Abstract: Anew recycling process, according to the zero-waste concept, was investigated for an iron rich waste stream, more specifically a secondary lead smelting matte. The process consists of a selective citrate leaching of Pb, Cu, Ni and Zn in combination with a roasting step, leading to a simultaneous recovery of hematite as a secondary iron resource. The parameters, such as leaching time, leaching temperature, H2O2 concentration and roasting temperature, were experimentally optimized. The maximum Pb leaching efficiency was 93% and the leachability of Cu (33%) and Zn (11%) increased slightly in the presence of 0.5 M H2O2 in 1 M citrate at 25 degrees C and pH 5.5. Importantly, almost no Fe was leached (< 0.6%) from the iron rich matrix material at this condition allowing for a maximal recovery of hematite as a secondary resource after further treatment (i.e. roasting or sulfur removal). The leachability of Pb, Cu, Ni and Zn was strongly affected by the roasting temperature. Maximum leaching efficiency in 1 M citrate (25 degrees C, L/S ratio 10, pH 6.5) was 93% for Pb, 80% for Cu and 60% for Zn at a roasting temperature of 600 degrees C, while for Ni the maximum leaching efficiency of 53% was reached after roasting at 650 degrees C. Furthermore, when oxidative roasting was applied, the leaching residue consists dominantly of hematite (Fe2O3) with minor quantities of PbSO4, which can be used as pig iron ore (Fe > 60 wt%). (C) 2017 Elsevier B.V. All rights reserved.

Abstract: The European automotive sector is faced with potentially disruptive challenges. In particular, the projected increase in the share of electric vehicles (EVs) and calls to prepare for the implementation of more circular economy (CE) strategies are increasingly demanding systemic adaptations. Given the goals of the CE, the adaptations should enable a maximal preservation of the function and value of products (e.g. extension of lifetime), components (e.g. reuse of parts) and materials (e.g., material recycling), thus saving on the energy, materials and effort that would be required to restore the lost functionalities. In this context, statistical entropy analysis (SEA) is proposed as a methodology to assess the effort needed for preserving and restoring functionality at different product, component and material life cycle stages. Effort is measured as changes in statistical entropy that are caused by concentration and dilution activities in the production – consumption – End-of-Life (EoL) system. SEA was applied to a generic model of the European automotive system, in combination with a stock-driven model and a material flow analysis (MFA), allowing statistical entropy changes to be projected over time. The paper demonstrates how SEA can facilitate decision making on the transition towards a more circular economy by quantifying the effects of particular CE strategies and their combinations. The results show that without any additional system adaptations, an increasing share of EVs towards the year 2050 will lead to substantially increased effort in production as well as end-of-life vehicle treatment.

Abstract: The chemical characterization of particulate matter inside and outside of confined bus shelters has been discerned for the first time. Transit patrons are at risk due to the close vicinity of densely trafficked areas resulting in elevated pollution footprints. Incomplete combustion processes, as well as exhaust and wear and tear emissions from public and personal transportation vehicles, are key contributors to degraded urban air quality and are often implicated as causal to various diseases in humans. Urban planning, therefore, includes efficient public transport systems to mitigate the effect. The bus rapid transit system was inaugurated in Curitiba to ensure dedicated traffic lanes, major bus interchanges and semi-confined bus stops called tube stations. To assess the chemical risk that the passengers are exposed to, an investigation of the aerosol inside and outside five of these tube stations was launched. Electron probe X-ray micro-analysis and X-ray fluorescence were used to determine the elemental composition of individual and of bulk particle samples. An aethalometer quantified the black carbon. Elemental concentrations inside the shelters were in general higher than outside, especially for traffic-related elements. The lead concentration exceeded the NAAS standard at times, although the average was below the guideline. The biogenic, organic and soot clusters showed the highest abundance for the city centre sites. The overall carcinogenic risk could be classed as moderate, and the risk was significant at two sites during one of the sampling campaigns. The non-carcinogenic risk is well below the significant value.

Abstract: Several HNO3-based leaching approaches were tested and optimized to selectively recover Pb and other minor metals (Cu, Ni, Zn) from secondary lead smelter residues (i.e., slag and matte). Firstly, the leaching behaviors of Pb and the matrix element Fe were studied at atmospheric pressure in the temperature range 25-70 degrees C. These elements were present in both materials studied as sulfide and oxide phases. For the sulfur-rich matte residue, the Pb leaching increased from 63% to 69% upon increasing the HNO3 concentration from 0.2 M to 0.5 M. However, by adding Fe(III) as an oxidation agent, Pb leaching from the matte amounted to 90% at 25 degrees C. At a higher temperature, Pb leaching was reduced due to PbSO4 precipitation. In this process, Cu, Zn and Ni leaching was insignificant. For the slag residue, HNO3 could not leach Pb (0.03% Pb leached), while Fe leaching was 19.8% due to a galvanic effect. However, Pb leaching of the slag was 82% in the presence of additional Fe(III). Secondly, to enhance leaching of the other base metals (Cu, Zn and Ni) from the matte, roasting followed by water leaching and (microwave assisted or autoclave) pressurized leaching in 0.5 M HNO3 were applied. During roasting, the FeS phase converted to Fe2O3 above 500 degrees C, and PbS and Pb phases were transformed into insoluble PbSO4 above 400 degrees C. Cu, Ni and Zn leaching was drastically enhanced by a roasting step at 600 degrees C followed by leaching with 0.5 M HNO3 at 50 degrees C, or by pressurized HNO3 leaching above 130 degrees C, whereby Pb leaching almost ceased due to PbSO4 precipitation. During the roasting above 600 degrees C, or microwave assisted extraction (MAE) at 160 degrees C for 15 min, FeS was completely converted to iron oxides that can be used as raw material for pig iron production. Based on the results, the methods investigated can be combined as process steps of two possible routes for the selective recovery of valuable metals and the production of a clean source of Fe oxides from the secondary lead smelting residues studied. (C) 2017 Elsevier B.V. All rights reserved.

Abstract: Nanocrystalline tungsten oxide with variable particle size and surface area was synthesized by aqueous deposition and heat treatment for use in resistive gas sensors. Surface modification with 1 wt.% Pd and Ru was performed by impregnation to improve the sensitivity to CO and ammonia. Acid and oxidation surface sites were evaluated by temperature-programmed techniques using probe molecules. The surface acidity dropped with increasing particle size, and was weakly affected by additives. Lower crystallinity of WO3 and the presence of Ru species favoured temperature-programmed reduction of the materials. Modifying WO3 increased its sensitivity, to CO at ambient condition for modification by Pd and to NH3 at elevated temperature for Ru modification. An in situ infrared study of the gas – solid interaction showed that the catalytic additives change the interaction route of tungsten oxide with the target gases and make the reception of detected molecules independent of the semiconductor oxide matrix.

Abstract: Energy-dispersive x-ray fluorescence is advantageous for trace analysis of soils present as thin films. A target thickness of about 2 mg cm-2 provides a compromise between optimal sensitivity and minimal absorption effect or optimal accuracy. Sample preparation involves only suspending the finely ground soil in water and drying this suspension on a thin mylar foil glued on a ring that fits into the x.r.f. spectrometer. The effective sample weight present in the exciting beam area is computed from the scatter peaks, a method that cancels out target heterogeneity problems. High accuracy is demonstrated for many elements in reference soil and rock materials; a precision around 5% and a detection limit around 10 ppm can be achieved. As an illustration, results for 16 trace elements and preliminary interpretation are given for a series of pedologically important soil samples from Brasil.

Abstract: The adsorptive voltammetric behaviour of tinidazole onto the HMDE was investigated and validated in solubilized system and biological fluids by CV, SWCAdSV and DPCAdSV. Addition of CTAB to the solution containing drug enhanced the peak current while anionic and non-ionic surfactants showed an opposite effect. The electrode process is irreversible and adsorption controlled. Various chemical and instrumental parameters affecting the monitored electroanalytical response were investigated and optimized for tinidazole determination. Under optimized conditions; the adsorptive stripping peak current is linear over the concentration range 7.0 × 10−9 to 6.2 × 10−7 mol/L with detection limit of 4.5 × 10−10 mol/L. The precision of the proposed method in terms of RSD is 1.2% and mean recovery of 100.01%. The applicability of proposed method is further extended to in vitro determination of the drug in biological fluids.