“In-situ TEM study of the Ni5Al3 to B2 + L12 decomposition in Ni65Al35”. Schryvers D, Ma Y, Materials letters 23, 105 (1995). http://doi.org/10.1016/0167-577X(95)00030-5
Abstract: Homogenised and quenched Ni65Al35 samples were heated and studied in situ in a CM20 electron microscope up to 900 degrees C. The Ni5Al3 phase first forming around 550 degrees C in the quenched L1(0) microtwinned martensite starts to decompose around 800 degrees C yielding B2 precipitates in a twinned L1(2) matrix. The latter twinning is a remainder of the microtwinning in the original room temperature martensite. Also the crystallographic relations between precipitates and matrix can be traced back to the original formation of twinned martensite plates within the austenite. Some aspects of the dynamics of the process are discussed on the basis of snap shots and video recordings.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.489
Times cited: 5
DOI: 10.1016/0167-577X(95)00030-5
|
|
|
“On the use of TEM in the characterization of nanocomposites”. Monticelli O, Musina Z, Russo S, Bals S, Materials letters 61, 3446 (2007). http://doi.org/10.1016/j.matlet.2006.11.086
Abstract: Both an organically modified commercial clay of montmorillonite type (MMT) and its nanocomposites, based either on polyamide 6 (PA6) or an epoxy resin, as matrix polymer, have been characterized by transmission electron microscopy (TEM). Sample micrographs, taken at increasing exposure times (t(e)), have shown the gradual disappearance of clay layers, because of an amorphisation of the MMT crystalline structures caused by prolonged sample exposure to electron beam. Indeed, the above phenomenon, which is mostly evident in the case of intercalated nanocomposites, makes the detection of the layered silicate dispersion in the polymer matrix rather difficult and compels to perform TEM measurements using very short exposure times. Moreover, the microscopy accelerating voltage has turned out to affect sample stability; namely, when decreasing the above parameter, the disappearance of clay structure occurs at lower exposure times. (C) 2006 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.572
Times cited: 28
DOI: 10.1016/j.matlet.2006.11.086
|
|
|
“Shape selective growth of single crystalline MnOOH multipods and 1D nanowires by a reductive hydrothermal method”. Mi Y, Zhang X, Yang Z, Li Y, Zhou S, Zhang H, Zhu W, He D, Wang J, Van Tendeloo G, Materials letters 61, 1781 (2007). http://doi.org/10.1016/j.matlet.2006.07.130
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.572
Times cited: 13
DOI: 10.1016/j.matlet.2006.07.130
|
|
|
“Quantifying inflow and RANS turbulence model form uncertainties for wind engineering flows”. Gorle C, Garcia Sánchez C, Iaccarino G, Journal of wind engineering and industrial aerodynamics
T2 –, 6th International Symposium on Computational Wind Engineering (CWE), JUN 08-12, 2014, Hamburg, GERMANY 144, 202 (2015). http://doi.org/10.1016/j.jweia.2015.03.025
Abstract: Reynolds-averaged Navier-Stokes (RANS) simulations are often used in the wind engineering practice for the analysis of turbulent bluff body flows. An approach that allows identifying the uncertainty related to the use of reduced-order turbulence models in RANS simulations would significantly increase the confidence in the use of simulation results as a basis for design decisions. In the present study we apply a strategy that enables quantifying these uncertainties by introducing perturbations in the Reynolds stress tensor to simulations of the flow in downtown Oklahoma City. The method is combined with a framework to quantify uncertainties in the inflow wind direction and intensity, and the final result of the UQ approach is compared to field measurement data for the velocity at 13 locations in the downtown area. (C) 2015 Elsevier Ltd. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.049
Times cited: 22
DOI: 10.1016/j.jweia.2015.03.025
|
|
|
“Advanced turbulence models and boundary conditions for flows around different configurations of ground-mounted buildings”. Longo R, Ferrarotti M, Garcia Sánchez C, Derudi M, Parente A, Journal of wind engineering and industrial aerodynamics 167, 160 (2017). http://doi.org/10.1016/J.JWEIA.2017.04.015
Abstract: When dealing with Atmospheric Boundary Layer (ABL) simulations, commercial computational fluid dynamics (CFD) acquires a strategic resonance. Thanks to its good compromise between accuracy of results and calculation time, RANS still represents a valid alternative to more resource-demanding methods. However, focusing on the models' performances in urban studies, LES generally outmatches RANS results, even if the former is at least one order of magnitude more expensive. Consequently, the present work aims to propose a variety of approaches meant to solve some of the major problems linked to RANS simulations and to further improve its accuracy in typical urban contexts. All of these models are capable of switching from an undisturbed flux formulation to a disturbed one through a local deviation or a marker function. For undisturbed flows, a comprehensive approach is adopted, solving the issue of the erroneous stream-wise gradients affecting the turbulent profiles. Around obstacles, Non-Linear Eddy-Viscosity closures are adopted, due to their prominent capability in capturing the anisotropy of turbulence. The purpose of this work is then to propose a new Building Influence Area concept and to offer more affordable alternatives to LES simulations without sacrificing a good grade of accuracy.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.049
Times cited: 9
DOI: 10.1016/J.JWEIA.2017.04.015
|
|
|
“Accurate infrared absorption measurement of interstitial and precipitated oxygen in p+ silicon wafers”. De Gryse O, Clauws P, Rossou L, van Landuyt J, Vanhellemont J, Microelectronic engineering 45, 277 (1999). http://doi.org/10.1016/S0167-9317(99)00180-X
Abstract: A novel infrared absorption method has been developed to measure [he interstitial oxygen concentration in highly doped silicon. Thin samples of the order of 10-30 mu m are prepared in an essentially stress-free state without changing the state of the crystal. The oxygen concentration is then determined by measuring the height of the 1136-cm(-1) absorption peak due to interstitial oxygen at 5.5 K. The obtained results on as-grown samples are compared with those from gas fusion analysis. The precipitated oxygen concentration in annealed samples is also determined with the new method. It will be shown that the interstitial oxygen concentration in highly doped silicon can be determined with high accuracy and down to concentrations of 10(17) cm(-3). (C) 1999 Elsevier Science B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.806
DOI: 10.1016/S0167-9317(99)00180-X
|
|
|
“Phase formation in intermixed NiGe thin films : influence of Ge content and low-temperature nucleation of hexagonal nickel germanides”. De Schutter B, Devulder W, Schrauwen A, van Stiphout K, Perkisas T, Bals S, Vantomme A, Detavernier C, Microelectronic engineering 120, 168 (2014). http://doi.org/10.1016/j.mee.2013.09.004
Abstract: In this study, we focus on phase formation in intermixed NiGe thin films as they represent a simplified model of the small intermixed interface layer that is believed to form upon deposition of Ni on Ge and where initial phase formation happens. A combinatorial sputter deposition technique was used to co-deposit a range of intermixed NiGe thin films with Ge concentrations varying between 0 and 50 at.%Ge in a single deposition on both Ge (100) and inert SiO2 substrates. In situ X-ray diffraction and transmission electron microscopy where used to study phase formation. In almost the entire composition range under investigation, crystalline phases where found to be present in the as-deposited films. Between 36 and 48 at.%Ge, high-temperature hexagonal nickel germanides were found to occur metastabily below 300 °C, both on SiO2 and Ge (100) substrates. For Ge concentrations in the range between 36 and 42 at.%, this hexagonal germanide phase was even found to be present at room temperature in the as-deposited films. The results obtained in this work could provide more insight in the phase sequence of a pure Ni film on Ge.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.806
Times cited: 9
DOI: 10.1016/j.mee.2013.09.004
|
|
|
“Comparative analysis of the low-energy He+ ions scattering on Al and Al2O3 surfaces”. Fomin VM, Misko VR, Devreese JT, Brongersma HH, Nuclear Instruments &, Methods In Physics Research Section B-Beam Interactions With Materials And Atoms 145, 545 (1998). http://doi.org/10.1016/S0168-583X(98)00530-8
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
Impact Factor: 1.109
Times cited: 9
DOI: 10.1016/S0168-583X(98)00530-8
|
|
|
“Defect characterization in high temperature implanted 6H-SiC using TEM”. Suvorov AV, Lebedev OI, Suvorova AA, van Landuyt J, Usov IO, Nuclear instruments and methods in physics research: B 127/128, 347 (1997). http://doi.org/10.1016/S0168-583X(96)00954-8
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.109
Times cited: 17
DOI: 10.1016/S0168-583X(96)00954-8
|
|
|
“Electron microscopy and Rutherford backscattering spectrometry characterisation of 6H SiC samples implanted with He+”. Frangis N, van Landuyt J, Grimaldi MG, Calcagno L, Nuclear instruments and methods in physics research: B: beam interactions with materials and atoms
T2 –, Symposium 1 on New Trends in Ion Beam Processing of Materials, at the, E-MRS 96 Spring Meeting, June 04-07, 1996, Strasbourg, France 120, 186 (1996). http://doi.org/10.1016/S0168-583X(96)00506-X
Abstract: 6H SiC single crystals were implanted al room temperature with 1 MeV He+ up to a fluence of 2 x 10(17) at./cm(2) RBS-channeling analysis with a 2 MeV He+ beam indicated the formation of extended defects or the generation of point defects at a constant concentration over a depth of about 1 mu m. Electron microscopy characterisation revealed the presence of two amorphous buried layers at depths of about 1,75 and 4.8 mu m. They an due to the implantation and to the analysing RES beam, respectively, No extended planar or linear faults were found in the region between the surface and the first amorphous layer. However, at the surface, a 50 nm thick amorphous layer was observed in which crystalline inclusions were embedded. Electron diffraction and HREM data of the inclusions were typical for diamond, These inclusions were even found in the crystalline SiC material below this layer, however at a reduced density.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.124
Times cited: 2
DOI: 10.1016/S0168-583X(96)00506-X
|
|
|
“Ion beam synthesis of Te and Bi nanoclusters in silicon: the effect of post-implantation high frequency electromagnetic field”. Kalitzova M, Peeva A, Ignatova V, Lebedev OI, Zollo G, Vitali G, Nuclear instruments and methods in physics research: B: beam interactions with materials and atoms 242, 209 (2006). http://doi.org/10.1016/j.nimb.2005.08.017
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.109
Times cited: 1
DOI: 10.1016/j.nimb.2005.08.017
|
|
|
“Ion beam synthesis of \beta-SiC at 950 degrees C and structural characterization”. Frangis N, Nejim A, Hemment PLF, Stoemenos J, van Landuyt J, Nuclear instruments and methods in physics research: B: beam interactions with materials and atoms
T2 –, Symposium J on Correlated Effects in Atomic and Cluster Ion Bombardment and Implantation/Symposium C on Pushing the Limits of Ion Beam, Processing –, Fr 112, 325 (1996). http://doi.org/10.1016/0168-583X(95)01236-2
Abstract: The structure of beta-SiC formed by carbon implantation into Si at high temperatures (850-950 degrees C) at doses ranging between 0.2 X 10(18) to 1 X 10(18) cm(-2) at 200 keV, was studied by combined cross section and high resolution transmission electron microscopy (XTEM and HRTEM). Implantation was performed on (001) and (111) Si wafers. In both cases a buried beta-SiC layer was formed having the same orientation as the Si matrix.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.124
Times cited: 9
DOI: 10.1016/0168-583X(95)01236-2
|
|
|
“Nanohardness and structure of nitrogen implanted SixAly coatings post-implanted with oxygen”. Jacobs M, Bodart F, Terwagne G, Schryvers D, Poulet A, Nuclear instruments and methods in physics research: B: beam interactions with materials and atoms 147, 231 (1999). http://doi.org/10.1016/S0168-583X(98)00535-7
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.109
Times cited: 3
DOI: 10.1016/S0168-583X(98)00535-7
|
|
|
“Observation of vacancy clustering in FZ-Si crystals during in situ electron irradiation in a high voltage electron microscope”. Fedina L, van Landuyt J, Vanhellemont J, Aseev AL, Nuclear instruments and methods in physics research B112, 133 (1996). http://doi.org/10.1016/0168-583X(95)01277-X
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 1.124
Times cited: 4
DOI: 10.1016/0168-583X(95)01277-X
|
|
|
“ALN nanoparticles XANES analysis: local atomic and electronic structure”. Soldatov A, Yalovega G, Smolentsev G, Kravtsova A, Lamoen D, Balasubramanian C, Marcelli A, Cinque G, Bellucci S, Nuclear Instruments &, Methods In Physics Research Section A-Accelerators Spectrometers Detectors And Associated Equipment 575, 85 (2007). http://doi.org/10.1016/j.nima.2007.01.031
Keywords: A1 Journal article; Electron Microscopy for Materials Science (EMAT);
Impact Factor: 1.362
Times cited: 3
DOI: 10.1016/j.nima.2007.01.031
|
|
|
“High reflective mirrors for in-vessel applications in ITER”. Razdobarin AG, Mukhin EE, Semenov VV, YuTolstyakov S, Kochergin MM, Kurskiev GS, Podushnikova KA, Kirilenko DA, Sitnikova AA, Gorodetsky АЕ, Bukhovets VL, Zalavutdinov RK, Zakharov АP, Arkhipov II, Voitsenya VS, Bondarenko VN, Konovalov VG, Ryzhkov IV;, Nuclear instruments and methods in physics research : A: accelerators, spectrometers, detectors and associated equipment 623, 809 (2010). http://doi.org/10.1016/j.nima.2010.04.047
Abstract: The structure and surface morphology of aluminum and silver mirrors covered with protective dielectric oxide layer were studied by means of TEM and SEM. The presence of needle-like pores throughout the thickness of the ZrO(2) film and bubble-like pores in Al(2)O(3) was observed. The test for resistivity to deuterium ion bombardment shows that the exposition to a fluence of similar to 2 x 10(20) ions/cm(2) with the ion energy of 40-50 eV results in appearance of blisters on the surface of mirrors covered wit h Al(2)O(3). For the mirrors protected with ZrO(2) no noticeable changes in surface morphology and reflectivity were found even after order of magnitude higher ion fluence. The effect of different porous structures on blistering phenomena is discussed. (C) 2010 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 1.362
Times cited: 4
DOI: 10.1016/j.nima.2010.04.047
|
|
|
“ZnAl layered double hydroxide based catalysts (with Cu, Mn, Ti) used as noble metal-free three-way catalysts”. Van Everbroeck T, Wu J, Arenas-Esteban D, Ciocarlan R-G, Mertens M, Bals S, Dujardin C, Granger P, Seftel EM, Cool P, Applied clay science 217, 106390 (2022). http://doi.org/10.1016/j.clay.2021.106390
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 5.6
Times cited: 6
DOI: 10.1016/j.clay.2021.106390
|
|
|
“The microstructure and interfaces of intermediate layers in sapphire bicrystals”. Vasiliev AL, Stepantsov EA, Ivanov ZG, Verbist K, Van Tendeloo G, Olsson E, Applied surface science 119, 215 (1997)
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.387
Times cited: 2
|
|
|
“Investigating the effect of sulphurization on volatility of compositions in Cu-poor and Sn-rich CZTS thin films”. Vishwakarma M, Agrawal K, Hadermann J, Mehta BR, Applied Surface Science 507, 145043 (2020). http://doi.org/10.1016/J.APSUSC.2019.145043
Abstract: In the present work, the Cu-poor and Sn-rich CZTS thin films were prepared in order to study the volatility of Sn with respect to other components. Thin film compositions were kept intentionally Sn-rich to understand the behaviour of loss and segregation of Sn during sulphurization. The homogeneous composition distribution in precursor thin films turns heterogeneous with a change in morphology after sulphurization. The inability of identifying nanoscale secondary phases in CZTS thin film by conventional analytical techniques such as XRD and Raman, can be fulfilled by employing HAADF-STEM analysis. XPS and HAADF-STEM analyses provide the quantification of nanoscale secondary phases across the thin film and surface, respectively. The volatility of Sn was revealed in the form of segregation in the middle layer of CZTS cross-sectional lamella rather than loss to annealing atmosphere. It was observed that among the cations of CZTS, Sn segregates more than Cu, while Zn segregates least. The nanoscale spurious phases were observed to vary across different regions in the sulphurized CZTS sample. The reactive annealing lead to grain growth and formation of grain boundary features in the CZTS thin films, where annealing significantly modifies the potential difference and band bending at grain boundaries with respect to intra-grains.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.7
Times cited: 4
DOI: 10.1016/J.APSUSC.2019.145043
|
|
|
“Synthesis &ndash, properties correlation and the unexpected role of the titania support on the Grignard surface modification”. Van Dijck JG, Mampuys P, Ching HYV, Krishnan D, Baert K, Hauffman T, Verbeeck J, Van Doorslaer S, Maes BUW, Dorbec M, Buekenhoudt A, Meynen V, Applied Surface Science 527, 146851 (2020). http://doi.org/10.1016/J.APSUSC.2020.146851
Abstract: While the impact of reaction conditions on surface modification with Grignard reactants has been studied for silica supports, such information is absent for metal oxides like titania. Differences between modified titania and silica are observed, making it paramount to explore the reaction mechanism. A detailed study on the impact of the reaction conditions is reported, with a focus on the chain length of the alkyl Grignard reactant, its concentration, the reaction time and temperature, and the type of titania support. While the increase in the chain length reduces the amount of organic groups on the surface, the concentration, time and temperature show little/no influence on the modification degree. However, the type of titania support used and the percentage of amorphous phase present has a significant impact on the amount of grafted groups. Even though the temperature and concentration show no clear impact on the modification degree, they can cause changes in the surface hydroxyl population, which are thus not linked to the modification degree. Furthermore, the titania support is reduced during functionalization. This reduction dependents on the reaction temperature, the titania support and the chain length of the Grignard reactant. Similarly, this reduction is not linked to the modification degree.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA); Organic synthesis (ORSY); Applied Electrochemistry & Catalysis (ELCAT)
Impact Factor: 6.7
Times cited: 5
DOI: 10.1016/J.APSUSC.2020.146851
|
|
|
“Impact of ordering on the reactivity of mixed crystals of topological insulators with anion substitution: Bi₂SeTe₂, and Sb₂SeTe₂”. Volykhov AA, Frolov AS, Neudachina VS, Vladimirova NV, Gerber E, Callaert C, Hadermann J, Khmelevsky NO, Knop-Gericke A, Sanchez-Barriga J, Yashina LV, Applied Surface Science 541, 148490 (2021). http://doi.org/10.1016/J.APSUSC.2020.148490
Abstract: Three-dimensional topological insulators are exotic materials with unique properties. Tetradymite type binary chalcogenides of bismuth and antimony, as well as their mixed crystals, belong to prototypical TIs. Potential device applications of these materials require in-depth knowledge of their stability in the ambient atmosphere and other media maintained during their processing. Here we investigated the reactivity of mixed crystals with anion substitution, Bi-2(Se1-xTex)(3) and Sb2(Se1-xTex)(3), towards molecular oxygen using both in situ and ex situ X-ray photoelectron spectroscopy. The results indicate that, in contrast to cation substitution, partial substitution of tellurium by selenium atoms leads to anomalously high surface reactivity, which even exceeds that of the most reactive binary constituent. We attribute this effect to anion ordering that essentially modifies the bond geometry, especially the respective bond angles as modeled by DFT.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.387
DOI: 10.1016/J.APSUSC.2020.148490
|
|
|
“Directly revealing the structure-property correlation in Na+-doped cathode materials”. Li C-F, Chen L-D, Wu L, Liu Y, Hu Z-Y, Cui W-J, Dong W-D, Liu X, Yu W-B, Li Y, Van Tendeloo G, Su B-L, Applied surface science 612, 155810 (2023). http://doi.org/10.1016/J.APSUSC.2022.155810
Abstract: The introduction of Na+ is considered as an effective way to improve the performance of Ni-rich cathode materials. However, the direct structure-property correlation for Na+ doped NCM-based cathode materials remain unclear, due to the difficulty of local and accurate structural characterization for light elements such as Li and Na. Moreover, there is the complexity of the modeling for the whole Li ion battery (LIB) system. To tackle the above-mentioned issues, we prepared Na+-doped LiNi0.6Co0.2Mn0.2O2 (Na-NCM622) material. The crystal structure change and the lattice distortion with picometers precision of the Na+-doped material is revealed by Cs-corrected scanning transmission electron microscopy (STEM). Density functional theory (DFT) and the recently proposed electrochemical model, i.e., modified Planck-Nernst-Poisson coupled Frumkin-Butler-Volmer (MPNP-FBV), has been applied to reveal correlations between the activation energy and the charge transfer resistance at multiscale. It is shown that Na+ doping can reduce the activation energy barrier from. G = 1.10 eV to 1.05 eV, resulting in a reduction of the interfacial resistance from 297 O to 134 Omega. Consequently, the Na-NCM622 cathode delivers a superior capacity retention of 90.8 % (159 mAh.g(-1)) after 100 cycles compared to the pristine NCM622 (67.5 %, 108 mAh.g(-1)). Our results demonstrate that the kinetics of Li+ diffusion and the electrochemical reaction can be enhanced by Na+ doping the cathode material.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.7
DOI: 10.1016/J.APSUSC.2022.155810
|
|
|
“Functionalization of graphitic carbon nitride systems by cobalt and cobalt-iron oxides boosts solar water oxidation performances”. Benedet M, Andrea Rizzi G, Gasparotto A, Gauquelin N, Orekhov A, Verbeeck J, Maccato C, Barreca D, Applied surface science 618, 156652 (2023). http://doi.org/10.1016/j.apsusc.2023.156652
Abstract: The ever-increasing energy demand from the world population has made the intensive use of fossil fuels an overarching threat to global environment and human health. An appealing alternative is offered by sunlight-assisted photoelectrochemical water splitting to yield carbon-free hydrogen fuel, but kinetic limitations associated to the oxygen evolution reaction (OER) render the development of cost-effective, eco-friendly and stable electrocatalysts an imperative issue. In the present work, OER catalysts based on graphitic carbon nitride (g-C3N4) were deposited on conducting glass substrates by a simple decantation procedure, followed by functionalization with low amounts of nanostructured CoO and CoFe2O4 by radio frequency (RF)-sputtering, and final annealing under inert atmosphere. A combination of advanced characterization tools was used to investigate the interplay between material features and electrochemical performances. The obtained results highlighted the formation of a p-n junction for the g-C3N4-CoO system, whereas a Z-scheme junction accounted for the remarkable performance enhancement yielded by g-C3N4-CoFe2O4. The intimate contact between the system components also afforded an improved electrocatalyst stability in comparison to various bare and functionalized g-C3N4-based systems. These findings emphasize the importance of tailoring g-C3N4 chemico-physical properties through the dispersion of complementary catalysts to fully exploit its applicative potential.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 6.7
Times cited: 11
DOI: 10.1016/j.apsusc.2023.156652
|
|
|
“Electron microscopy characterisation of erbium silicide-thin films grown on a Si(111) substrate”. Frangis N, Van Tendeloo G, van Landuyt J, Muret P, Nguyen TTA, Applied surface science 102, 163 (1996). http://doi.org/10.1016/0169-4332(96)00040-2
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.711
Times cited: 9
DOI: 10.1016/0169-4332(96)00040-2
|
|
|
“High crystalline quality erbium silicide films on (100) silicon grown in high vacuum”. Kaltsas G, Travlos A, Nassiopoulos AG, Frangis N, van Landuyt J, Applied surface science 102, 151 (1996). http://doi.org/10.1016/0169-4332(96)00036-0
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.711
Times cited: 14
DOI: 10.1016/0169-4332(96)00036-0
|
|
|
“Photoelectric and electrical responses of several erbium silicide/silicon interfaces”. Muret P, Nguyen TTA, Frangis N, Van Tendeloo G, van Landuyt J, Applied surface science
T2 –, International Symposium on Si Heterostructures –, From Physics to Devices, SEP 11-14, 1995, IRAKLION, GREECE 102, 173 (1996). http://doi.org/10.1016/0169-4332(96)00042-6
Abstract: In this work, photoelectric yield and electrical properties of several types of epitaxial erbium silicide on silicon Schottky diodes are studied, Different preparation conditions are used simultaneously on n- and p-Si(111) substrates for the 200 Angstrom thick silicide films. A last type of sample consists in 1.3 monolayer of epitaxial silicide with root 3 X root 3 superstructure on the Si substrate and covered by silver on the top. Photocurrent measurements are done as a function of photon energy at several temperatures. All these samples show barrier heights near 1 eV on p-type Si, even for the interface comprising only 1.3 monolayer of silicide whereas barrier heights on n-rype Si span the range from 0.28 to 0.67 eV for this last kind of sample, the sum of the barriers always exceeding the silicon band gap, These photoelectric results are confirmed by electrical characterisations, All these results show that the Fermi level is pinned 0.1 eV below the conduction band edge on p-type Si but shifts to various positions lower within the band gap on n-type Si. This fact leads to the hypothesis of a density of -7 interface states close to the charge change in the Si depletion zone from p- to n-type, namely 10(12) eV(-1) cm(-2). Although some inhomogeneities and defects at the interface are detected by electron microscopy for samples annealed at 750 degrees C, Fermi level position seems rather insensitive to the structural details of the interface while the silicide thickness plays a role on n-type Si.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.711
Times cited: 3
DOI: 10.1016/0169-4332(96)00042-6
|
|
|
“Round-robin investigation of silicon-oxide on silicon reference materials for ellipsometry”. Vanhellemont J, Maes HE, Schaekers M, Armigliato A, Cerva H, Cullis A, de Sande J, Dinges H, Hallais J, Nayar V, Pickering C, Stehlé, JL, Van Landuyt J, Walker C, Werner H, Salieri P;, Applied surface science
T2 –, SYMP ON DIAGNOSTIC TECHNIQUES FOR SEMICONDUCTOR MATERIALS ANALYSIS AND, FABRICATION PROCESS CONTROL, AT THE 1992 SPRING CONF OF THE EUROPEAN, MATERIALS RESEARCH SOC, JUN 02-05, 1992, STRASBOURG, FRANCE 63, 45 (1993). http://doi.org/10.1016/0169-4332(93)90062-G
Abstract: The main results and conclusions are presented of a round robin study of silicon oxide on silicon reference samples for ellipsometry. The oxide films with nominal thicknesses of 10, 50 and 120 nm are grown by thermal oxidation. The oxide film thicknesses have been determined by single wavelength ellipsometry (SWE), by spectroscopic ellipsometry (SE) and by cross-sectional conventional and high-resolution transmission electron microscopy (TEM and HREM) in different laboratories. The main conclusions are that special precautions have to be taken in order to use TEM as a reliable thickness measurement technique; that single wavelength ellipsometry can be used with great accuracy and reproducibility for the 50 and 120 nm film thicknesses but that it shows some inherent problems for the 10 nm films; and that spectroscopic ellipsometry showed for all film thicknesses an accuracy and reproducibility which is clearly superior to that of SWE.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.711
Times cited: 13
DOI: 10.1016/0169-4332(93)90062-G
|
|
|
“Community structure and feeding preference of nematodes associated with methane seepage at the Darwin mud volcano (Gulf of Cádiz)”. Pape E, Bezerra TN, Vanneste H, Heeschen K, Moodley L, Leroux F, van Breugel P, Vanreusel A, Marine ecology progress series 438, 71 (2011). http://doi.org/10.3354/meps09278
Abstract: We sampled the Darwin mud volcano (MV) for meiofaunal community and trophic structure in relation to pore-water geochemistry along a 10 m transect from a seep site on the rim of the crater towards the MV slope. Pore-water profiles indicated considerable variation in upward methane (CH4) flow among sediment cores taken along the transect, with highest flux in the seep sediment core, gradually decreasing along the transect, to no CH4 flux in the core taken at a 5 m distance. Low sulphate concentrations and high levels of total alkalinity and sulphide (H2S) suggested that anaerobic oxidation of methane (AOM) occurred close to the sediment surface in the seep sediment core. High H2S levels had a genus- and species-specific impact on meiofaunal densities. Nematode genus composition varied gradually between sediment cores, with the genus Sabatieria dominating almost all sediment cores. However, genus diversity increased with increasing distance from the seep site. These limited data suggest that the community structure of seep meiofauna is highly dependent on local (a)biotic habitat characteristics, and a typical seep meiofaunal community cannot be delineated. Stable isotope values suggested the nematode diet up to 10 m from the seep site included thiotrophic carbon. The thicker hemipelagic sediment layer (photosynthetic carbon), the increased trophic diversity, and the heavier nematode δ13C farther from the seep site suggest a decrease in thiotrophy and an increase in photosynthetic carbon in the nematode diet.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.292
Times cited: 18
DOI: 10.3354/meps09278
|
|
|
“High-resolution electron microscopy and electron energy-loss spectroscopy of giant palladium clusters”. Oleshko V, Volkov V, Gijbels R, Jacob W, Vargaftik M, Moiseev I, Van Tendeloo G, Zeitschrift für Physik : D : atoms, molecules and clusters 34, 283 (1995). http://doi.org/10.1007/BF01437574
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT); Electron microscopy for materials research (EMAT)
Times cited: 22
DOI: 10.1007/BF01437574
|
|
|
“Superconducting nanowires: quantum-confinement effect on the critical magnetic field and supercurrent”. Croitoru MD, Shanenko AA, Peeters FM, International journal of modern physics: B: condensed matter physics, statistical physics, applied physics
T2 –, 32nd International Workshop on Condensed Matter Theories, Aug 12-19, 2008, Loughborough Univ, Loughborough, England 23, 4257 (2009). http://doi.org/10.1142/S0217979209063419
Abstract: We study the effect of electron confinement on the superconducting-to-normal phase transition driven by a magnetic field and/or on the current-carrying state of the superconducting condensate in nanowires. Our investigation is based on a self-consistent numerical solution of the Bogoliubov-de Gennes equations. We show that in a parallel magnetic field and/or in the presence of supercurrent the transition from superconducting to normal phase occurs as a cascade of discontinuous jumps in the superconducting order parameter for diameters D < 10 divided by 15 nm at T = 0. The critical magnetic field exhibits quantum-size oscillations with pronounced resonant enhancements.
Keywords: A1 Journal article; Condensed Matter Theory (CMT); Electron microscopy for materials research (EMAT)
Impact Factor: 0.736
Times cited: 1
DOI: 10.1142/S0217979209063419
|
|