“Production and structure of exfoliated graphite/coke composites modified by ZrO2 nanoparticles”. Afanasov IM, Van Tendeloo G, Mateev AT, New carbon materials 25, 255 (2010). http://doi.org/10.1016/S1872-5805(09)60032-9
Abstract: Exfoliated graphite/coke composites modified by ZrO2 nanoparticles were produced using two different techniques and characterized by means of X-ray diffraction, scanning and transmission electron microscopy. In the first, low-density exfoliated graphite/coke blocks were dipped repeatedly and alternately in ZrO(NO3)2 and NH4OH solutions and subsequently heat treated at 1200°C in nitrogen to deposit thin layers of ZrO2 nanoparticles on the free surfaces of the carbon matrix. In the second, a mixture of expandable graphite, phenol-formaldehyde resin powder, and ZrOC2O4-modified fibrous cellulose in a sealed container was submitted to thermal shock at 900 °C followed by heat treatment at 1 200 °C in nitrogen to obtain the modified composites. The ZrO2 nanoparticles formed in the second technique were incorporated into the composites in three length scales: 6-30 nm-isolated nanoparticles and small blobs, 200-1000 nm-lengthy dendrite-like structures, and thin layer adhering to the surface of the 1-40 μm long cellulose carbon fibers.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1016/S1872-5805(09)60032-9
|
“Quantitative determination of strain fields around Ni4Ti3 precipitates in NiTi”. Tirry W, Schryvers D, Acta materialia 53, 1041 (2005). http://doi.org/10.1016/j.actamat.2004.10.049
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 97
DOI: 10.1016/j.actamat.2004.10.049
|
“Quantitative three-dimensional analysis of Ni4Ti3 precipitate morphology and distribution in polycrystalline Ni-Ti”. Cao S, Nishida M, Schryvers D, Acta materialia 59, 1780 (2011). http://doi.org/10.1016/j.actamat.2010.11.044
Abstract: The three-dimensional size, morphology and distribution of Ni4Ti3 precipitates in a Ni50.8Ti49.2 polycrystalline shape memory alloy with a heterogeneous microstructure have been investigated using a focused ion beam/scanning electron microscopy slice-and-view procedure. The mean volume, central plane diameter, thickness, aspect ratio and sphericity of the precipitates in the grain interior as well as near to the grain boundary were measured and/or calculated. The morphology of the precipitates was quantified by determining the equivalent ellipsoids with the same moments of inertia and classified according to the Zingg scheme. Also, the pair distribution functions describing the three-dimensional distributions were obtained from the coordinates of the precipitate mass centres. Based on this new data it is suggested that the existence of the heterogeneous microstructure could be due to a very small concentration gradient in the grains of the homogenized material and that the resulting multistage martensitic transformation originates in strain effects related to the size of the precipitates and scale differences of the available B2 matrix in between the precipitates.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 34
DOI: 10.1016/j.actamat.2010.11.044
|
“Self-organization of highly symmetric nanoassemblies : a matter of competition”. Galván-Moya JE, Altantzis T, Nelissen K, Peeters FM, Grzelczak M, Liz-Marán LM, Bals S, Van Tendeloo G, ACS nano 8, 3869 (2014). http://doi.org/10.1021/nn500715d
Abstract: The properties and applications of metallic nanoparticles are inseparably connected not only to their detailed morphology and composition but also to their structural configuration and mutual interactions. As a result, the assemblies often have superior properties as compared to individual nanoparticles. Although it has been reported that nanoparticles can form highly symmetric clusters, if the configuration can be predicted as a function of the synthesis parameters, more targeted and accurate synthesis will be possible. We present here a theoretical model that accurately predicts the structure and configuration of self-assembled gold nanoclusters. The validity of the model is verified using quantitative experimental data extracted from electron tomography 3D reconstructions of different assemblies. The present theoretical model is generic and can in principle be used for different types of nanoparticles, providing a very wide window of potential applications.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 13.942
Times cited: 34
DOI: 10.1021/nn500715d
|
“Spin effects in electron vortex states”. Van Boxem R, Verbeeck J, Partoens B, Europhysics letters 102, 40010 (2013). http://doi.org/10.1209/0295-5075/102/40010
Abstract: The recent experimental realization of electron vortex beams opens up a wide research domain previously unexplored. The present paper explores the relativistic properties of these electron vortex beams, and quantifies deviations from the scalar wave theory. It is common in electron optics to use the Schrodinger equation neglecting spin. The present paper investigates the role of spin and the total angular momentum J(z) and how it pertains to the vortex states. As an application, we also investigate if it is possible to use holographic reconstruction to create novel total angular momentum eigenstates in a transmission electron microscope. It is demonstrated that relativistic spin coupling effects disappear in the paraxial limit, and spin effects in holographically created electron vortex beams can only be exploited by using specialized magnetic apertures.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 1.957
Times cited: 11
DOI: 10.1209/0295-5075/102/40010
|
“Stable polyoxometalate insertion within the mesoporous metal organic framework MIL-100(Fe)”. Canioni R, Roch-Marchal C, Sécheresse F, Horcajada P, Serre C, Hardi-Dan M, Férey G, Grenèche J-M, Lefebvre F, Chang J-S, Hwang Y-K, Lebedev O, Turner S, Van Tendeloo G, Journal of materials chemistry 21, 1226 (2011). http://doi.org/10.1039/c0jm02381g
Abstract: Successful encapsulation of polyoxometalate (POM) within the framework of a mesoporous iron trimesate MIL-100(Fe) sample has been achieved by direct hydrothermal synthesis in the absence of fluorine. XRPD, 31P MAS NMR, IR, EELS, TEM and 57Fe Mössbauer spectrometry corroborate the insertion of POM within the cavities of the MOF. The experimental Mo/Fe ratio is 0.95, in agreement with the maximum theoretical amount of POM loaded within the pores of MIL-100(Fe), based on steric hindrance considerations. The POM-MIL-100(Fe) sample exhibits a pore volume of 0.373 cm3 g−1 and a BET surface area close to 1000 m2 g−1, indicating that small gas molecules can easily diffuse inside the cavities despite the presence of heavy phosphomolybdates. These latter contribute to the decrease in the overall surface area, due to the increase in molar weight, by 65%. Moreover, the resulting Keggin containing MIL-100(Fe) solid is stable in aqueous solution with no POM leaching even after more than 2 months. In addition, no exchange of the Keggin anions by tetrabutylammonium perchlorate in organic media has been observed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 158
DOI: 10.1039/c0jm02381g
|
“Stress-assisted crystallisation in anodic titania”. Vanhumbeeck J-F, Tian H, Schryvers D, Proost J, Corrosion science 53, 1269 (2011). http://doi.org/10.1016/j.corsci.2010.12.020
Abstract: The relationship between the microstructural and internal stress evolution during Ti anodising is discussed. Samples anodised galvanostatically to 12 V and 40 V, corresponding to different stages of the internal stress evolution, were examined by in-plane and cross-section transmission electron microscopy. Electron diffraction patterns have been complemented with stoichiometry data obtained from energy loss near edge structure spectra. The sample anodised to 40 V was observed to consist of two regions, with a crystallised inner region adjacent to the metal/oxide interface. Crystallisation of this region is associated with the presence of large compressive internal stresses which build up during anodising up to 12 V.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.245
Times cited: 11
DOI: 10.1016/j.corsci.2010.12.020
|
“Structural phase transition at the percolation threshold in epitaxial (La0.7Ca0.3MnO3)1-x:(MgO)x nanocomposite films”. Moshnyaga V, Damaschke B, Shapoval O, Belenchuk A, Faupel J, Lebedev OI, Verbeeck J, Van Tendeloo G, Mücksch M, Tsurkan V, Tidecks R, Samwer K, Nature materials 2, 247 (2003). http://doi.org/10.1038/nmat859
Abstract: 'Colossal magnetoresistance' in perovskite manganites such as La0.7Ca0.3MnO3 (LCMO), is caused by the interplay of ferro-paramagnetic, metal-insulator and structural phase transitions. Moreover, different electronic phases can coexist on a very fine scale resulting in percolative electron transport. Here we report on (LCMO)(1-x):(MgO)(x) (0 < x less than or equal to 0.8) epitaxial nano-composite films in which the structure and magnetotransport properties of the manganite nanoclusters can be tuned by the tensile stress originating from the MgO second phase. With increasing x, the lattice of LCMO was found to expand, yielding a bulk tensile strain. The largest colossal magnetoresistance of 10(5)% was observed at the percolation threshold in the conductivity at x(c) approximate to 0.3, which is coupled to a structural phase transition from orthorhombic (0 < x less than or equal to 0.1) to rhombohedral R (3) over barc structure (0.33 less than or equal to x less than or equal to 0.8). An increase of the Curie temperature for the R (3) over barc phase was observed. These results may provide a general method for controlling the magnetotransport properties of manganite-based composite films by appropriate choice of the second phase.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 39.737
Times cited: 177
DOI: 10.1038/nmat859
|
“Structural phase transition in the manganite Nd0.5Ca0.2Sr0.3MnO3-\delta”. Hervieu M, Van Tendeloo G, Schuddinck W, Richard O, Caignaert V, Millange F, Raveau B, Journal of electron microscopy 46, 263 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.9
Times cited: 2
|
“Structure and stability of Fe2 phases from density-functional theory calculations”. Fang CM, van Huis MA, Zandbergen HW, Scripta materialia 63, 418 (2010). http://doi.org/10.1016/j.scriptamat.2010.04.042
Abstract: Fe(2)C plays a crucial role in the precipitation of iron carbides. Jack's structural models for epsilon-Fe(2)C, and non-stoichiometric epsilon-Fe(2.4)C, are analyzed using first-principles calculations. Several new configurations of epsilon-Fe(2)C with even higher stability are found. We show how epsilon-Fe(2)C transforms into eta-Fe(2)C, and address the structural relationships with the chi-Fe(5)C(2), theta-Fe(3)C and Fe(7)C(3) phases. The relative occurrence of these phases in steel, as well as their probable evolution during tempering of quenched steels, is discussed. (C) 2010 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 32
DOI: 10.1016/j.scriptamat.2010.04.042
|
“Study of the packing of double-walled carbon nanotubes into bundles by transmission electron microscopy and electron diffraction”. Colomer J-F, Henrard L, Van Tendeloo G, Lucas A, Lambin P, Journal of materials chemistry 14, 603 (2004). http://doi.org/10.1039/b311551h
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 27
DOI: 10.1039/b311551h
|
“Symmetry and electronic states of Mn2+ in ZnS nanowires with mixed hexagonal and cubic stacking”. Chen L, Kirilenko D, Stesmans A, Nguyen XS, Binnemans K, Goderis B, Vanacken J, Lebedev O, Van Tendeloo G, Moshchalkov VV, Applied physics letters 97, 041918 (2010). http://doi.org/10.1063/1.3475017
Abstract: Electron spin resonance and electronic spectroscopy techniques were used to study the symmetry and electronic structure of Mn2+ dopants in solvothermally synthesized ZnS nanowires. The average diameter of ∼ 5 nm leads to the observable quantum confinement effects in the photoluminescence excitation spectra. The results clearly demonstrate the three symmetry locations of Mn2+ incorporation. Together with the inferred Mn2+ center densities, these data indicate a much higher efficiency of Mn2+ substitution in the nanowire sample with about two times larger diameter.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 5
DOI: 10.1063/1.3475017
|
“Synthesis and characterisation of lanthanide-based dioxide”. Esquivel MR, Zelaya E, Advances in applied ceramics 110, 219 (2011). http://doi.org/10.1179/1743676110Y.0000000021
Abstract: In the present work, the microstructure and structure of La(0.25)Ce(0.52)Nd(0.17)Pr(0.06)(OH)(3) and La(0.25)Ce(0.52)Nd(0.17)Pr(0.06)O(2) is obtained from transmission electron microscopy and X-ray diffraction measurements. Space group P6(3)/m is assigned to the structure of La(0.25)Ce(0.52)Nd(0.17)Pr(0.06)(OH)(3). Lanthanides are assigned to Wyckoff positions 2c. Cell parameters are a=6.375(5) angstrom and c=3.753(5) angstrom. The thermal decomposition of this compound was studied by differential scanning calorimetry. The process is exothermal with an enthalpy change Delta H degrees value of -254 +/- 10 kJ mol(-1). The decomposition kinetics is complex and two global processes with E(a) values of 98 +/- 4 and 61 +/- 2 kJ mol 21 were observed. The product is a lanthanide dioxide. Space group Fm3m is assigned to the La(0.25)Ce(0.52)Nd(0.17)Pr(0.06)O(2). Lanthanides are distributed in Wyckoff positions 4a. The cell parameter is a=5.479(5) angstrom. Nanopores in the oxide surface are obtained using this method and characterised by STEM measurements.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.325
Times cited: 3
DOI: 10.1179/1743676110Y.0000000021
|
“Synthesis and crystal structure of the new complex oxide Ca7Mn2.14Ga5.86O17.93”. Kalyuzhnaya AS, Abakumov AM, Rozova MG, d' Hondt H, Hadermann J, Antipov EV, Russian chemical bulletin 59, 706 (2010). http://doi.org/10.1007/s11172-010-0150-z
Abstract: The complex oxide Ca7Mn2.14Ga5.86O17.93 was synthesized by the solid-state reaction in a sealed evacuated quartz tube at 1000 °C. Its crystal structure was determined by electron diffraction and X-ray powder diffraction. The structure can be represented as a tetrahedral framework, viz., the polyanion [(Mn0.285Ga0.715)15O29.86]19- stabilized by the incorporated cation [Ca14GaO6]19+. The polycation consists of the GaO6 octahedra surrounded by the Ca atoms, which are arranged to form a cube capped at all places. The tetrahedral framework is partially disordered due to the presence of tetrahedra with two possible orientations in the positions (0, 0, 0) and (x, x, x) with x ≈ 0.15 and 0.17. The relationship between the Ca7Mn2.14Ga5.86O17.93 structures and related ordered phases with the symmetry F23, as well as the influence of the oxygen content on the ordering in the tetrahedral framework, are discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.529
Times cited: 1
DOI: 10.1007/s11172-010-0150-z
|
“Ag1/8Pr5/8MoO4: an incommensurately modulated scheelite-type structure”. Morozov VA, Mironov AV, Lazoryak BI, Khaikina EG, Basovich OM, Rossell MD, Van Tendeloo G, Journal of solid state chemistry 179, 1183 (2006). http://doi.org/10.1016/j.jssc.2005.12.041
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 35
DOI: 10.1016/j.jssc.2005.12.041
|
“The domain configuration of the Au11In3 phase”. Kifune K, Yamamoto K, Maruyama S, Van Tendeloo G, Philosophical magazine letters 69, 211 (1994). http://doi.org/10.1080/09500839408241594
Abstract: The crystal structure of Au11In3 thin film alloys have been analysed by means of electron diffraction and high-resolution electron microscopy. The electron diffraction pattern and the high-resolution electron microscopy revealed that this structure was incommensurate and had a domain structure consisting of three kinds of structural unit. The approximant structural model, which is based on a h.c.p. stacking of the layers, is hexagonal with lattice parameters a = 7.612 nm and c = 0-478 nm.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.087
Times cited: 2
DOI: 10.1080/09500839408241594
|
“The study of carbon nanotubules produced by catalytic method”. Ivanov V, Nagy JB, Lambin P, Lucas A, Zhang XB, Zhang XF, Bernaerts D, Van Tendeloo G, Amelinckx S, van Landuyt J, Chemical physics letters 223, 329 (1994). http://doi.org/10.1016/0009-2614(94)00467-6
Abstract: Catalytic methods for the production of carbon nanotubules have been developed based on the decomposition of acetylene on well-dispersed metal particles strongly adsorbed on a support. Cobalt on silica was found to be the best catalyst-support combination for the production of graphitic tubules. The method for the catalyst preparation and the reaction conditions were optimized. Straight and coiled carbon tubules were obtained with inner and outer diameter of 3-7 and 15-20 nm, respectively, and up to 30 mum in length. These nanotubules were not coated by amorphous carbon. Traces of amorphous carbon could be removed by hydrogen. High resolution electron microscopy images and electron diffraction patterns of the straight nanotubules were similar to those obtained by the arc-discharge method. Coiled nanotubules were revealed by TEM to be regular polygonized helices where the bends are caused by pairs of pentagon-heptagon carbon rings among the hexagonal network.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.897
Times cited: 405
DOI: 10.1016/0009-2614(94)00467-6
|
“Tomographic spectroscopic imaging, an experimental proof of concept”. van den Broek W, Verbeeck J, Schryvers D, de Backer S, Scheunders P, Ultramicroscopy 109, 296 (2009). http://doi.org/10.1016/j.ultramic.2008.11.022
Abstract: Recording the electron energy loss spectroscopy data cube with a series of energy filtered images is a dose inefficient process because the energy slit blocks most of the electrons. When recording the data cube by scanning an electron probe over the sample, perfect dose efficiency is attained; but due to the low current in nanoprobes, this often is slower, with a smaller field of view. In W. Van den Broek et al. [Ultramicroscopy, 106 (2006) 269], we proposed a new method to record the data cube, which is more dose efficient than an energy filtered series. It produces a set of projections of the data cube and then tomographically reconstructs it. In this article, we demonstrate these projections in practice, we present a simple geometrical model that allows for quantification of the projection angles and we present the first successful experimental reconstruction, all on a standard post-column instrument.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.843
Times cited: 1
DOI: 10.1016/j.ultramic.2008.11.022
|
“A vacancy-disordered, oxygen-deficient perovskite with long-range magnetic ordering : local and average structures and magnetic properties of Sr2Fe1.5Cr0.5O5”. Ramezanipour F, Greedan JE, Siewenie J, Donaberger RL, Turner S, Botton GA, Inorganic chemistry 51, 2638 (2012). http://doi.org/10.1021/ic202590r
Abstract: The local and average crystal structures and magnetic properties of the oxygen-deficient perovskite Sr2Fe1.5Cr0.5O5+y were studied using powder X-ray and neutron diffraction, neutron-pair distribution function analysis, and electron energy-loss spectroscopy. This material crystallizes in the cubic Pm3̅m space group, with a = 3.94491(14) Å. The oxygen vacancies are distributed randomly throughout the perovskite-type structure, and the average coordination number of the Fe(Cr) sites is 5. Refinement of the neutron diffraction data indicates y 0.05. This is in discordance with an earlier report on a material with the same nominal composition and cell constant. Electron energy-loss Cr L2,3-edge spectroscopy shows that Cr3+ is present, which is also contrary to previous speculation. Neutron-pair distribution function studies show that a brownmillerite-like model involving ordered vacancies and alternating octahedral and tetrahedral coordination at the metal sites, gives a better description of the local structure out to 5 Å. A remarkable phenomenon determined by neutron diffraction in Sr2Fe1.5Cr0.5O5 is the occurrence of a long-range G-type antiferromagnetic ordering with Tc ≈ 565 K because cubic oxygen-deficient perovskites with B-site disorder usually do not undergo transitions to magnetically ordered states. The observation of long-range antiferromagnetic order and the Tc value are in accordance with previous Mössbauer spectroscopic studies.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 12
DOI: 10.1021/ic202590r
|
“Well shaped Mn3O4 nano-octahedra with anomalous magnetic behavior and enhanced photodecomposition properties”. Li Y, Tan H, Yang X-Y, Goris B, Verbeeck J, Bals S, Colson P, Cloots R, Van Tendeloo G, Su B-L, Small 7, 475 (2011). http://doi.org/10.1002/smll.201001403
Abstract: Very uniform and well shaped Mn3O4 nano-octahedra are synthesized using a simple hydrothermal method under the help of polyethylene glycol (PEG200) as a reductant and shape-directing agent. The nano-octahedra formation mechanism is monitored. The shape and crystal orientation of the nanoparticles is reconstructed by scanning electron microscopy and electron tomography, which reveals that the nano-octahedra only selectively expose {101} facets at the external surfaces. The magnetic testing demonstrates that the Mn3O4 nano-octahedra exhibit anomalous magnetic properties: the Mn3O4 nano-octahedra around 150 nm show a similar Curie temperature and blocking temperature to Mn3O4 nanoparticles with 10 nm size because of the vertical axis of [001] plane and the exposed {101} facets. With these Mn3O4 nano-octahedra as a catalyst, the photodecomposition of rhodamine B is evaluated and it is found that the photodecomposition activity of Mn3O4 nano-octahedra is much superior to that of commercial Mn3O4 powders. The anomalous magnetic properties and high superior photodecomposition activity of well shaped Mn3O4 nano-octahedra should be related to the special shape of the nanoparticles and the abundantly exposed {101} facets at the external surfaces. Therefore, the shape preference can largely broaden the application of the Mn3O4 nano-octahedra.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.643
Times cited: 131
DOI: 10.1002/smll.201001403
|
“Enhanced 77K vortex-pinning in YBa2Cu3O7−x films with Ba2YTaO6 and mixed Ba2YTaO6 + Ba2YNbO6 nano-columnar inclusions with irreversibility field to 11T”. Rizzo F, Augieri A, Angrisani Armenio A, Galluzzi V, Mancini A, Pinto V, Rufoloni A, Vannozzi A, Bianchetti M, Kursumovic A, MacManus-Driscoll JL, Meledin A, Van Tendeloo G, Celentano G, APL materials 4, 061101 (2016). http://doi.org/10.1063/1.4953436
Abstract: Pulsed laser deposited thin YBa2Cu3O7−x (YBCO) films with pinning additions of 5at.% Ba2YTaO6 (BYTO) were compared to films with 2.5at.% Ba2YTaO6 + 2.5at.% Ba2YNbO6 (BYNTO) additions. Excellent magnetic flux-pinning at 77 K was obtained with remarkably high irreversibility fields greater than 10T (YBCO-BYTO) and 11T (YBCO-BYNTO), representing the highest ever achieved values in YBCO films.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.335
Times cited: 19
DOI: 10.1063/1.4953436
|
“Highly efficient rutile TiO2 photocatalysts with single Cu(II) and Fe(III) surface catalytic sites”. Neubert S, Mitoraj D, Shevlin SA, Pulisova P, Heimann M, Du Y, Goh GKL, Pacia M, Kruczała K, Turner S, Macyk W, Guo ZX, Hocking RK, Beranek R;, Journal of materials chemistry A : materials for energy and sustainability 4, 3127 (2016). http://doi.org/10.1039/c5ta07036h
Abstract: Highly active photocatalysts were obtained by impregnation of nanocrystalline rutile TiO2 powders with small amounts of Cu(II) and Fe(III) ions, resulting in the enhancement of initial rates of photocatalytic degradation of 4-chlorophenol in water by factors of 7 and 4, compared to pristine rutile, respectively. Detailed structural analysis by EPR and X-ray absorption spectroscopy (EXAFS) revealed that Cu(II) and Fe(III) are present as single species on the rutile surface. The mechanism of the photoactivity enhancement was elucidated by a combination of DFT calculations and detailed experimental mechanistic studies including photoluminescence measurements, photocatalytic experiments using scavengers, OH radical detection, and photopotential transient measurements. The results demonstrate that the single Cu(II) and Fe(III) ions act as effective cocatalytic sites, enhancing the charge separation, catalyzing “dark” redox reactions at the interface, thus improving the normally very low quantum yields of UV light-activated TiO2 photocatalysts. The exact mechanism of the photoactivity enhancement differs depending on the nature of the cocatalyst. Cu(II)-decorated samples exhibit fast transfer of photogenerated electrons to Cu(II/I) sites, followed by enhanced catalysis of dioxygen reduction, resulting in improved charge separation and higher photocatalytic degradation rates. At Fe(III)-modified rutile the rate of dioxygen reduction is not improved and the photocatalytic enhancement is attributed to higher production of highly oxidizing hydroxyl radicals produced by alternative oxygen reduction pathways opened by the presence of catalytic Fe(III/II) sites. Importantly, it was demonstrated that excessive heat treatment (at 450 degrees C) of photocatalysts leads to loss of activity due to migration of Cu(II) and Fe(III) ions from TiO2 surface to the bulk, accompanied by formation of oxygen vacancies. The demonstrated variety of mechanisms of photoactivity enhancement at single site catalyst-modified photocatalysts holds promise for developing further tailored photocatalysts for various applications.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 8.867
Times cited: 44
DOI: 10.1039/c5ta07036h
|
“PDMS membranes containing ZIF-coated mesoporous silica spheres for efficient ethanol recovery via pervaporation”. Naik PV, Wee LH, Meledina M, Turner S, Li Y, Van Tendeloo G, Martens JA, Vankelecom IFJ, Journal of materials chemistry A : materials for energy and sustainability 4, 12790 (2016). http://doi.org/10.1039/C6TA04700A
Abstract: The design of functional micro- and mesostructured composite materials is significantly important for separation processes. Mesoporous silica is an attractive material for fast diffusion, while microporous zeolitic imidazolate frameworks (ZIFs) are beneficial for selective adsorption and diffusion. In this work, ZIF-71 and ZIF-8 nanocrystals were grown on the surface of mesoporous silica spheres (MSS) via the seeding and regrowth approach in order to obtain monodispersed MSS-ZIF-71 and MSS-ZIF-8 spheres with a particle size of 2-3 mm. These MSS-ZIF spheres were uniformly dispersed into a polydimethylsiloxane (PDMS) matrix to prepare mixed matrix membranes (MMMs). These MMMs were evaluated for the separation of ethanol from water via pervaporation. The pervaporation results reveal that the MSS-ZIF filled MMMs substantially improve the ethanol recovery in both aspects viz. flux and separation factor. These MMMs outperforms the unfilled PDMS membranes and the conventional carbon and zeolite filled MMMs. As expected, the mesoporous silica core allows very fast flow of the permeating compound, while the hydrophobic ZIF coating enhances the ethanol selectivity through its specific pore structure, hydrophobicity and surface chemistry. It can be seen that ZIF-8 mainly has a positive impact on the selectivity, while ZIF-71 enhances fluxes more significantly.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 8.867
Times cited: 26
DOI: 10.1039/C6TA04700A
|
“The mechanical behavior during (de)lithiation of coated silicon nanoparticles as anode material for lithium-ion batteries studied by InSitu transmission electron microscopy”. Van Havenbergh K, Turner S, Marx N, Van Tendeloo G, Energy technology 4, 1005 (2016). http://doi.org/10.1002/ENTE.201600057
Abstract: One approach to cope with the continuous irreversible capacity loss in Si-based electrodes, attributed to lithiation-induced volume changes and the formation of a solid-electrolyte interface (SEI), is by coating silicon nanoparticles. A coating can improve the conductivity of the electrode, form a chemical shield against the electrolyte, or provide mechanical confinement to reduce the volume increase. The influence of such a coating on the mechanical behavior of silicon nanoparticles during Li insertion and Li extraction was investigated by insitu transmission electron microscopy. The type of coating was shown to influence the size of the unreacted core that remains after reaction of silicon with lithium. Furthermore, two mechanisms to relieve the stress generated during volume expansion are reported: the initiation of cracks and the formation of nanovoids. Both result in a full reaction of the silicon nanoparticles, whereas with the formation of cracks, additional surface area is created, on which an SEI can be formed.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.789
Times cited: 6
DOI: 10.1002/ENTE.201600057
|
“Energy Level Alignment and Cation Charge States at the LaFeO3/LaMnO3(001) Heterointerface”. Smolin SY, Choquette AK, Wilks RG, Gauquelin N, Félix R, Gerlach D, Ueda S, Krick AL, Verbeeck J, Bär M, Baxter JB, May SJ, Advanced Materials Interfaces 4, 1700183 (2017). http://doi.org/10.1002/admi.201700183
Abstract: The electronic properties of LaFeO 3 /LaMnO 3 epitaxial heterojunctions are investigated to determine the valence and conduction band offsets and the nominal Mn and Fe valence states at the interface. Studying a systematic series of (LaFeO 3 ) n /(LaMnO 3 ) m bilayers (m ≈ 50) epitaxially grown in the (001) orientation using molecular beam epitaxy, layer-resolved electron energy loss spectroscopy reveals a lack of significant interfacial charge transfer, with a nominal 3+ valence state observed for both Mn and Fe across the interface. Through a combination of variable angle spectroscopic ellipsometry and hard X-ray photoelectron spectroscopy, type I energy level alignments are obtained at the LaFeO 3 /LaMnO 3 interface with positive valence and conduction band offsets of (1.20 ± 0.07) eV and (0.5–0.7 ± 0.3) eV, respectively, with minimal band bending. Variable temperature resistivity measurements reveal that the bilayers remain insulating and that the presence of the heterojunction does not result in a conducting interface.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.279
Times cited: 14
DOI: 10.1002/admi.201700183
|
“Synthesis, structure, and electrochemical properties of k-based sulfates K2M2(SO4)3) with M = Fe and Cu”. Lander L, Rousse G, Batuk D, Colin CV, Dalla Corte DA, Tarascon J-M, Inorganic chemistry 56, 2013 (2017). http://doi.org/10.1021/ACS.INORGCHEM.6B02526
Abstract: Stabilizing new host structures through potassium extraction from K-based polyanionic materials has been proven to be an interesting approach to develop new Li+/Na+ insertion materials. Pursuing the same trend, we here report the feasibility of preparing langbeinite “Fe-2(SO4)(3)” via electrochemical and chemical oxidation of K2Fe2(SO4)(3). Additionally, we succeeded in stabilizing a new K2Cu2(SO4)(3) phase via a solid-state synthesis approach. This novel compound crystallizes in a complex orthorhombic structure that differs from that of langbeinite as deduced from synchrotron X-ray and neutron powder diffraction. Electrochemically, the performance of this new phase is limited, which we explain in terms of sluggish diffusion kinetics. We further show that K2Cu2(SO4)(3) decomposes into K2Cu3O(SO4)(3) on heating, and we report for the first time the synthesis of fedotovite K2Cu3O(SO4)(3). Finally, the fundamental attractiveness of these S = 1/2 systems for physicists is examined by neutron magnetic diffraction, which reveals the absence of a long-range ordering of Cu2+ magnetic moments down to 1.5 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 13
DOI: 10.1021/ACS.INORGCHEM.6B02526
|
“Tailoring microstructure and superconducting properties in thick BaHfO3 and Ba2YNb/Ta)O-6 doped YBCO films on technical templates”. Sieger M, Pahlke P, Lao M, Eisterer M, Meledin A, Van Tendeloo G, Ottolinger R, Haenisch J, Holzapfel B, Usoskin A, Kursumovic A, MacManus-Driscoll JL, Stafford BH, Bauer M, Nielsch K, Schultz L, Huehne R, IEEE transactions on applied superconductivity 27, 6601407 (2017). http://doi.org/10.1109/TASC.2016.2644858
Abstract: The current transport capability of YBa2Cu3O7-x(YBCO) based coated conductors (CCs) is mainly limited by two features: the grain boundaries of the used textured template, which are transferred into the superconducting film through the buffer layers, and the ability to pin magnetic flux lines by incorporation of defined defects in the crystal lattice. By adjusting the deposition conditions, it is possible to tailor the pinning landscape in doped YBCO in order to meet specific working conditions (T, B) for CC applications. To study these effects, we deposited YBCO layers with a thickness of about 1-2 mu m using pulsed laser deposition on buffered rolling-assisted biaxially textured Ni-W substrates as well as on metal tapes having either an ion-beam-texturedYSZbuffer or an MgO layer textured by inclined substrate deposition. BaHfO3 and the mixed double-perovskite Ba2Y(Nb/Ta)O-6 were incorporated as artificial pinning centers in these YBCO layers. X-ray diffraction confirmed the epitaxial growth of the superconductor on these templates as well as the biaxially oriented incorporation of the secondary phase additions in the YBCO matrix. A critical current density J(c) of more than 2 MA/cm(2) was achieved at 77 K in self-field for 1-2 mu m thick films. Detailed TEM (transmission electron microscopy) studies revealed that the structure of the secondary phase can be tuned, forming c-axis aligned nanocolumns, ab-oriented platelets, or a combination of both. Transport measurements show that the J(c) anisotropy in magnetic fields is reduced by doping and the peak in the J(c) (theta) curves can be correlated to the microstructural features.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 12
DOI: 10.1109/TASC.2016.2644858
|
“The influence of branched alkyl side chains in A-D-A oligothiophenes on the photovoltaic performance and morphology of solution-processed bulk-heterojunction solar cells”. Ata I, Ben Dkhil S, Pfannmoeller M, Bals S, Duche D, Simon J-J, Koganezawa T, Yoshimoto N, Videlot-Ackermann C, Margeat O, Ackermann J, Baeuerle P, Organic chemistry frontiers : an international journal of organic chemistry 4, 1561 (2017). http://doi.org/10.1039/C7QO00222J
Abstract: Besides providing sufficient solubility, branched alkyl chains also affect the film-forming and packing properties of organic semiconductors. In order to avoid steric hindrance as it is present in wide-spread alkyl chains comprising a branching point position at the C2-position, i.e., 2-ethylhexyl, the branching point can be moved away from the pi-conjugated backbone. In this report, we study the influence of the modification of the branching point position from the C2-position in 2-hexyldecylamine (1) to the C4-position in 4-hexyldecylamine (2) connected to the central dithieno[3,2-b: 2', 3'-d] pyrrole (DTP) moiety in a well-studied A-D-A oligothiophene on the optoelectronic properties and photovoltaic performance in solution- processed bulk heterojunction solar cells (BHJSCs) with [6,6]-phenyl-C71-butyric acid methyl ester (PC71BM) as the acceptor material. Post-treatment of the photoactive layers is performed via solvent vapor annealing (SVA) in order to improve the film microstructure of the bulk heterojunction. The time evolution of nanoscale morphological changes is followed by combining scanning transmission electron microscopy with low-energy-loss spectroscopic imaging (STEM-SI), solid-state absorption spectroscopy, and two-dimensional grazing incidence X-ray diffraction (2D-GIXRD). Our results show an improvement of the photovoltaic performance that is dependent on the branching point position in the donor oligomer. Optical spacers are utilized to increase light absorption inside the co-oligomer 2-based BHJSCs leading to increased power conversion efficiencies (PCEs) of 8.2% when compared to the corresponding co-oligomer 1-based devices. A STEM-SI analysis of the respective device cross-sections of active layers containing 1 and 2 as donor materials indeed reveals significant differences in their respective active layer morphologies.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.955
Times cited: 24
DOI: 10.1039/C7QO00222J
|
“Thermal characterization of polycrystalline diamond thin film heat spreaders grown on GaN HEMTs”. Zhou Y, Ramaneti R, Anaya J, Korneychuk S, Derluyn J, Sun H, Pomeroy J, Verbeeck J, Haenen K, Kuball M, Applied physics letters 111, 041901 (2017). http://doi.org/10.1063/1.4995407
Abstract: Polycrystalline diamond (PCD) was grown onto high-k dielectric passivated AlGaN/GaN-on-Si high electron mobility transistor (HEMT) structures, with film thicknesses ranging from 155 to 1000 nm. Transient thermoreflectance results were combined with device thermal simulations to investigate the heat spreading benefit of the diamond layer. The observed thermal conductivity (k(Dia)) of PCD films is one-to-two orders of magnitude lower than that of bulk PCD and exhibits a strong layer thickness dependence, which is attributed to the grain size evolution. The films exhibit a weak temperature dependence of k(Dia) in the measured 25-225 degrees C range. Device simulation using the experimental jDia and thermal boundary resistance values predicts at best a 15% reduction in peak temperature when the source-drain opening of a passivated AlGaN/GaN-on-Si HEMT is overgrown with PCD. Published by AIP Publishing.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 78
DOI: 10.1063/1.4995407
|
“Vapor Phase Fabrication of Nanoheterostructures Based on ZnO for Photoelectrochemical Water Splitting”. Barreca D, Carraro G, Gasparotto A, Maccato C, Altantzis T, Sada C, Kaunisto K, Ruoko T-P, Bals S, Advanced Materials Interfaces 4, 1700161 (2017). http://doi.org/10.1002/admi.201700161
Abstract: Nanoheterostructures based on metal oxide semiconductors have emerged
as promising materials for the conversion of sunlight into chemical energy.
In the present study, ZnO-based nanocomposites have been developed by
a hybrid vapor phase route, consisting in the chemical vapor deposition
of ZnO systems on fluorine-doped tin oxide substrates, followed by the
functionalization with Fe2O3 or WO3 via radio frequency-sputtering. The
target systems are subjected to thermal treatment in air both prior and after
sputtering, and their properties, including structure, chemical composition,
morphology, and optical absorption, are investigated by a variety of characterization
methods. The obtained results evidence the formation of highly
porous ZnO nanocrystal arrays, conformally covered by an ultrathin Fe2O3
or WO3 overlayer. Photocurrent density measurements for solar-triggered
water splitting reveal in both cases a performance improvement with respect
to bare zinc oxide, that is mainly traced back to an enhanced separation of
photogenerated charge carriers thanks to the intimate contact between the
two oxides. This achievement can be regarded as a valuable result in view of
future optimization of similar nanoheterostructured photoanodes.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.279
Times cited: 30
DOI: 10.1002/admi.201700161
|