Abstract: The cubic phase of HfO2 was stabilized by addition of yttrium in thin films grown on Si/SiO2 by metal-organic chemical vapor deposition. The cubic phase was obtained for contents of 6.5 at. % Y or higher at a temperature as low as 470 °C. The complete compositional range (from 1.5 to 99.5 at. % Y) was investigated. The crystalline structure of HfO2 was determined from x-ray diffraction, electron diffraction, and attenuated total-reflection infrared spectroscopy. For cubic films, the continuous increase in the lattice parameter indicates the formation of a solid-solution HfO2Y2O3. As shown by x-ray photoelectron spectroscopy, yttrium silicate is formed at the interface with silicon; the interfacial layer thickness increases with increasing yttrium content and increasing film thickness. The dependence of the intrinsic relative permittivity r as a function of Y content was determined. It exhibits a maximum of ~30 for ~8.8 at. % Y. The cubic phase is stable upon postdeposition high-temperature annealing at 900 °C under NH3.

Abstract: Atomic layer deposition (ALD) is a vapor phase technique that is able to deposit uniform, conformal thin films with an excellent thickness control at the atomic scale. 18 nm thick Al2O3 and TiO2 coatings were deposited conformaly and pinhole-free onto micrometer-sized Cu powder, using trimethylaluminum and tetrakis(dimethylamido)titanium(IV), respectively, as a precursor and de-ionized water as a reactant. The capability of the ALD coating to protect the Cu powder against corrosion was investigated. Therefore, the stability of the coatings was studied in solutions with different pH in the range of 0–14, and in situ raman spectroscopy was used to detect the emergence of corrosion products of Cu as an indication that the protective coating starts to fail. Both ALD coatings provide good protection at standard pH values in the range of 5–7. In general, the TiO2 coating shows a better barrier protection against corrosion than the Al2O3 coating. However, for the most extreme pH conditions, pH 0 and pH 14, the TiO2 coating starts also to degrade.

Abstract: Infrared absorption spectra of composite precipitates are analysed with a modified Day-Thorpe algorithm, assuming a precipitated phase consisting of a mixture of two components with known optical properties. Additional constraints are introduced when solving the model equations by using a priori knowledge making the algorithm more reliable. It is shown that this novel approach allows determining both morphology and composition of precipitates. The method is applied to characterise oxide precipitates in boron-doped silicon. The results indicate that for the resistivity range above 60 mOmegacm, the precipitated phase is most probably SiO1.17+/-0.14, while for resistivities below 20 mOmega cm, precipitates consist of a SiO2/B2O3 composite with a large volume fraction of B(2)0(3) (up to 40% for 8 mOmegacm material). (C) 2003 Elsevier B.V. All rights reserved.

Abstract: Infrared absorption spectra of polyhedral and platelet oxygen precipitates are analyzed using a modified Day-Thorpe approach (J. Phys.: Condens. Matter 11 (1999) 2551). The aspect ratio has been determined by TEM measurements. The reduced spectral function and the stoichiometry are extracted from the absorption spectra and the concentration of precipitated interstitial oxygen. One set of spectra reveal a Frohlich frequency around 1100 cm(-1) and another around 1110-1120 cm(-1). It is shown that the shift in the Frohlich frequency is not due to a different stoichiometry, but due to the detailed structure in the reduced spectral function. The oxygen precipitates consist of SiO. with gammaapproximate to1.1-1.2+/-0.1. (C) 2001 Elsevier Science B.V. All rights reserved.

Abstract: We used atom probe tomography to complement electron microscopy for the investigation of spinodal decomposition in alkali feldspar. To this end, gem-quality alkali feldspar of intermediate composition with a mole fraction of a(K) = 0.43 of the K end-member was prepared from Madagascar orthoclase by ion-exchange with (NaK)Cl molten salt. During subsequent annealing at 550 degrees C and close to ambient pressure the ion-exchanged orthoclase unmixed producing a coherent lamellar intergrowth of Na-rich and K-rich lamellae. The chemical separation was completed, and equilibrium Na-K partitioning between the different lamellae was attained within four days, which was followed by microstructural coarsening. After annealing for 4 days, the wavelength of the lamellar microstructure was approximate to 17 nm and it increased to approximate to 30 nm after annealing for 16 days. The observed equilibrium compositions of the Na-rich and K-rich lamellae are in reasonable agreement with an earlier experimental determination of the coherent solvus. The excess energy associated with compositional gradients at the lamellar interfaces was quantified from the initial wavelength of the lamellar microstructure and the lamellar compositions as obtained from atom probe tomography using the Cahn-Hilliard theory. The capability of atom probe tomography to deliver quantitative chemical compositions at nm resolution opens new perspectives for studying the early stages of exsolution. In particular, it helps to shed light on the phase relations in nm scaled coherent intergrowth.

Abstract: YBa(2)Cu(3)O(7-delta) (YBCO) grain boundaries characterized by a misalignment of the c-axes (45 degrees c-axis tilt or 45 degrees c-axis twist) have been obtained by employing a recently implemented biepitaxial technique. Junctions based on these grain boundaries exhibit good Josephson properties useful for applications. High values of the I(C)R(N) product and a Fraunhofer-like dependence of the critical current on the magnetic field, differently from traditional biepitaxial junctions, have been obtained. The correlation between transport properties and microstructure has been investigated by Transmission Electron Microscopy (TEM), which was also performed on previously measured junctions. The presence of atomically clean basal plane (BP) faced tilt boundaries, among other types of interfaces, has been shown. The possibility of selecting these kinds of boundaries by controlling film growth, and their possible advantages in terms of reproducibility and uniformity of the junction properties an discussed. The possibility of employing these junctions to explore the symmetry of the order parameter is also discussed. (C) 1999 Elsevier Science B.V. All rights reserved.

Abstract: Nanostripes are observed in melt-textured and single-crystalline samples of the ternary light rare earth (LRE)-compound (Nd0.33Eu0.33Gd0.33)Ba2Cu3Ox (NEG) by means of atomic force microscopy, scanning tunnelling microscopy at ambient conditions, combined with transmission electron microscopy and electron backscatter diffraction. This enables the observation of several important features: The nanostripes are formed by chains of nanoclusters, representing the LRE/Ba substitution. The dimensions of the nanostripes are similar for both types of NEG samples. The periodicity of the nanostripes is found to range between 40 and 60 nm; the shape of the nanoclusters is elliptic with a major axis length between 300 and 500 nm and a minor axis length of about 30150 nm. The stripes are filling effectively the space in between the twin boundaries. Concerning the flux pinning, the nanoclusters are the important pinning sites, not the nanostripes themselves.