoluminescence efficiency owing to a decrease of nonradiative decay rates. Importantly, we found that the perovskite NRs exhibit single photon emission as revealed by photon antibunching measurements, while it is not detected in parent NWs. This work not only reports on the quantum light emission of low aspect ratio perovskite NRs, but also expands our current understanding of shape-dependent optical properties of perovskite nanocrystals.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 11.994
Times cited: 70
DOI: 10.1002/ANIE.201810110
|
|
|
“Deactivation of Sn-Beta during carbohydrate conversion”. van der Graaf WNP, Tempelman CHL, Hendriks FC, Ruiz-Martinez J, Bals S, Weckhuysen BM, Pidko EA, Hensen EJM, Applied catalysis : A : general 564, 113 (2018). http://doi.org/10.1016/J.APCATA.2018.07.023
Abstract: The deactivation of Sn-Beta zeolite catalyst during retro-aldolization and isomerization of glucose is investigated. Confocal fluorescence microscopy reveals that retro-aldolization of glucose in CH3OH at 160 degrees C is accompanied with the build-up of insoluble oligomeric deposits in the micropores, resulting in a rapid catalyst deactivation. These deposits accumulate predominantly in the outer regions of the zeolite crystals, which points to mass transport limitations. Glucose isomerization in water is not only accompanied by the formation of insoluble deposits in the micropores, but also by the structural degradation of the zeolite due to desilication and destannation. Enhanced and sustained catalytic performance can be achieved by using ethanol/water mixtures as the reaction solvent instead of water.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.339
Times cited: 25
DOI: 10.1016/J.APCATA.2018.07.023
|
|
|
“The role of MOFs in Thin-Film Nanocomposite (TFN) membranes”. Van Goethem C, Verbeke R, Pfanmoeller M, Koschine T, Dickmann M, Timpel-Lindner T, Egger W, Bals S, Vankelecom IFJ, Journal of membrane science 563, 938 (2018). http://doi.org/10.1016/J.MEMSCI.2018.06.040
Abstract: Incorporation of MOFs in interfacially polymerized Thin-Film Nanocomposite (TFN) membranes has widely been shown to result in increased membrane performance. However, the exact functioning of these membranes is poorly understood as large variability in permeance increase, filler incorporation and rejection changes can be observed in literature. The synthesis and functioning of TFN membranes (herein exemplified by ZIF-8 filled polyamide (PA) membranes prepared via the EFP method) was investigated via targeted membrane synthesis and thorough characterization via STEM-EDX, XRD and PALS. It is hypothesized that the acid generated during the interfacial polymerization (IP) at least partially degrades the crystalline, acid-sensitive ZIF-8 and that this influences the membrane formation (through so-called secondary effects, i.e. not strictly linked to the pore morphology of the MOF). Nanoscale HAADF-STEM imaging and STEM-EDX Zn-mapping revealed no ZIF-8 particles but rather the presence of randomly shaped regions with elevated Zn-content. Also XRD failed to show the presence of crystalline areas in the composite PA films. As the addition of the acid-quenching TEA led to an increase in the diffraction signal observed in XRD, the role of the acid was confirmed. The separate addition of dissolved Zn2+ to the synthesis of regular TFC membranes showed an increase in permeance while losing some salt retention, similar to observations regularly made for TFN membranes. While the addition of a porous material to a TFC membrane is a straightforward concept, all obtained results indicate that the synthesis and performance of such composite membranes is often more complex than commonly accepted.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.035
Times cited: 84
DOI: 10.1016/J.MEMSCI.2018.06.040
|
|
|
“From precursor powders to CsPbX3 perovskite nanowires : one-pot synthesis, growth mechanism, and oriented self-assembly”. Tong Y, Bohn BJ, Bladt E, Wang K, Mueller-Buschbaum P, Bals S, Urban AS, Polavarapu L, Feldmann J, Angewandte Chemie: international edition in English 56, 13887 (2017). http://doi.org/10.1002/ANIE.201707224
Abstract: <script type='text/javascript'>document.write(unpmarked('The colloidal synthesis and assembly of semiconductor nanowires continues to attract a great deal of interest. Herein, we describe the single-step ligand-mediated synthesis of single-crystalline CsPbBr3 perovskite nanowires (NWs) directly from the precursor powders. Studies of the reaction process and the morphological evolution revealed that the initially formed CsPbBr3 nanocubes are transformed into NWs through an oriented-attachment mechanism. The optical properties of the NWs can be tuned across the entire visible range by varying the halide (Cl, Br, and I) composition through subsequent halide ion exchange. Single-particle studies showed that these NWs exhibit strongly polarized emission with a polarization anisotropy of 0.36. More importantly, the NWs can self-assemble in a quasi-oriented fashion at an air/liquid interface. This process should also be easily applicable to perovskite nanocrystals of different morphologies for their integration into nanoscale optoelectronic devices.'));
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 11.994
Times cited: 223
DOI: 10.1002/ANIE.201707224
|
|
|
“Highly Luminescent Cesium Lead Halide Perovskite Nanocrystals with Tunable Composition and Thickness by Ultrasonication”. Tong Y, Bladt E, Aygüler MF, Manzi A, Milowska KZ, Hintermayr VA, Docampo P, Bals S, Urban AS, Polavarapu L, Feldmann J, Angewandte Chemie: international edition in English 55, 13887 (2016). http://doi.org/10.1002/anie.201605909
Abstract: We describe the simple, scalable, single-step, and polar-solvent-free synthesis of high-quality colloidal CsPbX3 (X=Cl, Br, and I) perovskite nanocrystals (NCs) with tunable halide ion composition and thickness by direct ultrasonication of the corresponding precursor solutions in the presence of organic capping molecules. High angle annular dark field scanning transmission electron microscopy (HAADF-STEM) revealed the cubic crystal structure and surface termination of the NCs with atomic resolution. The NCs exhibit high photoluminescence quantum yields, narrow emission line widths, and considerable air stability. Furthermore, we investigated the quantum size effects in CsPbBr3 and CsPbI3 nanoplatelets by tuning their thickness down to only three to six monolayers. The high quality of the prepared NCs (CsPbBr3) was confirmed by amplified spontaneous emission with low thresholds. The versatility of this synthesis approach was demonstrated by synthesizing different perovskite NCs.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 11.994
Times cited: 549
DOI: 10.1002/anie.201605909
|
|
|
“Disentangling the effect of seed size and crystal habit on gold nanoparticle seeded growth”. González-Rubio G, de Oliveira TM, Altantzis T, La Porta A, Guerrero-Martínez A, Bals S, Scarabelli L, Liz-Marzán LM, Chemical communications 53, 11360 (2017). http://doi.org/10.1039/C7CC06854A
Abstract: Oxidative etching was used to produce gold seeds of different sizes and crystal habits. Following detailed characterization, the seeds were grown under different conditions. Our results bring new insights toward understanding the effect of size and crystallinity on the growth of anisotropic particles, whilst identifying guidelines for the optimisation of new synthetic protocols of predesigned seeds.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 29
DOI: 10.1039/C7CC06854A
|
|
|
“Janus Gold Nanoparticles Obtained via Spontaneous Binary Polymer Shell Segregation”. Percebom AMM, Giner-casares JJ, Claes N, Bals S, Loh W, Liz-Marzan LM, Chemical communications 52, 4278 (2016). http://doi.org/10.1039/C5CC10454H
Abstract: Janus gold nanoparticles are of high interest because they allow directed self-assembly and display plasmonic properties. We succeeded in coating gold nanoparticles with two different polymers that form a Janus shell. The spontaneous segregation of two immiscible polymers at the surface of the nanoparticles was verified by NOESY NMR and most importantly by electron microscopy analysis in two and three dimensions. The Janus structure is additionally shown to affect the aggregation behavior of the nanoparticles.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 44
DOI: 10.1039/C5CC10454H
|
|
|
“Heat-induced transformation of CdSe-CdS-ZnS coremultishell quantum dots by Zn diffusion into inner layers”. Yalcin AO, Goris B, van Dijk-Moes RJA, Fan Z, Erdamar AK, Tichelaar FD, Vlugt TJH, Van Tendeloo G, Bals S, Vanmaekelbergh D, Zandbergen HW, van Huis MA;, Chemical communications 51, 3320 (2015). http://doi.org/10.1039/C4CC08647C
Abstract: In this work, we investigate the thermal evolution of CdSeCdSZnS coremultishell quantum dots (QDs) in situ using transmission electron microscopy (TEM). Starting at a temperature of approximately 250 °C, Zn diffusion into inner layers takes place together with simultaneous evaporation of particularly Cd and S. As a result of this transformation, CdxZn1−xSeCdyZn1−yS coreshell QDs are obtained.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 21
DOI: 10.1039/C4CC08647C
|
|
|
“Direct operando visualization of metal support interactions induced by hydrogen spillover during CO₂, hydrogenation”. Jenkinson K, Spadaro MC, Golovanova V, Andreu T, Morante JR, Arbiol J, Bals S, Advanced materials 35, 2306447 (2023). http://doi.org/10.1002/ADMA.202306447
Abstract: The understanding of catalyst active sites is a fundamental challenge for the future rational design of optimized and bespoke catalysts. For instance, the partial reduction of Ce4+ surface sites to Ce3+ and the formation of oxygen vacancies are critical for CO2 hydrogenation, CO oxidation, and the water gas shift reaction. Furthermore, metal nanoparticles, the reducible support, and metal support interactions are prone to evolve under reaction conditions; therefore a catalyst structure must be characterized under operando conditions to identify active states and deduce structure-activity relationships. In the present work, temperature-induced morphological and chemical changes in Ni nanoparticle-decorated mesoporous CeO2 by means of in situ quantitative multimode electron tomography and in situ heating electron energy loss spectroscopy, respectively, are investigated. Moreover, operando electron energy loss spectroscopy is employed using a windowed gas cell and reveals the role of Ni-induced hydrogen spillover on active Ce3+ site formation and enhancement of the overall catalytic performance.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 29.4
DOI: 10.1002/ADMA.202306447
|
|
|
“CoFe nanodumbbells : synthesis, structure, and magnetic properties”. Liakakos N, Gatel C, Blon T, Altantzis T, Lentijo-Mozo S, Garcia-Marcelot C, Lacroix LM, Respaud M, Bals S, Van Tendeloo G, Soulantica K, Nano letters 14, 2747 (2014). http://doi.org/10.1021/nl500734k
Abstract: We report the solution phase synthesis, the structural analysis, and the magnetic properties of hybrid nanostructures combining two magnetic metals. These nano-objects are characterized by a remarkable shape, combining Fe nanocubes on Co nanorods. The topological composition, the orientation relationship, and the growth steps have been studied by advanced electron microscopy techniques, such as HRTEM, electron tomography, and state-of-the-art 3-dimensional elemental mapping by EDX tomography. The soft iron nanocubes behave as easy nucleation centers that induce the magnetization reversal of the entire nanohybrid, leading to a drastic modification of the overall effective magnetic anisotropy.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.712
Times cited: 27
DOI: 10.1021/nl500734k
|
|
|
“Conceptual frame rationalizing the self-stabilization of H-USY zeolites in hot liquid water”. Ennaert T, Geboers J, Gobechiya E, Courtin CM, Kurttepeli M, Houthoofd K, Kirschhock CEA, Magusin PCMM, Bals S, Jacobs PA, Sels BF, ACS catalysis 5, 754 (2015). http://doi.org/10.1021/cs501559s
Abstract: The wide range of liquid-phase reactions required for the catalytic conversion of biomass compounds into new bioplatform molecules defines a new set of challenges for the development of active, selective, and stable catalysts. The potential of bifunctional Ru/H-USY catalysts for conversions in hot liquid water (HLW) is assessed in terms of physicochemical stability and long-term catalytic performance of acid sites and noble metal functionality, as probed by hydrolytic hydrogenation of cellulose. It is shown that zeolite desilication is the main zeolite degradation mechanism in HLW. USY zeolite stability depends on two main parameters, viz., framework and extra-framework aluminum content. The former protects the zeolite lattice by counteracting hydrolysis of framework bonds, and the latter, when located at the external crystal surface, prevents solubilization of the zeolite framework which is the result of its low water-solubility. Hence, the hot liquid water stability of commercial H-USY zeolites, in contrast to their steam stability, increased with decreasing Si/AI ratio. As a result, mildly steamed USY zeolites containing a high amount of both Al species exhibit the highest resistance to HLW. During an initial period of transformations, Al-rich zeolites form additional protective extra-framework Al species at the outer surface, self-stabilizing the framework. A critical bulk Si/AI ratio of 3 was determined whereby USY zeolites with a lower Si/AI ratio will self-stabilize over time. Besides, due to the initial transformation period, the accessibility of the catalytic active sites is extensively enhanced resulting in a material that is more stable and drastically more accessible to large substrates than the original zeolite. When these findings are applied in the hydrolytic hydrogenation of cellulose, unprecedented nearly quantitative hexitol yields were obtained with a stable catalytic system.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 10.614
Times cited: 65
DOI: 10.1021/cs501559s
|
|
|
“End-to-end assembly of shape-controlled nanocrystals via a nanowelding approach mediated by gold domains”. Figuerola A, Franchini IR, Fiore A, Mastria R, Falqui A, Bertoni G, Bals S, Van Tendeloo G, Kudera S, Cingolani R, Manna L, Advanced materials 21, 550 (2009). http://doi.org/10.1002/adma.200801928
Abstract: Welding nanocrystals for assembly: The welding of Au domains grown on the tips of shape-controlled cadmium chalcogenide colloidal nanocrystals is used as a strategy for their assembly. Iodine-induced coagulation of selectively grown Au domains leads to assemblies such as flowerlike structures based on bullet-shaped nanocrystals, linear and cross-linked chains of nanorods, and globular networks with tetrapods as building blocks.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 19.791
Times cited: 110
DOI: 10.1002/adma.200801928
|
|
|
“Hydride destabilization in core-shell nanoparticles”. Pasquini L, Sacchi M, Brighi M, Boelsma C, Bals S, Perkisas T, Dam B, International journal of hydrogen energy 39, 2115 (2014). http://doi.org/10.1016/j.ijhydene.2013.11.085
Abstract: We present a model that describes the effect of elastic constraint on the thermodynamics of hydrogen absorption and desorption in biphasic core-shell nanoparticles, where the core is a hydride forming metal. In particular, the change of the hydride formation enthalpy and of the equilibrium pressure for the metal/hydride transformation are described as a function of nanoparticles radius, shell thickness, and elastic properties of both core and shell. To test the model, the hydrogen sorption isotherms of Mg-MgO core-shell nanoparticles, synthesized by inert gas condensation, were measured by means of optical hydrogenography. The model's predictions are in good agreement with the experimentally determined plateau pressure of hydrogen absorption. The features that a core-shell systems should exhibit in view of practical hydrogen storage applications are discussed with reference to the model and the experimental results. Copyright (C) 2013, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.582
Times cited: 32
DOI: 10.1016/j.ijhydene.2013.11.085
|
|
|
“New insights into the mesophase transformation of ethane-bridged PMOs by the influence of different counterions under basic conditions”. Lin F, Meng, Kukueva E, Mertens M, Van Doorslaer S, Bals S, Cool P, RSC advances 5, 5553 (2015). http://doi.org/10.1039/c4ra15849k
Abstract: The counterions are of crucial importance in determining the mesostructure and morphology of ethanebridged PMO materials synthesized under basic conditions. By using CTABr as the surfactant, the final PMO materials show a 2-D hexagonal (p6mm) mesophase, while PMO materials with cubic (Pm (3) over barn ) mesostructure are obtained when CTACl or CTA(SO4)(1)/(2) are used. With gradually replacing CTABr by CTACl or CTA(SO4) (1)/(2) while keeping the total surfactant concentration constant, a clear p6mm to Pm (3) over barn 3n mesophase evolution process is observed. For a given gel composition, the mesophase of ethanebridged PMO materials can also be adjusted by the addition of different sodium salts. In short, the effect of the counterions on the mesophase can be attributed to the binding strength of the ions on the surfactant micelles, which follows the Hofmeister series (SO42- < Cl- < Br-< NO3- < SCN-). Furthermore, it is found that the hydrolysis and condensation rate of the organosilica precursor also plays an important role in the formation of the final mesostructure
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.108
Times cited: 6
DOI: 10.1039/c4ra15849k
|
|
|
“A practical method to determine the effective resolution in incoherent experimental electron tomography”. Heidari Mezerji H, van den Broek W, Bals S, Ultramicroscopy 111, 330 (2011). http://doi.org/10.1016/j.ultramic.2011.01.021
Abstract: It is not straightforward to determine resolution for a 3D reconstruction when performing an electron tomography experiment. Different contributions such as missing wedge and misalignment add up and often influence the final resolution in an anisotropic manner. The conventional resolution measures can not be used for all of the reconstruction techniques, especially for iterative techniques which are more commonly used for electron tomography in materials science. Here we define a quantitative resolution measure that determines the resolution in three orthogonal directions of the reconstruction. As an application we use this measure to determine the optimum number of simultaneous iterative reconstruction technique (SIRT) iterations to reconstruct the gold nanoparticles, based on a high angle annular dark field STEM (HAADF-STEM) tilt series.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
Times cited: 26
DOI: 10.1016/j.ultramic.2011.01.021
|
|
|
“Shelf life degradation of bulk heterojunction solar cells : intrinsic evolution of charge transfer complex”. Guerrero A, Heidari H, Ripolles TS, Kovalenko A, Pfannmöller M, Bals S, Kauffmann L-D, Bisquert J, Garcia-Belmonte G, Laser physics review 5, 1401997 (2015). http://doi.org/10.1002/aenm.201401997
Abstract: Achievement of long-term stability of organic photovoltaics is currently one of the major topics for this technology to reach maturity. Most of the techniques used to reveal degradation pathways are destructive and/or do not allow for real-time measurements in operating devices. Here, three different, nondestructive techniques able to provide real-time information, namely, film absorbance, capacitance-voltage (C-V), and impedance spectroscopy (IS), are combined over a period of 1 year using non-accelerated intrinsic degradation conditions. It is discerned between chemical modifications in the active layer, physical processes taking place in the bulk of the blend from those at the active layer/contact interfaces. In particular, it is observed that during the ageing experiment, the main source for device performance degradation is the formation of donor-acceptor charge-transfer complex (P3HT(center dot+)-PCBM center dot-) that acts as an exciton quencher. Generation of these radical species diminishes photocurrent and reduces open-circuit voltage by the creation of electronic defect states. Conclusions extracted from absorption, C-V, and IS measurements will be further supported by a range of other techniques such as atomic force microscopy, X-ray diffraction, and dark-field imaging of scanning transmission electron microscopy on ultrathin cross-sections.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 16.721
Times cited: 30
DOI: 10.1002/aenm.201401997
|
|
|
“Transport, magnetic, and structural properties of La0.7Ce0.3MnO3 thin films: evidence for hole-doping”. Werner R, Raisch C, Leca V, Ion V, Bals S, Van Tendeloo G, Chasse T, Kleiner R, Koelle D, Physical review : B : solid state 79, 054416 (2009). http://doi.org/10.1103/PhysRevB.79.054416
Abstract: Cerium-doped manganite thin films were grown epitaxially by pulsed laser deposition at 720 °C and oxygen pressure pO2=125 Pa and were subjected to different annealing steps. According to x-ray diffraction (XRD) data, the formation of CeO2 as a secondary phase could be avoided for pO28 Pa. However, transmission electron microscopy shows the presence of CeO2 nanoclusters even in those films which appear to be single phase in XRD. With O2 annealing, the metal-to-insulator transition temperature increases, while the saturation magnetization decreases and stays well below the theoretical value for electron-doped La0.7Ce0.3MnO3 with mixed Mn3+/Mn2+ valences. The same trend is observed with decreasing film thickness from 100 to 20 nm, indicating a higher oxygen content for thinner films. Hall measurements on a film which shows a metal-to-insulator transition clearly reveal holes as dominating charge carriers. Combining data from x-ray photoemission spectroscopy, for determination of the oxygen content, and x-ray absorption spectroscopy (XAS), for determination of the hole concentration and cation valences, we find that with increasing oxygen content the hole concentration increases and Mn valences are shifted from 2+ to 4+. The dominating Mn valences in the films are Mn3+ and Mn4+, and only a small amount of Mn2+ ions can be observed by XAS. Mn2+ and Ce4+ XAS signals obtained in surface-sensitive total electron yield mode are strongly reduced in the bulk-sensitive fluorescence mode, which indicates hole-doping in the bulk for those films which do show a metal-to-insulator transition.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 25
DOI: 10.1103/PhysRevB.79.054416
|
|
|
“Direct synthesis of antimicrobial coatings based on tailored bi-elemental nanoparticles”. Benetti G, Cavaliere E, Canteri A, Landini G, Rossolini GM, Pallecchi L, Chiodi M, Van Bael MJ, Winckelmans N, Bals S, Gavioli L, APL materials 5, 036105 (2017). http://doi.org/10.1063/1.4978772
Abstract: Ultrathin coatings based on bi-elemental nanoparticles (NPs) are very promising to limit the surface-related spread of bacterial pathogens, particularly in nosocomial environments. However, tailoring the synthesis, composition, adhesion to substrate, and antimicrobial spectrum of the coating is an open challenge. Herein, we report on a radically new nanostructured coating, obtained by a one-step gas-phase deposition technique, and composed of bi-elemental Janus type Ag/Ti NPs. The NPs are characterized by a cluster-in-cluster mixing phase with metallic Ag nano-crystals embedded in amorphous TiO2 and present a promising antimicrobial activity including also multidrug resistant strains. We demonstrate the flexibility of the method to tune the embedded Ag nano-crystals dimension, the total relative composition of the coating, and the substrate type, opening the possibility of tailoring the dimension, composition, antimicrobial spectrum, and other physical/chemical properties of such multi-elemental systems. This work is expected to significantly spread the range of applications of NPs coatings, not only as an effective tool in the prevention of healthcare-associated infections but also in other technologically relevant fields like sensors or nano-/micro joining.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.335
Times cited: 21
DOI: 10.1063/1.4978772
|
|
|
“3D porous nanostructured platinum prepared using atomic layer deposition”. Pulinthanathu Sree S, Dendooven J, Geerts L, Ramachandran RK, Javon E, Ceyssens F, Breynaert E, Kirschhock CEA, Puers R, Altantzis T, Van Tendeloo G, Bals S, Detavernier C, Martens JA, Journal of materials chemistry A : materials for energy and sustainability 5, 19007 (2017). http://doi.org/10.1039/C7TA03257A
Abstract: A robust and easy to handle 3D porous platinum structure was created via replicating the 3D channel system
of an ordered mesoporous silica material using atomic layer deposition (ALD) over micrometer distances.
After ALD of Pt in the silica material, the host template was digested using hydrogen fluoride (HF). A fully
connected ordered Pt nanostructure was obtained with morphology and sizes corresponding to that of
the pores of the host matrix, as revealed with high-resolution scanning transmission electron
microscopy and electron tomography. The Pt nanostructure consisted of hexagonal Pt rods originating
from the straight mesopores (11 nm) of the host structure and linking features resulting from Pt
replication of the interconnecting mesopore segments (2–4 nm) present in the silica host structure.
Electron tomography of partial replicas, made by incomplete infilling of Zeotile-4 material with Pt,
provided insight in the connectivity and formation mechanism of the Pt nanostructure by ALD. The Pt
replica was evaluated for its potential use as electrocatalyst for the hydrogen evolution reaction, one of
the half-reactions of water electrolysis, and as microelectrode for biomedical sensing. The Pt replica
showed high activity for the hydrogen evolution reaction and electrochemical characterization revealed
a large impedance improvement in comparison with reference Pt electrodes.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 8.867
Times cited: 9
DOI: 10.1039/C7TA03257A
|
|
|
“Time evolution studies of dithieno[3,2-b:2 ',3 '-d] pyrrole-based A-D-A oligothiophene bulk heterojunctions during solvent vapor annealing towards optimization of photocurrent generation”. Ben Dkhil S, Pfannmöller M, Ata I, Duche D, Gaceur M, Koganezawa T, Yoshimoto N, Simon J-J, Escoubas L, Videlot-Ackermann C, Margeat O, Bals S, Bauerle P, Ackermann J, Journal of materials chemistry A : materials for energy and sustainability 5, 1005 (2017). http://doi.org/10.1039/C6TA08175D
Abstract: Solvent vapor annealing (SVA) is one of the main techniques to improve the morphology of bulk heterojunction solar cells using oligomeric donors. In this report, we study time evolution of nanoscale morphological changes in bulk heterojunctions based on a well-studied dithienopyrrole-based A-D-A oligothiophene (dithieno[3,2-b: 2',3'-d] pyrrole named here 1) blended with [6,6]-phenyl-C-71-butyric acid methyl ester (PC71BM) to increase photocurrent density by combining scanning transmission electron microscopy and low-energy-loss spectroscopy. Our results show that SVA transforms the morphology of 1 : PC71BM blends by a three-stage mechanism: highly intermixed phases evolve into nanostructured bilayers that correspond to an optimal blend morphology. Additional SVA leads to completely phaseseparated micrometer-sized domains. Optical spacers were used to increase light absorption inside optimized 1 : PC71BM blends leading to solar cells of 7.74% efficiency but a moderate photocurrent density of 12.3 mA cm (-2). Quantum efficiency analyses reveal that photocurrent density is mainly limited by losses inside the donor phase. Indeed, optimized 1 : PC71BM blends consist of large donor-enriched domains not optimal for exciton to photocurrent conversion. Shorter SVA times lead to smaller domains; however they are embedded in large mixed phases suggesting that introduction of stronger molecular packing may help us to better balance phase separation and domain size enabling more efficient bulk heterojunction solar cells.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 8.867
Times cited: 19
DOI: 10.1039/C6TA08175D
|
|
|
“Exciton Fine Structure and Lattice Dynamics in InP/ZnSe Core/Shell Quantum Dots”. Brodu A, Ballottin MV, Buhot J, van Harten EJ, Dupont D, La Porta A, Prins PT, Tessier MD, Versteegh MAM, Zwiller V, Bals S, Hens Z, Rabouw FT, Christianen PCM, de Donega CM, Vanmaekelbergh D, ACS Photonics 5, 3353 (2018). http://doi.org/10.1021/ACSPHOTONICS.8B00615
Abstract: Nanocrystalline InP quantum dots (QDs) hold promise for heavy-metal-free optoelectronic applications due to their bright and size tunable emission in the visible range. Photochemical stability and high photoluminescence (PL) quantum yield are obtained by a diversity of epitaxial shells around the InP core. To understand and optimize the emission line shapes, the exciton fine structure of InP core/shell QD systems needs be investigated. Here, we study the exciton fine structure of InP/ZnSe core/shell QDs with core diameters ranging from 2.9 to 3.6 nm (PL peak from 2.3 to 1.95 eV at 4 K). PL decay measurements as a function of temperature in the 10 mK to 300 K range show that the lowest exciton fine structure state is a dark state, from which radiative recombination is assisted by coupling to confined acoustic phonons with energies ranging from 4 to 7 meV, depending on the core diameter. Circularly polarized fluorescence line-narrowing (FLN) spectroscopy at 4 K under high magnetic fields (up to 30 T) demonstrates that radiative recombination from the dark F = +/- 2 state involves acoustic and optical phonons, from both the InP core and the ZnSe shell. Our data indicate that the highest intensity FLN peak is an acoustic phonon replica rather than a zero-phonon line, implying that the energy separation observed between the F = +/- 1 state and the highest intensity peak in the FLN spectra (6 to 16 meV, depending on the InP core size) is larger than the splitting between the dark and bright fine structure exciton states.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 6.756
Times cited: 40
DOI: 10.1021/ACSPHOTONICS.8B00615
|
|
|
“Three-Dimensional Nanoparticle Transformations Captured by an Electron Microscope”. Albrecht W, Van Aert S, Bals S, Accounts Of Chemical Research 54, 1189 (2021). http://doi.org/10.1021/acs.accounts.0c00711
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 20.268
Times cited: 12
DOI: 10.1021/acs.accounts.0c00711
|
|
|
“Photochemical production of hydrogen peroxide by digging pro-superoxide radical carbon vacancies in carbon nitride”. Ding Y, Maitra S, Arenas Esteban D, Bals S, Vrielinck H, Barakat T, Roy S, Van Tendeloo G, Liu J, Li Y, Vlad A, Su B-L, Cell reports physical science 3, 100874 (2022). http://doi.org/10.1016/J.XCRP.2022.100874
Abstract: Artificial photosynthesis of H2O2, an environmentally friendly oxidant and a clean fuel, holds great promise. However, improving its efficiency and stability for industrial implementation remains highly challenging. Here, we report the visible-light H2O2 artificial photosynthesis by digging pro-superoxide radical carbon vacancies in three-dimensional hierarchical porous g-C3N4 through a simple hydrolysis-freeze-drying-thermal treatment. A significant electronic structure change is revealed upon the implantation of carbon vacancies, broadening visible-light absorption and facilitating the photogenerated charge separation. The strong electron affinity of the carbon vacancies promotes superoxide radical (O-center dot(2)-) formation, significantly boosting the H2O2 photocatalytic production. The developed photocatalyst shows an H2O2 evolution rate of 6287.5 mM g(-1) h(-1) under visible-light irradiation with a long cycling stability being the best-performing photocatalyst among all reported g-C3N4-based systems. Our work provides fundamental insight into highly active and stable photocatalysts with great potential for safe industrial H2O2 production.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Times cited: 12
DOI: 10.1016/J.XCRP.2022.100874
|
|
|
“Deciphering the role of water in promoting the optoelectronic performance of surface-engineered lead halide perovskite nanocrystals”. Bhatia H, Martin C, Keshavarz M, Dovgaliuk I, Schrenker NJ, Ottesen M, Qiu W, Fron E, Bremholm M, Van de Vondel J, Bals S, Roeffaers MBJ, Hofkens J, Debroye E, ACS applied materials and interfaces 15, 7294 (2023). http://doi.org/10.1021/ACSAMI.2C20605
Abstract: Lead halide perovskites are promising candidates for applicability is limited by their structural instability toward moisture. Although a deliberate addition of water to the precursor solution has recently been shown to improve the crystallinity and optical properties of perovskites, the corresponding thin films still do not exhibit a near-unity quantum yield. Herein, we report that the direct addition of a minute amount of water to post-treated substantially enhances the stability while achieving a 95% photoluminescence quantum yield in a NC thin film. We unveil the mechanism of how moisture assists in the formation of an additional NH4Br component. Alongside, we demonstrate the crucial role of moisture in assisting localized etching of the perovskite crystal, facilitating the partial incorporation of NH4+, which is key for improved performance under ambient conditions. Finally, as a proof-of-concept, the application of post-treated and watertreated perovskites is tested in LEDs, with the latter exhibiting a superior performance, offering opportunities toward commercial application in moisture-stable optoelectronics.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 9.5
Times cited: 3
DOI: 10.1021/ACSAMI.2C20605
|
|