Abstract: A ''2222'' cuprate with mercury bilayers (Hg1.5Cu0.2Pr0.3)Ba2Pr2Cu2O10-delta, has been synthesized for the first time. It crystallizes in the P4/nmm space group with a = 3.9072(1) Angstrom and c = 17.219(1) Angstrom. The powder XRD and HREM studies of this new cuprate show that its structure consists of an intergrowth of double pyramidal (oxygen-deficient perovskite) copper layers, with double fluorite-type layers and distorted triple rock salt layers (mercury bilayers). The structure of this phase can be deduced from that of the ''2212'' mercury cuprate (Hg1.5Cu0.2Pr0.3)Ba2PrCu2O8-delta by the introduction of one additional [PrO2]infinity fluorite layer. The regular stacking of the metallic layer and the uniform cationic distribution in the mercury bilayers are remarkable features of this cuprate. The stabilization of the mercury bilayers by praseodymium and the absence of superconductivity are discussed. (C) 1995 Academic Press, Inc.

Abstract: The new families of superconducting compounds ''1201'' (Hg0.4Pr0.6Sr2CuO4+delta), ''1212'' (Hg0.4Pr0.6Sr2(Ca1-x-ySrxPry) Cu2O6+delta), and ''1222'' (Hg0.4Pr0.6Sr2(Pr1.7Sr0.3)(2)Cu2O8+delta) all show ordering between praseodymium and mercury in the (Hg,Pr)O-delta plane, reducing the symmetry from tetragonal to orthorhombic or even to monoclinic. In the 1201 compound the ordered superstructure can be described as O-I (a(I) approximate to 2a(p), b(I), approximate to a(p), c(I) approximate to c(1201)). In the 1212 compound two distinct superstructures are identified, O-I (a(I) approximate to 2a(p), b(II) approximate to a(p), c(I) approximate to c(1212)) and O-II (a(II) approximate to 2a(p), b(II) approximate to a(p), c(II) approximate to 2c(1212)). In some compounds, such as Hg0.4Pr0.6Sr2(Ca0.4Sr0.4Pr0.2) Cu2O6+delta, the Hg-Pr ordering is only present in microdomains, but due to an ordering between Sr layers and Ca layers, the c-axis doubles and one obtains a tetragonal superstructure T-III (a(III) approximate to a(p), c(III) approximate to 2c(1212)). In the 1222 compound, ordering in the (Pr,Hg)O-delta plane is very defective; a large number of translation defects actually reduce the symmetry to triclinic. (C) 1995 Academic Press, Inc.

Abstract: The structure and defect structure of Bi2-xPbxSr3.5Cu2 (CO3)O8-delta compounds with 0 less-than-or-equal-to x less-than-or-equal-to 0.75 are carefully investigated by electron diffraction and high-resolution electron microscopy. All compounds have an orthorhombic structure with a almost-equal-to b almost-equal-to 5.4 angstrom and c almost-equal-to 39.5 angstrom. The length of the b-axis decreases monotonically with increasing x. The space group for the basic structure is Abm2. The structure can be considered as an intergrowth of Bi2Sr2CuO6 lamellae with Sr2CuO2 (CO3) lamellae along the c-axis. CO3 groups behave as bridges connecting the CuO6 octahedra. In the x = 0 compound the carbon atoms are shifted away from their symmetry positions; the orientational ordering of the CO3 groups (or the carbon shift) in successive CO planes alternates along +b and -b. Typical Bi-type and Pb-type modulations are found along the b-axis up to a Pb content x = 0.5. Electron beam irradiation destroys the ordering of the CO3 groups and alters the modulated structure. (C) 1994 Academic press, inc.

Abstract: The ternary oxides Ba8Ta4Ti3O24 and Ba10Ta7.04Ti1.2O30 were synthesized and their crystal structures and defects were studied by means of X-ray powder diffraction, electron diffraction, and high resolution electron microscopy. The crystal structure of Ba8Ta4Ti3O24 is based on the 8H (cchc)(2) close-packed stacking (a 10.0314 Angstrom, c = 18.869 Angstrom, SG P6(3)/mcm, Z = 3) and that of Ba10Ta7.04Ti1.2O30 and on the 10H (cchcc)(2) close-packed stacking (a = 5.7981 Angstrom, c = 23.755 Angstrom, SG P6(3)/mmc, Z = 1) of BaO3 layers. The structural refinements gave the following values for the R factors for Ba8Ta4Ti3O24 (Ba10Ta7.04Ti1.2O30) R(I) = 0.041 (0.039), R(P) = 0.108 (0.118), and R(wP) = 0.094 (0.099). The main feature of both structures is the presence of two types of face-sharing octahedra (FSO) with different occupancies by Ta atoms, Ti atoms, and vacancies, which results in the formation of a superstructure. It was shown that in the Ba8Ta4Ti3O24 structure these pairs of FSO occur in an ordered fashion and in the Ba10Ta7.04Ti1.2O30 structure in a disordered fashion. The existence of the wide range of solid solutions was shown to be also a consequence of the presence of one of the two types of face-sharing octahedra. (C) 1995 Academic Press, Inc,

Abstract: The structure of Ca0.85CuO2 was reexamined by means of electron diffraction and electron microscopy using the newly developed method of selective imaging in intergrowth structures in which the two substructures are based on different sublattices. The results of previous work are confirmed. Moreover, it is shown that two stacking variants and their twin related structures occur in the calcium substructure. The copper-oxygen substructure occurs in one variant only; it is often modulated by the various calcium arrangements, leading to phase disorder in its modulation pattern. It is shown that the ribbons of CuO4 clusters are presumably tilted with respect to the (010) plane.

Abstract: Five new layered cuprates, with a 1222-type structure, have been synthesized according to the formula (Hg(1-x)M(x))(Sr,Ba)(2) Pr2Cu2O9-delta with M = Pr, Pb, Pi, and Tl. They crystallize in a tetragonal cell with a approximate to a(p) and c approximate to 29.5 Angstrom; their structure consists in a triple intergrowth of oxygen-deficient perovskite, rock-salt-and fluorite-type layers. They are characterized by a mixed [Hg(1-x)M(x)O(1-delta)] layer in the rock-sail-type slice. The ED and HREM studies show that Tl, Bi, and Pb are statistically distributed in the mixed [Hg(1-x)M(x)O(1-delta)] layer, contrary to Pr which involves an ordering phenomenon along a. Different stacking defects are observed and discussed as well as the cleavage mode of the crystals. (C) 1995 Academic Press, Inc.

Abstract: The possible role of a prior amorphous phase separation on the subsequent crystallization has been the topic of vigorous debates over the last decades and has not yet been clarified, especially regarding the role of the interfaces created by the phase separation. This study proposes to focus on the interplay between a prior amorphous phase separation and the crystallization of fresnoite in the BaO-TiO2-SiO2 system. The crystallization behavior of a non-stoichiometric composition inside the miscibility gap (called APS) is compared with the stoichiometric composition (called FRES) and a non-stoichiometric composition outside the miscibility gap (called NoAPS). The crystallization mechanisms are compared using differential thermal analysis (DTA) by calculating the Avrami parameters and the activation energies as a function of the particle size. The DTA study shows that the two non-stoichiometric compositions exhibit a pronounced surface crystallization behavior whereas FRES undergoes bulk nucleation. This is supported by a multi-scale microstructure characterization. Furthermore, this study demonstrates that the amorphous phase separation and the associated interfaces do not play any significant role in the nucleation step. Moreover, transmission electron microscope (TEM) and local orientation measurements show that the growth of the dendrites is not hindered by the SiO2-rich droplets. The final stage of crystallization of APS is tentatively explained by two composition effects that must be further investigated: the viscosity effect and the formation of a eutectic. (C) 2013 Elsevier B.V. All rights reserved.

Abstract: This study demonstrates that the mechanism responsible for the transformation of glass into a degradation layer is pH-dependent. In acid conditions, the transformed glass is homogeneous and brittle. In mild alkaline conditions, transformed glass is heterogeneous due to the presence of lamellae composed of silica nanoparticles and the occurrence of Ca-rich inclusions. The fundamental difference between acid and alkaline conditions cannot be explained by the currently accepted degradation mechanism based on ion exchange. To explain this critical observation, we propose a refined degradation mechanism based on existing knowledge that involves several inwardly moving reaction fronts. The fronts responsible for the transformation of the silicate network into amorphous silica are also responsible for the morphology of the transformed glass. We have identified the feedback mechanism that explains the formation of lamellae in alkaline conditions.