“Doping of Bi4Fe5O13F with pentagonal Cairo lattice with Cr and Mn: Synthesis, structure and magnetic properties”. Rozova MG, Grigoriev VV, Tyablikov OA, Filimonov DS, Zakharov KV, Volkova OS, Vasiliev AN, Antipov EV, Abakumov AM, Materials research bulletin 87, 54 (2017). http://doi.org/10.1016/J.MATERRESBULL.2016.11.018
Abstract: The substitution of Cr3+ and Mn3+ for Fe3+ in the Bi4Fe6O13F oxyfluoride featuring the magnetically frustrated pentagonal Cairo lattice is reported. Bi4Fe4.1Cr0.9O13F and BiFe4.2Mn0.8O13F have been prepared using a solid state reaction in inert atmosphere. Their crystal structures were studied with transmission electron microscopy, powder X-ray diffraction and Fe-57 Mossbauer spectroscopy (S.G. P4(2)/mbc, a = 8.27836(2)angstrom, c = 18.00330(9) angstrom, R-F = 0.031 (Bi4Fe4.1Cr0.9O13F)), a= 8.29535(3)angstrom, c= 18.0060(1)angstrom, R-F = 0.027 (Bi4Fe4.1Cr0.9O13F)). The structures are formed by infinite rutile-like chains of the edge sharing BO6 octahedra (B transition metal cations) linked by the Fe2O7 groups of two corner-sharing tetrahedra. The"voids in thus formed framework are occupied by the Bi4F tetrahedra. The Fe-57 Mossbauer spectroscopy reveals that Cr3+ and Mn3+ replace Fe3+. exclusively at the octahedral positions. The Mn- and Cr-doped compounds demonstrate antiferromagnetic ordering below T-N =165 K and 120 K, respectively. (C) 2016 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 1
DOI: 10.1016/J.MATERRESBULL.2016.11.018
|
|
|
“Crystal structure and magnetic properties of the Cr-doped spiral antiferromagnet BiMnFe2O6”. Batuk D, de Dobbelaere C, Tsirlin AA, Abakumov AM, Hardy A, van Bael MK, Greenblatt M, Hadermann J, Materials research bulletin 48, 2993 (2013). http://doi.org/10.1016/j.materresbull.2013.04.038
Abstract: We report the Cr3+ for Mn3+ substitution in the BiMnFe2O6 structure. The BiCrxMn1-xFe2O6 solid solution is obtained by the solution-gel synthesis technique for the x values up to 0.3. The crystal structure investigation using a combination of X-ray powder diffraction and transmission electron microscopy demonstrates that the compounds retain the parent BiMnFe2O6 structure (for x = 0.3, a = 5.02010(6)angstrom, b = 7.06594(7)angstrom, c = 12.6174(1)angstrom, S.G. Pbcm, R-1 = 0.036, R-p = 0.011) with only a slight decrease in the cell parameters associated with the Cr3+ for Mn3+ substitution. Magnetic susceptibility measurements suggest strong similarities in the magnetic behavior of BiCrxMn1-xFe2O6 (x = 0.2; 0.3) and parent BiMnFe2O6. Only T-N slightly decreases upon Cr doping that indicates a very subtle influence of Cr3+ cations on the magnetic properties at the available substitution rates. (C) 2013 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 3
DOI: 10.1016/j.materresbull.2013.04.038
|
|
|
“Crystal structure and properties of the new complex vanadium oxide K2SrV3O9”. Tsirlin AA, Chernaya VV, Shpanchenko RV, Antipov EV, Hadermann J, Materials research bulletin 40, 800 (2005). http://doi.org/10.1016/j.materresbull.2005.02.004
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 9
DOI: 10.1016/j.materresbull.2005.02.004
|
|
|
“Crystal structures of superconducting sodium intercalates of hafnium nitride chloride”. Oró-Solé, J, Frontera C, Beltrán-Porter D, Lebedev OI, Van Tendeloo G, Fuertes A, Materials research bulletin 41, 934 (2006). http://doi.org/10.1016/j.materresbull.2006.03.018
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 8
DOI: 10.1016/j.materresbull.2006.03.018
|
|
|
“Fluorine intercalation in the n=1 and n=2 layered manganites Sr2MnO3.5+x and Sr3Mn2O6”. Sullivan E, Gillie LJ, Hadermann J, Greaves C, Materials research bulletin 48, 1598 (2013). http://doi.org/10.1016/j.materresbull.2012.12.073
Abstract: Fluorine insertion into the oxygen defect superstructure manganite Sr2MnO3.5+x has been shown by transmission electron microscopy (TEM) to result in two levels of fluorination. In the higher fluorine content sections, the fluorine anions displace oxygen anions from their apical positions into the equatorial vacancies, thus destroying the superstructure and reverting to a K2NiF4-type structure (a = 3.8210(1) angstrom and c = 12.686(1) angstrom). Conversely, lower fluorine content sections retain the Sr2MnO3.5+x defect superstructure, crystallising in the P2(1)/c space group. Fluorine intercalation into the reduced double-layer manganite Sr3Mn2O6 occurs in a step-wise fashion according to the general formula Sr3Mn2O6Fy with y = 1, 2, and 3. It is proposed that the y = 1 phase (a = 3.815(1)angstrom, c = 20.29(2) angstrom) is produced by the filling of all the equatorial oxygen vacancies by fluorine atoms whilst the y = 2 phase (a = 3.8222(2) angstrom, c = 21.2435(3)angstrom) has a random distribution of fluorine anions throughout both interstitial rocksalt and equatorial sites. Neutron powder diffraction data suggest that the fully fluorinated y = 3 phase (a = 3.8157(6) angstrom, c = 23.666(4) angstrom) corresponds to the complete occupation of all the equatorial oxygen vacancies and the interstitial sites by intercalated fluorine. (C) 2013 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 4
DOI: 10.1016/j.materresbull.2012.12.073
|
|
|
“Fluorite-like phases in the BaF2-BiF3-Bi2O3 system-synthesis, conductivity and defect clustering”. Serov TV, Dombrovski EN, Ardashnikova EI, Dolgikh VA, el Omari M, el Omari M, Abaouz A, Senegas J, Chaban NG, Abakumov AM, Van Tendeloo G, Materials research bulletin 40, 821 (2005). http://doi.org/10.1016/j.materresbull.2005.02.007
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 4
DOI: 10.1016/j.materresbull.2005.02.007
|
|
|
“Influence of laser and isothermal treatments on microstructural properties of SnO2 films”. Rembeza ES, Richard O, van Landuyt J, Materials research bulletin 34, 1527 (1999). http://doi.org/10.1016/S0025-5408(99)00188-9
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 17
DOI: 10.1016/S0025-5408(99)00188-9
|
|
|
“New lead vanadium phosphate with langbeinite-type structure: Pb1.5V2(PO4)3”. Shpanchenko RV, Lapshina OA, Antipov EV, Hadermann J, Kaul EE, Geibel C, Materials research bulletin 40, 1569 (2005). http://doi.org/10.1016/j.materresbull.2005.04.037
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 14
DOI: 10.1016/j.materresbull.2005.04.037
|
|
|
“Properties and thermal stability of solution processed ultrathin, high-k bismuth titanate (Bi2Ti2O7) films”. Hardy A, Van Elshocht S, De Dobbelaere C, Hadermann J, Pourtois G, De Gendt S, Afanas'ev VV, Van Bael MK, Materials research bulletin 47, 511 (2012). http://doi.org/10.1016/j.materresbull.2012.01.001
Abstract: Ultrathin bismuth titanate films (Bi2Ti2O7, 5-25 nm) are deposited onto SiO2/Si substrates by aqueous chemical solution deposition and their evolution during annealing is studied. The films crystallize into a preferentially oriented, pure pyrochlore phase between 500 and 700 degrees C, depending on the film thickness and the total thermal budget. Crystallization causes a strong increase of surface roughness compared to amorphous films. An increase of the interfacial layer thickness is observed after anneal at 600 degrees C, together with intermixing of bismuth with the substrate as shown by TEM-EDX. The band gap was determined to be similar to 3 eV from photoconductivity measurements and high dielectric constants between 30 and 130 were determined from capacitance voltage measurements, depending on the processing conditions. (C) 2012 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 2.446
DOI: 10.1016/j.materresbull.2012.01.001
|
|
|
“Structural phase transition at low temperature, corresponding to charge ordering in the CMR perovskites LN0.5A0.5MNO3”. Laffez P, Van Tendeloo G, Millange F, Caignaert V, Hervieu M, Raveau B, Materials research bulletin 31, 905 (1996). http://doi.org/10.1016/S0025-5408(96)00090-6
Abstract: The magneto resistive perovskites Nd0.5Sr0.5MnO3 and Pr0.5Sr0.41Ca0.09MnO3 undergo a transition from anti ferromagnetic insulator to ferromagnetic metal as function of temperature. The room temperature phase is orthorhombic with the space group Imma and the cell parameters a approximate to root 2a(p), b approximate to 2a(p), and c approximate to root 2a(p). A structural phase transition related to charge ordering accompanying the transition from ferromagnetic state to antiferromagnetic state has been evidenced by low temperature electron diffraction. This transition is reversible and a new superstructure, with a P-type orthorhombic cell. and lattice parameters parameters a approximate to 2 root 2a(p), b approximate to 2a(p), and c approximate to root 2a(p), is formed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.288
Times cited: 25
DOI: 10.1016/S0025-5408(96)00090-6
|
|
|
“Structure and magnetic properties of a new anion-deficient perovskite Pb2Ba2BiFe4ScO13 with crystallographic shear structure”. Batuk M, Tyablikov OA, Tsirlin AA, Kazakov SM, Rozova MG, Pokholok KV, Filimonov DS, Antipov EV, Abakumov AM, Hadermann J, Materials research bulletin 48, 3459 (2013). http://doi.org/10.1016/j.materresbull.2013.05.028
Abstract: Pb2Ba2BiFe4ScO13, a new n = 5 member of the oxygen-deficient perovskite-based A(n)B(n)O(3n-2) homologous series, was synthesized using a solid-state method. The crystal structure of Pb2Ba2BiFe4ScO13 was investigated by a combination of synchrotron X-ray powder diffraction, electron diffraction, high-angle annular dark-field scanning transmission electron microscopy and Mossbauer spectroscopy. At 900 K, it crystallizes in the Ammm space group with the unit cell parameters a = 5.8459(1) angstrom, b = 4.0426(1) angstrom, and c=27.3435(1) angstrom. In the Pb2Ba2BiFe4ScO13 structure, quasi-two-dimensional perovskite blocks are periodically interleaved with 1/2[1 1 0] ((1) over bar 0 1)(p) crystallographic shear (CS) planes. At the CS planes, the corner-sharing FeO6 octahedra are transformed into chains of edge-sharing FeO5 distorted tetragonal pyramids. B-positions of the perovskite blocks between the CS planes are jointly occupied by Fe3+ and Sc3+. The chains of the FeO5 pyramids and (Fe,Sc)O-6 octahedra delimit six-sided tunnels that are occupied by double columns of cations with a lone electron pair (Pb2+). The remaining A-cations (Bi3+, Ba2+) occupy positions in the perovskite block. According to the magnetic susceptibility measurements, Pb2Ba2BiFe4ScO13 is antiferromagnetically ordered below T-N approximate to 350 K. (C) 2013 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 2
DOI: 10.1016/j.materresbull.2013.05.028
|
|
|
“Structure of the hexagonal 16l perovskites Ba4Ca0.9Mn3.1O11.3 and Ba4Ca0.5Mn3Cu0.5O12-\delta by high-resolution electron microscopy”. Schuddinck W, Van Tendeloo G, Hervieu M, Floros N, Raveau B, Materials research bulletin 36, 2689 (2001). http://doi.org/10.1016/S0025-5408(01)00744-9
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 4
DOI: 10.1016/S0025-5408(01)00744-9
|
|
|
“TEM study of laser induced phase transition in iron thin films”. Teodorescu VS, Nistor LC, van Landuyt J, Dinescu M, Materials research bulletin 29, 63 (1994). http://doi.org/10.1016/0025-5408(94)90106-6
Abstract: Laser induced phase transition from b.c.c.(alpha) to f.c.c.(gamma) iron thin films is studied by high resolution TEM. The iron film has been covered on both sides with carbon layers to protect it against oxidation. Single pulse, tau FWHM = 20ns KrF (lambda = 248nm) excimer laser irradiation was performed in air with the film on the substrate. The laser pulse acts like a heat pulse followed by a rapid quenching revealing sequential aspects of the phase transition process. The presence of a fine mixture of the alpha + gamma phases between the alpha and gamma regions of the film has been interpreted as an incomplet transformation. The results are explained by assuming that the transformation took place via a phonon drag mechanism.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.288
Times cited: 2
DOI: 10.1016/0025-5408(94)90106-6
|
|
|
“:Ba2.1Bi0.9(O, F)6.8-\delta: a new ordered anion-excess fluorite”. Prituzhalov VA, Abakumov AM, Ardashnikova EI, Dolgikh VA, Van Tendeloo G, Materials research bulletin 42, 861 (2007). http://doi.org/10.1016/j.materresbull.2006.08.023
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 4
DOI: 10.1016/j.materresbull.2006.08.023
|
|
|
“Impact of tank construction on corrosion of ship ballast tanks”. de Baere K, Verstraelen H, Dewil R, Lemmens L, Lenaerts S, Nkunzimana T, Potters G, Materials performance 49, 48 (2010)
Keywords: A1 Journal article; Theory of quantum systems and complex systems; Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 0.149
|
|
|
“In situ study of ballast tank corrosion on ships: part 1”. Verstraelen H, de Baere K, Schillemans W, Lemmens L, Dewil R, Lenaerts S, Potters G, Materials performance 48, 48 (2009)
Keywords: A1 Journal article; Engineering sciences. Technology; Theory of quantum systems and complex systems; Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 0.149
|
|
|
“In situ study of ballast tank corrosion on ships: part 2”. Verstraelen H, de Baere K, Schillemans W, Lemmens L, Dewil R, Lenaerts S, Potters G, Materials performance 48, 54 (2009)
Abstract: A study was undertaken to determine causes and effects of corrosion processes in ballast tanks. Part 1 of this article (October 2009 MP) described the data collection. Part 2 describes the development of a corrosion index (CI) derived from the general International Association of Classification Societies corrosion assessment methods. The CI can be used in situ to assess ballast tank corrosion. An average timeline for-corrosion of tanks is presented.
Keywords: A1 Journal article; Engineering sciences. Technology; Theory of quantum systems and complex systems; Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 0.149
|
|
|
“Strength, toughness and aging stability of highly-translucent Y-TZP ceramics for dental restorations”. Zhang F, Inokoshi M, Batuk M, Hadermann J, Naert I, Van Meerbeek B, Vleugels J, Dental Materials 32, e327 (2016). http://doi.org/10.1016/j.dental.2016.09.025
Abstract: OBJECTIVE: The aim was to evaluate the optical properties, mechanical properties and aging stability of yttria-stabilized zirconia with different compositions, highlighting the influence of the alumina addition, Y2O3 content and La2O3 doping on the translucency. METHODS: Five different Y-TZP zirconia powders (3 commercially available and 2 experimentally modified) were sintered under the same conditions and characterized by X-ray diffraction with Rietveld analysis and scanning electron microscopy (SEM). Translucency (n=6/group) was measured with a color meter, allowing to calculate the translucency parameter (TP) and the contrast ratio (CR). Mechanical properties were appraised with four-point bending strength (n=10), single edge V-notched beam (SEVNB) fracture toughness (n=8) and Vickers hardness (n=10). The aging stability was evaluated by measuring the tetragonal to monoclinic transformation (n=3) after accelerated hydrothermal aging in steam at 134 degrees C, and the transformation curves were fitted by the Mehl-Avrami-Johnson (MAJ) equation. Data were analyzed by one-way ANOVA, followed by Tukey's HSD test (alpha=0.05). RESULTS: Lowering the alumina content below 0.25wt.% avoided the formation of alumina particles and therefore increased the translucency of 3Y-TZP ceramics, but the hydrothermal aging stability was reduced. A higher yttria content (5mol%) introduced about 50% cubic zirconia phase and gave rise to the most translucent and aging-resistant Y-TZP ceramics, but the fracture toughness and strength were considerably sacrificed. 0.2mol% La2O3 doping of 3Y-TZP tailored the grain boundary chemistry and significantly improved the aging resistance and translucency. Although the translucency improvement by La2O3 doping was less effective than for introducing a substantial amount of cubic zirconia, this strategy was able to maintain the mechanical properties of typical 3Y-TZP ceramics. SIGNIFICANCE: Three different approaches were compared to improve the translucency of 3Y-TZP ceramics.
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
Impact Factor: 4.07
DOI: 10.1016/j.dental.2016.09.025
|
|
|
“Strength, toughness and aging stability of highly-translucent Y-TZP ceramics for dental restorations”. Zhang F, Inokoshi M, Batuk M, Hadermann J, Naert I, Van Meerbeek B, Vleugels J, Dental materials 32, E327 (2016). http://doi.org/10.1016/J.DENTAL.7016.09.075
Abstract: Objective. The aim was to evaluate the optical properties, mechanical properties and aging stability of yttria-stabilized zirconia with different compositions, highlighting the influence of the alumina addition, Y2O3 content and La2O3 doping on the translucency. Methods. Five different Y-TZP zirconia powders (3 commercially available and 2 experimentally modified) were sintered under the same conditions and characterized by X-ray diffraction with Rietveld analysis and scanning electron microscopy (SEM). Translucency (n = 6/group) was measured with a color meter, allowing to calculate the translucency parameter (TP) and the contrast ratio (CR). Mechanical properties were appraised with four-point bending strength (n = 10), single edge V-notched beam (SEVNB) fracture toughness (n = 8) and Vickers hardness (n = 10). The aging stability was evaluated by measuring the tetragonal to monoclinic transformation (n = 3) after accelerated hydrothermal aging in steam at 134 degrees C, and the transformation curves were fitted by the Mehl-Avrami-Johnson (MAJ) equation. Data were analyzed by one-way ANOVA, followed by Tukey's HSD test (alpha = 0.05). Results. Lowering the alumina content below 0.25 wt.% avoided the formation of alumina particles and therefore increased the translucency of 3Y-TZP ceramics, but the hydrothermal aging stability was reduced. A higher yttria content (5 mol%) introduced about 50% cubic zirconia phase and gave rise to the most translucent and aging-resistant Y-TZP ceramics, but the fracture toughness and strength were considerably sacrificed. 0.2 mol% La2O3 doping of 3Y-TZP tailored the grain boundary chemistry and significantly improved the aging resistance and translucency. Although the translucency improvement by La2O3 doping was less effective than for introducing a substantial amount of cubic zirconia, this strategy was able to maintain the mechanical properties of typical 3Y-TZP ceramics. Significance. Three different approaches were compared to improve the translucency of 3YTZP ceramics. (C) 2016 The Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.07
Times cited: 47
DOI: 10.1016/J.DENTAL.7016.09.075
|
|
|
“Engineering hepatitis B virus core particles for targeting HER2 receptors in vitro and in vivo”. Suffian IFBM, Wang JT-W, Hodgins NO, Klippstein R, Garcia-Maya M, Brown P, Nishimura Y, Heidari H, Bals S, Sosabowski JK, Ogino C, Kondo A, Al-Jamal KT, Biomaterials 120, 126 (2017). http://doi.org/10.1016/J.BIOMATERIALS.2016.12.012
Abstract: Hepatitis B Virus core (HBc) particles have been studied for their potential as drug delivery vehicles for cancer therapy. HBc particles are hollow nano-particles of 30-34 nm diameter and 7 nm thick envelopes, consisting of 180-240 units of 21 kDa core monomers. They have the capacity to assemble/dis-assemble in a controlled manner allowing encapsulation of various drugs and other biomolecules. Moreover, other functional motifs, i.e. receptors, receptor binding sequences, peptides and proteins can be expressed. This study focuses on the development of genetically modified HBc particles to specifically recognise and target human epidermal growth factor receptor-2 (HER2)-expressing cancer cells, in vitro and in vivo, for future cancer therapy. The non-specific binding capacity of wild type HBc particles was reduced by genetic deletion of the sequence encoding arginine-rich domains. A specific HER2-targeting was achieved by expressing the ZHER2 affibodies on the HBc particles surface. In vitro studies showed specific uptake of ZHER2-AHBc particles in HER2 expressing cancer cells. In vivo studies confirmed positive uptake of ZHER2-ABBc particles in HER2-expressing tumours, compared to non-targeted AHBc particles in intraperitoneal tumour-bearing mice models. The present results highlight the potential of these nanocarriers in targeting HER2-positive metastatic abdominal cancer following intra-peritoneal administration. (C) 2016 The Authors. Published by Elsevier Ltd.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.402
Times cited: 20
DOI: 10.1016/J.BIOMATERIALS.2016.12.012
|
|
|
“The influence of surface oxides on the distribution and release of nickel from Nitinol wires”. Shabalovskaya SA, Tian H, Anderegg JW, Schryvers DU, Carroll WU, van Humbeeck J, Biomaterials 30, 468 (2009). http://doi.org/10.1016/j.biomaterials.2008.10.014
Abstract: The patterns of Ni release from Nitinol vary depending on the type of material (NiTi alloys with low or no processing versus commercial wires or sheets). A thick TiO2 layer generated on the wire surface during processing is often considered as a reliable barrier against Ni release. The present study of Nitinol wires with surface oxides resulting from production was conducted to identify the sources of Ni release and its distribution in the surface sublayers. The chemistry and topography of the surfaces of Nitinol wires drawn using different techniques were studied with XPS and SEM. The distribution of Ni into surface depth and the surface oxide thickness were evaluated using Auger spectroscopy, TEM with FIB and ELNES. Ni release was estimated using either ICPA or AAS. Potentiodynamic potential polarization of selected wires was performed in as-received state with no strain and in treated strained samples. Wire samples in the as-received state showed low breakdown potentials (200 mV); the improved corrosion resistance of these wires after treatment was not affected by strain. It is shown how processing techniques affect surface topography, chemistry and also Ni release. Nitinol wires with the thickest surface oxide TiO2 (up to 720 nm) showed the highest Ni release, attributed to the presence of particles of essentially pure Ni whose number and size increased while approaching the interface between the surface and the bulk. The biological implications of high and lasting Ni release are also discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.402
Times cited: 102
DOI: 10.1016/j.biomaterials.2008.10.014
|
|
|
“Stabilization of mercury-based superconductors by foreign cations”. Raveau B, Michel C, Hervieu M, Van Tendeloo G, Maignan A, Annales de chimie (1914)
T2 –, 4th North-African Materials Science Symposium (JMSM 94), NOV 23-24, 1994, CASABLANCA, MOROCCO 19, 487 (1994)
Abstract: The recently discovered superconducting mercury-based cuprates HgBa2Can-1CunO2n+2+delta have proved difficult to synthesize as single phases and are sensitive to environment (CO2, moisture). The present paper gives an overview of new series mercury based superconductors, whose stabilisation is based on the fact that a foreign cation with a higher valency than Hg(II) must be introduced in the mercury layers, in order to fill up partially the oxygen vacancies of these layers. By this method, several new series of superconductors involving strontium instead of barium with critical temperatures ranging from 27 K to 95 K have been isolated : Hg0.5Bi0.5Sr2-xLaxCuO4+delta, Hg(0.5)Bi(0.5)Sr(2)Ca(1-x)R(x)Cu(2)O(6+delta) (R Y, Nd, Pr), Pb0.7Hg0.3Sr2-xLaxCuO4+delta, Pb(0.7)Hg(0.3)Sr(2)Ca(1-x)R(x)Cu(2)O(6+delta) (R = Y, Nd) Hg(1-x)Pr(x)Sr(2)A(1-x')Pr(x') Cu2O6+delta (A = Sr, Ca), Pb0.7Hg0.3Sr2Cu2CO3O7 and Hg1-xCrxSr2CuO4+delta. The behaviour of the praseodymium cuprates that exhibit a rather sharp transition and reach a Tc of 85 K is especially discussed. A method to synthesize new ''Ba-Hg'' superconducting cuprates with the 1212 structure at normal pressure with a Tc up to 110 K is also presented.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 2
|
|
|
“Streaming-to-accumulation transition in a two-dimensional electron system in a polar semiconductor”. Wen X, Peeters FM, Devreese JT, Physical review : B : condensed matter and materials physics 46, 7571 (1992). http://doi.org/10.1103/PhysRevB.46.7571
Keywords: A1 Journal article; Condensed Matter Theory (CMT); Theory of quantum systems and complex systems
Impact Factor: 3.736
Times cited: 13
DOI: 10.1103/PhysRevB.46.7571
|
|
|
“Strong-coupling analysis of large bipolarons in two and three dimensions”. Verbist G, Smondyrev MA, Peeters FM, Devreese JT, Physical review : B : condensed matter and materials physics 45, 5262 (1992). http://doi.org/10.1103/PhysRevB.45.5262
Keywords: A1 Journal article; Condensed Matter Theory (CMT); Theory of quantum systems and complex systems
Impact Factor: 3.736
Times cited: 68
DOI: 10.1103/PhysRevB.45.5262
|
|
|
“Acoustical polarons and bipolarons in two dimensions”. Farias GA, da Costa WB, Peeters FM, Physical review : B : condensed matter and materials physics 54, 12835 (1996). http://doi.org/10.1103/PhysRevB.54.12835
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 3.736
Times cited: 30
DOI: 10.1103/PhysRevB.54.12835
|
|
|
“Anisotropic cluster model for the short-range order in Cu1-xPdx-type alloys”. De Meulenaere P, Rodewald M, Van Tendeloo G, Physical review : B : condensed matter and materials physics 57, 11132 (1998). http://doi.org/10.1103/PhysRevB.57.11132
Abstract: The split diffuse maxima around the {110} and {100} positions in the diffraction pattern of short-range-ordered Cu1-xPdx alloys (x=0.10...0.60) are attributed to small atomic clusters, being part of the underlying fee lattice. By analyzing the reciprocal space geometry, our cluster method identifies two prominent cluster types: the tetrahedron of nearest neighbors and a linear three-points cluster along the [110] directions. Since both cluster types contain different information on the same nearest-neighbor correlations, local anisotropy has to be assumed. It is shown that the three interatomic pair interactions within these basic clusters are sufficient to generate the spot splitting in the diffraction pattern. A ground-state analysis with these interactions reproduces the results of the anisotropic next-nearest-neighbor Ising model.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 1
DOI: 10.1103/PhysRevB.57.11132
|
|
|
“Asymptotic expansions in the path integral approach to the bipolaron problem”. Smondyrev MA, Devreese JT, Peeters FM, Physical review : B : condensed matter and materials physics 51, 15008 (1995). http://doi.org/10.1103/PhysRevB.51.15008
Keywords: A1 Journal article; Condensed Matter Theory (CMT); Theory of quantum systems and complex systems
Impact Factor: 3.736
Times cited: 32
DOI: 10.1103/PhysRevB.51.15008
|
|
|
“Bending martensite needles in Ni65Al35 investigated by two-dimensional elasticity and high-resolution transmission electron microscopy”. Boullay P, Schryvers D, Kohn RV, Physical review : B : condensed matter and materials physics 64, 144105 (2001). http://doi.org/10.1103/PhysRevB.64.144105
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 18
DOI: 10.1103/PhysRevB.64.144105
|
|
|
“Bright to dark exciton transition in symmetric coupled quantum wells”. Chang K, Peeters FM, Physical review : B : condensed matter and materials physics 63 (2001). http://doi.org/10.1103/PhysRevB.63.153307
Abstract: The energy dispersion of an exciton in a coupled quantum well is modified by an external in-plane magnetic field. We find that the in-plane magnetic field can shift the ground state of the magnetoexciton from a zero in-plane center-of-mass (CM) momentum to a finite CM momentum, and render the ground state of the magnetoexciton stable against radiative recombination due to momentum conservation. At the same time, a spatial separation of the electron and hole is realized. Thus an in-plane magnetic field can be used to tailor the radiative properties of excitons in coupled quantum wells.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 3.836
Times cited: 42
DOI: 10.1103/PhysRevB.63.153307
|
|
|
“Comparative Hall studies in the electron- and hole-doped manganites La0.33Ca0.67MnO3 and La0.70Ca0.30MnO3”. Gordon I, Wagner P, Das A, Vanacken J, Moshchalkov VV, Bruynseraede Y, Schuddinck W, Van Tendeloo G, Ziese M, Borghs G, Physical review : B : condensed matter and materials physics 62, 11633 (2000). http://doi.org/10.1103/PhysRevB.62.11633
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.836
Times cited: 18
DOI: 10.1103/PhysRevB.62.11633
|
|