Abstract: The results of an in situ transmission electron microscopy study of the formation of Co-silicides on patterned (001) Si substrates are discussed. It is shown that the results of the in situ heating experiments agreed very well with the data based on standard rapid thermal annealing experiments. Fast heating rates resulted in better definition of the silicide lines. Also, better lines were obtained for samples that received already a low-temperature ex situ anneal. A Ti cap layer gave rise to a higher degree of epitaxy in the CoSi2 silicide.

Abstract: Nanocrystalline titanium dioxide was prepared via aerosol pyrolysis of titanium alkoxide precursor at 200-580 degrees C in air and in nitrogen atmospheres. Powders were characterized by x-ray diffraction, thermogravimetric analysis, Brunauer-Emmett-Teller analysis, scanning electron microscopy, transmission electron microscopy, energy dispersive spectroscopy, x-ray fluorescence, Raman and infrared spectroscopy, and Berner-type low-pressure impactor. The anatase phase transition was initiated at 500 degrees C in nitrogen and at 580 degrees C in air. Under other conditions amorphous powders were observed and transformed to nanocrystalline TiO2 via thermal postannealing. In air, smooth and spherical particles with 2-4-mu m diameter were formed with an as-expected tendency to convert to rutile in the thermal postannealings. In nitrogen, a fraction of the titanium tetrabutoxide precursor evaporated and formed ultrafine particles via the gas-to-particle conversion. At 500 degrees C thermally stable anatase phase was formed in nitrogen. A specific surface area as high as 280 m(2) g(-1) was observed for an as-prepared powder.

Abstract: We have investigated epitaxially grown single-crystalline Ca-doped LaMnO3 thin films using the pulsed laser deposition technique in a case study aimed to explore the possibilities buried in epitaxial stress tailoring in order to control the transport properties of CMR materials beyond the limits set by equilibrium thermodynamics. Depending on the film thickness there is an abrupt transition from pseudomorphic to epitaxial granular growth observable which is related to the epitaxial strain of the films. This is associated with microscopic stress relaxation and leads to well controllable modifications of the atomic arrangements of the Mn-O sublattice in the films. Due to the interrelation of double exchange, spin-, charge- and orbital ordering and the Jahn-Teller effect mediated coupling of the electronic system to the crystal lattice, the magnetotransport properties of the firms can be modified in a controllable way.

Abstract: Advanced transmission electron microscopy and statistical parameter estimated quantification procedures were applied to study the room temperature quasi-dynamical strain glass state in NiTi alloys. Nanosized strain pockets are visualised and the displacements of the atom columns are quantified. A comparison is made with conventional high-resolution transmission electron microscopy images of point defect induced strains in NiAl alloys.

Abstract: Various modes of transmission electron microscopy including aberration corrected imaging were used in order to unravel the fundamental mechanisms controlling the formation of growth twins and the evolution of twin boundaries under mechanical and hydrogen loading modes in nanocrystalline (nc) palladium thin films. The latter were produced by electron-beam evaporation and sputter deposition and subjected to uniaxial tensile deformation as well as hydriding/dehydriding cycles. The results show that the twins form by dissociation of grain boundaries. The coherency of Σ3{111} coherent twin boundaries considerably decreases with deformation due to dislocation/twin boundary interactions while Σ3{112} incoherent twin boundaries dissociate under hydrogen cycling into two-phase boundaries bounding a new and unstable 9R phase. The effect of these elementary mechanisms on the macroscopic behavior of the palladium films is discussed and compared to recent experimental and simulation works in the literature. The results provide insightful information to guide the production of well-controlled population of growth twins in high stacking fault energy nc metallic thin films. The results also indicate directions for further enhancement of the mechanical properties of palladium films as needed for instance in palladium-based membranes in hydrogen applications.

Abstract: Synergistic compositions of detonation nanodiamond (DND) particles with polytetrafluoroethylene and molybdenum dialkyldithiophosphate were used in ring-on-ring, four-ball, and block-on-ring tests as an additive to polyalphaolefins and engine oils. Modest to significant reductions in the friction coefficients, wear, or both were observed. In the wear scars produced in the block-on-ring tests, the friction surfaces were characterized by scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDX), and profilometry. Significant polishing effects of the friction surfaces in lubricants containing DND were revealed in SEM observations and roughness measurements. The roughness of the scar surfaces produced in the presence of DND additives was about 35% lower than the roughness of the scars observed in pure oil experiments.

Abstract: The chemical composition, nanostructure and electronic structure of nanosized oxide scales naturally formed on the surface of AISI 316L stainless steel microfibres used for strengthening of composite materials have been characterised using a combination of scanning and transmission electron microscopy with energy-dispersive X-ray, electron energy loss and Auger spectroscopy. The analysis reveals the presence of three sublayers within the total surface oxide scale of 5.0-6.7 nm thick: an outer oxide layer rich in a mixture of FeO.Fe2 O3 , an intermediate layer rich in Cr2 O3 with a mixture of FeO.Fe2 O3 and an inner oxide layer rich in nickel.

Abstract: The high temperature phase of Ni1-xS has the NiAs-type structure. The coexistence of two superstructures, ''3a3a3c'' and ''2a2a3c'' with the basic phase is confirmed by means of electron diffraction. The 2a2a3c superstructure is studied by means of electron diffraction and high resolution electron microscopy. A structure model is proposed based on the periodic insertion of stacking faults in the NiAs-type basic structure and the ordering of vacancies in alternate metal-atom layers. Microtwinning in very narrow slabs is found to be a main feature of the 2a2a3c regions and two defect models are discussed.