Montero-Sistiaga, M.L.; Pourbabak, S.; Van Humbeeck, J.; Schryvers, D.; Vanmeensel, K. |
|
|
Title |
Microstructure and mechanical properties of Hastelloy X produced by HP-SLM (high power selective laser melting) |
Type |
A1 Journal article |
|
Year |
2019 |
Publication |
Materials & design |
Abbreviated Journal |
Mater Design |
|
|
Volume |
165 |
Issue |
|
Pages |
107598 |
|
|
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
In order to increase the production rate during selective laser melting (SLM), a high power laser with a large beam diameter is used to build fully dense Hastelloy X parts. Compared to SLM with a low power and small diameter beam, the productivity was increased from 6 mm3/s to 16 mm3/s, i.e. 2.6 times faster. Besides the productivity benefit, the influence of the use of a high power laser on the rapid solidification microstructure and concomitant material properties is highlighted. The current paper compares the microstructure and tensile properties of Hastelloy X built with low and high power lasers. The use of a high power laser results in wider and shallower melt pools inducing an enhanced morphological and crystallographic texture along the building direction (BD). In addition, the increased heat input results in coarser sub-grains or high density dislocation walls for samples processed with a high power laser. Additionally, the influence of hot isostatic pressing (HIP) as a post-processing technique was evaluated. After HIP, the tensile fracture strain increased as compared to the strain in the as-built state and helped in obtaining competitive mechanical properties as compared to conventionally processed Hastelloy X parts. |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
|
Editor |
|
|
|
Language |
|
Wos |
000458259300020 |
Publication Date |
2019-01-09 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0264-1275 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
4.364 |
Times cited |
15 |
Open Access |
OpenAccess |
|
|
Notes |
This research was supported by the ENGIE Research and Technology Division. The authors acknowledge ENGIE Research and Technology Division for the use of the SLM280HL machine. S.P. likes to thank the Flemish Science Foundation FWO for financial support under Project G.0366.15N. |
Approved |
Most recent IF: 4.364 |
|
|
Call Number |
EMAT @ emat @UA @ admin @ c:irua:157469 |
Serial |
5176 |
|
Permanent link to this record |
|
|
|
|
Author |
Pauwels, D.; Geboes, B.; Hereijgers, J.; Choukroun, D.; De Wael, K.; Breugelmans, T. |
|
|
Title |
The application of an electrochemical microflow reactor for the electrosynthetic aldol reaction of acetone to diacetone alcohol |
Type |
A1 Journal article |
|
Year |
2017 |
Publication |
Chemical engineering research and design |
Abbreviated Journal |
Chem Eng Res Des |
|
|
Volume |
128 |
Issue |
|
Pages |
205-213 |
|
|
Keywords |
A1 Journal article; Engineering sciences. Technology; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation); Laboratory Experimental Medicine and Pediatrics (LEMP); Applied Electrochemistry & Catalysis (ELCAT) |
|
|
Abstract |
The design and application of an electrochemical micro-flow reactor for the aldol reaction of acetone to diacetone alcohol (DAA) is reported. The modular reactor could be readily disassembled and reassembled to change the electrodes, incorporate a membrane and remove possible obstructions. The productivity and efficiency was quantified. Using a platinum deposit as electrocatalyst or an inert glassy carbon electrode as working electrode, the maximum obtainable equilibrium concentration of ±15 m% was reached after a single pass up to a flow rate of 8 ml min−1, yielding 0.57 g min−1 DAA (3.46 mmol cm−3 min−1) at an efficiency of 0.33 g C−1 on platinum and 0.50 g min−1 (3.04 mmol cm−3 min−1) at 1.20 g C−1 on glassy carbon. Note that no optimisation studies have been made in the present paper. |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
|
Editor |
|
|
|
Language |
|
Wos |
000424736500018 |
Publication Date |
2017-10-20 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0263-8762 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
2.538 |
Times cited |
2 |
Open Access |
|
|
|
Notes |
; The authors would like to thank Bert De Mot for assisting with the measurements. Jonas Hereijgers greatly acknowledges the Research Foundation – Flanders (FWO) for support through a Post-Doctoral grant (12Q8817N). ; |
Approved |
Most recent IF: 2.538 |
|
|
Call Number |
UA @ admin @ c:irua:146943 |
Serial |
5871 |
|
Permanent link to this record |
|
|
|
|
Author |
Zhou, C.; Ji, G.; Chen, Z.; Wang, M.; Addad, A.; Schryvers, D.; Wang, H. |
|
|
Title |
Fabrication, interface characterization and modeling of oriented graphite flakes/Si/Al composites for thermal management applications |
Type |
A1 Journal article |
|
Year |
2014 |
Publication |
Materials and design |
Abbreviated Journal |
Mater Design |
|
|
Volume |
63 |
Issue |
|
Pages |
719-728 |
|
|
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
Highly thermally conductive graphite flakes (Gf)/Si/Al composites have been fabricated using Gf, Si powder and an AlSi7Mg0.3 alloy by an optimized pressure infiltration process for thermal management applications. In the composites, the layers of Gf were spaced apart by Si particles and oriented perpendicular to the pressing direction, which offered the opportunity to tailor the thermal conductivity (TC) and coefficient of thermal expansion (CTE) of the composites. Microstructural characterization revealed that the formation of a clean and tightly-adhered interface at the nanoscale between the side surface of the Gf and Al matrix, devoid of a detrimental Al4C3 phase and a reacted amorphous AlSiOC layer, contributed to excellent thermal performance along the alignment direction. With increasing volume fraction of Gf from 13.7 to 71.1 vol.%, the longitudinal (i.e. parallel to the graphite layers) TC of the composites increased from 179 to 526 W/m K, while the longitudinal CTE decreased from 12.1 to 7.3 ppm/K (matching the values of electronic components). Furthermore, the modified layers-in-parallel model better fitted the longitudinal TC data than the layers-in-parallel model and confirmed that the clean and tightly-adhered interface is favorable for the enhanced longitudinal TC. |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
Reigate |
Editor |
|
|
|
Language |
|
Wos |
000340949300086 |
Publication Date |
2014-07-17 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0261-3069; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
|
Times cited |
61 |
Open Access |
|
|
|
Notes |
|
Approved |
Most recent IF: NA |
|
|
Call Number |
UA @ lucian @ c:irua:118124 |
Serial |
1166 |
|
Permanent link to this record |
|
|
|
|
Author |
Mahieu, S.; Ghekiere, P.; de Winter, G.; de Gryse, R.; Depla, D.; Van Tendeloo, G.; Lebedev, O.I. |
|
|
Title |
Biaxially aligned titanium nitride thin films deposited by reactive unbalanced magnetron sputtering |
Type |
A1 Journal article |
|
Year |
2006 |
Publication |
Surface and coatings technology |
Abbreviated Journal |
Surf Coat Tech |
|
|
Volume |
200 |
Issue |
8 |
Pages |
2764-2768 |
|
|
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
|
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
Lausanne |
Editor |
|
|
|
Language |
|
Wos |
000235202100023 |
Publication Date |
2004-12-15 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0257-8972; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
2.589 |
Times cited |
36 |
Open Access |
|
|
|
Notes |
IWT-Vlaanderen |
Approved |
Most recent IF: 2.589; 2006 IF: 1.559 |
|
|
Call Number |
UA @ lucian @ c:irua:56554 |
Serial |
229 |
|
Permanent link to this record |
|
|
|
|
Author |
Major, L.; Morgiel, J.; Major, B.; Lackner, J.M.; Waldhauser, W.; Ebner, R.; Nistor, L.; Van Tendeloo, G. |
|
|
Title |
Crystallographic aspects related to advanced tribological multilayers of Cr/CrN and Ti/TiN types produced by pulsed laser deposition (PLD) |
Type |
A1 Journal article |
|
Year |
2006 |
Publication |
Surface and coatings technology |
Abbreviated Journal |
Surf Coat Tech |
|
|
Volume |
200 |
Issue |
22/23 |
Pages |
6190-6195 |
|
|
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
|
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
Lausanne |
Editor |
|
|
|
Language |
|
Wos |
000237842300007 |
Publication Date |
2005-12-10 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0257-8972; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
2.589 |
Times cited |
32 |
Open Access |
|
|
|
Notes |
|
Approved |
Most recent IF: 2.589; 2006 IF: 1.559 |
|
|
Call Number |
UA @ lucian @ c:irua:59459 |
Serial |
586 |
|
Permanent link to this record |
|
|
|
|
Author |
Neyts, E.; Bogaerts, A.; de Meyer, M.; van Gils, S. |
|
|
Title |
Macroscale computer simulations to investigate the chemical vapor deposition of thin metal-oxide films |
Type |
A1 Journal article |
|
Year |
2007 |
Publication |
Surface and coatings technology |
Abbreviated Journal |
Surf Coat Tech |
|
|
Volume |
201 |
Issue |
22/23 |
Pages |
8838-8841 |
|
|
Keywords |
A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT) |
|
|
Abstract |
|
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
Lausanne |
Editor |
|
|
|
Language |
|
Wos |
000249340400008 |
Publication Date |
2007-05-02 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0257-8972; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
2.589 |
Times cited |
5 |
Open Access |
|
|
|
Notes |
|
Approved |
Most recent IF: 2.589; 2007 IF: 1.678 |
|
|
Call Number |
UA @ lucian @ c:irua:64790 |
Serial |
1859 |
|
Permanent link to this record |
|
|
|
|
Author |
Major, L.; Tirry, W.; Van Tendeloo, G. |
|
|
Title |
Microstructure and defect characterization at interfaces in TiN/CrN multilayer coatings |
Type |
A1 Journal article |
|
Year |
2008 |
Publication |
Surface and coatings technology |
Abbreviated Journal |
Surf Coat Tech |
|
|
Volume |
202 |
Issue |
24 |
Pages |
6075-6080 |
|
|
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
Microstructures of TiN/CrN multilayer coatings deposited on austenite steel (Cr Ni 18 8) by pulsed laser deposition (PLD) are characterized using transmission electron microscopy while their mechanical properties were assessed in a ball-on-disk test. All coatings have the same total thickness of about 1 ìm. The individual layers show a highly defective columnar structure, which is characterized by conventional electron microscopy (TEM) as well as by high resolution TEM. These techniques, combined with measurements of the local chemical composition through EDS prove that PLD allows to produce fully separated CrN and TiN layers. The friction, and consequently the wear, are lowered by increasing the total number of layers in the coating. |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
Lausanne |
Editor |
|
|
|
Language |
|
Wos |
000260267100042 |
Publication Date |
2008-07-20 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0257-8972; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
2.589 |
Times cited |
23 |
Open Access |
|
|
|
Notes |
|
Approved |
Most recent IF: 2.589; 2008 IF: 1.860 |
|
|
Call Number |
UA @ lucian @ c:irua:76614 |
Serial |
2049 |
|
Permanent link to this record |
|
|
|
|
Author |
Bogaerts, A.; de Bleecker, K.; Kolev, I.; Madani, M. |
|
|
Title |
Modeling of gas discharge plasmas: What can we learn from it? |
Type |
A1 Journal article |
|
Year |
2005 |
Publication |
Surface and coatings technology |
Abbreviated Journal |
Surf Coat Tech |
|
|
Volume |
200 |
Issue |
|
Pages |
62-67 |
|
|
Keywords |
A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT) |
|
|
Abstract |
|
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
Lausanne |
Editor |
|
|
|
Language |
|
Wos |
000232327800014 |
Publication Date |
2005-03-22 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0257-8972; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
2.589 |
Times cited |
11 |
Open Access |
|
|
|
Notes |
|
Approved |
Most recent IF: 2.589; 2005 IF: 1.646 |
|
|
Call Number |
UA @ lucian @ c:irua:53629 |
Serial |
2122 |
|
Permanent link to this record |
|
|
|
|
Author |
Huq, M.Z.; Celis, J.P.; Meneve, J.; Stals, L.; Schryvers, D. |
|
|
Title |
Oscillating sliding wear of mono- and multilayer ceramic coatings in air |
Type |
A1 Journal article |
|
Year |
1999 |
Publication |
Surface and coatings technology |
Abbreviated Journal |
Surf Coat Tech |
|
|
Volume |
113 |
Issue |
|
Pages |
242-250 |
|
|
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
|
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
Lausanne |
Editor |
|
|
|
Language |
|
Wos |
000079807600007 |
Publication Date |
2002-07-25 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0257-8972; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
2.589 |
Times cited |
10 |
Open Access |
|
|
|
Notes |
|
Approved |
Most recent IF: 2.589; 1999 IF: 1.008 |
|
|
Call Number |
UA @ lucian @ c:irua:29379 |
Serial |
2532 |
|
Permanent link to this record |
|
|
|
|
Author |
Lamas, J.S.; Leroy, W.P.; Lu, Y.-G.; Verbeeck, J.; Van Tendeloo, G.; Depla, D. |
|
|
Title |
Using the macroscopic scale to predict the nano-scale behavior of YSZ thin films |
Type |
A1 Journal article |
|
Year |
2014 |
Publication |
Surface and coatings technology |
Abbreviated Journal |
Surf Coat Tech |
|
|
Volume |
238 |
Issue |
|
Pages |
45-50 |
|
|
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
In this work, Yttria-stabilized zirconia (YSZ) thin films were deposited using dual reactive magnetron sputtering. By varying the deposition conditions, the film morphology and texture of the thin films are tuned and biaxial alignment is obtained. Studying the crystallographic and microstructural properties of the YSZ thin films, a tilted columnar growth was identified. This tilt is shown to be dependent on the compositional gradient of the sample. The variation of composition within a single YSZ column measured via STEM-EDX is demonstrated to be equal to the macroscopic variation on a full YSZ sample when deposited under the same deposition parameters. A simple stress model was developed to predict the tilt of the growing columns. The results indicate that this model not only determines the column bending of the growing film but also confirms that a macroscopic approach is sufficient to determine the compositional gradient in a single column of the YSZ thin films. (C) 2013 Elsevier B.V. All rights reserved. |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
Lausanne |
Editor |
|
|
|
Language |
|
Wos |
000331028200005 |
Publication Date |
2013-10-29 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0257-8972; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
2.589 |
Times cited |
8 |
Open Access |
|
|
|
Notes |
246791 Countatoms; 278510 Vortex;Nmp3-La-2010-246102 Ifox; 312483 Esteem2; esteem2jra3 ECASJO; |
Approved |
Most recent IF: 2.589; 2014 IF: 1.998 |
|
|
Call Number |
UA @ lucian @ c:irua:115765 |
Serial |
3827 |
|
Permanent link to this record |
|
|
|
|
Author |
Cremers, V.; Rampelberg, G.; Barhoum, A.; Walters, P.; Claes, N.; Oliveira, T.M. de; Assche, G.V.; Bals, S.; Dendooven, J.; Detavernier, C. |
|
|
Title |
Oxidation barrier of Cu and Fe powder by Atomic Layer Deposition |
Type |
A1 Journal article |
|
Year |
2018 |
Publication |
Surface and coatings technology |
Abbreviated Journal |
Surf Coat Tech |
|
|
Volume |
349 |
Issue |
349 |
Pages |
1032-1041 |
|
|
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
Atomic layer deposition (ALD) is a vapor based technique which allows to deposit uniform, conformal films with a thickness control at the atomic scale. In this research, Al 2 O 3 coatings were deposited on micrometer-sized Fe and Cu powder (particles) using the thermal trimethylaluminum (TMA)/ water (H 2 O) process in a rotary pump-type ALD reactor. Rotation of the powder during deposition was required to obtain a pinhole-free ALD coating. The protective nature of the coating was evaluated by quantifying its effectiveness in protecting the metal particles during oxidative annealing treatments. The Al 2 O 3 coated powders were annealed in ambient air while in-situ thermogravimetric analysis (TGA) and in-situ x-ray diffraction (XRD) data were acquired. The thermal stability of a series of Cu and Fe powder with different Al 2 O 3 thicknesses were determined with TGA. In both samples a clear shift in oxidation temperature is visible. For Cu and Fe powder coated with 25 nm Al 2 O 3 , we observed an increase of the oxidation temperature with 300-400°C. For the Cu powder a thin film of only 8 nm is required to obtain an initial increase in oxidation temperature of 200°C. In contrast, for Fe powder a thicker coating of 25 nm is required. In both cases, the oxidation temperature increases with increasing thickness of the Al 2 O 3 coating. These results illustrate that the Al 2 O 3 thin film, deposited by the thermal ALD process (TMA/H 2 O) can be an efficient and pinhole-free barrier layer for micrometer-sized powder particles, provided that the powder is properly agitated during the process to ensure sufficient vapour-solid interaction. |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
|
Editor |
|
|
|
Language |
|
Wos |
000441492600108 |
Publication Date |
2018-06-25 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0257-8972 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
2.589 |
Times cited |
10 |
Open Access |
OpenAccess |
|
|
Notes |
The authors acknowledge financial support from the Strategic Initiative Materials in Flanders (SIM, SBO-FUNC project) and the Special Research Fund BOF of Ghent University (GOA 01G01513). J. D. acknowledges the Research Foundation Flanders (FWO-Vlaanderen) for a postdoctoral fellowship. N.C. and S.B. acknowledge financial support from European Research Council (ERC Starting Grant 335078-COLOURATOMS). The authors acknowledge S. Goeteyn for the assistance in preliminary depositions. (ROMEO:green; preprint:; postprint:can ; pdfversion:cannot); ecas_sara |
Approved |
Most recent IF: 2.589 |
|
|
Call Number |
EMAT @ emat @c:irua:152174UA @ admin @ c:irua:152174 |
Serial |
4994 |
|
Permanent link to this record |
|
|
|
|
Author |
Sharp, J.; Mueller, I.C.; Mandal, P.; Abbas, A.; Nord, M.; Doye, A.; Ehiasarian, A.; Hovsepian, P.; MacLaren, I.; Rainforth, W.M. |
|
|
Title |
Characterisation of a high-power impulse magnetron sputtered C/Mo/W wear resistant coating by transmission electron microscopy |
Type |
A1 Journal article |
|
Year |
2019 |
Publication |
Surface and coatings technology |
Abbreviated Journal |
Surf Coat Tech |
|
|
Volume |
377 |
Issue |
377 |
Pages |
124853 |
|
|
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
Thin films of C/Mo/W deposited using combined UBM/HIPIMS sputtering show 2-8 nm clusters of material richer in Mo and W than the matrix (found by EDS microanalysis), with structures that resemble graphitic onions with the metal atoms arranged regularly within them. EELS microanalysis showed the clusters to be rich in W and Mo. As the time averaged power used in the pulsed HIPIMS magnetron was increased, the clusters became more defined, larger, and arranged into layers with amorphous matrix between them. Films deposited with average HIPIMS powers of 4 kW and 6 kW also showed a periodic modulation of the cluster density within the finer layers giving secondary, wider stripes in TEM. By analysing the ratio between the finer and coarser layers, it was found that this meta-layering is related to the substrate rotation in the deposition chamber but in a non-straightforward way. Reasons for this are proposed. The detailed structure of the clusters remains unknown and is the subject of further work. Fluctuation electron microscopy results indicated the presence of crystal planes with the graphite interlayer spacing, crystal planes in hexagonal WC perpendicular to the basal plane, and some plane spacings found in Mo2C. Other peaks in the FEM results suggested symmetry-related starting points for future determination of the structure of the clusters. |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
|
Editor |
|
|
|
Language |
|
Wos |
000488417800015 |
Publication Date |
2019-08-03 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0257-8972 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
2.589 |
Times cited |
1 |
Open Access |
|
|
|
Notes |
; J.S. thanks the Mercury Centre at the University of Sheffield for funding, which was part funded by the ERDF under grant MERCURY 904467. I.C.M. acknowledges support from CONACyT and RobertoRocca Education Fellowship. We gratefully acknowledge funding from EPSRC for the pixelated STEM detector and the software used in its operation for the fluctuation microscopy (EP/M009963/ 1, EP/K503903/1 & EP/R511705/1). AD was supported by the EPSRC CDT in Integrative Sensing and Measurement, Grant Number EP/L016753/1. Funding sources did not influence the planning or execution of this work except to enable it. ; |
Approved |
Most recent IF: 2.589 |
|
|
Call Number |
UA @ admin @ c:irua:163700 |
Serial |
5383 |
|
Permanent link to this record |
|
|
|
|
Author |
van Landuyt, J.; Van Tendeloo, G.; Amelinckx, S.; Zhang, X.F.; Zhang, X.B.; Luyten, W. |
|
|
Title |
Crystallography of fullerites and related graphene textures |
Type |
A1 Journal article |
|
Year |
1994 |
Publication |
Materials science forum |
Abbreviated Journal |
|
|
|
Volume |
150/151 |
Issue |
|
Pages |
53-64 |
|
|
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
|
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
Lausanne |
Editor |
|
|
|
Language |
|
Wos |
A1994BC12F00004 |
Publication Date |
0000-00-00 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0255-5476; 1662-9752 |
ISBN |
|
Additional Links |
UA library record; WoS full record; |
|
|
Impact Factor |
|
Times cited |
|
Open Access |
|
|
|
Notes |
|
Approved |
no |
|
|
Call Number |
UA @ lucian @ c:irua:10001 |
Serial |
590 |
|
Permanent link to this record |
|
|
|
|
Author |
Teodorescu, V.S.; Nistor, L.C.; van Landuyt, J. |
|
|
Title |
High resolution TEM observation of in situ colloid formation in CaF2 crystals |
Type |
A1 Journal article |
|
Year |
1997 |
Publication |
Materials science forum |
Abbreviated Journal |
|
|
|
Volume |
239-241 |
Issue |
|
Pages |
671-674 |
|
|
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
|
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
Lausanne |
Editor |
|
|
|
Language |
|
Wos |
A1997BH33W00145 |
Publication Date |
0000-00-00 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0255-5476; 1662-9752 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
|
Times cited |
3 |
Open Access |
|
|
|
Notes |
|
Approved |
Most recent IF: NA |
|
|
Call Number |
UA @ lucian @ c:irua:21404 |
Serial |
1460 |
|
Permanent link to this record |
|
|
|
|
Author |
Veljkovic, D.; Tadić, M.; Peeters, F.M. |
|
|
Title |
Intersublevel absorption in stacked n-type doped self-assembled quantum dots |
Type |
A1 Journal article |
|
Year |
2005 |
Publication |
Materials science forum |
Abbreviated Journal |
Mater Sci Forum |
|
|
Volume |
494 |
Issue |
|
Pages |
37-42 |
|
|
Keywords |
A1 Journal article; Condensed Matter Theory (CMT) |
|
|
Abstract |
The intersublevel absorption in n-doped InAs/GaAs self-assembled quantum-dot molecules composed of three quantum dots is theoretically considered. The transition matrix elements and the transition energies are found to vary considerably with the spacer thickness. For s polarized light, decreasing the thickness of the spacer between the dots brings about crossings between the transition matrix elements, but the overall absorption is not affected by the variation of the spacer thickness. For p-polarized light and thick spacers, there are no available transitions in the single quantum dot, but a few of them emerge as a result of the electron state splitting in the stacks of coupled quantum dots, which leads to a considerable increase of the transition matrix elements, exceeding by an order of magnitude values of the matrix elements for s-polarized light. |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
Lausanne |
Editor |
|
|
|
Language |
|
Wos |
|
Publication Date |
0000-00-00 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0255-5476; 1662-9752 |
ISBN |
|
Additional Links |
UA library record; WoS full record; |
|
|
Impact Factor |
|
Times cited |
|
Open Access |
|
|
|
Notes |
|
Approved |
Most recent IF: NA |
|
|
Call Number |
UA @ lucian @ c:irua:94746 |
Serial |
1715 |
|
Permanent link to this record |
|
|
|
|
Author |
Partoens, B.; Matulis, A.; Peeters, F.M. |
|
|
Title |
Magnetoplasma excitations in vertically coupled quantum dot systems |
Type |
A1 Journal article |
|
Year |
1999 |
Publication |
Materials science forum |
Abbreviated Journal |
Mater Sci Forum |
|
|
Volume |
297/298 |
Issue |
|
Pages |
225-228 |
|
|
Keywords |
A1 Journal article; Condensed Matter Theory (CMT) |
|
|
Abstract |
|
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
Lausanne |
Editor |
|
|
|
Language |
|
Wos |
000080081600043 |
Publication Date |
0000-00-00 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0255-5476; 1662-9752 |
ISBN |
|
Additional Links |
UA library record; WoS full record; |
|
|
Impact Factor |
|
Times cited |
|
Open Access |
|
|
|
Notes |
|
Approved |
Most recent IF: NA |
|
|
Call Number |
UA @ lucian @ c:irua:24176 |
Serial |
1920 |
|
Permanent link to this record |
|
|
|
|
Author |
Kee-Hyun, K.; van Daele, B.; Van Tendeloo, G.; Jong-Kyu, Y. |
|
|
Title |
Observations of intermetallic compound formation of hot dip aluminized steel |
Type |
A1 Journal article |
|
Year |
2006 |
Publication |
Aluminium alloys: part 1-2 |
Abbreviated Journal |
|
|
|
Volume |
519-521 |
Issue |
1-2 |
Pages |
1871-1875 |
|
|
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
A hot dip aluminizing process to simulate the continuous galvanizing line (CGL) was carried out in three successive steps by a hot dip simulator: the pre-treatment for removing scales on the 200 x 250 mm(2) and 1mm in thickness cold rolled steel sheet, the dipping in 660 degrees C Al-Si melt for 3s and the cooling. In a pre-treatment, the steel specimen was partly coated by Au to confirm the mechanism of intermetallic compound (IMC) formation. Scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), and transmission electron microscopy (TEM) analyses were followed to observe the cross-section and the distribution of the elements. The specimen was analyzed in the boundary of the dipped-undipped part to see the formation mechanism of the aluminized steel. An intermetallic compound (IMC) is rapidly developed and grown in the steel-liquid interface. It has been usually reported that the IMC was formed by the dissolution of iron in the steel substrate toward the melt and the diffusion of aluminum in an opposite direction. The specimen is covered with aluminum-10 wt.% silicon, forms the IMC in the part that was not Au coated. However, IMC is not formed in the Au-coated part. The interface of the dipped-undipped is also analyzed by EDX. At the interface of the steel-IMC, it is clearly shown that the IMC is only formed in the dipped part and exists in the steel substrate as well, and contributes by iron, aluminum and silicon. The result clearly shows that only aluminum diffuses into the steel substrate without the dissolution of iron and forms the IMC between the steel substrate and the melt. Au coating and the short dipping time prevent the iron from dissolving into the aluminum melt. By TEM combined with focused ion beam (FIB) sample preparation, the IMC is confirmed as Fe2SiAl8, a hexagonal structure with space group P6(3)/mmc. |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
Lausanne |
Editor |
|
|
|
Language |
|
Wos |
|
Publication Date |
0000-00-00 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0255-5476; 1662-9752 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
|
Times cited |
|
Open Access |
|
|
|
Notes |
|
Approved |
Most recent IF: NA |
|
|
Call Number |
UA @ lucian @ c:irua:104062 |
Serial |
2425 |
|
Permanent link to this record |
|
|
|
|
Author |
Nistor, L.C.; van Landuyt, J.; Ralchenko, V.G.; Obratzova, E.D.; Korothushenko, K.G.; Smolin, A.A. |
|
|
Title |
Structural studies of nanocrystalline diamond thin films |
Type |
A1 Journal article |
|
Year |
1997 |
Publication |
Materials science forum |
Abbreviated Journal |
|
|
|
Volume |
239-241 |
Issue |
|
Pages |
115-118 |
|
|
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
|
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
Lausanne |
Editor |
|
|
|
Language |
|
Wos |
A1997BH33W00026 |
Publication Date |
0000-00-00 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0255-5476; 1662-9752 |
ISBN |
|
Additional Links |
UA library record; WoS full record; |
|
|
Impact Factor |
|
Times cited |
|
Open Access |
|
|
|
Notes |
|
Approved |
Most recent IF: NA |
|
|
Call Number |
UA @ lucian @ c:irua:21403 |
Serial |
3260 |
|
Permanent link to this record |
|
|
|
|
Author |
Romano-Rodriguez, A.; Perez-Rodriguez, A.; Serre, C.; van Landuyt, J.; et al. |
|
|
Title |
Epitaxial growth of \beta-SiC on ion-beam synthesized \beta-SiC : structural characterization |
Type |
A1 Journal article |
|
Year |
2000 |
Publication |
Materials science forum
T2 – International Conference on Silicon Carbide and Related Materials, OCT 10-15, 1999, RES TRIANGLE PK, NORTH CAROLINA |
Abbreviated Journal |
Mater Sci Forum |
|
|
Volume |
338-3 |
Issue |
|
Pages |
309-312 |
|
|
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
In this work we present for the first time, to our knowledge, the CVD epitaxial growth of beta -SiC using an ion beam synthesized (IBS) beta -SiC layer as seed, which has been formed by multiple implantation into Si wafers at 500 degreesC. The ion beam synthesized continuous layer is constituted by beta -SiC nanocrystals that are well oriented relative to the silicon substrate. Comparison of the epitaxial growth on these samples with that on silicon test samples, both on and off-axis, is performed. The results show that the epitaxial growth can be achieved on the IBS samples without the need of the carbonization step and that the structural quality of the CVD layer is comparable to that obtained on a carbonized silicon sample. Improvement of the quality of the deposited layer is proposed. |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
Trans tech publications ltd |
Place of Publication |
Zurich-uetikon |
Editor |
|
|
|
Language |
|
Wos |
000165996700075 |
Publication Date |
0000-00-00 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0255-5476 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
|
Times cited |
2 |
Open Access |
|
|
|
Notes |
|
Approved |
Most recent IF: NA |
|
|
Call Number |
UA @ lucian @ c:irua:104262 |
Serial |
1071 |
|
Permanent link to this record |
|
|
|
|
Author |
Krsmanovic, R.; Bertoni, G.; Van Tendeloo, G. |
|
|
Title |
Structural characterization of erbium doped LAS glass ceramics obtained by glass melting technique |
Type |
A1 Journal article |
|
Year |
2007 |
Publication |
Materials science forum |
Abbreviated Journal |
|
|
|
Volume |
555 |
Issue |
|
Pages |
377-381 |
|
|
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
Samples of transparent glass-ceramics in the ternary system Li2O-Al2O3-SiO2 (LAS), with Er2O3 as a luminescent dopant, are investigated. The initial glass is obtained by the classical melting technique. In order to induce ceramization of the glass, TiO2 and ZrO2 are added in small amount as nucleating agents. The thermal treatments at 730 and 770 degrees C are carried out to promote formation of titanium zirconate solid solution precipitates. The spatial distribution of the precipitates in the material, their morphology, and their composition are investigated with TEM, HRTEM, HAADF-STEM, EELS and EFTEM. The results demonstrate that with the glass-melting preparation technique it is possible to achieve small nanoparticles with uniform distribution and higher number density than with the sol-gel glass preparation. |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
Lausanne |
Editor |
|
|
|
Language |
|
Wos |
|
Publication Date |
0000-00-00 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0255-5476 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
|
Times cited |
|
Open Access |
|
|
|
Notes |
|
Approved |
Most recent IF: NA |
|
|
Call Number |
UA @ lucian @ c:irua:94673 |
Serial |
3220 |
|
Permanent link to this record |
|
|
|
|
Author |
Gonzalez-Quiroga, A.; Shtern, V.; Perreault, P.; Vandewalle, L.; Marin, G.B.; Van Geem, K.M. |
|
|
Title |
Intensifying mass and heat transfer using a high-g stator-rotor vortex chamber |
Type |
A1 Journal article |
|
Year |
2021 |
Publication |
Chemical Engineering And Processing |
Abbreviated Journal |
Chem Eng Process |
|
|
Volume |
169 |
Issue |
|
Pages |
108638-11 |
|
|
Keywords |
A1 Journal article; Engineering sciences. Technology; Sustainable Energy, Air and Water Technology (DuEL) |
|
|
Abstract |
Vortex reactors take advantage of the synergy between enhanced heat and mass transfer rates and multifunctional phenomena at different temporal and spatial scales. Proof-of-concept experiments with our novel and innovative STAtor-Rotor VOrtex Chamber (STARVOC) confirm its advantageous features for the sustainable production of chemicals and fuels. STARVOC is a high-g contactor that uses carrier flow (gas or liquid) tangential injection to drive a rotor attached to low-friction bearings. The vortex chamber inside the rotor contains a secondary phase or phases, such as a solids bed, a liquid layer, or a suspension. Carrier fluid passes through the perforated rotor wall and contacts a densely and uniformly distributed secondary phase with enhanced slip velocities. Experiments focused on pressure profiles, rotor angular velocity, and solids azimuthal velocity. With air as the carrier fluid and different solid particle beds as the secondary phase, STARVOC reached bed azimuthal velocities up to four-fold compared to those reached in Gas-Solid Vortex Units with fully static geometry. These results show its potential to improve interfacial heat and mass transfer rates and take advantage of flow energy and angular momentum. Due to its process intensification capabilities, STARVOC is a promising alternative for the state-of-the-art chemical industry. |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
|
Editor |
|
|
|
Language |
|
Wos |
000704946900008 |
Publication Date |
2021-09-17 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0255-2701 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
2.234 |
Times cited |
|
Open Access |
Not_Open_Access |
|
|
Notes |
|
Approved |
Most recent IF: 2.234 |
|
|
Call Number |
UA @ admin @ c:irua:181062 |
Serial |
8111 |
|
Permanent link to this record |
|
|
|
|
Author |
Bampouli, A.; Goris, Q.; Hussain, M.N.; Louisnard, O.; Stefanidis, G.D.; Van Gerven, T. |
|
|
Title |
Importance of design and operating parameters in a sonication system for viscous solutions : effects of input power, horn tip diameter and reactor capacity |
Type |
A1 Journal article |
|
Year |
2024 |
Publication |
Chemical engineering and processing |
Abbreviated Journal |
|
|
|
Volume |
198 |
Issue |
|
Pages |
109715-12 |
|
|
Keywords |
A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
This study investigates the distribution of ultrasound (US) energy in a batch system for solutions with viscosity ranging from 1 to approximately 3000 mPas. Sonication was performed using horn type configurations operating at 20-30 kHz and rated power capacity of 50 or 200 W. Two different tip diameters (3 or 7 mm) and two insertion depths (35 or 25 mm) within vessels of different sizes ( approximate to 60 or 130 ml) were utilized. Additionally, a special conical tip design was employed. For each experimental setup, the calorimetric efficiency was estimated, the cavitationally active regions were visualized using the sonochemiluminescence (SCL) method and bubble cluster formation inside the vessel was macroscopically observed using a high speed camera (HSC). In the viscosity range tested, the calorimetry results showed that the efficiency and continuous operation of the device depend on both the rated power and the horn tip diameter. The ratio between electrical and calorimetric power input remained consistently around 40 to 50% across the different configurations for water, but for the 123.2 mPas solution exhibited significant variation ranging from 40 to 85%. Moreover, the power density in the smaller reactor was found to be nearly double compared to the larger one. The SCL analysis showed multiple cavitationally active zones in all setups, and the zones intensity decreased considerably with increase of the solutions viscosity. The results for the cone tip were not conclusive, but can be used as the basis for further investigation. The current research highlights the importance of thoroughly understanding the impact of each design parameter, and of establishing characterization methodologies to assist in the future development of scaled-up, commercial applications. |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
|
Editor |
|
|
|
Language |
|
Wos |
001218630800001 |
Publication Date |
2024-02-21 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0255-2701 |
ISBN |
|
Additional Links |
UA library record; WoS full record |
|
|
Impact Factor |
4.3 |
Times cited |
|
Open Access |
|
|
|
Notes |
|
Approved |
Most recent IF: 4.3; 2024 IF: 2.234 |
|
|
Call Number |
UA @ admin @ c:irua:206003 |
Serial |
9154 |
|
Permanent link to this record |
|
|
|
|
Author |
Potgieter-Vermaak, S.; Stranger, M.; Verlinden, L.; Roekens, E.; Van Grieken, R. |
|
|
Title |
NO2 verkeersmetingen in Vlaanderen door passieve bemonstering |
Type |
A1 Journal article |
|
Year |
2008 |
Publication |
Die Suid-Afrikaanse tydskrif vir natuurwetenskap en tegnologie |
Abbreviated Journal |
|
|
|
Volume |
27 |
Issue |
4 |
Pages |
266-286 |
|
|
Keywords |
A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation) |
|
|
Abstract |
|
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
|
Editor |
|
|
|
Language |
|
Wos |
|
Publication Date |
|
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0254-3486; 2222-4173 |
ISBN |
|
Additional Links |
UA library record |
|
|
Impact Factor |
|
Times cited |
|
Open Access |
|
|
|
Notes |
|
Approved |
no |
|
|
Call Number |
UA @ admin @ c:irua:72494 |
Serial |
8650 |
|
Permanent link to this record |
|
|
|
|
Author |
Thomé, T.; Colaux, J.L.; Colomer, J.-F.; Bertoni, G.; Terwagne, G. |
|
|
Title |
Formation of carbon nitride nanospheres by ion implantation |
Type |
A1 Journal article |
|
Year |
2007 |
Publication |
Materials chemistry and physics |
Abbreviated Journal |
Mater Chem Phys |
|
|
Volume |
103 |
Issue |
2-3 |
Pages |
290-294 |
|
|
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
Carbon nitride nanospheres have been synthesized into copper by simultaneous high fluence (10(18) at. cm(-2)) implantations of C-12 and N-15 ions. The composition of the implanted region has been measured using C-12(d,p(0))C-13 and N-15(d,alpha(0))C-13 nuclear reactions induced by a 1.05 MeV deuteron beam. The C-12 and N-15 depth profiles are very close and the retained doses into copper are relatively high, which indicates that carbon and nitrogen diffusion processes are likely limited during implantation. High resolution transmission electron microscopy (HRTEM) observations and electron diffraction (ED) analyses have been carried out to determine the structure of the nanospheres formed during implantation. Some consist in small hollow amorphous nanocapsules with sizes ranging from 30 to 100 nm. Large gas bubbles with diameters up to 300 mn have also been observed in the copper matrix. Electron energy-loss spectroscopy (EELS) measurements performed on the small nanocapsules indicate that their shells are composed of carbon and nitrogen. (c) 2007 Elsevier B.V. All rights reserved. |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
Lausanne |
Editor |
|
|
|
Language |
|
Wos |
000247715300016 |
Publication Date |
2007-02-25 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0254-0584; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
2.084 |
Times cited |
1 |
Open Access |
|
|
|
Notes |
|
Approved |
Most recent IF: 2.084; 2007 IF: 1.871 |
|
|
Call Number |
UA @ lucian @ c:irua:102670 |
Serial |
1258 |
|
Permanent link to this record |
|
|
|
|
Author |
Navío, C.; Vallejos, S.; Stoycheva, T.; Llobet, E.; Correig, X.; Snyders, R.; Blackman, C.; Umek, P.; Ke, X.; Van Tendeloo, G.; Bittencourt, C.; |
|
|
Title |
Gold clusters on WO3 nanoneedles grown via AACVD : XPS and TEM studies |
Type |
A1 Journal article |
|
Year |
2012 |
Publication |
Materials chemistry and physics |
Abbreviated Journal |
Mater Chem Phys |
|
|
Volume |
134 |
Issue |
2/3 |
Pages |
809-813 |
|
|
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
We have prepared tungsten oxide films decorated with gold particles on Si substrates by aerosol assisted chemical vapor deposition (AACVD) and characterized them using scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS). SEM shows that the films are composed of needle-like structures and TEM shows that both the needles and the gold particles are crystalline. XPS indicates the presence of oxygen vacancies, i.e. the films are WO3−x, and hence the deposited material is composed of semiconducting nanostructures and that the interaction between the gold particles and the WO3 needles surface is weak. The synthesis of semiconducting tungsten oxide nanostructures decorated with metal particles represents an important step towards the development of sensing devices with optimal properties. |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
Lausanne |
Editor |
|
|
|
Language |
|
Wos |
000305918200038 |
Publication Date |
2012-04-30 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0254-0584; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
2.084 |
Times cited |
52 |
Open Access |
|
|
|
Notes |
Iap |
Approved |
Most recent IF: 2.084; 2012 IF: 2.072 |
|
|
Call Number |
UA @ lucian @ c:irua:97705 |
Serial |
1356 |
|
Permanent link to this record |
|
|
|
|
Author |
Lorenz, H.; Zhao, Q.; Turner, S.; Lebedev, O.I.; Van Tendeloo, G.; Klötzer, B.; Rameshan, C.; Penner, S. |
|
|
Title |
Preparation and structural characterization of SnO2 and GeO2 methanol steam reforming thin film model catalysts by (HR)TEM |
Type |
A1 Journal article |
|
Year |
2010 |
Publication |
Materials chemistry and physics |
Abbreviated Journal |
Mater Chem Phys |
|
|
Volume |
122 |
Issue |
2/3 |
Pages |
623-629 |
|
|
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
Structure, morphology and composition of different tin oxide and germanium oxide thin film catalysts for the methanol steam reforming (MSR) reaction have been studied by a combination of (high-resolution) transmission electron microscopy, selected area electron diffraction, dark-field imaging and electron energy-loss spectroscopy. Deposition of the thin films on NaCl(0 0 1) cleavage faces has been carried out by thermal evaporation of the respective SnO2 and GeO2 powders in varying oxygen partial pressures and at different substrate temperatures. Preparation of tin oxide films in high oxygen pressures (10−1 Pa) exclusively resulted in SnO phases, at and above 473 K substrate temperature epitaxial growth of SnO on NaCl(0 0 1) leads to well-ordered films. For lower oxygen partial pressures (10−3 to 10−2 Pa), mixtures of SnO and β-Sn are obtained. Well-ordered SnO2 films, as verified by electron diffraction patterns and energy-loss spectra, are only obtained after post-oxidation of SnO films at temperatures T ≥ 673 K in 105 Pa O2. Preparation of GeOx films inevitably results in amorphous films with a composition close to GeO2, which cannot be crystallized by annealing treatments in oxygen or hydrogen at temperatures comparable to SnO/SnO2. Similarities and differences to neighbouring oxides relevant for selective MSR in the third group of the periodic system (In2O3 and Ga2O3) are also discussed with the aim of cross-correlation in formation of nanomaterials, and ultimately, also catalytic properties. |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
Lausanne |
Editor |
|
|
|
Language |
|
Wos |
000278637900054 |
Publication Date |
2010-04-18 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0254-0584; |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
2.084 |
Times cited |
15 |
Open Access |
|
|
|
Notes |
Esteem 026019 |
Approved |
Most recent IF: 2.084; 2010 IF: 2.356 |
|
|
Call Number |
UA @ lucian @ c:irua:83099 |
Serial |
2699 |
|
Permanent link to this record |
|
|
|
|
Author |
Tit, N.; Al Ezzi, M.M.; Abdullah, H.M.; Yusupov, M.; Kouser, S.; Bahlouli, H.; Yamani, Z.H. |
|
|
Title |
Detection of CO2 using CNT-based sensors: Role of Fe catalyst on sensitivity and selectivity |
Type |
A1 Journal article |
|
Year |
2017 |
Publication |
Materials chemistry and physics |
Abbreviated Journal |
Mater Chem Phys |
|
|
Volume |
186 |
Issue |
186 |
Pages |
353-364 |
|
|
Keywords |
A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT) |
|
|
Abstract |
The adsorption of CO2 on surfaces of graphene and carbon nanotubes (CNTs), decorated with Fe atoms, are investigated using the self-consistent-charge density-functional tight-binding (SCC-DFTB) method, neglecting the heat effects. Fe ad-atoms are more stable when they are dispersed on hollow sites. They introduce a large density of states at the Fermi level (N-F); where keeping such density low would help in gas sensing. Furthermore, the Fe ad-atom can weaken the C=O double bonds of the chemisorbed CO2 molecule, paving the way for oxygen atoms to drain more charges from Fe. Consequently, chemisorption of CO2 molecules reduces both N-F and the conductance while it enhances the sensitivity with the increasing gas dose. Conducting armchair CNTs (ac-CNTs) have higher sensitivity than graphene and semiconducting zigzag CNTs (zz-CNT5). Comparative study of sensitivity of ac-CNT-Fe composite towards various gases (e.g., O-2, N-2, H-2, H2O, CO and CO2) has shown high sensitivity and selectivity towards CO, CO2 and H2O gases. (C) 2016 Elsevier B.V. All rights reserved. |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
Lausanne |
Editor |
|
|
|
Language |
|
Wos |
000390621200044 |
Publication Date |
2016-11-04 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0254-0584 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
2.084 |
Times cited |
17 |
Open Access |
Not_Open_Access |
|
|
Notes |
|
Approved |
Most recent IF: 2.084 |
|
|
Call Number |
UA @ lucian @ c:irua:140333 |
Serial |
4465 |
|
Permanent link to this record |
|
|
|
|
Author |
De Dobbelaere, C.; Lourdes Calzada, M.; Bretos, I.; Jimenez, R.; Ricote, J.; Hadermann, J.; Hardy, A.; Van Bael, M.K. |
|
|
Title |
Gaining new insight into low-temperature aqueous photochemical solution deposited ferroelectric PbTiO3 films |
Type |
A1 Journal article |
|
Year |
2016 |
Publication |
Materials chemistry and physics |
Abbreviated Journal |
Mater Chem Phys |
|
|
Volume |
174 |
Issue |
|
Pages |
28-40 |
|
|
Keywords |
A1 Journal article; Electron microscopy for materials research (EMAT) |
|
|
Abstract |
The nature of the low-temperature photochemical assisted formation process of ferroelectric lead titanate (PbTiO3) films is studied in the present work. Films are obtained by the deposition of an aqueous solution containing citric acid based (citrato) metal ion complexes with intrinsic UV activity. This UV activity is crucial for the aqueous photochemical solution deposition (aqueous PCSD) route being used. UV irradiation enhances the early decomposition of organics and results in improved electrical properties for the crystalline oxide film, even if the film is crystallized at low temperature. GATR-FTIR shows that UV irradiation promotes the decomposition of organic precursor components, resulting in homogeneous films if applied in the right temperature window during film processing. The organic content, morphology and crystallinity of the irradiated films, achieved at different processing atmospheres and temperatures, is studied and eventually correlated to the functional behavior of the obtained films. This is an important issue, as crystalline films obtained at low temperatures often lack ferroelectric responses. In this work, the film prepared in pure oxygen at the very low temperature of 400 degrees C and after an optimized UV treatment presents a significant remanent polarization value of P-r = 8.8 mu C cm(-2). This value is attributed to the better crystallinity, the larger grain size and the reduced porosity obtained thanks to the early film crystallization effectively achieved through the UV treatment in oxygen. (C) 2016 Elsevier B.V. All rights reserved. |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
Lausanne |
Editor |
|
|
|
Language |
|
Wos |
000373865700005 |
Publication Date |
2016-03-16 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0254-0584 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
2.084 |
Times cited |
4 |
Open Access |
|
|
|
Notes |
|
Approved |
Most recent IF: 2.084 |
|
|
Call Number |
UA @ lucian @ c:irua:144729 |
Serial |
4659 |
|
Permanent link to this record |
|
|
|
|
Author |
Topalovic, D.B.; Arsoski, V.V.; Pavlovic, S.; Cukaric, N.A.; Tadic, M.Z.; Peeters, F.M. |
|
|
Title |
On improving accuracy of finite-element solutions of the effective-mass Schrodinger equation for interdiffused quantum wells and quantum wires |
Type |
A1 Journal article |
|
Year |
2016 |
Publication |
Communications in theoretical physics |
Abbreviated Journal |
Commun Theor Phys |
|
|
Volume |
65 |
Issue |
1 |
Pages |
105-113 |
|
|
Keywords |
A1 Journal article; Condensed Matter Theory (CMT) |
|
|
Abstract |
We use the Galerkin approach and the finite-element method to numerically solve the effective-mass Schrodinger equation. The accuracy of the solution is explored as it varies with the range of the numerical domain. The model potentials are those of interdiffused semiconductor quantum wells and axially symmetric quantum wires. Also, the model of a linear harmonic oscillator is considered for comparison reasons. It is demonstrated that the absolute error of the electron ground state energy level exhibits a minimum at a certain domain range, which is thus considered to be optimal. This range is found to depend on the number of mesh nodes N approximately as alpha(0) log(e)(alpha 1) (alpha N-2), where the values of the constants alpha(0), alpha(1), and alpha(2) are determined by fitting the numerical data. And the optimal range is found to be a weak function of the diffusion length. Moreover, it was demonstrated that a domain range adaptation to the optimal value leads to substantial improvement of accuracy of the solution of the Schrodinger equation. |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
Wallingford |
Editor |
|
|
|
Language |
|
Wos |
|
Publication Date |
|
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0253-6102; 1572-9494 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
0.989 |
Times cited |
|
Open Access |
|
|
|
Notes |
|
Approved |
Most recent IF: 0.989 |
|
|
Call Number |
UA @ lucian @ c:irua:133213 |
Serial |
4216 |
|
Permanent link to this record |
|
|
|
|
Author |
Subramanian, V.; Van 't dack, L.; Van Grieken, R. |
|
|
Title |
Preliminary studies on the geochemistry of the Cauvery river basin |
Type |
A1 Journal article |
|
Year |
1985 |
Publication |
Proceedings of the Indian Academy of Sciences: earth and planetary sciences |
Abbreviated Journal |
|
|
|
Volume |
94 |
Issue |
2 |
Pages |
99-110 |
|
|
Keywords |
A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation) |
|
|
Abstract |
Samples of water and sediments were collected over a three year period from the entire region of Cauvery river basin excluding the estuary. On the basis of our observations, we have calculated the average composition of the Cauvery river at several locations from the catchment to the river mouth, the downstream profile of sediment load, annual erosion rates, solute and sediment fluxes and have predicted on long term changes. The sediment chemistry was determined by x-ray fluorescence (xrf) technique, and calculated mean compositions of the Cauvery and its tributary bed and the suspended sediment were compared to those of world average river sediments. Downstream profiles of some of the elements appear to be controlled by size and mineralogical characteristics besides local factors specific to the location of the samples. Interelemental relationships indicated good correlation among the transition elements indicating their co-genetic behaviour within the drainage basin. |
|
|
Address |
|
|
|
Corporate Author |
|
Thesis |
|
|
|
Publisher |
|
Place of Publication |
|
Editor |
|
|
|
Language |
|
Wos |
A1985ARL3300004 |
Publication Date |
2010-08-25 |
|
|
Series Editor |
|
Series Title |
|
Abbreviated Series Title |
|
|
|
Series Volume |
|
Series Issue |
|
Edition |
|
|
|
ISSN |
0253-4126 |
ISBN |
|
Additional Links |
UA library record; WoS full record; WoS citing articles |
|
|
Impact Factor |
|
Times cited |
|
Open Access |
|
|
|
Notes |
|
Approved |
no |
|
|
Call Number |
UA @ admin @ c:irua:111503 |
Serial |
8410 |
|
Permanent link to this record |