“Near-Infrared-Emitting CuInS2/ZnS Dot-in-Rod Colloidal Heteronanorods by Seeded Growth”. Xia C, Winckelmans N, Prins PT, Bals S, Gerritsen HC, de Mello Donegá, C, Journal of the American Chemical Society 140, 5755 (2018). http://doi.org/10.1021/jacs.8b01412
Abstract: Synthesis protocols for anisotropic CuInX2 (X = S, Se, Te)-based heteronanocrystals (HNCs) are scarce due to the difficulty in balancing the reactivities of multiple precursors and the high solid-state diffusion rates of the cations involved in the CuInX2 lattice. In this work, we report a multistep seeded growth synthesis protocol that yields colloidal wurtzite CuInS2/ZnS dot core/rod shell HNCs with photoluminescence in the NIR (∼800 nm). The wurtzite CuInS2 NCs used as seeds are obtained by topotactic partial Cu+ for In3+ cation exchange in template Cu2–xS NCs. The seed NCs are injected in a hot solution of zinc oleate and hexadecylamine in octadecene, 20 s after the injection of sulfur in octadecene. This results in heteroepitaxial growth of wurtzite ZnS primarily on the Sulfur-terminated polar facet of the CuInS2 seed NCs, the other facets being overcoated only by a thin (∼1 monolayer) shell. The fast (∼21 nm/min) asymmetric axial growth of the nanorod proceeds by addition of [ZnS] monomer units, so that the polarity of the terminal (002) facet is preserved throughout the growth. The delayed injection of the CuInS2 seed NCs is crucial to allow the concentration of [ZnS] monomers to build up, thereby maximizing the anisotropic heteroepitaxial growth rates while minimizing the rates of competing processes (etching, cation exchange, alloying). Nevertheless, a mild etching still occurred, likely prior to the onset of heteroepitaxial overgrowth, shrinking the core size from 5.5 to ∼4 nm. The insights provided by this work open up new possibilities in designing multifunctional Cu-chalcogenide based colloidal heteronanocrystals.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 43
DOI: 10.1021/jacs.8b01412
|
“Nanocrystals of lead chalcohalides : a series of kinetically trapped metastable nanostructures”. Toso S, Akkerman QA, Martin-Garcia B, Prato M, Zito J, Infante I, Dang Z, Moliterni A, Giannini C, Bladt E, Lobato I, Ramade J, Bals S, Buha J, Spirito D, Mugnaioli E, Gemmi M, Manna L, Journal Of The American Chemical Society 142, 10198 (2020). http://doi.org/10.1021/JACS.0C03577
Abstract: We report the colloidal synthesis of a series of surfactant-stabilized lead chalcohalide nanocrystals. Our work is mainly focused on Pb4S3Br2, a chalcohalide phase unknown to date that does not belong to the ambient-pressure PbS-PbBr2 phase diagram. The Pb4S3Br2 nanocrystals herein feature a remarkably narrow size distribution (with a size dispersion as low as 5%), a good size tunability (from 7 to similar to 30 nm), an indirect bandgap, photoconductivity (responsivity = 4 +/- 1 mA/W), and stability for months in air. A crystal structure is proposed for this new material by combining the information from 3D electron diffraction and electron tomography of a single nanocrystal, X-ray powder diffraction, and density functional theory calculations. Such a structure is closely related to that of the recently discovered high-pressure chalcohalide Pb4S3I2 phase, and indeed we were able to extend our synthesis scheme to Pb4S3I2 colloidal nanocrystals, whose structure matches the one that has been published for the bulk. Finally, we could also prepare nanocrystals of Pb3S2Cl2, which proved to be a structural analogue of the recently reported bulk Pb3Se2Br2 phase. It is remarkable that one high-pressure structure (for Pb4S3I2) and two metastable structures that had not yet been reported (for Pb4S3Br2 and Pb3S2Cl2) can be prepared on the nanoscale by wet-chemical approaches. This highlights the important role of colloidal chemistry in the discovery of new materials and motivates further exploration into metal chalcohalide nanocrystals.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 15
Times cited: 32
DOI: 10.1021/JACS.0C03577
|
“Universal a-cation splitting in LiNbO₃-type structure driven by intrapositional multivalent coupling”. Han Y, Zeng Y, Hendrickx M, Hadermann J, Stephens PW, Zhu C, Grams CP, Hemberger J, Frank C, Li S, Wu MX, Retuerto M, Croft M, Walker D, Yao D-X, Greenblatt M, Li M-R, Journal Of The American Chemical Society 142, 7168 (2020). http://doi.org/10.1021/JACS.0C01814
Abstract: Understanding the electric dipole switching in multiferroic materials requires deep insight of the atomic-scale local structure evolution to reveal the ferroelectric mechanism, which remains unclear and lacks a solid experimental indicator in high-pressure prepared LiNbO3-type polar magnets. Here, we report the discovery of Zn-ion splitting in LiNbO3-type Zn2FeNbO6 established by multiple diffraction techniques. The coexistence of a high-temperature paraelectric-like phase in the polar Zn2FeNbO6 lattice motivated us to revisit other high-pressure prepared LiNbO3-type A(2)BB'O-6 compounds. The A-site atomic splitting (similar to 1.0-1.2 angstrom between the split-atom pair) in B/B'-mixed Zn2FeTaO6 and O/N-mixed ZnTaO2N is verified by both powder X-ray diffraction structural refinements and high angle annular dark field scanning transmission electron microscopy images, but is absent in single-B-site ZnSnO3. Theoretical calculations are in good agreement with experimental results and suggest that this kind of A-site splitting also exists in the B-site mixed Mn-analogues, Mn2FeMO6 (M = Nb, Ta) and anion-mixed MnTaO2N, where the smaller A-site splitting (similar to 0.2 angstrom atomic displacement) is attributed to magnetic interactions and bonding between A and B cations. These findings reveal universal A-site splitting in LiNbO3-type structures with mixed multivalent B/B', or anionic sites, and the splitting-atomic displacement can be strongly suppressed by magnetic interactions and/or hybridization of valence bands between d electrons of the A- and B-site cations.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 15
Times cited: 1
DOI: 10.1021/JACS.0C01814
|
“Halide perovskite-lead chalcohalide nanocrystal heterostructures”. Imran M, Peng L, Pianetti A, Pinchetti V, Ramade J, Zito J, Di Stasio F, Buha J, Toso S, Song J, Infante I, Bals S, Brovelli S, Manna L, Journal Of The American Chemical Society 143, 1435 (2021). http://doi.org/10.1021/JACS.0C10916
Abstract: We report the synthesis of colloidal CsPbX3-Pb4S3Br2 (X = Cl, Br, I) nanocrystal heterostructures, providing an example of a sharp and atomically resolved epitaxial interface between a metal halide perovskite and a non-perovskite lattice. The CsPbBr3-Pb4S3Br2 nanocrystals are prepared by a two-step direct synthesis using preformed subnanometer CsPbBr3 clusters. Density functional theory calculations indicate the creation of a quasi-type II alignment at the heterointerface as well as the formation of localized trap states, promoting ultrafast separation of photogenerated excitons and carrier trapping, as confirmed by spectroscopic experiments. Postsynthesis reaction with either Cl- or I- ions delivers the corresponding CsPbCI3-Pb4S3Br2 and CsPbI3-Pb4S3Br2 heterostructures, thus enabling anion exchange only in the perovskite domain. An increased structural rigidity is conferred to the perovskite lattice when it is interfaced with the chalcohalide lattice. This is attested by the improved stability of the metastable gamma phase (or “black” phase) of CsPbI3 in the CsPbI3-Pb4S3Br2 heterostructure.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 54
DOI: 10.1021/JACS.0C10916
|
“Topochemical deintercalation of Li from layered LiNiB : toward 2D MBene”. Bhaskar G, Gvozdetskyi V, Batuk M, Wiaderek KM, Sun Y, Wang R, Zhang C, Carnahan SL, Wu X, Ribeiro RA, Bud'ko SL, Canfield PC, Huang W, Rossini AJ, Wang C-Z, Ho K-M, Hadermann J, Zaikina J V, Journal Of The American Chemical Society 143, 4213 (2021). http://doi.org/10.1021/JACS.0C11397
Abstract: The pursuit of two-dimensional (2D) borides, MBenes, has proven to be challenging, not the least because of the lack of a suitable precursor prone to the deintercalation. Here, we studied room-temperature topochemical deintercalation of lithium from the layered polymorphs of the LiNiB compound with a considerable amount of Li stored in between [NiB] layers (33 at. % Li). Deintercalation of Li leads to novel metastable borides (Li similar to 0.5NiB) with unique crystal structures. Partial removal of Li is accomplished by exposing the parent phases to air, water, or dilute HCl under ambient conditions. Scanning transmission electron microscopy and solid-state Li-7 and B-1(1) NMR spectroscopy, combined with X-ray pair distribution function (PDF) analysis and DFT calculations, were utilized to elucidate the novel structures of (Li similar to 0.5NiB) and the mechanism of Li-deintercalation. We have shown that the deintercalation of Li proceeds via a “zip-lock” mechanism, leading to the condensation of single [NiB] layers into double or triple layers bound via covalent bonds, resulting in structural fragments with Li[NiB](2) and Li[NiB](3) compositions. The crystal structure of Li similar to 0.5NiB is best described as an intergrowth of the ordered single [NiB], double [NiB](2), or triple [NiB](3) layers alternating with single Li layers; this explains its structural complexity. The formation of double or triple [NiB] layers induces a change in the magnetic behavior from temperature-independent paramagnets in the parent LiNiB compounds to the spin-glassiness in the deintercalated Li similar to 0.5NiB counterparts. LiNiB compounds showcase the potential to access a plethora of unique materials, including 2D MBenes (NiB).
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
DOI: 10.1021/JACS.0C11397
|
“Creation of Exclusive Artificial Cluster Defects by Selective Metal Removal in the (Zn, Zr) Mixed-Metal UiO-66”. Feng X, Jena HS, Krishnaraj C, Arenas-Esteban D, Leus K, Wang G, Sun J, Rüscher M, Timoshenko J, Roldan Cuenya B, Bals S, Voort PVD, Journal Of The American Chemical Society , jacs.1c05357 (2021). http://doi.org/10.1021/jacs.1c05357
Abstract: The differentiation between missing linker defects
and missing cluster defects in MOFs is difficult, thereby limiting the
ability to correlate materials properties to a specific type of defects.
Herein, we present a novel and easy synthesis strategy for the
creation of solely “missing cluster defects” by preparing mixed-metal
(Zn, Zr)-UiO-66 followed by a gentle acid wash to remove the Zn
nodes. The resulting material has the reo UiO-66 structure, typical
for well-defined missing cluster defects. The missing clusters are
thoroughly characterized, including low-pressure Ar-sorption, iDPCSTEM
at a low dose (1.5 pA), and XANES/EXAFS analysis. We
show that the missing cluster UiO-66 has a negligible number of missing linkers. We show the performance of the missing cluster
UiO-66 in CO2 sorption and heterogeneous catalysis.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
Times cited: 29
DOI: 10.1021/jacs.1c05357
|
“Emergence of coupled rotor dynamics in metal-organic frameworks via tuned steric interactions”. Gonzalez-Nelson A, Mula S, Simenas M, Balciunas S, Altenhof AR, Vojvodin CS, Canossa S, Banys J, Schurko RW, Coudert F-X, van der Veen MA, Journal Of The American Chemical Society 143, 12053 (2021). http://doi.org/10.1021/JACS.1C03630
Abstract: The organic components in metal-organic frameworks (MOFs) are unique: they are embedded in a crystalline lattice, yet, as they are separated from each other by tunable free space, a large variety of dynamic behavior can emerge. These rotational dynamics of the organic linkers are especially important due to their influence over properties such as gas adsorption and kinetics of guest release. To fully exploit linker rotation, such as in the form of molecular machines, it is necessary to engineer correlated linker dynamics to achieve their cooperative functional motion. Here, we show that for MIL-53, a topology with closely spaced rotors, the phenylene functionalization allows researchers to tune the rotors' steric environment, shifting linker rotation from completely static to rapid motions at frequencies above 100 MHz. For steric interactions that start to inhibit independent rotor motion, we identify for the first time the emergence of coupled rotation modes in linker dynamics. These findings pave the way for function-specific engineering of gear-like cooperative motion in MOFs.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 13.858
DOI: 10.1021/JACS.1C03630
|
“Heterometallic molecular complexes act as messenger building units to encode desired metal-atom combinations to multivariate metal-organic frameworks”. Lopez-Garcia C, Canossa S, Hadermann J, Gorni G, Oropeza FE, de la Pena O'Shea VA, Iglesias M, Monge MA, Gutierrez-Puebla E, Gandara F, Journal of the American Chemical Society 144, 16262 (2022). http://doi.org/10.1021/JACS.2C06142
Abstract: A novel synthetic approach is described for the targeted preparation of multivariate metal-organic frameworks (MTV-MOFs) with specific combinations of metal elements. This methodology is based on the use of molecular complexes that already comprise desired metal-atom combinations, as building units for the MTV-MOF synthesis. These units are transformed into the MOF structural constituents through a ligand/linker exchange process that involves structural modifications while preserving their origina l l y encoded atomic combination. Thus, through the use of heterometalli c ring-shaped molecules combining gallium and nickel or cobalt, we have obtained MOFs with identical combinations of the metal elements, now incorporated in the rod-shaped secondary building unit, as confirmed with a combination of X-ray and electron diffraction, electron microscopy, and X-ray absorption spectroscopy techniques.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 15
DOI: 10.1021/JACS.2C06142
|
“An atomically dispersed Mn-photocatalyst for generating hydrogen peroxide from seawater via the Water Oxidation Reaction (WOR)”. Ren P, Zhang T, Jain N, Ching HYV, Jaworski A, Barcaro G, Monti S, Silvestre-Albero J, Celorrio V, Chouhan L, Rokicinska A, Debroye E, Kustrowski P, Van Doorslaer S, Van Aert S, Bals S, Das S, Journal of the American Chemical Society 145, 16584 (2023). http://doi.org/10.1021/JACS.3C03785
Abstract: In this work, we have fabricatedan aryl amino-substitutedgraphiticcarbon nitride (g-C3N4) catalyst with atomicallydispersed Mn capable of generating hydrogen peroxide (H2O2) directly from seawater. This new catalyst exhibitedexcellent reactivity, obtaining up to 2230 & mu;M H2O2 in 7 h from alkaline water and up to 1800 & mu;Mfrom seawater under identical conditions. More importantly, the catalystwas quickly recovered for subsequent reuse without appreciable lossin performance. Interestingly, unlike the usual two-electron oxygenreduction reaction pathway, the generation of H2O2 was through a less common two-electron water oxidation reaction(WOR) process in which both the direct and indirect WOR processesoccurred; namely, photoinduced h(+) directly oxidized H2O to H2O2 via a one-step 2e(-) WOR, and photoinduced h(+) first oxidized a hydroxide (OH-) ion to generate a hydroxy radical ((OH)-O-& BULL;), and H2O2 was formed indirectly by thecombination of two (OH)-O-& BULL;. We have characterized thematerial, at the catalytic sites, at the atomic level using electronparamagnetic resonance, X-ray absorption near edge structure, extendedX-ray absorption fine structure, high-resolution transmission electronmicroscopy, X-ray photoelectron spectroscopy, magic-angle spinningsolid-state NMR spectroscopy, and multiscale molecular modeling, combiningclassical reactive molecular dynamics simulations and quantum chemistrycalculations.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Organic synthesis (ORSY); Theory and Spectroscopy of Molecules and Materials (TSM²)
Impact Factor: 15
Times cited: 21
DOI: 10.1021/JACS.3C03785
|
“Two-dimensional halide Pb-perovskite-double perovskite epitaxial heterostructures”. Singh A, Yuan B, Rahman MH, Yang H, De A, Park JY, Zhang S, Huang L, Mannodi-Kanakkithodi A, Pennycook TJ, Dou L, Journal of the American Chemical Society 145, 19885 (2023). http://doi.org/10.1021/JACS.3C06127
Abstract: Epitaxial heterostructures of two-dimensional (2D) halide perovskites offer a new platform for studying intriguing structural, optical, and electronic properties. However, difficulties with the stability of Pb- and Sn-based heterostructures have repeatedly slowed the progress. Recently, Pb-free halide double perovskites are gaining a lot of attention due to their superior stability and greater chemical diversity, but they have not been successfully incorporated into epitaxial heterostructures for further investigation. Here, we report epitaxial core-shell heterostructures via growing Pb-free double perovskites (involving combinations of Ag(I)-Bi(III), Ag-Sb, Ag-In, Na-Bi, Na-Sb, and Na-In) around Pb perovskite 2D crystals. Distinct from Pb-Pb and Pb-Sn perovskite heterostructures, growths of the Pb-free shell at 45 degrees on the (100) surface of the lead perovskite core are observed in all Pb-free cases. The in-depth structural analysis carried out with electron diffraction unequivocally demonstrates the growth of the Pb-free shell along the [110] direction of the Pb perovskite, which is likely due to the relatively lower surface energy of the (110) surface. Furthermore, an investigation of anionic interdiffusion across heterostructure interfaces under the influence of heat was carried out. Interestingly, halide anion diffusion in the Pb-free 2D perovskites is found to be significantly suppressed as compared to Pb-based 2D perovskites. The great structural tunability and excellent stability of Pb-free perovskite heterostructures may find uses in electronic and optoelectronic devices in the near future.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 15
DOI: 10.1021/JACS.3C06127
|
“Chemistry and structure of anion-deficient perovskites with translational interfaces”. Abakumov AM, Hadermann J, Van Tendeloo G, Antipov EV, Journal of the American Ceramic Society 91, 1807 (2008). http://doi.org/10.1111/j.1551-2916.2008.02351.x
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.841
Times cited: 39
DOI: 10.1111/j.1551-2916.2008.02351.x
|
“Effect of powder coating on stabilizer distribution in CeO2-stabilized ZrO2 ceramics”. Fang Pa, Gu H, Wang Pl, Van Landuyt J, Vleugels J, Van der Biest O;, Journal of the American Ceramic Society 88, 1929 (2005). http://doi.org/10.1111/j.1551-2916.2005.00342.x
Abstract: The phase and microstructure relationship of 12 mol% CeO2-stabilized ZrO2 ceramics prepared from coated powder was investigated using scanning electron microscopy (SEM), transmission electron microscopy (TEM), and energy-dispersed Xray spectroscopy (EDS). As compared with the sample prepared with co-precipitated method, which exhibited a similar grain size distribution, the EDS analysis revealed that the powder coating induced a wide distribution of CeO2 solubility, which decreases monotonically with the increase of grain size. This variation of stabilizer content from grain to grain rendered many large grains in the monoclinic phase. Stronger cerium segregation to grain boundaries was observed between large grains, which often form thin amorphous films there. The inhomogeneous; CeO2 distribution keeps more tetragonal ZrO2 grains close to the phase boundary to facilitate the transforming toughness. Addition of an Al2O3 precursor in coated powders effectively raises the overall CeO2 stabilizer content in the grains and preserves more transformable tetragonal phase in the microstructure, which further enhanced the fracture toughness. The dependence of CeO2 solubility on grain size may be explained in a simple coating-controlled diffusion and growth process that deserves further investigation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.841
Times cited: 11
DOI: 10.1111/j.1551-2916.2005.00342.x
|
“Quantitative electron microscopy of (Bi,Pb)2Sr2Ca2Cu3O10+\delta/Ag multifilament tapes during initial stages of annealing”. Bals S, Verbeeck J, Van Tendeloo G, Liu Y-L, Grivel J-C, Journal of the American Ceramic Society 88, 431 (2005). http://doi.org/10.1111/j.1551-2916.2005.00094.x
Abstract: The microstructural and compositional evolution during initial annealing of a superconducting (Bi,Pb)(2)Sr2Ca2Cu3O10+delta/Ag tape is studied using quantitative transmission electron microscopy. Special attention is devoted to the occurrence of Pb-rich liquids, which are crucial for the Bi2Sr2CaCu2O8+delta to (Bi,Pb)(2)Sr2Ca2Cu3O10+delta transformation. Ca and/or Pb-rich (Bi,Pb)(2)Sr2CaCu2O8+delta grains dissolve into a liquid, which reacts with Ca-rich phases to increase the liquid's Ca-content. This leads to (Bi,Pb)(2)Sr2Ca2Cu3O10+delta formation. Apparently, a Ca/Sr ratio of around I is sufficient to keep (Bi,Pb)(2)Sr2Ca2Cu3O10+delta nucleation going. It is confirmed that Ag particles are transported from the Ag-sheath into the oxide core by the liquid and not by mechanical treatment of the tape.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.841
Times cited: 1
DOI: 10.1111/j.1551-2916.2005.00094.x
|
“NiMn₂O₄, revisited : temperature-dependent cation distribution from in situ neutron diffraction and thermopower studies”. Dinger J, Friedrich T, Reimann T, Toepfer J, Journal of the American Ceramic Society 106, 1834 (2023). http://doi.org/10.1111/JACE.18865
Abstract: The cation distribution of the negative temperature coefficient (NTC) thermistor spinel NiMn2O4 was studied in the temperature range from 55 to 900 degrees C, using a combined in situ neutron diffraction and thermopower study. Rietveld refinements of in situ neutron diffraction data reveal a temperature dependence of the degree of inversion with an inversion parameter of 0.70(1) at 900 degrees C and 0.87(1) at 55 degrees C. Thermopower measurements were evaluated using a modified Heikes formula, and the [Mn4+]/[Mn3+] ratio on octahedral sites of the spinel structure was calculated considering spin and orbital degeneracy. The inversion degree and disproportionation parameter, determined independently as function of temperature, were used to calculate the cation distribution of NiMn2O4 in the whole temperature range. At high temperature, within the stability range of the spinel, the cation distribution is characterized by a moderate degree of inversion with a concentration of NiB2+${\mathrm{Ni}}\mathrm{B}<
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.9
DOI: 10.1111/JACE.18865
|
“Three-Dimensional Nanoparticle Transformations Captured by an Electron Microscope”. Albrecht W, Van Aert S, Bals S, Accounts Of Chemical Research 54, 1189 (2021). http://doi.org/10.1021/acs.accounts.0c00711
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 20.268
Times cited: 12
DOI: 10.1021/acs.accounts.0c00711
|
“Surfactant layers on gold nanorods”. Mosquera J, Wang D, Bals S, Liz-Marzan LM, Accounts of chemical research 56, 1204 (2023). http://doi.org/10.1021/ACS.ACCOUNTS.3C00101
Abstract: Gold nanorods (Au NRs) are an exceptionally promising tool in nanotechnology due to three key factors: (i) their strong interaction with electromagnetic radiation, stemming from their plasmonic nature, (ii) the ease with which the resonance frequency of their longitudinal plasmon mode can be tuned from the visible to the near-infrared region of the electromagnetic spect r u m based on their aspect ratio, and (iii) their simple and cost-effective preparation through seed-mediated chemical growth. In this synthetic method, surfactants play a critical role in controlling the size, shape, and colloidal stabi l i t y of Au NRs. For example, surfactants can stabilize specific crystallographic facets during the formation of Au NRs, leading to t h e formation of NRs with specific morphologies. The process of surfactant adsorption onto the NR surface may result in various assemblies of surfactant molecules, such as spherical micelles, elongated micelles, or bilayers. Again, the assembly mode is critical toward determining the further availabi l i t y of the Au NR surface to the surrounding medium. Despite its importance and a great deal of research effort, the interaction between Au NPs and surfactants remains insufficiently understood, because the assembly process is influenced by numerous factors, including the chemical nature of the surfactant, the surface morphology of Au NPs, and solution parameters. Therefore, gaining a more comprehensive understanding of these interactions is essential to unlock the full potential of the seed-mediated growth method and the applications of plasmonic NPs. A plethora of characterization techniques have been applied to reach such an understanding , but many open questions remain. In this Account, we review the current knowledge on the interactions between surfactants and Au NRs. We briefly introduce the state-of-the-art methods for synthesizing Au NRs and highlight the crucial role of cationic surfactants during this process. The self-assembly and organization of surfactants on the Au NR surface is then discussed to better understand their role in seed-mediated growth. Subsequently, we provide examples and elucidate how chemical additives can be used to modulate micellar assemblies, in turn allowing for a finer control over the growth of Au NRs, including chiral NRs. Next, we review the main experimental characterization and computational modeling techniques that have been applied to shed light on the arrangement of surfactants on Au NRs and summarize the advantages and disadvantages for each technique. The Account ends with a “Conclusions and Outlook” section, outlining promising future research directions and developments that we consider are sti l l required, mostly related to the application of electron microscopy in liquid and in 3D. Finally, we remark on the potential of exploiting machine learning techniques to predict synthetic routes for NPs with predefined structures and properties.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 18.3
Times cited: 8
DOI: 10.1021/ACS.ACCOUNTS.3C00101
|
“Defect induced thickness growth in silver chloride (111) tabular crystals: a TEM study”. Van Renterghem W, Schryvers D, van Landuyt J, Bollen D, Van Roost C, De Keyzer RB, , 38 (2000)
Abstract: Defects in AgG tabular crystals with {111} surfaces are characterised by transmission electron microscopy (TEM) and their influence on the growth process is discussed. In the tabular crystals, twins parallel to the tabular face as well as dislocations along different directions are observed. The twins induce the tabular growth, while the dislocations do not influence the morphology. In 10 to 30% of the crystals that have been characterised, thickness growth is observed and it is shown that in all cases twins on other planes than the tabular ones are present. Two configurations occur more frequently and are analysed in detail. For the first group, twins parallel to the tabular face as well as a microtwin along a non-parallel {111} plane and ending inside the crystal are present. In the crystals of the second group only one extra non-parallel twin occurs giving rise to a bicrystal built up by a tetrahedral shaped part and a flat triangular or trapezoidal part. More complex twin configurations give rise to various, less characteristic morphologies.
Keywords: P1 Proceeding; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
|
“The influence of the precipitation method on defect formation in multishell AgBrI (111) tabular crystals”. Van Renterghem W, Karthauser S, Schryvers D, van Landuyt J, De Keyzer R, Van Roost C, , 167 (2000)
Abstract: Multishell tabular grains have a higher speed than pure AgBr tabular grains. Usually the shells differ in size and iodide content, but also the precipitation method for the iodide containing shells has an influence on the iodide incorporation. A TEM investigation was performed to determine the defect structure of multishell AgBr (111) tabular crystals containing a shell with a low iodide concentration and one with a high iodide concentration. The twins that induce tabular growth and stacking fault contrast in the region of the iodide shells have been observed, similar to previously studied AgBr/Ag(Br,I) coreshell crystals. Moreover in some of the crystals dislocations have been observed, sometimes even an entire network. The number of dislocations formed varies for the different methods of iodide addition. Also variations in average thickness between the different iodide addition methods have been observed. A higher number of dislocations and thicker crystals point towards a higher local concentration of iodide. These observations allow deciding which iodide incorporation method is most useful for a preferred dislocation pattern.
Keywords: P1 Proceeding; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
|
“Positron annihilation study of nanocrystalline Ni3Al : simulations and measurements”. Kuriplach J, van Petegem S, Hou M, Van Tendeloo G, Schryvers D, et al, Materials science forum
T2 –, 12th International Conference on Positron Annihilation (ICPA-12), AUG 06-12, 2000, UNIV BUNDERSWEHR MUNCHEN, NEUBIBERG, GERMANY 363-3, 94 (2001)
Abstract: A positron lifetime experiment is performed on samples produced by the compaction of nanocrystalline Ni3Al powder synthesized by the inert-gas condensation technique. In the lifetime spectrum we observe two components corresponding to defects. Computer (virtual) samples of n-Ni3Al are obtained using molecular dynamics combined with the Metropolis Monte Carlo technique. Positron lifetime calculations are then performed on selected regions of simulated samples. For this purpose, a new computational technique based on a generalization of the atomic superposition method for non-periodic systems was developed. Lifetimes calculated in this way are compared to experiment.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
“Electron-microscopy and the structural studies of superconducting materials and fullerites”. Van Tendeloo G, Amelinckx S, NATO Advanced Study Institutes series: series E : applied sciences
T2 –, NATO Advanced Study Institute on Materials and crystallographic Aspects, of HT(c)-Superconductivity, May 17-30, 1993, Erice, Italy , 521 (1994)
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
|
“A microstructural study of the thermal stability of atomic layer deposited Al2O3 thin films”. Nistor LC, Richard O, Zhao O, Bender H, Stesmans A, Van Tendeloo G, Institute of physics conference series
T2 –, Microscopy of semiconducting materials , 397 (2003)
Abstract: The thermal stability of amorphous Al2O3 films (similar to8 and 80 nut thick) deposited by atomic layer deposition on HF-last and thin SiO2 covered (001) Si substrates is studied by transmission electron microscopy. The layers are in- and ex-situ annealed in the same temperature range.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
“Present state of the composition evaluation of ternary semiconductor nanostructures by lattice fringe analysis”. Rosenauer A, Gerthsen D, Van Aert S, van Dyck D, den Dekker AJ, Institute of physics conference series , 19 (2003)
Abstract: Semiconductor heterostructures are used for the fabrication of optoelectronic devices. Performance of such devices is governed by their chemical morphology. The composition distribution of quantum wells and dots is influenced by kinetic growth processes which are not understood completely at present. To obtain more information about these effects, methods for composition determination with a spatial resolution at a near atomic scale are necessary. In this paper we focus on the present state of the composition evaluation by the lattice fringe analysis (CELFA) technique and explain the basic ideas, optimum imaging conditions, precision and accuracy.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
|
“EFTEM study of plasma etched low-k Si-O-C dielectrics”. Hens S, Bender H, Donaton RA, Maex K, Vanhaelemeersch S, van Landuyt J, Institute of physics conference series
T2 –, Royal-Microscopical-Society Conference on Microscopy of Semiconducting, Materials, MAR 25-29, 2001, UNIV OXFORD, OXFORD, ENGLAND , 415 (2001)
Abstract: Materials with low dielectric constant ("low-k'') in combination with Cu metallization are replacing the oxide based dielectrics with Al metallization in future generations of micro-electronic devices. In this work, a carbon doped oxide low-k dielectric material is studied after different kinds of etch/strip steps in single damascene Cu. filled line structures. Interline capacitance measurements indicate a dependence of the dielectric constant on the strip conditions. EFTEM is used to study the composition of the dielectric material and the modification of the low-k material at the sidewall of the etched structures for the various treatment conditions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
“Characterisation of the local stress induced by shallow trench isolation and CoSi2 silicidation”. Stuer C, Steegen A, van Landuyt J, Bender H, Maex K, Institute of physics conference series , 481 (2001)
Abstract: With further down-scaling below 0.25mum technologies, CoSi2 is replacing TiSi2 because of its superior formation chemistry on narrow lines and favourable stress behaviour. Shallow trench isolation (STI) is used as the isolation technique in these technologies. In this study, convergent beam electron diffraction (CBED) measurements and finite element modelling (FEM) are performed to evaluate the local stress components in the silicon substrate, induced in STI structures with a 45 nm or a 85 nm CoSi2 silicidation. High compressive stresses in the active area and tensile stress around the trench corners are observed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
“HREM investigation of a Fe/GaN/Fe tunnel junction”. Nistor L, Bender H, van Landuyt J, Nemeth S, Boeve H, De Boeck J, Borghs G, Institute of physics conference series
T2 –, Royal-Microscopical-Society Conference on Microscopy of Semiconducting, Materials, MAR 25-29, 2001, Univ of Oxford, Oxford, England , 53 (2001)
Abstract: The structure of Fe/GaN/Fe ferromagnetic electrodes is studied by high resolution transmission electron microscopy. The layers grow epitaxially on the GaAs substrate with the top Fe layer 90degrees rotated compared to the bottom one. The interfaces are quite rough. There is an indication of the possible occurrence of Fe3GaAs formation on the GaAs interface.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
“Clustering of vacancies on {113} planes in Si layers close to Si-Si3N4 interfaces and further aggregation of self-interstitials inside vacancy clusters during electron irradiation”. Fedina L, Gutakovskii A, Aseev A, van Landuyt J, Vanhellemont J, Institute of physics conference series
T2 –, Conference on Microscopy of Semiconducting Materials, MAR 22-25, 1999, UNIV OXFORD, OXFORD, ENGLAND , 495 (1999)
Abstract: In situ HREM irradiation of (110) FZ-Si crystals covered with thin Si3N4 films was carried out in a JEOL-4000EX microscope, operated at 400 keV at room temperature. It is found that clustering of vacancies on (113) planes is realised in a Si layer close to the Si-Si3N4 interface at the initial stage of irradiation. Further aggregation of self-interstitials inside vacancy clusters is considered as an alternative way of point defect recombination in extended shape, to be accomplished with the formation of the extended defects of interstitial type upon interstitial supersaturation.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
|
“Electron microscopy study of ternary precipitates in Ni39.6Mn47.5Ti12.9”. Seo JW, Schryvers D, Potapov P, , 17 (1998)
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
|
“HREM investigation of La(1-x)Ca(x)MnO3-delta thin films”. Lebedev O, Van Tendeloo G, Amelinckx S, Leibold B, Habermeier HU, , 517 (1998)
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
|
“Microstructure of artificial [100] 45 degrees twist grain boundaries in YBa2Cu3O7-delta”. Verbist K, Tafuri F, Granozio FM, Di Chiara S, Van Tendeloo G, Electron Microscopy 1998, Vol 2: Materials Science 1 , 593 (1998)
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
|
“Laser thermotreatment of the SnO2layers”. Rembeza SI, Loginov VA, Svistova TV, Podkopaeva OI, Rembeza ES, van Landuyt J, Eurosensors XII, vols 1 and 2 , 481 (1998)
Abstract: The optical and electrical properties and pi ase composition of magnetron sputtered antimony-doped SnOx thin films are investigated before and after laser thermotreatment The temperature dependencies on mobility and concentration of free charges are measured by Van der Pauw method. The gas sensitivity of SnOx has been measured before and after laser thermotreatment.
Keywords: P1 Proceeding; Electron microscopy for materials research (EMAT)
|