Abstract: In this paper, an overview of the fabrication and properties of high-quality La0.67Sr0.33MnO3 (LSMO) thin films is given. A high-quality LSMO film combines a smooth surface morphology with a large magnetization and a small residual resistivity, while avoiding precipitates and surface segregation. In the literature, typically only a few of these issues are adressed. We therefore present a thorough characterization of our films, which were grown by pulsed laser deposition. The films were characterized with reflection high energy electron diffraction, atomic force microscopy, x-ray diffraction, magnetization and transport measurements, x-ray photoelectron spectroscopy and scanning transmission electron microscopy. The films have a saturation magnetization of 4.0 µB/Mn, a Curie temperature of 350 K and a residual resistivity of 60 µΩ cm. These results indicate that high-quality films, combining both large magnetization and small residual resistivity, were realized. A comparison between different samples presented in the literature shows that focussing on a single property is insufficient for the optimization of the deposition process. For high-quality films, all properties have to be adressed. For LSMO devices, the thin-film quality is crucial for the device performance. Therefore, this research is important for the application of LSMO in devices.

Abstract: The crystal structure of the newly discovered double-Hg-layer copper oxide superconductor (Hg, Pr)(2)Ba-2(Y, Ca)Cu2O8-delta was studied as a function of chemical doping using neutron and electron diffraction and high-resolution transmission electron microscopy (HREM). Rietveld refinements of the structural parameters from neutron powder diffraction data indicate that the oxygen site O3 on the mercury plane is highly defective, being both partially occupied and displaced from the high-symmetry position. The variable concentration of oxygen vacancies partially compensates for the cation doping and, together with the O3 displacement field, makes some of the Hg atoms acquire an unusual pyramidal coordination. HREM images confirm that the structure is of the '2212' type, with very few defects. In some grains, faint superstructure reflections were evidenced by electron diffraction, suggesting that both the oxygen vacancies and the O3 displacement field may order at least on a local scale.

Abstract: The present paper describes the synthesis, characterization of mixed-valence bismuthates with 3- or 2-dimensional perovskite-like structures and structural criteria that influence superconductivity in these compounds. Single-phase samples of Sr1-xKxBiO3 were prepared for the broad range of K-content: 0.25 less than or equal to x less than or equal to 0.65. For these bismuthates the symmetry of the structure changes from monoclinic to orthorhombic and finally to tetragonal upon increasing the K-content thus resulting in the decrease of the Bi-O distances and reduction of the network distortions. Superconductivity with maximum T-c = 12K exists in the narrow range (x approximate to 0.5 – 0.6) within the stability field of the tetragonal phase (0.33 less than or equal to x less than or equal to 0.65), when the 3-dimensional octahedral framework has close to the ideal perovskite structure arrangement. At the same time compositions with close to optimal Bi-valence (x = 0.33 and 0.43) do not show any sign of superconductivity, probably, due to structural distortions. The layered type (BaK)(3)Bi2O7 and (Ba,K)(2)BiO4 bismuthates belonging to the A(n+1)B(n)O(3n+1) homologous series were investigated Buckling of the (BiO2) layers in the structure of the n = 2 member was revealed The formation of the n=1 bismuthate was found by Electron Microscopy and X-ray powder diffraction studies. Both types of compounds are considered to be possible candidates for new superconducting materials among bismuthates.

Abstract: The microstructure and phase transitions in the perovskite-based ferroelectric lead scandium tantalate, Pb(Sc0.5Ta0.5)O-3 have been investigated by transmission electron microscopy. The effects of ordering of Sc and Ta cations are apparent in reciprocal space as well as in direct space images. High-resolution observations allow direct structure imaging of the domain structure. The structure of the low temperature ferroelectric phase is studied by selected area electron diffraction (SAED) and electron microdiffraction. The relaxer behaviour of this paraelectric-ferroelectric transition is displayed by diffuse intensities in the SAED patterns at temperatures around the Curie point.

Abstract: The high temperature phase of Ni1-xS has the NiAs-type structure. The coexistence of two superstructures, ''3a3a3c'' and ''2a2a3c'' with the basic phase is confirmed by means of electron diffraction. The 2a2a3c superstructure is studied by means of electron diffraction and high resolution electron microscopy. A structure model is proposed based on the periodic insertion of stacking faults in the NiAs-type basic structure and the ordering of vacancies in alternate metal-atom layers. Microtwinning in very narrow slabs is found to be a main feature of the 2a2a3c regions and two defect models are discussed.