“Self-Assembly of Pluronic F127—Silica Spherical Core–Shell Nanoparticles in Cubic Close-Packed Structures”. Kerkhofs S, Willhammar T, Van Den Noortgate H, Kirschhock CEA, Breynaert E, Van Tendeloo G, Bals S, Martens JA, Chemistry of materials 27, 5161 (2015). http://doi.org/10.1021/acs.chemmater.5b01772
Abstract: A new ordered mesoporous silica material (COK-19) with cubic symmetry is synthesized by silicate polycondensation in a citric acid/citrate buffered micellar solution of Pluronic F127 triblock copolymer near neutral pH. SAXS, nitrogen adsorption, TEM, and electron tomography reveal the final material has a cubic close packed symmetry (Fm3̅m) with isolated spherical mesopores interconnected through micropores. Heating of the synthesis medium from room temperature to 70 °C results in a mesopore size increase from 7.0 to 11.2 nm. Stepwise addition of the silicate source allows isolation of a sequence of intermediates that upon characterization with small-angle X-ray scattering uncovers the formation process via formation and aggregation of individual silica-covered Pluronic micelles.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 39
DOI: 10.1021/acs.chemmater.5b01772
|
“Postsynthetic high-alumina zeolite crystal engineering in organic free hyper-alkaline media”. Van Tendeloo L, Wangermez W, Vandekerkhove A, Willhammar T, Bals S, Maes A, Martens JA, Kirschhock CEA, Breynaert E, Chemistry of materials 29, 629 (2017). http://doi.org/10.1021/ACS.CHEMMATER.6B04052
Abstract: Postsynthetic modification of high -alumina zeolites in hyper alkaline media can be tailored toward alteration of framework topology, crystal size and morphology, or desired Si/A1 ratio. FAU, EMT, MAZ, KFI, HEU, and LTA starting materials were treated with 1.2 M MOH (M = Na, K, RE, or Cs), leading to systematic ordered porosity or fully transformed frameworks with new topology and adjustable Si/Al ratio. In addition to the versatility of this tool for zeolite crystal engineering, these alterations improve understanding of the crystal chemistry. Such knowledge can guide further development in zeolite crystal engineering. Postsynthetic alteration also provides insight on the long-term stability of aluminosilicate zeolites that are used as a sorption sink in concrete -based waste disposal facilities in harsh alkaline conditions.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 16
DOI: 10.1021/ACS.CHEMMATER.6B04052
|
“Luminescent CuInS2 quantum dots by partial cation exchange in Cu2-xS nanocrystals”. van der Stam W, Berends AC, Rabouw FT, Willhammar T, Ke X, Meeldijk JD, Bals S, de Donega CM, Chemistry of materials 27, 621 (2015). http://doi.org/10.1021/cm504340h
Abstract: Here, we show successful partial cation exchange reactions in Cu2-xS nanocrystals (NCs) yielding luminescent CuInS2 (CIS) NCs. Our approach of mild reaction conditions ensures slow Cu extraction rates, which results in a balance with the slow In incorporation rate. With this method, we obtain CIS NCs with photoluminescence (PL) far in the near-infrared (NIR), which cannot be directly synthesized by currently available synthesis protocols. We discuss the factors that favor partial, self-limited cation exchange from Cu2-xS to CIS NCs, rather than complete cation exchange to In2S3. The product CIS NCs have the wurtzite crystal structure, which is understood in terms of conservation of the hexagonal close packing of the anionic sublattice of the parent NCs into the product NCs. These results are an important step toward the design of CIS NCs with sizes and shapes that are not attainable by direct synthesis protocols and may thus impact a number of potential applications.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
Times cited: 119
DOI: 10.1021/cm504340h
|
“Post-synthesis bromination of benzene bridged PMO as a way to create a high potential hybrid material”. Huybrechts W, Mali G, Kuśtrowski P, Willhammar T, Mertens M, Bals S, Van Der Voort P, Cool P, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 236, 244 (2016). http://doi.org/10.1016/j.micromeso.2016.09.003
Abstract: Periodic mesoporous organosilicas provide the best of two worlds: the strength and porosity of an inorganic framework combined with the infinite possibilities created by the organic bridging unit. In this work we focus on post-synthetical modification of benzene bridged PMO, in order to create bromobenzene PMO. In the past, this proved to be very challenging due to unwanted structural deterioration. However, now we have found a way to brominate this material whilst keeping the structure intact. In-depth structural analysis by solid state NMR and XPS shows both vast progress over previous attempts as well as potential for improvement.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT); Laboratory of adsorption and catalysis (LADCA)
Impact Factor: 3.615
Times cited: 7
DOI: 10.1016/j.micromeso.2016.09.003
|
“A titanium(IV)-based metal-organic framework featuring defect-rich Ti-O sheets as an oxidative desulfurization catalyst”. Smolders S, Willhammar T, Krajnc A, Şentosun K, Wharmby MT, Lomachenko KA, Bals S, Mali G, Roeffaers MBJ, De Vos DE, Bueken B, Angewandte Chemie: international edition in English 58, 9160 (2019). http://doi.org/10.1002/ANIE.201904347
Abstract: While titanium-based metal-organic frameworks (MOFs) have been widely studied for their (photo) catalytic potential, only a few Ti-IV MOFs have been reported owing to the high reactivity of the employed titanium precursors. The synthesis of COK-47 is now presented, the first Ti carboxylate MOF based on sheets of (TiO6)-O-IV octahedra, which can be synthesized with a range of different linkers. COK-47 can be synthesized as an inherently defective nanoparticulate material, rendering it a highly efficient catalyst for the oxidation of thiophenes. Its structure was determined by continuous rotation electron diffraction and studied in depth by X-ray total scattering, EXAFS, and solid-state NMR. Furthermore, its photoactivity was investigated by electron paramagnetic resonance and demonstrated by catalytic photodegradation of rhodamine 6G.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 11.994
Times cited: 97
DOI: 10.1002/ANIE.201904347
|
“Phase transformation behavior of a two-dimensional zeolite”. Bae J, Cichocka MO, Zhang Y, Bacsik Z, Bals S, Zou X, Willhammar T, Hong SB, Angewandte Chemie: international edition in English 58, 10230 (2019). http://doi.org/10.1002/ANIE.201904825
Abstract: Understanding the molecular-level mechanisms of phase transformation in solids is of fundamental interest for functional materials such as zeolites. Two-dimensional (2D) zeolites, when used as shape-selective catalysts, can offer improved access to the catalytically active sites and a shortened diffusion length in comparison with their 3D analogues. However, few materials are known to maintain both their intralayer microporosity and structure during calcination for organic structure-directing agent (SDA) removal. Herein we report that PST-9, a new 2D zeolite which has been synthesized via the multiple inorganic cation approach and fulfills the requirements for true layered zeolites, can be transformed into the small-pore zeolite EU-12 under its crystallization conditions through the single-layer folding process, but not through the traditional dissolution/recrystallization route. We also show that zeolite crystal growth pathway can differ according to the type of organic SDAs employed.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 2
DOI: 10.1002/ANIE.201904825
|
“Structure and vacancy distribution in copper telluride nanoparticles influence plasmonic activity in the near-infrared”. Willhammar T, Sentosun K, Mourdikoudis S, Goris B, Kurttepeli M, Bercx M, Lamoen D, Partoens B, Pastoriza-Santos I, Pérez-Juste J, Liz-Marzán LM, Bals S, Van Tendeloo G, Nature communications 8, 14925 (2017). http://doi.org/10.1038/ncomms14925
Abstract: Copper chalcogenides find applications in different domains including photonics, photothermal therapy and photovoltaics. CuTe nanocrystals have been proposed as an alternative to noble metal particles for plasmonics. Although it is known that deviations from stoichiometry are a prerequisite for plasmonic activity in the near-infrared, an accurate description of the material and its (optical) properties is hindered by an insufficient understanding of the atomic structure and the influence of defects, especially for materials in their nanocrystalline form. We demonstrate that the structure of Cu1.5±xTe nanocrystals canbe determined using electron diffraction tomography. Real-space high-resolution electron tomography directly reveals the three-dimensional distribution of vacancies in the structure. Through first-principles density functional theory, we furthermore demonstrate that the influence of these vacancies on the optical properties of the nanocrystals is determined. Since our methodology is applicable to a variety of crystalline nanostructured materials, it is expected to provide unique insights concerning structure–property correlations.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT); Condensed Matter Theory (CMT)
Impact Factor: 12.124
Times cited: 37
DOI: 10.1038/ncomms14925
|
“Gel-based morphological design of zirconium metal-organic frameworks”. Bueken B, Van Velthoven N, Willhammar T, Stassin T, Stassen I, Keen DA, Baron GV, Denayer JFM, Ameloot R, Bals S, De Vos D, Bennett TD, Chemical science 8, 3939 (2017). http://doi.org/10.1039/C6SC05602D
Abstract: The ability of metal-organic frameworks (MOFs) to gelate under specific synthetic conditions opens up new opportunities in the preparation and shaping of hierarchically porous MOF monoliths, which could be directly implemented for catalytic and adsorptive applications. In this work, we present the first examples of xero-or aerogel monoliths consisting solely of nanoparticles of several prototypical Zr4+-based MOFs: UiO-66-X (X – H, NH2, NO2, (OH)(2)), UiO-67, MOF-801, MOF-808 and NU-1000. High reactant and water concentrations during synthesis were observed to induce the formation of gels, which were converted to monolithic materials by drying in air or supercritical CO2. Electron microscopy, combined with N-2 physisorption experiments, was used to show that irregular nanoparticle packing leads to pure MOF monoliths with hierarchical pore systems, featuring both intraparticle micropores and interparticle mesopores. Finally, UiO-66 gels were shaped into monolithic spheres of 600 mm diameter using an oil-drop method, creating promising candidates for packed-bed catalytic or adsorptive applications, where hierarchical pore systems can greatly mitigate mass transfer limitations.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 8.668
Times cited: 168
DOI: 10.1039/C6SC05602D
|
“Controlled growth of hexagonal gold nanostructures during thermally induced self-assembling on Ge(001) surface”. Jany BR, Gauquelin N, Willhammar T, Nikiel M, van den Bos KHW, Janas A, Szajna K, Verbeeck J, Van Aert S, Van Tendeloo G, Krok F, Scientific reports 7, 42420 (2017). http://doi.org/10.1038/srep42420
Abstract: Nano-sized gold has become an important material in various fields of science and technology, where control over the size and crystallography is desired to tailor the functionality. Gold crystallizes in the face-centered cubic (fcc) phase, and its hexagonal closed packed (hcp) structure is a very unusual and rare phase. Stable Au hcp phase has been reported to form in nanoparticles at the tips of some Ge nanowires. It has also recently been synthesized in the form of thin graphene-supported sheets which are unstable under electron beam irradiation. Here, we show that stable hcp Au 3D nanostructures with well-defined crystallographic orientation and size can be systematically created in a process of thermally induced self-assembly of thin Au layer on Ge(001) monocrystal. The Au hcp crystallite is present in each Au nanostructure and has been characterized by different electron microscopy techniques. We report that a careful heat treatment above the eutectic melting temperature and a controlled cooling is required to form the hcp phase of Au on a Ge single crystal. This new method gives scientific prospects to obtain stable Au hcp phase for future applications in a rather simple manner as well as redefine the phase diagram of Gold with Germanium.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 4.259
Times cited: 25
DOI: 10.1038/srep42420
|