“Local destruction of superconductivity by non-magnetic impurities in mesoscopic iron-based superconductors”. Li J, Ji M, Schwarz T, Ke X, Van Tendeloo G, Yuan J, Pereira PJ, Huang Y, Zhang G, Feng HL, Yuan YH, Hatano T, Kleiner R, Koelle D, Chibotaru LF, Yamaura K, Wang HB, Wu PH, Takayama-Muromachi E, Vanacken J, Moshchalkov VV;, Nature communications 6, 7614 (2015). http://doi.org/10.1038/ncomms8614
Abstract: The determination of the pairing symmetry is one of the most crucial issues for the iron-based superconductors, for which various scenarios are discussed controversially. Non-magnetic impurity substitution is one of the most promising approaches to address the issue, because the pair-breaking mechanism from the non-magnetic impurities should be different for various models. Previous substitution experiments demonstrated that the non-magnetic zinc can suppress the superconductivity of various iron-based superconductors. Here we demonstrate the local destruction of superconductivity by non-magnetic zinc impurities in Ba0.5K0.5Fe2As2 by exploring phase-slip phenomena in a mesoscopic structure with 119 × 102 nm2 cross-section. The impurities suppress superconductivity in a three-dimensional Swiss cheese-like pattern with in-plane and out-of-plane characteristic lengths slightly below ~1.34 nm. This causes the superconducting order parameter to vary along abundant narrow channels with effective cross-section of a few square nanometres. The local destruction of superconductivity can be related to Cooper pair breaking by non-magnetic impurities.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 12.124
Times cited: 12
DOI: 10.1038/ncomms8614
|
“Antiferromagnetic order breaks inversion symmetry in a metallic double perovskite, Pb₂NiOsO₆”. Feng HL, Kang C-J, Manuel P, Orlandi F, Su Y, Chen J, Tsujimoto Y, Hadermann J, Kotliar G, Yamaura K, McCabe EE, Greenblatt M, Chemistry Of Materials 33, 4188 (2021). http://doi.org/10.1021/ACS.CHEMMATER.1C01032
Abstract: A polycrystalline sample of Pb2NiOsO6 was synthesized under high-pressure (6 GPa) and high-temperature (1575 K) conditions. Pb2NiOsO6 crystallizes in a monoclinic double perovskite structure with a centrosymmetric space group P2(1)/n at room temperature. Pb2NiOsO6 is metallic down to 2 K and shows a single antiferromagnetic (AFM) transition at T-N = 58 K. Pb2NiOsO6 is a new example of a metallic and AFM oxide with three-dimensional connectivity. Neutron powder diffraction and first-principles calculation studies indicate that both Ni and Os moments are ordered below T-N and the AFM magnetic order breaks inversion symmetry. This loss of inversion symmetry driven by AFM order is unusual in metallic systems, and the 3d-Sd double-perovskite oxides represent a new class of noncentrosymmetric AFM metallic oxides.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 9.466
DOI: 10.1021/ACS.CHEMMATER.1C01032
|