“3Y-TZP ceramics with improved hydrothermal degradation resistance and fracture toughness”. Zhang F, Vanmeensel K, Inokoshi M, Batuk M, Hadermann J, Van Meerbeek B, Naert I, Vleugels J, Journal of the European Ceramic Society 34, 2453 (2014). http://doi.org/10.1016/j.jeurceramsoc.2014.02.026
Abstract: Different factors such as the way of incorporating the Y2O3 stabilizer, alumina addition and sintering temperature were assessed with the goal to improve the low temperature degradation (LTD) resistance of 3Y-TZP without compromising on the mechanical properties. The degradation of hydrothermally treated specimens was studied by X-ray diffraction, micro-Raman spectroscopy and scanning electron microscopy. Decreasing the sintering temperature decreased the LTD susceptibility of 3Y-TZPs but did not allow to obtain a LTD resistant 3Y-TZP with optimized mechanical properties. Alumina addition along with the use of Y2O3 stabilizer coated starting powder allowed to combine both an excellent toughness and LTD resistance, as compared to alumina-free and stabilizer co-precipitated powder based equivalents. Transmission electron microscopy revealed that the improved LTD resistance could be attributed to the segregation of Al3+ at the grain boundary and the heterogeneously distributed Y3+ stabilizer.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 48
DOI: 10.1016/j.jeurceramsoc.2014.02.026
|
“Critical influence of alumina content on the low temperature degradation of 2-3 mol% yttria-stabilized TZP for dental restorations”. Zhang F, Vanmeensel K, Inokoshi M, Batuk M, Hadermann J, Van Meerbeek B, Naert I, Vleugels J, Journal of the European Ceramic Society 35, 741 (2015). http://doi.org/10.1016/j.jeurceramsoc.2014.09.018
Abstract: The influence of 0.25, 2 and 5 wt.% alumina addition on the mechanical properties and low temperature degradation (LTD) of 3, 2.5 and 2 mol% yttria-stabilized TZP ceramics was investigated. The amount of alumina addition was observed to have a crucial impact on the degradation of Y-TZP ceramics. Independent on the yttria stabilizer content, 0.25 wt.% alumina had a higher degradation retarding effect to Y-TZP ceramics than 2 and 5 wt.% of alumina addition, which had a comparable effect. The apparent activation energy for the degradation process was increased by adding alumina, but it was the same for 0.255 wt.% alumina doped 3Y-TZP ceramics. For Y-TZPs containing a small amount of alumina addition, only the segregated Al3+ at the grain boundaries of the zirconia grains was effective to retard the degradation of Y-TZPs. The secondary phase Al2O3 grains increased the degradation kinetics, which might be attributed to the residual stresses.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 37
DOI: 10.1016/j.jeurceramsoc.2014.09.018
|
“HREM of ceramic high Tc superconductors”. Van Tendeloo G, Krekels T, Journal of the European Ceramic Society 16, 367 (1996). http://doi.org/10.1016/0955-2219(95)00193-X
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.947
Times cited: 1
DOI: 10.1016/0955-2219(95)00193-X
|
“Phase assembly and microstructure of CeO2-doped ZrO2 ceramics prepared by spark plasma sintering”. Xu T, Wang P, Fang P, Kan Y, Chen L, Vleugels J, Van der Biest O, van Landuyt J, Journal of the European Ceramic Society 25, 3437 (2005). http://doi.org/10.1016/j.jeurceramsoc.2004.09.004
Abstract: CeO2-doped ZrO2, (8 mol%) starting powder was sintered by means of spark plasma sintering (SPS) at 1300 degrees C without holding time. The stability of the tetragonal ZrO2 phase in the Ce-ZrO2 ceramic sintered under strongly reducing conditions was investigated. The SPS sample consisted of monoclinic and tetragonal ZrO2 phase, with a volume ratio of two to one, as well as a trace amount of a Zr-Ce-O cubic solid solution phase. In contrast, the same powder sintered by hot-pressing in nitrogen at 1300 and 1500 degrees C for 1h showed no tetragonal ZrO2. Microstructural observation of the SPS ceramic by SEM and TEM revealed grains with and without twins. The reason for the appearance of the tetragonal phase in the SPS sample sintered under strongly reducing conditions is discussed. (c) 2004 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 13
DOI: 10.1016/j.jeurceramsoc.2004.09.004
|
“The effect of hydrogen on the electronic and bonding properties of amorphous carbon”. Titantah JT, Lamoen D, Neyts E, Bogaerts A, Journal of physics : condensed matter 18, 10803 (2006). http://doi.org/10.1088/0953-8984/18/48/007
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 2.649
Times cited: 13
DOI: 10.1088/0953-8984/18/48/007
|
“The effect of temperature on the structural, electronic and optical properties of sp3-rich amorphous carbon”. Titantah JT, Lamoen D, Journal of physics : condensed matter 20, 035216 (2008). http://doi.org/10.1088/0953-8984/20/03/035216
Abstract: The effect of temperature on the structural, electronic and optical properties of dense tetrahedral amorphous carbon made of similar to 80% sp(3)-bonded atoms is investigated using a combination of the classical Monte Carlo technique and density functional theory. A structural transformation accompanied by a slight decrease of the sp(3) fraction is evidenced above a temperature of about 600 degrees C. A structural analysis in combination with energy-loss near-edge structure calculations shows that beyond this temperature, the sp(2)-bonded C sites arrange themselves so as to enhance the conjugation of the p electrons. The Tauc optical band gap deduced from the calculated dielectric function shows major changes beyond this temperature in accordance with experimental results. Energy-loss near-edge structure and band gap calculations additionally reveal a massive destabilization of the of sp(3) bonding phase in favour of sp(2) bonding at a temperature of about 1300 degrees C which agrees very well with the reported value of 1100 degrees C.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.649
Times cited: 11
DOI: 10.1088/0953-8984/20/03/035216
|
“Electronic structure of transparent oxides with the Tran-Blaha modified Becke-Johnson potential”. Dixit H, Saniz R, Cottenier S, Lamoen D, Partoens B, Journal of physics : condensed matter 24, 205503 (2012). http://doi.org/10.1088/0953-8984/24/20/205503
Abstract: We present electronic band structures of transparent oxides calculated using the Tran-Blaha modified Becke-Johnson (TB-mBJ) potential. We studied the basic n-type conducting binary oxides In2O3, ZnO, CdO and SnO2 along with the p-type conducting ternary oxides delafossite CuXO2 (X = Al, Ga, In) and spinel ZnX2O4 (X = Co, Rh, Ir). The results are presented for calculated band gaps and effective electron masses. We discuss the improvements in the band gap determination using TB-mBJ compared to the standard generalized gradient approximation (GGA) in density functional theory (DFT) and also compare the electronic band structure with available results from the quasiparticle GW method. It is shown that the calculated band gaps compare well with the experimental and GW results, although the electron effective mass is generally overestimated.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 2.649
Times cited: 113
DOI: 10.1088/0953-8984/24/20/205503
|
“Magnetodielectric CuCr0.5V0.5O2 : an example of a magnetic and dielectric multiglass”. Singh K, Maignan A, Simon C, Kumar S, Martin C, Lebedev O, Turner S, Van Tendeloo G, Journal of physics : condensed matter 24, 226002 (2012). http://doi.org/10.1088/0953-8984/24/22/226002
Abstract: The complex dielectric susceptibility and spin glass properties of polycrystalline CuCr0.5V 0.5O2 delafossite have been investigated. Electron diffraction, high resolution electron microscopy and electron energy loss spectroscopy show that the Cr3+ and V 3+ magnetic cations are randomly distributed on the triangular network of CdI2-type layers. In contrast to CuCrO2, CuCr0.5V 0.5O2 exhibits two distinctive (magnetic and electric) glassy states evidenced by memory effects in electric and magnetic susceptibilities. A large magnetodielectric coupling is observed at low temperature.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.649
Times cited: 19
DOI: 10.1088/0953-8984/24/22/226002
|
“The martensitic phase transition in Ni-Al: experimental observation of excess entropy and heterogeneous spontaneous strain”. Zhang H, Salje EKH, Schryvers D, Bartova B, Journal of physics : condensed matter 20, 055220 (2008). http://doi.org/10.1088/0953-8984/20/5/055220
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.649
Times cited: 7
DOI: 10.1088/0953-8984/20/5/055220
|
“Perovskite transparent conducting oxides : an ab initio study”. Dabaghmanesh S, Saniz R, Amini MN, Lamoen D, Partoens B, Journal of physics : condensed matter 25, 415503 (2013). http://doi.org/10.1088/0953-8984/25/41/415503
Abstract: We present an ab initio study of the electronic structure and of the formation energies of various point defects in BaSnO3 and SrGeO3. We show that La and Y impurities substituting Ba or Sr are shallow donors with a preferred 1 + charge state. These defects have a low formation energy within all the suitable equilibrium growth conditions considered. Oxygen vacancies behave as shallow donors as well, preferring the 2 + charge state. Their formation energies, however, are higher in most growth conditions, indicating a limited contribution to conductivity. The calculated electron effective mass in BaSnO3, with a value of 0.21 me, and the very high mobility reported recently in La-doped BaSnO3 single-crystals, suggest that remarkably low scattering rates can be achieved in the latter. In the case of SrGeO3, our results point to carrier density and mobility values in the low range for typical polycrystalline TCOs, in line with experiment.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT); Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 2.649
Times cited: 17
DOI: 10.1088/0953-8984/25/41/415503
|
“Quasiparticle band structure of rocksalt-CdO determined using maximally localized Wannier functions”. Dixit H, Lamoen D, Partoens B, Journal of physics : condensed matter 25, 035501 (2013). http://doi.org/10.1088/0953-8984/25/3/035501
Abstract: CdO in the rocksalt structure is an indirect band gap semiconductor. Thus, in order to determine its band gap one needs to calculate the complete band structure. However, in practice, the exact evaluation of the quasiparticle band structure for the large number of k-points which constitute the different symmetry lines in the Brillouin zone can be an extremely demanding task compared to the standard density functional theory (DFT) calculation. In this paper we report the full quasiparticle band structure of CdO using a plane-wave pseudopotential approach. In order to reduce the computational effort and time, we make use of maximally localized Wannier functions (MLWFs). The MLWFs offer a highly accurate method for interpolation of the DFT or GW band structure from a coarse k-point mesh in the irreducible Brillouin zone, resulting in a much reduced computational effort. The present paper discusses the technical details of the scheme along with the results obtained for the quasiparticle band gap and the electron effective mass.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 2.649
Times cited: 7
DOI: 10.1088/0953-8984/25/3/035501
|
“The quasiparticle band structure of zincblende and rocksalt ZnO”. Dixit H, Saniz R, Lamoen D, Partoens B, Journal of physics : condensed matter 22, 125505 (2010). http://doi.org/10.1088/0953-8984/22/12/125505
Abstract: We present the quasiparticle band structure of ZnO in its zincblende (ZB) and rocksalt (RS) phases at the Γ point, calculated within the GW approximation. The effect of the pd hybridization on the quasiparticle corrections to the band gap is discussed. We compare three systems, ZB-ZnO which shows strong pd hybridization and has a direct band gap, RS-ZnO which is also hybridized but includes inversion symmetry and therefore has an indirect band gap, and ZB-ZnS which shows a weaker hybridization due to a change of the chemical species from oxygen to sulfur. The quasiparticle corrections are calculated with different numbers of valence electrons in the Zn pseudopotential. We find that the Zn20 + pseudopotential is essential for the adequate treatment of the exchange interaction in the self-energy. The calculated GW band gaps are 2.47 eV and 4.27 eV respectively, for the ZB and RS phases. The ZB-ZnO band gap is underestimated compared to the experimental value of 3.27 by ~ 0.8 eV. The RS-ZnO band gap compares well with the experimental value of 4.5 eV. The underestimation for ZB-ZnO is correlated with the strong pd hybridization. The GW band gap for ZnS is 3.57 eV, compared to the experimental value of 3.8 eV.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 2.649
Times cited: 53
DOI: 10.1088/0953-8984/22/12/125505
|
“Superconducting nanowires: quantum confinement and spatially dependent Hartree-Fock potential”. Chen Y, Croitoru MD, Shanenko AA, Peeters FM, Journal of physics : condensed matter 21, 435701 (2009). http://doi.org/10.1088/0953-8984/21/43/435701
Abstract: It is well known that, in bulk, the solution of the Bogoliubovde Gennes equations is the same whether or not the HartreeFock term is included. Here the HartreeFock potential is position independent and so gives the same contribution to both the single-electron energies and the Fermi level (the chemical potential). Thus, the single-electron energies measured from the Fermi level (they control the solution) stay the same. This is not the case for nanostructured superconductors, where quantum confinement breaks the translational symmetry and results in a position-dependent HartreeFock potential. In this case its contribution to the single-electron energies depends on the relevant quantum numbers. We numerically solved the Bogoliubovde Gennes equations with the HartreeFock term for a clean superconducting nanocylinder and found a shift of the curve representing the thickness-dependent oscillations of the critical superconducting temperature to larger diameters.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 2.649
Times cited: 12
DOI: 10.1088/0953-8984/21/43/435701
|
“Swift heavy ion irradiation of Cu-Zn-Al and Cu-Al-Ni alloys”. Zelaya E, Tolley A, Condo AM, Schumacher G, Journal of physics : condensed matter 21, 185009 (2009). http://doi.org/10.1088/0953-8984/21/18/185009
Abstract: The effects produced by swift heavy ions in the martensitic (18R) and austenitic phase (beta) of Cu based shape memory alloys were characterized. Single crystal samples with a surface normal close to [210](18R) and [001](beta) were irradiated with 200 MeV of Kr(15+), 230 MeV of Xe(15+), 350 and 600 MeV of Au(26+) and Au(29+). Changes in the microstructure were studied with transmission electron microscopy (TEM) and high resolution transmission electron microscopy (HRTEM). It was found that swift heavy ion irradiation induced nanometer sized defects in the 18R martensitic phase. In contrast, a hexagonal close-packed phase formed on the irradiated surface of beta phase samples. HRTEM images of the nanometer sized defects observed in the 18R martensitic phase were compared with computer simulated images in order to interpret the origin of the observed contrast. The best agreement was obtained when the defects were assumed to consist of local composition modulations.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.649
Times cited: 8
DOI: 10.1088/0953-8984/21/18/185009
|
“Microstructure and spectroscopy studies on cubic boron nitride synthesized under high-pressure conditions”. Nistor LC, Nistor SV, Dinca G, Georgeoni P, van Landuyt J, Manfredotti C, Vittone E, Journal of physics : condensed matter 14, 10983 (2002). http://doi.org/10.1088/0953-8984/14/44/414
Abstract: High-resolution electron microscopy (HREM) studies of the microstructure and specific defects in hexagonal boron nitride (h-BN) precursors and cubic boron nitride (c-BN) crystals made under high-pressure high-temperature conditions revealed the presence of half-nanotubes at the edges of the h-BN particles. Their sp(3) bonding tendency could strongly influence the nucleation rates of c-BN. The atomic resolution at extended dislocations was insufficient to allow us to determine the stacking fault energy in the c-BN crystals. Its mean value of 191 +/- 15 mJ m(-2) is of the same order of magnitude as that of diamond. High-frequency (94 GHz) electron paramagnetic resonance studies on c-BN single crystals have produced new data on the D1 centres associated with the boron species. Ion-beam-induced luminescence measurements have indicated that c-BN is a very interesting luminescent material, which is characterized by four luminescence bands and exhibits a better resistance to ionizing radiation than CVD diamond.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.649
Times cited: 7
DOI: 10.1088/0953-8984/14/44/414
|
“Optical spectroscopy of oxygen precipitates in heavily doped p-type silicon”. Simoen E, Loo R, Claeys C, de Gryse O, Clauws P, van Landuyt J, Lebedev O, Journal of physics : condensed matter
T2 –, Conference on Extended Defects in Semiconductors (EDS 2002), JUN 01-06, 2002, BOLOGNA, ITALY 14, 13185 (2002). http://doi.org/10.1088/0953-8984/14/48/367
Abstract: Results are presented on the photoluminescence (PL) characterization of heavily doped p(+) Czochralski silicon, which has been subjected to a two-step, oxygen precipitation heat treatment. It will be shown that the presence of oxygen precipitates gives rise to the D1, D2 and D5 lines, where the energy of the D1 line shifts to lower values for a stronger degree of precipitation. The occurrence of these PL features is also a function of the boron concentration in the p(+) material. The PL results are compared with Fourier transform infrared absorption data and with transmission electron microscope, results. From this, it is concluded that PL has a good potential for use in the assessment of oxygen precipitation in heavily doped silicon.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.649
Times cited: 3
DOI: 10.1088/0953-8984/14/48/367
|
“Neutron and X-ray scattering cross sections of orientationally disordered solid C60”. Copley JRD, Michel KH, Journal Of Physics-Condensed Matter 5, 4353 (1993)
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
Impact Factor: 2.346
Times cited: 34
|
“Structure of nanoscale mesoporous silica spheres?”.Van Tendeloo G, Lebedev OI, Collart O, Cool P, Vansant EF, Journal of physics : condensed matter 15, S3037 (2003)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 2.649
|
“Physical properties of epitaxial SrMnO2.5−δFγoxyfluoride films”. Wang J, Shin Y, Gauquelin N, Yang Y, Lee C, Jannis D, Verbeeck J, Rondinelli JM, May SJ, Journal of physics : condensed matter 31, 365602 (2019). http://doi.org/10.1088/1361-648X/ab2414
Abstract: Recently, topotactic fluorination has become an alternative way of doping epitaxial perovskite oxides through anion substitution to engineer their electronic properties instead of the more commonly used cation substitution. In this work, epitaxial oxyfluoride SrMnO2.5−δ F γ films were synthesized via topotactic fluorination of SrMnO2.5 films using polytetrafluoroethylene as the fluorine source. Oxidized SrMnO3 films were also prepared for comparison with the fluorinated samples. The F content, probed by x-ray photoemission spectroscopy, was systematically controlled by adjusting fluorination conditions. Electronic transport measurements reveal that increased F content (up to γ = 0.14) systematically increases the electrical resistivity, despite the nominal electron-doping induced by F substitution for O in these films. In contrast, oxidized SrMnO3 exhibits a decreased resistivity and conduction activation energy. A blue-shift of optical absorption features occurs with increasing F content. Density functional theory calculations indicate that F acts as a scattering center for electronic transport, controls the observed weak ferromagnetic behavior of the films, and reduces the inter-band optical transitions in the manganite films. These results stand in contrast to bulk electron-doped La1−x Ce x MnO3, illustrating how aliovalent anionic substitutions can yield physical behavior distinct from A-site substituted perovskites with the same nominal B-site oxidation states.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.649
Times cited: 5
DOI: 10.1088/1361-648X/ab2414
|
“Inhomogeneous superconductivity and quasilinear magnetoresistance at amorphous LaTiO₃/SrTiO₃, interfaces”. Lebedev N, Stehno M, Rana A, Gauquelin N, Verbeeck J, Brinkman A, Aarts J, Journal Of Physics-Condensed Matter 33, 055001 (2020). http://doi.org/10.1088/1361-648X/ABC102
Abstract: We have studied the transport properties of LaTiO3/SrTiO3 (LTO/STO) heterostructures. In spite of 2D growth observed in reflection high energy electron diffraction, transmission electron microscopy images revealed that the samples tend to amorphize. Still, we observe that the structures are conducting, and some of them exhibit high conductance and/or superconductivity. We established that conductivity arises mainly on the STO side of the interface, and shows all the signs of the two-dimensional electron gas usually observed at interfaces between STO and LTO or LaAlO3, including the presence of two electron bands and tunability with a gate voltage. Analysis of magnetoresistance (MR) and superconductivity indicates the presence of spatial fluctuations of the electronic properties in our samples. That can explain the observed quasilinear out-of-plane MR, as well as various features of the in-plane MR and the observed superconductivity.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.7
Times cited: 1
DOI: 10.1088/1361-648X/ABC102
|
“Barrier efficiency of sponge-like La2Zr2O7 buffer layers for YBCO-coated conductors”. Molina L, Tan H, Biermans E, Batenburg KJ, Verbeeck J, Bals S, Van Tendeloo G, Superconductor science and technology 24, 065019 (2011). http://doi.org/10.1088/0953-2048/24/6/065019
Abstract: Solution derived La2Zr2O7 films have drawn much attention for potential applications as thermal barriers or low-cost buffer layers for coated conductor technology. Annealing and coating parameters strongly affect the microstructure of La2Zr2O7, but different film processing methods can yield similar microstructural features such as nanovoids and nanometer-sized La2Zr2O7 grains. Nanoporosity is a typical feature found in such films and the implications for the functionality of the films are investigated by a combination of scanning transmission electron microscopy (STEM), electron energy-loss spectroscopy (EELS) and quantitative electron tomography. Chemical solution based La2Zr2O7 films deposited on flexible Ni5 at.%W substrates with a {100}lang001rang biaxial texture were prepared for an in-depth characterization. A sponge-like structure composed of nanometer-sized voids is revealed by high-angle annular dark-field scanning transmission electron microscopy in combination with electron tomography. A three-dimensional quantification of nanovoids in the La2Zr2O7 film is obtained on a local scale. Mostly non-interconnected highly faceted nanovoids compromise more than one-fifth of the investigated sample volume. The diffusion barrier efficiency of a 170 nm thick La2Zr2O7 film is investigated by STEM-EELS, yielding a 1.8 ± 0.2 nm oxide layer beyond which no significant nickel diffusion can be detected and intermixing is observed. This is of particular significance for the functionality of YBa2Cu3O7 − δ coated conductor architectures based on solution derived La2Zr2O7 films as diffusion barriers.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.878
Times cited: 31
DOI: 10.1088/0953-2048/24/6/065019
|
“Chemical solution deposition: a path towards low cost coated conductors”. Obradors X, Puig T, Pomar A, Sandiumenge F, Piñol S, Mestres N, Castaño O, Coll M, Cavallaro A, Palau A, Gázquez J, González JC, Gutiérrez J, Romá, N, Ricart S, Moretó, JM, Rossell MD, Van Tendeloo G, Superconductor science and technology 17, 1055 (2004). http://doi.org/10.1088/0953-2048/17/8/020
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 107
DOI: 10.1088/0953-2048/17/8/020
|
“Critical assessment of the process of growth of a YBa2Cu3O7-\delta layer on Y2BaCuO5”. Jacques P, Verbist K, Lapin J, Ryelandt L, Van Tendeloo G, Delannay F, Superconductor science and technology 9, 176 (1996). http://doi.org/10.1088/0953-2048/9/3/008
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.325
Times cited: 1
DOI: 10.1088/0953-2048/9/3/008
|
“Interlayer structure in YBCO-coated conductors prepared by chemical solution deposition”. Molina L, Egoavil R, Turner S, Thersleff T, Verbeeck J, Holzapfel B, Eibl O, Van Tendeloo G, Superconductor science and technology 26, 075016 (2013). http://doi.org/10.1088/0953-2048/26/7/075016
Abstract: The functionality of YBa2Cu3O7−δ (YBCO)-coated conductor technology depends on the reliability and microstructural properties of a given tape or wire architecture. Particularly, the interface to the metal tape is of interest since it determines the adhesion, mechanical stability of the film and thermal contact of the film to the substrate. A trifluoroacetate (TFA)metal organic deposition (MOD) prepared YBCO film deposited on a chemical solution-derived buffer layer architecture based on CeO2/La2Zr2O7 and grown on a flexible Ni5 at.%W substrate with a {100}⟨001⟩ biaxial texture was investigated. The YBCO film had a thickness was 440 nm and a jc of 1.02 MA cm−2 was determined at 77 K and zero external field. We present a sub-nanoscale analysis of a fully processed solution-derived YBCO-coated conductor by aberration-corrected scanning transmission electron microscopy (STEM) combined with electron energy-loss spectroscopy (EELS). For the first time, structural and chemical analysis of the valence has been carried out on the sub-nm scale. Intermixing of Ni, La, Ce, O and Ba takes place at these interfaces and gives rise to nanometer-sized interlayers which are a by-product of the sequential annealing process. Two distinct interfacial regions were analyzed in detail: (i) the YBCO/CeO2/La2Zr2O7 region (10 nm interlayer) and (ii) the La2Zr2O7/Ni5 at.%W substrate interface region (20 nm NiO). This is of particular significance for the functionality of these YBCO-coated conductor architectures grown by chemical solution deposition.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 11
DOI: 10.1088/0953-2048/26/7/075016
|
“Low- or high-angle Ar ion-beam etching to create ramp-type Josephson junctions”. Verbist K, Lebedev OI, Van Tendeloo G, Verhoeven MAJ, Rijnders AJHM, Blank DHA, Superconductor science and technology 9, 978 (1996). http://doi.org/10.1088/0953-2048/9/11/009
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.325
Times cited: 10
DOI: 10.1088/0953-2048/9/11/009
|
“Epitaxial YBa2Cu3O7−xnanocomposite thin films from colloidal solutions”. Cayado P, De Keukeleere K, Garzón A, Perez-Mirabet L, Meledin A, De Roo J, Vallés F, Mundet B, Rijckaert H, Pollefeyt G, Coll M, Ricart S, Palau A, Gázquez J, Ros J, Van Tendeloo G, Van Driessche I, Puig T, Obradors X, Superconductor science and technology 28, 124007 (2015). http://doi.org/10.1088/0953-2048/28/12/124007
Abstract: A methodology of general validity to prepare epitaxial nanocomposite films based on the use of colloidal solutions containing different crystalline preformed oxide nanoparticles ( ex situ nanocomposites) is reported. The trifluoroacetate (TFA) metal–organic chemical solution deposition route is used with alcoholic solvents to grow epitaxial YBa 2 Cu 3 O 7 (YBCO) films. For this reason stabilizing oxide nanoparticles in polar solvents is a challenging goal. We have used scalable nanoparticle synthetic methodologies such as thermal and microwave-assisted solvothermal techniques to prepare CeO 2 and ZrO 2 nanoparticles. We show that stable and homogeneous colloidal solutions with these nanoparticles can be reached using benzyl alcohol, triethyleneglycol, nonanoic acid, trifluoroacetic acid or decanoic acid as protecting ligands, thereby allowing subsequent mixing with alcoholic TFA solutions. An elaborate YBCO film growth analysis of these nanocomposites allows the identification of the different relevant growth phenomena, e.g. nanoparticles pushing towards the film surface, nanoparticle reactivity, coarsening and nanoparticle accumulation at the substrate interface. Upon mitigation of these effects, YBCO nanocomposite films with high self-field critical currents ( J c ∼ 3–4 MA cm −2 at 77 K) were reached, indicating no current limitation effects associated with epitaxy perturbation, while smoothed magnetic field dependences of the critical currents at high magnetic fields and decreased effective anisotropic pinning behavior confirm the effectiveness of the novel developed approach to enhance vortex pinning. In conclusion, a novel low cost solution-derived route to high current nanocomposite superconducting films and coated conductors has been developed with very promising features.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 32
DOI: 10.1088/0953-2048/28/12/124007
|
“Microstructure of YBa2Cu3O7-\delta Josephson junctions in relation to their properties”. Verbist K, Lebedev OI, Verhoeven MAJ, Winchern R, Rijnders AJHM, Blank DHA, Tafuri F, Bender H, Van Tendeloo G, Superconductor science and technology 11, 13 (1998). http://doi.org/10.1088/0953-2048/11/1/004
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
DOI: 10.1088/0953-2048/11/1/004
|
“Structural properties of Zn-substituted epitaxial YBa2Cu3O7-\delta thin films”. Ye M, Schroeder J, Mehbod M, Deltour R, Naessens G, Duvigneaud PH, Verbist K, Van Tendeloo G, Superconductor science and technology 9, 543 (1996). http://doi.org/10.1088/0953-2048/9/7/006
Abstract: We optimized the deposition of YBa2(Cu1-xZnx)(3)O-7-delta thin-films using inverted cylindrical magnetron sputtering and report here a detailed structural study, especially in relation to crystal growth, associated surface morphology, Y2O3 precipitation and other secondary phases important for flux pinning. We find that the epitaxial quality of the Zn-substituted YBa2Cu3O7-delta films is decreased compared with high-quality pure YBa2Cu3O7-delta films prepared under identical conditions. The pure films have smoother surfaces, while those of Zn-substituted films contain pinholes and outgrowths. Secondary phases and a-axis grains were observed in the Zn-substituted films. Y2O3 precipitates with typical dimensions of 50-100 Angstrom have been found in both pure and Zn-substituted samples. However, their density of about 10(23) m(-3), observed in the pure films, is significantly reduced in the Zn-substituted films when increasing the Zn concentration up to 4%.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.325
Times cited: 7
DOI: 10.1088/0953-2048/9/7/006
|
“The superstructure and superconductivity of Ru1222 based RuSr2Gd2-x-yYyCexCu2O10-\delta compounds”. Tan H, Lebedev OI, McLaughlin AC, Van Tendeloo G, Superconductor science and technology 23, 115013 (2010). http://doi.org/10.1088/0953-2048/23/11/115013
Abstract: For the first time, the local structure and physical properties of Ru1222 based compounds (RuSr(2)Gd(1.4)Ce(0.6)Cu(2)O(10-delta) and RuSr(2)Gd(1.8-x)Y(0.2)CexCu(2)O(10) (x = 0.90-0.55)) have been investigated and analyzed together on the very same compounds. The Ru1222 superstructure was confirmed by TEM at a local scale and was suggested to have an orthorhombic symmetry with space group Aba2 and lattice parameters a(s) similar or equal to root 2a, b(s) similar or equal to root 2a and c(s) = c. This new Ru1222 superstructure distortion from tetragonal symmetry is proposed to have a positive correlation with the superconductivity variation of these compounds. The more the distortion towards orthorhombic symmetry, the higher the critical superconducting temperature these compounds can achieve. The T(c)(0) of RuSr(2)Gd(1.8-x)Y(0.2)Ce(x)Cu(2)O(10-delta) (x = 0.85-0.55) increases monotonically from 4 to 16 K when x decreases from 0.85 to 0.70, then RuSr(2)Gd(2)Cu(2)O(8) defects emerge and the T(c) decreases with decreasing x. Ru1212 defects are observed to intergrow epitaxially with the Ru1222 structure as lamellas along the c-axis in RuSr(2)Gd(1.4)Ce(0.6)Cu(2)O(10-delta). Although Ru1212 is a superconductor, the intergrowth severely restrains its superconductivity.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 1
DOI: 10.1088/0953-2048/23/11/115013
|
“YBa2Cu3O7-x Josephson junctions and dc SQUIDs based on 45\text{\textdegree} a-axis tilt and twist grain boundaries : atomically clean interfaces for applications”. Tafuri F, Carillo F, Lombardi F, Granozio FM, dii Uccio US, Testa G, Sarnelli E, Verbist K, Van Tendeloo G, Superconductor science and technology
T2 –, International Superconductive Electronics Conference, JUN 21-25, 1999, BERKELEY, CALIFORNIA 12, 1007 (1999). http://doi.org/10.1088/0953-2048/12/11/393
Abstract: YBa2Cu3O7-x artificial grain boundary Josephson junctions have been fabricated, employing a recently implemented biepitaxial technique. The grain boundaries can be obtained by controlling the orientation of the MgO seed layer and are characterized by a misalignment of the c-axes (45 degrees a-axis tilt or 45 degrees a-axis twist). These types of grain boundaries are still mostly unexplored. We carried out a complete characterization of their transport properties and microstructure. Junctions and de SQUIDs associated with these grain boundaries exhibit an excellent Josephson phenomenology and high values of the ICRN product and of the magnetic flux-to-voltage transfer parameter respectively. Remarkable differences in the transport parameters of tilt and twist junctions have been observed, which can be of interest for several applications. A maximum speed of Josephson vortices as calculated from the voltage step values of the order of 2 x 10(6) m s(-1) is obtained. These devices could also have some impact on experiments designed to study the symmetry of the order parameter, exploiting their microstructure and anisotropic properties. High-resolution electron microscopy showed the presence of perfect basal plane faced boundaries in the cross sections of tilt boundaries.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.878
Times cited: 3
DOI: 10.1088/0953-2048/12/11/393
|