Abstract: A LuFe2O4+delta sample, previously characterized by X-ray synchrotron and neutron diffraction, has been studied by electron microscopy techniques, in order to get a precise description of its micro- and nanostructures at room temperature. The X-ray synchrotron data vs. temperature show that the monoclinic distortion is associated with the charge ordering; this distortion results in elongated twinning domains, which enhance the complexity of the microstructural state at room temperature. The structural modulation associated with oxygen excess is observed in large domains inside a non modulated matrix, in contrast with the modulations associated with the charge ordering of the Fe2+ and Fe3+ species, which are mostly short-range. The investigation of the nature and density of defects in the sample shows that they are nano-scaled, preserving the regularity of the layer stacking mode, and limited to the formation of one- or two-units large stacking faults, associated with gliding mechanisms. Based on these observations, an original description of the LuFe2O4 ferrite structure, through puckered [LuO4](infinity) sandwiching [Fe-2](infinity) layers, is proposed. (C) 2013 Elsevier Masson SAS. All rights reserved.

Abstract: The Fe2(Sr2 − xAx)FeO6.5 − ä/2 systems have been investigated, by doping the iron rich 2201-type parent structure with Ba2+, La3+ and 5d10 post-transition cations. The syntheses have been carried out up to the limit of the 2201-type solid solutions, in order to test the role of the double iron layer Fe2O2.5 − ä/2. The localisation of the charge carriers in these compounds is consistent with their strong antiferro-magnetism. The investigation was then carried out in the transition part of the diagram up to the formation of stable phases. The study of structural mechanisms was carried using high resolution electron microscopy (transmission and scanning transmission), electron diffraction and energy dispersive spectroscopy. Different non-stoichiometry mechanisms are observed, depending on the electronic structure and chemical properties of the doping elements. The specific behavior of the modulated double iron layer is discussed.

Abstract: Neodymium nickelate thin films have been prepared on NdGaO3 substrates by RF magnetron sputtering and post-annealing treatment under oxygen pressure. Transport properties are found to depend strongly on film thickness. Thick films show transport properties close to bulk ceramics, while very thin films exhibit a large transition from metal to insulator which occurs over a wide temperature range with high resistivity. Structure and surface morphology of the films have been investigated by Transmission Electron Microscopy (TEM) and Atomic Force Microscopy (AFM). Thin films (approximate to17 nm) grow heteroepitaxially, while thicker films (approximate to73 nm) show a granular structure. The thinnest sample suggests a symmetry change induced by the epitaxial strain of the substrate. This paper discusses the relationship between microstructure and transport properties.

Abstract: The present paper gives a review of results of recent studies investigating the fundamentals of the martensitic and related phase transformations in Ni-Al. For the former case, the emphasis will be on the microstructure of martensite plates. The latter include the metastable Ni2Al omega-like and stable Ni5Al3 bainitic phases. These phases will be discussed in view of their atomic structure, nucleation, growth and effect on the martensitic transformation. A separate chapter will deal with precursor effects.

Abstract: We measured the electrical resistivity R(T) and specific heat C-p(T) between room temperature (RT) and 4.2 K as well as the microstructure by transmission electron microscopy (TEM) of a Ni-52 Ti-48 SMA quenched from 1000degreesC (B2-Phase range) to RT and then annealed for 1h at T=380degreesC, 550degreesC and 650degreesC. In the “as quenched” and the “650degreesC annealed” state no martensitic transformations (MT's) occur. The diffraction patterns show faint reflections originating from coherent Ni4Ti3 precipitates in an early state of formation. Additional reflections of the type 1/2 <110>, 1/2 <111> and 1/3 <110> result from various lattice displacement waves, which are precursors of the MT's to the B19' and R-phase, respectively. Indeed, high resolution TEM micrographs of the [001] zone of the “as quenched” sample reveal transverse 1/2 <110> <110> lattice displacement waves, precursors of the B19' martensite. The coherent Ni4Ti3 precipitates, homogeneously distributed on a small length scale, binder the MT's in the “as quenched” and the “650degreesC annealed” state, and thus only the precursors appear. When annealed at T=380degreesC, however, coherent Ni4Ti3 precipitates with a length of 10nm are clearly visible in TEM. These precipitates trigger the NIT from the B2 to the R-phase on cooling, as evidenced also by anomalies in R(T) and C-p(T). Annealing at T-550degreesC leads to the well known two step MT's from the B2 to the R-phase and then into the B19'-phase. These martensitic transitions are clearly seen as additional peaks in the specific heat and anomalies in the resistance, while the “as quenched” and 650degreesC annealed samples show weak features in R(T) and C-p(T).