“Effect of selenium content of CuInSex alloy nanopowder precursors on recrystallization of printed CuInSe2 absorber layers during selenization heat treatment”. E Zaghi A, Buffière M, Koo J, Brammertz G, Batuk M, Verbist C, Hadermann J, Kim WK, Meuris M, Poortmans J, Vleugels J;, Thin solid films : an international journal on the science and technology of thin and thick films , 1 (2014). http://doi.org/10.1016/j.tsf.2014.10.003
Abstract: Polycrystalline CuInSe2 semiconductors are efficient light absorber materials for thin film solar cell technology, whereas printing is one of the promising low cost and non-vacuum approaches for the fabrication of thin film solar cells. The printed precursors are transformed into a dense polycrystalline CuInSe2 semiconductor film via thermal treatment in ambient selenium atmosphere (selenization). In this study, the effect of the selenium content in high purity mechanically synthesized CuInSex (x = 2, 1.5, 1 or 0.5) alloy precursors on the recrystallization of the CuInSe2 phase during the selenization process was investigated. The nanostructure and phase variation of CuInSex nanopowders were investigated by different characterization techniques. The recrystallization process of the 12 μm thick CuInSex coatings into the CuInSe2 phase during selenization in selenium vapor was investigated via in-situ high temperature X-ray diffraction. The CuInSex precursors with lower selenium content showed a more pronounced phase conversion into CuInSe2 compared to the higher selenium content CuInSex precursors. Moreover, the CuInSex (x = 0.5 and 1) precursor resulted in a denser polycrystalline CuInSe2 semiconductor film with larger crystals. This could be attributed to a more intensive atomic interdiffusion within the CuInSex precursor system compared to a CuInSe2 phase precursor, and the formation of intermediate CuSe and CuSe2 fluxing phases during selenization.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.879
Times cited: 7
DOI: 10.1016/j.tsf.2014.10.003
|
|
|
“High magnetic ordering temperature in the perovskites Sr4-xLaxFe3ReO12 (x=0.0, 1.0, 2.0)”. Retuerto M, Li MR, Go YB, Ignatov A, Croft M, Ramanujachary KV, Herber RH, Nowik I, Hodges JP, Dachraoui W, Hadermann J, Greenblatt M;, Journal of solid state chemistry 194, 48 (2012). http://doi.org/10.1016/j.jssc.2012.06.031
Abstract: A series of perovskites Sr4−xLaxFe3ReO12 (x=0.0, 1.0, 2.0) has been prepared by wet chemistry methods. The structure analyses by powder X-ray and neutron diffraction and electron microscopy show that these compounds adopt simple perovskite structures without cation ordering over the B sites: tetragonal (I4/mcm) for x=0.0 and 1.0 and orthorhombic (Pbmn) for x=2.0. The oxidation states of the cations in the compound with x=0.0 appear to be Fe3+/4+ and Re7+ and decrease for both with La substitution as evidenced by X-ray absorption spectroscopy. All the compounds are antiferromagnetically ordered above room temperature, as demonstrated by Mössbauer spectroscopy and the magnetic structures, which were determined by powder neutron diffraction. The substitution of Sr by La strongly affects the magnetic properties with an increase of TN up to ∼750 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 9
DOI: 10.1016/j.jssc.2012.06.031
|
|
|
“HREM study of fluorinated Nd2CuO4”. Hadermann J, Van Tendeloo G, Abakumov AM, Rozova MG, Antipov EV, Journal of solid state chemistry 157, 56 (2001). http://doi.org/10.1006/jssc.2000.9038
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 7
DOI: 10.1006/jssc.2000.9038
|
|
|
“The metastable Ni7\pm xS6 and mixed Ni6\pm x(S1-ySey)5 phases”. Liu Y, Norén L, Withers RL, Hadermann J, Van Tendeloo G, Garcia-Garcia J, Journal of solid state chemistry 170, 351 (2003). http://doi.org/10.1016/S0022-4596(02)00123-8
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 5
DOI: 10.1016/S0022-4596(02)00123-8
|
|
|
“Novel, oxygen-deficient n=3 RP-member Sr3NdFe3O9-\delta and its topotactic derivatives”. Pelloquin D, Hadermann J, Giot M, Caignaert V, Michel C, Hervieu M, Raveau B, Chemistry of materials 16, 1715 (2004). http://doi.org/10.1021/cm030351n
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 24
DOI: 10.1021/cm030351n
|
|
|
“Structural changes in fluorinated T{'} and T* phases”. Hadermann J, Abakumov AM, Lebedev OI, Antipov EV, Van Tendeloo G, , 193 (2000)
Keywords: P3 Proceeding; Electron microscopy for materials research (EMAT)
|
|
|
“Structural transformations in the fluorinated T* phase”. Hadermann J, Abakumov AM, Lebedev OI, Van Tendeloo G, Rozova MG, Shpanchenko RV, Pavljuk BP, Kopnin EM, Antipov EV, Journal of solid state chemistry 147, 647 (1999). http://doi.org/10.1006/jssc.1999.8438
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 8
DOI: 10.1006/jssc.1999.8438
|
|
|
“Suppression of modulations in fluorinated Bi-2201 phases”. Hadermann J, Khasanova NR, Van Tendeloo G, Abakumov AM, Rozova MG, Alekseeva AM, Antipov EV, Journal of solid state chemistry 156, 445 (2001). http://doi.org/10.1006/jssc.2000.9020
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 8
DOI: 10.1006/jssc.2000.9020
|
|
|
“Synthesis and characterization of the reduced double-layer manganite Sr3Mn2O6+x”. Gillie LJ, Wright AJ, Hadermann J, Van Tendeloo G, Greaves C, Journal of solid state chemistry 175, 188 (2003). http://doi.org/10.1016/S0022-4596(03)00245-7
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 18
DOI: 10.1016/S0022-4596(03)00245-7
|
|
|
“Synthesis and characterization of the reduced single-layer manganite Sr2MnO3.5+x”. Gillie LJ, Wright AJ, Hadermann J, Van Tendeloo G, Greaves C, Journal of solid state chemistry 167, 145 (2002). http://doi.org/10.1006/jssc.2002.9636
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 25
DOI: 10.1006/jssc.2002.9636
|
|
|
“Synthesis and charactreization of the new Ln(2)FeMoO(7) (Ln = Y, Dy, Ho) compounds”. Veith GM, Lobanov MV, Emge TJ, Greenblatt M, Croft M, Stowasser F, Hadermann J, Van Tendeloo G, Journal of materials chemistry 14, 1623 (2004). http://doi.org/10.1039/b315028c
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 17
DOI: 10.1039/b315028c
|
|
|
“Synthesis and crystal structure of a new complex oxyfluoride La0.813Sr0.187Cu(o,F)3-\delta”. Abakumov AM, Hadermann J, Rozova MG, Pavljuk BP, Antipov EV, Lebedev OI, Van Tendeloo G, Journal of solid state cemistry 149, 189 (2000). http://doi.org/10.1006/jssc.1999.8521
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 8
DOI: 10.1006/jssc.1999.8521
|
|
|
“Synthesis and crystal structure of the novel Pb5Sb2MnO11 compound”. Abakumov AM, Rozova MG, Chizhov PS, Antipov EV, Hadermann J, Van Tendeloo G, Journal of solid state chemistry 177, 2855 (2004). http://doi.org/10.1016/j.jssc.2004.04.047
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 3
DOI: 10.1016/j.jssc.2004.04.047
|
|
|
“Synthesis and crystal structure of the Sr2MnGa(O,F)6 oxyfluorides”. Alekseeva AM, Abakumov AM, Rozova MG, Antipov EV, Hadermann J, Journal of solid state chemistry 177, 731 (2004). http://doi.org/10.1016/j.jssc.2003.09.002
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 23
DOI: 10.1016/j.jssc.2003.09.002
|
|
|
“Synthesis and investigation of novel Mn-based oxyfluoride Sr2Mn2O5-xF1+x”. Lobanov MV, Abakumov AM, Sidorova AV, Rozova MG, D'yachenko OG, Antipov EV, Hadermann J, Van Tendeloo G, Solid state sciences 4, 19 (2002). http://doi.org/10.1016/S1293-2558(01)01209-2
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.811
Times cited: 21
DOI: 10.1016/S1293-2558(01)01209-2
|
|
|
“Synthesis, cation ordering, and magnetic properties of the (Sb1-xPbx)2(Mn1-ySby)O4 solid solutions with the Sb2MnO4-type structure”. Abakumov AM, Rozova MG, Antipov EV, Hadermann J, Van Tendeloo G, Lobanov MV, Greenblatt M, Croft M, Tsiper EV, Llobet A, Lokshin KA, Zhao Y, Chemistry of materials 17, 1123 (2005). http://doi.org/10.1021/cm048791h
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 16
DOI: 10.1021/cm048791h
|
|
|
“Synthesis, crystal structure, and magnetic properties of new layered hexagonal perovskite Ba8Ta4Ru8/3Co2/3O24”. Kopnin EM, Belik AA, Shpanchenko RV, Antipov EV, Izumi F, Takayama-Muromachi E, Hadermann J, Journal of solid state chemistry 177, 3499 (2004). http://doi.org/10.1016/j.jssc.2004.04.032
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 1
DOI: 10.1016/j.jssc.2004.04.032
|
|
|
“Synthesis, crystal structure, and properties of KSbO3-type Bi3Mn1.9Te1.1O11”. Li MR, Retuerto M, Bok Go Y, Emge TJ, Croft M, Ignatov A, Ramanujachary KV, Dachraoui W, Hadermann J, Tang MB, Zhao JT, Greenblatt M;, Journal of solid state chemistry 197, 543 (2013). http://doi.org/10.1016/j.jssc.2012.07.038
Abstract: Single crystals of Bi3Mn1.9Te1.1O11 were prepared from NaCl+KCl flux. This compound adopts KSbO3-type crystal structure as evidenced by electron and single crystal X-ray diffraction analysis. The three-dimensional channel structure is formed by corner-sharing octahedral (Mn0.63Te0.37)2O10 dimers and two identical (Bi1)4(Bi2)2 interpenetrating lattices. The intra-dimer Mn/TeMn/Te distances in Bi3Mn1.9Te1.1O11 are short and are consistent with weak metalmetal interactions. The mixed oxidation state of manganese and the edge-sharing octahedral features are confirmed by X-ray near edge absorption spectroscopy measurements, which indicate Bi3(MnIII1.1MnIV0.8)TeVI1.1O11 with 57.7% Mn3+ and 42.3% Mn4+. The partial substitution of Te for Mn perturbs long-range magnetic interactions, thereby destroying the ferromagnetic ordering found in Bi3Mn3O11 (TC=150 K).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 13
DOI: 10.1016/j.jssc.2012.07.038
|
|
|
“Synthesis, structure and magnetic properties of the new mixed-valence vanadate Na2SrV3O9”. Shpanchenko RV, Chernaya VV, Antipov EV, Hadermann J, Kaul EE, Geibel C, Journal of solid state chemistry 173, 244 (2003). http://doi.org/10.1016/S0022-4596(03)00039-2
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 5
DOI: 10.1016/S0022-4596(03)00039-2
|
|
|
“Pb5Fe3TiO11Cl : a rare example of Ti(IV) in a square pyramidal oxygen coordination”. Batuk M, Batuk D, Abakumov AM, Hadermann J, Journal of solid state chemistry 215, 245 (2014). http://doi.org/10.1016/j.jssc.2014.04.002
Abstract: A new oxychloride Pb5Fe3TiO11Cl has been synthesized using the solid state method. Its crystal and magnetic structure was investigated in the 1.5550 K temperature range using electron diffraction, high angle annular dark field scanning transmission electron microscopy, atomic resolution energy dispersive X-ray spectroscopy, neutron and X-ray powder diffraction. At room temperature Pb5Fe3TiO11Cl crystallizes in the P4/mmm space group with the unit cell parameters a=3.91803(3) Å and c=19.3345(2) Å. Pb5Fe3TiO11Cl is a new n=4 member of the oxychloride perovskite-based homologous series An+1BnO3n−1Cl. The structure is built of truncated Pb3Fe3TiO11 quadruple perovskite blocks separated by CsCl-type Pb2Cl slabs. The perovskite blocks consist of two layers of (Fe,Ti)O6 octahedra sandwiched between two layers of (Fe,Ti)O5 square pyramids. The Ti4+ cations are preferentially located in the octahedral layers, however, the presence of a noticeable amount of Ti4+ in a five-fold coordination environment has been undoubtedly proven using neutron powder diffraction and atomic resolution compositional mapping. Pb5Fe3TiO11Cl is antiferromagnetically ordered below 450(10) K. The ordered Fe magnetic moments at 1.5 K are 4.06(4) μB and 3.86(5) μB on the octahedral and square-pyramidal sites, respectively.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 4
DOI: 10.1016/j.jssc.2014.04.002
|
|
|
“SrMn3O6: an incommensurate modulated tunnel structure”. Gillie LJ, Hadermann J, Pérez O, Martin C, Hervieu M, Suard E, Journal of solid state chemistry 177, 3383 (2004). http://doi.org/10.1016/j.jssc.2004.05.057
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 19
DOI: 10.1016/j.jssc.2004.05.057
|
|
|
“The interplay of microstructure and magnetism in La3Ni2SbO9”. Battle PD, Avdeev M, Hadermann J, Journal of solid state chemistry 220, 163 (2014). http://doi.org/10.1016/j.jssc.2014.08.024
Abstract: La3Ni2SbO9 adopts a perovskite-related structure in which the six-coordinate cation sites are occupied alternately by Ni2+ and a disordered arrangement of Ni2+/Sb5+. A polycrystalline sample has been studied by neutron diffraction in applied magnetic fields of 0 <= H/kOe <= 50 at 5 K. In 0 kOe, weak magnetic Bragg scattering consistent with the adoption of a G-type ferrimagnetic structure is observed; the ordered component of the magnetic moment was found to be 0.89(7) mu(B) per Ni2+ cation. This increased to 1.60(3) mu(B) in a field of 50 kOe. Transmission electron microscopy revealed variations in the Ni:Sb ratio across crystallites of the sample. It is proposed that these composition variations disrupt the magnetic superexchange interactions within the compound, leading to domain formation and a reduced average moment. The application of a magnetic field aligns the magnetisation vectors across the crystal and the average moment measured by neutron diffraction increases accordingly. The role played by variations in the local chemical composition in determining the magnetic properties invites comparison with the behaviour of relaxor ferroelectrics. (C) 2014 Elsevier Inc. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 13
DOI: 10.1016/j.jssc.2014.08.024
|
|
|
“Process variability in Cu2ZnSnSe4 solar cell devices: Electrical and structural investigations”. Brammertz G, Buffiere M, Verbist C, Bekaert J, Batuk M, Hadermann J, et al, The conference record of the IEEE Photovoltaic Specialists Conference
T2 –, IEEE 42nd Photovoltaic Specialist Conference (PVSC), JUN 14-19, 2015, New Orleans, LA (2015)
Abstract: We have fabricated 9.7% efficient Cu2ZnSnSe4/CdS/ZnO solar cells by H2Se selenization of sequentially sputtered metal layers. Despite the good efficiency obtained, process control appears to be difficult. In the present contribution we compare the electrical and physical properties of two devices with nominal same fabrication procedure, but 1% and 9.7% power conversion efficiency respectively. We identify the problem of the lower performing device to be the segregation of ZnSe phases at the backside of the sample. This ZnSe seems to be the reason for the strong bias dependent photocurrent observed in the lower performing devices, as it adds a potential barrier for carrier collection. The reason for the different behavior of the two nominally same devices is not fully understood, but speculated to be related to sputtering variability.
Keywords: P1 Proceeding; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
|
|
|
“Ferrimagnetism as a consequence of cation ordering in the perovskite LaSr2Cr2SbO9”. Hunter EC, Battle PD, Sena RP, Hadermann J, Journal of solid state chemistry 248, 96 (2017). http://doi.org/10.1016/J.JSSC.2017.01.024
Abstract: A polycrystalline sample of LaSr2Cr2SbO9 has been synthesised using a standard ceramic method and characterized by x-ray and neutron diffraction, magnetometry and electron microscopy. The perovskite-related compound crystallises in the triclinic space group I1 with unit cell parameters of a=5.5344(6) angstrom, b=5.5562(5) angstrom, c=7.8292(7) angstrom, a=89.986(12)degrees, beta=90.350(5)degrees and gamma=89.926(9)degrees at room temperature. The two crystallographically-distinct, six-coordinate cation sites are occupied by Cr3+ and Sb5+ in ratios of 0.868(2):0.132(2) and 0.462(2):0.538(2). Ac and de magnetometry revealed that LaSr2Cr2SbO9 is ferrimagnetic below 150 K with a magnetisation of similar to 1.25 mu(B) per formula unit in 50 kOe at 5 K. Neutron diffraction showed that the cations on the two sites order in a G-type arrangement with a mean Cr3+ moment of 2.17(1) mu(B) at 5 K, consistent with a magnetisation of 1.32 mu(B) per formula unit.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 14
DOI: 10.1016/J.JSSC.2017.01.024
|
|
|
“Gaining new insight into low-temperature aqueous photochemical solution deposited ferroelectric PbTiO3 films”. De Dobbelaere C, Lourdes Calzada M, Bretos I, Jimenez R, Ricote J, Hadermann J, Hardy A, Van Bael MK, Materials chemistry and physics 174, 28 (2016). http://doi.org/10.1016/J.MATCHEMPHYS.2016.02.047
Abstract: The nature of the low-temperature photochemical assisted formation process of ferroelectric lead titanate (PbTiO3) films is studied in the present work. Films are obtained by the deposition of an aqueous solution containing citric acid based (citrato) metal ion complexes with intrinsic UV activity. This UV activity is crucial for the aqueous photochemical solution deposition (aqueous PCSD) route being used. UV irradiation enhances the early decomposition of organics and results in improved electrical properties for the crystalline oxide film, even if the film is crystallized at low temperature. GATR-FTIR shows that UV irradiation promotes the decomposition of organic precursor components, resulting in homogeneous films if applied in the right temperature window during film processing. The organic content, morphology and crystallinity of the irradiated films, achieved at different processing atmospheres and temperatures, is studied and eventually correlated to the functional behavior of the obtained films. This is an important issue, as crystalline films obtained at low temperatures often lack ferroelectric responses. In this work, the film prepared in pure oxygen at the very low temperature of 400 degrees C and after an optimized UV treatment presents a significant remanent polarization value of P-r = 8.8 mu C cm(-2). This value is attributed to the better crystallinity, the larger grain size and the reduced porosity obtained thanks to the early film crystallization effectively achieved through the UV treatment in oxygen. (C) 2016 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.084
Times cited: 4
DOI: 10.1016/J.MATCHEMPHYS.2016.02.047
|
|
|
“Interplay of structural chemistry and magnetism in perovskites : a study of CaLn2Ni2WO9: Ln=La, Pr, Nd”. Chin C-M, Sena RP, Hunter EC, Hadermann J, Battle PD, Journal of solid state chemistry 251, 224 (2017). http://doi.org/10.1016/J.JSSC.2017.04.023
Abstract: Polycrystalline samples of CaLn(2)Ni(2)WO(9) (Ln=La, Pr, Nd) have been synthesized and characterised by a combination of X-ray and neutron diffraction, electron microscopy and magnetometry. Each composition adopts a perovskite-like structure with a similar to 5.50, b similar to 5.56, c similar to 7.78 angstrom beta similar to 90.1 degrees in space group P2(1)/n. Of the two crystallographically distinct six-coordinate sites, one is occupied entirely (Ln=Pr) or predominantly (Ln=La, Nd) by Ni2+ and the other by Ni2+ and W6+ in a ratio of approximately 1:2. None of the compounds shows long-range magnetic order at 5 K. The magnetometry data show that the magnetic moments of the Ni2+ cations form a spin glass below 30 K in each case. The Pr3+ moments in CaPr2Ni2WO9 also freeze but the Nd3+ moments in CaNd2Ni2WO9 do not. This behaviour is contrasted with that observed in other (A,A')B2B'O-9 perovskites.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 5
DOI: 10.1016/J.JSSC.2017.04.023
|
|
|
“Cobalt location in p-CoOxIn-SnO2 nanocomposites : correlation with gas sensor performances”. Vladimirova SA, Rumyantseva MN, Filatova DG, Chizhov AS, Khmelevsky NO, Konstantinova EA, Kozlovsky VF, Marchevsky AV, Karakulina OM, Hadermann J, Gaskov AM, Journal of alloys and compounds 721, 249 (2017). http://doi.org/10.1016/JJALLCOM.2017.05.332
Abstract: Nanocomposites CoOx/SnO2 based on tin oxide powders with different crystallinity have been prepared by wet chemical synthesis and characterized in detail by ICP-MS, XPS, EPR, XRD, HAADF-STEM imaging and EDX-STEM mapping. It was shown that cobalt is distributed differently between the bulk and surface of SnO2 nanocrystals, which depends on the crystallinity of the SnO2 matrix. The measurements of gas sensor properties have been carried out during exposure to CO (10 ppm), and H2S (2 ppm) in dry air. The decrease of sensor signal toward CO was attributed to high catalytic activity of Co3O4 leading to oxidation of carbon monoxide entirely on the surface of catalyst particles. The formation of a p-CoOx/n-SnO2 heterojunction results in high sensitivity of nanocomposites in H2S detection. The conductance significantly changed in the presence of H2S, which was attributed to the formation of metallic cobalt sulfide and removal of the p – n junction. (C) 2017 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
DOI: 10.1016/JJALLCOM.2017.05.332
|
|
|
“Magnetic properties of the 6H perovskite Ba3Fe2TeO9”. Tang Y, Sena RP, Aydeev M, Battle PD, Cadogan JM, Hadermann J, Hunter EC, Journal of solid state chemistry 253, 347 (2017). http://doi.org/10.1016/J.JSSC.2017.06.019
Abstract: A polycrystalline sample of Ba3Fe2TeO9 having the 6H perovskite structure has been prepared in a solid-state reaction and studied by a combination of electron microscopy, Mossbauer spectroscopy, magnetometry, X-ray diffraction and neutron diffraction. Partial ordering of Fe3+ and Te6+ cations occurs over the six-coordinate sites; the corner-sharing octahedra are predominantly occupied by the former and the face-sharing octahedra by a 1:1 mixture of the two. On cooling through the temperature range 18 < T/K < 295 an increasing number of spins join an antiferromagnetic backbone running through the structure while the remainder show complex relaxation effects. At 3 K an antiferromagnetic phase and a spin glass coexist.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 6
DOI: 10.1016/J.JSSC.2017.06.019
|
|
|
“Role of graphene inter layer on the formation of the MoS2 –, CZTS interface during growth”. Vishwakarma M, Thota N, Karakulina O, Hadermann J, Mehta BR, (icc-2017) (2018). http://doi.org/10.1063/1.5033000
Abstract: The growth of MoS2 layer near the Mo/CZTS interface during sulphurization process can have an impact on back contact cell parameters (series resistance and fill factor) depending upon the thickness or quality of MoS2. This study reports the dependence of the thickness of interfacial MoS2 layer on the growth of graphene at the interface between molybdenum back contact and deposited CZTS layer. The graphene layer reduces the accumulation of Zn/ZnS, Sn/SnO2 and formation of pores near the MoS2-CZTS interface. The use of graphene as interface layer can be potentially useful for improving the quality of Mo/MoS2/CZTS interface.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
Times cited: 1
DOI: 10.1063/1.5033000
|
|
|
“Compatibility of Zr₂AlC MAX phase-based ceramics with oxygen-poor, static liquid lead-bismuth eutectic”. Tunca B, Lapauw T, Callaert C, Hadermann J, Delville R, Caspi E'ad N, Dahlqvist M, Rosen J, Marshal A, Pradeep KG, Schneider JM, Vleugels J, Lambrinou K, Corrosion Science 171, 108704 (2020). http://doi.org/10.1016/J.CORSCI.2020.108704
Abstract: This work investigates the compatibility of Zr2AlC MAX phase-based ceramics with liquid LBE, and proposes a mechanism to explain the observed local Zr2AlC/LBE interaction. The ceramics were exposed to oxygen-poor (C-O <= 2.2 x 10(-10) mass%), static liquid LBE at 500 degrees C for 1000 h. A new Zr-2(Al,Bi,Pb)C MAX phase solid solution formed in-situ in the LBE-affected Zr2AlC grains. Out-of-plane ordering was favorable in the new solid solution, whereby A-layers with high and low-Bi/Pb contents alternated in the crystal structure, in agreement with first-principles calculations. Bulk Zr-2(Al,Bi,Pb)C was synthesized by reactive hot pressing to study the crystal structure of the solid solution by neutron diffraction.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 8.3
Times cited: 3
DOI: 10.1016/J.CORSCI.2020.108704
|
|