Abstract: A two-step process for the formation of sensitivity centers different from earlier described two-step processes was found for sulfur sensitized emulsions. After deposition of sulfur in the first step, it was found that the second step does not consist of rearrangement of sulfur over the surface, but of the supply of silver interstitial ions towards the deposited sulfur clusters. The two processes could be separated by adsorbing and desorbing TAI (4-hydroxy-1, 3,3a, 7-tetraazaindene) at/from the silver halide surface. When 1.5 mmol TAI/mol Ag is added before the sulfur reaction, the silver interstitials are immobilized but sulfur still can be deposited at the same level. By lowering the pH to 2.50 after this sulfur reaction, TAI is desorbed from the surface and the released interstitials then cause a restoration of the properties of a sulfur system without TAI. These effects could be demonstrated via diffuse reflectance spectroscopy (DRS), sensitometry and dielectric loss measurements. We could also confirm the isolation of silver sulfide clusters by TAI from other chemicals in the solution, by adsorption of TAI on the clusters.

Abstract: Rutherford backscattering and channeling spectrometry (RBS), photoluminescence (PL) spectroscopy and transmission electron microscopy (TEM) have been used to investigate macroscopic and microscopic segregation in MOCVD grown InGaN layers. The PL peak energy and In content (measured by RES) were mapped at a large number of distinct points on the samples. An indium concentration of 40%, the highest measured in this work, corresponds to a PL peak of 710 nn strongly suggesting that the light-emitting regions of the sample me very indium-rich compared to the average measured by RES. Cross-sectional TEM observations show distinctive layering of the InGaN films. The TEM study further reveals that these layers consist of amorphous pyramidal contrast features with sizes of order 10 nm The composition of these specific contrast features is shown to be In-rich compared to the nitride matrix.

Abstract: Addition of a labile sulphur donor to light sensitive silver halide microcrystals results in the formation of a distribution of silver sulphide clusters on the crystal surface. These silver sulphide clusters enhance the efficiency of image formation during the photographic process. Their activity towards the capturing of light photons, however, is very critical to their size (aggregation number) and concentration. By incorporating gold ions into silver sulphide clusters it was possible to monitor the size distribution by measuring the amount of gold reacted. From these experiments, no evidence was found for aggregation of the reacted sulphur entities on the surface. The uptake of gold ions at different sulphur concentrations could well be fitted with a simulated size distribution when a catalyzed deposition of sulphur was assumed, with a reactivity of the surface equal to 1.0 % for the microcrystals studied. From a simulation of the silver sulphide cluster size distribution a correlation could also be found between increasing aggregation numbers and the absorption at increasing wavelengths in diffuse reflectance spectroscopy.