“Quantified contribution of β&Prime, and β&prime, precipitates to the strengthening of an aged Al–Mg–Si alloy”. Yang M, Chen H, Orekhov A, Lu Q, Lan X, Li K, Zhang S, Song M, Kong Y, Schryvers D, Du Y, Materials Science And Engineering A-Structural Materials Properties Microstructure And Processing 774, 138776 (2020). http://doi.org/10.1016/j.msea.2019.138776
Abstract: It is generally believed that β00 precipitates, rather than β0 precipitates, are the major strengthening precipitates in
aged Al–Mg–Si alloys. The reason for this difference is not well understood. To clarify this, two samples of the
same Al–Mg–Si alloy but with different aging states were prepared. The under-aged sample only contains nanoprecipitates
of the β00 type, while the peak-aged one contains nearly equal volumes of β00 and β0 precipitates. We
have, for the first time, separated the strengthening effect of the contribution from βʺ and βʹ precipitates,
respectively, by an indirect approach based on high-precision measurements of volume fractions, number densities,
sizes, proportions of the precipitates, their lattice strains, the composition and grain size of the matrix. The
β0 precipitates, which take 45.6% of the total precipitate volume in the peak-aged sample, contribute to the entire
precipitation strengthening by only 31.6%. The main reason why they are less useful compared to β00 precipitates
has been found to be associated with their smaller lattice strains relative to the matrix, which is 0.99% versus
2.10% (for β00 ).
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 6.4
DOI: 10.1016/j.msea.2019.138776
|
|
|
“Interfacial characteristics and cohesion mechanisms of linear friction welded dissimilar titanium alloys: Ti–5Al–2Sn–2Zr–4Mo–4Cr (Ti17) and Ti–6Al–2Sn–4Zr–2Mo (Ti6242)”. Boyat X, Ballat-Durand D, Marteau J, Bouvier S, Favergeon J, Orekhov A, Schryvers D, Materials characterization 158, 109942 (2019). http://doi.org/10.1016/j.matchar.2019.109942
Abstract: A detailed microstructural examination endeavoring to understand the interfacial phenomena yielding to cohesion
in solid-state assembling processes was performed. This study focuses on the transition zone of a dissimilar
titanium alloy joint obtained by Linear Friction Welding (LFW) the β-metastable Ti17 to the near-α
Ti6242. The transition zone delimitating both alloys is characterized by a sharp microstructure change from
acicular HCP (Hexagonal Close-Packed) α′ martensitic laths in the Ti6242 to equiaxed BCC β (Body-Centered
Cubic) subgrains in the Ti17; these α′ plates were shown to precipitate within prior-β subgrains remarkably more
rotated than the ones formed in the Ti17. Both α′ and β microstructures were found to be intermingled within
transitional subgrains demarcating a limited gradient from one chemical composition to the other. These peculiar
interfacial grains revealed that the cohesive mechanisms between the rubbing surfaces occurred in the
single-phase β domain under severe strain and high-temperature conditions. During the hot deformation process,
the mutual migration of the crystalline interfaces from one material to another assisted by a continuous dynamic
recrystallization process was identified as the main adhesive mechanism at the junction zone. The latter led to
successful cohesion between the rubbing surfaces. Once the reciprocating motion stopped, fast cooling caused
both materials to experience either a βlean→α′ or βlean→βmetastable transformation in the interfacial zone depending
on their local chemical composition. The limited process time and the subsequent hindered chemical
homogenization at the transition zone led to retaining the so-called intermingled α’/βm subgrains constituting
the border between both Ti-alloys.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.714
DOI: 10.1016/j.matchar.2019.109942
|
|
|
“Analysis of internal stress build-up during deposition of nanocrystalline Ni thin films using transmission electron microscopy”. Lumbeeck G, Delvaux A, Idrissi H, Proost J, Schryvers D, Thin solid films : an international journal on the science and technology of thin and thick films 707, 138076 (2020). http://doi.org/10.1016/j.tsf.2020.138076
Abstract: Ni thin films sputter-deposited at room temperature with varying Ar pressures were investigated with automated crystal orientation mapping in a transmission electron microscope to uncover the mechanisms controlling the internal stress build-up recorded in-situ during deposition. Large grains were found to induce behaviour similar to a stress-free nucleation layer. The measurements of grain size in most of the Ni thin films are in agreement with the island coalescence model. Low internal stress was observed at low Ar pressure and was explained by the presence of large grains. Relaxation of high internal stress was also noticed at the highest Ar pressure, which was attributed to a decrease of Σ3 twin boundary density due to a low deposition rate. The results provide insightful information to better understand the relationship between structural boundaries and the evolution of internal stress upon deposition of thin films.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1016/j.tsf.2020.138076
|
|
|
“Novel class of nanostructured metallic glass films with superior and tunable mechanical properties”. Ghidelli M, Orekhov A, Bassi AL, Terraneo G, Djemia P, Abadias G, Nord M, Béché, A, Gauquelin N, Verbeeck J, Raskin J-p, Schryvers D, Pardoen T, Idrissi H, Acta Materialia , 116955 (2021). http://doi.org/10.1016/j.actamat.2021.116955
Abstract: A novel class of nanostructured Zr50Cu50 (%at.) metallic glass films with superior and tunable mechanical
properties is produced by pulsed laser deposition. The process can be controlled to synthetize a wide
range of film microstructures including dense fully amorphous, amorphous embedded with nanocrystals
and amorphous nano-granular. A unique dense self-assembled nano-laminated atomic arrangement
characterized by alternating Cu-rich and Zr/O-rich nanolayers with different local chemical enrichment
and amorphous or amorphous-crystalline composite nanostructure has been discovered, while
significant in-plane clustering is reported for films synthetized at high deposition pressures. This unique
nanoarchitecture is at the basis of superior mechanical properties including large hardness and elastic
modulus up to 10 and 140 GPa, respectively and outstanding total elongation to failure (>9%), leading to
excellent strength/ductility balance, which can be tuned by playing with the film architecture. These
results pave the way to the synthesis of novel class of engineered nanostructured metallic glass films
with high structural performances attractive for a number of applications in microelectronics and
coating industry.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 27
DOI: 10.1016/j.actamat.2021.116955
|
|
|
““Branched&rdquo, structural transformation of the L12-Al3Zr phase manipulated by Cu substitution/segregation in the Al-Cu-Zr alloy system”. Ding L, Zhao M, Ehlers FJH, Jia Z, Zhang Z, Weng Y, Schryvers D, Liu Q, Idrissi H, Journal of materials science &, technology 185, 186 (2024). http://doi.org/10.1016/j.jmst.2023.11.015
Abstract: The effect of Cu on the evolution of the Al3Zr phase in an Al-Cu-Zr cast alloy during solution treatment at 500 °C has been thoroughly studied by combining atomic resolution high-angle annular dark-field scanning transmission electron microscopy, energy-dispersive X-ray spectroscopy and first-principles cal- culations. The heat treatment initially produces a pure L12-Al3Zr microstructure, allowing for about 13 % Cu to be incorporated in the dispersoid. Cu incorporation increases the energy barrier for anti-phase boundary (APB) activation, thus stabilizing the L12 structure. Additional heating leads to a Cu-induced “branched”path for the L12 structural transformation, with the latter process accelerated once the first APB has been created. Cu atoms may either (i) be repelled by the APBs, promoting the transformation to a Cu-poor D023 phase, or (ii) they may segregate at one Al-Zr layer adjacent to the APB, promoting a transformation to a new thermodynamically favored phase, Al4CuZr, formed when these segregation layers are periodically arranged. Theoretical studies suggest that the branching of the L12 transformation path is linked to the speed at which an APB is created, with Cu attraction triggered by a comparatively slow process. This unexpected transformation behavior of the L12-Al3Zr phase opens a new path to understanding, and potentially regulating the Al3Zr dispersoid evolution for high temperature applications.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 10.9
DOI: 10.1016/j.jmst.2023.11.015
|
|
|
“On the formation mechanisms of intragranular shear bands in olivine by stress-induced amorphization”. Idrissi H, Béché, A, Gauquelin N, Ul-Haq I, Bollinger C, Demouchy S, Verbeeck J, Pardoen T, Schryvers D, Cordier P, Acta materialia 239, 118247 (2022). http://doi.org/10.1016/J.ACTAMAT.2022.118247
Abstract: Intragranular amorphization shear lamellae are found in deformed olivine aggregates. The detailed trans-mission electron microscopy analysis of intragranular lamella arrested in the core of a grain provides novel information on the amorphization mechanism. The deformation field is complex and heteroge-neous, corresponding to a shear crack type instability involving mode I, II and III loading components. The formation and propagation of the amorphous lamella is accompanied by the formation of crystal defects ahead of the tip. These defects are geometrically necessary [001] dislocations, characteristics of high-stress deformation in olivine, and rotational nanodomains which are tentatively interpreted as disclinations. We show that these defects play an important role in dictating the path followed by the amorphous lamella. Stress-induced amorphization in olivine would thus result from a direct crystal-to -amorphous transformation associated with a shear instability and not from a mechanical destabilization due to the accumulation of high number of defects from an intense preliminary deformation. The pref-erential alignment of some lamellae along (010) is a proof of the lower ultimate mechanical strength of these planes.(c) 2022 The Authors. Published by Elsevier Ltd on behalf of Acta Materialia Inc. This is an open access article under the CC BY license ( http://creativecommons.org/licenses/by/4.0/ )
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 9.4
Times cited: 5
DOI: 10.1016/J.ACTAMAT.2022.118247
|
|
|
“Advanced electron microscopy characterisation of important precipitation and ordering phenomena in shape memory systems”. Schryvers D, Shape memory and superelasticity 1, 78 (2015). http://doi.org/10.1007/s40830-015-0006-3
Abstract: The present paper discusses some important aspects of precipitation and ordering in alloy systems that show a martensitic transformation and can or are used as shape memory or superelastic metallic systems. The precipitates are investigated by a variety of conventional and advanced electron microscopy techniques, including atomic resolution, 3D slice-and-view, energy loss spectroscopy etc. Depending on the system, such secondary phases can decrease the probability of a displacive transformation by changing the phase stability in the system, such as in the case of NiAl or NiTiPd, or can mechanically hinder the passage of the transformation interface, as in NiTiNb. On the other hand, properly controlling the nucleation and growth of some precipitates can strongly improve the properties of some types of materials, as is the case for the well-known Ni4Ti3 precipitates.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1007/s40830-015-0006-3
|
|
|
“Advanced three-dimensional electron microscopy techniques in the quest for better structural and functional materials”. Schryvers D, Cao S, Tirry W, Idrissi H, Van Aert S, Science and technology of advanced materials 14, 014206 (2013). http://doi.org/10.1088/1468-6996/14/1/014206
Abstract: After a short review of electron tomography techniques for materials science, this overview will cover some recent results on different shape memory and nanostructured metallic systems obtained by various three-dimensional (3D) electron imaging techniques. In binary NiTi, the 3D morphology and distribution of Ni4Ti3 precipitates are investigated by using FIB/SEM slice-and-view yielding 3D data stacks. Different quantification techniques will be presented including the principal ellipsoid for a given precipitate, shape classification following a Zingg scheme, particle distribution function, distance transform and water penetration. The latter is a novel approach to quantifying the expected matrix transformation in between the precipitates. The different samples investigated include a single crystal annealed with and without compression yielding layered and autocatalytic precipitation, respectively, and a polycrystal revealing different densities and sizes of the precipitates resulting in a multistage transformation process. Electron tomography was used to understand the interaction between focused ion beam-induced Frank loops and long dislocation structures in nanobeams of Al exhibiting special mechanical behaviour measured by on-chip deposition. Atomic resolution electron tomography is demonstrated on Ag nanoparticles in an Al matrix.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.798
Times cited: 6
DOI: 10.1088/1468-6996/14/1/014206
|
|
|
“Characterization of nickel silicides using EELS-based methods”. Verleysen E, Bender H, Richard O, Schryvers D, Vandervorst W, Journal of microscopy 240, 75 (2010). http://doi.org/10.1111/j.1365-2818.2010.03391.x
Abstract: The characterization of Ni-silicides using electron energy loss spectroscopy (EELS) based methods is discussed. A series of Ni-silicide phases is examined: Ni3Si, Ni31Si12, Ni2Si, NiSi and NiSi2. The composition of these phases is determined by quantitative core-loss EELS. A study of the low loss part of the EELS spectrum shows that both the energy and the shape of the plasmon peak are characteristic for each phase. Examination of the Ni-L edge energy loss near edge structure (ELNES) shows that the ratio and the sum of the L2 and L3 white line intensities are also characteristic for each phase. The sum of the white line intensities is used to determine the trend in electron occupation of the 3d states of the phases. The dependence of the plasmon energy on the electron occupation of the 3d states is demonstrated.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.692
Times cited: 11
DOI: 10.1111/j.1365-2818.2010.03391.x
|
|
|
“Dedicated TEM on domain boundaries from phase transformations and crystal growth”. Schryvers D, Van Aert S, Delville R, Idrissi H, Turner S, Salje EKH, Phase transitions 86, 15 (2013). http://doi.org/10.1080/01411594.2012.694435
Abstract: Investigating domain boundaries and their effects on the behaviour of materials automatically implies the need for detailed knowledge on the structural aspects of the atomic configurations at these interfaces. Not only in view of nearest neighbour interactions but also at a larger scale, often surpassing the unit cell, the boundaries can contain structural elements that do not exist in the bulk. In the present contribution, a number of special boundaries resulting from phase transformations or crystal growth and those recently investigated by advanced transmission electron microscopy techniques in different systems will be reviewed. These include macrotwins between microtwinned martensite plates in NiAl, austenite-single variant martensite habit planes in low hysteresis NiTiPd, nanotwins in non-textured nanostructured Pd and ferroelastic domain boundaries in CaTiO3. In all discussed cases these boundaries play an essential role in the properties of the respective materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.06
DOI: 10.1080/01411594.2012.694435
|
|
|
“Intergrowth of components and ramps in coffin-shaped ZSM-5 zeolite crystals unraveled by focused ion beam-assisted transmission electron microscopy”. Lu J, Roeffaers MBJ, Bartholomeeusen E, Sels BF, Schryvers D, Microscopy and microanalysis 20, 42 (2014). http://doi.org/10.1017/S1431927613013731
Abstract: Scanning electron microscopy, focused ion beam (FIB), and transmission electron microscopy are combined to study the intergrowth of 90 degrees rotational components and of ramps in coffin-shaped ZSM-5 crystals. The 90 degrees rotational boundaries with local zig-zag features between different intergrowth components are observed in the main part of crystal. Also a new kind of displacement boundary is described. At the displacement boundary there is a shift of the unit cells along the boundary without a change in orientation. Based on lamellae prepared with FIB from different positions of the ramps and crystal, the orientation relationships between ramps and the main part of the crystal are studied and the three-dimensional morphology and growth mechanism of the ramp are illustrated.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 7
DOI: 10.1017/S1431927613013731
|
|
|
“Microstructure and precipitates in as-cast Co38Ni33Al29 shape memory alloy”. Bartova B, Schryvers D, Yang Z, Ignacova S, Sittner P, Scripta materialia 57, 37 (2007). http://doi.org/10.1016/j.scriptamat.2007.03.007
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 22
DOI: 10.1016/j.scriptamat.2007.03.007
|
|
|
“Nanodiamonds do not provide unique evidence for a Younger Dryas impact”. Tian H, Schryvers D, Claeys P, Proceedings of the National Academy of Sciences of the United States of America 108, 40 (2011). http://doi.org/10.1073/pnas.1007695108
Abstract: Microstructural, δ13C isotope and C/N ratio investigations were conducted on excavated material from the black Younger Dryas boundary in Lommel, Belgium, aiming for a characterisation of the carbon content and structures. Cubic diamond nanoparticles are found in large numbers. The larger ones with diameters around or above 10 nm often exhibit single or multiple twins. The smaller ones around 5 nm in diameter are mostly defect-free. Also larger flake-like particles, around 100 nm in lateral dimension, with a cubic diamond structure are observed as well as large carbon onion structures. The combination of these characteristics does not yield unique evidence for an exogenic impact related to the investigated layer.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.661
Times cited: 32
DOI: 10.1073/pnas.1007695108
|
|
|
“Optimization of a FIB/SEM slice-and-view study of the 3D distribution of Ni4Ti3 precipitates in NiTi”. Cao S, Tirry W, van den Broek W, Schryvers D, Journal of microscopy 233, 61 (2009). http://doi.org/10.1111/j.1365-2818.2008.03095.x
Abstract: The 3D morphology and distribution of lenticular Ni4Ti3 precipitates in the austenitic B2 matrix of a binary Ni51Ti49 alloy has been investigated by a slice-and-view procedure in a dual-beam focused ion beam/scanning electron microscope system. Due to the weak contrast of the precipitates, proper imaging conditions need to be selected first to allow for semi-automated image treatment. Knowledgeable imaging is further needed to ensure that all variants of the precipitates are observed with equal probability, regardless of sample orientation. Finally, a volume ratio of 10.2% for the Ni4Ti3 precipitates could be calculated, summed over all variants, which yields a net composition of Ni50.27Ti49.73 for the matrix, leading to an increase of 125 degrees for the martensitic start temperature. Also, the expected relative orientation of the different variants of the precipitates could be confirmed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 1.692
Times cited: 22
DOI: 10.1111/j.1365-2818.2008.03095.x
|
|
|
“Reducing the formation of FIB-induced FCC layers on Cu-Zn-Al austenite”. Zelaya E, Schryvers D, Microscopy research and technique 74, 84 (2011). http://doi.org/10.1002/jemt.20877
Abstract: The irradiation effects of thinning a sample of a Cu-Zn-Al shape memory alloy to electron transparency by a Ga+ focused ion beam were investigated. This thinning method was compared with conventional electropolishing and Ar+ ion milling. No implanted Ga was detected but surface FCC precipitation was found as a result of the focused ion beam sample preparation. Decreasing the irradiation dose by lowering the energy and current of the Ga+ ions did not lead to a complete disappearance of the FCC structure. The latter could only be removed after gentle Ar+ ion milling of the sample. It was further concluded that the precipitation of the FCC is independent of the crystallographic orientation of the surface.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.147
Times cited: 2
DOI: 10.1002/jemt.20877
|
|
|
“Dislocation driven nanosample plasticity: new insights from quantitative in-situ TEM tensile testing”. Samaee V, Gatti R, Devincre B, Pardoen T, Schryvers D, Idrissi H, Scientific Reports 8, 12012 (2018). http://doi.org/10.1038/s41598-018-30639-8
Abstract: Intrinsic dislocation mechanisms in the vicinity of free surfaces of an almost FIB damage-free single crystal Ni sample have been quantitatively investigated owing to a novel sample preparation method combining twin-jet electro-polishing, in-situ TEM heating and FIB. The results reveal that the small-scale plasticity is mainly controlled by the conversion of few tangled dislocations, still present after heating, into stable single arm sources (SASs) as well as by the successive operation of these sources. Strain hardening resulting from the operation of an individual SAS is reported and attributed to the decrease of the length of the source. Moreover, the impact of the shortening of the dislocation source on the intermittent plastic flow, characteristic of SASs, is discussed. These findings provide essential information for the understanding of the regime of ‘dislocation source’ controlled plasticity and the related mechanical size effect.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 4.259
Times cited: 9
DOI: 10.1038/s41598-018-30639-8
|
|
|
“Atomic-scale viscoplasticity mechanisms revealed in high ductility metallic glass films”. Idrissi H, Ghidelli M, Béché, A, Turner S, Gravier S, Blandin J-J, Raskin J-P, Schryvers D, Pardoen T, Scientific reports 9, 13426 (2019). http://doi.org/10.1038/s41598-019-49910-7
Abstract: The fundamental plasticity mechanisms in thin freestanding Zr65Ni35 metallic glass films are investigated in order to unravel the origin of an outstanding strength/ductility balance. The deformation process is homogenous until fracture with no evidence of catastrophic shear banding. The creep/relaxation behaviour of the films was characterized by on-chip tensile testing, revealing an activation volume in the range 100–200 Å3. Advanced high-resolution transmission electron microscopy imaging and spectroscopy exhibit a very fine glassy nanostructure with well-defined dense Ni-rich clusters embedded in Zr-rich clusters of lower atomic density and a ~2–3 nm characteristic length scale. Nanobeam electron diffraction analysis reveals that the accumulation of plastic deformation at roomtemperature
correlates with monotonously increasing disruption of the local atomic order. These results provide experimental evidences of the dynamics of shear transformation zones activation in metallic glasses. The impact of the nanoscale structural heterogeneities on the mechanical properties including the rate dependent behaviour is discussed, shedding new light on the governing plasticity mechanisms in metallic glasses with initially heterogeneous atomic arrangement.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.259
DOI: 10.1038/s41598-019-49910-7
|
|
|
“Deciphering the interactions between single arm dislocation sources and coherent twin boundary in nickel bi-crystal”. Samaee V, Dupraz M, Pardoen T, VAn Swygenhoven H, Schryvers D, Idrissi H, Nature Communications 12, 962 (2021). http://doi.org/10.1038/S41467-021-21296-Z
Abstract: The introduction of a well-controlled population of coherent twin boundaries (CTBs) is an attractive route to improve the strength ductility product in face centered cubic (FCC) metals. However, the elementary mechanisms controlling the interaction between single arm dislocation sources (SASs), often present in nanotwinned FCC metals, and CTB are still not well understood. Here, quantitative in-situ transmission electron microscopy (TEM) observations of these mechanisms under tensile loading are performed on submicron Ni bi-crystal. We report that the absorption of curved screw dislocations at the CTB leads to the formation of constriction nodes connecting pairs of twinning dislocations at the CTB plane in agreement with large scale 3D atomistic simulations. The coordinated motion of the twinning dislocation pairs due to the presence of the nodes leads to a unique CTB sliding mechanism, which plays an important role in initiating the fracture process at a CTB ledge. TEM observations of the interactions between non-screw dislocations and the CTB highlight the importance of the synergy between the repulsive force of the CTB and the back stress from SASs when the interactions occur in small volumes. Interactions of dislocations with coherent twin boundaries contribute to strength and ductility in metals, but investigating the interaction mechanisms is challenging. Here the authors unravel these mechanisms through quantitative in-situ transmission electron microscopy observations in nickel bi-crystal samples under tensile loading.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
DOI: 10.1038/S41467-021-21296-Z
|
|
|
“Unravelling the multi-scale structure-property relationship of laser powder bed fusion processed and heat-treated AlSi10Mg”. Van Cauwenbergh P, Samaee V, Thijs L, Nejezchlebova J, Sedlak P, Ivekovic A, Schryvers D, Van Hooreweder B, Vanmeensel K, Scientific Reports 11, 6423 (2021). http://doi.org/10.1038/S41598-021-85047-2
Abstract: Tailoring heat treatments for Laser Powder Bed Fusion (LPBF) processed materials is critical to ensure superior and repeatable material properties for high-end applications. This tailoring requires in-depth understanding of the LPBF-processed material. Therefore, the current study aims at unravelling the threefold interrelationship between the process (LPBF and heat treatment), the microstructure at different scales (macro-, meso-, micro-, and nano-scale), and the macroscopic material properties of AlSi10Mg. A similar solidification trajectory applies at different length scales when comparing the solidification of AlSi10Mg, ranging from mould-casting to rapid solidification (LPBF). The similarity in solidification trajectories triggers the reason why the Brody-Flemings cellular microsegregation solidification model could predict the cellular morphology of the LPBF as-printed microstructure. Where rapid solidification occurs at a much finer scale, the LPBF microstructure exhibits a significant grain refinement and a high degree of silicon (Si) supersaturation. This study has identified the grain refinement and Si supersaturation as critical assets of the as-printed microstructure, playing a vital role in achieving superior mechanical and thermal properties during heat treatment. Next, an electrical conductivity model could accurately predict the Si solute concentration in LPBF-processed and heat-treated AlSi10Mg and allows understanding the microstructural evolution during heat treatment. The LPBF-processed and heat-treated AlSi10Mg conditions (as-built (AB), direct-aged (DA), stress-relieved (SR), preheated (PH)) show an interesting range of superior mechanical properties (tensile strength: 300-450 MPa, elongation: 4-13%) compared to the mould-cast T6 reference condition.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.259
DOI: 10.1038/S41598-021-85047-2
|
|
|
“In situ high resolution electron microscopy observation of electron-irradiation-induced martensitic transformation in a Ni63Al37 alloy”. Muto S, Schryvers D, Journal of alloys and compounds 199, 1 (1993). http://doi.org/10.1016/0925-8388(93)90422-J
Abstract: An electron-irradiation-induced transformation from cubic beta2 austenite to monoclinic 7M martensite was observed in situ under high resolution electron microscopy conditions in a thin foil of Ni63Al37 beta2 phase (B2, CsCl structure), with the start temperature of the martensitic transformation below but very close to room temperature. The structure of the martensite is consistent with thermoelastic or stress-induced martensite at this composition, including the existence of multiple stacking faults. The transformation is described by a gradual increase in the shear and shuffle amplitudes already existing in the precursor domains. Possible origins of the transformation are discussed.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 2.999
Times cited: 8
DOI: 10.1016/0925-8388(93)90422-J
|
|
|
“Applications of advanced transmission electron microscopic techniques to Ni-Ti based shape memory materials”. Schryvers D, Potapov P, Santamarta R, Tirry W, Materials science and engineering: part A: structural materials: properties, microstructure and processing 378, 11 (2004). http://doi.org/10.1016/j.msea.2003.10.325
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 6
DOI: 10.1016/j.msea.2003.10.325
|
|
|
“Composition gradients surrounding Ni4Ti3 precipitates in a NiTi alloy studied by EELS, EFTEM and EDX”. Yang Z, Schryvers D, International journal of applied electromagnetics and mechanics 23, 17 (2006)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.769
|
|
|
“High resolution TEM study of Ni4Ti3 precipitates in austenitic Ni51Ti49”. Tirry W, Schryvers D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 378, 157 (2004). http://doi.org/10.1016/j.msea.2003.10.336
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 19
DOI: 10.1016/j.msea.2003.10.336
|
|
|
“Structure of multi-grain spherical particles in an amorphous Ti50Ni25Cu25 melt-spun ribbon”. Santamarta R, Schryvers D, Materials science and engineering: part A: structural materials: properties, microstructure and processing 378, 143 (2004). http://doi.org/10.1016/j.msea.2003.11.060
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.094
Times cited: 5
DOI: 10.1016/j.msea.2003.11.060
|
|
|
“Unexpected ordering behaviour of Pt3Al intermetallic precipitates”. Douglas A, Neethling JH, Santamarta R, Schryvers D, Cornish LA, Journal of alloys and compounds 432, 96 (2007). http://doi.org/10.1016/j.jallcom.2006.05.106
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.133
Times cited: 18
DOI: 10.1016/j.jallcom.2006.05.106
|
|
|
“Transmission electron microscopy study of phase compatibility in low hysteresis shape memory alloys”. Delville R, Kasinathan S, Zhang Z, van Humbeeck J, James RD, Schryvers D, Philosophical magazine 90, 177 (2010). http://doi.org/10.1080/14786430903074755
Abstract: Recent findings have linked low hysteresis in shape memory alloys with phase compatibility between austenite and martensite. To investigate the evolution of microstructure as phase compatibility increases and hysteresis is reduced, transmission electron microscopy was used to study the alloy system Ti50Ni50xPdx, where the composition is systemically tuned to approach perfect compatibility. Changes in morphology, twinning density and twinning modes are reported, along with special microstructures occurring when compatibility is achieved. In addition, the interface between austenite and a single variant of martensite was studied by high-resolution and conventional electron microscopy. The low energy configuration of the interface detailed in this article suggests that it plays an important role in the lowering of hysteresis compared to classical habit plane interfaces.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.505
Times cited: 70
DOI: 10.1080/14786430903074755
|
|
|
“Lattice deformations in quasi-dynamic strain glass visualised and quantified by aberration corrected electron microscopy”. Lu J, Martinez GT, Van Aert S, Schryvers D, Physica status solidi: B: basic research 251, 2034 (2014). http://doi.org/10.1002/pssb.201350351
Abstract: Advanced transmission electron microscopy and statistical parameter estimated quantification procedures were applied to study the room temperature quasi-dynamical strain glass state in NiTi alloys. Nanosized strain pockets are visualised and the displacements of the atom columns are quantified. A comparison is made with conventional high-resolution transmission electron microscopy images of point defect induced strains in NiAl alloys.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.674
Times cited: 2
DOI: 10.1002/pssb.201350351
|
|
|
“On the relationship between the twin internal structure and the work-hardening rate of TWIP steels”. Idrissi H, Renard K, Schryvers D, Jacques PJ, Scripta materialia 63, 961 (2010). http://doi.org/10.1016/j.scriptamat.2010.07.016
Abstract: FeMnC and FeMnSiAl TWIP steels deformed under the same conditions exhibit different work-hardening rates. The present study investigates the microstructure of plastically deformed FeMnC and FeMnSiAl samples, particularly the internal structure of the mechanically generated twins and their topology at the grain scale. Twins in the FeMnC steel are finer and full of sessile dislocations, rendering this material distinctly stronger with an improved work-hardening rate.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 145
DOI: 10.1016/j.scriptamat.2010.07.016
|
|
|
“Plasticity mechanisms in ultrafine grained freestanding aluminum thin films revealed by in-situ transmission electron microscopy nanomechanical testing”. Idrissi H, Kobler A, Amin-Ahmadi B, Coulombier M, Galceran M, Raskin J-P, Godet S, Kuebel C, Pardoen T, Schryvers D, Applied physics letters 104, 101903 (2014). http://doi.org/10.1063/1.4868124
Abstract: In-situ bright field transmission electron microscopy (TEM) nanomechanical tensile testing and in-situ automated crystallographic orientation mapping in TEM were combined to unravel the elementary mechanisms controlling the plasticity of ultrafine grained Aluminum freestanding thin films. The characterizations demonstrate that deformation proceeds with a transition from grain rotation to intragranular dislocation glide and starvation plasticity mechanism at about 1% deformation. The grain rotation is not affected by the character of the grain boundaries. No grain growth or twinning is detected. (C) 2014 AIP Publishing LLC.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 24
DOI: 10.1063/1.4868124
|
|
|
“The role of phase compatibility in martensite”. Salman OU, Finel A, Delville R, Schryvers D, Journal of applied physics
T2 –, 22nd International Symposium on Integrated Functionalities (ISIF), JUN 13-16, 2010, San Juan, PR 111, 103517 (2012). http://doi.org/10.1063/1.4712629
Abstract: Shape memory alloys inherit their macroscopic properties from their mesoscale microstructure originated from the martensitic phase transformation. In a cubic to orthorhombic transition, a single variant of martensite can have a compatible (exact) interface with the austenite for some special lattice parameters in contrast to conventional austenite/twinned martensite interface with a transition layer. Experimentally, the phase compatibility results in a dramatic drop in thermal hysteresis and gives rise to very stable functional properties over cycling. Here, we investigate the microstructures observed in Ti50Ni50-xPdx alloys that undergo a cubic to orthorhombic martensitic transformation using a three-dimensional phase field approach. We will show that the simulation results are in very good agreement with transmission electron microscopy observations. However, the understanding of the drop in thermal hysteresis requires the coupling of phase transformation with plastic activity. We will discuss this point within the framework of thermoelasticity, which is a generic feature of the martensitic transformation. (C) 2012 American Institute of Physics. [http://dx.doi.org/10.1063/1.4712629]
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.068
Times cited: 11
DOI: 10.1063/1.4712629
|
|