“Effect of selenium content of CuInSex alloy nanopowder precursors on recrystallization of printed CuInSe2 absorber layers during selenization heat treatment”. E Zaghi A, Buffière M, Koo J, Brammertz G, Batuk M, Verbist C, Hadermann J, Kim WK, Meuris M, Poortmans J, Vleugels J;, Thin solid films : an international journal on the science and technology of thin and thick films , 1 (2014). http://doi.org/10.1016/j.tsf.2014.10.003
Abstract: Polycrystalline CuInSe2 semiconductors are efficient light absorber materials for thin film solar cell technology, whereas printing is one of the promising low cost and non-vacuum approaches for the fabrication of thin film solar cells. The printed precursors are transformed into a dense polycrystalline CuInSe2 semiconductor film via thermal treatment in ambient selenium atmosphere (selenization). In this study, the effect of the selenium content in high purity mechanically synthesized CuInSex (x = 2, 1.5, 1 or 0.5) alloy precursors on the recrystallization of the CuInSe2 phase during the selenization process was investigated. The nanostructure and phase variation of CuInSex nanopowders were investigated by different characterization techniques. The recrystallization process of the 12 μm thick CuInSex coatings into the CuInSe2 phase during selenization in selenium vapor was investigated via in-situ high temperature X-ray diffraction. The CuInSex precursors with lower selenium content showed a more pronounced phase conversion into CuInSe2 compared to the higher selenium content CuInSex precursors. Moreover, the CuInSex (x = 0.5 and 1) precursor resulted in a denser polycrystalline CuInSe2 semiconductor film with larger crystals. This could be attributed to a more intensive atomic interdiffusion within the CuInSex precursor system compared to a CuInSe2 phase precursor, and the formation of intermediate CuSe and CuSe2 fluxing phases during selenization.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.879
Times cited: 7
DOI: 10.1016/j.tsf.2014.10.003
|
|
|
|
Batuk M (2013) New perovskite-based homologous series : AnBnO3n-2 and An+1BnO3n-1Cl. Antwerpen
Keywords: Doctoral thesis; Electron microscopy for materials research (EMAT)
|
|
|
|
“Pb5Fe3TiO11Cl : a rare example of Ti(IV) in a square pyramidal oxygen coordination”. Batuk M, Batuk D, Abakumov AM, Hadermann J, Journal of solid state chemistry 215, 245 (2014). http://doi.org/10.1016/j.jssc.2014.04.002
Abstract: A new oxychloride Pb5Fe3TiO11Cl has been synthesized using the solid state method. Its crystal and magnetic structure was investigated in the 1.5550 K temperature range using electron diffraction, high angle annular dark field scanning transmission electron microscopy, atomic resolution energy dispersive X-ray spectroscopy, neutron and X-ray powder diffraction. At room temperature Pb5Fe3TiO11Cl crystallizes in the P4/mmm space group with the unit cell parameters a=3.91803(3) Å and c=19.3345(2) Å. Pb5Fe3TiO11Cl is a new n=4 member of the oxychloride perovskite-based homologous series An+1BnO3n−1Cl. The structure is built of truncated Pb3Fe3TiO11 quadruple perovskite blocks separated by CsCl-type Pb2Cl slabs. The perovskite blocks consist of two layers of (Fe,Ti)O6 octahedra sandwiched between two layers of (Fe,Ti)O5 square pyramids. The Ti4+ cations are preferentially located in the octahedral layers, however, the presence of a noticeable amount of Ti4+ in a five-fold coordination environment has been undoubtedly proven using neutron powder diffraction and atomic resolution compositional mapping. Pb5Fe3TiO11Cl is antiferromagnetically ordered below 450(10) K. The ordered Fe magnetic moments at 1.5 K are 4.06(4) μB and 3.86(5) μB on the octahedral and square-pyramidal sites, respectively.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 4
DOI: 10.1016/j.jssc.2014.04.002
|
|
|
|
“Process variability in Cu2ZnSnSe4 solar cell devices: Electrical and structural investigations”. Brammertz G, Buffiere M, Verbist C, Bekaert J, Batuk M, Hadermann J, et al, The conference record of the IEEE Photovoltaic Specialists Conference
T2 –, IEEE 42nd Photovoltaic Specialist Conference (PVSC), JUN 14-19, 2015, New Orleans, LA (2015)
Abstract: We have fabricated 9.7% efficient Cu2ZnSnSe4/CdS/ZnO solar cells by H2Se selenization of sequentially sputtered metal layers. Despite the good efficiency obtained, process control appears to be difficult. In the present contribution we compare the electrical and physical properties of two devices with nominal same fabrication procedure, but 1% and 9.7% power conversion efficiency respectively. We identify the problem of the lower performing device to be the segregation of ZnSe phases at the backside of the sample. This ZnSe seems to be the reason for the strong bias dependent photocurrent observed in the lower performing devices, as it adds a potential barrier for carrier collection. The reason for the different behavior of the two nominally same devices is not fully understood, but speculated to be related to sputtering variability.
Keywords: P1 Proceeding; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
|
|
|
|
“Sensitivity of nanocrystalline tungsten oxide to CO and ammonia gas determined by surface catalysts”. Marikutsa A, Yang L, Rumyantseva M, Batuk M, Hadermann J, Gaskov A, Sensors and actuators : B : chemical 277, 336 (2018). http://doi.org/10.1016/J.SNB.2018.09.004
Abstract: Nanocrystalline tungsten oxide with variable particle size and surface area was synthesized by aqueous deposition and heat treatment for use in resistive gas sensors. Surface modification with 1 wt.% Pd and Ru was performed by impregnation to improve the sensitivity to CO and ammonia. Acid and oxidation surface sites were evaluated by temperature-programmed techniques using probe molecules. The surface acidity dropped with increasing particle size, and was weakly affected by additives. Lower crystallinity of WO3 and the presence of Ru species favoured temperature-programmed reduction of the materials. Modifying WO3 increased its sensitivity, to CO at ambient condition for modification by Pd and to NH3 at elevated temperature for Ru modification. An in situ infrared study of the gas – solid interaction showed that the catalytic additives change the interaction route of tungsten oxide with the target gases and make the reception of detected molecules independent of the semiconductor oxide matrix.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1016/J.SNB.2018.09.004
|
|
|
|
“Synthesis and structural characterization of a novel Sillén &ndash, Aurivillius bismuth oxyhalide, PbBi3VO7.5Cl, and its derivatives”. Charkin DO, Plokhikh IV, Kazakov SM, Kalmykov SN, Akinfiev VS, Gorbachev AV, Batuk M, Abakumov AM, Teterin YA, Maslakov KI, Teterin AY, Ivanov KE, Solid state sciences 75, 27 (2018). http://doi.org/10.1016/j.solidstatesciences.2017.11.006
Abstract: A new Sillen – Aurivillius family of layered bismuth oxyhalides has been designed and successfully constructed on the basis of PbBiO2X(X = halogen) synthetic perites and g-form of Bi2VO5.5 solid elec- trolyte. This demonstrates, for the first time, the ability of the latter to serve as a building block in construction of mixed-layer structures. The parent compound PbBi3VO7.5-dCl (d = 0.05) has been investigated by powder XRD, TEM, XPS methods and magnetic susceptibility measurements. An unexpected but important condition for the formation of the mixed-layer structure is partial (ca. 5%) reduction of VV into VIV which probably suppresses competitive formation of apatite-like Pb – Bi vanadates. This reduction also stabilizes the g polymorphic form of Bi2VO5.5 not only in the intergrowth structure, but in Bi2V1-xMxO5.5-y (M – Nb, Sb) solid solutions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.811
Times cited: 1
DOI: 10.1016/j.solidstatesciences.2017.11.006
|
|
|
|
“Revealing pH-Dependent Activities and Surface Instabilities for Ni-Based Electrocatalysts during the Oxygen Evolution Reaction”. Yang C, Batuk M, Jacquet Q, Rousse G, Yin W, Zhang L, Hadermann J, Abakumov AM, Cibin G, Chadwick A, Tarascon J-M, Grimaud A, ACS energy letters , 2884 (2018). http://doi.org/10.1021/acsenergylett.8b01818
Abstract: Multiple electrochemical processes are involved at the catalyst/ electrolyte interface during the oxygen evolution reaction (OER). With the purpose of elucidating the complexity of surface dynamics upon OER, we systematically studied two Ni-based crystalline oxides (LaNiO3−δ and La2Li0.5Ni0.5O4) and compared them with the state-of-the-art Ni−Fe (oxy)- hydroxide amorphous catalyst. Electrochemical measurements such as rotating ring disk electrode (RRDE) and electrochemical quartz microbalance microscopy (EQCM) coupled with a series of physical characterizations including transmission electron microscopy (TEM) and X-ray absorption spectroscopy (XAS) were conducted to unravel the exact pH effect on both the OER activity and the catalyst stability. We demonstrate that for Ni-based crystalline catalysts the rate for surface degradation depends on the pH and is greater than the rate for surface reconstruction. This behavior is unlike that for the amorphous Ni oxyhydroxide catalyst, which is found to be more stable and pH-independent.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
DOI: 10.1021/acsenergylett.8b01818
|
|
|
|
“First-principles study of CO and OH adsorption on in-doped ZnO surfaces”. Saniz R, Sarmadian N, Partoens B, Batuk M, Hadermann J, Marikutsa A, Rumyantseva M, Gaskov A, Lamoen D, The journal of physics and chemistry of solids 132, 172 (2019). http://doi.org/10.1016/j.jpcs.2019.04.023
Abstract: We present a first-principles computational study of CO and OH adsorption on non-polar ZnO (10¯10) surfaces doped with indium. The calculations were performed using a model ZnO slab. The position of the In dopants was varied from deep bulk-like layers to
the surface layers. It was established that the preferential location of the In atoms is at the surface by examining the dependence of
the defect formation energy as well as the surface energy on In location. The adsorption sites on the surface of ZnO and the energy
of adsorption of CO molecules and OH-species were determined in connection to In doping. It was found that OH has higher
bonding energy to the surface than CO. The presence of In atoms at the surface of ZnO is favorable for CO adsorption, resulting
in an elongation of the C-O bond and in charge transfer to the surface. The effect of CO and OH adsorption on the electronic
and conduction properties of surfaces was assessed. We conclude that In-doped ZnO surfaces should present a higher electronic
response upon adsorption of CO.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 2.059
Times cited: 7
DOI: 10.1016/j.jpcs.2019.04.023
|
|
|
|
“Spinel nanoparticles on stick-like Freudenbergite nanocomposites as effective smart-removal photocatalysts for the degradation of organic pollutants under visible light”. Ciocarlan R-G, Seftel EM, Gavrila R, Suchea M, Batuk M, Mertens M, Hadermann J, Cool P, Journal Of Alloys And Compounds 820, 153403 (2020). http://doi.org/10.1016/j.jallcom.2019.153403
Abstract: A series of mixed nanocomposite materials was synthetized, containing a Ferrite phase type Zn1-xNixFe2O4 and a Freudenbergite phase type Na2Fe2Ti6O16, where x = 0; 0.2; 0.4; 0.6; 0.8; 1. The choice for this combination is based on the good adsorption properties of Freudenbergite for dye molecules, and the small bandgap energy of Ferrite spinel, allowing activation of the catalysts under visible light irradiation. A two steps synthesis protocol was used to obtain the smart-removal nanocomposites. Firstly, the spinel structure was obtained via the co-precipitation route followed by the addition of the Ti-source and formation of the Freudenbergite system. The role of cations on the formation mechanism and an interesting interchange of cations between spinel and Freudenbergite structures was clarified by a TEM study. Part of the Ti4+ penetrated the spinel structure and, at the same time, part of the Fe3+ formed the Freudenbergite system. The photocatalytic activity was studied under visible light, reaching for the best catalysts a 67% and 40% mineralization degree for methylene blue and rhodamine 6G respectively, after 6 h of irradiation. In the same conditions, the well-known commercial P25 (Degussa) managed to mineralize only 12% and 3% of methylene blue and rhodamine 6G, respectively. Due to the remarkable magnetic properties of Ferrites, a convenient recovery and reuse of the catalysts is possible after the photocatalytic tests. Based on the excellent catalytic performance of the nanocomposites under visible light and their ease of separation out of the solution after the catalytic reaction, the newly developed composite catalysts are considered very effective for wastewater treatment.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 6.2
DOI: 10.1016/j.jallcom.2019.153403
|
|
|
|
“Sub-ppm H2S sensing by tubular ZnO-Co3O4 nanofibers”. Rumyantseva MN, Vladimirova SA, Platonov VB, Chizhov AS, Batuk M, Hadermann J, Khmelevsky NO, Gaskov AM, Sensors And Actuators B-Chemical 307, 127624 (2020). http://doi.org/10.1016/j.snb.2019.127624
Abstract: Tubular ZnO – Co3O4 nanofibers were co-electrospun from polymer solution containing zinc and cobalt acetates. Phase composition, cobalt electronic state and element distribution in the fibers were investigated by XRD, SEM, HRTEM, HAADF-STEM with EDX mapping, and XPS. Bare ZnO has high selective sensitivity to NO and NO2, while ZnO-Co3O4 composites demonstrate selective sensitivity to H2S in dry and humid air. This effect is discussed in terms of transformation of cobalt oxides into cobalt sulfides and change in the acidity of ZnO oxide surface upon cobalt doping. Reduction in response and recovery time is attributed to the formation of a tubular structure facilitating gas transport through the sensitive layer.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.401
DOI: 10.1016/j.snb.2019.127624
|
|
|
|
“The path towards efficient wide band gap thin-film kesterite solar cells with transparent back contact for viable tandem application”. Khelifi S, Brammertz G, Choubrac L, Batuk M, Yang S, Meuris M, Barreau N, Hadermann J, Vrielinck H, Poelman D, Neyts K, Vermang B, Lauwaert J, Solar Energy Materials And Solar Cells 219, 110824 (2021). http://doi.org/10.1016/j.solmat.2020.110824
Abstract: Wide band gap thin-film kesterite solar cell based on non-toxic and earth-abundant materials might be a suitable candidate as a top cell for tandem configuration in combination with crystalline silicon as a bottom solar cell. For this purpose and based on parameters we have extracted from electrical and optical characterization techniques of Cu2ZnGeSe4 absorbers and solar cells, a model has been developed to describe the kesterite top cell efficiency limitations and to investigate the different possible configurations with transparent back contact for fourterminal tandem solar cell application. Furthermore, we have studied the tandem solar cell performance in view of the band gap and the transparency of the kesterite top cell and back contact engineering. Our detailed analysis shows that a kesterite top cell with efficiency > 14%, a band gap in the range of 1.5-1.7 eV and transparency above 80% at the sub-band gaps photons energies are required to achieve a tandem cell with higher efficiency than with a single silicon solar cell.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 4.784
DOI: 10.1016/j.solmat.2020.110824
|
|
|
|
“Photoresistive gas sensor based on nanocrystalline ZnO sensitized with colloidal perovskite CsPbBr3 nanocrystals”. Chizhov As, Rumyantseva Mn, Drozdov Ka, Krylov Iv, Batuk M, Hadermann J, Filatova Dg, Khmelevsky No, Kozlovsky Vf, Maltseva Ln, Gaskov Am, Sensors And Actuators B-Chemical 329, 129035 (2021). http://doi.org/10.1016/j.snb.2020.129035
Abstract: The development of sensor materials of which gas sensitivity activates under light illumination is of great importance for the design of portable gas analyzers with low power consumption. In the present work a ZnO/CsPbBr3 nanocomposite based on nanocrystalline ZnO and colloidal cubic-shaped perovskite CsPbBr3 nanocrystals (NCs) capped by oleic acide and oleylamine was synthesized. The individual materials and obtained nanocomposite are characterized by x-ray diffraction, low-temperature nitrogen adsorption, x-ray photoelectron spectroscopy, high angle annular dark field scanning transmission electron microscopy with energy-dispersive Xray spectroscopy mapping and UV-vis absorption spectroscopy. The spectral dependence of the photoconductivity of the ZnO/CsPbBr3 nanocomposite reveals a well-defined peak that strongly correlates with the its optical absorption spectrum. The nanocomposite ZnO/CsPbBr3 shows enhanced photoresponse under visible light illumination (lambda(max) = 470 nm, 8 mW/cm(2)) in air, oxygen and argone, compared with pure nanocrystalline ZnO. Under periodic illumination in the temperature range of 25-100 degrees C, the ZnO/CsPbBr3 nanocomposite shows a sensor response to 0.5-3.0 ppm NO2, unlike pure nanocrystalline ZnO matrix, which demonstrates sensor sensitivity to NO2 under the same conditions above 100 degrees C. The effects of humidity on the sensor signal and photoresponse are also discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.401
DOI: 10.1016/j.snb.2020.129035
|
|
|
|
“Topotactic redox cycling in SrFeO2.5+&delta, explored by 3D electron diffraction in different gas atmospheres”. Batuk M, Vandemeulebroucke D, Ceretti M, Paulus W, Hadermann J, Journal of materials chemistry A : materials for energy and sustainability (2022). http://doi.org/10.1039/D2TA03247C
Abstract: For oxygen conducting materials applied in solid oxide fuel cells and chemical-looping processes, the understanding of the oxygen diffusion mechanism and the materials’ crystal structure at different stages of the redox reactions is a key parameter to control their performance. In this paper we report the first ever in situ 3D ED experiment in a gas environment and with it uncover the structure evolution of SrFeO2.5 as notably different from that reported from in situ X-ray and in situ neutron powder diffraction studies in gas environments. Using in situ 3D ED on submicron sized single crystals obtained from a high quality monodomain SrFeO2.5 single crystal , we observe the transformation under O2 flow of SrFeO2.5 with an intra- and interlayer ordering of the left and right twisted (FeO4) tetrahedral chains (space group Pcmb) into consecutively SrFeO2.75 with space group Cmmm (at 350°C, 33% O2) and SrFeO3-δ with space group Pm3 ̅m (at 400°C, 100% O2). Upon reduction in H2 flow, the crystals return to the brownmillerite structure with intralayer order, but without regaining the interlayer order of the pristine crystals. Therefore, redox cycling of SrFeO2.5 crystals in O2 and H2 introduces stacking faults into the structure, resulting in an I2/m(0βγ)0s symmetry with variable β.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 11.9
DOI: 10.1039/D2TA03247C
|
|
|
|
“Incommensurate Modulations and Perovskite Growth in LaxSr2–xMnO4−δAffecting Solid Oxide Fuel Cell Conductivity”. Vandemeulebroucke D, Batuk M, Hajizadeh A, Wastiaux M, Roussel P, Hadermann J, Chemistry of Materials (2024). http://doi.org/10.1021/acs.chemmater.3c03199
Abstract: Ruddlesden-Popper La????Sr2−????MnO4−???? materials are interesting symmetric solid oxide
fuel cell electrodes due to their good redox stability, mixed ionic and electronic conducting behavior and thermal expansion that matches well with common electrolytes. In reducing environments – as at a solid oxide fuel cell anode – the x = 0.5 member, i.e. La0.5Sr1.5MnO4−????, has a much higher total conductivity than compounds with a different La/Sr ratio, although all those compositions have the same K2NiF4-type I4/mmm structure. The origin for this conductivity difference is not yet known in literature. Now, a combination of in-situ and ex-situ 3D electron diffraction, high-resolution imaging, energy-dispersive X-ray analysis and electron energy-loss spectroscopy uncovered clear differences between x=0.25 and x=0.5 in the pristine structure, as well as in the transformations upon high-temperature reduction. In La0.5Sr1.5MnO4−????, Ruddlesden-Popper n=2 layer defects and an amorphous surface layer are present, but not in La0.25Sr1.75MnO4−????. After annealing at 700°C in 5% H2/Ar, La0.25Sr1.75MnO4−???? transforms to a tetragonal 2D incommensurately modulated structure with modulation vectors ⃗????1 = 0.2848(1) · (⃗????* +⃗????*) and ⃗????2 =0.2848(1) · (⃗????* – ⃗????*), whereas La0.5Sr1.5MnO4−???? only partially transforms to an orthorhombic 1D incommensurately modulated structure,
with ⃗???? = 0.318(2) · ⃗????*. Perovskite domains grow at the crystal edge at 700°C in 5%
H2 or vacuum, due to the higher La concentration on the surface compared to the bulk, which leads to a different thermodynamic equilibrium. Since it is known that a lower degree of oxygen vacancy ordering and a higher amount of perovskite blocks enhance oxygen mobility, those differences in defect structure and structural transformation upon reduction, might all contribute to the higher conductivity of La0.5Sr1.5MnO4−???? in solid oxide fuel cell anode conditions compared to other La/Sr ratios.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 8.6
DOI: 10.1021/acs.chemmater.3c03199
|
|
|
|
“Misfit phase (BiSe)1.10NbSe2 as the origin of superconductivity in niobium-doped bismuth selenide”. Kamminga ME, Batuk M, Hadermann J, Clarke SJ, Communications Materials 1, 82 (2020). http://doi.org/10.1038/s43246-020-00085-z
Abstract: Topological superconductivity is of great contemporary interest and has been proposed in doped Bi<sub>2</sub>Se<sub>3</sub>, in which electron-donating atoms such as Cu, Sr or Nb have been intercalated into the Bi<sub>2</sub>Se<sub>3</sub>structure. For Nb<sub><italic>x</italic></sub>Bi<sub>2</sub>Se<sub>3</sub>, with<italic>T</italic><sub>c</sub> ~ 3 K, it is assumed in the literature that Nb is inserted in the van der Waals gap. However, in this work an alternative origin for the superconductivity in Nb-doped Bi<sub>2</sub>Se<sub>3</sub>is established. In contrast to previous reports, it is deduced that Nb intercalation in Bi<sub>2</sub>Se<sub>3</sub>does not take place. Instead, the superconducting behaviour in samples of nominal composition Nb<sub><italic>x</italic></sub>Bi<sub>2</sub>Se<sub>3</sub>results from the (BiSe)<sub>1.10</sub>NbSe<sub>2</sub>misfit phase that is present in the sample as an impurity phase for small<italic>x</italic>(0.01 ≤ <italic>x</italic> ≤ 0.10) and as a main phase for large<italic>x</italic>(<italic>x</italic> = 0.50). The structure of this misfit phase is studied in detail using a combination of X-ray diffraction and transmission electron microscopy techniques.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1038/s43246-020-00085-z
|
|
|
|
“Anion redox as a means to derive layered manganese oxychalcogenides with exotic intergrowth structures”. Sasaki S, Giri S, Cassidy SJ, Dey S, Batuk M, Vandemeulebroucke D, Cibin G, Smith RI, Holdship P, Grey CP, Hadermann J, Clarke SJ, Nature communications 14, 2917 (2023). http://doi.org/10.1038/S41467-023-38489-3
Abstract: Topochemistry enables step-by-step conversions of solid-state materials often leading to metastable structures that retain initial structural motifs. Recent advances in this field revealed many examples where relatively bulky anionic constituents were actively involved in redox reactions during (de)intercalation processes. Such reactions are often accompanied by anion-anion bond formation, which heralds possibilities to design novel structure types disparate from known precursors, in a controlled manner. Here we present the multistep conversion of layered oxychalcogenides Sr(2)MnO(2)Cu(1.5)Ch(2) (Ch=S, Se) into Cu-deintercalated phases where antifluorite type [Cu(1.5)Ch(2)](2.5-) slabs collapsed into two-dimensional arrays of chalcogen dimers. The collapse of the chalcogenide layers on deintercalation led to various stacking types of Sr(2)MnO(2)Ch(2) slabs, which formed polychalcogenide structures unattainable by conventional high-temperature syntheses. Anion-redox topochemistry is demonstrated to be of interest not only for electrochemical applications but also as a means to design complex layered architectures. Low temperature chemical transformations of solids using high-energy intermediates have enabled the synthesis of a new series of layered oxide chalcogenide containing oxidised chalcogenide dimers promising a new range of solids.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 16.6
DOI: 10.1038/S41467-023-38489-3
|
|
|
|
“3Y-TZP ceramics with improved hydrothermal degradation resistance and fracture toughness”. Zhang F, Vanmeensel K, Inokoshi M, Batuk M, Hadermann J, Van Meerbeek B, Naert I, Vleugels J, Journal of the European Ceramic Society 34, 2453 (2014). http://doi.org/10.1016/j.jeurceramsoc.2014.02.026
Abstract: Different factors such as the way of incorporating the Y2O3 stabilizer, alumina addition and sintering temperature were assessed with the goal to improve the low temperature degradation (LTD) resistance of 3Y-TZP without compromising on the mechanical properties. The degradation of hydrothermally treated specimens was studied by X-ray diffraction, micro-Raman spectroscopy and scanning electron microscopy. Decreasing the sintering temperature decreased the LTD susceptibility of 3Y-TZPs but did not allow to obtain a LTD resistant 3Y-TZP with optimized mechanical properties. Alumina addition along with the use of Y2O3 stabilizer coated starting powder allowed to combine both an excellent toughness and LTD resistance, as compared to alumina-free and stabilizer co-precipitated powder based equivalents. Transmission electron microscopy revealed that the improved LTD resistance could be attributed to the segregation of Al3+ at the grain boundary and the heterogeneously distributed Y3+ stabilizer.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 48
DOI: 10.1016/j.jeurceramsoc.2014.02.026
|
|
|
|
“Effects of Ag additive in low temperature CO detection with In2O3 based gas sensors”. Naberezhnyi D, Rumyantseva M, Filatova D, Batuk M, Hadermann J, Baranchikov A, Khmelevsky N, Aksenenko A, Konstantinova E, Gaskov A, Nanomaterials 8, 801 (2018). http://doi.org/10.3390/NANO8100801
Abstract: Nanocomposites In2O3/Ag obtained by ultraviolet (UV) photoreduction and impregnation methods were studied as materials for CO sensors operating in the temperature range 25-250 degrees C. Nanocrystalline In2O3 and In2O3/Ag nanocomposites were characterized by X-ray diffraction (XRD), single-point Brunauer-Emmet-Teller (BET) method, scanning electron microscopy (SEM), transmission electron microscopy (TEM), and high angle annular dark field scanning transmission electron microscopy (HAADF-STEM) with energy dispersive X-ray (EDX) mapping. The active surface sites were investigated using Fourier-transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), electron paramagnetic resonance (EPR) spectroscopy and thermo-programmed reduction with hydrogen (TPR-H-2) method. Sensor measurements in the presence of 15 ppm CO demonstrated that UV treatment leads to a complete loss of In2O3 sensor sensitivity, while In2O3/Ag-UV nanocomposite synthesized by UV photoreduction demonstrates an increased sensor signal to CO at T < 200 degrees C. The observed high sensor response of the In2O3/Ag-UV nanocomposite at room temperature may be due to the realization of an additional mechanism of CO oxidation with participation of surface hydroxyl groups associated via hydrogen bonds.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
DOI: 10.3390/NANO8100801
|
|
|
|
“Effect of cation dopant radius on the hydrothermal stability of tetragonal zirconia: Grain boundary segregation and oxygen vacancy annihilation”. Zhang F, Batuk M, Hadermann J, Manfredi G, Mariën A, Vanmeensel K, Inokoshi M, Van Meerbeek B, Naert I, Vleugels J, Acta materialia 106, 48 (2016). http://doi.org/10.1016/j.actamat.2015.12.051
Abstract: The hydrothermal aging stability of 3Y-TZP-xM2O3 (M = La, Nd, Sc) was investigated as a function of 0.02–5 mol% M2O3 dopant content and correlated to the overall phase content, t-ZrO2 lattice parameters, grain size distribution, grain boundary chemistry and ionic conductivity.
The increased aging stability with increasing Sc2O3 content and the optimum content of 0.4–0.6 mol% Nd2O3 or 0.2–0.4 mol% La2O3, resulting in the highest aging resistance, could be directly related to the constituent phases and the lattice parameters of the remaining tetragonal zirconia.
At low M2O3 dopant contents ≤0.4 mol%, the different aging behavior of tetragonal zirconia was attributed to the defect structure of the zirconia grain boundary which was influenced by the dopant cation radius. It was observed that the grain boundary ionic resistivity and the aging resistance followed the same trend: La3+ > Nd3+ > Al3+ > Sc3+, proving that hydrothermal aging is driven by the diffusion of water-derived mobile species through the oxygen vacancies. Accordingly, we elucidated the underlying mechanism by which a larger trivalent cation segregating at the zirconia grain boundary resulted in a higher aging resistance.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 5.301
Times cited: 37
DOI: 10.1016/j.actamat.2015.12.051
|
|
|
|
“Influence of Mono- and Bimetallic PtOx, PdOx, PtPdOx Clusters on CO Sensing by SnO2 Based Gas Sensors”. Kutukov P, Rumyantseva M, Krivetskiy V, Filatova D, Batuk M, Hadermann J, Khmelevsky N, Aksenenko A, Gaskov A, Nanomaterials 8, 917 (2018). http://doi.org/10.3390/nano8110917
Abstract: To obtain a nanocrystalline SnO2 matrix and mono- and bimetallic nanocomposites SnO2/Pd, SnO2/Pt, and SnO2/PtPd, a flame spray pyrolysis with subsequent impregnation was used. The materials were characterized using X-ray diffraction (XRD), a single-point BET method, transmission electron microscopy (TEM), and high angle annular dark field scanning transmission electron microscopy (HAADF-STEM) with energy dispersive X-ray (EDX) mapping. The electronic state of the metals in mono- and bimetallic clusters was determined using X-ray photoelectron spectroscopy (XPS). The active surface sites were investigated using the Fourier Transform infrared spectroscopy (FTIR) and thermo-programmed reduction with hydrogen (TPR-H-2) methods. The sensor response of blank SnO2 and nanocomposites had a carbon monoxide (CO) level of 6.7 ppm and was determined in the temperature range 60-300 degrees C in dry (Relative Humidity (RH) = 0%) and humid (RH = 20%) air. The sensor properties of the mono- and bimetallic nanocomposites were analyzed on the basis of information on the electronic state, the distribution of modifiers in SnO2 matrix, and active surface centers. For SnO2/PtPd, the combined effect of the modifiers on the electrophysical properties of SnO2 explained the inversion of sensor response from n- to p-types observed in dry conditions.
Keywords: A1 Journal Article; Electron Microscopy for Materials Science (EMAT) ;
Impact Factor: 3.553
Times cited: 7
DOI: 10.3390/nano8110917
|
|
|
|
“Recent Advances in Transmission Electron Microscopy for Materials Science at the EMAT Lab of the University of Antwerp”. Guzzinati G, Altantzis T, Batuk M, De Backer A, Lumbeeck G, Samaee V, Batuk D, Idrissi H, Hadermann J, Van Aert S, Schryvers D, Verbeeck J, Bals S, Materials 11, 1304 (2018). http://doi.org/10.3390/ma11081304
Abstract: The rapid progress in materials science that enables the design of materials down to the nanoscale also demands characterization techniques able to analyze the materials down to the same scale, such as transmission electron microscopy. As Belgium’s foremost electron microscopy group, among the largest in the world, EMAT is continuously contributing to the development of TEM techniques, such as high-resolution imaging, diffraction, electron tomography, and spectroscopies, with an emphasis on quantification and reproducibility, as well as employing TEM methodology at the highest level to solve real-world materials science problems. The lab’s recent contributions are presented here together with specific case studies in order to highlight the usefulness of TEM to the advancement of materials science.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.654
Times cited: 15
DOI: 10.3390/ma11081304
|
|
|
|
“Topochemical deintercalation of Li from layered LiNiB : toward 2D MBene”. Bhaskar G, Gvozdetskyi V, Batuk M, Wiaderek KM, Sun Y, Wang R, Zhang C, Carnahan SL, Wu X, Ribeiro RA, Bud'ko SL, Canfield PC, Huang W, Rossini AJ, Wang C-Z, Ho K-M, Hadermann J, Zaikina J V, Journal Of The American Chemical Society 143, 4213 (2021). http://doi.org/10.1021/JACS.0C11397
Abstract: The pursuit of two-dimensional (2D) borides, MBenes, has proven to be challenging, not the least because of the lack of a suitable precursor prone to the deintercalation. Here, we studied room-temperature topochemical deintercalation of lithium from the layered polymorphs of the LiNiB compound with a considerable amount of Li stored in between [NiB] layers (33 at. % Li). Deintercalation of Li leads to novel metastable borides (Li similar to 0.5NiB) with unique crystal structures. Partial removal of Li is accomplished by exposing the parent phases to air, water, or dilute HCl under ambient conditions. Scanning transmission electron microscopy and solid-state Li-7 and B-1(1) NMR spectroscopy, combined with X-ray pair distribution function (PDF) analysis and DFT calculations, were utilized to elucidate the novel structures of (Li similar to 0.5NiB) and the mechanism of Li-deintercalation. We have shown that the deintercalation of Li proceeds via a “zip-lock” mechanism, leading to the condensation of single [NiB] layers into double or triple layers bound via covalent bonds, resulting in structural fragments with Li[NiB](2) and Li[NiB](3) compositions. The crystal structure of Li similar to 0.5NiB is best described as an intergrowth of the ordered single [NiB], double [NiB](2), or triple [NiB](3) layers alternating with single Li layers; this explains its structural complexity. The formation of double or triple [NiB] layers induces a change in the magnetic behavior from temperature-independent paramagnets in the parent LiNiB compounds to the spin-glassiness in the deintercalated Li similar to 0.5NiB counterparts. LiNiB compounds showcase the potential to access a plethora of unique materials, including 2D MBenes (NiB).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
DOI: 10.1021/JACS.0C11397
|
|
|
|
“Determination of spinel content in cycled Li1.2Ni0.13Mn0.54Co0.13O2 using three-dimensional electron diffraction and precession electron diffraction”. Quintelier M, Perkisas T, Poppe R, Batuk M, Hendrickx M, Hadermann J, Symmetry-Basel 13, 1989 (2021). http://doi.org/10.3390/SYM13111989
Abstract: Among lithium battery cathode materials, Li1.2Ni0.13Mn0.54Co0.13O2 (LR-NMC) has a high theoretical capacity, but suffers from voltage and capacity fade during cycling. This is partially ascribed to transition metal cation migration, which involves the local transformation of the honeycomb layered structure to spinel-like nano-domains. Determination of the honeycomb layered/spinel phase ratio from powder X-ray diffraction data is hindered by the nanoscale of the functional material and the domains, diverse types of twinning, stacking faults, and the possible presence of the rock salt phase. Determining the phase ratio from transmission electron microscopy imaging can only be done for thin regions near the surfaces of the crystals, and the intense beam that is needed for imaging induces the same transformation to spinel as cycling does. In this article, it is demonstrated that the low electron dose sufficient for electron diffraction allows the collection of data without inducing a phase transformation. Using calculated electron diffraction patterns, we demonstrate that it is possible to determine the volume ratio of the different phases in the particles using a pair-wise comparison of the intensities of the reflections. Using this method, the volume ratio of spinel structure to honeycomb layered structure is determined for a submicron sized crystal from experimental three-dimensional electron diffraction (3D ED) and precession electron diffraction (PED) data. Both twinning and the possible presence of the rock salt phase are taken into account. After 150 charge-discharge cycles, 4% of the volume in LR-NMC particles was transformed irreversibly from the honeycomb layered structure to the spinel structure. The proposed method would be applicable to other multi-phase materials as well.
Keywords: A1 Journal article; Engineering sciences. Technology; Engineering Management (ENM); Electron microscopy for materials research (EMAT)
Impact Factor: 1.457
DOI: 10.3390/SYM13111989
|
|
|
|
“Pb2.85Ba2.15Fe4SnO13 : a new member of the AnBnO3n-2 anion-deficient perovskite-based homologous series”. Korneychik OE, Batuk M, Abakumov AM, Hadermann J, Rozova MG, Sheptyakov DV, Pokholok KV, Filimonov DS, Antipov EV, Journal of solid state chemistry 184, 3150 (2011). http://doi.org/10.1016/j.jssc.2011.09.029
Abstract: Pb2.85Ba2.15Fe4SnO13, a new n=5 member of the anion-deficient perovskite based AnBnO3n−2 (A=Pb, Ba, B=Fe, Sn) homologous series, was synthesized by the solid state method. The crystal structure of Pb2.85Ba2.15Fe4SnO13 was investigated using a combination of neutron powder diffraction, electron diffraction, high angle annular dark field scanning transmission electron microscopy and Mössbauer spectroscopy. It crystallizes in the Ammm space group with unit cell parameters a=5.7990(1) Å, b=4.04293(7) Å and c=26.9561(5) Å. The Pb2.85Ba2.15Fe4SnO13 structure consists of quasi two-dimensional perovskite blocks separated by 1/2[110](1̄01)p crystallographic shear (CS) planes. The corner-sharing FeO6 octahedra at the CS planes are transformed into edge-sharing FeO5 distorted tetragonal pyramids. The octahedral positions in the perovskite blocks between the CS planes are jointly taken up by Fe and Sn, with a preference of Sn towards the position at the center of the perovskite block. The chains of FeO5 pyramids and (Fe,Sn)O6 octahedra of the perovskite blocks delimit six-sided tunnels at the CS planes occupied by double chains of Pb atoms. The compound is antiferromagnetically ordered below TN=368±15 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 7
DOI: 10.1016/j.jssc.2011.09.029
|
|
|
|
“Strength, toughness and aging stability of highly-translucent Y-TZP ceramics for dental restorations”. Zhang F, Inokoshi M, Batuk M, Hadermann J, Naert I, Van Meerbeek B, Vleugels J, Dental materials 32, E327 (2016). http://doi.org/10.1016/J.DENTAL.7016.09.075
Abstract: Objective. The aim was to evaluate the optical properties, mechanical properties and aging stability of yttria-stabilized zirconia with different compositions, highlighting the influence of the alumina addition, Y2O3 content and La2O3 doping on the translucency. Methods. Five different Y-TZP zirconia powders (3 commercially available and 2 experimentally modified) were sintered under the same conditions and characterized by X-ray diffraction with Rietveld analysis and scanning electron microscopy (SEM). Translucency (n = 6/group) was measured with a color meter, allowing to calculate the translucency parameter (TP) and the contrast ratio (CR). Mechanical properties were appraised with four-point bending strength (n = 10), single edge V-notched beam (SEVNB) fracture toughness (n = 8) and Vickers hardness (n = 10). The aging stability was evaluated by measuring the tetragonal to monoclinic transformation (n = 3) after accelerated hydrothermal aging in steam at 134 degrees C, and the transformation curves were fitted by the Mehl-Avrami-Johnson (MAJ) equation. Data were analyzed by one-way ANOVA, followed by Tukey's HSD test (alpha = 0.05). Results. Lowering the alumina content below 0.25 wt.% avoided the formation of alumina particles and therefore increased the translucency of 3Y-TZP ceramics, but the hydrothermal aging stability was reduced. A higher yttria content (5 mol%) introduced about 50% cubic zirconia phase and gave rise to the most translucent and aging-resistant Y-TZP ceramics, but the fracture toughness and strength were considerably sacrificed. 0.2 mol% La2O3 doping of 3Y-TZP tailored the grain boundary chemistry and significantly improved the aging resistance and translucency. Although the translucency improvement by La2O3 doping was less effective than for introducing a substantial amount of cubic zirconia, this strategy was able to maintain the mechanical properties of typical 3Y-TZP ceramics. Significance. Three different approaches were compared to improve the translucency of 3YTZP ceramics. (C) 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.07
Times cited: 47
DOI: 10.1016/J.DENTAL.7016.09.075
|
|
|
|
“Understanding the Activation of Anionic Redox Chemistry in Ti4+-Substituted Li2MnO3as a Cathode Material for Li-Ion Batteries”. Paulus A, Hendrickx M, Mayda S, Batuk M, Reekmans G, von Holst M, Elen K, Abakumov AM, Adriaensens P, Lamoen D, Partoens B, Hadermann J, Van Bael MK, Hardy A, ACS applied energy materials 6, 6956 (2023). http://doi.org/10.1021/acsaem.3c00451
Abstract: Layered Li-rich oxides, demonstrating both cationic and anionic redox chemistry being used as positive electrodes for Li-ion batteries,have raised interest due to their high specific discharge capacities exceeding 250 mAh/g. However, irreversible structural transformations triggered by anionic redox chemistry result in pronounced voltagefade (i.e., lowering the specific energy by a gradual decay of discharge potential) upon extended galvanostatic cycling. Activating or suppressing oxygen anionic redox through structural stabilization induced by redox-inactivecation substitution is a well-known strategy. However, less emphasishas been put on the correlation between substitution degree and theactivation/suppression of the anionic redox. In this work, Ti4+-substituted Li2MnO3 was synthesizedvia a facile solution-gel method. Ti4+ is selected as adopant as it contains no partially filled d-orbitals. Our study revealedthat the layered “honeycomb-ordered” C2/m structure is preserved when increasing the Ticontent to x = 0.2 in the Li2Mn1-x Ti (x) O-3 solidsolution, as shown by electron diffraction and aberration-correctedscanning transmission electron microscopy. Galvanostatic cycling hintsat a delayed oxygen release, due to an improved reversibility of theanionic redox, during the first 10 charge-discharge cyclesfor the x = 0.2 composition compared to the parentmaterial (x = 0), followed by pronounced oxygen redoxactivity afterward. The latter originates from a low activation energybarrier toward O-O dimer formation and Mn migration in Li2Mn0.8Ti0.2O3, as deducedfrom first-principles molecular dynamics (MD) simulations for the“charged” state. Upon lowering the Ti substitution to x = 0.05, the structural stability was drastically improvedbased on our MD analysis, stressing the importance of carefully optimizingthe substitution degree to achieve the best electrochemical performance.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 6.4
DOI: 10.1021/acsaem.3c00451
|
|
|
|
“Structural and magnetic phase transitions in the AnBnO3n-2 anion-deficient perovskites Pb2Ba2BiFe5O13 and Pb1.5Ba2.5Bi2Fe6O16”. Abakumov AM, Batuk M, Tsirlin AA, Tyablikov OA, Sheptyakov DV, Filimonov DS, Pokholok KV, Zhidal VS, Rozova MG, Antipov EV, Hadermann J, Van Tendeloo G;, Inorganic chemistry 52, 7834 (2013). http://doi.org/10.1021/ic3026667
Abstract: Novel anion-deficient perovskite-based ferrites Pb2Ba2BiFe5O13 and Pb1.5Ba2.5Bi2Fe6O16 were synthesized by solid-state reaction in air. Pb2Ba2BiFe5O13 and Pb1.5Ba2.5Bi2Fe6O16 belong to the perovskite-based AnBnO3n2 homologous series with n = 5 and 6, respectively, with a unit cell related to the perovskite subcell ap as ap√2 × ap × nap√2. Their structures are derived from the perovskite one by slicing it with 1/2[110]p(1̅01)p crystallographic shear (CS) planes. The CS operation results in (1̅01)p-shaped perovskite blocks with a thickness of (n 2) FeO6 octahedra connected to each other through double chains of edge-sharing FeO5 distorted tetragonal pyramids which can adopt two distinct mirror-related configurations. Ordering of chains with a different configuration provides an extra level of structure complexity. Above T ≈ 750 K for Pb2Ba2BiFe5O13 and T ≈ 400 K for Pb1.5Ba2.5Bi2Fe6O16 the chains have a disordered arrangement. On cooling, a second-order structural phase transition to the ordered state occurs in both compounds. Symmetry changes upon phase transition are analyzed using a combination of superspace crystallography and group theory approach. Correlations between the chain ordering pattern and octahedral tilting in the perovskite blocks are discussed. Pb2Ba2BiFe5O13 and Pb1.5Ba2.5Bi2Fe6O16 undergo a transition into an antiferromagnetically (AFM) ordered state, which is characterized by a G-type AFM ordering of the Fe magnetic moments within the perovskite blocks. The AFM perovskite blocks are stacked along the CS planes producing alternating FM and AFM-aligned FeFe pairs. In spite of the apparent frustration of the magnetic coupling between the perovskite blocks, all n = 4, 5, 6 AnFenO3n2 (A = Pb, Bi, Ba) feature robust antiferromagnetism with similar Néel temperatures of 623632 K.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 10
DOI: 10.1021/ic3026667
|
|
|
|
“Chemistry, local molybdenum clustering, and electrochemistry in the Li2+xMo1-xO3 solid solutions”. Savina AA, Saiutina VV, Morozov AV, Boev AO, Aksyonov DA, Dejoie C, Batuk M, Bals S, Hadermann J, Abakumov AM, Inorganic chemistry 61, 5637 (2022). http://doi.org/10.1021/ACS.INORGCHEM.2C00420
Abstract: A broad range of cationic nonstoichiometry has been demonstratedfor the Li-rich layered rock-salt-type oxide Li2MoO3, which has generally been considered as a phase with a well-defined chemical composition. Li2+xMo1-xO3(-0.037 <= x <= 0.124) solid solutions were synthesized via hydrogen reduction ofLi2MoO4in the temperature range of 650-1100 degrees C, withxdecreasing with theincrease of the reduction temperature. The solid solutions adopt a monoclinicallydistorted O3-type layered average structure and demonstrate a robust localordering of the Li cations and Mo3triangular clusters within the mixed Li/Mocationic layers. The local structure was scrutinized in detail by electron diffractionand aberration-corrected scanning transmission electron microcopy (STEM),resulting in an ordering model comprising a uniform distribution of the Mo3clusters compatible with local electroneutrality and chemical composition. The geometry of the triangular clusters with their oxygenenvironment (Mo3O13groups) has been directly visualized using differential phase contrast STEM imaging. The established localstructure was used as input for density functional theory (DFT)-based calculations; they support the proposed atomic arrangementand provide a plausible explanation for the staircase galvanostatic charge profiles upon electrochemical Li+extraction fromLi2+xMo1-xO3in Li cells. According to DFT, all electrochemical capacity in Li2+xMo1-xO3solely originates from the cationic Moredox process, which proceeds via oxidation of the Mo3triangular clusters into bent Mo3chains where the electronic capacity of the clusters depends on the initial chemical composition and Mo oxidation state defining the width of the first charge low-voltageplateau. Further oxidation at the high-voltage plateau proceeds through decomposition of the Mo3chains into Mo2dimers and further into individual Mo6+cations
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.6
Times cited: 3
DOI: 10.1021/ACS.INORGCHEM.2C00420
|
|
|
|
“Highly-translucent, strong and aging-resistant 3Y-TZP ceramics for dental restoration by grain boundary segregation”. Zhang F, Vanmeensel K, Batuk M, Hadermann J, Inokoshi M, Van Meerbeek B, Naert I, Vleugels J, Acta biomaterialia 16, 215 (2015). http://doi.org/10.1016/j.actbio.2015.01.037
Abstract: Latest trends in dental restorative ceramics involve the development of full-contour 3Y-TZP ceramics which can avoid chipping of veneering porcelains. Among the challenges are the low translucency and the hydrothermal stability of 3Y-TZP ceramics. In this work, different trivalent oxides (Al2O3, Sc2O3, Nd2O3 and La2O3) were selected to dope 3Y-TZP ceramics. Results show that dopant segregation was a key factor to design hydrothermally stable and high-translucent 3Y-TZP ceramics and the cation dopant radius could be used as a controlling parameter. A large trivalent dopant, oversized as compared to Zr4+, exhibiting strong segregation at the ZrO2 grain boundary was preferred. The introduction of 0.2 mol% La2O3 in conventional 0.10.25 wt.% Al2O3-doped 3Y-TZP resulted in an excellent combination of high translucency and superior hydrothermal stability, while retaining excellent mechanical properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 54
DOI: 10.1016/j.actbio.2015.01.037
|
|
|
|
“Effect of lone-electron-pair cations on the orientation of crystallographic shear planes in anion-deficient perovskites”. Batuk D, Batuk M, Abakumov AM, Tsirlin AA, McCammon CM, Dubrovinsky L, Hadermann J, Inorganic chemistry 52, 10009 (2013). http://doi.org/10.1021/ic4012845
Abstract: Factors affecting the structure and orientation of the crystallographic shear (CS) planes in anion-deficient perovskites are investigated using the (Pb1−zSrz)1−xFe1+xO3−y perovskites as a model system. The orientation of the CS planes in the system varies unevenly with z. A comparison of the structures with different CS planes revels that the orientation of the CS planes is governed mainly by the stereochemical activity of the lone-electron-pair cations inside the perovskite blocks.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.857
Times cited: 11
DOI: 10.1021/ic4012845
|
|