“Electron microscopy study of Nb-rich nanoprecipitates in NiTiNb and their influence on the martensitic transformation”. Shi H, Pourbabak S, Van Humbeeck J, Schryvers D, Scripta materialia 67, 939 (2012). http://doi.org/10.1016/j.scriptamat.2012.08.020
Abstract: Nb-rich nanoprecipitates in the matrix of an annealed commercial NiTiNb alloy are investigated by scanning and transmission electron microscopy, including slice-and-view and chemical analysis. The precipitates have a diameter of around 100 nm, are faceted and have a cube-on-cube relation with the B2 matrix. In situ TEM cooling shows that the martensitic transformation is hampered by the presence of these precipitates. The latter could explain the increase in hysteresis when compared with the binary system.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 29
DOI: 10.1016/j.scriptamat.2012.08.020
|
|
|
“Focused ion beam/scanning electron microscopy tomography and conventional transmission electron microscopy assessment of Ni4Ti3 morphology in compression-aged Ni-rich Ni-Ti single crystals”. Cao S, Somsen C, Croitoru M, Schryvers D, Eggeler G, Scripta materialia 62, 399 (2010). http://doi.org/10.1016/j.scriptamat.2009.11.040
Abstract: The size, morphology and configuration of Ni4Ti3 precipitates in a single-crystal NiTi alloy have been investigated by two-dimensional transmission electron microscopy-based image analysis and three-dimensional reconstruction from slice-and-view images obtained in a focused ion beam/scanning electron microscopy (FIB/SEM) dual-beam system. Average distances between the precipitates measured along the compression direction correlate well between both techniques, while particle shape and configuration data is best obtained from FIB/SEM. Precipitates form pockets of B2 of 0.54 ìm in the compression direction and 1 ìm perpendicular to the compression direction.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 3.747
Times cited: 16
DOI: 10.1016/j.scriptamat.2009.11.040
|
|
|
“HREM investigation of martensite precursor effects and stacking sequences in Ni-Mn-Ti alloys”. Schryvers D, Lahjouji DE, Slootmaekers B, Potapov PL, Scripta metallurgica et materialia 35, 1235 (1996). http://doi.org/10.1016/1359-6462(96)00271-0
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.224
Times cited: 2
DOI: 10.1016/1359-6462(96)00271-0
|
|
|
“Is there a relationship between the stacking fault character and the activated mode of plasticity of FeMn-based austenitic steels?”.Idrissi H, Ryelandt L, Veron M, Schryvers D, Jacques PJ, Scripta materialia 60, 941 (2009). http://doi.org/10.1016/j.scriptamat.2009.01.040
Abstract: By changing the testing temperature, an austenitic FeMnAlSi alloy presents either å-martensite transformation or mechanical twinning during straining. In order to understand the nucleation and growth mechanisms involved in both phenomena, defects and particularly stacking faults, were characterized by transmission electron microscopy. It is observed that the character of the stacking faults also changes (from extrinsic to intrinsic) together with the temperature and the activated mode of plasticity.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 84
DOI: 10.1016/j.scriptamat.2009.01.040
|
|
|
“Microstructure and precipitates in as-cast Co38Ni33Al29 shape memory alloy”. Bartova B, Schryvers D, Yang Z, Ignacova S, Sittner P, Scripta materialia 57, 37 (2007). http://doi.org/10.1016/j.scriptamat.2007.03.007
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 22
DOI: 10.1016/j.scriptamat.2007.03.007
|
|
|
“On the crystal structure of TiNi-Cu martensite”. Potapov P, Shelyakov A, Schryvers D, Scripta materialia 44, 1 (2001). http://doi.org/10.1016/S1359-6462(00)00555-8
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 36
DOI: 10.1016/S1359-6462(00)00555-8
|
|
|
“On the relationship between the twin internal structure and the work-hardening rate of TWIP steels”. Idrissi H, Renard K, Schryvers D, Jacques PJ, Scripta materialia 63, 961 (2010). http://doi.org/10.1016/j.scriptamat.2010.07.016
Abstract: FeMnC and FeMnSiAl TWIP steels deformed under the same conditions exhibit different work-hardening rates. The present study investigates the microstructure of plastically deformed FeMnC and FeMnSiAl samples, particularly the internal structure of the mechanically generated twins and their topology at the grain scale. Twins in the FeMnC steel are finer and full of sessile dislocations, rendering this material distinctly stronger with an improved work-hardening rate.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 145
DOI: 10.1016/j.scriptamat.2010.07.016
|
|
|
“On the stress state dependence of the twinning rate and work hardening in twinning-induced plasticity steels”. Renard K, Idrissi H, Schryvers D, Jacques PJ, Scripta materialia 66, 966 (2012). http://doi.org/10.1016/j.scriptamat.2012.01.063
Abstract: The influence of the stress state on the twinning rate and work hardening is studied in the case of an FeMnC TWIP steel strained in uniaxial tension, simple shear and rolling. The resulting stressstrain responses exhibit marked differences. The twinning rate, number of activated twinning systems in each grain, twin thickness and transmission of twins across grain boundaries are dependent on the imposed stress state during straining. Relationships between twin features and macroscopic work hardening rate are established.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 41
DOI: 10.1016/j.scriptamat.2012.01.063
|
|
|
“Quantitative 3-D morphologic and distributional study of Ni4Ti3 precipitates in a Ni51Ti49 single crystal alloy”. Cao S, Pourbabak S, Schryvers D, Scripta materialia 66, 650 (2012). http://doi.org/10.1016/j.scriptamat.2012.01.045
Abstract: The size, shape and distribution of Ni4Ti3 precipitates in Ni51Ti49 single crystals annealed under stress-free and 〈1 1 1〉B2 compressive conditions are studied via focused ion beam/scanning electron microscopy slice-and-view. The precipitates in the stress-free material grow in autocatalytic pockets with larger size, lower number density, flatter shape and larger inter-particle distance than in the compressed material. Nevertheless, a new quantification method called water penetration reveals that, due to the precipitate alignment, martensite can grow more easily in the compressed material perpendicular to the compression direction.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 8
DOI: 10.1016/j.scriptamat.2012.01.045
|
|
|
“R-phase transition and related mechanical properties controlled by low-temperature aging treatment in a Ti50.8 at.% Ni thin wire”. Wang X, Li K, Schryvers D, Verlinden B, Van Humbeeck J, Scripta materialia 72-73, 21 (2014). http://doi.org/10.1016/j.scriptamat.2013.10.006
Abstract: A cold-drawn Ti50.8 at.% Ni wire was annealed at 600 °C for 30 min, followed by aging at 250 °C for different times. A microstructure with small grains and nanoscaled precipitates was obtained. The thermally induced martensite transformation is suppressed in the samples aged for 4 h or longer, leaving a one-stage R-phase transition between −150 and +150 °C. The transformation behavior, work output and recovery stress associated with the R-phase transition are presented.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 27
DOI: 10.1016/j.scriptamat.2013.10.006
|
|
|
“Texture-dependent twin formation in nanocrystalline thin Pd films”. Wang B, Idrissi H, Shi H, Colla MS, Michotte S, Raskin JP, Pardoen T, Schryvers D, Scripta materialia 66, 866 (2012). http://doi.org/10.1016/j.scriptamat.2012.01.038
Abstract: Nanocrystalline Pd films were produced by electron-beam evaporation and sputter deposition. The electron-beam-evaporated films reveal randomly oriented nanograins with a relatively high density of growth twins, unexpected in view of the high stacking fault energy of Pd. In contrast, sputter-deposited films show a clear 〈1 1 1〉 crystallographic textured nanostructure without twins. These results provide insightful information to guide the generation of microstructures with enhanced strength/ductility balance in high stacking fault energy nanocrystalline metallic thin films.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 19
DOI: 10.1016/j.scriptamat.2012.01.038
|
|
|
“Transmission electron microscopy investigation of microstructures in low-hysteresis alloys with special lattice parameters”. Delville R, Schryvers D, Zhang Z, James RD, Scripta materialia 60, 293 (2009). http://doi.org/10.1016/j.scriptamat.2008.10.025
Abstract: A sharp drop in hysteresis is observed for shape memory alloys satisfying the compatibility condition between austenite and martensite, i.e. ë2 = 1, where ë2 is the middle eigenvalue of the transformation strain matrix. The present work investigates the evolution of microstructure by transmission electron microscopy as the composition of the Ti50Ni50−xPdx system is systemically tuned to achieve the condition ë2 = 1. Changes in morphology, twinning density and twinning modes are reported along with twinless martensite and exact austenitemartensite interfaces.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.747
Times cited: 56
DOI: 10.1016/j.scriptamat.2008.10.025
|
|
|
“Optical encoding of luminescent carbon nanodots in confined spaces”. Bartholomeeusen E, De Cremer G, Kennes K, Hammond C, Hermans I, Lu J-B, Schryvers D, Jacobs PA, Roeffaers MBJ, Hofkens J, Sels BF, Coutino-Gonzalez E, Chemical Communications 57, 11952 (2021). http://doi.org/10.1039/D1CC04777A
Abstract: Stable emissive carbon nanodots were generated in zeolite crystals using near infrared photon irradiation gradually converting the occluded organic template, originally used to synthesize the zeolite crystals, into discrete luminescent species consisting of nano-sized carbogenic fluorophores, as ascertained using Raman microscopy, and steady-state and time-resolved spectroscopic techniques. Photoactivation in a confocal laser fluorescence microscope allows 3D resolved writing of luminescent carbon nanodot patterns inside zeolites providing a cost-effective and non-toxic alternative to previously reported metal-based nanoclusters confined in zeolites, and opens up opportunities in bio-labelling and sensing applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.319
DOI: 10.1039/D1CC04777A
|
|
|
“Displacive-replacive phase transformation in a Ni62.5Al37.5 phase studies by HREM and microdiffraction”. Muto S, Merk N, Schryvers D, Tanner LE, Philosophical magazine: B: physics of condensed matter: electronic, optical and magnetic properties 67, 673 (1993). http://doi.org/10.1080/13642819308219316
Abstract: The structure of the metastable Ni2Al phase, which has long been a matter of controversy, has been carefully re-examined by means of high-resolution transmission electron microscopy (HREM) and electron microdiffraction. First, it is concluded that theas-quenched NixAl100-x(60 less-than-or-equal-to x less-than-or-equal-to 65) material already exhibits a partial omega-type collapse in a one-dimensional fashion which and is consistent with the anomalous dip in the phonon dispersion curve. Ni2Al precipitates are formed on annealing by thermal decomposition of the high-temperature NixAl100-xB2 phase and still retain the small omega-type shuffle. The amount of displacement in the well developed Ni2Al phase was estimated to be between 20 and 50% of the ideal omega collapse; this was determined by means of a combined technique of HREM and microdiffraction together with dynamical calculations of HREM images and diffraction intensities.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 16
DOI: 10.1080/13642819308219316
|
|
|
“Composition gradients surrounding Ni4Ti3 precipitates in a NiTi alloy studied by EELS, EFTEM and EDX”. Yang Z, Schryvers D, International journal of applied electromagnetics and mechanics 23, 17 (2006)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 0.769
|
|
|
“Melamine–Formaldehyde Microcapsules: Micro- and Nanostructural Characterization with Electron Microscopy”. Heidari H, Rivero G, Idrissi H, Ramachandran D, Cakir S, Egoavil R, Kurttepeli M, Crabbé, AC, Hauffman T, Terryn H, Du Prez F, Schryvers D, Microscopy and microanalysis 22, 1222 (2016). http://doi.org/10.1017/S1431927616012484
Abstract: A systematic study has been carried out to compare the surface morphology, shell thickness, mechanical properties, and binding behavior of melamine–formaldehyde microcapsules of 5–30 μm diameter size with various amounts of core content by using scanning and transmission electron microscopy including electron tomography, in situ nanomechanical tensile testing, and electron energy-loss spectroscopy. It is found that porosities are present on the outside surface of the capsule shell, but not on the inner surface of the shell. Nanomechanical tensile tests on the capsule shells reveal that Young’s modulus of the shell material is higher than that of bulk melamine–formaldehyde and that the shells exhibit a larger fracture strain compared with the bulk. Core-loss elemental analysis of microcapsules embedded in epoxy indicates that during the curing process, the microcapsule-matrix interface remains uniform and the epoxy matrix penetrates into the surface micro-porosities of the capsule shells.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 2
DOI: 10.1017/S1431927616012484
|
|
|
“High-quality sample preparation by low kV FIB thinning for analytical TEM measurements”. Bals S, Tirry W, Geurts R, Yang Z, Schryvers D, Microscopy and microanalysis 13, 80 (2007). http://doi.org/10.1017/S1431927607070018
Abstract: Focused ion beam specimen preparation has been used for NiTi samples and SrTiO(3)/SrRuO(3) multilayers with prevention of surface amorphization and Ga implantation by a 2-kV cleaning procedure. Transmission electron microscopy techniques show that the samples are of high quality with a controlled thickness over large scales. Furthermore, preferential thinning effects in multicompounds are avoided, which is important when analytical transmission electron microscopy measurements need to be interpreted in a quantitative manner. The results are compared to similar measurements acquired for samples obtained using conventional preparation techniques such as electropolishing for alloys and ion milling for oxides.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 82
DOI: 10.1017/S1431927607070018
|
|
|
“Intergrowth of components and ramps in coffin-shaped ZSM-5 zeolite crystals unraveled by focused ion beam-assisted transmission electron microscopy”. Lu J, Roeffaers MBJ, Bartholomeeusen E, Sels BF, Schryvers D, Microscopy and microanalysis 20, 42 (2014). http://doi.org/10.1017/S1431927613013731
Abstract: Scanning electron microscopy, focused ion beam (FIB), and transmission electron microscopy are combined to study the intergrowth of 90 degrees rotational components and of ramps in coffin-shaped ZSM-5 crystals. The 90 degrees rotational boundaries with local zig-zag features between different intergrowth components are observed in the main part of crystal. Also a new kind of displacement boundary is described. At the displacement boundary there is a shift of the unit cells along the boundary without a change in orientation. Based on lamellae prepared with FIB from different positions of the ramps and crystal, the orientation relationships between ramps and the main part of the crystal are studied and the three-dimensional morphology and growth mechanism of the ramp are illustrated.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 7
DOI: 10.1017/S1431927613013731
|
|
|
“Microstructure of surface and subsurface layers of a Ni-Ti shape memory microwire”. Tian H, Schryvers D, Shabalovskaya S, van Humbeeck J, Microscopy and microanalysis 15, 62 (2009). http://doi.org/10.1017/S1431927609090059
Abstract: The microstructure of a 55 Êm diameter, cold-worked Ni-Ti microwire is investigated by different transmission electron microscopy techniques. The surface consists of a few hundred nanometer thick oxide layer composed of TiO and TiO2 with a small fraction of inhomogeneously distributed Ni. The interior of the wire has a core-shell structure with primarily B2 grains in the 1 Êm thick shell, and heavily twinned B19 martensite in the core. This core-shell structure can be explained by a concentration gradient of the alloying elements resulting in a structure separation due to the strong temperature dependence of the martensitic start temperature. Moreover, in between the B2 part of the metallic core-shell and the oxide layer, a Ni3Ti interfacial layer is detected.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 15
DOI: 10.1017/S1431927609090059
|
|
|
“Optimal sample preparation to characterize corrosion in historical photographs with analytical TEM”. Grieten E, Caen J, Schryvers D, Microscopy and microanalysis 20, 1585 (2014). http://doi.org/10.1017/S1431927614012860
Abstract: An alternative focused ion beam preparation method is used for sampling historical photographs containing metallic nanoparticles in a polymer matrix. We use the preparation steps of classical ultra-microtomy with an alternative final sectioning with a focused ion beam. Transmission electron microscopy techniques show that the lamella has a uniform thickness, which is an important factor for analytical transmission electron microscopy. Furthermore, the method maintains the spatial distribution of nanoparticles in the soft matrix. The results are compared with traditional preparation techniques such as ultra-microtomy and classical focused ion beam milling.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Antwerp Cultural Heritage Sciences (ARCHES)
Impact Factor: 1.891
DOI: 10.1017/S1431927614012860
|
|
|
“Point defect clusters and dislocations in FIB irradiated nanocrystalline aluminum films : an electron tomography and aberration-corrected high-resolution ADF-STEM study”. Idrissi H, Turner S, Mitsuhara M, Wang B, Hata S, Coulombier M, Raskin J-P, Pardoen T, Van Tendeloo G, Schryvers D, Microscopy and microanalysis 17, 983 (2011). http://doi.org/10.1017/S143192761101213X
Abstract: Focused ion beam (FIB) induced damage in nanocrystalline Al thin films has been characterized using advanced transmission electron microscopy techniques. Electron tomography was used to analyze the three-dimensional distribution of point defect clusters induced by FIB milling, as well as their interaction with preexisting dislocations generated by internal stresses in the Al films. The atomic structure of interstitial Frank loops induced by irradiation, as well as the core structure of Frank dislocations, has been resolved with aberration-corrected high-resolution annular dark-field scanning TEM. The combination of both techniques constitutes a powerful tool for the study of the intrinsic structural properties of point defect clusters as well as the interaction of these defects with preexisting or deformation dislocations in irradiated bulk or nanostructured materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.891
Times cited: 25
DOI: 10.1017/S143192761101213X
|
|
|
“Effect of interface evolution on thermal conductivity of vacuum hot pressed SiC/Al composites”. Chen Z, Tan Z, Ji G, Schryvers D, Ouyang Q, Li Z, Advanced engineering materials 17, 1076 (2015). http://doi.org/10.1002/adem.201400412
Abstract: The SiC/Al composites have been fabricated by a vacuum hot pressing (VHP) process in order to study the effect of interface evolution on the global thermal conductivity (TC). By optimizing the VHP parameters of sintering temperature and time, the three different kinds of SiC/Al interface configurations, that is, non-bonded, diffusion-bonded, and reaction-bonded interfaces, are formed and identified by measurement of relative density, X-ray diffraction, scanning and (high-resolution) transmission electron microscopy. The VHPed composite sintered at 655 °C for 60 min is fully dense and presents a tightly-adhered and clean SiC/Al interface at the nanoscale, the ideal diffusion-bonded interface being the most favorable for minimizing interfacial thermal resistance, which in turn results in the highest TC of around 270 W/mK.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.319
Times cited: 9
DOI: 10.1002/adem.201400412
|
|
|
“Advanced three-dimensional electron microscopy techniques in the quest for better structural and functional materials”. Schryvers D, Cao S, Tirry W, Idrissi H, Van Aert S, Science and technology of advanced materials 14, 014206 (2013). http://doi.org/10.1088/1468-6996/14/1/014206
Abstract: After a short review of electron tomography techniques for materials science, this overview will cover some recent results on different shape memory and nanostructured metallic systems obtained by various three-dimensional (3D) electron imaging techniques. In binary NiTi, the 3D morphology and distribution of Ni4Ti3 precipitates are investigated by using FIB/SEM slice-and-view yielding 3D data stacks. Different quantification techniques will be presented including the principal ellipsoid for a given precipitate, shape classification following a Zingg scheme, particle distribution function, distance transform and water penetration. The latter is a novel approach to quantifying the expected matrix transformation in between the precipitates. The different samples investigated include a single crystal annealed with and without compression yielding layered and autocatalytic precipitation, respectively, and a polycrystal revealing different densities and sizes of the precipitates resulting in a multistage transformation process. Electron tomography was used to understand the interaction between focused ion beam-induced Frank loops and long dislocation structures in nanobeams of Al exhibiting special mechanical behaviour measured by on-chip deposition. Atomic resolution electron tomography is demonstrated on Ag nanoparticles in an Al matrix.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.798
Times cited: 6
DOI: 10.1088/1468-6996/14/1/014206
|
|
|
“Linking a completely three-dimensional nanostrain to a structural transformation eigenstrain”. Tirry W, Schryvers D, Nature materials 8, 752 (2009). http://doi.org/10.1038/NMAT2488
Abstract: NiTi is one of the most popular shape-memory alloys, a phenomenon resulting from a martensitic transformation. Commercial NiTi-based alloys are often thermally treated to contain Ni4Ti3 precipitates. The presence of these precipitates can introduce an extra transformation step related to the so-called R-phase. It is believed that the strain field surrounding the precipitates, caused by the matrixprecipitate lattice mismatch, lies at the origin of this intermediate transformation step. Atomic-resolution transmission electron microscopy in combination with geometrical phase analysis is used to measure the elastic strain field surrounding these precipitates. By combining measurements from two different crystallographic directions, the three-dimensional strain matrix is determined from two-dimensional measurements. Comparison of the measured strain matrix to the eigenstrain of the R-phase shows that both are very similar and that the introduction of the R-phase might indeed compensate the elastic strain introduced by the precipitate.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 39.737
Times cited: 53
DOI: 10.1038/NMAT2488
|
|
|
“Crack initiation in tapered high Si stainless steel specimens : stress threshold analyses”. Penders A, Konstantinovic MJ, Bosch RW, Schryvers D, Corrosion Engineering Science And Technology , 1 (2020). http://doi.org/10.1080/1478422X.2020.1785651
Abstract: Tapered specimens were used for an accelerated test technique to study the crack initiation of high Si stainless steel by means of constant elongation rate tensile testing in a simulated pressurised water reactor environment. Detailed crack density distributions were obtained by applying an advanced crack detection algorithm on iteratively displaced scanning electron microscopy pictures featuring stress corrosion cracks along the specimen's gauge length. By means of finite-element analysis, prominent peaks in the crack density graphs are demonstrated to be related to stress relief and stress build-up during the crack initiation phase. Intrinsic scatter related to the crack detection suggests that stress corrosion cracking is independent of the strain-rate for strain-rates lower than 10(-6 )s(-1). Based on the extrapolation to constant load conditions, the critical threshold value for the duplex high Si stainless steel is estimated to be around 580 MPa.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.8
Times cited: 1
DOI: 10.1080/1478422X.2020.1785651
|
|
|
“TEM investigation of SCC crack tips in high Si stainless steel tapered specimens”. Penders A, Konstantinovic MJ, Van Renterghem W, Bosch RW, Schryvers D, Corrosion Engineering Science And Technology (2021). http://doi.org/10.1080/1478422X.2021.1961665
Abstract: The stress corrosion cracking (SCC) mechanism is investigated in high Si duplex stainless steel in a simulated PWR environment based on TEM analysis of FIB-extracted SCC crack tips. The microstructural investigation in the near vicinity of SCC crack tips illustrates a strain-rate dependence in SCC mechanisms. Detailed analysis of the crack tip morphology, that includes crack tip oxidation and surrounding deformation field, indicates the existence of an interplay between corrosion- and deformation-driven failure as a function of the strain rate. Slow strain-rate crack tips exhibit a narrow cleavage failure which can be linked to the film-induced failure mechanism, while rounded shaped crack tips for faster strain rates could be related to the strain-induced failure. As a result, two nominal strain-rate-dependent failure regimes dominated either by corrosion or deformation-driven cracking mechanisms can be distinguished.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 0.879
DOI: 10.1080/1478422X.2021.1961665
|
|
|
“TEM investigation of the formation mechanism of deformation twins in Fe-Mn-Si-Al TWIP steels”. Idrissi H, Renard K, Schryvers D, Jacques PJ, Philosophical magazine 93, 4378 (2013). http://doi.org/10.1080/14786435.2013.832837
Abstract: The microstructure of a Fe-Mn-Si-Al twinning-induced plasticity (TWIP) steel exhibiting remarkable work hardening rate under uniaxial tensile deformation was investigated using transmission electron microscopy to uncover the mechanism(s) controlling the nucleation and growth of the mechanically induced twins. The results show that the stair-rod cross-slip deviation mechanism is necessary for the formation of the twins, while large extrinsic stacking faults homogenously distributed within the grains could act as preferential sources for the activation of the deviation process. The influence of such features on the thickness and strength of the twins and the resulting mechanical behaviour is discussed and compared to similar works recently performed on Fe-Mn-C TWIP steels.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.505
Times cited: 15
DOI: 10.1080/14786435.2013.832837
|
|
|
“Transmission electron microscopy study of phase compatibility in low hysteresis shape memory alloys”. Delville R, Kasinathan S, Zhang Z, van Humbeeck J, James RD, Schryvers D, Philosophical magazine 90, 177 (2010). http://doi.org/10.1080/14786430903074755
Abstract: Recent findings have linked low hysteresis in shape memory alloys with phase compatibility between austenite and martensite. To investigate the evolution of microstructure as phase compatibility increases and hysteresis is reduced, transmission electron microscopy was used to study the alloy system Ti50Ni50xPdx, where the composition is systemically tuned to approach perfect compatibility. Changes in morphology, twinning density and twinning modes are reported, along with special microstructures occurring when compatibility is achieved. In addition, the interface between austenite and a single variant of martensite was studied by high-resolution and conventional electron microscopy. The low energy configuration of the interface detailed in this article suggests that it plays an important role in the lowering of hysteresis compared to classical habit plane interfaces.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.505
Times cited: 70
DOI: 10.1080/14786430903074755
|
|
|
“Multiscale characterization of the work hardening mechanisms in Fe-Mn based TWIP steels”. Renard K, Idrissi H, Schryvers D, Jacques PJ, Steel research international 83, 385 (2012). http://doi.org/10.1002/srin.201100312
Abstract: When strained in tension, high-manganese austenitic twinning induced plasticity (TWIP) steels achieve very high strength and elongation before necking. The main hypotheses available in the literature about the origin of their excellent work hardening include deformation twinning and dynamic strain ageing. In order to provide some answers, various experiments at different scales were conducted on FeMnC steels and the Fe28 wt%Mn3.5 wt%Al2.8 wt%Si alloy. At a macroscopic scale, tensile tests were performed on all the studied grades. It was shown that, though the FeMnAlSi based alloy retains very high elongation, the FeMnC steels properties are even more extraordinary. Tensile tests at different strain rates with the help of digital image correlation were also performed on the Fe20 wt%Mn1.2 wt%C steel to study the PLC effect occurring in this type of steel. It is suggested that supplementary hardening could come from reorientation of MnC pairs in the cores of the dislocations. At a microscopic scale, the Fe20 wt%Mn1.2 wt%C TWIP steel and the FeMnAlSi grade were thoroughly investigated by means of in situ TEM analysis. In the FeMnC steel, the formed twins could also lead to a composite effect, since they contain plenty of sessile dislocations. In the FeMnAlSi alloy, mechanical twins are thicker and contain fewer defects, leading to a lower work hardening than the other grade.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.235
Times cited: 12
DOI: 10.1002/srin.201100312
|
|
|
“Direct Observation of Ferroelectric Domain Walls in LiNbO3: Wall-Meanders, Kinks, and Local Electric Charges”. Gonnissen J, Batuk D, Nataf GF, Jones L, Abakumov AM, Van Aert S, Schryvers D, Salje EKH, Advanced functional materials 26, 7599 (2016). http://doi.org/10.1002/adfm.201603489
Abstract: Direct observations of the ferroelectric domain boundaries in LiNbO3 are performed using high-resolution high-angle annular dark field scanning transmission electron microscopy imaging, revealing a very narrow width of the domain wall between the 180° domains. The domain walls demonstrate local side-way meandering, which results in inclinations even when the overall wall orientation follows the ferroelectric polarization. These local meanders contain kinks with “head-to-head” and “tail-to-tail” dipolar configurations and are therefore locally charged. The charged meanders are confined to a few cation layers along the polarization direction and are separated by longer stretches of straight domain walls.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 23
DOI: 10.1002/adfm.201603489
|
|