Abstract: The exploration of the Mn4+-rich side of the Pr1-xSrxMnO3 system has allowed the extension of the domain of the cubic perovskite, by using a two-step process, combining synthesis under Ar flow at high temperature and O-2 pressure annealing at lower temperature. We show that these Pr-doped cubic perovskites exhibit a coupled structural (cubic-tetragonal) and magnetic (para-antiferro) transition connected with a resistivity jump at the same temperature. The strong interplay between lattice, charges, and spins for these oxides results from the appearance at low temperature of the distorted C-type antiferromagnetic structure. The Pr1-xSrxMnO3 magnetic phase diagram shows, for 0.9 less than or equal to x less than or equal to 1 (i.e., on the Mn4+-rich side), the existence at low temperature of C- and G-type antiferromagnetism. The absence of ferromagnetic-antiferromagnetic competition explains that magnetoresistante properties are not observed in this system, in contrast to Mn4+-rich Ln(1-x)Ca(x)MnO(3) systems.

Abstract: Transmission electron microscopy and X-ray diffraction proved chain/ladder incommensurate single crystal structure of investigated samples. The incommensurate ratio was determined from the X-ray and electron diffraction being equal to 0.704. Diffuse scattering intensities localised on the planes perpendicular to the c*-axis and passing through the spots originating from the periodicity of chain sublattice were detected. High-angle grain boundary or twinning formed by rotation of 33.3 degrees around [100] direction was observed. High-resolution electron microscopy images revealed the stacking faults in ac planes.

Abstract: Accuracy and precision of silicon determination in biological matrices (serum, urine, water, beer and spinach) by spectrometric techniques (when necessary after acid destruction) were assessed by means of a collaborative interlaboratory trial. The trial was set up in accordance with ISO 5725-2 (1994). The relative overall repeatability standard deviation was acceptable. It varied between 4% for spinach powder (mean content: 176 mg kg(-1)) and 11% for serum (mean content: 5.33 mg L-1). On the other hand, the relative overall between-laboratory standard deviation was found to vary from a satisfactorily 15% for spinach after destruction (mean content: 3.32 mg L-1) to an unacceptable 107% for spinach powder (mean content: 176 mg kg(-1)). The overall conclusion of the trial was that silicon determination in biological matrices can properly be performed by spectrometric techniques. However, when sample pretreatment (i.e., acid destruction) is needed prior to silicon determination problems still remain.

Abstract: The melting transition of the five different lattices of a bilayer crystal is studied using the Monte-Carlo (MC) technique. We found the surprising result that the square lattice has a substantial larger melting temperature as compared to the other lattice structures, which is a consequence of the specific topology of the temperature induced defects. A new melting criterion is formulated which we show to be universal for bilayers as well as for single layer crystals.

Abstract: Rutherford backscattering and channeling spectrometry (RBS), photoluminescence (PL) spectroscopy and transmission electron microscopy (TEM) have been used to investigate macroscopic and microscopic segregation in MOCVD grown InGaN layers. The PL peak energy and In content (measured by RES) were mapped at a large number of distinct points on the samples. An indium concentration of 40%, the highest measured in this work, corresponds to a PL peak of 710 nn strongly suggesting that the light-emitting regions of the sample me very indium-rich compared to the average measured by RES. Cross-sectional TEM observations show distinctive layering of the InGaN films. The TEM study further reveals that these layers consist of amorphous pyramidal contrast features with sizes of order 10 nm The composition of these specific contrast features is shown to be In-rich compared to the nitride matrix.