Abstract: This work addresses the dissolution corrosion behaviour of 316L austenitic stainless steels. For this purpose, solution-annealed and cold-deformed 316L steels were simultaneously exposed to oxygen-poor (<10-8 mass%) static liquid lead-bismuth eutectic (LBE) for 253e3282 h at 500 °C. Corrosion was consistently more severe for the cold-drawn steels than the solution-annealed steel, indicating the importance of the steel thermomechanical state. The thickness of the dissolution-affected zone was nonuniform, and sites of locally-enhanced dissolution were occasionally observed. The progress of LBE dissolution attack was promoted by the interplay of certain steel microstructural features (grain boundaries, deformation twin laths, precipitates) with the dissolution corrosion process. The identified dissolution mechanisms were selective leaching leading to steel ferritization, and non-selective leaching; the latter was mainly observed in the solution-annealed steel. The maximum corrosion rate decreased with exposure time and was found to be inversely proportional to the depth of dissolution attack.

Abstract: The present work reports on the microstructural evolution of a new heat of 24% cold worked austenitic DIN 1.4970 (15-15Ti) nuclear cladding steel subjected to ageing heat treatments of varying duration between 500 and 800 degrees C (by steps of 100 degrees C). The primary aim was studying the finely dispersed Ti-C nanoprecipitate population, which are thought to be beneficial for creep and swelling resistance during service. Their size distribution and number density were estimated through dark field imaging and bright field Moire imaging techniques in the transmission electron microscope. Nanoprecipitates formed at and above 600 degrees C, which is a lower temperature than previously reported. The observed nucleation, growth and coarsening behavior of the nanoprecipitates were consistent with simple diffusion arguments. The formation of nanoprecipitates coincided with significant dissociation of dislocations as evidenced by weak beam dark field imaging. Possible mechanisms, including Silcock's stacking fault growth model and Suzuki segregation, are discussed. Recrystallization observed after extended ageing at 800 degrees C caused the redissolution of nanoprecipitates. Large primary Ti(C,N) and (Ti,Mo)C precipitates that occur in the as-received material, and M23C6 precipitates that nucleate on grain boundaries at low temperatures were also characterized by a selective dissolution procedure involving filtration, X-ray diffraction and quantitative Rietveld refinement. The partitioning of key elements between the different phases was derived by combining these findings and was consistent with thermodynamic considerations and the processing history of the steel. (C) 2018 Elsevier B.V. All rights reserved.

Abstract: The microstructural features of intergranular irradiation-assisted stress corrosion crack tips from a redeemed neutron-irradiated flux thimble tube (60 dpa) have been investigated using focused-ion beam analysis and (scanning) transmission electron microscopy. The current work presents a close examination of the deformation field and oxide assembly associated with intergranular cracking, in addition to the analysis of radiation-induced segregation at leading grain boundaries. Evidence of stress induced martensitic transformation extending from the crack tips is presented. Intergranular crack arrest is demonstrated on the account of the external tensile stress orientation, and as a consequence of MnS inclusion particles segregating close to the fractured grain boundary. Exclusive observations of grain boundary oxidation prior to the cracking are presented, which is in full-agreement with the internal oxidation model.(c) 2022 Elsevier B.V. All rights reserved.

Abstract: Soil samples from an abandoned uranium mine have been investigated in order to determine the molecular phases of uranium compounds. The experiments were carried out with soil particulate matter, collected randomly from the area of the formerly exploited ore. To select the particles rich with uranium, scanning electron microscopy with energy-dispersive X-ray attachment (SEM/EDX) was applied first. Afterwards, the particles were relocated and measured by l-Raman spectrometry (MRS). Residues of the main deposit, uraninite UO2, were detected, along with its alteration products. In terms of Raman scattering properties, uranium oxides are quite sensitive to the laser beam wavelength, which results in very specific features of their Raman spectra. In this paper the Raman spectra of uranium oxides of different origin and oxidation states, measured with 514 and 785 nm lasers, are also presented

Abstract: Hollow silica spheres were quickly synthesized by an octylamine (OA) templating method using tetraethyl orthosilicate (TEOS) as the silica source. N2-sorption results indicate that the hollow spheres have high surface areas and pore volumes. XRD and TEM measurements reveal that the structure of the hollow spheres depends on the amount of TEOS used in the synthesis. When low amount of TEOS is added, the template-containing precursor spheres depict an XRD pattern with two peaks, which can be indexed to a lamellar phase. After the removal of the template, the obtained hollow spheres show no diffraction peaks in the XRD pattern, suggesting that the nanopores in the silica shells are disordered. If increasing the amount of TEOS, either the uncalcined or the calcined sample gives an XRD pattern with a single diffraction peak. The mesostructure of these hollow silica spheres is typically as HMS materials. TGA analyses suggest that the interaction between the silica species and surfactant is stronger in the latter case.

Abstract: This study demonstrates that the mechanism responsible for the transformation of glass into a degradation layer is pH-dependent. In acid conditions, the transformed glass is homogeneous and brittle. In mild alkaline conditions, transformed glass is heterogeneous due to the presence of lamellae composed of silica nanoparticles and the occurrence of Ca-rich inclusions. The fundamental difference between acid and alkaline conditions cannot be explained by the currently accepted degradation mechanism based on ion exchange. To explain this critical observation, we propose a refined degradation mechanism based on existing knowledge that involves several inwardly moving reaction fronts. The fronts responsible for the transformation of the silicate network into amorphous silica are also responsible for the morphology of the transformed glass. We have identified the feedback mechanism that explains the formation of lamellae in alkaline conditions.

Abstract: The formation of CH⋯S and CH⋯P hydrogen bonded complexes of halothane, CHBrClCF3, with dimethyl sulfide(-d6) and trimethylphosphine(-d9) have been studied in solutions of liquid krypton using infrared and Raman spectroscopy. In the 1:1 complexes, the halothane CH stretching mode is found to be red-shifted by 43 cm−1 in the dimethyl sulfide complex, and by 63 cm−1 in the trimethylphosphine complex. The complexation enthalpies were derived and amount to −10.7(2) and −11.2(2) kJ mol−1 for the respective complexes. The experiments were supported by ab initio calculations and Monte Carlo simulations. The obtained data for the CH⋯S and CH⋯P hydrogen bonds is compared to that of corresponding CH⋯O and CH⋯N hydrogen bonds.

Abstract: The reinvestigation of the EDA-HIO3-H2O system using a different stoichiometric ratio gives rise to a new iodate salt C2H10N2(IO3)(2 center dot)HIO3 denoted as EBIMIA. In this study, we reported the structural properties of ethylenediammonium bis iodate mono iodic acid using X-ray powder and single crystal diffraction at room temperature. The Hirshfeld and the potential energy surface analysis reveal that I center dot center dot center dot O and N-H center dot center dot center dot O are the most noticeable interactions that took place inside the crystal and contribute to the cohesion and stability of the synthesized compound. The DSC measurement shows that this iodate salt undergoes two structural phase transitions, the first occurs at T = 290 K while the second occurs at T = 363 K. However, the dielectric analysis confirms only the second transition because it lies in the studied temperature domain 338-413K. Besides, the impedance data obey a circuit model consisting of a parallel combination of a bulk resistance and CPE. The frequency dispersion of the conductivity follows Jonscher's law and the charge carrier transport may be interpreted using the correlation barrier hopping mechanism (CBH). Finally, the electronic properties and the vibrational analysis of this novel iodate salt are studied using DFT and compared to the experimental data given by the FT-IR, Raman and UV-visible spectroscopies. (C) 2020 Elsevier B.V. All rights reserved.