“Influence of artificial pinning centers on structural and superconducting properties of thick YBCO films on ABAD-YSZ templates”. Pahlke P, Sieger M, Ottolinger R, Lao M, Eisterer M, Meledin A, Van Tendeloo G, Haenisch J, Holzapfel B, Schultz L, Nielsch K, Huehne R, Superconductor science and technology 31, 044007 (2018). http://doi.org/10.1088/1361-6668/AAAFBE
Abstract: Recent efforts in the development of YBa2Cu3O7-x (YBCO) coated conductors are devoted to the increase of the critical current I-c in magnetic fields. This is typically realized by growing thicker YBCO layers as well as by the incorporation of artificial pinning centers. We studied the growth of doped YBCO layers with a thickness of up to 7 mu m using pulsed laser deposition with a growth rate of about 1.2 nm s(-1). Industrially fabricated ion-beam textured YSZ templates based on metal tapes were used as substrates for this study. The incorporation of BaHfO3 (BHO) or Ba2Y(Nb0.5Ta0.5)O-6 (BYNTO) secondary phase additions leads to a denser microstructure compared to undoped films. A purely c-axis-oriented YBCO growth is preserved up to a thickness of about 4 mu m, whereas misoriented texture components were observed in thicker films. The critical temperature is slightly reduced compared to undoped films and independent of film thickness. The critical current density J(c) of the BHO- and BYNTO-doped YBCO layers is lower at 77 K and self-field compared to pure YBCO layers; however, I-c increases up to a thickness of 5 mu m. A comparison between films with a thickness of 1.3 mu m revealed that the anisotropy of the critical current density J(c)(theta) strongly depends on the incorporated pinning centers. Whereas BHO nanorods lead to a strong B vertical bar vertical bar c-axis peak, the overall anisotropy is significantly reduced by the incorporation of BYNTO forming a mixture of short c-axis-oriented nanorods and small (a-b)-oriented platelets. As a result, the J(c) values of the doped films outperform the undoped samples at higher fields and lower temperatures for most magnetic field directions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 9
DOI: 10.1088/1361-6668/AAAFBE
|
“A Roman Egyptian Painting Workshop : technical investigation of the portraits from Tebtunis, Egypt”. Salvant J, Williams J, Ganio M, Casadio F, Daher C, Sutherland K, Monico L, Vanmeert F, De Meyer S, Janssens K, Cartwright C, Walton M, Archaeometry 60, 815 (2018). http://doi.org/10.1111/ARCM.12351
Abstract: Roman-period mummy portraits are considered to be ancient antecedents of modern portraiture. However, the techniques and materials used in their manufacture are not thoroughly understood. Analytical study of the pigments as well as the binding materials helps to address questions on what aspects of the painting practices originate from Pharaonic and/or Graeco-Roman traditions, and can aid in determining the provenance of the raw materials from potential locations across the ancient Mediterranean and European worlds. Here, one of the largest assemblages of mummy portraits to remain intact since their excavation from the site of Tebtunis in Egypt was examined using multiple analytical techniques to address how they were made. The archaeological evidence suggests that these portraits were products of a single workshop and, correspondingly, they are found to be made using similar techniques and materials: wax-based and lead white-rich paint combined with a variety of iron-based pigments (including hematite, goethite and jarosite), as well as Egyptian blue, minium, indigo and madder lake to create subtle variations and tones.
Keywords: A1 Journal article; History; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 1.47
Times cited: 6
DOI: 10.1111/ARCM.12351
|
“Low Loss Atomic Layer Deposited Al2O3 Waveguides for Applications in On-Chip Optical Amplifiers”. Demirtas M, Odaci C, Perkgoz NK, Sevik C, Ay F, IEEE journal of selected topics in quantum electronics 24, 3100508 (2018). http://doi.org/10.1109/JSTQE.2018.2825880
Abstract: We present the growth and optimization of ultralow loss Si-based Al2O3 planar waveguides, which have a high potential to boost the performance of rare-earth ion doped waveguide devices operating at visible and C-band wavelength ranges. The planar waveguide structures are grown using thermal atomic layer deposition. Systematic characterization of the obtained thin films is performed by spectroscopic ellipsometry, X-ray diffraction, Fourier transform infrared spectroscopy, and X-ray photoelectron spectroscopy analyses, and the optimum parameters are identified. The optical loss measurements for both transverse electric (TE) and transverse magnetic polarized light at 633, 829, and 1549 nm are performed. The lowest propagation loss value of 0.04 +/- 0.02 dB/cm for the Al2O3 waveguides for TE polarization at 1549 nm is demonstrated.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
DOI: 10.1109/JSTQE.2018.2825880
|
“Modeling electron competition among nitrogen oxides reduction and N2Oaccumulation in hydrogenotrophic denitrification”. Liu Y, Ngo HH, Guo W, Peng L, Chen X, Wang D, Pan Y, Ni B-J, Biotechnology and bioengineering 115, 978 (2018). http://doi.org/10.1002/BIT.26512
Abstract: Hydrogenotrophic denitrification is a novel and sustainable process for nitrogen removal, which utilizes hydrogen as electron donor, and carbon dioxide as carbon source. Recent studies have shown that nitrous oxide (N2O), a highly undesirable intermediate and potent greenhouse gas, can accumulate during this process. In this work, a new mathematical model is developed to describe nitrogen oxides dynamics, especially N2O, during hydrogenotrophic denitrification for the first time. The model describes electron competition among the four steps of hydrogenotrophic denitrification through decoupling hydrogen oxidation and nitrogen reduction processes using electron carriers, in contrast to the existing models that couple these two processes and also do not consider N2O accumulation. The developed model satisfactorily describes experimental data on nitrogen oxides dynamics obtained from two independent hydrogenotrophic denitrifying cultures under various hydrogen and nitrogen oxides supplying conditions, suggesting the validity and applicability of the model. The results indicated that N2O accumulation would not be intensified under hydrogen limiting conditions, due to the higher electron competition capacity of N2O reduction in comparison to nitrate and nitrite reduction during hydrogenotrophic denitrification. The model is expected to enhance our understanding of the process during hydrogenotrophic denitrification and the ability to predict N2O accumulation.
Keywords: A1 Journal article; Engineering sciences. Technology; Sustainable Energy, Air and Water Technology (DuEL)
DOI: 10.1002/BIT.26512
|
“Role of the carbon support on the oxygen reduction and evolution activities in LaNiO3 composite electrodes in alkaline solution”. Alexander CT, Abakumov AM, Forslund RP, Johnston KP, Stevenson KJ, ACS applied energy materials 1, 1549 (2018). http://doi.org/10.1021/ACSAEM.7B00339
Abstract: Metal-air batteries and fuel cells show a great deal of promise in advancing low-cost, high-energy-density charge storage solutions for sustainable energy applications. To improve the activities and stabilities of electrocatalysts for the critical oxygen reduction and evolution reactions (ORR and OER, respectively), a greater understanding is needed of the catalyst/carbon interactions and carbon stability. Herein, we report how LaNiO3 (LNO) supported on nitrogen-doped carbon nanotubes (N-CNT) made from a high-yield synthesis lowers the overpotential for both the OER and ORR markedly to enable a low bifunctional window of 0.81 V at only a 51 mu g cm(-2) mass loading. Furthermore, the addition of LNO to the N-CNTs improves the galvanostatic stability for the OER by almost 2 orders of magnitude. The nanoscale geometries of the perovskites and the CNTs enhance the number of metal-support and charge transfer interactions and thus the activity. We use rotating ring disk electrodes (RRDEs) combined with Tafel slope analysis and ICP-OES to quantitatively separate current contributions from the OER, carbon oxidation, and even anodic iron leaching from carbon nanotubes.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1021/ACSAEM.7B00339
|
“Optical readout of controlled monomer-dimer self-assembly”. Tarakanov PA, Tarakanova EN, Dorovatovskii PV, Zubavichus YV, Khrustalev VN, Trashin SA, De Wael K, Neganova ME, Mischenko DV, Sessler JL, Stuzhin PA, Pushkarev VE, Tomilova LG, Journal of the Chemical Society : Dalton transactions 47, 14169 (2018). http://doi.org/10.1039/C8DT00384J
Abstract: 5,7-Substituted 1,4-diazepinoporphyrazine magnesium(II) complexes were synthesized via Mg(II)-alkoxide templated macrocyclization. A single crystal growth synchrotron diffraction analysis permitted what is to our knowledge the first structural characterization of a 1,4-diazepinoporphyrazine. It exists as a dimer in the solid state. In silico calculations supported by solution phase spectral studies involving a series of representative derivatives, provided insights into the factors governing dimerization of 1,4-diazepinoporphyrazines. The present 1,4-diazepinoporphyrazines serve as useful probes for understanding the determinants that guide dimermonomer equilibria and the self-assembly of phthalocyanine derivatives.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Times cited: 4
DOI: 10.1039/C8DT00384J
|
“Assessing the success of electricity demand response programs : a meta-analysis”. Srivastava A, Van Passel S, Laes E, Energy Research and Social Science 40, 110 (2018). http://doi.org/10.1016/J.ERSS.2017.12.005
Abstract: This paper conducts a meta-analysis of 32 electricity demand response programs in the residential sector to understand whether their success is dependent on specific characteristics. The paper analyses several regression models using various combinations of variables that capture the designs of the programs and the socio-economic conditions in which the programs are implemented. The analysis reveals that demand response programs are more likely to succeed in highly urbanized areas, in areas where economic growth rates are high, and in areas where the renewable energy policy is favorable. These findings provide useful guidance in determining where and how to implement future demand response programs.
Keywords: A1 Journal article; Economics; Engineering Management (ENM)
Times cited: 18
DOI: 10.1016/J.ERSS.2017.12.005
|
“Experimental and computational investigation of graphene/SAMs/n-Si Schottky diodes”. Aydin H, Bacaksiz C, Yagmurcukardes N, Karakaya C, Mermer O, Can M, Senger RT, Sahin H, Selamet Y, Applied Surface Science 428, 1010 (2018). http://doi.org/10.1016/J.APSUSC.2017.09.204
Abstract: We have investigated the effect of two different self-assembled monolayers (SAMs) on electrical characteristics of bilayer graphene (BLG)/n-Si Schottky diodes. Novel 4“bis(diphenylamino)-1, 1':3”-terpheny1-5' carboxylic acids (TPA) and 4,4-di-9H-carbazol-9-y1-1,1':3'1'-terpheny1-5' carboxylic acid (CAR) aromatic SAMs have been used to modify n-Si surfaces. Cyclic voltammetry (CV) and Kelvin probe force microscopy (KPFM) results have been evaluated to verify the modification of n-Si surface. The current-voltage (I-V) characteristics of bare and SAMs modified devices show rectification behaviour verifying a Schottky junction at the interface. The ideality factors (n) from ln(I)-V dependences were determined as 2.13,1.96 and 2.07 for BLG/n-Si, BLG/TPA/n-Si and BLG/CAR/n-Si Schottky diodes, respectively. In addition, Schottky barrier height (SBH) and series resistance (Rs) of SAMs modified diodes were decreased compared to bare diode due to the formation of a compatible interface between graphene and Si as well as n-n interaction between aromatic SAMs and graphene. The CAR-based device exhibits better diode characteristic compared to the TPA-based device. Computational simulations show that the BLG/CAR system exhibits smaller energy-level-differences than the BLG/TPA, which supports the experimental findings of a lower Schottky barrier and series resistance in BLG/CAR diode. (C) 2017 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 3.387
Times cited: 2
DOI: 10.1016/J.APSUSC.2017.09.204
|
“A comparative DFT study on CO oxidation reaction over Si-doped BC2N nanosheet and nanotube”. Nematollahi P, Neyts EC, Applied surface science 439, 934 (2018). http://doi.org/10.1016/J.APSUSC.2017.12.254
Abstract: In this study, we performed density functional theory (DFT) calculations to investigate different reaction mechanisms of CO oxidation catalyzed by the Si atom embedded defective BC2N nanostructures as well as the analysis of the structural and electronic properties. The structures of all the complexes are optimized and characterized by frequency calculations at the M062X/6-31G* computational level. Also, The electronic structures and thermodynamic parameters of adsorbed CO and O-2 molecules over Si-doped BC2N nanostructures are examined in detail. Moreover, to investigate the curvature effect on the CO oxidation reaction, all the adsorption and CO oxidation reactions on a finite-sized armchair (6,6) Si-BC2NNT are also studied. Our results indicate that there can be two possible pathways for the CO oxidation with O-2 molecule: O-2(g) + CO(g) -> O-2(ads) + CO(ads) -> CO2(g) + O-(ads) and O-(ads) + CO(g) -> CO2(g). The first reaction proceeds via the Langmuir-Hinshelwood (LH) mechanism while the second goes through the Eley-Rideal (ER) mechanism. On the other hand, by increasing the tube diameter, the energy barrier increases due to the strong adsorption energy of the O-2 molecule which is related to its dissociation over the tube surface. Our calculations indicate that the two step energy barrier of the oxidation reaction over Si-BC2NNS is less than that over the Si-BC2NNT. Hence, Si-BC2NNS may serve as an efficient and highly activated substrate to CO oxidation rather than (4,4) Si-BC2NNT. (C) 2018 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 3.387
Times cited: 8
DOI: 10.1016/J.APSUSC.2017.12.254
|
“Small-moment paramagnetism and extensive twinning in the topochemically reduced phase Sr2ReLiO5.5”. Hasanli N, Gauquelin N, Verbeeck J, Hadermann J, Hayward MA, Journal of the Chemical Society : Dalton transactions 47, 15783 (2018). http://doi.org/10.1039/C8DT03463J
Abstract: Reaction of the cation-ordered double perovskite Sr2ReLiO6 with dilute hydrogen at 475 degrees C leads to the topochemical deintercalation of oxide ions from the host lattice and the formation of a phase of composition Sr2ReLiO5.5, as confirmed by thermogravimetric and EELS data. A combination of neutron and electron diffraction data reveals the reduction process converts the -Sr2O2-ReLiO4-Sr2O2-ReLiO4- stacking sequence of the parent phase into a -Sr2O2-ReLiO3-Sr2O2-ReLiO4-, partially anion-vacant ordered sequence. Furthermore a combination of electron diffraction and imaging reveals Sr2ReLiO5.5 exhibits extensive twinning – a feature which can be attributed to the large, anisotropic volume expansion of the material on reduction. Magnetisation data reveal a strongly reduced moment of (eff) = 0.505(B) for the d(1) Re6+ centres in the phase, suggesting there remains a large orbital component to the magnetism of the rhenium centres, despite their location in low symmetry coordination environments.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.029
DOI: 10.1039/C8DT03463J
|
“Tailoring the functional properties of polyurethane foam with dispersions of carbon nanofiber for power generator applications”. Sathiyamoorthy S, Girijakumari G, Kannan P, Venugopal K, Thiruvottriyur Shanmugam S, Veluswamy P, De Wael K, Ikeda H, Applied surface science 449, 507 (2018). http://doi.org/10.1016/J.APSUSC.2018.01.088
Abstract: To produce effective thermoelectric nanocomposites, carbon nanofibers (CNF) incorporated polyurethane (PU) foams with nanocomposites are prepared via in-situ polymerization method to create a synergy that would produce a high thermopower. The formation mechanism of foams, the reaction kinetics, and the physical properties such as density and water absorption studied before and after CNF incorporation. The microscopy images showed a uniform dispersion of CNF in the PU matrix of the prepared foams. Spectroscopic studies such as X-ray photoelectron and laser Raman spectroscopy suggested the existence of a tight intermolecular binding interaction between the carbon nanofibers and the PU matrix in the prepared composite foams. It found that the thermopower is directly dependent on the concentration of carbon nanofiber since, with rising concentration of 1%3%, the coefficient values increased from 1.2 μV/K to 11.9 μV/K respectively, a value higher than that of earlier report. This unique nanocomposite offers a new opportunity to recycle waste heat in portable/wearable electronics and other applications, which will broaden the development of low weight and mechanical flexibility.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.387
Times cited: 4
DOI: 10.1016/J.APSUSC.2018.01.088
|
“Supersonic Microwave Plasma: Potential and Limitations for Energy-Efficient CO2Conversion”. Vermeiren V, Bogaerts A, Journal Of Physical Chemistry C 122, 25869 (2018). http://doi.org/10.1021/acs.jpcc.8b08498
Abstract: Supersonic flows provide a high thermodynamic
nonequilibrium, which is crucial for energy-efficient conversion of
CO 2 in microwave plasmas and are therefore of great interest.
However, the effect of the flow on the chemical reactions is poorly
understood. In this work, we present a combined flow and plasma
chemical kinetics model of a microwave CO 2 plasma in a Laval
nozzle setup. The effects of the flow field on the different dissociation
and recombination mechanisms, the vibrational distribution, and the
vibrational transfer mechanism are discussed. In addition, the effect
of experimental parameters, like position of power deposition, outlet
pressure, and specific energy input, on the CO 2 conversion and
energy efficiency is examined. The short residence time of the gas in
the plasma region, the shockwave, and the maximum critical heat,
and thus power, that can be added to the flow to avoid thermal
choking are the main obstacles to reaching high energy efficiencies.
Keywords: A1 Journal Article; Plasma, laser ablation and surface modeling Antwerp (PLASMANT) ;
Impact Factor: 4.536
Times cited: 5
DOI: 10.1021/acs.jpcc.8b08498
|
“Role of the relative humidity and the Cd/Zn stoichiometry in the photooxidation process of cadmium yellows (CdS/Cd1-xZnxS) in oil paintings”. Monico L, Chieli A, De Meyer S, Cotte M, de Nolf W, Falkenberg G, Janssens K, Romani A, Miliani C, Chemistry: a European journal 24, 11584 (2018). http://doi.org/10.1002/CHEM.201801503
Abstract: Cadmium yellows (CdYs) refer to a family of cadmium sulfide pigments, which have been widely used by artists since the late 19th century. Despite being considered stable, they are suffering from discoloration in iconic paintings, such as Joy of Life by Matisse, Flowers in a blue vase by Van Gogh, and The Scream by Munch, most likely due to the formation of CdSO4 center dot nH(2)O. The driving factors of the CdYs degradation and how these affect the overall process are still unknown. Here, we study a series of oil mock-up paints made of CdYs of different stoichiometry (CdS/Cd0.76Zn0.24S) and crystalline structure (hexagonal/ cubic) before and after aging at variable relative humidity under exposure to light and in darkness. Synchrotron radiation-based X-ray methods combined with UV-Vis and FTIR spectroscopy show that: 1) Cd0.76Zn0.24S is more susceptible to photooxidation than CdS; both compounds can act as photocatalysts for the oil oxidation. 2) The photooxidation of CdS/Cd0.76Zn0.24S to CdSO4 center dot nH(2)O is triggered by moisture. 3) The nature of alteration products depends on the aging conditions and the Cd/Zn stoichiometry. Based on our findings, we propose a scheme for the mechanism of the photocorrosion process and the photocatalytic activity of CdY pigments in the oil binder. Overall, our results form a reliable basis for understanding the degradation of CdS-based paints in artworks and contribute towards developing better ways of preserving them for future generations.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 5.317
Times cited: 5
DOI: 10.1002/CHEM.201801503
|
“Enhanced stability of single-layer w-Gallenene through hydrogenation”. Badalov SV, Yagmurcukardes M, Peeters FM, Sahin H, The journal of physical chemistry: C : nanomaterials and interfaces 122, 28302 (2018). http://doi.org/10.1021/ACS.JPCC.8B07353
Abstract: Using density functional theory based first-principles calculations, the effect of surface hydrogenation on the structural, dynamical, electronic, and mechanical properties of monolayer washboard-gallenene (w-gallenene) is investigated. It is found that the dynamically stabilized strained monolayer of w-gallenene has a metallic nonmagnetic ground state. Both one-sided and two-sided hydrogenations of w-gallenene suppress its dynamical instability even when unstrained. Unlike one-sided hydrogenated monolayer w-gallenene (os-w-gallenene), two-sided hydrogenated monolayer w-gallenene (ts-w-gallenene) possesses the same crystal structure as w-gallenene. Electronic band structure calculations reveal that monolayers of hydrogenated derivatives of w-gallenene exhibit also metallic nonmagnetic ground state. Moreover, the linear-elastic constants, in-plane stiffness and Poisson ratio, are enhanced by hydrogenation, which is opposite to the behavior of other hydrogenated monolayer crystals. Furthermore, monolayer w-gallenene and ts-w-gallenene remain dynamically stable up to relatively higher biaxial strains as compared to borophene. With its enhanced dynamical stability, robust metallic character, and enhanced linear-elastic properties, hydrogenated monolayer w-gallenene is a potential candidate for nanodevice applications as a two-dimensional flexible metal.
Keywords: A1 Journal article; Engineering sciences. Technology; Condensed Matter Theory (CMT)
Impact Factor: 4.536
Times cited: 20
DOI: 10.1021/ACS.JPCC.8B07353
|
“MXenes/graphene heterostructures for Li battery applications : a first principles study”. Aierken Y, Sevik C, Gulseren O, Peeters FM, Çakir D, Journal of materials chemistry A : materials for energy and sustainability 6, 2337 (2018). http://doi.org/10.1039/C7TA09001C
Abstract: MXenes are the newest class of two-dimensional (2D) materials, and they offer great potential in a wide range of applications including electronic devices, sensors, and thermoelectric and energy storage materials. In this work, we combined the outstanding electrical conductivity, that is essential for battery applications, of graphene with MXene monolayers (M2CX2 where M = Sc, Ti, V and X = OH, O) to explore its potential in Li battery applications. Through first principles calculations, we determined the stable stacking configurations of M2CX2/graphene bilayer heterostructures and their Li atom intercalation by calculating the Li binding energy, diffusion barrier and voltage. We found that: (1) for the ground state stacking, the interlayer binding is strong, yet the interlayer friction is small; (2) Li binds more strongly to the O-terminated monolayer, bilayer and heterostructure MXene systems when compared with the OHterminated MXenes due to the H+ induced repulsion to the Li atoms. The binding energy of Li decreases as the Li concentration increases due to enhanced repulsive interaction between the positively charged Li ions; (3) Ti2CO2/graphene and V2CO2/graphene heterostructures exhibit large Li atom binding energies making them the most promising candidates for battery applications. When fully loaded with Li atoms, the binding energy is -1.43 eV per Li atom and -1.78 eV per Li atom for Ti2CO2/graphene and V2CO2/graphene, respectively. These two heterostructures exhibit a nice compromise between storage capacity and kinetics. For example, the diffusion barrier of Li in Ti2CO2/graphene is around 0.3 eV which is comparable to that of graphite. Additionally, the calculated average voltages are 1.49 V and 1.93 V for Ti2CO2/graphene and V2CO2/graphene structures, respectively; (4) a small change in the in-plane lattice parameters (<1%), interatomic bond lengths and interlayer distances (<0.5 angstrom) proves the stability of the heterostructures against Li intercalation, and the impending phase separation into constituent layers and capacity fading during charge-discharge cycles in real battery applications; (5) as compared to bare M2CX2 bilayers, M2CX2/graphene heterostructures have lower molecular mass, offering high storage capacity; (6) the presence of graphene ensures good electrical conductivity that is essential for battery applications. Given these advantages, Ti2CO2/graphene and V2CO2/graphene heterostructures are predicted to be promising for lithium-ion battery applications.
Keywords: A1 Journal article; Engineering sciences. Technology; Condensed Matter Theory (CMT)
Impact Factor: 8.867
Times cited: 131
DOI: 10.1039/C7TA09001C
|
“Flux quantization and Aharonov-Bohm effect in superconducting rings”. Kenawy A, Magnus W, Sorée B, Journal of superconductivity and novel magnetism 31, 1351 (2018). http://doi.org/10.1007/S10948-017-4369-X
Abstract: Superconductivity is a macroscopic coherent state exhibiting various quantum phenomena such as magnetic flux quantization. When a superconducting ring is placed in a magnetic field, a current flows to expel the field from the ring and to ensure that the enclosed flux is an integer multiple of h/(2|e|). Although the quantization of magnetic flux in ring structures is extensively studied in literature, the applied magnetic field is typically assumed to be homogeneous, implicitly implying an interplay between field expulsion and flux quantization. Here, we propose to decouple these two effects by employing an Aharonov-Bohm-like structure where the superconducting ring is threaded by a magnetic core (to which the applied field is confined). Although the magnetic field vanishes inside the ring, the formation of vortices takes place, corresponding to a change in the flux state of the ring. The time evolution of the density of superconducting electrons is studied using the time-dependent Ginzburg-Landau equations.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 1.18
DOI: 10.1007/S10948-017-4369-X
|
“Enhancement of plasma generation in catalyst pores with different shapes”. Zhang Y-R, Neyts EC, Bogaerts A, Plasma sources science and technology 27, 055008 (2018). http://doi.org/10.1088/1361-6595/aac0e4
Abstract: Plasma generation inside catalyst pores is of utmost importance for plasma catalysis, as the existence of plasma species inside the pores affects the active surface area of the catalyst available to the plasma species for catalytic reactions. In this paper, the electric field enhancement, and thus the plasma production inside catalyst pores with different pore shapes is studied with a two-dimensional fluid model. The results indicate that the electric field will be significantly enhanced near tip-like structures. In a conical pore with small opening, the strongest electric field appears at the opening and bottom corners of the pore, giving rise to a prominent ionization rate throughout the pore. For a cylindrical pore, the electric field is only enhanced at the bottom corners of the pore, with lower absolute value, and thus the ionization rate inside the pore is only slightly enhanced. Finally, in a conical pore with large opening, the electric field is characterized by a maximum at the bottom of the pore, yielding a similar behavior for the ionization rate. These results demonstrate that the shape of the pore has a significantly influence on the electric field enhancement, and thus modifies the plasma properties.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 3.302
Times cited: 11
DOI: 10.1088/1361-6595/aac0e4
|
“Single Atom Detection from Low Contrast-to-Noise Ratio Electron Microscopy Images”. Fatermans J, den Dekker A J, Müller-Caspary K, Lobato I, O’Leary C M, Nellist P D, Van Aert S, Physical review letters 121, 056101 (2018). http://doi.org/10.1103/PhysRevLett.121.056101
Abstract: Single atom detection is of key importance to solving a wide range of scientific and technological problems. The strong interaction of electrons with matter makes transmission electron microscopy one of the most promising techniques. In particular, aberration correction using scanning transmission electron microscopy has made a significant step forward toward detecting single atoms. However, to overcome radiation damage, related to the use of high-energy electrons, the incoming electron dose should be kept low enough. This results in images exhibiting a low signal-to-noise ratio and extremely weak contrast, especially for light-element nanomaterials. To overcome this problem, a combination of physics-based model fitting and the use of a model-order selection method is proposed, enabling one to detect single atoms with high reliability.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 8.462
Times cited: 6
DOI: 10.1103/PhysRevLett.121.056101
|
“Nature of the Positron State in CdSe Quantum Dots”. Shi W, Callewaert V, Barbiellini B, Saniz R, Butterling M, Egger W, Dickmann M, Hugenschmidt C, Shakeri B, Meulenberg R W, Brück E, Partoens B, Bansil A, Eijt SW H, Physical review letters 121, 057401 (2018). http://doi.org/10.1103/PhysRevLett.121.057401
Abstract: Previous studies have shown that positron-annihilation spectroscopy is a highly sensitive probe of the electronic structure and surface composition of ligand-capped semiconductor quantum dots (QDs) embedded in thin films. The nature of the associated positron state, however, whether the positron is confined inside the QDs or localized at their surfaces, has so far remained unresolved. Our positron-annihilation lifetime spectroscopy studies of CdSe QDs reveal the presence of a strong lifetime component in the narrow range of 358–371 ps, indicating abundant trapping and annihilation of positrons at the surfaces of the QDs. Furthermore, our ab initio calculations of the positron wave function and lifetime employing a recent formulation of the weighted density approximation demonstrate the presence of a positron surface state and predict positron lifetimes close to experimental values. Our study thus resolves the long-standing question regarding the nature of the positron state in semiconductor QDs and opens the way to extract quantitative information on surface composition and ligand-surface interactions of colloidal semiconductor QDs through highly sensitive positron-annihilation techniques.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 8.462
Times cited: 6
DOI: 10.1103/PhysRevLett.121.057401
|
“Atomic-scale identification of novel planar defect phases in heteroepitaxial YBa2Cu3O7-\delta thin films”. Gauquelin N, Zhang H, Zhu G, Wei JYT, Botton GA, AIP advances 8, 055022 (2018). http://doi.org/10.1063/1.5011761
Abstract: We have discovered two novel types of planar defects that appear in heteroepitaxial YBa2Cu3O7-delta(YBCO123) thin films, grown by pulsed-laser deposition (PLD) either with or without a La2/3Ca1/3MnO3 (LCMO) overlayer, using the combination of highangle annular dark-field scanning transmission electron microscopy (HAADF-STEM) imaging and electron energy loss spectroscopy (EELS) mapping for unambiguous identification. These planar lattice defects are based on the intergrowth of either a BaO plane between two CuO chains or multiple Y-O layers between two CuO2 planes, resulting in non-stoichiometric layer sequences that could directly impact the high-Tc superconductivity. (C) 2018 Author(s).
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.568
Times cited: 1
DOI: 10.1063/1.5011761
|
“Thermal recrystallization of short-range ordered WS2 films”. Heyne MH, de Marneffe J-F, Radu I, Neyts EC, De Gendt S, Journal of vacuum science and technology: A: vacuum surfaces and films 36, 05g501 (2018). http://doi.org/10.1116/1.5036654
Abstract: The integration of van der Waals materials in nanoelectronic devices requires the deposition of few-layered MX2 films with excellent quality crystals covering a large area. In recent years, astonishing progress in the monolayer growth of WS2 and MoS2 was demonstrated, but multilayer growth resulted often in separated triangular or hexagonal islands. These polycrystalline films cannot fully employ the specific MX2 properties since they are not connected in-plane to the other domains. To coalesce separated islands, ultrahigh-temperature postdeposition anneals in H2S are applied, which are not compatible with bare silicon substrates. Starting from the deposition of stoichiometric short-ordered films, the present work studies different options for subsequent high-temperature annealing in an inert atmosphere to form crystalline films with large grains from stoichiometric films with small grains. The rapid thermal annealing, performed over a few seconds, is compared to excimer laser annealing in the nanosecond range, which are both able to crystallize the thin WS2. The WS2 recrystallization temperature can be lowered using metallic crystallization promoters (Co and Ni). The best result is obtained using a Co cap, due to the circumvention of Co and S binary phase formation below the eutectic temperature. The recrystallization above a critical temperature is accompanied by sulfur loss and 3D regrowth. These undesired effects can be suppressed by the application of a dielectric capping layer prior to annealing. A SiO2 cap can suppress the sulfur loss successfully during annealing and reveals improved material quality in comparison to noncapped films Published by the AVS.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 1.374
Times cited: 2
DOI: 10.1116/1.5036654
|
“On the evolution of strain and electrical properties in as-grown and annealed Si:P epitaxial films for source-drain stressor applications”. Dhayalan SK, Kujala J, Slotte J, Pourtois G, Simoen E, Rosseel E, Hikavyy A, Shimura Y, Loo R, Vandervorst W, ECS journal of solid state science and technology 7, P228 (2018). http://doi.org/10.1149/2.0071805JSS
Abstract: Heavily P doped Si:P epitaxial layers have gained interest in recent times as a promising source-drain stressor material for n type FinFETs (Fin Field Effect Transistors). They are touted to provide excellent conductivity as well as tensile strain. Although the as-grown layers do provide tensile strain, their conductivity exhibits an unfavorable behavior. It reduces with increasing P concentration (P > 1E21 at/cm(3)), accompanied by a saturation in the active carrier concentration. Subjecting the layers to laser annealing increases the conductivity and activates a fraction of P atoms. However, there is also a concurrent reduction in tensile strain (<1%). Literature proposes the formation of local semiconducting Si3P4 complexes to explain the observed behaviors in Si:P [Z. Ye et al., ECS Trans., 50(9) 2013, p. 1007-10111. The development of tensile strain and the saturation in active carrier is attributed to the presence of local complexes while their dispersal on annealing is attributed to strain reduction and increase in active carrier density. However, the existence of such local complexes is not proven and a fundamental void exists in understanding the structure-property correlation in Si:P films. In this respect, our work investigates the reason behind the evolution of strain and electrical properties in the as-grown and annealed Si:P epitaxial layers using ab-initio techniques and corroborate the results with physical characterization techniques. It will be shown that the strain developed in Si:P films is not due to any specific complexes while the formation of Phosphorus-vacancy complexes will be shown responsible for the carrier saturation and the increase in resistivity in the as-grown films. Interstitial/precipitate formation is suggested to be a reason for the strain loss in the annealed films. (C) The Author(s) 2018. Published by ECS.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 1.787
Times cited: 4
DOI: 10.1149/2.0071805JSS
|
“Exciton Fine Structure and Lattice Dynamics in InP/ZnSe Core/Shell Quantum Dots”. Brodu A, Ballottin MV, Buhot J, van Harten EJ, Dupont D, La Porta A, Prins PT, Tessier MD, Versteegh MAM, Zwiller V, Bals S, Hens Z, Rabouw FT, Christianen PCM, de Donega CM, Vanmaekelbergh D, ACS Photonics 5, 3353 (2018). http://doi.org/10.1021/ACSPHOTONICS.8B00615
Abstract: Nanocrystalline InP quantum dots (QDs) hold promise for heavy-metal-free optoelectronic applications due to their bright and size tunable emission in the visible range. Photochemical stability and high photoluminescence (PL) quantum yield are obtained by a diversity of epitaxial shells around the InP core. To understand and optimize the emission line shapes, the exciton fine structure of InP core/shell QD systems needs be investigated. Here, we study the exciton fine structure of InP/ZnSe core/shell QDs with core diameters ranging from 2.9 to 3.6 nm (PL peak from 2.3 to 1.95 eV at 4 K). PL decay measurements as a function of temperature in the 10 mK to 300 K range show that the lowest exciton fine structure state is a dark state, from which radiative recombination is assisted by coupling to confined acoustic phonons with energies ranging from 4 to 7 meV, depending on the core diameter. Circularly polarized fluorescence line-narrowing (FLN) spectroscopy at 4 K under high magnetic fields (up to 30 T) demonstrates that radiative recombination from the dark F = +/- 2 state involves acoustic and optical phonons, from both the InP core and the ZnSe shell. Our data indicate that the highest intensity FLN peak is an acoustic phonon replica rather than a zero-phonon line, implying that the energy separation observed between the F = +/- 1 state and the highest intensity peak in the FLN spectra (6 to 16 meV, depending on the InP core size) is larger than the splitting between the dark and bright fine structure exciton states.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 6.756
Times cited: 40
DOI: 10.1021/ACSPHOTONICS.8B00615
|
“Technoques and applications of Surface-Enhanced Raman Scattering Spectroscopy (SERSS) focused on cultural heritage”. Kuckova S, Hamidi-Asl E, Matulkova I, Hynek R, De Wael K, Sanyova J, Janssens K, Chemické, listy 112, 312 (2018)
Abstract: The review is devoted to a modern method of vibrational spectroscopy – surface enhanced Raman spectroscopy Its principle and some of its special variants (imunnoSERS and TERS (Tip-Enhanced Raman Spectroscopy)) are described m a simpinified manner Wide application possibilities are demonstrated on selected examples from its application m culturinl heritage.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 0.387
|
“External costs from fossil electricity generation : a review of the applied impact pathway approach”. Jorli M, Van Passel S, Saghdel HS, Energy &, Environment 29, 635 (2018). http://doi.org/10.1177/0958305X18761616
Abstract: This paper reviews and compares 11 studies that have estimated external costs of fossil electricity generation by benefits transfer. These studies include 13 countries and most of these countries are developing countries. The impact pathway approach is applied to estimate the environmental impact arising from fossil fuel-fired power plant's air emission and the related damages on human health. The estimated damages are used to value the monetary external costs from fossil fuel electricity generation. The estimated external costs in the 13 countries vary from 0.51 to 213.5 USD (2005) per MWh due to differences in fossil fuel quality, location, technology, and efficiency of power plants and additionally differences in assumptions, monetization values, and impact estimations. Accounting for these externalities can indicate the actual costs of fossil energy. The results can be applied by policy makers to take measures to avoid additional costs and to apply newer and cleaner energy sources. The described methods in the selected studies for estimating the external costs with respect to incomplete local data can be applied as a useful example for other developing countries.
Keywords: A1 Journal article; Engineering Management (ENM)
Impact Factor: 0.302
Times cited: 3
DOI: 10.1177/0958305X18761616
|
“Hierarchically dual-mesoporous TiO2 microspheres for enhanced photocatalytic properties and lithium storage”. Xiao S, Lu Y, Xiao B-Y, Wu L, Song J-P, Xiao Y-X, Wu S-M, Hu J, Wang Y, Chang G-G, Tian G, Lenaerts S, Janiak C, Yang X-Y, Su B-L, Chemistry: a European journal 24, 13246 (2018). http://doi.org/10.1002/CHEM.201801933
Abstract: Hierarchically dual‐mesoporous TiO2 microspheres have been synthesized via a solvothermal process in the presence of 1‐butyl‐3‐methylmidazolium tetrafluoroborate ([BMIm][BF4]) and diethylenetriamine (DETA) as co‐templates. Secondary mesostructured defects in the hierarchical TiO2 microspheres produce the oxygen vacancies, which not only significantly enhance the photocatalytic activity on degrading methyl blue (over 1.7 times to P25) and acetone (over 2.9 times of P25), but which also are beneficial for lithium storage. Moreover, we propose a mechanism to obtain a better understanding of the role of dual mesoporosity of TiO2 microspheres for enhancing the molecular diffusion, ion transportation and electron transformation.
Keywords: A1 Journal article; Engineering sciences. Technology; Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 5.317
Times cited: 6
DOI: 10.1002/CHEM.201801933
|
“Thermal properties of the mixed spin-1 and spin-3/2 Ising ferrimagnetic system with two different random single-ion anisotropies”. Pereira JRV, Tunes TM, De Arruda AS, Godoy M, Physica: A : theoretical and statistical physics 500, 265 (2018). http://doi.org/10.1016/J.PHYSA.2018.02.085
Abstract: In this work, we have performed Monte Carlo simulations to study a mixed spin-1 and spin-3/2 Ising ferrimagnetic system on a square lattice with two different random single-ion anisotropies. This lattice is divided in two interpenetrating sublattices with spins S-A = 1 in the sublattice A and S-B = 3/2 in the sublattice B. The exchange interaction between the spins on the sublattices is antiferromagnetic (J < 0). We used two random single-ion anisotropies, D-i(A) and D-j(B), on the sublattices A and B, respectively. We have determined the phase diagram of the model in the critical temperature T-c versus strength of the random single-ion anisotropy D plane and we shown that it exhibits only second-order phase transition lines. We also shown that this system displays compensation temperatures for some cases of the random single-ion distribution. (C) 2018 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 2.243
Times cited: 3
DOI: 10.1016/J.PHYSA.2018.02.085
|
“Tailoring the Ti-C nanoprecipitate population and microstructure of titanium stabilized austenitic steels”. Cautaerts N, Delville R, Stergar E, Schryvers D, Verwerft M, Journal of nuclear materials 507, 177 (2018). http://doi.org/10.1016/J.JNUCMAT.2018.04.041
Abstract: The present work reports on the microstructural evolution of a new heat of 24% cold worked austenitic DIN 1.4970 (15-15Ti) nuclear cladding steel subjected to ageing heat treatments of varying duration between 500 and 800 degrees C (by steps of 100 degrees C). The primary aim was studying the finely dispersed Ti-C nanoprecipitate population, which are thought to be beneficial for creep and swelling resistance during service. Their size distribution and number density were estimated through dark field imaging and bright field Moire imaging techniques in the transmission electron microscope. Nanoprecipitates formed at and above 600 degrees C, which is a lower temperature than previously reported. The observed nucleation, growth and coarsening behavior of the nanoprecipitates were consistent with simple diffusion arguments. The formation of nanoprecipitates coincided with significant dissociation of dislocations as evidenced by weak beam dark field imaging. Possible mechanisms, including Silcock's stacking fault growth model and Suzuki segregation, are discussed. Recrystallization observed after extended ageing at 800 degrees C caused the redissolution of nanoprecipitates. Large primary Ti(C,N) and (Ti,Mo)C precipitates that occur in the as-received material, and M23C6 precipitates that nucleate on grain boundaries at low temperatures were also characterized by a selective dissolution procedure involving filtration, X-ray diffraction and quantitative Rietveld refinement. The partitioning of key elements between the different phases was derived by combining these findings and was consistent with thermodynamic considerations and the processing history of the steel. (C) 2018 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.048
Times cited: 1
DOI: 10.1016/J.JNUCMAT.2018.04.041
|
“Negative magnetoresistance in thin superconducting films with parallel orientation of current and magnetic field”. Vodolazov DY, Berdiyorov G, Peeters FM, Physica: C : superconductivity 552, 64 (2018). http://doi.org/10.1016/J.PHYSC.2018.07.002
Abstract: Thin superconducting films can exhibit negative magnetoresistance when an in-plane external magnetic field is aligned parallel with the transport current. We explain this effect as due to appearance of parallel vortices in the plain of the film at the first critical magnetic field H-c1 which leads to an enhancement of the superconducting properties and impedes the motion of the current induced perpendicular vortices. Our theoretical results are based on a numerical solution of the time-dependent and stationary 3D Ginzburg-Landau equations.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 1.404
Times cited: 6
DOI: 10.1016/J.PHYSC.2018.07.002
|
“The role of MOFs in Thin-Film Nanocomposite (TFN) membranes”. Van Goethem C, Verbeke R, Pfanmoeller M, Koschine T, Dickmann M, Timpel-Lindner T, Egger W, Bals S, Vankelecom IFJ, Journal of membrane science 563, 938 (2018). http://doi.org/10.1016/J.MEMSCI.2018.06.040
Abstract: Incorporation of MOFs in interfacially polymerized Thin-Film Nanocomposite (TFN) membranes has widely been shown to result in increased membrane performance. However, the exact functioning of these membranes is poorly understood as large variability in permeance increase, filler incorporation and rejection changes can be observed in literature. The synthesis and functioning of TFN membranes (herein exemplified by ZIF-8 filled polyamide (PA) membranes prepared via the EFP method) was investigated via targeted membrane synthesis and thorough characterization via STEM-EDX, XRD and PALS. It is hypothesized that the acid generated during the interfacial polymerization (IP) at least partially degrades the crystalline, acid-sensitive ZIF-8 and that this influences the membrane formation (through so-called secondary effects, i.e. not strictly linked to the pore morphology of the MOF). Nanoscale HAADF-STEM imaging and STEM-EDX Zn-mapping revealed no ZIF-8 particles but rather the presence of randomly shaped regions with elevated Zn-content. Also XRD failed to show the presence of crystalline areas in the composite PA films. As the addition of the acid-quenching TEA led to an increase in the diffraction signal observed in XRD, the role of the acid was confirmed. The separate addition of dissolved Zn2+ to the synthesis of regular TFC membranes showed an increase in permeance while losing some salt retention, similar to observations regularly made for TFN membranes. While the addition of a porous material to a TFC membrane is a straightforward concept, all obtained results indicate that the synthesis and performance of such composite membranes is often more complex than commonly accepted.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.035
Times cited: 84
DOI: 10.1016/J.MEMSCI.2018.06.040
|