“R-phase transition and related mechanical properties controlled by low-temperature aging treatment in a Ti50.8 at.% Ni thin wire”. Wang X, Li K, Schryvers D, Verlinden B, Van Humbeeck J, Scripta materialia 72-73, 21 (2014). http://doi.org/10.1016/j.scriptamat.2013.10.006
Abstract: A cold-drawn Ti50.8 at.% Ni wire was annealed at 600 °C for 30 min, followed by aging at 250 °C for different times. A microstructure with small grains and nanoscaled precipitates was obtained. The thermally induced martensite transformation is suppressed in the samples aged for 4 h or longer, leaving a one-stage R-phase transition between −150 and +150 °C. The transformation behavior, work output and recovery stress associated with the R-phase transition are presented.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 27
DOI: 10.1016/j.scriptamat.2013.10.006
|
“Stability and structures of the \epsilon-phases of iron nitrides and iron carbides from first principles”. Fang CM, van Huis MA, Zandbergen HW, Scripta materialia 64, 296 (2011). http://doi.org/10.1016/j.scriptamat.2010.08.048
Abstract: First-principles calculations were performed for the ε-phases and other iron carbides/nitrides with hexagonal close-packed Fe sublattices. Although these nitrides/carbides have similar crystal structures, they exhibit different chemical and physical properties. Relative to α-Fe, graphite and N2, all the ε-type nitrides are stable, while all the carbides are metastable. The lattice parameters of the ε-iron nitrides vary differently from those of the ε-carbides, as a function of the concentration of X (Xdouble bond; length as m-dashN, C). The structural relationships of ε-Fe2X with η-Fe2X and ζ-Fe2X are discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 29
DOI: 10.1016/j.scriptamat.2010.08.048
|
“Structure and formation mechanism of rolled-in oxide areas on aluminum lithographic printing sheets”. Tzedaki G, M, Turner S, Godet S, De Graeve I, Kernig B, Hasenclever J, Terryn H, Scripta materialia 68, 233 (2013). http://doi.org/10.1016/j.scriptamat.2012.10.021
Abstract: The subsurface area introduced during rolling on the 1100 aluminum alloy series alters its surface properties, which makes it more susceptible to corrosion. A combination of different transmission electron microscopy techniques is employed to observe the orientation of small grain structures and the distribution elements in the subsurface layer. This approach provided valuable insight into the formation mechanism of the layer and the phenomena taking place during rolling.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 6
DOI: 10.1016/j.scriptamat.2012.10.021
|
“Structure and stability of Fe2 phases from density-functional theory calculations”. Fang CM, van Huis MA, Zandbergen HW, Scripta materialia 63, 418 (2010). http://doi.org/10.1016/j.scriptamat.2010.04.042
Abstract: Fe(2)C plays a crucial role in the precipitation of iron carbides. Jack's structural models for epsilon-Fe(2)C, and non-stoichiometric epsilon-Fe(2.4)C, are analyzed using first-principles calculations. Several new configurations of epsilon-Fe(2)C with even higher stability are found. We show how epsilon-Fe(2)C transforms into eta-Fe(2)C, and address the structural relationships with the chi-Fe(5)C(2), theta-Fe(3)C and Fe(7)C(3) phases. The relative occurrence of these phases in steel, as well as their probable evolution during tempering of quenched steels, is discussed. (C) 2010 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 32
DOI: 10.1016/j.scriptamat.2010.04.042
|
“Texture-dependent twin formation in nanocrystalline thin Pd films”. Wang B, Idrissi H, Shi H, Colla MS, Michotte S, Raskin JP, Pardoen T, Schryvers D, Scripta materialia 66, 866 (2012). http://doi.org/10.1016/j.scriptamat.2012.01.038
Abstract: Nanocrystalline Pd films were produced by electron-beam evaporation and sputter deposition. The electron-beam-evaporated films reveal randomly oriented nanograins with a relatively high density of growth twins, unexpected in view of the high stacking fault energy of Pd. In contrast, sputter-deposited films show a clear 〈1 1 1〉 crystallographic textured nanostructure without twins. These results provide insightful information to guide the generation of microstructures with enhanced strength/ductility balance in high stacking fault energy nanocrystalline metallic thin films.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 19
DOI: 10.1016/j.scriptamat.2012.01.038
|
“Transmission electron microscopy investigation of microstructures in low-hysteresis alloys with special lattice parameters”. Delville R, Schryvers D, Zhang Z, James RD, Scripta materialia 60, 293 (2009). http://doi.org/10.1016/j.scriptamat.2008.10.025
Abstract: A sharp drop in hysteresis is observed for shape memory alloys satisfying the compatibility condition between austenite and martensite, i.e. ë2 = 1, where ë2 is the middle eigenvalue of the transformation strain matrix. The present work investigates the evolution of microstructure by transmission electron microscopy as the composition of the Ti50Ni50−xPdx system is systemically tuned to achieve the condition ë2 = 1. Changes in morphology, twinning density and twinning modes are reported along with twinless martensite and exact austenitemartensite interfaces.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 56
DOI: 10.1016/j.scriptamat.2008.10.025
|
“Highly-translucent, strong and aging-resistant 3Y-TZP ceramics for dental restoration by grain boundary segregation”. Zhang F, Vanmeensel K, Batuk M, Hadermann J, Inokoshi M, Van Meerbeek B, Naert I, Vleugels J, Acta biomaterialia 16, 215 (2015). http://doi.org/10.1016/j.actbio.2015.01.037
Abstract: Latest trends in dental restorative ceramics involve the development of full-contour 3Y-TZP ceramics which can avoid chipping of veneering porcelains. Among the challenges are the low translucency and the hydrothermal stability of 3Y-TZP ceramics. In this work, different trivalent oxides (Al2O3, Sc2O3, Nd2O3 and La2O3) were selected to dope 3Y-TZP ceramics. Results show that dopant segregation was a key factor to design hydrothermally stable and high-translucent 3Y-TZP ceramics and the cation dopant radius could be used as a controlling parameter. A large trivalent dopant, oversized as compared to Zr4+, exhibiting strong segregation at the ZrO2 grain boundary was preferred. The introduction of 0.2 mol% La2O3 in conventional 0.10.25 wt.% Al2O3-doped 3Y-TZP resulted in an excellent combination of high translucency and superior hydrothermal stability, while retaining excellent mechanical properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 54
DOI: 10.1016/j.actbio.2015.01.037
|
“Stability of Ni in nitinol oxide surfaces”. Tian H, Schryvers D, Liu D, Jiang Q, van Humbeeck J, Acta biomaterialia 7, 892 (2011). http://doi.org/10.1016/j.actbio.2010.09.009
Abstract: The stability of Ni in titanium oxide surface layers on nitinol wires known to release certain amounts of Ni was investigated by first principles density functional theory and transmission electron microscopy. The oxides were identified as a combination of TiO and TiO2 depending on the thickness of the layer. The calculations indicate that free Ni atoms can exist in TiO at ambient temperature while Ni particles form in TiO2, which was confirmed by the transmission electron microscopy observations. The results are discussed with respect to surface stability and Ni release due to free Ni atoms and Ni particles.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
Times cited: 39
DOI: 10.1016/j.actbio.2010.09.009
|
“On the nucleation mechanism of {112} <, 111 >, mechanical twins in as-quenched beta metastable Ti-12 wt.% Mo alloy”. Marteleur M, Idrissi H, Amin-Ahmadi B, Prima F, Schryvers D, Jacques PJ, Materialia 7, Unsp 100418 (2019). http://doi.org/10.1016/J.MTLA.2019.100418
Abstract: Recently developed beta-metastable Ti grades take advantage of the simultaneous activation of TRIP and TWIP effects for enhancing their work hardening rate. However, the role of each plasticity mechanism on the macroscopic mechanical response is still unclear. In this work, the nucleation mechanism of the first activated plasticity mechanism, namely {112} < 111 > twinning, was investigated. Firstly, post-mortem TEM analysis showed that twins nucleate on pre-existing microstructural defects such as thermal jogs with the zonal dislocation mechanism. The precipitation of the omega phase on twin boundaries has been observed, as well as the emission of numerous dislocations from super-jogs present in these twin boundaries. It is also shown that {112} < 111 > twins act as effective dislocation sources for the subsequent plasticity mechanisms such as beta -> alpha '' martensitic transformation and {332} < 111 > twinning. Secondly, in situ TEM tensile testing of the investigated Ti grade highlighted the primary role of the initial defect configuration present in the microstructure. It is shown that twins cannot nucleate without the presence of specific defects allowing the triggering of the dislocation decomposition needed for the twinning mechanism highlighted in investigated bulk samples.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1016/J.MTLA.2019.100418
|
“Towards ductilization of high strength 7XXX aluminium alloys via microstructural modifications obtained by friction stir processing and heat treatments”. Lezaack MB, Hannard F, Zhao L, Orekhov A, Adrien J, Miettinen A, Idrissi H, Simar A, Materialia 20, 101248 (2021). http://doi.org/10.1016/J.MTLA.2021.101248
Abstract: High strength 7XXX aluminium series reach exceptional strength, higher than all other industrial aluminium alloys. However, they suffer from a lack of ductility compared to softer series. This work presents a procedure to improve the ductility of 7475 Al alloy in high strength condition, reaching a true fracture strain of 70% at full 500 MPa T6 yield strength. Using friction stir processing (FSP) and post-FSP heat treatments, 100% of industrial rolled material T6 yield stress is maintained but a 180% increase in fracture strain is measured for the processed material. This ductility improvement is studied by in-situ synchrotron X-ray tomography and is explained by the reduction of intermetallic particles size and the homogenization of their spatial distribution. Furthermore, the microstructure after FSP shows equiaxed refined grains which favour crack deviation as opposed to large cracks parallel to the elongated coarse grains in rolled plate. These results are paving the way to better formability and crashworthiness of 7XXX alloys.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
DOI: 10.1016/J.MTLA.2021.101248
|