Abstract: The limitations of the loading of the porous metalorganic framework [Zn4O(bdc)3] (bdc = benzene-1,4-dicarboxylate; MOF-5 or IRMOF-1) with Pd nanoparticles was investigated. First, the volatile organometallic precursor [Pd(5-C5H5)(3-C3H5)] was employed to get the inclusion compound [Pd(5-C5H5)(3-C3H5)]x@MOF-5 via gas-phase infiltration at 10-3 mbar. A loading of four molecules of [Pd(5-C5H5)(3-C3H5)] per formula unit of MOF-5 (x = 4) can be reached (35 wt.% Pd). Second, the metalorganic precursor [Pd(acac)2] (acac = 2,4-pentanedionate) was used and the inclusion materials [Pd(acac)2]x@MOF-5 of different Pd loadings were obtained by incipient wetness infiltration. However, the maximum loading was lower as compared with the former case with about two precursor molecules per formula unit of MOF-5. Both loading routes are suitable for the synthesis of Pd nanoparticles inside the porous host matrix. Homogeneously distributed nanoparticles with diameter of 2.4(±0.2) nm can be achieved by photolysis of the inclusion compounds [Pd(5-C5H5)(3-C3H5)]x@MOF-5 (x 4), while the hydrogenolysis of [Pd(acac)2]x@MOF-5 (x 2) leads to a mixture of small particles inside the network (< 3 nm) and large Pd agglomerates (40 nm) on the outer surface of the MOF-5 specimens. The pure Pdx@MOF-5 materials proved to be stable under hydrogen pressure (2 bar) at 150 °C over many hours. Neither hydrogenation of the bdc linkers nor particle growth was observed. The new composite materials were characterized by 1H/13C-MAS-NMR, powder XRD, ICP-AES, FT-IR, N2 sorption measurements and high resolution TEM. Raising the Pd loading of a representative sample Pd4@MOF-5 (35 wt.% Pd) by using [Pd(5-C5H5)(3-C3H5)] as precursor in a second cycle of gas-phase infiltration and photolysis was accompanied by the collapse of the long-range crystalline order of the MOF.

Abstract: Successful encapsulation of polyoxometalate (POM) within the framework of a mesoporous iron trimesate MIL-100(Fe) sample has been achieved by direct hydrothermal synthesis in the absence of fluorine. XRPD, 31P MAS NMR, IR, EELS, TEM and 57Fe Mössbauer spectrometry corroborate the insertion of POM within the cavities of the MOF. The experimental Mo/Fe ratio is 0.95, in agreement with the maximum theoretical amount of POM loaded within the pores of MIL-100(Fe), based on steric hindrance considerations. The POM-MIL-100(Fe) sample exhibits a pore volume of 0.373 cm3 g−1 and a BET surface area close to 1000 m2 g−1, indicating that small gas molecules can easily diffuse inside the cavities despite the presence of heavy phosphomolybdates. These latter contribute to the decrease in the overall surface area, due to the increase in molar weight, by 65%. Moreover, the resulting Keggin containing MIL-100(Fe) solid is stable in aqueous solution with no POM leaching even after more than 2 months. In addition, no exchange of the Keggin anions by tetrabutylammonium perchlorate in organic media has been observed.

Abstract: The synthesis, electron diffraction (ED), synchrotron X-ray and neutron structure, X-ray absorption spectroscopy (XAS) and magnetic property studies of La2MnVO6 double perovskite are described. Analysis of the synchrotron powder X-ray diffraction data for La2MnVO6 indicates a disordered arrangement of Mn and V at the B-site of the perovskite structure. Absence of super-lattice reflections in the ED patterns for La2MnVO6 supports the disordered cation arrangement. Room temperature time-of-flight (TOF) neutron powder diffraction (NPD) data show no evidence of cation ordering, in corroboration with the ED and synchrotron studies (orthorhombic Pnma, a = 5.6097(3), b = 7.8837(5) and c = 5.5668(3) ; 295 K, NPD). A comparison of XAS analyses of La2TVO6 with T = Ni and Co shows T2+ formal oxidation state while the T = Mn material evidences a Mn3+ admixture into a dominantly Mn2+ ground state. V-K edge measurements manifest a mirror image behavior with a V4+ state for T = Ni and Co with a V3+ admixture arising in the T = Mn material. The magnetic susceptibility data for La2MnVO6 show ferromagnetic correlations; the observed effective moment, µeff (5.72 µB) is much smaller than the calculated moment (6.16 µB) based on the spin-only formula for Mn2+ (d5, HS) /V4+ (d1), supportive of the partly oxidized Mn and reduced V scenario (Mn3+/V3+).

Abstract: The microporous and activated zeolitic imidazolate framework (Zn(MeIM)2; MeIM = imidazolate-2-methyl; ZIF-8) was loaded with the MOCVD precursor diethyl zinc [Zn(C2H5)2]. Exposure of ZIF-8 to the vapour of the volatile organometallic molecule resulted in the formation of the inclusion compound [Zn(C2H5)2]0.38@ZIF-8 revealing two precursor molecules per cavity. In a second step the obtained material was treated with oxygen (5 vol% in argon) at various temperatures (oxidative annealing) to achieve the composite material ZnO0.35@ZIF-8. The new material was characterized with powder XRD, FT-IR, UV-vis, solid state NMR, elemental analysis, N2 sorption measurements, and transmission electron microscopy. The data give evidence for the presence of nano-sized ZnO particles stabilized by ZIF-8 showing a blue-shift of the UV-vis absorption caused by quantum size effect (QSE). The surface structure and reactivity of embedded ZnO nanoparticles were characterized via carbon dioxide adsorption at different temperatures monitored by ultra-high vacuum FTIR techniques. It was found that the surface of ZnO nanoparticles is dominated by polar OZnO and ZnZnO facets as well as by defect sites, which all exhibit high reactivity towards CO2 activation forming various adsorbed carbonate and chemisorbed CO2δ− species.

Abstract: The giant cationic palladium clusters, approximate formula Pd561L60(OAc)180 (L = Dipy, Phen), were characterized by electron diffraction and high resolution microscopy to contain an FCC metal core, most of the larger Pd particles (8 nm) exhibiting multiple twinning, evidence for a distorted icosahedral structure.

Abstract: The one-step preparation of capped PbS nanoparticles in an inorganic matrix via UV-induced decomposition of lead thiosulfate complexes intercalated into a hydrotalcite-type layered double hydroxide is reported.

Abstract: In the light of global warming, renewables such as solar photovoltaics (PV) are important to decrease greenhouse gas emissions. An important issue regarding implementation of solar panels on large scale, is the limited available area. Therefore, it can be interesting to combine PV with alternative applications, as a ways of not requiring “additional” space. One example is a photovoltaic noise barrier (PVNB), where a noise barrier located along a highway or railway is used as substructure for PV modules. Even though a PVNB is not a novel concept, the absence of economic assessments in literature can be a barrier to their wider implementation. In this paper, a feasibility study of a PVNB in Belgium is conducted, using a cost benefit analysis including a Monte Carlo sensitivity analysis. Besides purely economic aspects, also ecological benefits are monetized. The sensitivity analysis indicates that the ecological benefit of noise reduction, which is valuated using a noise sensitivity depreciation index applied to real estate prices, is of major importance in determining the net present value of the case study. On the contrary, the impact of reducing CO2 emissions seems to be negligible when expressed in monetary terms. The results suggest that the PVNB as a whole and also its separate components -.e. the PV array and the noise barrier can be profitable projects, when ecological benefits are included. (C) 2012 Elsevier Ltd. All rights reserved.

Abstract: Three-dimensional (3D) computational fluid dynamics (CFD) simulations were performed to study solids flow dynamics and solids back-mixing behavior in a screw reactor (designed for thermal conversion of dry biomass particles) based on the Eulerian-Eulerian method. Simulation results were compared against experimental data with respect to filling degree and mean residence time of particles. The mean deviations for filling degree and for mean residence time between simulation and experiment were about 0.01 and 11.4 s, respectively, which shows that the model is reasonably accurate in predicting solids flow behavior in the screw reactor. The solids flow dynamics inside the reactor were discussed. The solids residence time distribution (RTD) was calculated and the degree of solids back-mixing in the forward transportation direction of the reactor was analyzed. It was found that solids being flung over the shaft and solids back-leakage, resulting from the low solids forward transportation velocity at the clearance between the flight and the bottom shell of the screw reactor, were responsible for solids back-mixing. The degree of solids back-mixing can be reduced at higher screw rotating speeds when keeping inlet mass flow rate of solids constant. (C) 2019 Elsevier Ltd. All rights reserved.