“Existence of superstructures due to large amounts of Fe vacancies in the LiFePO4-type framework”. Hamelet S, Casas-Cabanas M, Dupont L, Davoisne C, Tarascon JM, Masquelier C, Chemistry of materials 23, 32 (2011). http://doi.org/10.1021/cm102511m
Abstract: LiFePO4 has been under intense scrutiny over the past decade because it stands as an attractive positive electrode material for the next generation of Li-ion batteries to power electric vehicles and hybrid electric vehicles, hence the importance of its thermal behavior. The reactivity of LiFePO4 with air at moderate temperatures is shown to be dependent on its particle size. For nanosized materials, a progressive displacement of Fe from the core structure leading to a composite made of nanosize Fe2O3 and highly defective, oxidized LixFeyPO4 compositions, among which the “ideal” formula LiFe2/3PO4. Herein we report, from both temperature-controlled X-ray diffraction and electronic diffraction microscopy, that these off-stoichiometry olivine-type compounds show a defect ordering resulting in the formation of a superstructure. Such a finding shows striking similarities with the temperature-driven oxidation of fayalite Fe2SiO4 (another olivine) to structurally defective laihunite, reported in the literature three decades ago.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 30
DOI: 10.1021/cm102511m
|
“Iron catalysts for the growth of carbon nanofibers : Fe, Fe3C or both?”.He Z, Maurice J-L, Gohier A, Lee CS, Pribat D, Cojocaru CS, Chemistry of materials 23, 5379 (2011). http://doi.org/10.1021/cm202315j
Abstract: Iron is a widely used catalyst for the growth of carbon nanotubes (CNTs) or carbon nanofibers (CNFs) by catalytic chemical vapor deposition. However, both Fe and FeC compounds (generally, Fe3C) have been found to catalyze the growth of CNTs/CNFs, and a comparison study of their respective catalytic activities is still missing. Furthermore, the control of the crystal structure of iron-based catalysts, that is α-Fe or Fe3C, is still a challenge, which not only obscures our understanding of the growth mechanisms of CNTs/CNFs, but also complicates subsequent procedures, such as the removal of catalysts for better industrial applications. Here, we show a partial control of the phase of iron catalysts (α-Fe or Fe3C), obtained by varying the growth temperatures during the synthesis of carbon-based nanofibers/nanotubes in a plasma-enhanced chemical vapor deposition reactor. We also show that the structure of CNFs originating from Fe3C is bamboo-type, while that of CNFs originating from Fe is not. Moreover, we directly compare the growth rates of carbon-based nanofibers/nanotubes during the same experiments and find that CNFs/CNTs grown by α-Fe nanoparticles are longer than CNFs grown from Fe3C nanoparticles. The influence of the type of catalyst on the growth of CNFs is analyzed and the corresponding possible growth mechanisms, based on the different phases of the catalysts, are discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 91
DOI: 10.1021/cm202315j
|
“Off-stoichiometry effects on the crystalline and defect structure of hexagonal manganite REMnO3 films (RE = Y, Er, Dy)”. Gélard J, Jehanathan N, Roussel H, Gariglio S, Lebedev OI, Van Tendeloo G, Dubourdieu C, Chemistry of materials 23, 1232 (2011). http://doi.org/10.1021/cm1029358
Abstract: The crystalline and defect structure of epitaxial hexagonal RExMnyO3 (RE = Er, Dy) films with varying cationic composition was investigated by X-ray diffraction and transmission electron microscopy. The films are composed of a strained layer at the interface with the substrate and of a relaxed layer on top of it. The critical thickness is of 10 to 25 nm. For Mn-rich films (or RE deficient), an off-stoichiometric composition maintaining the hexagonal LuMnO3-type structure is stabilized over a large range of the RE/Mn ratio (0.72−1.00), with no Mn-rich secondary phases observed. A linear dependence of the out-of-plane lattice parameter with RE/Mn is observed in this range. Out-of-phase boundary (OPB) extended defects are observed in all films and exhibit a local change in stoichiometry. Such a large solubility limit in the RE deficient region points toward the formation of vacancies on the RE site (RExMnO3−δ, with 0.72 ≤ x < 1), a phenomenon that is encountered in perovskite manganites such as LaxMnO3−δ (x < 1) and that may strongly impact the physical properties of hexagonal manganites.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 17
DOI: 10.1021/cm1029358
|
“Short-range layered A-site ordering in double perovskites NaLaBB'O6 (B = Mn, Fe, B' = Nb, Ta)”. Dachraoui W, Yang T, Liu C, Ling G, Hadermann J, Van Tendeloo G, Llobet A, Greenblatt M, Chemistry of materials 23, 2398 (2011). http://doi.org/10.1021/cm200226u
Abstract: The new compounds NaLaFeTaO6, NaLaFeNbO6, NaLaMnTaO6, and NaLaMnNbO6 have been synthesized and characterized with a combination of transmission electron microscopy, X-ray powder diffraction (XRPD), neutron powder diffraction (NPD), and magnetization measurements. Through electron microscopy study, a local layered order of the A-cations has been detected without the typical occurrence of rock salt order at the B-cation site. Satellite reflections in the electron diffraction related to the local layered order are not visible on the XRPD or NPD patterns. The occurrence of local layered order is supported by pair distribution function analysis, which also reveals the presence of uncorrelated displacements of the Nb and Ta cations. The octahedra are tilted according to the system a−b+a−, and the coordinates were refined from XRPD and NPD with a disordered cation distribution in the space group Pnma. The magnetic exchange interactions in NaLaFeTaO6 and NaLaFeNbO6 are antiferromagnetic, while they are ferromagnetic in NaLaMnTaO6 and NaLaMnNbO6. Long-range magnetic ordering is not observed down to 4 K for any of the compositions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 14
DOI: 10.1021/cm200226u
|
“Solving the structure of Li ion battery materials with precession electron diffraction : application to Li2CoPo4F”. Hadermann J, Abakumov AM, Turner S, Hafideddine Z, Khasanova NR, Antipov EV, Van Tendeloo G, Chemistry of materials 23, 3540 (2011). http://doi.org/10.1021/cm201257b
Abstract: The crystal structure of the Li2CoPO4F high-voltage cathode for Li ion rechargeable batteries has been completely solved from precession electron diffraction (PED) data, including the location of the Li atoms. The crystal structure consists of infinite chains of CoO4F2 octahedra sharing common edges and linked into a 3D framework by PO4 tetrahedra. The chains and phosphate anions together delimit tunnels filled with the Li atoms. This investigation demonstrates that PED can be successfully applied for obtaining structural information on a variety of Li-containing electrode materials even from single micrometer-sized crystallites.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 46
DOI: 10.1021/cm201257b
|
“Structural evolution of the BiFeO3-LaFeO3 system”. Rusakov D, Abakumov AM, Yamaura K, Belik AA, Van Tendeloo G, Takayama-Muromachi E, Chemistry of materials 23, 285 (2011). http://doi.org/10.1021/cm1030975
Abstract: The (1 − x)BiFeO3−xLaFeO3 system has been investigated and characterized by room-temperature and high-temperature laboratory and synchrotron powder X-ray diffraction, electron diffraction, high-resolution transmission electron microscopy, differential scanning calorimetry, and magnetization measurements. At room temperature, the ferroelectric R3c phase is observed for 0.0 ≤ x ≤ 0.10. The PbZrO3-related √2ap × 2√2ap × 4ap superstructure (where ap is the parameter of the cubic perovskite subcell) is observed for Bi0.82La0.18FeO3, while an incommensurately modulated phase is formed for 0.19 ≤ x ≤ 0.30 with the √2ap × 2ap × √2ap basic unit cell. The GdFeO3-type phase with space group Pnma (√2ap × 2ap × √2ap) is stable at 0.50 ≤ x ≤ 1. Bi0.82La0.18FeO3 has no detectable homogeneity range (space group Pnam, a = 5.6004(1) Å, b = 11.2493(3) Å, c = 15.6179(3) Å). The incommensurately modulated Bi0.75La0.25FeO3 structure was solved from synchrotron X-ray powder diffraction data (Imma(00γ)s00 superspace group, a = 5.5956(1) Å, b = 7.8171(1) Å, c = 5.62055(8) Å, q = 0.4855(4)c*, RP = 0.023, RwP = 0.033). In this structure, cooperative displacements of the Bi and O atoms occur, which order within the (AO) (where A = Bi, La) layers, resulting in an antipolar structure. Local fluctuations of the intralayer antipolar ordering are compensated by an interaction with the neighboring (AO) layers. A coupling of the antipolar displacements with the cooperative tilting distortion of the perovskite octahedral framework is proposed as the origin of the incommensurability. All the phases transform to the GdFeO3-type structure at high temperatures. Bi0.82La0.18FeO3 shows an intermediate PbZrO3-type phase with √2ap × 2√2ap × 2ap (space group Pbam; a = 5.6154(2) Å, b = 11.2710(4) Å, and c = 7.8248(2) Å at 570 K). The compounds in the compositional range of 0.18 ≤ x ≤ 0.95 are canted antiferromagnets.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 133
DOI: 10.1021/cm1030975
|
“Theoretical investigation of grain size tuning during prolonged bias-enhanced nucleation”. Eckert M, Mortet V, Zhang L, Neyts E, Verbeeck J, Haenen ken, Bogaerts A, Chemistry of materials 23, 1414 (2011). http://doi.org/10.1021/cm102481y
Abstract: In this paper, the effects of prolonged bias-enhanced nucleation (prolonged BEN) on the growth mechanisms of diamond are investigated by molecular dynamics (MD) and combined MD-Metropolis Monte Carlo (MD-MMC) simulations. First, cumulative impacts of CxHy+ and Hx+ on an a-C:H/nanodiamond composite were simulated; second, nonconsecutive impacts of the dominant ions were simulated in order to understand the observed phenomena in more detail. As stated in the existing literature, the growth of diamond structures during prolonged BEN is a process that takes place below the surface of the growing film. The investigation of the penetration behavior of CxHy+ and Hx+ species shows that the carbon-containing ions remain trapped within this amorphous phase where they dominate mechanisms like precipitation of sp3 carbon clusters. The H+ ions, however, penetrate into the crystalline phase at high bias voltages (>100 V), destroying the perfect diamond structure. The experimentally measured reduction of grain sizes at high bias voltage, reported in the literature, might thus be related to penetrating H+ ions. Furthermore, the CxHy+ ions are found to be the most efficient sputtering agents, preventing the build up of defective material.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 9.466
Times cited: 9
DOI: 10.1021/cm102481y
|
“Uniform patterns of Fe-vacancy ordering in the Kx(Fe,Co)2-ySe2 superconductors”. Kazakov SM, Abakumov AM, Perz-Mato JM, Ovchinnikov AV, Roslova MV, Boltalin AI, Morozov IV, Antipov EV, Van Tendeloo G, Chemistry of materials 23, 4311 (2011). http://doi.org/10.1021/cm201203h
Abstract: The Fe-vacancy ordering patterns in the superconducting KxFe2ySe2 and nonsuperconducting Kx(Fe,Co)2ySe2 samples have been investigated by electron diffraction and high angle annular dark field scanning transmission electron microscopy. The Fe-vacancy ordering occurs in the ab plane of the parent ThCr2Si2-type structure, demonstrating two types of patterns. Superstructure I retains the tetragonal symmetry and can be described with the aI = bI = as√5 (as is the unit cell parameter of the parent ThCr2Si2-type structure) supercell and I4/m space group. Superstructure II reduces the symmetry to orthorhombic with the aII = as√2, bII = 2as√2 supercell and the Ibam space group. This type of superstructure is observed for the first time in KxFe2ySe2. The Fe-vacancy ordering is inhomogeneous: the disordered areas interleave with the superstructures I and II in the same crystallite. The observed superstructures represent the compositionally dependent uniform ordering patterns of two species (the Fe atoms and vacancies) on a square lattice. More complex uniform ordered configurations, including compositional stripes, can be predicted for different chemical compositions of the KxFe2ySe2 (0 < y < 0.5) solid solutions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 20
DOI: 10.1021/cm201203h
|
“Diagnostic mirrors with transparent protection layer for ITER”. Razdobarin AG, Mukhin EE, Semenov VV, Tolstyakov SY, Kochergin MM, Kurskiev GS, Podushnikova KA, Kirilenko DA, Sitnikova AA, Konovalov VG, Solodovchenko SI, Nekhaieva OM, Skorik OA, Bondarenko VN, Voitsenya VS;, Fusion engineering and design 86, 1341 (2011). http://doi.org/10.1016/j.fusengdes.2011.02.052
Abstract: Fast degradation of in-vessel optics is one of the most serious problems for all optical diagnostics in ITER. To provide the resistance to mechanical and thermal stresses along with a high stability of optical characteristics under deposition-dominated conditions we suggest using high-reflective metallic (Ag or Al) film mirrors coated on silicon substrate and protected with thin oxide film in the divertor Thomson Scattering (TS) diagnostics. The mirrors coated with Al2O3 and ZrO2 films were tested under irradiation by deuterium ions. The experimental results on the oxide films sputtering are discussed in the context of their applicability for the first mirror protection in ITER.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.319
Times cited: 6
DOI: 10.1016/j.fusengdes.2011.02.052
|
“Catalytic and molecular separation properties of Zeogrids and Zeotiles”. Martens JA, Thybaut JW, Denayer JFM, Sree SP, Aerts A, Reyniers M-F, van Speybroeck V, Waroquier M, Buekenhoudt A, Vankelecom I, Buijs W, Persoons J, Baron GV, Bals S, Van Tendeloo G, Marin GB, Jacobs PA, Kirschhock CEA, Catalysis today 168, 17 (2011). http://doi.org/10.1016/j.cattod.2011.01.036
Abstract: Zeogrids and Zeotiles are hierarchical materials built from assembled MFI zeolite precursor units. Permanent secondary porosity in these materials is obtained through self assembly of nanoparticles encountered in MFI zeolite synthesis in the presence of supramolecular templates. Hereon, the aggregated species are termed nanoslabs. Zeogrids are layered materials with lateral spacings between nanoslabs creating galleries qualifying as supermicropores. Zeotiles present a diversity of tridimensional nanoslab assemblies with mesopores. Zeotile-1, -4 and -6 are hexagonal mesostructures. Zeotile-1 has triangular and hexagonal channels; Zeotile-4 has hexagonal channels interconnected via slits. Zeotile-2 has a cubic structure with gyroid type mesoporosity. The behavior of Zeogrids and Zeotiles in adsorption, membrane and chromatographic separation and catalysis has been characterized and compared with zeolites and mesoporous materials derived from unstructured silica sources. Shape selectivity was detected via adsorption of n- and iso-alkanes. The mesoporosity of Zeotiles can be exploited in chromatographic separation of biomolecules. Zeotiles present attractive separation properties relevant to CO2 sequestration. Because of its facile synthesis procedure without hydrothermal steps Zeogrid is convenient for membrane synthesis. The performance of Zeogrid membrane in gas separation, nanofiltration and pervaporation is reported. In the Beckmann rearrangement of cyclohexanone oxime Zeogrids and Zeotiles display a catalytic activity characteristic of silicalite-1 zeolites. Introduction of acidity and redox catalytic activity can be achieved via incorporation of Al and Ti atoms in the nanoslabs during synthesis. Zeogrids are active in hydrocracking, catalytic cracking, alkylation and epoxidation reactions. Zeogrids and Zeotiles often behave differently from ordered mesoporous materials as well as from zeolites and present a valuable extension of the family of hierarchical silicate based materials.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.636
Times cited: 13
DOI: 10.1016/j.cattod.2011.01.036
|
“An aggregate resource efficiency perspective on sustainability : a sustainable value application to the EU-15 countries”. Ang F, Van Passel S, Mathijs E, Ecological Economics 71, 99 (2011). http://doi.org/10.1016/J.ECOLECON.2011.08.008
Abstract: The Sustainable Value approach integrates the efficiency with regard to environmental, social and economic resources into a monetary indicator. It gained significant popularity as evidenced by diverse applications at the corporate level. However, its introduction as a measure adhering to the strong sustainability paradigm sparked an ardent debate. This study explores its validity as a macroeconomic strong sustainability measure by applying the Sustainable Value approach to the EU-15 countries. Concretely, we assessed environmental, social and economic resources in combination with the GDP for all EU-15 countries from 1995 to 2006 for three benchmark alternatives. The results show that several countries manage to adequately delink resource use from GDP growth. Furthermore, the remarkable difference in outcome between the national and EU-15 benchmark indicates a possible inefficiency of the current allocation of national resource ceilings imposed by the European institutions. Additionally, by using an effects model we argue that the service degree of the economy and governmental expenditures on social protection and research and development are important determinants of overall resource efficiency. Finally, we sketch out three necessary conditions to link the Sustainable Value approach to the strong sustainability paradigm. (C) 2011 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Economics
Impact Factor: 2.965
Times cited: 12
DOI: 10.1016/J.ECOLECON.2011.08.008
|
“Monolayer graphene from graphite oxide”. Dideykin A, Aleksenskiy AE, Kirilenko D, Brunkov P, Goncharov V, Baidakova M, Sakseev D, Vul' AY, Diamond and related materials 20, 105 (2011). http://doi.org/10.1016/j.diamond.2010.10.007
Abstract: Graphene, a new carbon material, is attracting presently an increasing research interest. It stems from the unique electrical and mechanical properties of graphene predicted by theory. Experimental studies of graphene are, however, severely curtailed by a lack of an appropriate technique for its preparation. Mechanical cleavage of graphite proved to be ineffective, since it yields only very small (a few microns in size) particles of monolayer graphene. The rapidly developing approach based on chemical exfoliation of graphite produces large-area coatings composed primarily of arbitrarily oriented multilayer graphene particles. We have developed a technique for preparation of monolayer graphene sheets involving liquid exfoliation of crystalline graphite, which includes synthesis of graphite oxide by deep oxidation as an intermediate stage. Electron diffraction traces, as well as the variation of diffracted intensities with local orientation of graphene sheets, AFM, and HRTEM images testify to a remarkably good monolayer structure of the graphite oxide particles obtained by our technique. These results open a way to setting up high-efficiency production of monolayer graphene sheets appropriate for electrical and optical measurements and fabrication of structures for use in the field of applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.561
Times cited: 48
DOI: 10.1016/j.diamond.2010.10.007
|
“Elucidating the photocatalytic degradation pathway of acetaldehyde : an FTIR in situ study under atmospheric conditions”. Hauchecorne B, Terrens D, Verbruggen S, Martens JA, van Langenhove H, Demeestere K, Lenaerts S, Applied catalysis : B : environmental 106, 630 (2011). http://doi.org/10.1016/J.APCATB.2011.06.026
Abstract: In this paper, new insights of the photocatalytic oxidation pathway of acetaldehyde are obtained by means of an in-house constructed FTIR in situ reactor. It is shown that there are generally three different intermediates present: acetic acid, formic acid and formaldehyde. By means of FTIR in situ spectroscopy, this study revealed that these intermediates are bound on the TiO2 surface in different ways, resulting in the presence of more intermediate species, such as molecularly adsorbed acetic acid, bidentate acetate, molecularly adsorbed formic acid, monodentate formate, bidentate formate, formaldehyde and dioxymethylene. Furthermore, spectroscopic evidence is obtained concerning the formation of 3-hydroxybutanal and crotonaldehyde upon adsorption of acetaldehyde on TiO2 prior to UV illumination. The presented results thus give new insights in the photocatalytic oxidation pathway of acetaldehyde.
Keywords: A1 Journal article; Engineering sciences. Technology; Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 9.446
Times cited: 46
DOI: 10.1016/J.APCATB.2011.06.026
|
“Photocatalytic degradation of ethylene : an FTIR in situ study under atmospheric conditions”. Hauchecorne B, Tytgat T, Verbruggen SW, Hauchecorne D, Terrens D, Smits M, Vinken K, Lenaerts S, Applied catalysis : B : environmental 105, 111 (2011). http://doi.org/10.1016/J.APCATB.2011.03.041
Abstract: In this paper, the reaction mechanism of the photocatalytic oxidation of ethylene is elucidated by means of an in-house developed FTIR in situ reactor. This reactor allowed us to look at the catalytic surface at the moment the reactions actually occur. This new approach gave some exciting new insights in how ethylene is photocatalytically oxidised. It was found that there is a change in dipole moment of the ethylene molecule when it is brought in the neighbourhood of the catalyst. From this finding, a hypothesis was formulated on how the CC-bond from ethylene will break. It was found that the aforementioned interaction between the catalyst and the molecule, allows the excited electrons from the UV irradiated catalyst to occupy the lowest unoccupied molecular orbital (LUMO) of the ethylene molecule through a process known as backdonation. Following this hypothesis, it was found that the degradation occurs through the formation of two intermediates: formaldehyde and formic acid, for which formaldehyde is bound in two different ways (coordinatively and as bidentate). Finally CO2 and H2O are found as end products, resulting in the complete mineralisation of the pollutant.
Keywords: A1 Journal article; Engineering sciences. Technology; Molecular Spectroscopy (MolSpec); Sustainable Energy, Air and Water Technology (DuEL)
Impact Factor: 9.446
Times cited: 29
DOI: 10.1016/J.APCATB.2011.03.041
|
“Atomen tellen”. Van Aert S, Batenburg J, Van Tendeloo S, Nederlands tijdschrift voor natuurkunde (1991) 77, 292 (2011)
Keywords: A3 Journal article; Electron microscopy for materials research (EMAT); Vision lab
|
“Three-dimensional reconstruction of a nanoparticle at atomic resolution”. Batenburg J, Van Aert S, ERCIM news 86, 52 (2011)
Keywords: A2 Journal article; Electron microscopy for materials research (EMAT); Vision lab
|
“Stripping voltammetry of tinidazole in solubilized system and biological fluids”. Jain R, Rather JA, Colloids and surfaces: A: physicochemical and engineering aspects 378, 27 (2011). http://doi.org/10.1016/J.COLSURFA.2011.01.045
Abstract: The adsorptive voltammetric behaviour of tinidazole onto the HMDE was investigated and validated in solubilized system and biological fluids by CV, SWCAdSV and DPCAdSV. Addition of CTAB to the solution containing drug enhanced the peak current while anionic and non-ionic surfactants showed an opposite effect. The electrode process is irreversible and adsorption controlled. Various chemical and instrumental parameters affecting the monitored electroanalytical response were investigated and optimized for tinidazole determination. Under optimized conditions; the adsorptive stripping peak current is linear over the concentration range 7.0 × 10−9 to 6.2 × 10−7 mol/L with detection limit of 4.5 × 10−10 mol/L. The precision of the proposed method in terms of RSD is 1.2% and mean recovery of 100.01%. The applicability of proposed method is further extended to in vitro determination of the drug in biological fluids.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1016/J.COLSURFA.2011.01.045
|
“Voltammetric behaviour of drotaverine hydrochloride in surfactant media and its enhancement determination in Tween-20”. Jain R, Vikas, Rather JA, Colloids and surfaces: B : biointerfaces 82, 333 (2011). http://doi.org/10.1016/J.COLSURFB.2010.09.005
Abstract: Simple, sensitive and rapid adsorptive voltammetric behaviour of drotaverine hydrochloride onto the HMDE has been explored and validated in surfactant media by using cyclic, differential pulse and square-wave voltammetry. Addition of Tween-20 to the drotaverine hydrochloride containing electrolyte enhances the reduction current signal. The voltammograms of the drug with Tween-20 in phosphate buffers of pH 2.511.0 exhibit a single well defined reduction peak which may be due to the reduction of Cdouble bond; length as m-dashC group. The cyclic voltammetric studies indicated the reduction of drotaverine hydrochloride at the electrode surface through two electron irreversible step and diffusion-controlled. The peak current showed a linear dependence with the drug concentration over the range 0.87.2 μg mL−1. The calculated LOD and LOQ are 1.8 and 6.0 ng mL−1 by SWCAdSV and 8.1 and 27.2 ng mL−1 by DPCAdSV, respectively. The procedure was applied to the assay of the drug in tablet form with mean percentage recoveries of 100.2% with SWCAdSV and 99.7% with DPCAdSV. The validity of the proposed methods was further assessed by applying a standard addition technique.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1016/J.COLSURFB.2010.09.005
|
“Voltammetric determination of antibacterial drug gemifloxacin in solubilized systems at multi-walled carbon nanotubes modified glassy carbon electrode”. Jain R, Rather JA, Colloids and surfaces: B : biointerfaces 83, 340 (2011). http://doi.org/10.1016/J.COLSURFB.2010.12.003
Abstract: A sensitive electroanalytical method for determination of gemifloxacin in pharmaceutical formulation has been investigated on the basis of the enhanced electrochemical response at multi-walled carbon nanotubes modified glassy carbon electrode in the presence of CTAB. Solubilized system of different surfactants including SDS, Tween-20 and CTAB were taken for the study of electrochemical behaviour of gemifloxacin at modified electrode. The reduction peak current increases in the presence of CTAB while other surfactants show opposite effect. The modified electrode exhibits catalytic activity, high sensitivity, stability and is applicable over wide range of concentration for the determination of gemifloxacin. The mechanism of electrochemical reduction of gemifloxacin has been proposed on the basis of CV, SWV, DPV and coulometeric techniques. The proposed squarewave voltammetric method shows linearity over the concentration range 2.4715.5 μg/mL. The achieved limits of detection (LOD) and quantification (LOQ) are 0.90 ng/mL and 3.0 ng/mL respectively.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1016/J.COLSURFB.2010.12.003
|
“Voltammetric behaviour of nitroxazepine in solubilized system and biological fluids”. Jain R, Rather JA, Dwivedi A, Materials science and engineering: part C: biomimetic materials 31, 230 (2011). http://doi.org/10.1016/J.MSEC.2010.09.001
Abstract: This study reports the development and validation of sensitive and selective assay method for the determination of the antidepressant drug in solubilized system and biological fluids. Solubilized system of different surfactants including cationic, anionic and non-ionic influences the electrochemical response of drug. Addition of cationic surfactant cetrimide to the solution containing drug enhances the peak current signal while anionic and non-ionic showed an opposite effect. The current signal due to reduction process was function of concentration of nitroxazepine, pH, type of surfactant and preconcentration time at the electrode surface. The reduction process is irreversible and adsorption controlled at HMDE. Various chemical and instrumental parameters affecting the monitored electroanalytical response were investigated and optimized for niroxazepine hydrochloride determination. The proposed SWCAdSV and DPCAdSV methods are linear over the concentration range 2.0 × 10-7 5.0 × 10-9 mol/L and 6.1 × 10-7 1.0 × 10-8 mol/L with detection limit of 1.62 × 10-10 mo/L and 1.4 × 10-9 mo/L respectively. The method shows good sensitivity, selectivity, accuracy and precision that makes it very suitable for determination of nitroxazepine in pharmaceutical formulation and biological fluids.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1016/J.MSEC.2010.09.001
|
“Ultrahigh strain hardening in thin palladium films with nanoscale twins”. Idrissi H, Wang B, Colla MS, Raskin JP, Schryvers D, Pardoen T, Advanced materials 23, 2119 (2011). http://doi.org/10.1002/adma.201004160
Abstract: Nanocrystalline Pd thin films containing coherent growth twin boundaries are deformed using on-chip nanomechanical testing. A large work-hardening capacity is measured. The origin of the observed behavior is unraveled using transmission electron microscopy and shows specific dislocations and twin boundaries interactions. The results indicate the potential for large strength and ductility balance enhancement in Pd films, as needed in membranes for H technologies.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 19.791
Times cited: 57
DOI: 10.1002/adma.201004160
|
“Semiclathrates of the GePTe system : synthesis and crystal structures”. Kirsanova MA, Reshetova LN, Olenev AV, Abakumov AM, Shevelkov AV, Chemistry: a European journal 17, 5719 (2011). http://doi.org/10.1002/chem.201003553
Abstract: Novel compounds [Ge46−xPx]Tey (13.9≤x≤15.6, 5.92≤y≤7.75) with clathrate-like structures have been prepared and structurally characterized. They crystallize in the space group Fmequation image with the unit cell parameter changing from 20.544(2) to 20.698(2) Å (Z=8) on going from x=13.9 to x=15.6. Their crystal structure is composed of a covalently bonded Ge[BOND]P framework that hosts tellurium atoms in the guest positions and can be viewed as a peculiar variant of the type I clathrate superstructure. In contrast to the conventional type I clathrates, [Ge46−xPx]Tey contain tricoordinated (3b) atoms and no vacancies in the framework positions. As a consequence of the transformation of the framework, the majority of the guest tellurium atoms form a single covalent bond with the host framework and thus the title compounds are the first representative of semiclathrates with covalent bonding. A comparison is made with silicon clathrates and the evolution of the crystal structure upon changing the tellurium content is discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.317
Times cited: 17
DOI: 10.1002/chem.201003553
|
“Titanosilicate beads with hierarchical porosity : synthesis and application as epoxidation catalysts”. Lin K, Lebedev OI, Van Tendeloo G, Jacobs PA, Pescarmona PP, Chemistry: a European journal 16, 13509 (2011). http://doi.org/10.1002/chem.201001508
Abstract: Porous titanosilicate beads with a diameter of 0.51.5 mm (TiSil-HPB-60) were synthesized from a preformed titanosilicate solution with a porous anion-exchange resin as template. The bead format of this material enables its straightforward separation from the reaction mixture in its application as a liquid-phase heterogeneous catalyst. The material displays hierarchical porosity (micro/mesopores) and incipient TS-1 structure building units. The titanium species are predominantly located in tetrahedral framework positions. TiSil-HPB-60 is a highly active catalyst for the epoxidation of cyclohexene with t-butyl hydroperoxide (TBHP) and aqueous H2O2. With both oxidants, TiSil-HPB-60 gave higher epoxide yields than Ti-MCM-41 and TS-1. The improved catalytic performance of TiSil-HPB-60 is mainly ascribed to the large mesopores favoring the diffusion of reagents and products to and from the titanium active sites. The epoxide yield and selectivity could be further improved by silylation of the titanosilicate beads. Importantly, TiSil-HPB-60 is a stable catalyst immune to titanium leaching, and can be easily recovered and reused in successive catalytic cycles without significant loss of activity. Moreover, TiSil-HPB-60 is active and selective in the epoxidation of a wide range of bulky alkenes.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.317
Times cited: 38
DOI: 10.1002/chem.201001508
|
“Well-organized zeolite nanocrystal aggregates with interconnected hierarchically micro-meso-macropore systems showing enhanced catalytic performance”. Yang X-Y, Tian G, Chen L-H, Li Y, Rooke JC, Wei Y-X, Liu Z-M, Deng Z, Van Tendeloo G, Su B-L, Chemistry: a European journal 17, 14987 (2011). http://doi.org/10.1002/chem.201101594
Abstract: Preparation and characterization of well-organized zeolitic nanocrystal aggregates with an interconnected hierarchically micromesomacro porous system are described. Amorphous nanoparticles in bimodal aluminosilicates were directly transformed into highly crystalline nanosized zeolites, as well as acting as scaffold template. All pores on three length scales incorporated in one solid body are interconnected with each other. These zeolitic nanocrystal aggregates with hierarchically micromesomacroporous structure were thoroughly characterized. TEM images and 29Si NMR spectra showed that the amorphous phase of the initial material had been completely replaced by nanocrystals to give a micromesomacroporous crystalline zeolitic structure. Catalytic testing demonstrated their superiority due to the highly active sites and the presence of interconnected micromesomacroporosity in the cracking of bulky 1,3,5-triisopropylbenzene (TIPB) compared to traditional zeolite catalysts. This synthesis strategy was extended to prepare various zeolitic nanocrystal aggregates (ZSM-5, Beta, TS-1, etc.) with well-organized hierarchical micromesomacroporous structures.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 5.317
Times cited: 61
DOI: 10.1002/chem.201101594
|
“Chemical composition of building materials used in Turkey”. Čevik U, Damla N, Van Grieken R, Vefa Akpinar M, Construction and building materials 25, 1546 (2011). http://doi.org/10.1016/J.CONBUILDMAT.2010.08.011
Abstract: The main goal of this work was to determine the chemical composition of building materials used in Turkey by utilizing energy dispersive X-ray fluorescence (EDXRF) spectrometry. Gas concrete, cement, sand, bricks, roofing tiles, marble, lime and gypsum materials were selected as building materials for this research. The chemical contents and their trace concentrations of the selected samples were determined. The most abundant oxides measured were generally SiO2, Al2O3, CaO, MgO, Fe2O3, K2O and SO3 for all samples. While the main chemical component of gas concrete, cement, sand and marble samples were SiO2 and CaO, brick and roofing tile mainly consisted of SiO2 and Al2O3. CaO and SO3 were major component of lime and gypsum samples, respectively. For U and Th concentrations in the samples, activities of 226Ra and 232Th were measured by utilizing gamma spectrometry. ANOVA and Pearson correlation analyses were performed on the studied data for statistical analysis.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1016/J.CONBUILDMAT.2010.08.011
|
“Barrier efficiency of sponge-like La2Zr2O7 buffer layers for YBCO-coated conductors”. Molina L, Tan H, Biermans E, Batenburg KJ, Verbeeck J, Bals S, Van Tendeloo G, Superconductor science and technology 24, 065019 (2011). http://doi.org/10.1088/0953-2048/24/6/065019
Abstract: Solution derived La2Zr2O7 films have drawn much attention for potential applications as thermal barriers or low-cost buffer layers for coated conductor technology. Annealing and coating parameters strongly affect the microstructure of La2Zr2O7, but different film processing methods can yield similar microstructural features such as nanovoids and nanometer-sized La2Zr2O7 grains. Nanoporosity is a typical feature found in such films and the implications for the functionality of the films are investigated by a combination of scanning transmission electron microscopy (STEM), electron energy-loss spectroscopy (EELS) and quantitative electron tomography. Chemical solution based La2Zr2O7 films deposited on flexible Ni5 at.%W substrates with a {100}lang001rang biaxial texture were prepared for an in-depth characterization. A sponge-like structure composed of nanometer-sized voids is revealed by high-angle annular dark-field scanning transmission electron microscopy in combination with electron tomography. A three-dimensional quantification of nanovoids in the La2Zr2O7 film is obtained on a local scale. Mostly non-interconnected highly faceted nanovoids compromise more than one-fifth of the investigated sample volume. The diffusion barrier efficiency of a 170 nm thick La2Zr2O7 film is investigated by STEM-EELS, yielding a 1.8 ± 0.2 nm oxide layer beyond which no significant nickel diffusion can be detected and intermixing is observed. This is of particular significance for the functionality of YBa2Cu3O7 − δ coated conductor architectures based on solution derived La2Zr2O7 films as diffusion barriers.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 2.878
Times cited: 31
DOI: 10.1088/0953-2048/24/6/065019
|
“The guidance of vortex-antivortex pairs by in-plane magnetic dipoles in a superconducting finite-size film”. Kapra AV, Misko VR, Vodolazov DY, Peeters FM, Superconductor science and technology 24, 024014 (2011). http://doi.org/10.1088/0953-2048/24/2/024014
Abstract: The possibility of manipulating vortex matter by using various artificial pinning arrays is of significant importance for possible applications in nano and micro fluxonics devices. By numerically solving the time-dependent GinzburgLandau equations, we study the vortexantivortex (vav) dynamics in a hybrid structure consisting of a finite-size superconductor with magnetic dipoles on top which generate vav pairs in the presence of an external current. The vav dynamics is analyzed for different arrangements and magnetic moments of the dipoles, as a function of angle α between the direction of the magnetic dipole and that of the Lorentz force produced by the applied current. The interplay of the attractive interaction between a vav pair and the Lorentz force leads either to the separation of (anti)vortices and their motion in opposite directions or to their annihilation. We found a critical angle αc, below which vortices and antivortices are repelled, while for larger angles they annihilate. In case of a single (few) magnetic dipole(s), this magnetic dipole induced vav guidance is influenced by the self-interaction of the vav pairs with their images in a finite-size sample, while for a periodic array of dipoles the guidance is determined by the interaction of a vav pair with other dipoles and vav pairs created by them. This effect is tunable through the external current and the magnetization and size of the magnetic dipoles.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 2.878
Times cited: 28
DOI: 10.1088/0953-2048/24/2/024014
|
“Vortex manipulation in superconducting films with tunable magnetic topology”. Milošević, MV, Peeters FM, Jankó, B, Superconductor science and technology 24, 024001 (2011). http://doi.org/10.1088/0953-2048/24/2/024001
Abstract: Using a combination of the phenomenological GinzburgLandau theory and micromagnetic simulations, we study properties of a superconducting film with an array of soft magnetic dots on top. An external in-plane magnetic field gradually drives the magnets from an out-of-plane or magnetic vortex state to an in-plane single-domain state, which changes spatially the distribution of the superconducting condensate. If induced by the magnets, the vortexantivortex molecules exhibit rich transitions as a function of the applied in-plane field. At the same time, we show how the magnetic dots act as very effective dynamic pinning centers for vortices in an applied perpendicular magnetic field.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 2.878
Times cited: 8
DOI: 10.1088/0953-2048/24/2/024001
|
“Buckled circular monolayer graphene : a graphene nano-bowl”. Neek-Amal M, Peeters FM, Journal of physics : condensed matter 23, 045002 (2011). http://doi.org/10.1088/0953-8984/23/4/045002
Abstract: We investigate the stability of circular monolayer graphene subjected to a radial load using non-equilibrium molecular dynamics simulations. When monolayer graphene is radially stressed, after some small circular strain (~0.4%) it buckles and bends into a new bowl-like shape. Young's modulus is calculated from the linear relation between stress and strain before the buckling threshold, which is in agreement with experimental results. The prediction of elasticity theory for the buckling threshold of a radially stressed plate is presented and its results are compared to the one of our atomistic simulation. The Jarzynski equality is used to estimate the difference between the free energy of the non-compressed states and the buckled states. From a calculation of the free energy we obtain the optimum radius for which the system feels the minimum boundary stress.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 2.649
Times cited: 27
DOI: 10.1088/0953-8984/23/4/045002
|
“Graphene in inhomogeneous magnetic fields : bound, quasi-bound and scattering states”. Masir MR, Vasilopoulos P, Peeters FM, Journal of physics : condensed matter 23, 315301 (2011). http://doi.org/10.1088/0953-8984/23/31/315301
Abstract: The electron states in graphene-based magnetic dot and magnetic ring structures and combinations of both are investigated. The corresponding spectra are studied as a function of the radii, the strengths of the inhomogeneous magnetic field and of a uniform background field, the strength of an electrostatic barrier and the angular momentum quantum number. In the absence of an external magnetic field we have only long-lived quasi-bound and scattering states and we assess their influence on the density of states. In addition, we consider elastic electron scattering by a magnetic dot, whose average B vanishes, and show that the Hall and longitudinal resistivities, as a function of the Fermi energy, exhibit a pronounced oscillatory structure due to the presence of quasi-bound states. Depending on the dot parameters this oscillatory structure differs substantially for energies below and above the first Landau level.
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 2.649
Times cited: 38
DOI: 10.1088/0953-8984/23/31/315301
|