Abstract: Electron energy loss spectroscopy was used to investigate the bonding of plasma deposited carbon films. The experimental conditions include the use of a specific collection angle for which the shape of the spectra is free of the orientation dependency usually encountered in graphite due to its anisotropic structure. The first quantification process of the energy loss near-edge structure was performed by a standard fit of the collected spectrum, corrected for background and multiple scattering, with three Gaussian functions followed by a comparison with the graphite spectrum obtained under equivalent experimental conditions. In a second approach a fitting model directly incorporating the background subtraction and multiple scattering removal was applied. The final numerical results are interpreted in view of the deposition conditions of the films and the actual fitting procedure with the related choice of parameters.

Abstract: Lath martensite is important in industry because it is the key strengthening component in many advanced high strength steels. The study of crystallography and chemistry of lath martensite is extensive in the literature, however, mostly based on fully martensitic steels. In this work, lath martensite in dual phase steels is investigated with a focus on the substructure identification of the martensite islands and microstructural bands using electron backscattered diffraction, and on the influence of the accompanied tempering process during industrial coating process on the distribution of alloying elements using atom probe tomography. Unlike findings for the fully martensitic steels, no martensite islands with all 24 Kurdjumov-Sachs variants have been observed. Almost all martensite islands contain only one main packet with all six variants and minor variants from the remaining three packets of the same prior austenite grain. Similarly, the martensite bands are typically composed of connected domains originating from prior austenite grains, each containing one main packets (mostly with all variants) and few separate variants. The effect of tempering at similar to 450 degrees C (due to the industrial zinc coating process) has also been investigated. The results show a strong carbon partitioning to lath boundaries and Cottrell atmospheres at dislocation core regions due to the thermal process of coating. In contrast, auto-tempering contributes to the carbon redistribution only in a limited manner. The substitutional elements are all homogenously distributed. The phase transformation process has two effects on the material: mechanically, the earlier-formed laths are larger and softer and therefore more ductile (as revealed by nanoindentation); chemically, due to the higher dislocation density inside the later-formed laths, which are generally smaller, carbon Cottrell atmospheres are predominantly observed.

Abstract: Nanometer sized (Ti,Mo,Cr)C (MX-type) precipitates that grew in a 24% cold worked Ti-stabilized austenitic stainless steel (grade DIN 1.4970, member of the 15-15Ti austenitic stainless steels) after heat treatment were fully characterized with transmission electron microscopy (TEM), probe corrected high angle annular dark field scanning transmission electron microscopy (HR-HAADF STEM), and atom probe tomography (APT). The precipitates shared the cube-on-cube orientation with the matrix and were facetted on {111} planes, yielding octahedral and elongated octahedral shapes. The misfit dislocations were believed to have Burgers vectors a/6<112> which was verified by geometrical phase analysis (GPA) strain mapping of a matrix-precipitate interface. The dislocations were spaced five to seven atomic
planes apart, on average slightly wider than expected for the lattice parameters of steel and TiC. Quantitative atom probe tomography analysis of the precipitates showed that precipitates were significantly enriched in Mo, Cr and V, and that they were hypostoichiometric with respect to C. These findings were consistent with a reduced lattice parameter. The precipitates were found primarily on Shockley
partial dislocations originating from the original perfect dislocation network. These novel findings could contribute to the understanding of how TiC nanoprecipitates interact with point defects and matrix dislocations. This is essential for the application of these Ti-stabilized steels in high temperature environments or fast spectrum nuclear fission reactors.

Abstract: Microtwin sequences in Ni66Al34 martensite plates of different size were investigated by electron microscopy. Although mostly irregular sequences were observed an average twin width w can be determined which increases with twin length L following the expected relation w ~ sqrt(L). High resolution electron microscopy was used to study the twin branching close to the plate boundaries and an atomic model for the branching of a microtwin and the changes in twin thickness is suggested

Abstract: The existence of the (52) stacking of the 7M martensite structure in Ni-Al is discussed in view of different experimental observations relating this structure to the premartensitic anomalies. It is concluded that the extreme fineness of the twinning is inherited from the wavelength of the premartensitic anomalies, while, given this dimension, the actual stacking tries to comply with stress free habit plane conditions by choosing the specific (52) stacking.

Abstract: The deployment of Gen-IV lead-cooled fast reactors requires a good compatibility between the selected structural/cladding steels and the inherently corrosive heavy liquid metal coolant. An effective liquid metal corrosion mitigation strategy involves the in-situ steel passivation in contact with the oxygen-containing Pb-alloy coolant. Transmission electron microscopy was used in this work to study the multi-layered oxide scales forming on an austenitic stainless steel fuel cladding exposed to oxygen-containing (CO ≈ 10−6 mass%) static liquid leadbismuth eutectic (LBE) for 1000 h between 400 and 500 °C. The oxide scale constituents were analyzed, including the intertwined phases comprising the innermost biphasic layer.

Abstract: Microstructural characteristics of Hastelloy X produced by Selective Laser Melting have been investigated by various microscopic techniques in the as built (AB) condition and after hot isostatic pressing (HIP). At sub-grain level the AB material consists of columnar high density dislocation cells while the HIP sample consists of columnar sub-grains with lower dislocation density that originate from the original dislocation cells, contradicting existing models. The sub-grains contain nanoscale precipitates enriched in Al, Ti, Cr and O, located at sub-grain boundaries in the AB condition and within the grains after HIP. At some grain boundaries, micrometer sized chromium carbides are detected after HIP. Micro hardness within the grains was found to decrease after HIP, which was attributed to the decrease in dislocation density due to recovery annealing.

Abstract: It is generally believed that β00 precipitates, rather than β0 precipitates, are the major strengthening precipitates in
aged Al–Mg–Si alloys. The reason for this difference is not well understood. To clarify this, two samples of the
same Al–Mg–Si alloy but with different aging states were prepared. The under-aged sample only contains nanoprecipitates
of the β00 type, while the peak-aged one contains nearly equal volumes of β00 and β0 precipitates. We
have, for the first time, separated the strengthening effect of the contribution from βʺ and βʹ precipitates,
respectively, by an indirect approach based on high-precision measurements of volume fractions, number densities,
sizes, proportions of the precipitates, their lattice strains, the composition and grain size of the matrix. The
β0 precipitates, which take 45.6% of the total precipitate volume in the peak-aged sample, contribute to the entire
precipitation strengthening by only 31.6%. The main reason why they are less useful compared to β00 precipitates
has been found to be associated with their smaller lattice strains relative to the matrix, which is 0.99% versus
2.10% (for β00 ).

Abstract: Ni thin films sputter-deposited at room temperature with varying Ar pressures were investigated with automated crystal orientation mapping in a transmission electron microscope to uncover the mechanisms controlling the internal stress build-up recorded in-situ during deposition. Large grains were found to induce behaviour similar to a stress-free nucleation layer. The measurements of grain size in most of the Ni thin films are in agreement with the island coalescence model. Low internal stress was observed at low Ar pressure and was explained by the presence of large grains. Relaxation of high internal stress was also noticed at the highest Ar pressure, which was attributed to a decrease of Σ3 twin boundary density due to a low deposition rate. The results provide insightful information to better understand the relationship between structural boundaries and the evolution of internal stress upon deposition of thin films.

Abstract: The effect of Cu on the evolution of the Al3Zr phase in an Al-Cu-Zr cast alloy during solution treatment at 500 °C has been thoroughly studied by combining atomic resolution high-angle annular dark-field scanning transmission electron microscopy, energy-dispersive X-ray spectroscopy and first-principles cal- culations. The heat treatment initially produces a pure L12-Al3Zr microstructure, allowing for about 13 % Cu to be incorporated in the dispersoid. Cu incorporation increases the energy barrier for anti-phase boundary (APB) activation, thus stabilizing the L12 structure. Additional heating leads to a Cu-induced “branched”path for the L12 structural transformation, with the latter process accelerated once the first APB has been created. Cu atoms may either (i) be repelled by the APBs, promoting the transformation to a Cu-poor D023 phase, or (ii) they may segregate at one Al-Zr layer adjacent to the APB, promoting a transformation to a new thermodynamically favored phase, Al4CuZr, formed when these segregation layers are periodically arranged. Theoretical studies suggest that the branching of the L12 transformation path is linked to the speed at which an APB is created, with Cu attraction triggered by a comparatively slow process. This unexpected transformation behavior of the L12-Al3Zr phase opens a new path to understanding, and potentially regulating the Al3Zr dispersoid evolution for high temperature applications.

Abstract: The three-dimensional size, morphology and distribution of Ni4Ti3 precipitates growing in binary Ni-rich Ni-Ti alloys have been investigated via a slice view procedure in a Dual-Beam FIB/SEM system, in order to better stress-free Ni50.8Ti49.2 alloy with all four variants of precipitates and a compressed Ni51Ti49 alloy with aligned precipitates in one family were studied. The Ni4Ti3 precipitates reach a volume fraction of 9.6% in the reconstructed region of the stress-free alloy and 4.3% in the compressed one. In both cases, the mean volume, specific surface area, sphericity and aspect ratio of the precipitates are calculated and the Pair Distribution Functions of the precipitates are obtained. It is shown that most precipitates in the stress-free sample grow larger and have a more lenticular shape, while those in the compressed sample are more cylindrical. Deviations from these ideal shapes reveal internal steps in the stress-free sample and lamellae formation in the compressed one.

Abstract: Ni4Ti3 precipitates play an important role in the shape memory and superelastic behaviour of thermo-mechanically treated Ni-Ti material. The 3D morphology and distribution of such precipitates with lenticular shape and rhombohedral atomic structure in the austenitic B2 matrix of a binary Ni-rich Ni-Ti alloy has been elucidated via a slice view procedure in a Dual-Beam FIB/SEM system. With the sequence of cross-section SE images obtained from the SEM, a 3D reconstruction has been achieved after proper alignment and image processing, from which both qualitative and quantitative analysis can be performed. Careful imaging is needed to ensure that all variants of the precipitates are observed with equal probability, regardless sample orientation. Moreover, due to the weak contrast of the precipitates, proper imaging conditions need to be selected to allow for semi-automated image treatment. Finally, a volume ratio of 10.2% for the Ni4Ti3 precipitates could be calculated, summed over all variants, which yields a net composition of Ni50.36Ti49.64 for the matrix, leading to an increase of 113 degrees for the martensitic start temperature Ms. Also, the expected relative orientation of the different variants of the precipitates could be confirmed. In the near future, other quantitative measures on the distribution of the precipitates can be expected.

Abstract: Two different kinds of experimental approaches yielding three-dimensional structural information on metastable semi-coherent precipitates are demonstrated. By combining high-resolution images from two independent viewing directions a full description of the strain field surrounding a nano-sized Ni4Ti3 precipitate in Ni-Ti can be obtained. The principal axes and strains correlate well with the transformation strain of the observed R-phase transformation close to the precipitate. Using a slice-and-view procedure in a FIB/SEM dual-beam instrument, a three-dimensional voxel dataset is produced from which morphological and distributional information on the same precipitates can be obtained yielding new insight into the particular transformation paths of these alloys, relevant for their functional behaviour.

Abstract: Lattice deformations and concentration gradients surrounding Ni4Ti3 precipitates grown by appropriate annealing in a Ni51Ti49 B2 austenite matrix are determined by a combination of TEM techniques. Quantitative Fourier analysis of HRTEM images reveals a deformed nanoscale region with lattice deformations up to 2% while EELS and EDX indicate a Ni depleted zone up to 150 nm away from the matrix-precipitate interface.