“Synthesis of aluminum-containing hierarchical mesoporous materials with columnar mesopore ordering by evaporation induced self assembly”. Kurttepeli M, Locus R, Verboekend D, de Clippel F, Breynaert E, Martens J, Sels B, Bals S, Microporous and mesoporous materials: zeolites, clays, carbons and related materials 234, 186 (2016). http://doi.org/10.1016/J.MICROMESO.2016.07.002
Abstract: The incorporation of aluminum into the silica columns of hierarchical mesoporous materials (HMMs) was studied. The HMMs were synthesized by a combination of hard and soft templating methods, forming mesoporous SBA-15-type silica columns inside the pores of anodic aluminum oxide membranes via evaporation induced self-assembly (EISA). By adding Al-isopropoxide to the EISA-mixture a full tetrahedral incorporation of Al and thus the creation of acid sites was achieved, which was proved by nuclear magnetic resonance spectroscopy. Electron microscopy showed that the use of Al-isopropoxide as an Al source for the HMMs led to a change in the mesopore ordering of silica material from circular hexagonal (donut-like) to columnar hexagonal and a 37% increase in specific surface (BET surface). These results were confirmed by a combination of nitrogen physisorption and small-angle X-ray scattering experiments and can be attributed to a swelling of the P123 micelles with isopropanol. The columnar mesopore ordering of silica is advantageous towards the pore accessibility and therefore preferential for many possible applications including catalysis and adsorption on the acid tetrahedral Al-sites. (C) 2016 Elsevier Inc. All rights reserved.
Keywords: A1 Journal article; Engineering sciences. Technology; Electron microscopy for materials research (EMAT)
Impact Factor: 3.615
Times cited: 5
DOI: 10.1016/J.MICROMESO.2016.07.002
|
“Thick homoepitaxial (110)-oriented phosphorus-doped n-type diamond”. Balasubramaniam Y, Pobedinskas P, Janssens SD, Sakr G, Jomard F, Turner S, Lu YG, Dexters W, Soltani A, Verbeeck J, Barjon J, Nesládek M, Haenen K;, Applied physics letters 109, 062105 (2016). http://doi.org/10.1063/1.4960970
Abstract: The fabrication of n-type diamond is essential for the realization of electronic components for extreme environments. We report on the growth of a 66 mu m thick homoepitaxial phosphorus-doped diamond on a (110)-oriented diamond substrate, grown at a very high deposition rate of 33 mu m h(-1). A pristine diamond lattice is observed by high resolution transmission electron microscopy, which indicates the growth of high quality diamond. About 2.9 x 10(16) cm(-3) phosphorus atoms are electrically active as substitutional donors, which is 60% of all incorporated dopant atoms. These results indicate that P-doped (110)-oriented diamond films deposited at high growth rates are promising candidates for future use in high-power electronic applications. Published by AIP Publishing.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 3.411
Times cited: 20
DOI: 10.1063/1.4960970
|
“An alternative approach for \zeta-factor measurement using pure element nanoparticles”. Zanaga D, Altantzis T, Sanctorum J, Freitag B, Bals S, Ultramicroscopy 164, 11 (2016). http://doi.org/10.1016/J.ULTRAMIC.2016.03.002
Abstract: It is very challenging to measure the chemical composition of hetero nanostructures in a reliable and quantitative manner. Here, we propose a novel and straightforward approach that can be used to quantify energy dispersive X-ray spectra acquired in a transmission electron microscope. Our method is based on a combination of electron tomography and the so-called zeta-factor technique. We will demonstrate the reliability of our approach as well as its applicability by investigating Au-Ag and Au-Pt hetero nanostructures. Given its simplicity, we expect that the method could become a new standard in the field of chemical characterization using electron microscopy. (C) 2016 Elsevier B.V. All rights reserved.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 2.843
Times cited: 19
DOI: 10.1016/J.ULTRAMIC.2016.03.002
|
“PdPb-catalyzed decarboxylation of proline to pyrrolidine : highly selective formation of a biobased amine in water”. Verduyckt J, Van Hoof M, De Schouwer F, Wolberg M, Kurttepeli M, Eloy P, Gaigneaux EM, Bals S, Kirschhock CEA, De Vos DE, ACS catalysis 6, 7303 (2016). http://doi.org/10.1021/ACSCATAL.6B02561
Abstract: Amino acids have huge potential as platform chemicals in the biobased industry. Pd-catalyzed decarboxylation is a very promising route for the valorization of these natural compounds derived from protein waste or fermentation. We report that the highly abundant and nonessential amino acid L-proline is very reactive in the Pd-catalyzed decarboxylation. Full conversions are obtained with Pd/C and different Pd/MeOx catalysts; this allowed the identification of the different side reactions and the mapping of the reaction network. Due to the high reactivity of pyrrolidine, the selectivity for pyrrolidine was initially low. By carefully modifying Pd/ZrO2 with Pb in a controlled manner-via two incipient wetness impregnation steps-the selectivity increased remarkably. Finally, a thorough investigation of the reaction parameters resulted in an increased activity of this modified catalyst and an even further enhanced selectivity under a low H-2 pressure of 4 bar at 235 degrees C in water. This results in a very selective and sustainable production route for the highly interesting pyrrolidine.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Impact Factor: 10.614
Times cited: 27
DOI: 10.1021/ACSCATAL.6B02561
|
“Silver Ions Direct Twin-Plane Formation during the Overgrowth of Single-Crystal Gold Nanoparticles”. Grzelczak M, Sanchez-Iglesias A, Heidari H, Bals S, Pastoriza-Santos I, Perez-Juste J, Liz-Marzan LM, ACS Omega 1, 177 (2016). http://doi.org/10.1021/ACSOMEGA.6B00066
Abstract: It is commonly agreed that the crystalline structure of seeds dictates the crystallinity of final nanoparticles in a seeded-growth process. Although the formation of monocrystalline particles does require the use of single-crystal seeds, twin planes may stem from either single-or polycrystalline seeds. However, experimental control over twin-plane formation remains difficult to achieve synthetically. Here, we show that a careful interplay between kinetics and selective surface passivation offers a unique handle over the emergence of twin planes (in decahedra and triangles) during the growth over single-crystalline gold nanoparticles of quasi-spherical shape. Twinning can be suppressed under conditions of slow kinetics in the presence of silver ions, yielding single-crystalline particles with high-index facets.
Keywords: A1 Journal article; Electron microscopy for materials research (EMAT)
Times cited: 18
DOI: 10.1021/ACSOMEGA.6B00066
|
“Multi-level molecular modelling for plasma medicine”. Bogaerts A, Khosravian N, Van der Paal J, Verlackt CCW, Yusupov M, Kamaraj B, Neyts EC, Journal Of Physics D-Applied Physics 49, 054002 (2016)
Keywords: A1 Journal article; Plasma, laser ablation and surface modeling – Antwerp (PLASMANT)
Impact Factor: 2.588
|
“Plasma processes and polymers third special issue on plasma and cancer”. Laroussi M, Bogaerts A, Barekzi N, Plasma processes and polymers 13, 1142 (2016). http://doi.org/10.1002/ppap.201600193
Keywords: Editorial; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 2.846
Times cited: 1
DOI: 10.1002/ppap.201600193
|
“Analysis and comparison of the co2 and co dielectric barrier discharge solid products”. Belov I, Paulussen S, Bogaerts A, Hakone Xv: International Symposium On High Pressure Low Temperature Plasma Chemistry: With Joint Cost Td1208 Workshop: Non-equilibrium Plasmas With Liquids For Water And Surface Treatment (2016)
Abstract: The CO and CO2 Dielectric Barrier Discharges (DBD) and their solid products were analyzed keeping similar energy input regimes. Gas chromatography analysis revealed the presence of CO2, CO and O-2 mixture in the exhaust of the CO2 DBD, while no O-2 was found when CO was used as a feed gas. It was shown that the C-2 Swan lines observed with optical emission spectroscopy were distinct in the CO plasma while they were not observed in the CO2 emission spectrum. Also the solid products of the plasmas exhibited remarkable differences. Nanoparticles with a diameter between10 and 300 nm, composed of Fe, O and C (Fe: O: C similar to 13: 50: 30) were produced by the CO2 DBD, while microscopic dendrite-like carbon structure (C: O similar to 73: 27) were formed in the CO plasma. The growth rate in the CO2 and CO DBDs was evaluated to be on the level of 0.15 mg/min and 15 mg/min, respectively. The difference of the CO and CO2 discharges and their products might be attributed to the oxygen content in the latter (6.4 mol.% O-2 in the exhaust) and subsequent etching of the carbonaceous film.
Keywords: P1 Proceeding; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
|
“Plasma based co2 conversion: a combined modeling and experimental study”. Bogaerts A, Snoeckx R, Berthelot A, Heijkers S, Wang W, Sun S, Van Laer K, Ramakers M, Michielsen I, Uytdenhouwen Y, Meynen V, Cool P, Hakone Xv: International Symposium On High Pressure Low Temperature Plasma Chemistry: With Joint Cost Td1208 Workshop: Non-equilibrium Plasmas With Liquids For Water And Surface Treatment (2016)
Abstract: In recent years there is increased interest in plasma-based CO2 conversion. Several plasma setups are being investigated for this purpose, but the most commonly used ones are a dielectric barrier discharge (DBD), a microwave (MW) plasma and a gliding arc (GA) reactor. In this proceedings paper, we will show results from our experiments in a (packed bed) DBD reactor and in a vortex-flow GA reactor, as well as from our model calculations for the detailed plasma chemistry in a DBD, MW and GA, for pure CO2 as well as mixtures of CO2 with N-2, CH4 and H2O.
Keywords: P1 Proceeding; Laboratory of adsorption and catalysis (LADCA); Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
|
“Plasma–liquid interactions: a review and roadmap”. Bruggeman PJ, Kushner MJ, Locke BR, Gardeniers JGE, Graham WG, Graves DB, Hofman-Caris RCHM, Maric D, Reid JP, Ceriani E, Fernandez Rivas D, Foster JE, Garrick SC, Gorbanev Y, Hamaguchi S, Iza F, Jablonowski H, Klimova E, Kolb J, Krcma F, Lukes P, Machala Z, Marinov I, Mariotti D, Mededovic Thagard S, Minakata D, Neyts EC, Pawlat J, Petrovic ZL, Pflieger R, Reuter S, Schram DC, Schröter S, Shiraiwa M, Tarabová, B, Tsai PA, Verlet JRR, von Woedtke T, Wilson KR, Yasui K, Zvereva G, Plasma sources science and technology 25, 053002 (2016). http://doi.org/10.1088/0963-0252/25/5/053002
Abstract: Plasma–liquid interactions represent a growing interdisciplinary area of research involving plasma science, fluid dynamics, heat and mass transfer, photolysis, multiphase chemistry and aerosol science. This review provides an assessment of the state-of-the-art of this multidisciplinary area and identifies the key research challenges. The developments in diagnostics, modeling and further extensions of cross section and reaction rate databases that are necessary to address these challenges are discussed. The review focusses on nonequilibrium plasmas.
Keywords: A1 Journal article; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
Impact Factor: 3.302
Times cited: 460
DOI: 10.1088/0963-0252/25/5/053002
|
“Superconductivity between standard types: Multiband versus single-band materials”. Vagov A, Shanenko AA, Milošević, MV, Axt VM, Vinokur VM, Aguiar JA, Peeters FM, Physical review B 93, 174503 (2016). http://doi.org/10.1103/PhysRevB.93.174503
Keywords: A1 Journal article; Condensed Matter Theory (CMT)
Impact Factor: 3.836
Times cited: 37
DOI: 10.1103/PhysRevB.93.174503
|
“Glow discharge optical spectroscopy and mass spectrometry”. Bogaerts A John Wiley & Sons, Chichester, page 1 (2016).
Abstract: Atomic Spectroscopy Optical (atomic absorption spectroscopy, AAS; atomic emission spectroscopy, AES; atomic fluorescence spectroscopy, AFS; and optogalvanic spectroscopy) and mass spectrometric (magnetic sector, quadrupole mass analyzer, QMA; quadrupole ion trap, QIT; Fourier transform ion cyclotron resonance, FTICR; and time-of-flight, TOF) instrumentation are well suited for coupling to the glow discharge (GD). The GD is a relatively simple device. A potential gradient (500–1500 V) is applied between an anode and a cathode. In most cases, the sample is also the cathode. A noble gas (mostly Ar) is introduced into the discharge region before power initiation. When a potential is applied, electrons are accelerated toward the anode. As these electrons accelerate, they collide with gas atoms. A fraction of these collisions are of sufficient energy to remove an electron from a support gas atom, forming an ion. These ions are, in turn, accelerated toward the cathode. These ions impinge on the surface of the cathode, sputtering sample atoms from the surface. Sputtered atoms that do not redeposit on the surface diffuse into the excitation/ionization regions of the plasma where they can undergo excitation and/or ionization via a number of collisional processes, and the photons or ions created in this way can be detected with optical emission spectroscopy or mass spectrometry. GD sources offer a number of distinct advantages that make them well suited for specific types of analyses. These sources afford direct analysis of solid samples, thus minimizing the sample preparation required for analysis. The nature of the plasma also provides mutually exclusive atomization and excitation processes that help to minimize the matrix effects that plague so many other elemental techniques. In recent years, there is also increasing interest for using GD sources for liquid and gas analyses. In this article, first, the principles of operation of the GD plasma are reviewed, with an emphasis on how those principles relate to optical spectroscopy and mass spectrometry. Basic applications of the GD techniques are considered next. These include bulk analysis, surface analysis, and the analysis of solution and gaseous samples. The requirements necessary to obtain optical information are addressed following the analytical applications. This article focuses on the instrumentation needed to make optical measurements using the GD as an atomization/excitation source. Finally, mass spectrometric instrumentation and interfaces are addressed as they pertain to the use of a GD plasma as an ion source. GD sources provide analytically useful gas-phase species from solid samples. These sources can be interfaced with a variety of spectroscopic and spectrometric instruments for both quantitative and qualitative analyses.
Keywords: H1 Book chapter; Plasma Lab for Applications in Sustainability and Medicine – Antwerp (PLASMANT)
|
“Biofilms for one-stage autotrophic nitrogen removal”. Carvajal-Arroyo JM, Vitor Akaboci TR, Ruscalleda M, Colprim J, Courtens E, Vlaeminck SE page 205 (2016).
Keywords: H3 Book chapter; Engineering sciences. Technology; Sustainable Energy, Air and Water Technology (DuEL)
|
Fenu A (2016) Modelling and operations of municipal membrane bioreactors : from conventional to novel applications. 180 p
Keywords: Doctoral thesis; Engineering sciences. Technology; Sustainable Energy, Air and Water Technology (DuEL)
|
Van Wesenbeeck K (2016) Plasma catalysis as an efficient and sustainable air purification technology. 171 p
Keywords: Doctoral thesis; Engineering sciences. Technology; Sustainable Energy, Air and Water Technology (DuEL)
|
“Art, science and sustainability = Kunst, wetenschap en duurzaamheid”. Van Tendeloo G Vrienden van het M HKA, Antwerpen, page 24 (2016).
Keywords: H2 Book chapter; Art; Electron microscopy for materials research (EMAT)
|
“Fundamentals of Focal Series Inline Electron Holography”. Lubk A, Vogel K, Wolf D, Krehl J, Röder F, Clark L, Guzzinati G, Verbeeck J Advances in imaging and electron physics
T2 – Advances in imaging and electron physics / Hawkes, P.W. [edit.]. Elsevier BV, page 105 (2016).
Keywords: H1 Book chapter; Electron microscopy for materials research (EMAT)
DOI: 10.1016/bs.aiep.2016.08.003
|