“The fine structure of YCuO2+x delafossite determined by synchrotron powder diffraction and electron microscopy”. Van Tendeloo G, Garlea O, Darie C, Bougerol-Chaillout C, Bordet P, Journal of solid state chemistry 156, 428 (2001). http://doi.org/10.1006/jssc.2000.9018
Abstract: YCuO2 delafossite crystallizes into two stacking variants; hexagonal 2H or rhombohedral 3R, depending on the preparation conditions. The structure of the fully oxygenated material YCuO2.50 has been determined as orthorhombic (a(O) = 6.1961 Angstrom; b(O) = 11.2158 Angstrom; c(O) = 7.1505 Angstrom; space group Pnma). The structure is based on the hexagonal 2H structure (a(O) = a(H)root3; b(O) = c(H); c(O) = 2a(H)). Upon incomplete oxidation, a different YCuOZ phase with ideal composition YCuO2.33 and lattice parameters a(H root)3, a(H)root3, c(H) is also formed. Diffraction patterns are often very complex because of the presence of planar defects and intergrowth of both phases. Under electron beam irradiation, oxygen is released from the structure and one phase gradually transforms into the other. (C) 2001 Academic Press.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 33
DOI: 10.1006/jssc.2000.9018
|
|
|
“The interplay of microstructure and magnetism in La3Ni2SbO9”. Battle PD, Avdeev M, Hadermann J, Journal of solid state chemistry 220, 163 (2014). http://doi.org/10.1016/j.jssc.2014.08.024
Abstract: La3Ni2SbO9 adopts a perovskite-related structure in which the six-coordinate cation sites are occupied alternately by Ni2+ and a disordered arrangement of Ni2+/Sb5+. A polycrystalline sample has been studied by neutron diffraction in applied magnetic fields of 0 <= H/kOe <= 50 at 5 K. In 0 kOe, weak magnetic Bragg scattering consistent with the adoption of a G-type ferrimagnetic structure is observed; the ordered component of the magnetic moment was found to be 0.89(7) mu(B) per Ni2+ cation. This increased to 1.60(3) mu(B) in a field of 50 kOe. Transmission electron microscopy revealed variations in the Ni:Sb ratio across crystallites of the sample. It is proposed that these composition variations disrupt the magnetic superexchange interactions within the compound, leading to domain formation and a reduced average moment. The application of a magnetic field aligns the magnetisation vectors across the crystal and the average moment measured by neutron diffraction increases accordingly. The role played by variations in the local chemical composition in determining the magnetic properties invites comparison with the behaviour of relaxor ferroelectrics. (C) 2014 Elsevier Inc. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 13
DOI: 10.1016/j.jssc.2014.08.024
|
|
|
“The modulated structure of Ca.85CuO2 as studied by means of electron diffraction and microscopy”. Milat O, Van Tendeloo G, Amelinckx S, Babu TGN, Greaves C, Journal of solid state chemistry 97, 405 (1992). http://doi.org/10.1016/0022-4596(92)90050-6
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.133
Times cited: 15
DOI: 10.1016/0022-4596(92)90050-6
|
|
|
“The synthesis and complex anion-vacancy ordered structure of La0.33Sr0.67MnO2.42”. Dixon E, Hadermann J, Hayward MA, Journal of solid state chemistry 184, 1791 (2011). http://doi.org/10.1016/j.jssc.2011.05.026
Abstract: The low-temperature topotactic reduction of La0.33Sr0.67MnO3 with NaH results in the formation of La0.33Sr0.67MnO2.42. A combination of neutron powder and electron diffraction data show that La0.33Sr0.67MnO2.42 adopts a novel anion-vacancy ordered structure with a 6-layer OOTOOT' stacking sequence of the octahedral and tetrahedral layers (Pcmb, a=5.5804(1) Å, b=23.4104(7) Å, c=11.2441(3) Å). A significant concentration of anion vacancies at the anion site, which links neighbouring octahedral layers means that only 25% of the octahedral manganese coordination sites actually have 6-fold MnO6 coordination, the remainder being MnO5 square-based pyramidal sites. The chains of cooperatively twisted apex-linked MnO4 tetrahedra adopt an ordered -LRLR- arrangement within each tetrahedral layer. This is the first published example of a fully refined structure of this type which exhibits such intralayer ordering of the twisted tetrahedral chains. The rationale behind the contrasting structures of La0.33Sr0.67MnO2.42 and other previously reported reduced La1−xSrxMnO3−y phases is discussed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.299
Times cited: 8
DOI: 10.1016/j.jssc.2011.05.026
|
|
|
“A case study of ship track formation in a polluted marine boundary layer”. Noone KJ, Johnson DW, Taylor JP, Ferek RJ, Garrett T, Hobbs PV, Durkee PA, Nielsen K, Öström E, O'Dowd CD, Smith MH, Russell LM, Flagan RC, Seinfeld JH, de Bock L, Van Grieken RE, Hudson JG, Brooks I, Gasparovic RF, Pockalny RA, Journal of the atmospheric sciences 57, 2748 (2000). http://doi.org/10.1175/1520-0469(2000)057<2748:ACSOST>2.0.CO;2
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1175/1520-0469(2000)057<2748:ACSOST>2.0.CO;2
|
|
|
“A case study of ships forming and not forming tracks in moderately polluted clouds”. Noone KJ, Öström E, Ferek RJ, Garrett T, Hobbs PV, Johnson DW, Taylor JP, Russell LM, Flagan RC, Seinfeld JH, O'Dowd CD, Smith MH, Durkee PA, Nielsen K, Hudson JG, Pockalny RA, de Bock L, Van Grieken RE, Gasparovic RF, Brooks I, Journal of the atmospheric sciences 57, 2729 (2000). http://doi.org/10.1175/1520-0469(2000)057<2729:ACSOSF>2.0.CO;2
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1175/1520-0469(2000)057<2729:ACSOSF>2.0.CO;2
|
|
|
“An electron microscopic study of highly oriented undoped and FeCl3-doped poly (p-phenylenevinylene)”. Zhang XB, Van Tendeloo G, van Landuyt J, van Dyck D, Briers J, Bao Y, Geise HJ, Macromolecules 29, 1554 (1996). http://doi.org/10.1021/ma9513067
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Vision lab
Impact Factor: 5.8
Times cited: 10
DOI: 10.1021/ma9513067
|
|
|
“Distribution of atmospheric marine salt depositions over Continental Western Europe”. Delalieux F, Van Grieken R, Potgieter JH, Marine pollution bulletin 52, 606 (2006). http://doi.org/10.1016/J.MARPOLBUL.2005.08.018
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1016/J.MARPOLBUL.2005.08.018
|
|
|
“Heavy metal contamination in sediments from the Belgian coast and Scheldt estuary”. Araújo MFD, Bernard PC, Van Grieken RE, Marine pollution bulletin 19, 269 (1988). http://doi.org/10.1016/0025-326X(88)90597-8
Abstract: Sixty-two samples of total sediments and the separated clay/silt size fractions were analysed by energy-dispersive X-ray fluorescence spectrometry to evaluate the pollution level and the trends in samples collected along the Belgian coast over a period of 6 yr and at four stations located in the Scheldt estuary where two of these were sampled periodically for 4 yr. Three correction methods for grain size effects were applied, either to the bulk sediment samples or to the clay/silt size fractions, and the results were compared. Local variations on the concentrations in some of the elements determined were used to establish whether they result from an anthropogenic or natural origin. The level of pollution was assessed as a function of the location, sampling date, and depth.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1016/0025-326X(88)90597-8
|
|
|
“Heavy metals in the Ganges estuary”. Subramanian V, Jha PK, Van Grieken R, Marine pollution bulletin 19, 290 (1988). http://doi.org/10.1016/0025-326X(88)90602-9
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
DOI: 10.1016/0025-326X(88)90602-9
|
|
|
“Electron microscopy and diffraction study of the composition dependency of the 3R microtwinned martensite in Ni-Al”. Schryvers D, de Saegher B, van Landuyt J, Materials research bulletin 26, 57 (1991)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.288
Times cited: 11
|
|
|
“Doping of Bi4Fe5O13F with pentagonal Cairo lattice with Cr and Mn: Synthesis, structure and magnetic properties”. Rozova MG, Grigoriev VV, Tyablikov OA, Filimonov DS, Zakharov KV, Volkova OS, Vasiliev AN, Antipov EV, Abakumov AM, Materials research bulletin 87, 54 (2017). http://doi.org/10.1016/J.MATERRESBULL.2016.11.018
Abstract: The substitution of Cr3+ and Mn3+ for Fe3+ in the Bi4Fe6O13F oxyfluoride featuring the magnetically frustrated pentagonal Cairo lattice is reported. Bi4Fe4.1Cr0.9O13F and BiFe4.2Mn0.8O13F have been prepared using a solid state reaction in inert atmosphere. Their crystal structures were studied with transmission electron microscopy, powder X-ray diffraction and Fe-57 Mossbauer spectroscopy (S.G. P4(2)/mbc, a = 8.27836(2)angstrom, c = 18.00330(9) angstrom, R-F = 0.031 (Bi4Fe4.1Cr0.9O13F)), a= 8.29535(3)angstrom, c= 18.0060(1)angstrom, R-F = 0.027 (Bi4Fe4.1Cr0.9O13F)). The structures are formed by infinite rutile-like chains of the edge sharing BO6 octahedra (B transition metal cations) linked by the Fe2O7 groups of two corner-sharing tetrahedra. The"voids in thus formed framework are occupied by the Bi4F tetrahedra. The Fe-57 Mossbauer spectroscopy reveals that Cr3+ and Mn3+ replace Fe3+. exclusively at the octahedral positions. The Mn- and Cr-doped compounds demonstrate antiferromagnetic ordering below T-N =165 K and 120 K, respectively. (C) 2016 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 1
DOI: 10.1016/J.MATERRESBULL.2016.11.018
|
|
|
“Crystal structure and magnetic properties of the Cr-doped spiral antiferromagnet BiMnFe2O6”. Batuk D, de Dobbelaere C, Tsirlin AA, Abakumov AM, Hardy A, van Bael MK, Greenblatt M, Hadermann J, Materials research bulletin 48, 2993 (2013). http://doi.org/10.1016/j.materresbull.2013.04.038
Abstract: We report the Cr3+ for Mn3+ substitution in the BiMnFe2O6 structure. The BiCrxMn1-xFe2O6 solid solution is obtained by the solution-gel synthesis technique for the x values up to 0.3. The crystal structure investigation using a combination of X-ray powder diffraction and transmission electron microscopy demonstrates that the compounds retain the parent BiMnFe2O6 structure (for x = 0.3, a = 5.02010(6)angstrom, b = 7.06594(7)angstrom, c = 12.6174(1)angstrom, S.G. Pbcm, R-1 = 0.036, R-p = 0.011) with only a slight decrease in the cell parameters associated with the Cr3+ for Mn3+ substitution. Magnetic susceptibility measurements suggest strong similarities in the magnetic behavior of BiCrxMn1-xFe2O6 (x = 0.2; 0.3) and parent BiMnFe2O6. Only T-N slightly decreases upon Cr doping that indicates a very subtle influence of Cr3+ cations on the magnetic properties at the available substitution rates. (C) 2013 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 3
DOI: 10.1016/j.materresbull.2013.04.038
|
|
|
“Crystal structure and properties of the new complex vanadium oxide K2SrV3O9”. Tsirlin AA, Chernaya VV, Shpanchenko RV, Antipov EV, Hadermann J, Materials research bulletin 40, 800 (2005). http://doi.org/10.1016/j.materresbull.2005.02.004
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 9
DOI: 10.1016/j.materresbull.2005.02.004
|
|
|
“Crystal structures of superconducting sodium intercalates of hafnium nitride chloride”. Oró-Solé, J, Frontera C, Beltrán-Porter D, Lebedev OI, Van Tendeloo G, Fuertes A, Materials research bulletin 41, 934 (2006). http://doi.org/10.1016/j.materresbull.2006.03.018
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 8
DOI: 10.1016/j.materresbull.2006.03.018
|
|
|
“Fluorine intercalation in the n=1 and n=2 layered manganites Sr2MnO3.5+x and Sr3Mn2O6”. Sullivan E, Gillie LJ, Hadermann J, Greaves C, Materials research bulletin 48, 1598 (2013). http://doi.org/10.1016/j.materresbull.2012.12.073
Abstract: Fluorine insertion into the oxygen defect superstructure manganite Sr2MnO3.5+x has been shown by transmission electron microscopy (TEM) to result in two levels of fluorination. In the higher fluorine content sections, the fluorine anions displace oxygen anions from their apical positions into the equatorial vacancies, thus destroying the superstructure and reverting to a K2NiF4-type structure (a = 3.8210(1) angstrom and c = 12.686(1) angstrom). Conversely, lower fluorine content sections retain the Sr2MnO3.5+x defect superstructure, crystallising in the P2(1)/c space group. Fluorine intercalation into the reduced double-layer manganite Sr3Mn2O6 occurs in a step-wise fashion according to the general formula Sr3Mn2O6Fy with y = 1, 2, and 3. It is proposed that the y = 1 phase (a = 3.815(1)angstrom, c = 20.29(2) angstrom) is produced by the filling of all the equatorial oxygen vacancies by fluorine atoms whilst the y = 2 phase (a = 3.8222(2) angstrom, c = 21.2435(3)angstrom) has a random distribution of fluorine anions throughout both interstitial rocksalt and equatorial sites. Neutron powder diffraction data suggest that the fully fluorinated y = 3 phase (a = 3.8157(6) angstrom, c = 23.666(4) angstrom) corresponds to the complete occupation of all the equatorial oxygen vacancies and the interstitial sites by intercalated fluorine. (C) 2013 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 4
DOI: 10.1016/j.materresbull.2012.12.073
|
|
|
“Fluorite-like phases in the BaF2-BiF3-Bi2O3 system-synthesis, conductivity and defect clustering”. Serov TV, Dombrovski EN, Ardashnikova EI, Dolgikh VA, el Omari M, el Omari M, Abaouz A, Senegas J, Chaban NG, Abakumov AM, Van Tendeloo G, Materials research bulletin 40, 821 (2005). http://doi.org/10.1016/j.materresbull.2005.02.007
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 4
DOI: 10.1016/j.materresbull.2005.02.007
|
|
|
“Influence of laser and isothermal treatments on microstructural properties of SnO2 films”. Rembeza ES, Richard O, van Landuyt J, Materials research bulletin 34, 1527 (1999). http://doi.org/10.1016/S0025-5408(99)00188-9
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 17
DOI: 10.1016/S0025-5408(99)00188-9
|
|
|
“New lead vanadium phosphate with langbeinite-type structure: Pb1.5V2(PO4)3”. Shpanchenko RV, Lapshina OA, Antipov EV, Hadermann J, Kaul EE, Geibel C, Materials research bulletin 40, 1569 (2005). http://doi.org/10.1016/j.materresbull.2005.04.037
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 14
DOI: 10.1016/j.materresbull.2005.04.037
|
|
|
“Properties and thermal stability of solution processed ultrathin, high-k bismuth titanate (Bi2Ti2O7) films”. Hardy A, Van Elshocht S, De Dobbelaere C, Hadermann J, Pourtois G, De Gendt S, Afanas'ev VV, Van Bael MK, Materials research bulletin 47, 511 (2012). http://doi.org/10.1016/j.materresbull.2012.01.001
Abstract: Ultrathin bismuth titanate films (Bi2Ti2O7, 5-25 nm) are deposited onto SiO2/Si substrates by aqueous chemical solution deposition and their evolution during annealing is studied. The films crystallize into a preferentially oriented, pure pyrochlore phase between 500 and 700 degrees C, depending on the film thickness and the total thermal budget. Crystallization causes a strong increase of surface roughness compared to amorphous films. An increase of the interfacial layer thickness is observed after anneal at 600 degrees C, together with intermixing of bismuth with the substrate as shown by TEM-EDX. The band gap was determined to be similar to 3 eV from photoconductivity measurements and high dielectric constants between 30 and 130 were determined from capacitance voltage measurements, depending on the processing conditions. (C) 2012 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 2.446
DOI: 10.1016/j.materresbull.2012.01.001
|
|
|
“Structural phase transition at low temperature, corresponding to charge ordering in the CMR perovskites LN0.5A0.5MNO3”. Laffez P, Van Tendeloo G, Millange F, Caignaert V, Hervieu M, Raveau B, Materials research bulletin 31, 905 (1996). http://doi.org/10.1016/S0025-5408(96)00090-6
Abstract: The magneto resistive perovskites Nd0.5Sr0.5MnO3 and Pr0.5Sr0.41Ca0.09MnO3 undergo a transition from anti ferromagnetic insulator to ferromagnetic metal as function of temperature. The room temperature phase is orthorhombic with the space group Imma and the cell parameters a approximate to root 2a(p), b approximate to 2a(p), and c approximate to root 2a(p). A structural phase transition related to charge ordering accompanying the transition from ferromagnetic state to antiferromagnetic state has been evidenced by low temperature electron diffraction. This transition is reversible and a new superstructure, with a P-type orthorhombic cell. and lattice parameters parameters a approximate to 2 root 2a(p), b approximate to 2a(p), and c approximate to root 2a(p), is formed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.288
Times cited: 25
DOI: 10.1016/S0025-5408(96)00090-6
|
|
|
“Structure and magnetic properties of a new anion-deficient perovskite Pb2Ba2BiFe4ScO13 with crystallographic shear structure”. Batuk M, Tyablikov OA, Tsirlin AA, Kazakov SM, Rozova MG, Pokholok KV, Filimonov DS, Antipov EV, Abakumov AM, Hadermann J, Materials research bulletin 48, 3459 (2013). http://doi.org/10.1016/j.materresbull.2013.05.028
Abstract: Pb2Ba2BiFe4ScO13, a new n = 5 member of the oxygen-deficient perovskite-based A(n)B(n)O(3n-2) homologous series, was synthesized using a solid-state method. The crystal structure of Pb2Ba2BiFe4ScO13 was investigated by a combination of synchrotron X-ray powder diffraction, electron diffraction, high-angle annular dark-field scanning transmission electron microscopy and Mossbauer spectroscopy. At 900 K, it crystallizes in the Ammm space group with the unit cell parameters a = 5.8459(1) angstrom, b = 4.0426(1) angstrom, and c=27.3435(1) angstrom. In the Pb2Ba2BiFe4ScO13 structure, quasi-two-dimensional perovskite blocks are periodically interleaved with 1/2[1 1 0] ((1) over bar 0 1)(p) crystallographic shear (CS) planes. At the CS planes, the corner-sharing FeO6 octahedra are transformed into chains of edge-sharing FeO5 distorted tetragonal pyramids. B-positions of the perovskite blocks between the CS planes are jointly occupied by Fe3+ and Sc3+. The chains of the FeO5 pyramids and (Fe,Sc)O-6 octahedra delimit six-sided tunnels that are occupied by double columns of cations with a lone electron pair (Pb2+). The remaining A-cations (Bi3+, Ba2+) occupy positions in the perovskite block. According to the magnetic susceptibility measurements, Pb2Ba2BiFe4ScO13 is antiferromagnetically ordered below T-N approximate to 350 K. (C) 2013 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 2
DOI: 10.1016/j.materresbull.2013.05.028
|
|
|
“Structure of the hexagonal 16l perovskites Ba4Ca0.9Mn3.1O11.3 and Ba4Ca0.5Mn3Cu0.5O12-\delta by high-resolution electron microscopy”. Schuddinck W, Van Tendeloo G, Hervieu M, Floros N, Raveau B, Materials research bulletin 36, 2689 (2001). http://doi.org/10.1016/S0025-5408(01)00744-9
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 4
DOI: 10.1016/S0025-5408(01)00744-9
|
|
|
“TEM study of laser induced phase transition in iron thin films”. Teodorescu VS, Nistor LC, van Landuyt J, Dinescu M, Materials research bulletin 29, 63 (1994). http://doi.org/10.1016/0025-5408(94)90106-6
Abstract: Laser induced phase transition from b.c.c.(alpha) to f.c.c.(gamma) iron thin films is studied by high resolution TEM. The iron film has been covered on both sides with carbon layers to protect it against oxidation. Single pulse, tau FWHM = 20ns KrF (lambda = 248nm) excimer laser irradiation was performed in air with the film on the substrate. The laser pulse acts like a heat pulse followed by a rapid quenching revealing sequential aspects of the phase transition process. The presence of a fine mixture of the alpha + gamma phases between the alpha and gamma regions of the film has been interpreted as an incomplet transformation. The results are explained by assuming that the transformation took place via a phonon drag mechanism.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.288
Times cited: 2
DOI: 10.1016/0025-5408(94)90106-6
|
|
|
“:Ba2.1Bi0.9(O, F)6.8-\delta: a new ordered anion-excess fluorite”. Prituzhalov VA, Abakumov AM, Ardashnikova EI, Dolgikh VA, Van Tendeloo G, Materials research bulletin 42, 861 (2007). http://doi.org/10.1016/j.materresbull.2006.08.023
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.446
Times cited: 4
DOI: 10.1016/j.materresbull.2006.08.023
|
|
|
“Some examples of electron microscopy studies of microstructures and phase transitions in solids”. Schryvers D, Van Tendeloo G, van Landuyt J, Amelinckx S, Meccanica 30, 433 (1995). http://doi.org/10.1007/BF01557075
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.949
Times cited: 1
DOI: 10.1007/BF01557075
|
|
|
“Air quality monitoring in a museum for preventive conservation : results of a three-year study in the Plantin-Moretus Museum in Antwerp, Belgium”. Krupińska B, Van Grieken R, De Wael K, Microchemical journal 110, 350 (2013). http://doi.org/10.1016/J.MICROC.2013.05.006
Abstract: Through different research projects on air quality in museums, researcher and conservators try identifying various risks of air pollution on materials. The conclusions may be later translated into specific actions for a maximum preservation of the museum collections, a process known as preventive conservation. Air pollution is a particular problem in historical buildings such as museums, because they were not originally built to exhibit and protect art objects in a sustainable way. This article reports on the data and results that were obtained during 10 sampling campaigns, in the period between November 2008 and February 2012 in a museum in Antwerp (Belgium), i.e. Plantin-Moretus Museum/Print Room. Different pollutants were measured inside and outside the museum such as inorganic gases, particulate matter and black carbon. The report specifically addresses environmental factors that may be responsible for damage to the collections present in museums. Thanks to the knowledge about the current situation in the museum, accurate solutions regarding preventive conservation, in general, are suggested.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.034
Times cited: 46
DOI: 10.1016/J.MICROC.2013.05.006
|
|
|
“Assessing the stability of arsenic sulfide pigments and influence of the binding media on their degradation by means of spectroscopic and electrochemical techniques”. Vermeulen M, Janssens K, Sanyova J, Rahemi V, McGlinchey C, De Wael K, Microchemical journal 138, 82 (2018). http://doi.org/10.1016/J.MICROC.2018.01.004
Abstract: In this paper, we used the semiconducting and lightfastness properties of synthetic and mineral arsenic sulfide pigments to study their stability by means of electrochemical and microfadometric techniques. A combination of these techniques shows that in the early stage of the degradation process, amorphous arsenic sulfides are more stable than both crystalline forms, while upon longer exposure time, amorphous pigments will fade more than both mineral pigments, making it less suitable. While the stability study was carried out on unbound pigments, the influence of the organic binder on the relative degradation of the arsenic sulfide pigments was investigated through a multi-analytical approach on pigment/binder mock-up paint samples. For this purpose, the formation of arsenic trioxide was assessed by micro Fourier transform infrared (μ-FTIR) spectroscopy while the influence of the binder on the formation of sulfates was studied by means of synchrotron radiation X-ray near edge structure (μ-XANES). Both techniques elucidate a higher stability of all pigments in gum arabic while the use of egg yolk as binder leads to the most degradation, most likely due to its sulfur-rich composition. In the context of the degradation of arsenic sulfide pigments, other binders such as animal glue, egg white or linseed oil show an intermediate impact.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation)
Impact Factor: 3.034
Times cited: 4
DOI: 10.1016/J.MICROC.2018.01.004
|
|
|
“Assessment of the air quality (NO2, SO2, O3 and particulate matter) in the Plantin-Moretus Museum/Print Room in Antwerp, Belgium, in different seasons of the year”. Krupińska B, Worobiec A, Rotondo GG, Novaković, V, Kontozova V, Ro C-U, Van Grieken R, De Wael K, Microchemical journal 102, 49 (2012). http://doi.org/10.1016/J.MICROC.2011.11.008
Abstract: The Plantin-Moretus Museum/Print Room in Antwerp, Belgium, gathers one of the most precious collections of typographical material and old printed books in the world. Rich decorations of this former printing-house and the history of the building itself underline its uniqueness. The cultural heritage (CH) objects collected in the museum, in particular books and manuscripts are vulnerable to the atmospheric pollution and can be irreversibly damaged. To assess the air quality inside the museum, four consecutive sampling campaigns were performed in each season of the year. The gas monitoring of nitrogen dioxide (NO2), sulphur dioxide (SO2) and ozone (O3) was carried out outside the building, in galleries and in showcases by means of using diffusive samplers. The particulate matter (PM) was collected in bulk form and as single particles and then analysed with use of energy dispersive X-ray fluorescence (EDXRF) and electron probe micro-analyser (EPMA), respectively. The museum complex turned out to show good protection against gaseous pollutants, especially SO2 and O3. The concentrations of these pollutants were significantly reduced inside the building in comparison to the outdoor ones. Similar protective character of the museum complex was established in case of the coarse fraction of PM; however with some limitations. Single particle analysis showed that the relative abundance of carbon-rich particles inside the museum was greater than outside. Moreover, these particles contributed more to the fine fraction of PM than to the coarse fraction. Therefore, for better preservation of cultural heritage, special attention should be paid to the small particles and their distribution within the museum.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation); Laboratory Experimental Medicine and Pediatrics (LEMP)
Impact Factor: 3.034
Times cited: 25
DOI: 10.1016/J.MICROC.2011.11.008
|
|
|
“Chemical imaging of stained-glass windows by means of macro X-ray fluorescence (MA-XRF) scanning”. van der Snickt G, Legrand S, Caen J, Vanmeert F, Alfeld M, Janssens K, Microchemical journal 124, 615 (2016). http://doi.org/10.1016/J.MICROC.2015.10.010
Abstract: Since the recent development of a mobile setup, MA-XRF scanning proved a valuable tool for the non-invasive, technical study of paintings. In this work, the applicability of MA-XRF scanning for investigating stained-glass windows inside a conservation studio is assessed by analysis of a high-profile, well-studied late-mediaeval panel. Although accurate quantification of components is not feasible with this analytical imaging technique, plotting the detected intensities of K versus Ca in a scatter plot allowed distinguishing glass fragments of different compositional types within the same panel. In particular, clusters in the Ca/K correlation plot revealed the presence of two subtypes of potash glass and three subtypes of high lime low alkali glass. MA-XRF results proved consistent with previous quantitative SEM-EDX analysis on two samples and analytical-based theories on glass production in the Low Countries formulated in literature. A bi-plot of the intensities of the more energetic Rb-K versus Sr-K emission lines yielded a similar glass type differentiation and is here presented as suitable alternative in case the Ca/K signal ratio is affected by superimposed weathering crusts. Apart from identification of the chromophores responsible for the green, blue and red glass colors, contrasting the associated elemental distribution maps obtained on the exterior and interior side of the glass permitted discriminating between colored pot metal glass and multi-layered flashed glass as well. Finally, the benefit of obtaining compositional information from the entire surface, as opposed to point analysis, was illustrated by the discovery of what appears to be a green cobalt glass a feature that was previously missed on this well-studied stained-glass window, both by connoisseurs and spectroscopic sample analysis. (C) 2015 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; AXES (Antwerp X-ray Analysis, Electrochemistry and Speciation); Antwerp Cultural Heritage Sciences (ARCHES)
Impact Factor: 3.034
Times cited: 22
DOI: 10.1016/J.MICROC.2015.10.010
|
|