Abstract: High-quality single-walled carbon nanotubes (SWNTs) are synthesized in gram amount on Fe-Mo/MgO catalysts by catalytic decomposition of CH4 in H-2 or N-2. Raman data reveal that the as-prepared SATNTs have a diameter of about 0.74-1.29 nm. It is found that the diameter of the as-prepared SWNTs can be controlled mainly by adjusting the molar ratio of Fe-Mo versus the MgO support. Several other factors that potentially influence the growth of SWNTs have been studied in detail. The experimental results show that the nature of the catalyst determines the diameter of the as-prepared SWNTs. (C) 2004 Elsevier B.V. All rights reserved.

Abstract: The relationships between incommensurability, charge ordering and magnetotransport properties in Nd0.5Ca0.5Mn1-xCrxO3 manganites have been studied by electron diffraction and lattice imaging versus temperature with 0.02 less than or equal to x less than or equal to 0.07. All compositions show an incommensurate superstructure over the whole temperature domain, despite the fact that they are ferromagnetic and conductive below 140 K, The q-vector (1/2 – delta)a* decreases with increasing temperature for all compositions x. For a given temperature q also decreases with x. Lattice images obtained at low temperature give a clear view of the characteristics of the incommensurate structure. They also provide a better understanding of the charge ordering process. The low-temperature form of the Cr-doped manganites is not a perfectly doubled cell [[2a(p)root 2 x 2a(p) x a(p)root 2]], but defects inducing a tripled cell occur pseudo-periodically. (C) 2000 Elsevier Science B.V. All rights reserved.

Abstract: 6H SiC single crystals were implanted al room temperature with 1 MeV He+ up to a fluence of 2 x 10(17) at./cm(2) RBS-channeling analysis with a 2 MeV He+ beam indicated the formation of extended defects or the generation of point defects at a constant concentration over a depth of about 1 mu m. Electron microscopy characterisation revealed the presence of two amorphous buried layers at depths of about 1,75 and 4.8 mu m. They an due to the implantation and to the analysing RES beam, respectively, No extended planar or linear faults were found in the region between the surface and the first amorphous layer. However, at the surface, a 50 nm thick amorphous layer was observed in which crystalline inclusions were embedded. Electron diffraction and HREM data of the inclusions were typical for diamond, These inclusions were even found in the crystalline SiC material below this layer, however at a reduced density.

Abstract: The structure of beta-SiC formed by carbon implantation into Si at high temperatures (850-950 degrees C) at doses ranging between 0.2 X 10(18) to 1 X 10(18) cm(-2) at 200 keV, was studied by combined cross section and high resolution transmission electron microscopy (XTEM and HRTEM). Implantation was performed on (001) and (111) Si wafers. In both cases a buried beta-SiC layer was formed having the same orientation as the Si matrix.

Abstract: The evolution of the use of the 1250 keV high-voltage electron microscope in Antwerp is sketched by illustrating a non-exhaustive set of examples in various fields. One of the main present fields of application gets some more attention, i.e. the defect studies as produced by processing steps in microelectronic devices: (i) strain-induced dislocations at the edges of various device isolation interlayers, (ii) morphologies resulting from high-energy ion implantation creating buried layers for silicon on insulator (SOI) and other implantation technologies.

Abstract: Titania nanoparticles have been deposited on inert porous silica supports with high specific surface area. These materials have potential applications in paint and textile industry as the titania particles selectively deposited on the inner surface of the silica supports act as a photocatalyst. The inert external surface is necessary to avoid photodegradation of the textile material or the paint components. The photocatalytic activity of the catalysts has been evaluated with two catalytic setups. One setup in aqueous phase, for the degradation of dyes such as rhodamine-6G, is commonly used. The second setup is a continuous flow gaseous phase setup which was used for the mineralization of ethanol as a representative volatile organic compound (VOC). The influence of the porosity and the morphology of the silica supports on the photocatalytic activity are discussed.

Abstract: Mesoporous carbon, which can be replicated from mesoporous silica and whose surface is hydrophobic, can be an ideal catalyst for the esterification of fatty acids. Here we report an easy and low cost way to prepare sulfonic acid group-functionalized mesoporous carbon. A sample of calcined mesoporous silica SBA-15 was added to an aqueous sucrose solution followed by drying and calcination at different temperatures. In contrast to existing procedures, the obtained hybrid Si/C material was then first sulfonated in H2SO4, before the final removal of the silica template in order to stabilize the porous structure towards the liquid phase sulfonation treatment. Thus the silicacarbon composites, instead of the mesoporous carbon, were successfully sulfonated to introduce SO3H groups, while keeping the ordered mesoporous structure intact. The influence of carbonization temperature was investigated, suggesting an optimum temperature of 873 K. The SO3H group-functionalized mesoporous carbon, denoted as CMK-3-873-SO3H, was characterized by means of XRD, N2 physisorption, SEM, FT-IR, elemental analysis and TEM. It followed that a uniform mesoporous carbon was obtained with an average pore size of 3.89 nm, a specific surface of 807 m2/g and a SO3H group loading of 0.39 meq/g of dry material. Compared with other solid acid catalysts, the resulting material shows enhanced activity in the acid-catalyzed esterification of oleic acid with methanol, and can be used repeatedly. The increased catalytic performance is attributed to the hydrophobic surface and larger pore size of the new catalyst. It can effectively accommodate long chain fatty acids and reject formed water, making the active sites easily accessible.

Abstract: In Bi2Sr2Ca0.6Y0.4Cu2Oy single crystals we have identified the intergrowth of two phases; a normal Bi2Sr2CaCu2Oy type phase with a 4.6b modulation period and a secondary,phase with a 9.4b modulation period. Both the two phases have orthorhombic basic structures with similar lattice parameters but different symmetries, i.e. Bbmb for the normal phase and Ccca for the secondary phase. The c-parameters of these two phases are found to vary independently upon changing the nominal Y content. The modulation characteristics of the secondary phase implies a close structural relation between the two phases. Both phases are discussed from a structural and a compositional point of view.

Abstract: The use of an energy-filtering held emission gun transmission electron microscope (CM30 FEG Ultratwin) allows, apart from imaging morphologies down to nanometer scale, the fast acquisition of high-resolution element distributions. Electrons that have lost energy corresponding to characteristic inner-shell loss edges are used to form the element maps. The production of Ultra Large-Scale Integration (ULSI) devices with dimensions below 0.25 mum requires among others the formation of a multilayer metallization scheme by means of repeatedly applying the deposition and etching of dielectrics and metals. In this work the evolution of the surface chemical species on etched Al lines in a post-etch cleaning process has been investigated by energy filtering transmission electron microscopy, with the aim to understand the role of each process step on the removal of the etching residues. (C) 2001 Elsevier Science Ltd. All rights reserved.

Abstract: This work presents a new carbonsilica hybrid material, denoted as CSM, with remarkable sorption properties. It consists of intraporous graphitic nanocrystals grown in the pores of mesoporous silica. CSM is obtained by a subtle incipient wetness impregnation of Al-containing mesoporous silica with furfuryl alcohol (FA)/hemelitol solutions. Both the volume match of the impregnation solution with that of the silica template pore volume, and the presence of Al3+ in the silica, are crucial to polymerize FA selectively inside the mesopores. Carbonization of the intraporous polymer was then performed by pyrolysis under He up to 1273 K. The resulting CSMs were examined by SEM, HRTEM, 27Al MAS NMR, N2 adsorption, XRD, TGA, TPD, XPS, pycnometry and Raman spectroscopy. Mildly oxidized graphitic-like carbon nanoblocks, consisting of a few graphene-like sheets, were thus identified inside the template mesopores. Random stacking of these carbon crystallites generates microporosity resulting in biporous materials at low carbon content and microporous materials at high carbon loadings. Very narrow pore distributions were obtained when pyrolysis was carried out under slow heating rate, viz. 1 K min−1. Adsorption and shape selective properties of the carbon filled mesoporous silica were studied by performing pulse chromatography and breakthrough experiments, and by measuring adsorption isotherms of linear and branched alkanes. Whereas the parent mesoporous silica shows unselective adsorption, their CSM analogues preferentially adsorb linear alkanes. The sorption capacity and selectivity can be adjusted by changing the pore size of the template or by varying the synthesis conditions. A relation between the carbon crystallites size and the shape selective behaviour of the corresponding CSM for instance is demonstrated. Most interestingly, CSM shows separation factors for linear and branched alkanes up to values comparable to those of zeolitic molecular sieves.