Abstract: Oxygen-deficient complex cobalt oxides BaCo1 − xYxO3 − y, = 0.15, 0.25 and 0.33, with a cubic perovskite structure have been synthesized in air at 1100 °C using a citrate route. Cation composition of the compounds was confirmed by energy-dispersed X-ray (EDX) microanalysis while oxygen content was determined by iodometric titration. An electron diffraction (ED) study of the x = 0.25 and 0.33 compositions show the presence of a diffuse intensity, indicating possible short-range ordering of the B cations. It was found that the treatment of BaCo0.75Y0.25O2.55 in a humid atmosphere leads to the absorption of water vapour at the first stage. Oxygen permeation studies of the ceramic membranes of BaCo0.75Y0.25O2.55 and BaCo0.67Y0.33O2.55 with variable thickness showed high oxygen fluxes of 0.170.32 µmol/cm2/s at 950 °C.

Abstract: The electro-phonon resonance effect is a consequence of a resonant interaction between two electric subbands mediated by an optical phonon. It occurs in a quasi-two-dimensional electron system each time the energy difference between two electric subbands equals the energy of a Lo phonon. We study the influence of this effect on the electron mobility by using the momentum balance equation. The temperature and electron density dependences of the resonances are studied in the linear and non-linear response regimes.

Abstract: We optimized the deposition of YBa2(Cu1-xZnx)(3)O-7-delta thin-films using inverted cylindrical magnetron sputtering and report here a detailed structural study, especially in relation to crystal growth, associated surface morphology, Y2O3 precipitation and other secondary phases important for flux pinning. We find that the epitaxial quality of the Zn-substituted YBa2Cu3O7-delta films is decreased compared with high-quality pure YBa2Cu3O7-delta films prepared under identical conditions. The pure films have smoother surfaces, while those of Zn-substituted films contain pinholes and outgrowths. Secondary phases and a-axis grains were observed in the Zn-substituted films. Y2O3 precipitates with typical dimensions of 50-100 Angstrom have been found in both pure and Zn-substituted samples. However, their density of about 10(23) m(-3), observed in the pure films, is significantly reduced in the Zn-substituted films when increasing the Zn concentration up to 4%.

Abstract: The SiC/Al composites have been fabricated by a vacuum hot pressing (VHP) process in order to study the effect of interface evolution on the global thermal conductivity (TC). By optimizing the VHP parameters of sintering temperature and time, the three different kinds of SiC/Al interface configurations, that is, non-bonded, diffusion-bonded, and reaction-bonded interfaces, are formed and identified by measurement of relative density, X-ray diffraction, scanning and (high-resolution) transmission electron microscopy. The VHPed composite sintered at 655 °C for 60 min is fully dense and presents a tightly-adhered and clean SiC/Al interface at the nanoscale, the ideal diffusion-bonded interface being the most favorable for minimizing interfacial thermal resistance, which in turn results in the highest TC of around 270 W/mK.

Abstract: Electrochemical impedance measurements have been used to investigate the influence of the deposition method, including time and temperature, upon the corrosion inhibition characteristics of lead dodecanoate coatings on lead electrodes. The results were analysed using multivariate statistics and show that, in general, these easily prepared coatings are very protective against corrosion. The temperature proves to be an important parameter for the quality and the corrosion inhibition efficiency of the coating. A comparison between two different electrochemically assisted deposition methods, immersion using a reduction pretreatment and cyclic voltammetry, does not show significant differences. Using the immersion technique at room temperature, the deposition time was tested as the third influencing parameter for the corrosion inhibition efficiency of the deposited lead dodecanoate coatings. A longer deposition time of the lead into the sodium dodecanoate solution provides a layer with a somewhat higher corrosion resistance.

Abstract: The oxidation states of uranium in depleted uranium (DU) particles were determined by synchrotron radiation based mu-XANES, applied to individual particles isolated from selected samples collected at different sites in Kuwait. Based on scanning electron microscopy with X-ray microanalysis prior to mu-XANES, DU particles ranging from sub-microns to several hundred micrometers were observed. The.median particle size depended on sources and sampling sites; small-sized particles (median 13 mum) were identified in swipes taken from the inside of DU penetrators holes in tanks and in sandy soil collected below DU penetrators, while larger particles (median 44 mum) were associated with fire in a DU ammunition storage facility. Furthermore, the U-236/U-235 ratios obtained from accelerator mass spectrometry demonstrated that uranium in the DU particles originated from reprocessed fuel (about 10(-2) in DU from the ammunition facility, about 10(-3) for DU in swipes). Compared to well-defined standards, all investigated DU particles were oxidized. Uranium particles collected from swipes were characterized as UO2, U3O8 or a mixture of these oxidized forms, similar to that observed in DU affected areas in Kosovo. Uranium particles formed during fire in the DU ammunition facility were, however, present as oxidation state +5 and +6, with XANES spectra similar to solid uranyl standards. Environmental or health impact assessments for areas affected by DU munitions should therefore take into account the presence of respiratory UO2, U3O8 and even UO3 particles, their corresponding weathering rates and the subsequent mobilisation of U from oxidized DU particles. (C) 2004 Elsevier Ltd. All rights reserved.

Abstract: A combination of synchrotron radiation based X-ray microscopic techniques (ì-XRF, ì-XANES, ì-XRD) applied on single depleted uranium (DU) particles and semi-bulk leaching experiments has been employed to link the potential bioavailability of DU particles to site-specific particle characteristics. The oxidation states and crystallographic forms of U in DU particles have been determined for individual particles isolated from selected samples collected at different sites in Kosovo and Kuwait that were contaminated by DU ammunition during the 1999 Balkan conflict and the 1991 Gulf war. Furthermore, small soil or sand samples heavily contaminated with DU particles were subjected to simulated gastrointestinal fluid (0.16 M HCl) extractions. Characteristics of DU particles in Kosovo soils collected in 2000 and in Kuwait soils collected in 2002 varied significantly depending on the release scenario and to some extent on weathering conditions. Oxidized U (+6) was determined in large, fragile and bright yellow DU particles released during fire at a DU ammunition storage facility and crystalline phases such as schoepite (UO3·2.25H2O), dehydrated schoepite (UO3·0.75H2O) and metaschoepite (UO3·2.0H2O) were identified. As expected, these DU particles were rapidly dissolved in 0.16 M HCl (84 ± 3% extracted after 2 h) indicating a high degree of potential mobility and bioavailability. In contrast, the 2 h extraction of samples contaminated with DU particles originating either from corrosion of unspent DU penetrators or from impacted DU ammunition appeared to be much slower (2030%) as uranium was less oxidized (+4 to +6). Crystalline phases such as UO2, UC and metallic U or UTi alloy were determined in impacted DU particles from Kosovo and Kuwait, while the UO2,34 phase, only determined in particles from Kosovo, could reflect a more corrosive environment. Although the results are based on a limited number of DU particles, they indicate that the structure and extractability of DU particles released from similar sources (metallic U penetrators) will depend on the release scenarios (fire, impact) and to some extent environmental conditions. However, most of the DU particles (7396%) in all investigated samples were dissolved in 0.16 M HCl after one week indicating that a majority of the DU material is bioaccessible.